Recent progress on advanced infrared photodetectors

Hu Wei-Da; Li Qing; Chen Xiao-Shuang; Lu Wei

doi:10.7498/aps.68.20190281

Abstract

Modern infrared detector technology has a history of nearly eighty years. Since the first PbS photodiode was put into use during the World War II, infrared detectors have achieved significant progress, even the third-generation infrared systems have been proposed. In the past decades, the traditional infrared detectors represented by HgCdTe, InSb and InGaAs have been widely applied in military, remote sensing, communication, bioscience, and space exploration. However, the increasing applications demand higher performance infrared detectors. Especially in recent years, the intelligent infrared detection technique was strongly demanded in many high-tech fields such as artificial intelligence, virtual reality systems and smart city. Therefore, the fabricating of infrared detection systems with smaller size, lighter weight, lower power, higher performance and lower price has become an urgent task. At present, the infrared photodetectors are in an age of rapid change, and many new type of advanced infrared photodetectors come to the fore quickly. For the purpose of summarizing these detectors, they are reviewed covering four parts: microstructure coupled infrared detector, infrared detector based on band engineering, new type of low-dimensional material infrared detector, and new directions for traditional infrared detectors. In the infrared detection systems, these photodetectors can be fully used for their prominent performance. The microstructure coupled infrared detector can improve chip integration with high quantum efficiency. Precise design of band structure will raise the operating temperature for mid and long wavelenth infrared photodetectors. Owing to the unique structures and physical properties, low-dimensional material infrared photodetectors have shown their potential application value in flexibility and room temperature detection systems. The ability of avalanche photodetector to detect the extremely weak signal makes it possible using in the frontier science such as quantum private communication and three-dimensional radar imaging systems. The device based on hot electron effect provides a new idea for far infrared detection. The barrier detectors will reduce the manufacturing cost of traditional materials and the design is also very illuminating for other new materials. In this review, firstly we present the history of infrared photodetectors in short. Then the mechanism and achievements of the advanced infrared photodetectors are introduced in detail. Finally, the opportunities and challenges of infrared detection are summarized and predicted.

Keywords:

Authors and contacts

1.
State Key Laboratory of Infrared Physics, Shanghai Institute of Technical Physics, Shanghai 200083, China
2.
University of Chinese Academy of Sciences, Beijing 100084, China

Corresponding author: Hu Wei-Da, wdhu@mail.sitp.ac.cn ; Lu Wei, luwei@mail.sitp.ac.cn

Funds: Project supported by the National Science Fund for Distinguished Young Scholars of China (Grant No. 61725505), the Key Program of the National Natural Science Foundation of China (Grant No. 11734016), the Science Fund for Creative Research Groups of the National Natural Science Foundation of China (Grant No. 61521005), and the Program of Shanghai Subject Chief Scientist, China (Grant No. 19XD1404100).

