Research progress of magnetic anisotropy enhancement mechanism of high-performance La-Co co-substituted M-type permanent magnet ferrites

Liu Ruo-Shui; Wang Li-Chen; Yu Xiang; Sun Yang; He Shi-Yue; Zhao Tong-Yun; Shen Bao-Gen

doi:10.7498/aps.73.20240190

Abstract

La-Co co-substituted M-type ferrite, which was first reported at the end of the 20th century, as the cornerstone of high-performance permanent magnet ferrites, has received increasing attention from researchers around the world. The unquenched orbital moments of Co²⁺ play a pivotal role in enhancing the uniaxial anisotropy of M-type ferrites. However, a comprehensive understanding of its microscopic mechanism remains elusive. In order to meet the increasing performance requirements of ferrite materials, it is imperative to clarify the mechanism behind the enhancement of magnetic anisotropy, and at the same time seek the guiding principles that are helpful to develop high-performance product quickly and economically. But its mechanism at a microscopic level has not been explained. This review comprehensively analyzes various studies aiming at pinpointing the crystal sites of Co substitution within the lattice. These investigations including neutron diffraction, nuclear magnetic resonance, and Mössbauer spectroscopy can reveal the fundamental origins behind the enhancement of magnetic anisotropy, thereby providing valuable insights for material design strategies aiming at further enhancing the magnetic properties of permanent magnet ferrites.The exploration of co-substitution sites has yielded noteworthy findings. Through careful examination and analysis, researchers have discovered the complex interplay between Co ions and the lattice structure, revealing the mechanisms of enhanced magnetic anisotropy. The current mainstream view is that Co ions tend to occupy more than one site, namely the 4f₁, 12k, and 2a sites, all of which are located within the spinel lattice. However, there have also been differing viewpoints, implying that further exploration is needed to uncover the primary controlling factors influencing Co occupancy. It is worth noting that the identification of specific Co substitution sites, especially the spin-down tetrahedron 4f₁, has achieved targeted modifications, ultimately fine-tuning the magnetic properties with remarkable precision.Furthermore, the reviewed research emphasizes the pivotal role of crystallographic engineering in tailoring the magnetic characteristics of ferrite materials. By strategically manipulating Co substitution, researchers have utilized the intrinsic properties of the lattice to amplify magnetic anisotropy, thereby unlocking new avenues for the advancement of permanent magnet ferrites.In conclusion, the collective findings outlined in this review herald a promising trajectory for the field of permanent magnet ferrites. With a detailed understanding of Co-substitution mechanisms, researchers are preparing to open up new avenues for developing next-generation ferrite materials with enhanced magnetic properties.

Keywords:

Authors and contacts

1.
Ningbo Institute of Materials Technology and Engineering, Chinese Academy of Sciences, Ningbo 315201, China
2.
Beijing State Key Laboratory of Condensed Matter Physics, Institute of Physics, Chinese Academy of Sciences, Beijing 100190, China
3.
Ganjiang Innovation Research Institute, Chinese Academy of Sciences, Ganzhou 341119, China
4.
School of Rare Earths, University of Science and Technology of China, Hefei 230026, China

Corresponding author: Shen Bao-Gen, shenbaogen@nimte.ac.cn

Funds: Project supported by the Basic Science Center Program of the National Science Foundation of China (Grant No. 52088101), the Kunpeng Plan of Zhejiang Province, China, and the Ningbo Top Talent Program, Zhejiang, China.