FullText HTML : translate this paragraph

References

[1]	Herschel W 1800 Philos. Trans. Roy. Soc. London 90 284 Google Scholar
[2]	Rogalski A 2012 Opt. Electron. Rev. 20 279
[3]	Becquerel M 1839 Comptes Rendus Hebdomadaires des Séances de l'Académie des Sciences 9 561
[4]	Smith W 1873 Nature 7 303 Google Scholar
[5]	Case T W 1917 Phys. Rev. 9 305 Google Scholar
[6]	Lange B 1930 Phys. Zeitschr 31 139
[7]	Lange B 1931 Naturwissenschaften 19 525 Google Scholar
[8]	Lovell D 1969 Am. J. Phys. 37 467 Google Scholar
[9]	Avery D, Goodwin D, Lawson W, Moss T 1954 Proc. Phys. Soc.Section B 67 761 Google Scholar
[10]	Lawson W, Nielsen S, Putley E, Young A 1959 J.Phys. Chem. Solids 9 325 Google Scholar
[11]	汤定元 1991 激光与红外 21 5 Tang D Y 1991 Laser & Infrared 21 5
[12]	茅文英, 褚君浩, 李言谨, 王子孟, 方家熊 1994 红外与毫米波学报 13 352 Mao W Y, Chu J H, Li Y J, Wang Z M, Fang J X 1994 J. Infrared Millim.Waves 13 352
[13]	杨建荣, 何进 1994 红外与毫米波学报 13 191 Yang J R, He J 1994 J. Infrared Millim.Waves 13 191
[14]	Rogalski A, Antoszewski J, Faraone L 2009 J. Appl. Phys. 105 091101 Google Scholar
[15]	杨建荣 2012 碲镉汞材料物理与技术第一版 (北京: 国防工业出版社) 第3—7页 Yang J R 2012 Physics and Technology of HgCdTe Materials (1st Ed.) (Beijing: National Defense Industry Press) pp3−7 (in Chinese)
[16]	Esaki L, Tsu R 1970 IBM J. Res. Dev. 14 61 Google Scholar
[17]	Lin H, Cheung H Y, Xiu F, Wang F, Yip S, Han N, Hung T, Zhou J, Ho J C, Wong C Y 2013 J. Mater. Chem. A 1 9942 Google Scholar
[18]	Cansizoglu H, Bartolo-Perez C, Gao Y, Devine E P, Ghandiparsi S, Polat K G, Mamtaz H H, Yamada T, Elrefaie A F, Wang S Y 2018 Photon. Res. 6 734 Google Scholar
[19]	胡伟达, 梁健, 越方禹, 陈效双, 陆卫 2016 红外与毫米波学报 35 25 Google Scholar Hu W D, Liang J, Yue F Y, Chen X S, Lu W 2016 J. Infrared Millim. Waves 35 25 Google Scholar
[20]	Krishna S, Posani K T, Tripathi V, Annamalai S 2005 The 18th Annual Meeting of the IEEE Sydney, Australia October 22−28, 2005 p909
[21]	Hiralal P, Chien C, Lal N N, Abeygunasekara W, Kumar A, Butt H, Zhou H, Unalan H E, Baumberg J J, Amaratunga G A 2014 Nanoscale 6 14555 Google Scholar
[22]	Wehner J, Smith E, Venzor G, Smith K, Ramirez A, Kolasa B, Olsson K, Vilela M 2011 J. Electron. Mater. 40 1840 Google Scholar
[23]	Pinkie B, Schuster J, Bellotti E 2013 Opt. Lett. 38 2546 Google Scholar
[24]	Gao Y, Cansizoglu H, Polat K G, Ghandiparsi S, Kaya A, Mamtaz H H, Mayet A S, Wang Y, Zhang X, Yamada T 2017 Nat. Photon. 11 301 Google Scholar
[25]	Novotny L, Hecht B 2012 Principles of Nano-Optics (Cambridge: Cambridge University Press)
[26]	Ritchie R 1957 Phys. Rev. 106 874 Google Scholar
[27]	Li Q, Li Z, Li N, Chen X, Chen P, Shen X, Lu W 2014 Sci. Rep. 4 6332
[28]	Sommerfeld A 1899 Annalen der Physik 303 233
[29]	Wood R W 1902 Philos. Mag. 4 396 Google Scholar
[30]	Kretschmann E, Raether H 1968 Zeitschrift für Naturforschung A 23 2135
[31]	Bouchon P, Pardo F, Portier B, Ferlazzo L, Ghenuche P, Dagher G, Dupuis C, Bardou N, Haïdar R, Pelouard J L 2011 Appl. Phys. Lett. 98 191109 Google Scholar
[32]	Chang C C, Sharma Y D, Kim Y S, Bur J A, Shenoi R V, Krishna S, Huang D, Lin S Y 2010 Nano Lett. 10 1704 Google Scholar
[33]	Thio T, Pellerin K M, Linke R A, Lezec H J, Ebbesen T W 2001 Opt. Lett. 26 1972 Google Scholar
[34]	Ren F F, Ang K W, Ye J, Yu M, Lo G Q, Kwong D L 2011 Nano Lett. 11 1289 Google Scholar
[35]	Echtermeyer T, Milana S, Sassi U, Eiden A, Wu M, Lidorikis E, Ferrari A C 2016 Nano Lett. 16 8
[36]	Laux E, Genet C, Skauli T, Ebbesen T W 2008 Nat. Photon. 2 161 Google Scholar
[37]	Mie G 1908 Annalen der Physik 330 377
[38]	Jackson J D 2012 Classical Electrodynamics (New York: John Wiley & Sons)
[39]	Novotny L, van Hulst N 2011 Nature Photon. 5 83 Google Scholar
[40]	Miao J, Hu W, Jing Y, Luo W, Liao L, Pan A, Wu S, Cheng J, Chen X, Lu W 2015 Small 11 2392 Google Scholar
[41]	Zhu Z, Zou Y, Hu W, Li Y, Gu Y, Cao B, Guo N, Wang L, Song J, Zhang S 2016 Adv. Funct. Mater. 26 1793 Google Scholar
[42]	Ni Z, Ma L, Du S, Xu Y, Yuan M, Fang H, Wang Z, Xu M, Li D, Yang J 2017 ACS Nano 11 9854 Google Scholar
[43]	Knight M W, Sobhani H, Nordlander P, Halas N J 2011 Science 332 702 Google Scholar
[44]	Chalabi H, Schoen D, Brongersma M L 2014 Nano Lett. 14 1374 Google Scholar
[45]	Fang Z, Liu Z, Wang Y, Ajayan P M, Nordlander P, Halas N J 2012 Nano Lett. 12 3808 Google Scholar
[46]	Brongersma M L, Halas N J, Nordlander P 2015 Nature Nanotechnol. 10 25 Google Scholar
[47]	Christopher P, Moskovits M 2017 Ann. Rev. Phys. Chem. 68 379 Google Scholar
[48]	West L, Eglash S 1985 Appl. Phys. Lett. 46 1156 Google Scholar
[49]	Levine B, Malik R, Walker J, Choi K, Bethea C, Kleinman D, Vandenberg J 1987 Appl. Phys. Lett. 50 273 Google Scholar
[50]	Smith D, Mailhiot C 1987 J. Appl. Phys. 62 2545 Google Scholar
[51]	Gendron L, Carras M, Huynh A, Ortiz V, Koeniguer C, Berger V 2004 Appl. Phys. Lett. 85 2824 Google Scholar
[52]	Giorgetta F R, Baumann E, Hofstetter D, Manz C, Yang Q, Köhler K, Graf M 2007 Appl. Phys. Lett. 91 111115 Google Scholar
[53]	Giorgetta F R, Baumann E, Théron R, Pellaton M, Hofstetter D, Fischer M, Faist J 2008 Appl. Phys. Lett. 92 121101 Google Scholar
[54]	Giorgetta F R, Baumann E, Graf M, Yang Q, Manz C, Köhler K, Beere H E, Ritchie D A, Linfield E, Davies A G 2009 IEEE J. Quantum Electron. 45 1039 Google Scholar
[55]	Vardi A, Bahir G, Guillot F, Bougerol C, Monroy E, Schacham S, Tchernycheva M, Julien F 2008 Appl. Phys. Lett. 92 011112 Google Scholar
[56]	Li L, Xiong D, Wen J, Li N, Zhu Z 2016 Infrared Phys. Technol. 79 45 Google Scholar
[57]	Hofstetter D, Giorgetta F R, Baumann E, Yang Q, Manz C, Köhler K 2008 Appl. Phys. Lett. 93 221106 Google Scholar
[58]	Li L, Xiong D, Tang Z, Wen J, Li N, Chen P, Zhu Z 2017 J. Appl. Phys. 121 083102 Google Scholar
[59]	李梁 2017 博士学位论文(上海: 华东师范大学) Li L 2017 Ph. D. Dissertation (Shanghai: East China Normal University) (in Chinese)
[60]	Dougakiuchi T, Fujita K, Hirohata T, Ito A, Hitaka M, Edamura T 2016 Appl. Phys. Lett. 109 261107 Google Scholar
[61]	Li J V, Yang R Q, Hill C J, Chuang S L 2005 Appl. Phys. Lett. 86 101102 Google Scholar
[62]	Yang R Q, Tian Z, Cai Z, Klem J, Johnson M B, Liu H 2010 J. Appl. Phys. 107 054514 Google Scholar
[63]	Yang R Q, Tian Z, Klem J, Mishima T D, Santos M B, Johnson M B 2010 Appl. Phys. Lett. 96 063504 Google Scholar
[64]	Zhou Y, Chen J, Xu Z, He L 2016 Semicond. Sci. Technol. 31 085005 Google Scholar
[65]	Fang H H, Hu W D 2017 Adv. Sci. 4 1700323 Google Scholar
[66]	Kufer D, Konstantatos G 2016 ACS Photon. 3 2197 Google Scholar
[67]	Kufer D, Lasanta T, Bernechea M, Koppens F H L, Konstantatos G 2016 ACS Photon. 3 1324 Google Scholar
[68]	Sun Z, Liu Z, Li J, Tai G A, Lau S P, Yan F 2012 Adv. Mater. 24 5878 Google Scholar
[69]	Hu C, Dong D, Yang X, Qiao K, Yang D, Deng H, Yuan S, Khan J, Lan Y, Song H, Tang J 2017 Adv. Funct. Mater. 27 1603605 Google Scholar
[70]	Kufer D, Nikitskiy I, Lasanta T, Navickaite G, Koppens F H L, Konstantatos G 2015 Adv. Mater. 27 176 Google Scholar
[71]	Furchi M M, Polyushkin D K, Pospischil A, Mueller T 2014 Nano Lett. 14 6165 Google Scholar
[72]	Island J O, Blanter S I, Buscema M, van der Zant H S, Castellanos-Gomez A 2015 Nano Lett. 15 7853 Google Scholar
[73]	Guo Q, Pospischil A, Bhuiyan M, Jiang H, Tian H, Farmer D, Deng B, Li C, Han S J, Wang H, Xia Q, Ma T P, Mueller T, Xia F 2016 Nano Lett. 16 4648 Google Scholar
[74]	Konstantatos G, Badioli M, Gaudreau L, Osmond J, Bernechea M, Garcia de Arquer F P, Gatti F, Koppens F H 2012 Nature Nanotechnol. 7 363 Google Scholar
[75]	Goossens S, Navickaite G, Monasterio C, Gupta S, Piqueras J J, Pérez R, Burwell G, Nikitskiy I, Lasanta T, Galán T, Puma E, Centeno A, Pesquera A, Zurutuza A, Konstantatos G, Koppens F 2017 Nat. Photon. 11 366 Google Scholar
[76]	Guo N, Hu W, Liao L, Yip S, Ho J C, Miao J, Zhang Z, Zou J, Jiang T, Wu S, Chen X, Lu W 2014 Adv. Mater. 26 8203 Google Scholar
[77]	Fang H, Hu W, Wang P, Guo N, Luo W, Zheng D, Gong F, Luo M, Tian H, Zhang X, Luo C, Wu X, Chen P, Liao L, Pan A, Chen X, Lu W 2016 Nano Lett. 16 6416 Google Scholar
[78]	Adinolfi V, Sargent E H 2017 Nature 542 324 Google Scholar
[79]	Guo X, Wang W, Nan H, Yu Y, Jiang J, Zhao W, Li J, Zafar Z, Xiang N, Ni Z, Hu W, You Y, Ni Z 2016 Optica 3 1066 Google Scholar
[80]	Fukushima S, Shimatani M, Okuda S, Ogawa S, Kanai Y, Ono T, Matsumoto K 2018 Appl. Phys. Lett. 113 061102 Google Scholar
[81]	Legrand J F 1989 Ferroelectrics 91 303
[82]	Wang X, Wang P, Wang J, Hu W, Zhou X, Guo N, Huang H, Sun S, Shen H, Lin T 2015 Adv. Mater. 27 6575 Google Scholar
[83]	Wu G, Wang X, Wang P, Huang H, Chen Y, Sun S, Shen H, Lin T, Wang J, Zhang S 2016 Nanotechnology 27 364002 Google Scholar
[84]	Huang H, Wang X, Wang P, Wu G, Chen Y, Meng C, Liao L, Wang J, Hu W, Shen H 2016 RSC Adv. 6 87416 Google Scholar
[85]	Zheng D, Wang J, Hu W, Liao L, Fang H, Guo N, Wang P, Gong F, Wang X, Fan Z 2016 Nano Lett. 16 2548 Google Scholar
[86]	Zheng D, Fang H, Wang P, Luo W, Gong F, Ho J C, Chen X, Lu W, Liao L, Wang J 2016 Adv. Funct. Mater. 26 7690 Google Scholar
[87]	Sassi U, Parret R, Nanot S, Bruna M, Borini S, de Fazio D, Zhao Z, Lidorikis E, Koppens F, Ferrari A C 2017 Nat. Commun. 8 14311 Google Scholar
[88]	Hsieh C Y, Chen Y T, Tan W J, Chen Y F, Shih W Y, Shih W H 2012 Appl. Phys. Lett. 100 113507 Google Scholar
[89]	Wang L 2013 Science 342 614 Google Scholar
[90]	Geim A K, Grigorieva I V 2013 Nature 499 419 Google Scholar
[91]	Roy K, Padmanabhan M, Goswami S, Sai T P, Ramalingam G, Raghavan S, Ghosh A 2013 Nat. Nanotechnol. 8 826 Google Scholar
[92]	Zhang W, Chuu C P, Huang J K, Chen C H, Tsai M L, Chang Y H, Liang C T, Chen Y Z, Chueh Y L, He J H 2014 Sci. Rep. 4 3826
[93]	Liu C H, Chang Y C, Norris T B, Zhong Z 2014 Nat. Nanotechnol. 9 273 Google Scholar
[94]	Chen X, Lu X, Deng B, Sinai O, Shao Y, Li C, Yuan S, Tran V, Watanabe K, Taniguchi T 2017 Nat. Commun. 8 1672 Google Scholar
[95]	Han J, Wang J, Yang M, Kong X, Chen X, Huang Z, Guo H, Gou J, Tao S, Liu Z 2018 Adv. Mater. 30 1804020 Google Scholar
[96]	Yang M, Wang J, Han J, Ling J, Ji C, Kong X, Liu X, Huang Z, Gou J, Liu Z 2018 ACS Photon. 5 3438 Google Scholar
[97]	Yang M, Wang J, Zhao Y, He L, Ji C, Liu X, Zhou H, Wu Z, Wang X, Jiang Y 2019 ACS Nano 13 755
[98]	Long M S, Liu E F, Wang P, Gao A Y, Xia H, Luo W, Wang B G, Zeng J W, Fu Y J, Xu K, Zhou W, Lv Y Y, Yao S H, Lu M H, Chen Y F, Ni Z H, You Y M, Zhang X A, Qin S Q, Shi Y, Hu W D, Xing D Y, Miao F 2016 Nano Lett. 16 2254 Google Scholar
[99]	Bullock J, Amani M, Cho J, Chen Y Z, Ahn G H, Adinolfi V, Shrestha V R, Gao Y, Crozier K B, Chueh Y L 2018 Nat. Photon. 12 601 Google Scholar
[100]	Gibson S J, van Kasteren B, Tekcan B, Cui Y, van Dam D, Haverkort J E, Bakkers E P, Reimer M E 2019 Nature Nanotechnol. 14 473 Google Scholar
[101]	Jiang X, Itzler M A, Ben-Michael R, Slomkowski K 2007 IEEE J. Selected Topics in Quantum Electronics 13 895 Google Scholar
[102]	Lacaita A, Francese P, Zappa F, Cova S 1994 Appl. Opt. 33 6902 Google Scholar
[103]	Kang Y, Mages P, Clawson A, Yu P, Bitter M, Pan Z, Pauchard A, Hummel S, Lo Y 2002 IEEE Photon.Technol. Lett. 14 1593 Google Scholar
[104]	胡伟达, 李庆, 温洁, 王文娟, 陈效双, 陆卫 2018 红外技术 40 201 Hu W D, Li Q, Wen J, Wang W J, Chen X S, Lu W 2018 Infrared Technol. 40 201
[105]	Singh A, Srivastav V, Pal R 2011 Opt. Laser Technol. 43 1358 Google Scholar
[106]	Webb P P, McIntyre R J, Conradi J 1974 RCA Rev. 35 234
[107]	McIntyre R 1966 IEEE Trans. Electron Dev. 13 164
[108]	Wen J, Wang W, Li N, Li Z, Lu W 2017 Appl. Phys. Lett. 110 231105 Google Scholar
[109]	Wen J, Wang W, Li N, Li Z, Lu W 2016 Opt. Quantum Electron. 48 150 Google Scholar
[110]	Wen J, Wang W, Chen X, Li N, Chen X, Lu W 2018 J. Appl. Phys. 123 161530 Google Scholar
[111]	Gao A, Lai J, Wang Y, Zhu Z, Zeng J, Yu G, Wang N, Chen W, Cao T, Hu W, Sun D, Chen X, Miao F, Shi Y, Wang X 2019 Nature Nanotechnol. 14 217 Google Scholar
[112]	Leveque G, Nasser M, Bertho D, Orsal B, Alabedra R 1993 Semicond. Sci. Technol. 8 1317 Google Scholar
[113]	Beck J D, Wan C F, Kinch M A, Robinson J E 2001 Proc. SPIE 4454 188 Google Scholar
[114]	Kinch M, Beck J, Wan C F, Ma F, Campbell J 2004 J. Electron. Mater. 33 630 Google Scholar
[115]	Beck J, Woodall M, Scritchfield R, Ohlson M, Wood L, Mitra P, Robinson J 2007 Proc. SPIE 6542 654217 Google Scholar
[116]	Beck J, Wan C, Kinch M, Robinson J, Mitra P, Scritchfield R, Ma F, Campbell J 2006 J. Electron. Mater. 35 1166 Google Scholar
[117]	de Borniol E, Guellec F, Rothman J, Perez A, Zanatta J P, Tchagaspanian M, Castelein P, Destéfanis G, Peyrard J C, Pistone F 2010 Proc. SPIE 7660 76603D Google Scholar
[118]	de Borniol E D, Rothman J, Guellec F, Vojetta G, Destéfanis G, Pacaud O 2012 Opt. Eng. 51 061305 Google Scholar
[119]	Kerlain A, Bonnouvrier G, Rubaldo L, Decaens G, Reibel Y, Abraham P, Rothman J, Mollard L, de Borniol E 2012 J. Electron. Mater. 41 2943 Google Scholar
[120]	Qiu W C, Hu W D, Chen L, Lin C, Cheng X A, Chen X S, Lu W 2015 IEEE Trans. Electron Dev. 62 1926 Google Scholar
[121]	Li Q, He J L, Hu W D, Chen L, Chen X S, Lu W 2018 IEEE Trans. Electron Dev. 65 572 Google Scholar
[122]	Lao Y F, Perera A U, Li L, Khanna S, Linfield E, Liu H 2014 Nat. Photon. 8 412 Google Scholar
[123]	Perera A U, Chauhan D, Lao Y F, Li L, Khanna S P, Linfield E H 2016 Proc. SPIE 9844 98440X Google Scholar
[124]	Esaev D, Rinzan M, Matsik S, Perera A 2004 J. Appl. Phys. 96 4588 Google Scholar
[125]	Chauhan D, Perera A, Li L, Chen L, Linfield E 2018 Infrared Phys. Technol. 95 148 Google Scholar
[126]	Maimon S, Wicks G 2006 Appl. Phys. Lett. 89 151109
[127]	Klipstein P 2008 Proc. SPIE 6940 69402U Google Scholar
[128]	Evirgen A, Abautret J, Perez J, Aït-Kaci H, Christol P, Fleury J, Sik H, Nedelcu A, Cluzel R, Cordat A 2014 Proc. SPIE 8993 899313 Google Scholar
[129]	Perez J P, Evirgen A, Abautret J, Christol P, Cordat A, Nedelcu A 2015 Proc. SPIE 9370 93700N Google Scholar
[130]	Rodriguez J B, Plis E, Bishop G, Sharma Y, Kim H, Dawson L, Krishna S 2007 Appl. Phys. Lett. 91 043514 Google Scholar
[131]	Haddadi A, Chevallier R, Dehzangi A, Razeghi M 2017 Appl. Phys. Lett. 110 101104 Google Scholar
[132]	Hood A, Razeghi M, Aifer E H, Brown G J 2005 Appl. Phys. Lett. 87 151113 Google Scholar
[133]	Haddadi A, Chen G, Chevallier R, Hoang A, Razeghi M 2014 Appl. Phys. Lett. 105 121104 Google Scholar
[134]	Kim H, Plis E, Rodriguez J, Bishop G, Sharma Y, Dawson L, Krishna S, Bundas J, Cook R, Burrows D 2008 Appl. Phys. Lett. 92 183502 Google Scholar
[135]	Plis E, Myers S, Khoshakhlagh A, Kim H S, Sharma Y, Gautam N, Dawson R, Krishna S 2009 Infrared Phys. Technol. 52 335 Google Scholar
[136]	Plis E, Rodriguez J B, Balakrishnan G, Sharma Y, Kim H, Rotter T, Krishna S 2010 Semicond. Sci. Technol. 25 085010 Google Scholar
[137]	Plis E, Myers S, Kutty M, Mailfert J, Smith E, Johnson S, Krishna S 2010 Appl. Phys. Lett. 97 123503 Google Scholar
[138]	Khoshakhlagh A, Myers S, Plis E, Kutty M, Klein B, Gautam N, Kim H, Smith E, Rhiger D, Johnson S 2010 Proc. SPIE 7660 76602Z Google Scholar
[139]	Plis E, Gautam N, Myers S, Krishna S, Smith E, Johnson S, Krishna S 2011 Proc. SPIE 8012 80120X Google Scholar
[140]	Klipstein P, Klin O, Grossman S, Snapi N, Lukomsky I, Aronov D, Yassen M, Glozman A, Fishman T, Berkowicz E 2011 Opt. Eng. 50 061002 Google Scholar
[141]	Klipstein P, Avnon E, Benny Y, Fraenkel A, Glozman A, Hojman E, Ilan E, Kahanov E, Klin O, Langof L 2015 Proc. SPIE 9451 94510K Google Scholar
[142]	Klipstein P, Avnon E, Benny Y, Berkowicz E, Cohen Y, Dobromislin R, Fraenkel R, Gershon G, Glozman A, Hojman E 2017 J. Electron. Mater. 46 5386 Google Scholar
[143]	Klipstein P, Avnon E, Benny Y, Cohen Y, Fraenkel R, Gliksman S, Glozman A, Hojman E, Klin O, Krasovitsky L 2018 J. Electron. Mater. 47 5725 Google Scholar
[144]	Itsuno A, Phillips J, Velicu S 2011 J. Electron. Mater. 40 1624 Google Scholar
[145]	Itsuno A M, Phillips J D, Velicu S 2012 J. Electron. Mater. 41 2886 Google Scholar
[146]	Rogalski A 2002 Infrared Phys. Technol. 43 187 Google Scholar
[147]	李庆, 白杰, 吕衍秋, 胡伟达, 陈效双, 陆卫 2017 红外与毫米波学报 36 385 Google Scholar Li Q, Bai J, Lü Y Q, Hu W D, Chen X S, Lu W 2017 J. Infrared Millim.Waves 36 385 Google Scholar
[148]	Blazejewski E, Arias J, Williams G, McLevige W, Zandian M, Pasko J 1992 J. Vacuum Sci. Technol. B 10 1626 Google Scholar
[149]	Arias J, Zandian M, Williams G, Blazejewski E, DeWames R, Pasko J 1991 J. Appl. Phys. 70 4620 Google Scholar
[150]	Rogalski A 2010 J. Mod. Opt. 57 1716 Google Scholar
[151]	Hu W, Ye Z, Liao L, Chen H, Chen L, Ding R, He L, Chen X, Lu W 2014 Opt. Lett. 39 5184 Google Scholar
[152]	Liu H, Song C, Shen A, Gao M, Wasilewski Z, Buchanan M 2000 Appl. Phys. Lett. 77 2437 Google Scholar
[153]	Eker S, Kaldirim M, Arslan Y, Besikci C 2008 IEEE Electron Dev. Lett. 29 1121 Google Scholar
[154]	Haddadi A, Chevallier R, Chen G, Hoang A, Razeghi M 2015 Appl. Phys. Lett. 106 011104 Google Scholar
[155]	Khoshakhlagh A, Rodriguez J, Plis E, Bishop G, Sharma Y, Kim H, Dawson L, Krishna S 2007 Appl. Phys. Lett. 91 263504 Google Scholar
[156]	Hoang A, Chen G, Haddadi A, Razeghi M 2013 Appl. Phys. Lett. 102 011108 Google Scholar
[157]	Tang X, Ackerman M M, Chen M, Guyot-Sionnest P 2019 Nat. Photon. 13 277 Google Scholar