FullText HTML : translate this paragraph

References

[1]	Went J, Rathenau G, Gorter E, Van Oosterhout G 1952 Phy. Rev. 86 424 Google Scholar
[2]	Went J J, Rathenau G W, Gorter E W, Oosterhout G W V 1952 Philips Tech. Rev. 13 194
[3]	Granados-Miralles C, Jenuš P 2021 J. Phys. D Appl. Phys. 54 303001 Google Scholar
[4]	Coey J M D 2002 J. Magn. Magn. Mater. 248 441 Google Scholar
[5]	Pullar R C 2012 Prog. Mater. Sci. 57 1191 Google Scholar
[6]	Gutfleisch O, Willard M A, Bruck E, Chen C H, Sankar S G, Liu J P 2011 Adv. Mater. 23 821 Google Scholar
[7]	de Julian Fernandez C, Sangregorio C, de la Figuera J, Belec B, Makovec D, Quesada A 2020 J. Phys. D Appl. Phys. 54 153001 Google Scholar
[8]	Bollero A, Rial J, Villanueva M, Golasinski K M, Seoane A, Almunia J, Altimira R 2017 ACS Sustain. Chem. Eng. 5 3243 Google Scholar
[9]	Iida K, Minachi Y, Masuzawa K, Kawakami M, Nishio H, Taguchi H 1999 J. Magn. Soc. Jpn. 23 1093 Google Scholar
[10]	Coey J M 2014 J. Phys. Condens. Matter 26 064211 Google Scholar
[11]	Cochardt A 1966 J. Appl. Phys. 37 1112 Google Scholar
[12]	Taguchi H 1998 KONA Powder Part. J. 16 116 Google Scholar
[13]	Goldman A 2006 Modern Ferrite Technology (New York: Springer Science & Business Media
[14]	Went J 1952 Philips Tech. Rev. 13 361
[15]	Stuijts A, Rathenau G, Weber G 1954 Philips Tech. Rev. 16 209
[16]	Deshpande U S 2003 IEEE International Electric Machines and Drives Conference IEMDC'03 Madison, WI, USA, June 1-4, 2003 p509
[17]	Chen C H, Yi P 2014 Proceedings of 2014 International Conference on NdFeB Magnets: Supply Chain, Critical Properties, & Applications Ningbo, China, March 2−5, 2014 p126
[18]	Tech-Mag T https://www.tdk.com/en/tech-mag/ferrite02/012#section3 [2021-12-3]
[19]	Coey J M D 2020 Engineering 6 119 Google Scholar
[20]	Bollero A, Palmero E M 2022 Modern Permanent Magnets Chapter 3-Recent Advances in Hard-Ferrite Magnets ( Woodhead Publishing
[21]	TDK https://product.tdk.com/en/system/files?file=dam/doc/product/magnet/magnet/ferrite/datasheets/magnet_fb_summary_en.pdf [2021-12-3]
[22]	Hitachi Metals L http://www.hitachi-metals.co.jp/e/products/auto/el/p03_01_g.html [2021-12-3]
[23]	TDK Ferrite Magnets Catalog https://product.tdk.com/en/products/magnet/magnet/ferrite/index.html [2021-12-3]
[24]	翁兴园 2021 新材料产业 4 32 Google Scholar Weng X Y 2021 Adv. Mater. Indus. 4 32 Google Scholar
[25]	华经产业研究 https://baijiahao.baidu.com/s?id=1749074365467103880&wfr=spider&for=pc [2023-2-13]
[26]	陈羽峰, 徐斌 2022 磁性材料及器件 54 108 Google Scholar Chen Y F, Xu B 2022 J. Mag. Mater. Dev. 54 108 Google Scholar
[27]	横店东磁磁性产品 http://www.chinadmegc.com/product/1.html [2024-1-28]
[28]	北矿磁材科技有限公司-烧结永磁铁氧体磁粉(BGRIMM Magnetic Materials & Technology Co. , Ltd) http://www.magmat.com/cpysc/yctytcf/index.htm [2022-11-15]
[29]	江益磁材湿式异方性铁氧体永磁产品结构http://www.jpmf.com.cn/displayproduct.html?id=3806471777899840 [2022-11-15]
[30]	安徽龙磁科技股份有限公司永磁铁氧体磁性能牌号表https://www.sinomagtech.com/cpzx/yctyt/ [2024-1-28]
[31]	Hitachi catalogue http://www.hitachi-metals.co.jp/e/products/auto/el/p03_05.html [2022-11-15]
[32]	翁兴园 2013 新材料产业 4 31 Google Scholar Weng X Y 2013 Adv. Mater. Indus. 4 31 Google Scholar
[33]	Smit B J, Wijn H P 1959 Ferrites, Philips Technical Library (The Netherlands: Eindhoven
[34]	Aminoff G 1925 Geologiska Fö reningen i Stockholm Fö rhandlingar 47 283 Google Scholar
[35]	Adelsköld V 1938 Arkiv. Kemi. Min. Geol. 12a 1
[36]	Harris V G, Geiler A, Chen Y, Yoon S D, Wu M, Yang A, Chen Z, He P, Parimi P V, Zuo X, Patton C E, Abe M, Acher O, Vittoria C 2009 J. Magn. Magn. Mater. 321 2035 Google Scholar
[37]	Kojima H 1982 Handb. Ferromagn. Mater. 3 305 Google Scholar
[38]	Kreisel J, Vincent H, Tasset F, Paté M, Ganne J P 2001 J. Magn. Magn. Mater. 224 17 Google Scholar
[39]	Townes W, Fang J, Perrotta A 1967 Z. Krist. -Cryst. Mater. 125 437 Google Scholar
[40]	Braun P B 1957 Philips Res. Rep. 12 491
[41]	Bilovol V, Martínez-García R 2015 J. Phy. Chem. Solids 86 131 Google Scholar
[42]	Harris V G 2012 IEEE T. Magn. 48 1075 Google Scholar
[43]	Cullity B D, Graham C D 2011 Introduction to Magnetic Materials (Hoboken: John Wiley & Sons
[44]	Jahn L, Müller H G 1969 Phys. Status Solidi B 35 723 Google Scholar
[45]	Coey J M 2010 Magnetism and Magnetic Materials (Cambridge: Cambridge University Press
[46]	Stäblein H 1982 Handb. Ferromagn. Mater. 3 441 Google Scholar
[47]	Cui J, Kramer M, Zhou L, Liu F, Gabay A, Hadjipanayis G, Balasubramanian B, Sellmyer D 2018 Acta Mater. 158 118 Google Scholar
[48]	Selvaraj S, Gandhi U, Berchmans L J, Mangalanathan U 2021 Mater. Tech. 36 36 Google Scholar
[49]	Waki T 2022 J. Jpn. Soc. Powder Powder Metall. 69 149 (in Japanese Google Scholar
[50]	Mahmood S H, Abu-Aljarayesh I 2016 Hexaferrite Permanent Magnetic Materials (Materials Research Forum LLC
[51]	Lisjak D, Mertelj A 2018 Prog. Mater. Sci. 95 286 Google Scholar
[52]	任延英, 李雅宁, 柳洪盛, 徐楠, 郭坤, 徐朝辉, 陈鑫, 高峻峰 2024 物理学报 73 066104 Google Scholar Ren Y Y, Li Y N, Liu H S, Xu N, Guo K, Xu Z H, Chen X, Gao J F 2024 Acta Phys. Sin. 73 066104 Google Scholar
[53]	Rhein F, Helbig T, Neu V, Krispin M, Gutfleisch O 2018 Acta Mater. 146 85 Google Scholar
[54]	Trukhanov A V, Kostishyn V G, Panina L V, Jabarov S H, Korovushkin V V, Trukhanov S V, Trukhanova E L 2017 Ceram. Int. 43 12822 Google Scholar
[55]	Trukhanov S V, Trukhanov A V, Turchenko V A, Kostishyn V G, Panina L V, Kazakevich I S, Balagurov A M 2016 J. Alloy Compd. 689 383 Google Scholar
[56]	Li J, Hong Y, He S, Li W K, Bai H, Xia Y H, Sun G A, Zhou Z X 2022 J. Adv. Ceram. 11 263 Google Scholar
[57]	Nguyen H H, Jeong W H, Phan T L, Lee B W, Yang D S, Tran N, Dang N T 2021 J. Magn. Magn. Mater. 537 168195 Google Scholar
[58]	Albanese G, Deriu A 1979 Ceram. Int. 5 3 Google Scholar
[59]	Dionne G F 2009 Magnetic Oxides (New York: Springer
[60]	Summergrad R N, Banks E 1957 J. Phys. Chem. Solids 2 312 Google Scholar
[61]	Le Roux D, Vincent H, Joubert J C, Vallet-Regi M 1988 Mater. Res. Bull. 23 299 Google Scholar
[62]	Ogata Y, Kubota Y, Takami T, Tokunaga M, Shinokara T 1999 IEEE T. Magn. 35 3334 Google Scholar
[63]	Tenaud P, Morel A, Kools F, Le Breton J M, Lechevallier L 2004 J. Alloy Compd. 370 331 Google Scholar
[64]	Kools F, Morel A, Grössinger R, Le Breton J M, Tenaud P 2002 J. Magn. Magn. Mater. 242-245 1270 Google Scholar
[65]	Nishio H, Minachi Y, Yamamoto H 2009 IEEE T. Magn. 45 5281 Google Scholar
[66]	Kikuchi T, Nakamura T, Yamasaki T, Nakanishi M, Fujii T, Takada J, Ikeda Y 2010 J. Magn. Magn. Mater. 322 2381 Google Scholar
[67]	Nishio H, Yamamoto H 2011 IEEE T. Magn. 47 3641 Google Scholar
[68]	Kobayashi Y, Hosokawa S, Oda E, Toyota S 2008 J. Jpn. Soc. Powder Powder Metall. 55 541 Google Scholar
[69]	Du Y B, Liu Y, Lian L X, Du J 2019 J. Magn. Magn. Mater. 469 189 Google Scholar
[70]	Chen Z, Wang F, Yan S, Nie Y, Feng Z, Chen Y, Harris V G, Zhang S 2014 J. Am. Ceram. Soc. 97 1873 Google Scholar
[71]	Chen Z, Wang F, Yan S, Feng Z 2014 Mat. Sci. Eng. B 182 69 Google Scholar
[72]	Zhu D, Geng Z, Liu R S, Zhou X, Jia L, Hu G, Wang Q, Li B 2020 Rare Metals 39 89 Google Scholar
[73]	Li X, Yang W G, Bao D X, Meng X D, Lou B Y 2013 J. Magn. Magn. Mater. 329 1 Google Scholar
[74]	Huang X, Liu X S, Yang Y J, Huang K, Niu X F, Jin D L, Gao S, Ma Y Q, Huang F, Lv F R, Feng S J 2015 J. Magn. Magn. Mater. 378 424 Google Scholar