Cited By

图 1 红外探测器发展历史

Figure 1. History of infrared photodetectors.

DownLoad: Full-Size Img PowerPoint

图 2 美国Raytheon公司制备的不同陷光结构的中波HgCdTe红外探测^[22]

Figure 2. Raytheon company investigates the use of photon trapping structures with varying fill factor in HgCdTe detectors for use in mid-wavelength infrared (MWIR) detectors^[22].

DownLoad: Full-Size Img PowerPoint

图 3 HgCdTe陷光结构^[23]　(a)像元间距为8 μm的HgCdTe红外探测器阵列的单个像元示意图; (b) 3 × 3阵列像元阵列三维示意图

Figure 3. Photo-trapping (PT) structure^[23]: (a) Schematic representing a single pixel of an array with 8 μm pixels; (b) three dimensional view of 3 × 3 pixel array.

DownLoad: Full-Size Img PowerPoint

图 4 单个像元间距为6 μm的陷光结构与非陷光结构阵列数值模拟的(a)反射谱和(b)量子效率^[23]

Figure 4. Calculated (a) reflectance spectra and (b) quantum efficiency for a single 6 μm pixel of the PT and non-PT arrays^[23].

DownLoad: Full-Size Img PowerPoint

图 5 (a) Si光电二极管的示意图; (b) Si晶元衬底上的n-i-p光电二极管, 锥形小孔贯穿n, i, p层^[24]

Figure 5. (a) Schematic of the Si photodiode; (b) the n-i-p photodiode structure on an silicon-on-insulator (SOI) wafer, the integrated tapered holes that span the n, i and p layers^[24].