[75]	Yang Y J, Wang F H, Shao J X, Huang D H, Liu X X, Feng S J, Wen C E 2015 J. Magn. Magn. Mater. 384 64 Google Scholar
[76]	Kang Y M, Moon K S 2015 Ceram. Int. 41 12828 Google Scholar
[77]	Lotgering F K 1974 J. Phys. Chem. Solids 35 1633 Google Scholar
[78]	Deschamps A, Bertaut F 1957 Compt. Rend. 244 3069
[79]	Wang J F, Ponton C B, Harris I R 2001 J. Magn. Magn. Mater. 234 233 Google Scholar
[80]	Lechevallier L, Le Breton J M, Wang J F, Harris I R 2004 J. Magn. Magn. Mater. 269 192 Google Scholar
[81]	Wang J F, Ponton C B, Grössinger R, Harris I R 2004 J. Alloys Compd. 369 170 Google Scholar
[82]	Sharma P, Verma A, Sidhu R K, Pandey O P 2003 J. Alloys Compd. 361 257 Google Scholar
[83]	Grossinger R, Kupferling M, Tellez Blanco J C, Wiesinger G, Muller M, Hilscher G, Pieper M W, Wang J F, Harris I R 2003 IEEE T. Magn. 39 2911 Google Scholar
[84]	Mocuta H, Lechevallier L, Le Breton J M, Wang J F, Harris I R 2004 J. Alloys Compd. 364 48 Google Scholar
[85]	Wang J F, Ponton C B, Harris I R 2005 J. Alloys Compd. 403 104 Google Scholar
[86]	Ounnunkad S 2006 Solid State Commun. 138 472 Google Scholar
[87]	Litsardakis G, Manolakis I, Efthimiadis K 2007 J. Alloys Compd. 427 194 Google Scholar
[88]	Lechevallier L, Le Breton J M, Morel A, Tenaud P 2008 J. Phys. Condens. Mat. 20 175203 Google Scholar
[89]	Seifert D, Töpfer J, Stadelbauer M, Grössinger R, Le Breton J M 2011 J. Am. Ceram. Soc. 94 2109 Google Scholar
[90]	Waki T, Inoue G, Tabata Y, Nakamura H 2020 IEEE T. Magn. 56 6702304 Google Scholar
[91]	Lucchini E, Slokar G 1980 J. Magn. Magn. Mater. 21 93 Google Scholar
[92]	Blanco A M, Gonzalez C 1991 J. Phys. D Appl. Phys. 24 612 Google Scholar
[93]	Lechevallier L, Le Breton J M, Morel A, Tenaud P 2007 J. Magn. Magn. Mater. 316 e109 Google Scholar
[94]	Chlan V, Kouřil K, Uličná K, Štěpánková H, Töpfer J, Seifert D 2015 Phys. Rev. B 92 125125 Google Scholar
[95]	Sauer C, Köbler U, Zinn W, Stäblein H 1978 J. Phys. Chem. Solids 39 1197 Google Scholar
[96]	Le Breton J M, Seifert D, Töpfer J, Lechevallier L 2015 Physica B 470 33 Google Scholar
[97]	Lechevallier L, Le Breton J M, Teillet J, Morel A, Kools F, Tenaud P 2003 Physica B 327 135 Google Scholar
[98]	Graetsch H, Leckebusch R, Sahl K, Haberey F, Rosenberg M S 1984 IEEE T. Magn. 20 495 Google Scholar
[99]	Lee H B, Chun S H, Shin K W, Jeon B G, Chai Y S, Kim K H, Schefer J, Chang H, Yun S N, Joung T Y, Chung J H 2012 Phys. Rev. B 86 094435 Google Scholar
[100]	Pieper M W, Morel A, Kools F 2002 J. Magn. Magn. Mater. 242-245 1408 Google Scholar
[101]	Pieper M W, Kools F, Morel A 2002 Phys. Rev. B 65 184402 Google Scholar
[102]	Morel A, Le Breton J M, Kreisel J, Wiesinger G, Kools F, Tenaud P 2002 J. Magn. Magn. Mater. 242-245 1405 Google Scholar
[103]	Le Breton J M, Teillet J, Wiesinger G, Morel A, Kools F, Tenaud P 2002 IEEE T. Magn. 38 2952 Google Scholar
[104]	Wiesinger G, Mller M, Grssinger R, Pieper M, Morel A, Kools F, Tenaud P, Le Breton J M, Kreisel J 2002 Phys. Status Solidi A 189 499 Google Scholar
[105]	Lechevallier L, Le Breton J M, Wang J F, Harris I R 2004 J. Phys. Condens. Mat. 16 5359 Google Scholar
[106]	Choi D H, Lee S W, Shim I B, Kim C S 2006 J. Magn. Magn. Mater. 304 e243 Google Scholar
[107]	Kobayashi Y, Oda E, Nishiuchi T, Nakagawa T 2011 J. Ceram. Soc. Jpn. 119 285 Google Scholar
[108]	Langhof N, Göbbels M 2009 J. Solid State Chem. 182 2725 Google Scholar
[109]	Kouřil K 2013 Ph. D. Dissertation (Prague: Charles University
[110]	Wu C J, Yu Z, Yang Y, Sun K, Guo R D, Jiang X N, Lan Z W 2015 J. Appl. Phys. 118 103907 Google Scholar