DownLoad: Full-Size Img PowerPoint

图 6 FDTD数值模拟在垂直光照射时小孔周围横向电场的模式(顶部是XY截面, 底部为YZ截面; 时间从左到右增加, T = 1.4, 6.2, 11, 16, 21 fs)^[24]　(a)圆柱形小孔; (b)漏斗形小孔

Figure 6. FDTD numerical simulations show the formation of lateral electric field modes around holes when illuminated by a normal incident beam of light^[24]: (a) Cylindrical holes; (b) funnel-shaped holes. Top, X-Y plane; bottom, Y-Z plane. Time increased from left to right: T = 1.4, 6.2, 11, 16, 21 fs.

DownLoad: Full-Size Img PowerPoint

图 7 表面等离激元波示意图(金属表面的电子对入射光的响应产生了表面几十纳米内的电子密度的轻微扰动, 构成了金属中表面电子的集体激发模式)

Figure 7. Representation of surface plasmon polaritons: Under the excition of injection light, the density of electrons in the surface of metal experience a little change, which correspond to the collective excition modes of surface electrons.

DownLoad: Full-Size Img PowerPoint

图 8 (a)金属光栅制备过程; (b) GaAs的扫描电子显微镜(scanning electron microscope, SEM)照片; (c)坡印亭矢量的流线图, 可见在共振波长10.05 μm处, 光场被几乎全被限制到了狭缝中^[31]

Figure 8. (a) Fabrication steps of the metal grating; (b) SEM photograph of GaAs; (c) streamline diagram of Poynting vector. At the resonance wavelength of 10.05 μm, the light field is almost completely confined into the slit^[31].

DownLoad: Full-Size Img PowerPoint

图 9 (a)量子点红外探测器上覆盖金属孔洞阵列SPP结构的器件示意图^[32]; (b)金属孔洞阵列SPP结构的SEM照片^[32]; (c)牛眼探测器的SEM照片^[33]; (d)劈裂牛眼结构^[34]; (e)石墨烯表面等离激元器件结构示意图^[35]; (f)偏振多波长SPP结构^[36]

Figure 9. (a) Schematic diagram of the SPP structure with the metal hole array on the quantum dot infrared detector^[32]; (b) SEM photograph of the metal hole array SPP structure^[32]; (c) SEM photograph of the bull's eye detector^[33]; (d) the bull's eye structure with slit^[34]; copyright 2011 American Chemical Society (e) schematic diagram of graphene-surface plasmon photodetector^[35]; (f) polarization dependent multi-wavelength SPP structure^[36].

DownLoad: Full-Size Img PowerPoint

图 10 (a) TiS₂纳米片的吸收谱; (b) LSP与SPP共同增强量子阱红外探测器; (c), (d)纳米片的LSP共振与非共振模式下的电场分布图^[41]; (e)硅量子点辅助的超宽谱石墨烯探测器^[42]; (f)—(h)金阵列增强型MoS₂光电二极管^[40]

Figure 10. (a) Absorption spectra of TiS₂ nanosheets; (b) quantum well infrared detectors enhanced by LSP and SPP together; (c),(d) electric field distribution of nanosheets of LSP resonance and non-resonant mode^[41]; (e) ultra-wide spectrum graphene detector auxiliary by silicon quantum dots^[42]; (f)−(h) Au arrays enhanced MoS₂ phototransistors^[40].

DownLoad: Full-Size Img PowerPoint

图 11 等离激元热电子能带图(肖特基势垒为ϕ_B; 电子-空穴对受激光激发; 满足动量守恒要求对应的过程为声子辅助或杂质辅助的)^[43]

Figure 11. The band diagram of plasmon hot electrons. Schottky barrier is ϕ_B. The illuminating light photoexcited electrons in metal, generating electron-hole pairs. Taking conservation of momentum in to consideration, this process may be aided by phonons or impurities^[43].

DownLoad: Full-Size Img PowerPoint

图 12 (a)基于LSP的光电探测器结构示意图; (b)基于LSP的光电探测器SEM照片^[43]; (c)基于SPP的光电探测器结构示意图; (d)基于SPP热电子的光电探测器SEM照片; (e) SPP等离激元热电子器件的光电流Mapping图^[44]

Figure 12. (a) Schematic diagram of LSP-based photodetector; (b) SEM photo of photodetector based on LSP^[43]; (c) schematic diagram of photodetector based on SPP; (d) SEM photograph of photodetector based on SPP thermoelectron; (e) photocurrent mapping of SPP plasmon thermal electronic devices^[44].

DownLoad: Full-Size Img PowerPoint

图 13 量子级联探测器能带结构示意图

Figure 13. Band diagram of quantum cascade detectors.

DownLoad: Full-Size Img PowerPoint

图 14 表面等离激元微腔结构耦合量子级联探测器结构示意图^[56,58]

Figure 14. Diagram of plasmonic micro-cavity coupled QCDs^[56,58].

DownLoad: Full-Size Img PowerPoint

图 15 宽光谱量子级联探测器设计　(a)双阱吸收; (b)微带吸收; (c)低势垒

Figure 15. Designs of broadband spectrum QCDs: (a) Double quantum wells absorption; (b) mini-band absorption; (c) low barrier design.

DownLoad: Full-Size Img PowerPoint

图 16 量子阱耦合型In_0.53Ga_0.47As/In_0.52Al_0.48As量子级联探测器^[60]　(a)能带结构; (b)响应率; (c)探测率

Figure 16. Quantum well coupled In_0.53Ga_0.47As/In_0.52Al_0.48As QCDs^[60]: (a) Band diagram; (b) responsivity; (c) detectivity.

DownLoad: Full-Size Img PowerPoint

图 17 带间级联探测器能带结构示意图

Figure 17. Band diagram of interband cascade detectors.

DownLoad: Full-Size Img PowerPoint

图 18 (a)带间级联探测器弛豫区的优化设计; (b)探测率随温度的变化^[63]

Figure 18. (a) Optimization design of relaxation region in ICDs; (b) temperature dependent of the detectivity ^[63].

DownLoad: Full-Size Img PowerPoint

图 19 响应率随温度的变化　(a)单周期结构; (b)双周器结构^[64]

Figure 19. Responsivity varies with temperature for one stage structure (a) and two stage structure (b) interband cascade detectors ^[64]

DownLoad: Full-Size Img PowerPoint

图 20 常温工作时典型探测器峰值探测率对比

Figure 20. Comparison of peak detectivity among typical photodetector at room temperature.

DownLoad: Full-Size Img PowerPoint

图 21 (a)石墨烯/量子点复合结构增益原理图^[74]; (b) CMOS集成的石墨烯/量子点焦平面结构示意图^[75]; (c)室温中红外高增益黑磷探测器结构示意图^[73]; (d)室温高增益高响应InAs纳米线^[76]; (e)室温高性能中红外InAs纳米线^[77]

Figure 21. (a) Energy band diagram for interpretation of optical gain in graphene/quantum dots heterostructure^[74]; (b) schematic diagram of CMOS integrated graphene/quantum dots focal array plane^[75]; (c) schematic diagram of mid-infrared pure black phosphorous photodetector^[73]; (d) high gain and high responsivity InAs nanowire^[76]; (e) high performance mid-wavelength InAs nanowire^[77].

DownLoad: Full-Size Img PowerPoint

图 22 (a)光伏场效应晶体管示意图^[78]; (b)不同器件的增益带宽积^[65]; (c) InSb作光敏介质调控石墨烯器件结构示意图; (d)器件不同工作温度下的响应^[78,80]

Figure 22. (a) Schematic diagram of photovoltage field-effect transistors^[78]; (b) gain-bandwidth product for different types of photodetectors^[65]; (c) schematic diagram of mid-infrared graphene detector through interfacial gating of InSb; (d) the photoresponse of device in (c) at various temperatures^[78,80].

DownLoad: Full-Size Img PowerPoint

图 23 (a) 300 nm P(VDF-TrFE)薄膜的电滞回线; (b) P(VDF-TrFE)处于三种极化状态下, P(VDF-TrFE)-MoS₂晶体管的I_ds-V_ds曲线, fresh指未极化状态, P up, P down分别代表极化向上和极化向下状态; (c), (d) P(VDF-TrFE)极化向上和极化向下时器件示意图以及能带图^[82]

Figure 23. (a) The ferroelectric hysteresis loop 300 nm P(VDF-TrFE) film capacitor; (b) the I_ds-V_dscharacteristics (at ZERO gate voltage) with three states of ferroelectric layer, and the three states are fresh state (ferroelectric layer without polarization), polarization up (polarized by a pulse V_g of –40 V), and polarization down (polarized by a pulse V_g of –40 V) states, respectively; (c), (d) the cross-section structures of the device and equilibrium energy band diagrams of three different ferroelectric polarization states^[82].

DownLoad: Full-Size Img PowerPoint

图 24 (a)石墨烯-PZT场效应晶体管结构示意图; (b)石墨烯- LiNbO₃热释电探测器器件结构图; (c)器件的工作原理图^[87]

Figure 24. (a) The schematic diagram of the graphene-PZT field effect transistor; (b) schematic of a graphene pyroelectric bolometer; (c) working mechanism diagram for the device in panel (b) ^[87].

DownLoad: Full-Size Img PowerPoint

图 25 (a) Graphene/Ta₂O₅/graphene隧道结红外探测器结构示意图; (b)多种功率下红外响应曲线, 入射光波长3.2 μm; (c) h-BN/b-P/h-BN垂直异质结的红外探测器; (d) h-BN/b-P/h-BN垂直异质结器件7.7 μm红外光电响应^[93,94]

Figure 25. (a) Structure diagram of graphene/Ta₂O₅/graphene tunneling diode; (b) infrared responsivity curve of variable incident power with 3.2 μm wavelength; (c) h-BN/b-P/h-BN vertical heterojunction photodetectors; (d) 7.7 μm infrared responsivity of h-BN/b-P/h-BN vertical heterojunction photodetectors^[93,94].

DownLoad: Full-Size Img PowerPoint

图 26 (a) p-g-n异质结光电探测器的结构示意图; (b) p-g-n异质结光电探测器的光电响应; (c)黑砷磷b-As_0.83P_0.17样品的光学吸收谱, 插图为黑砷磷合金b-AsP/MoS₂异质结器件结构示意图; (d) b-AsP/MoS₂异质结光电探测器在中波红外的光电响应^[98]

Figure 26. (a) Structure diagram of p-g-n heterojunction photodetectors; (b) responsivity of p-g-n heterojunction photodetectors; (c) absorption spectrum of b-As_0.83P_0.17; (d) mid-infrared response of b-AsP/MoS₂ heterojunction photodetectors^[98].

DownLoad: Full-Size Img PowerPoint

图 27 BP与MoS₂异质结红外探测器^[99] (a) 1000 K黑体源辐射下光电流与暗电流; (b)探测率的对比; (c)响应时间

Figure 27. BP/MoS2 infrared photodetector^[99]: (a) Photocurrent with 1000 K blackbody source and the dark current; (b) detectivity comparison of typical infrared photodetectors; (c) response time

DownLoad: Full-Size Img PowerPoint

图 28 传统光伏型红外探测器　(a)和雪崩光电探测器(b)工作时的能带结构图

Figure 28. The tunneling effect (a) and avalanche effect (b) in p-n junction under large reverse bias.

DownLoad: Full-Size Img PowerPoint

图 29 InGaAs/InP APD的MIM结构示意图^[108—110]　(a)偏振选择型结构示意图; (b)无偏振选择型结构示意图; (c), (d)分别为SEM图

Figure 29. MIM structure diagram used for InGaAs/InP avalanche photodiode^[108-110]: (a) Polarization selective structure; (b) non-polarization selective structure; (c) and (d) are the SEM image.

DownLoad: Full-Size Img PowerPoint

图 30 (a) BP/InSe雪崩光电二极管的电流特性; (b)器件的噪声及增益水平; (c)传统的雪崩光电探测器载流子碰撞过程; (d)弹道雪崩效应示意图

Figure 30. (a) I-V characteristics of BP/InSe APD; (b) noise and gain of BP/InSe APD; (c) traditional ionizing collision process; (d) ballistic avalanche mechanism of BP/InSe APD^[111].

DownLoad: Full-Size Img PowerPoint

图 31 离化过程能带结构示意图　(a)空穴注入型; (b)电子注入型

Figure 31. The diagram of ionization process: (a) Hole injection; (b) electron injection.

DownLoad: Full-Size Img PowerPoint

图 32 DRS制备的128 × 128 HgCdTe APD焦平面器件照片和器件平均增益^[115]

Figure 32. The photograph of 128 × 128 HgCdTe APD FPA fabricated in DRS and the average gain^[115].

DownLoad: Full-Size Img PowerPoint

图 33 Sofradir公司利用HgCdTe APD 3D实时成像截图^[118]

Figure 33. The 3D real time imaging print screen of HgCdTe APD fabricated in Sofradir^[118].

DownLoad: Full-Size Img PowerPoint

图 34 平面结(a)和台面结(b)碲镉汞雪崩光电探测器在不同工艺下的暗电流特性曲线^[121]

Figure 34. The I-V characteristic of planar (a) and mesa (b) HgCdTe APD with variable fabrication process^[121].

DownLoad: Full-Size Img PowerPoint

图 35 热载流子红外探测器器件结构和能带示意图^[122]

Figure 35. Structure and band diagram of hot carriers infrared photodetectors^[122].

DownLoad: Full-Size Img PowerPoint

图 36 热载流子红外探测器的光谱响应^[122]

Figure 36. Photo response of hot carriers infrared photodetectors^[122].

DownLoad: Full-Size Img PowerPoint

图 37 热载流子红外探测器光谱权重图^[122]

Figure 37. Spectral weight diagram of hot carriers infrared photodetectors^[122].

DownLoad: Full-Size Img PowerPoint

图 38 不同波长泵浦光下器件光谱权重图^[122]

Figure 38. Spectral weight diagram with variable pump light^[122].

DownLoad: Full-Size Img PowerPoint

图 39 nBn型器件和能带结构示意图

Figure 39. Structure and band diagram of nBn devices.

DownLoad: Full-Size Img PowerPoint

图 40 普通PN结二极管器件与XBn器件的暗电流与温度相关性^[127]

Figure 40. Schematic Arrhenius plot of the dark current in a standard diode and XBn device^[127].

DownLoad: Full-Size Img PowerPoint

图 41 InSb nBn探测器(a)器件结构示意图和(b)能带结构示意图^[128,129]

Figure 41. Schematic diagram of (a) design of InSb nBn structure and (b) energy band of InSb nBn structure^[128,129].

DownLoad: Full-Size Img PowerPoint

图 42 nBn结构InSb探测器　(a) 77 K下暗电流特性; (b) 104—170 K暗电流特性; (c) 77 K下光谱响应; (d)不同温度和结构下的暗电流特性^[128,129]

Figure 42. For InSb nBn infrared photodetectors, the dark current characteristics at (a) 77 K and (b) 104−170 K, (c) the spectral response at 77 K, and (d) the dark current characteristics at different temperatures and structures^[128,129].

DownLoad: Full-Size Img PowerPoint

图 43 短波红外InAs/GaSb/AlSb/GaSb Ⅱ类超晶格nBn探测器　(a)结构示意图; (b)量子效率; (c)暗电流特性; (d)探测率^[131]

Figure 43. SWIR InAs/GaSb/AlSb/GaSb nBn detector based on Type-II superlattice: (a) Structure diafram; (b) quantum efficiency; (c) dark current characteristics; (d) detectivity at different temperature^[131].

DownLoad: Full-Size Img PowerPoint

图 44 以色列SCD公司制备Pelican-D系列长波探测器　(a)探测器组件; (b) 77 K下成像结果^[141—143]

Figure 44. (a) Photograph of long-wavelength infrared (LWIR) InAs/GaSb pBp device based on Type-II superlattice fabricated by Israel SCD company; (b) image at 77 K^[141—143].

DownLoad: Full-Size Img PowerPoint

图 45 碲镉汞nBvn, nBn及DLPH器件的(a)中波暗电流、(b)长波暗电流、(c)中波探测率和(d)长波探测率^[144]

Figure 45. The dark current of (a) MWIR and (b) LWIR HgCdTe nBvn, nBn and DLPH devices; (c) and (d) show the detectivity of MWIR and LWIR devices, respectively^[144].

DownLoad: Full-Size Img PowerPoint

图 46 128 × 128长波/中波双色碲镉汞红外焦平面探测器　(a)暗电流特性; (b)中波/长波光谱响应曲线; (c)中波长波成像效果

Figure 46. 128 × 128 long-wavelength/mid-wavelength two-color HgCdTe infrared focal plane: (a) Dark current characteristic; (b) spectral response; (c) two-color imaging.

DownLoad: Full-Size Img PowerPoint

图 47 (a) HgTe量子点双色红外探测器结构; (b)双色探测率随温度的变化; (c)冷水与热水的双色成像^[157]

Figure 47. (a) Structure of HgTe quantum dot dual-band infrared photodetector; (b) temperature dependent short-wavelength and mid-wavelength detectivity; (c) two-color imaging of cold and hot water^[157].