[111]	Ohtsuka M, Muto S, Tatsumi K, Kobayashi Y, Kawata T 2016 Microscopy 65 127 Google Scholar
[112]	Mahadevan S, Sathe V, Raghavendra Reddy V, Sharma P 2020 IEEE T. Magn. 56 1800106 Google Scholar
[113]	Nagasawa N, Ikeda S, Shimoda A, Waki T, Tabata Y, Nakamura H, Kobayashi H 2016 Hyperfine Interact. 237 39 Google Scholar
[114]	Oura M, Nagasawa N, Ikeda S, Shimoda A, Waki T, Tabata Y, Nakamura H, Hiraoka N, Kobayashi H 2018 J. Appl. Phys. 123 033907 Google Scholar
[115]	Sakai H, Hattori T, Tokunaga Y, Kambe S, Ueda H, Tanioku Y, Michioka C, Yoshimura K, Takao K, Shimoda A, Waki T, Tabata Y, Nakamura H 2018 Phys. Rev. B 98 064403 Google Scholar
[116]	Nakamura H, Waki T, Tabata Y, Mény C 2019 J. Phys. Mater. 2 015007 Google Scholar
[117]	Nagasawa N, Oura M, Ikeda S, Waki T, Tabata Y, Nakamura H, Kobayashi H 2020 J. Appl. Phys. 128 133901 Google Scholar
[118]	Balbashov A M, Egorov S K 1981 J. Cryst. Growth 52 498 Google Scholar
[119]	Morishita H, Amano A, Ueda H, Michioka C, Yoshimura K 2014 J. Jpn. Soc. Powder Powder Metall. 61 S64 Google Scholar
[120]	Gambino R J, Leonhard F 1961 J. Am. Ceram. Soc. 44 221 Google Scholar
[121]	Shirk B T, Buessem W R 1969 J. Appl. Phys. 40 1294 Google Scholar
[122]	Goto Y, Takahashi K 1972 J. Ceram. Soc. Jpn. 80 358 Google Scholar
[123]	Obradors X, Solans X, Collomb A, Samaras D, Rodriguez J, Pernet M, Font-Altaba M 1988 J. Solid State Chem. 72 218 Google Scholar
[124]	Vinnik D A, Tarasova A Y, Zherebtsov D A, Gudkova S A, Galimov D M, Zhivulin V E, Trofimov E A, Nemrava S, Perov N S, Isaenko L I, Niewa R 2017 Materials 10 578 Google Scholar
[125]	Vinnik D A, Gudkova S A, Zherebtsov D A, Trofimov E A, Mashkovtseva L S, Trukhanov A V, Trukhanov S V, Nemrava S, Blaschkowski B, Niewa R 2019 J. Magn. Magn. Mater. 470 97 Google Scholar
[126]	Vincent H, Sugg B, Lefez V, Bochu B, Boursier D, Chaudouet P 1991 J. Magn. Magn. Mater. 101 170 Google Scholar
[127]	Takaoka H, Suito H 1994 J. Cryst. Growth 137 493 Google Scholar
[128]	Eraky M R, Beslepkin A A, Kuntsevich S P 2003 Mater. Lett. 57 3427 Google Scholar
[129]	Jalli J, Yang-Ki H, Sung-Hoon G, Seok B, Jaejin L, Sur J C, Abo G S, Lyle A, Sung-Ik L, Hwachol L, Mewes T 2008 IEEE T. Magn. 44 2978 Google Scholar
[130]	Pavlova S G, Balbashov A M, Rybina L N 2012 J. Cryst. Growth 351 161 Google Scholar
[131]	Vinnik D A, Zherebtsov D A, Mashkovtseva L S, Nemrava S, Semisalova A S, Galimov D M, Gudkova S A, Chumanov I V, Isaenko L I, Niewa R 2015 J. Alloys Compd. 628 480 Google Scholar
[132]	Shlyk L, Vinnik D A, Zherebtsov D A, Hu Z, Kuo C Y, Chang C F, Lin H J, Yang L Y, Semisalova A S, Perov N S, Langer T, Pöttgen R, Nemrava S, Niewa R 2015 Solid State Sci. 50 23 Google Scholar
[133]	Vinnik D A, Tarasova A Y, Zherebtsov D A, et al. 2015 Ceram. Int. 41 9172 Google Scholar
[134]	Vinnik D A, Zherebtsov D A, Mashkovtseva L S, et al. 2015 Mater. Chem. Phys. 155 99 Google Scholar
[135]	Vinnik D A, Semisalova A S, Mashkovtseva L S, Yakushechkina A K, Nemrava S, Gudkova S A, Zherebtsov D A, Perov N S, Isaenko L I, Niewa R 2015 Mater. Chem. Phys. 163 416 Google Scholar
[136]	Gudkova S A, Vinnik D A, Zhivulin V E, et al. 2019 J. Magn. Magn. Mater. 470 101 Google Scholar
[137]	Hassner M, Vinnik D A, Niewa R 2020 Materials 13 858 Google Scholar
[138]	Vinnik D A, Prosvirin I P, Zhivulin V E, et al. 2020 J. Alloys Compd. 844 156036 Google Scholar
[139]	Zhivulin V E, Trofimov E A, Zaitseva O V, Zherebtsov D A, Uchaev D A, Vinnik D A 2020 Crystals 10 264 Google Scholar
[140]	Shimoda A, Takao K, Uji K, Waki T, Tabata Y, Nakamura H 2016 J. Solid State Chem. 239 153 Google Scholar