DownLoad: Full-Size Img PowerPoint

[1]	Herschel W 1800 Philos. Trans. Roy. Soc. London 90 284 Google Scholar
[2]	Rogalski A 2012 Opt. Electron. Rev. 20 279
[3]	Becquerel M 1839 Comptes Rendus Hebdomadaires des Séances de l'Académie des Sciences 9 561
[4]	Smith W 1873 Nature 7 303 Google Scholar
[5]	Case T W 1917 Phys. Rev. 9 305 Google Scholar
[6]	Lange B 1930 Phys. Zeitschr 31 139
[7]	Lange B 1931 Naturwissenschaften 19 525 Google Scholar
[8]	Lovell D 1969 Am. J. Phys. 37 467 Google Scholar
[9]	Avery D, Goodwin D, Lawson W, Moss T 1954 Proc. Phys. Soc.Section B 67 761 Google Scholar
[10]	Lawson W, Nielsen S, Putley E, Young A 1959 J.Phys. Chem. Solids 9 325 Google Scholar
[11]	汤定元 1991 激光与红外 21 5 Tang D Y 1991 Laser & Infrared 21 5
[12]	茅文英, 褚君浩, 李言谨, 王子孟, 方家熊 1994 红外与毫米波学报 13 352 Mao W Y, Chu J H, Li Y J, Wang Z M, Fang J X 1994 J. Infrared Millim.Waves 13 352
[13]	杨建荣, 何进 1994 红外与毫米波学报 13 191 Yang J R, He J 1994 J. Infrared Millim.Waves 13 191
[14]	Rogalski A, Antoszewski J, Faraone L 2009 J. Appl. Phys. 105 091101 Google Scholar
[15]	杨建荣 2012 碲镉汞材料物理与技术第一版 (北京: 国防工业出版社) 第3—7页 Yang J R 2012 Physics and Technology of HgCdTe Materials (1st Ed.) (Beijing: National Defense Industry Press) pp3−7 (in Chinese)
[16]	Esaki L, Tsu R 1970 IBM J. Res. Dev. 14 61 Google Scholar
[17]	Lin H, Cheung H Y, Xiu F, Wang F, Yip S, Han N, Hung T, Zhou J, Ho J C, Wong C Y 2013 J. Mater. Chem. A 1 9942 Google Scholar
[18]	Cansizoglu H, Bartolo-Perez C, Gao Y, Devine E P, Ghandiparsi S, Polat K G, Mamtaz H H, Yamada T, Elrefaie A F, Wang S Y 2018 Photon. Res. 6 734 Google Scholar
[19]	胡伟达, 梁健, 越方禹, 陈效双, 陆卫 2016 红外与毫米波学报 35 25 Google Scholar Hu W D, Liang J, Yue F Y, Chen X S, Lu W 2016 J. Infrared Millim. Waves 35 25 Google Scholar
[20]	Krishna S, Posani K T, Tripathi V, Annamalai S 2005 The 18th Annual Meeting of the IEEE Sydney, Australia October 22−28, 2005 p909
[21]	Hiralal P, Chien C, Lal N N, Abeygunasekara W, Kumar A, Butt H, Zhou H, Unalan H E, Baumberg J J, Amaratunga G A 2014 Nanoscale 6 14555 Google Scholar
[22]	Wehner J, Smith E, Venzor G, Smith K, Ramirez A, Kolasa B, Olsson K, Vilela M 2011 J. Electron. Mater. 40 1840 Google Scholar
[23]	Pinkie B, Schuster J, Bellotti E 2013 Opt. Lett. 38 2546 Google Scholar
[24]	Gao Y, Cansizoglu H, Polat K G, Ghandiparsi S, Kaya A, Mamtaz H H, Mayet A S, Wang Y, Zhang X, Yamada T 2017 Nat. Photon. 11 301 Google Scholar
[25]	Novotny L, Hecht B 2012 Principles of Nano-Optics (Cambridge: Cambridge University Press)
[26]	Ritchie R 1957 Phys. Rev. 106 874 Google Scholar
[27]	Li Q, Li Z, Li N, Chen X, Chen P, Shen X, Lu W 2014 Sci. Rep. 4 6332
[28]	Sommerfeld A 1899 Annalen der Physik 303 233
[29]	Wood R W 1902 Philos. Mag. 4 396 Google Scholar
[30]	Kretschmann E, Raether H 1968 Zeitschrift für Naturforschung A 23 2135
[31]	Bouchon P, Pardo F, Portier B, Ferlazzo L, Ghenuche P, Dagher G, Dupuis C, Bardou N, Haïdar R, Pelouard J L 2011 Appl. Phys. Lett. 98 191109 Google Scholar
[32]	Chang C C, Sharma Y D, Kim Y S, Bur J A, Shenoi R V, Krishna S, Huang D, Lin S Y 2010 Nano Lett. 10 1704 Google Scholar
[33]	Thio T, Pellerin K M, Linke R A, Lezec H J, Ebbesen T W 2001 Opt. Lett. 26 1972 Google Scholar
[34]	Ren F F, Ang K W, Ye J, Yu M, Lo G Q, Kwong D L 2011 Nano Lett. 11 1289 Google Scholar
[35]	Echtermeyer T, Milana S, Sassi U, Eiden A, Wu M, Lidorikis E, Ferrari A C 2016 Nano Lett. 16 8
[36]	Laux E, Genet C, Skauli T, Ebbesen T W 2008 Nat. Photon. 2 161 Google Scholar
[37]	Mie G 1908 Annalen der Physik 330 377
[38]	Jackson J D 2012 Classical Electrodynamics (New York: John Wiley & Sons)
[39]	Novotny L, van Hulst N 2011 Nature Photon. 5 83 Google Scholar
[40]	Miao J, Hu W, Jing Y, Luo W, Liao L, Pan A, Wu S, Cheng J, Chen X, Lu W 2015 Small 11 2392 Google Scholar
[41]	Zhu Z, Zou Y, Hu W, Li Y, Gu Y, Cao B, Guo N, Wang L, Song J, Zhang S 2016 Adv. Funct. Mater. 26 1793 Google Scholar
[42]	Ni Z, Ma L, Du S, Xu Y, Yuan M, Fang H, Wang Z, Xu M, Li D, Yang J 2017 ACS Nano 11 9854 Google Scholar
[43]	Knight M W, Sobhani H, Nordlander P, Halas N J 2011 Science 332 702 Google Scholar
[44]	Chalabi H, Schoen D, Brongersma M L 2014 Nano Lett. 14 1374 Google Scholar
[45]	Fang Z, Liu Z, Wang Y, Ajayan P M, Nordlander P, Halas N J 2012 Nano Lett. 12 3808 Google Scholar
[46]	Brongersma M L, Halas N J, Nordlander P 2015 Nature Nanotechnol. 10 25 Google Scholar
[47]	Christopher P, Moskovits M 2017 Ann. Rev. Phys. Chem. 68 379 Google Scholar
[48]	West L, Eglash S 1985 Appl. Phys. Lett. 46 1156 Google Scholar
[49]	Levine B, Malik R, Walker J, Choi K, Bethea C, Kleinman D, Vandenberg J 1987 Appl. Phys. Lett. 50 273 Google Scholar
[50]	Smith D, Mailhiot C 1987 J. Appl. Phys. 62 2545 Google Scholar
[51]	Gendron L, Carras M, Huynh A, Ortiz V, Koeniguer C, Berger V 2004 Appl. Phys. Lett. 85 2824 Google Scholar
[52]	Giorgetta F R, Baumann E, Hofstetter D, Manz C, Yang Q, Köhler K, Graf M 2007 Appl. Phys. Lett. 91 111115 Google Scholar
[53]	Giorgetta F R, Baumann E, Théron R, Pellaton M, Hofstetter D, Fischer M, Faist J 2008 Appl. Phys. Lett. 92 121101 Google Scholar
[54]	Giorgetta F R, Baumann E, Graf M, Yang Q, Manz C, Köhler K, Beere H E, Ritchie D A, Linfield E, Davies A G 2009 IEEE J. Quantum Electron. 45 1039 Google Scholar
[55]	Vardi A, Bahir G, Guillot F, Bougerol C, Monroy E, Schacham S, Tchernycheva M, Julien F 2008 Appl. Phys. Lett. 92 011112 Google Scholar
[56]	Li L, Xiong D, Wen J, Li N, Zhu Z 2016 Infrared Phys. Technol. 79 45 Google Scholar
[57]	Hofstetter D, Giorgetta F R, Baumann E, Yang Q, Manz C, Köhler K 2008 Appl. Phys. Lett. 93 221106 Google Scholar
[58]	Li L, Xiong D, Tang Z, Wen J, Li N, Chen P, Zhu Z 2017 J. Appl. Phys. 121 083102 Google Scholar
[59]	李梁 2017 博士学位论文(上海: 华东师范大学) Li L 2017 Ph. D. Dissertation (Shanghai: East China Normal University) (in Chinese)
[60]	Dougakiuchi T, Fujita K, Hirohata T, Ito A, Hitaka M, Edamura T 2016 Appl. Phys. Lett. 109 261107 Google Scholar
[61]	Li J V, Yang R Q, Hill C J, Chuang S L 2005 Appl. Phys. Lett. 86 101102 Google Scholar
[62]	Yang R Q, Tian Z, Cai Z, Klem J, Johnson M B, Liu H 2010 J. Appl. Phys. 107 054514 Google Scholar
[63]	Yang R Q, Tian Z, Klem J, Mishima T D, Santos M B, Johnson M B 2010 Appl. Phys. Lett. 96 063504 Google Scholar
[64]	Zhou Y, Chen J, Xu Z, He L 2016 Semicond. Sci. Technol. 31 085005 Google Scholar
[65]	Fang H H, Hu W D 2017 Adv. Sci. 4 1700323 Google Scholar
[66]	Kufer D, Konstantatos G 2016 ACS Photon. 3 2197 Google Scholar
[67]	Kufer D, Lasanta T, Bernechea M, Koppens F H L, Konstantatos G 2016 ACS Photon. 3 1324 Google Scholar
[68]	Sun Z, Liu Z, Li J, Tai G A, Lau S P, Yan F 2012 Adv. Mater. 24 5878 Google Scholar
[69]	Hu C, Dong D, Yang X, Qiao K, Yang D, Deng H, Yuan S, Khan J, Lan Y, Song H, Tang J 2017 Adv. Funct. Mater. 27 1603605 Google Scholar
[70]	Kufer D, Nikitskiy I, Lasanta T, Navickaite G, Koppens F H L, Konstantatos G 2015 Adv. Mater. 27 176 Google Scholar
[71]	Furchi M M, Polyushkin D K, Pospischil A, Mueller T 2014 Nano Lett. 14 6165 Google Scholar
[72]	Island J O, Blanter S I, Buscema M, van der Zant H S, Castellanos-Gomez A 2015 Nano Lett. 15 7853 Google Scholar
[73]	Guo Q, Pospischil A, Bhuiyan M, Jiang H, Tian H, Farmer D, Deng B, Li C, Han S J, Wang H, Xia Q, Ma T P, Mueller T, Xia F 2016 Nano Lett. 16 4648 Google Scholar
[74]	Konstantatos G, Badioli M, Gaudreau L, Osmond J, Bernechea M, Garcia de Arquer F P, Gatti F, Koppens F H 2012 Nature Nanotechnol. 7 363 Google Scholar
[75]	Goossens S, Navickaite G, Monasterio C, Gupta S, Piqueras J J, Pérez R, Burwell G, Nikitskiy I, Lasanta T, Galán T, Puma E, Centeno A, Pesquera A, Zurutuza A, Konstantatos G, Koppens F 2017 Nat. Photon. 11 366 Google Scholar
[76]	Guo N, Hu W, Liao L, Yip S, Ho J C, Miao J, Zhang Z, Zou J, Jiang T, Wu S, Chen X, Lu W 2014 Adv. Mater. 26 8203 Google Scholar
[77]	Fang H, Hu W, Wang P, Guo N, Luo W, Zheng D, Gong F, Luo M, Tian H, Zhang X, Luo C, Wu X, Chen P, Liao L, Pan A, Chen X, Lu W 2016 Nano Lett. 16 6416 Google Scholar
[78]	Adinolfi V, Sargent E H 2017 Nature 542 324 Google Scholar
[79]	Guo X, Wang W, Nan H, Yu Y, Jiang J, Zhao W, Li J, Zafar Z, Xiang N, Ni Z, Hu W, You Y, Ni Z 2016 Optica 3 1066 Google Scholar
[80]	Fukushima S, Shimatani M, Okuda S, Ogawa S, Kanai Y, Ono T, Matsumoto K 2018 Appl. Phys. Lett. 113 061102 Google Scholar
[81]	Legrand J F 1989 Ferroelectrics 91 303
[82]	Wang X, Wang P, Wang J, Hu W, Zhou X, Guo N, Huang H, Sun S, Shen H, Lin T 2015 Adv. Mater. 27 6575 Google Scholar
[83]	Wu G, Wang X, Wang P, Huang H, Chen Y, Sun S, Shen H, Lin T, Wang J, Zhang S 2016 Nanotechnology 27 364002 Google Scholar
[84]	Huang H, Wang X, Wang P, Wu G, Chen Y, Meng C, Liao L, Wang J, Hu W, Shen H 2016 RSC Adv. 6 87416 Google Scholar
[85]	Zheng D, Wang J, Hu W, Liao L, Fang H, Guo N, Wang P, Gong F, Wang X, Fan Z 2016 Nano Lett. 16 2548 Google Scholar
[86]	Zheng D, Fang H, Wang P, Luo W, Gong F, Ho J C, Chen X, Lu W, Liao L, Wang J 2016 Adv. Funct. Mater. 26 7690 Google Scholar
[87]	Sassi U, Parret R, Nanot S, Bruna M, Borini S, de Fazio D, Zhao Z, Lidorikis E, Koppens F, Ferrari A C 2017 Nat. Commun. 8 14311 Google Scholar
[88]	Hsieh C Y, Chen Y T, Tan W J, Chen Y F, Shih W Y, Shih W H 2012 Appl. Phys. Lett. 100 113507 Google Scholar
[89]	Wang L 2013 Science 342 614 Google Scholar
[90]	Geim A K, Grigorieva I V 2013 Nature 499 419 Google Scholar
[91]	Roy K, Padmanabhan M, Goswami S, Sai T P, Ramalingam G, Raghavan S, Ghosh A 2013 Nat. Nanotechnol. 8 826 Google Scholar
[92]	Zhang W, Chuu C P, Huang J K, Chen C H, Tsai M L, Chang Y H, Liang C T, Chen Y Z, Chueh Y L, He J H 2014 Sci. Rep. 4 3826
[93]	Liu C H, Chang Y C, Norris T B, Zhong Z 2014 Nat. Nanotechnol. 9 273 Google Scholar
[94]	Chen X, Lu X, Deng B, Sinai O, Shao Y, Li C, Yuan S, Tran V, Watanabe K, Taniguchi T 2017 Nat. Commun. 8 1672 Google Scholar
[95]	Han J, Wang J, Yang M, Kong X, Chen X, Huang Z, Guo H, Gou J, Tao S, Liu Z 2018 Adv. Mater. 30 1804020 Google Scholar
[96]	Yang M, Wang J, Han J, Ling J, Ji C, Kong X, Liu X, Huang Z, Gou J, Liu Z 2018 ACS Photon. 5 3438 Google Scholar
[97]	Yang M, Wang J, Zhao Y, He L, Ji C, Liu X, Zhou H, Wu Z, Wang X, Jiang Y 2019 ACS Nano 13 755
[98]	Long M S, Liu E F, Wang P, Gao A Y, Xia H, Luo W, Wang B G, Zeng J W, Fu Y J, Xu K, Zhou W, Lv Y Y, Yao S H, Lu M H, Chen Y F, Ni Z H, You Y M, Zhang X A, Qin S Q, Shi Y, Hu W D, Xing D Y, Miao F 2016 Nano Lett. 16 2254 Google Scholar
[99]	Bullock J, Amani M, Cho J, Chen Y Z, Ahn G H, Adinolfi V, Shrestha V R, Gao Y, Crozier K B, Chueh Y L 2018 Nat. Photon. 12 601 Google Scholar
[100]	Gibson S J, van Kasteren B, Tekcan B, Cui Y, van Dam D, Haverkort J E, Bakkers E P, Reimer M E 2019 Nature Nanotechnol. 14 473 Google Scholar
[101]	Jiang X, Itzler M A, Ben-Michael R, Slomkowski K 2007 IEEE J. Selected Topics in Quantum Electronics 13 895 Google Scholar
[102]	Lacaita A, Francese P, Zappa F, Cova S 1994 Appl. Opt. 33 6902 Google Scholar
[103]	Kang Y, Mages P, Clawson A, Yu P, Bitter M, Pan Z, Pauchard A, Hummel S, Lo Y 2002 IEEE Photon.Technol. Lett. 14 1593 Google Scholar
[104]	胡伟达, 李庆, 温洁, 王文娟, 陈效双, 陆卫 2018 红外技术 40 201 Hu W D, Li Q, Wen J, Wang W J, Chen X S, Lu W 2018 Infrared Technol. 40 201
[105]	Singh A, Srivastav V, Pal R 2011 Opt. Laser Technol. 43 1358 Google Scholar
[106]	Webb P P, McIntyre R J, Conradi J 1974 RCA Rev. 35 234
[107]	McIntyre R 1966 IEEE Trans. Electron Dev. 13 164
[108]	Wen J, Wang W, Li N, Li Z, Lu W 2017 Appl. Phys. Lett. 110 231105 Google Scholar
[109]	Wen J, Wang W, Li N, Li Z, Lu W 2016 Opt. Quantum Electron. 48 150 Google Scholar
[110]	Wen J, Wang W, Chen X, Li N, Chen X, Lu W 2018 J. Appl. Phys. 123 161530 Google Scholar
[111]	Gao A, Lai J, Wang Y, Zhu Z, Zeng J, Yu G, Wang N, Chen W, Cao T, Hu W, Sun D, Chen X, Miao F, Shi Y, Wang X 2019 Nature Nanotechnol. 14 217 Google Scholar
[112]	Leveque G, Nasser M, Bertho D, Orsal B, Alabedra R 1993 Semicond. Sci. Technol. 8 1317 Google Scholar
[113]	Beck J D, Wan C F, Kinch M A, Robinson J E 2001 Proc. SPIE 4454 188 Google Scholar
[114]	Kinch M, Beck J, Wan C F, Ma F, Campbell J 2004 J. Electron. Mater. 33 630 Google Scholar
[115]	Beck J, Woodall M, Scritchfield R, Ohlson M, Wood L, Mitra P, Robinson J 2007 Proc. SPIE 6542 654217 Google Scholar
[116]	Beck J, Wan C, Kinch M, Robinson J, Mitra P, Scritchfield R, Ma F, Campbell J 2006 J. Electron. Mater. 35 1166 Google Scholar
[117]	de Borniol E, Guellec F, Rothman J, Perez A, Zanatta J P, Tchagaspanian M, Castelein P, Destéfanis G, Peyrard J C, Pistone F 2010 Proc. SPIE 7660 76603D Google Scholar
[118]	de Borniol E D, Rothman J, Guellec F, Vojetta G, Destéfanis G, Pacaud O 2012 Opt. Eng. 51 061305 Google Scholar
[119]	Kerlain A, Bonnouvrier G, Rubaldo L, Decaens G, Reibel Y, Abraham P, Rothman J, Mollard L, de Borniol E 2012 J. Electron. Mater. 41 2943 Google Scholar
[120]	Qiu W C, Hu W D, Chen L, Lin C, Cheng X A, Chen X S, Lu W 2015 IEEE Trans. Electron Dev. 62 1926 Google Scholar
[121]	Li Q, He J L, Hu W D, Chen L, Chen X S, Lu W 2018 IEEE Trans. Electron Dev. 65 572 Google Scholar
[122]	Lao Y F, Perera A U, Li L, Khanna S, Linfield E, Liu H 2014 Nat. Photon. 8 412 Google Scholar
[123]	Perera A U, Chauhan D, Lao Y F, Li L, Khanna S P, Linfield E H 2016 Proc. SPIE 9844 98440X Google Scholar
[124]	Esaev D, Rinzan M, Matsik S, Perera A 2004 J. Appl. Phys. 96 4588 Google Scholar
[125]	Chauhan D, Perera A, Li L, Chen L, Linfield E 2018 Infrared Phys. Technol. 95 148 Google Scholar
[126]	Maimon S, Wicks G 2006 Appl. Phys. Lett. 89 151109
[127]	Klipstein P 2008 Proc. SPIE 6940 69402U Google Scholar
[128]	Evirgen A, Abautret J, Perez J, Aït-Kaci H, Christol P, Fleury J, Sik H, Nedelcu A, Cluzel R, Cordat A 2014 Proc. SPIE 8993 899313 Google Scholar
[129]	Perez J P, Evirgen A, Abautret J, Christol P, Cordat A, Nedelcu A 2015 Proc. SPIE 9370 93700N Google Scholar
[130]	Rodriguez J B, Plis E, Bishop G, Sharma Y, Kim H, Dawson L, Krishna S 2007 Appl. Phys. Lett. 91 043514 Google Scholar
[131]	Haddadi A, Chevallier R, Dehzangi A, Razeghi M 2017 Appl. Phys. Lett. 110 101104 Google Scholar
[132]	Hood A, Razeghi M, Aifer E H, Brown G J 2005 Appl. Phys. Lett. 87 151113 Google Scholar
[133]	Haddadi A, Chen G, Chevallier R, Hoang A, Razeghi M 2014 Appl. Phys. Lett. 105 121104 Google Scholar
[134]	Kim H, Plis E, Rodriguez J, Bishop G, Sharma Y, Dawson L, Krishna S, Bundas J, Cook R, Burrows D 2008 Appl. Phys. Lett. 92 183502 Google Scholar
[135]	Plis E, Myers S, Khoshakhlagh A, Kim H S, Sharma Y, Gautam N, Dawson R, Krishna S 2009 Infrared Phys. Technol. 52 335 Google Scholar
[136]	Plis E, Rodriguez J B, Balakrishnan G, Sharma Y, Kim H, Rotter T, Krishna S 2010 Semicond. Sci. Technol. 25 085010 Google Scholar
[137]	Plis E, Myers S, Kutty M, Mailfert J, Smith E, Johnson S, Krishna S 2010 Appl. Phys. Lett. 97 123503 Google Scholar
[138]	Khoshakhlagh A, Myers S, Plis E, Kutty M, Klein B, Gautam N, Kim H, Smith E, Rhiger D, Johnson S 2010 Proc. SPIE 7660 76602Z Google Scholar
[139]	Plis E, Gautam N, Myers S, Krishna S, Smith E, Johnson S, Krishna S 2011 Proc. SPIE 8012 80120X Google Scholar
[140]	Klipstein P, Klin O, Grossman S, Snapi N, Lukomsky I, Aronov D, Yassen M, Glozman A, Fishman T, Berkowicz E 2011 Opt. Eng. 50 061002 Google Scholar
[141]	Klipstein P, Avnon E, Benny Y, Fraenkel A, Glozman A, Hojman E, Ilan E, Kahanov E, Klin O, Langof L 2015 Proc. SPIE 9451 94510K Google Scholar
[142]	Klipstein P, Avnon E, Benny Y, Berkowicz E, Cohen Y, Dobromislin R, Fraenkel R, Gershon G, Glozman A, Hojman E 2017 J. Electron. Mater. 46 5386 Google Scholar
[143]	Klipstein P, Avnon E, Benny Y, Cohen Y, Fraenkel R, Gliksman S, Glozman A, Hojman E, Klin O, Krasovitsky L 2018 J. Electron. Mater. 47 5725 Google Scholar
[144]	Itsuno A, Phillips J, Velicu S 2011 J. Electron. Mater. 40 1624 Google Scholar
[145]	Itsuno A M, Phillips J D, Velicu S 2012 J. Electron. Mater. 41 2886 Google Scholar
[146]	Rogalski A 2002 Infrared Phys. Technol. 43 187 Google Scholar
[147]	李庆, 白杰, 吕衍秋, 胡伟达, 陈效双, 陆卫 2017 红外与毫米波学报 36 385 Google Scholar Li Q, Bai J, Lü Y Q, Hu W D, Chen X S, Lu W 2017 J. Infrared Millim.Waves 36 385 Google Scholar
[148]	Blazejewski E, Arias J, Williams G, McLevige W, Zandian M, Pasko J 1992 J. Vacuum Sci. Technol. B 10 1626 Google Scholar
[149]	Arias J, Zandian M, Williams G, Blazejewski E, DeWames R, Pasko J 1991 J. Appl. Phys. 70 4620 Google Scholar
[150]	Rogalski A 2010 J. Mod. Opt. 57 1716 Google Scholar
[151]	Hu W, Ye Z, Liao L, Chen H, Chen L, Ding R, He L, Chen X, Lu W 2014 Opt. Lett. 39 5184 Google Scholar
[152]	Liu H, Song C, Shen A, Gao M, Wasilewski Z, Buchanan M 2000 Appl. Phys. Lett. 77 2437 Google Scholar
[153]	Eker S, Kaldirim M, Arslan Y, Besikci C 2008 IEEE Electron Dev. Lett. 29 1121 Google Scholar
[154]	Haddadi A, Chevallier R, Chen G, Hoang A, Razeghi M 2015 Appl. Phys. Lett. 106 011104 Google Scholar
[155]	Khoshakhlagh A, Rodriguez J, Plis E, Bishop G, Sharma Y, Kim H, Dawson L, Krishna S 2007 Appl. Phys. Lett. 91 263504 Google Scholar
[156]	Hoang A, Chen G, Haddadi A, Razeghi M 2013 Appl. Phys. Lett. 102 011108 Google Scholar
[157]	Tang X, Ackerman M M, Chen M, Guyot-Sionnest P 2019 Nat. Photon. 13 277 Google Scholar