[141]	Liu R S, Wang L C, Xu Z, Qin C, Li Z, Yu X, Liu D, Gong H, Zhao T Y, Sun J, Hu F, Shen B G 2022 Mater. Today Commun. 32 103996 Google Scholar
[142]	Ueda H, Tanioku Y, Michioka C, Yoshimura K 2017 Phys. Rev. B 95 224421 Google Scholar
[143]	Waki T, Okazaki S, Tabata Y, Kato M, Hirota K, Nakamura H 2018 Mater. Res. Bull. 104 87 Google Scholar
[144]	Waki T, Uji K, Tabata Y, Nakamura H 2019 J Solid State Chem. 270 366 Google Scholar
[145]	Waki T, Takao K, Tabata Y, Nakamura H 2020 J. Solid State Chem. 282 121071 Google Scholar
[146]	Waki T, Hani K, Tabata Y, Nakamura H 2023 Mater. Trans. 64 564 Google Scholar
[147]	Küpferling M, Novák P, Knížek K, Pieper M W, Grössinger R, Wiesinger G, Reissner M 2005 J. Appl. Phys. 97 10 Google Scholar
[148]	Küpferling M, Grössinger R, Pieper M W, et al. 2006 Phys. Rev. B 73 144408 Google Scholar
[149]	Komabuchi M, Urushihara D, Kimata Y, Okabe M, Asaka T, Fukuda K 2019 Phys. Rev. B 100 094406 Google Scholar
[150]	Komabuchi M, Urushihara D, Kimata Y, Okabe M, Asaka T, Fukuda K, Nakano K, Yamamoto K 2020 J. Magn. Magn. Mater. 498 166115 Google Scholar
[151]	Liu R S, Wang L C, Yu X, Xu Z, Gong H, Zhao T Y, Hu F, Shen B G 2023 Ceram. Int. 49 1888 Google Scholar
[152]	Williams J M, Adetunji J, Gregori M 2000 J. Magn. Magn. Mater. 220 124 Google Scholar
[153]	Kobayashi Y, Oda E, Nakagawa T, Nishiuchi T 2016 J. Jpn. Soc. Powder Powder Metall. 63 101 Google Scholar
[154]	Kobayashi Y, Oda E, Kawata T, Nakagawa T 2017 Hitachi Metal Tech. Rev. 33 34 (in Japanese
[155]	Nakamura H, Shimoda A, Waki T, Tabata Y, Meny C 2016 J. Phys. Condens Mat. 28 346002 Google Scholar
[156]	Nishikubo T, Motizuki K 1962 J. Phys. Soc. Jpn. 17 871 Google Scholar
[157]	Tsuda T, Okada K, Yasuoka H 1974 J. Phys. Soc. Jpn. 37 1713 Google Scholar
[158]	Jung H, Lee S J, Song M, Lee S, Lee H J, Kim D H, Kang J S, Zhang C L, Cheong S W 2009 New J. Phys. 11 043008 Google Scholar
[159]	Miyatani K, Kohn K, Kamimura H, Iida S 1966 J. Phys. Soc. Jpn. 21 464 Google Scholar
[160]	Itoh M, Nawata Y, Kiyama T, Akahoshi D, Fujiwara N, Ueda Y 2003 Physica B 329 751 Google Scholar
[161]	Ghoshray A, Bandyopadhyay B, Ghoshray K, Morchshakov V, Bärner K, Troyanchuk I O, Nakamura H, Kohara T, Liu G Y, Rao G H 2004 Phys. Rev. B 69 064424 Google Scholar
[162]	Julien M H, de Vaulx C, Mayaffre H, et al. 2008 Phys. Rev. Let. 100 096405 Google Scholar
[163]	Park J, Hong Y K, Lee W, Choi B C, Choi C J 2016 IEEE Magn. Lett. 7 5500403 Google Scholar
[164]	Dixit V, Kim S G, Park J, Hong Y K 2017 AIP Adv. 7 115209 Google Scholar
[165]	Hui Y J, Cheng W M, Lin G Q, Miao X S 2014 IEEE T. Magn. 50 2800904 Google Scholar
[166]	Hou Y H, Chen X, Guo X L, Li W, Huang Y L, Tao X M 2021 J. Magn. Magn. Mater. 538 168257 Google Scholar
[167]	Ravindran P, Delin A, James P, Johansson B, Wills J, Ahuja R, Eriksson O 1999 Phys. Rev. B 59 15680 Google Scholar
[168]	Feng M, Shao B, Wu J, Zuo X 2013 J. Appl. Phys. 113 17D909 Google Scholar
[169]	Ahn K, Ryu B, Korolev D, Jae Kang Y 2013 Appl. Phys. Lett. 103 242417 Google Scholar
[170]	Halilov S, Perlov A Y, Oppeneer P, Yaresko A, Antonov V 1998 Phys. Rev. B 57 9557 Google Scholar
[171]	Wang G Y, Yang K, Ma Y Z H, Liu L, Lu D, Zhou Y X, Wu H 2023 Chin. Phys. Lett. 40 077301 Google Scholar
[172]	蒋有为 2020 硕士学位论文 (成都: 电子科技大学) Jiang Y W 2020 M. S. Thesis (Chengdu: University of Electronic Science and Technology of China
[173]	Inoue J, Onoda H, Yanagihara H 2020 J. Phys. D Appl. Phys. 53 195003 Google Scholar
[174]	Inoue J, Nakamura H, Yanagihara H 2019 T. Magn. Soc. Jpn. (Special Issues) 3 12 Google Scholar
[175]	Silva L M, da Silva R B, Silva R L, et al. 2022 Ceram. Int. 48 23224 Google Scholar