[1]	Zhou Fei, Chen Qi, Liu Hao, Dai Yue, Wei Chen, Yuan Hang, Wang Hao, Tu Xue-Cou, Kang Lin, Jia Xiao-Qing, Zhao Qing-Yuan, Chen Jian, Zhang La-Bao, Wu Pei-Heng. Noise characteristics analysis and suppression of optical system based on infrared superconducting single-photon detector. Acta Physica Sinica, 2024, 73(6): 068501. doi: 10.7498/aps.73.20231526
[2]	Zhao Hua-Liang, Peng Hong-Ling, Zhou Xu-Yan, Zhang Jian-Xin, Niu Bo-Wen, Shang Xiao, Wang Tian-Cai, Cao Peng. Structural design of dual carrier multiplication avalanche photodiodes on InP substrate. Acta Physica Sinica, 2023, 72(19): 198502. doi: 10.7498/aps.72.20230885
[3]	Ge Hao-Nan, Xie Run-Zhang, Guo Jia-Xiang, Li Qing, Yu Yi-Ye, He Jia-Le, Wang Fang, Wang Peng, Hu Wei-Da. Artificial micro- and nano-structure enhanced long and very long-wavelength infrared detectors. Acta Physica Sinica, 2022, 71(11): 110703. doi: 10.7498/aps.71.20220380
[4]	Cheng Kai, Wei Xin, Zeng De-Kai, Ji Xuan-Tao, Zhu Kun, Wang Xiao-Dong. Unfolding simulation of single-energy and continuous fast neutrons spectrum based on micro-pattern gas detector. Acta Physica Sinica, 2021, 70(11): 112901. doi: 10.7498/aps.70.20201954
[5]	Sun Yong-Feng, Xu Liang, Shen Xian-Chun, Jin Ling, Xu Han-Yang, Cheng Xiao-Xiao, Wang Yu-Hao, Liu Wen-Qing, Liu Jian-Guo. High-order nonlinear response correction method for infrared radiation detector. Acta Physica Sinica, 2021, 70(6): 060701. doi: 10.7498/aps.70.20201530
[6]	Han Dong, Sun Fei-Yang, Lu Ji-Yuan, Song Fu-Ming, Xu Yue. Reducing dark count of single-photon avalanche diode detector with polysilicon field plate. Acta Physica Sinica, 2020, 69(14): 148501. doi: 10.7498/aps.69.20200523
[7]	Zhang Hai-Yan, Wang Lin-Li, Wu Chen-Yi, Wang Yu-Rong, Yang Lei, Pan Hai-Feng, Liu Qiao-Li, Guo Xia, Tang Kai, Zhang Zhong-Ping, Wu Guang. Avalanche photodiode single-photon detector with high time stability. Acta Physica Sinica, 2020, 69(7): 074204. doi: 10.7498/aps.69.20191875
[8]	Wang Hai-Yun, Qi Hui-Rong, Liu Ling, Yuan Zhi-Yang, Zhang Yu-Lian, Wen Zhi-Wen, Zhang Jian, Chen Yuan-Bo, Ouyang Qun. Signal and pointing accuracy of ultraviolet laser in micro-pattern gaseous detector. Acta Physica Sinica, 2019, 68(2): 022901. doi: 10.7498/aps.68.20181613
[9]	An Tao, Tu Chuan-Bao, Gong Wei. Organic color photodetectors based on tri-phase bulk heterojunction with wide sectrum and photoelectronic mltiplication. Acta Physica Sinica, 2018, 67(19): 198503. doi: 10.7498/aps.67.20180502
[10]	Xiao Biao, Zhang Min-Li, Wang Hong-Bo, Liu Ji-Yan. High performence visble-near infrared photovoltaic detector based on narrow bandgap polymer. Acta Physica Sinica, 2017, 66(22): 228501. doi: 10.7498/aps.66.228501
[11]	Zhang Hui, Cai Xiao-Ming, Hao Zhen-Liang, Ruan Zi-Lin, Lu Jian-Chen, Cai Jin-Ming. Fabrication and electrical engineering of graphene nanoribbons. Acta Physica Sinica, 2017, 66(21): 218103. doi: 10.7498/aps.66.218103
[12]	Wang Chao, Hao Zhi-Biao, Wang Lei, Kang Jian-Bin, Xie Li-Li, Luo Yi, Wang Lai, Wang Jian, Xiong Bing, Sun Chang-Zheng, Han Yan-Jun, Li Hong-Tao, Wang Lu, Wang Wen-Xin, Chen Hong. Improvement on the efficiency of up-conversion infrared photodetectors using surface microstructure. Acta Physica Sinica, 2016, 65(10): 108501. doi: 10.7498/aps.65.108501
[13]	Yang Dan, Zhang Li, Yang Sheng-Yi, Zou Bing-Suo. Low-voltage pentacene photodetector based on a vertical transistor configuration. Acta Physica Sinica, 2015, 64(10): 108503. doi: 10.7498/aps.64.108503
[14]	Shi Wei, Yan Zhi-Jin. Research progress on avalanche multiplication GaAs photoconductive terahertz emitter. Acta Physica Sinica, 2015, 64(22): 228702. doi: 10.7498/aps.64.228702
[15]	Fan Sheng-Nan, Wang Bo, Qi Hui-Rong, Liu Mei, Zhang Yu-Lian, Zhang Jian, Liu Rong-Guang, Yi Fu-Ting, Ouyang Qun, Chen Yuan-Bo. Study on the performance of a high-gain gas electron multiplier-MicroMegas chamber. Acta Physica Sinica, 2013, 62(12): 122901. doi: 10.7498/aps.62.122901
[16]	Huo Yong-Heng, Ma Wen-Quan, Zhang Yan-Hua, Huang Jian-Liang, Wei Yang, Cui Kai, Chen Liang-Hui. Dual-band quantum well infrared photodetectors with two ohmic contacts. Acta Physica Sinica, 2011, 60(9): 098401. doi: 10.7498/aps.60.098401
[17]	Xiao Ying, Zhang Wan-Rong, Jin Dong-Yue, Chen Liang, Wang Ren-Qing, Xie Hong-Yun. Effect of bandgap engineering on thermal characteristic of radiofrequency power SiGe heterojunction bipolar transistor. Acta Physica Sinica, 2011, 60(4): 044402. doi: 10.7498/aps.60.044402
[18]	Ni Pei-Gen. Progress in the fabrication and application of photonic crystals. Acta Physica Sinica, 2010, 59(1): 340-350. doi: 10.7498/aps.59.340
[19]	Wang Jin-Dong, Wu Zu-Heng, Zhang Bing, Wei Zheng-Jun, Liao Chang-Jun, Liu Song-Hao. A new circuit model for avalanche photodiodes to detect infrared single photon by transient process of transmission lines. Acta Physica Sinica, 2008, 57(9): 5620-5626. doi: 10.7498/aps.57.5620
[20]	CHEN YAN-SONG. EXPERIMENTAL STUDY ON INFRARED PHOTORESPONSE OF FERROELECTRIC THIN FILM DETECTOR PbZrTiO3. Acta Physica Sinica, 1998, 47(8): 1378-1382. doi: 10.7498/aps.47.1378

Catalog

Vol. 68, Issue 12 - 2019-06-20

Metrics

Abstract views: 38839
PDF Downloads: 1779
Cited By: 0

姓名
邮箱
手机号码
标题
留言内容
验证码

Search

Article

留言板