Cited By

图 1 从1950年代至2023年关于铁氧体作为永磁材料的科学论文发表量的历史演变(来源: Scopus-以关键词“Ferrite permanent magnet”搜索获得的结果)

Figure 1. Historical evolution of the number of scientific papers published on ferrite as a permanent magnet material from the 1950 s to 2023 (Source: Scopus- search results by keyword “Ferrite permanent magnet”).

DownLoad: Full-Size Img PowerPoint

图 2 TDK公司铁氧体磁体的磁特性变化^[23]

Figure 2. Changes in magnetic properties of ferrite magnets in TDK corporation^[23].

DownLoad: Full-Size Img PowerPoint

图 3 2021—2025年三大领域永磁铁氧体需求预测(数据来源: 中国电子材料协会磁性材料分会华经产业研究院^[25])

Figure 3. Forecast of ferrite magnets demand in three major fields, 2021—2025 (Data source: Huajng Industrial Research Institute of Magnetic Materials Branch, China Electronic Materials Association^[25]).

DownLoad: Full-Size Img PowerPoint

图 4 BaFe₁₂O₁₉单位晶胞的晶体结构和各Fe晶位示意图

Figure 4. Crystal structure of the unit cell of BaFe₁₂O₁₉ and the schematic diagrams of each Fe crystal site.

DownLoad: Full-Size Img PowerPoint

图 5 (a) Sr_1–xLa_xCo_xFe_12–xO₁₉在1200 ℃烧结温度下的磁性能^[9]; (b)各向同性Sr铁氧体经La-Co添加后的磁性能变化(空心符号表示La-Co添加样品, 实心符号表示Cr₂O₃添加样品)^[62]; (c)在–100—+140 ℃温度范围内, x = 0.0—0.2的La-Co替代Sr铁氧体的B_r[α(B_r)]和H_cJ[β(H_cJ)]的温度系数^[62]

Figure 5. (a) Magnetic properties of Sr_1–xLa_xCo_xFe_12–xO₁₉ at a sintering temperature of 1200 ℃^[9]; (b) variation of magnetic properties of isotropic Sr ferrite with La-Co addition (hollow symbols denote the La-Co added samples and solid symbols denote the Cr₂O₃ added samples)^[62]; (c) in the temperature range of –100 ℃ to +140 ℃, the temperature coefficients of B_r[α(B_r)] and H_cJ[β(H_cJ)] for La-Co substituted Sr ferrites with x = 0.0–0.2^[62].

DownLoad: Full-Size Img PowerPoint

图 6 离子RE替代SrM铁氧体的(a)饱和磁化强度和(b)磁各向异性^[89]

Figure 6. (a) Saturation magnetization and (b) magnetic anisotropy of RE-substituted SrM^[89].

DownLoad: Full-Size Img PowerPoint

图 7 在四面体和八面体配位环境中晶体场分裂和Co²⁺ (3d⁷)的占据^[49]

Figure 7. Crystal field splitting and Co²⁺ (3d⁷) occupation in tetrahedral and octahedral coordination environments^[49].

DownLoad: Full-Size Img PowerPoint

图 8 对于Sr_1–xLa_xFe_12–yCo_yO₁₉, WDX测定的Co浓度y与La浓度x的比值(虚线分别代表x = y和y/x = 0.75)^[140], x > y样品中的La³⁺电荷补偿由Co²⁺和Fe²⁺完成

Figure 8. Ratio of Co concentration y to La concentration x determined by WDX for Sr_1–xLa_xFe_12–yCo_yO₁₉ (dashed lines represent x = y and y/x = 0.75, respectively) ^[140]. Charge compensation for La³⁺ in the sample x > y is accomplished by Co²⁺ and Fe²⁺.

DownLoad: Full-Size Img PowerPoint

图 9 Na₂O助熔剂法制备的(a) La-SrM和(b) La-Co SrM单晶的难、易轴磁化曲线^[140]; (c) (Na/Ca-)La-Co替代SrM系列样品在5 K下的磁各向异性场H_A随Co替代浓度的变化^{[140,142–145]}(图中直线帮助判断H_A增长趋势)

Figure 9. Hard- and easy-axis magnetization curves of (a) La-SrM and (b) La-Co SrM single crystals prepared by the Na₂O flux method^[140]; (c) variation of the magnetic anisotropy field H_A with the concentration of Co substitution for a series of samples of (Na/Ca-)La-Co substituted SrM at 5 K ^{[140,142–145]} (the straight line helps to determine the trend of the H_A growth).

DownLoad: Full-Size Img PowerPoint

图 10 (a) SrFe_12–xCo_xO₁₉在5 K下的磁各向异性场H_A随Co浓度x的变化, 与文献[140]中La-Co SrM单晶(蓝色方块)的数据进行对比, 高亮区域表明, 在该Co浓度范围内, Co-SrM的H_A高于La-Co SrM, 插图是Co-SrM和La-Co SrM晶格参数c/a比值; (b)所有样品H_A的温度依赖性^[151]

Figure 10. (a) Variation of the magnetic anisotropy field H_A of SrFe_12–xCo_xO₁₉ as a function of Co concentration x at 5 K, compared with data for La-Co SrM single crystals (blue squares) from the literature^[140]. The highlighted regions indicate that the H_A of Co-SrM is higher than that of La-Co SrM in this Co concentration range. And the inset is the ratio of the lattice parameters c/a for Co-SrM and La-Co SrM. (b) Temperature dependence of H_A for all samples^[151].

DownLoad: Full-Size Img PowerPoint

图 11 (a) (La, Co)_0.4共替代M型锶铁氧体单晶的零场⁵⁹Co NMR谱; (b)高频区放大的单晶⁵⁹Co NMR谐振S2和S3^[115]

Figure 11. (a) Zero-field ⁵⁹Co NMR spectrum of (La, Co)_0.4 substituted M-type ferrite single crystal; (b) amplified ⁵⁹Co NMR resonances S2 and S3 in the high-frequency region^[115].

DownLoad: Full-Size Img PowerPoint

图 12 La-Co SrM中Co的电荷和自旋态以及替代晶位的总结^[115], 说明了S1的两种情况, Co²⁺的主要替代晶位发生在(a)八面体4f₂晶位, (b)四面体4f₁晶位

Figure 12. Charge and spin states of Co in La-Co SrM and summary of alternative crystal sites^[115]. Two cases of S1 are illustrated: The main alternative sites for Co²⁺ occur in (a) the octahedral 4f₂, (b) the tetrahedral 4f₁.

DownLoad: Full-Size Img PowerPoint

图 13 Co浓度(y)对S1信号恢复场(H_r)的依赖性. 作为参考, 5 K时各向异性场H_A的Co浓度依赖性如红点所示. 插图为S2和S3的H_r^[116]

Figure 13. Dependence of Co concentration (y) on the recovery field (H_r) of S1signal. As a reference, the Co concentration dependence of the anisotropic field H_A at 5 K is shown in red dots. The insets show the H_r of S2 and S3^[116] .

DownLoad: Full-Size Img PowerPoint

图 14 当前La-Co SrM中Co占位的主流观点

Figure 14. Current view of Co occupnacy in La-Co SrM.

DownLoad: Full-Size Img PowerPoint

表 1 国内外永磁铁氧体产品的最高性能

Table 1. Top performance of domestic and international ferrite magnets.

公司	国家	牌号	B_r/mT	H_cb/(kA·m^–1)	H_cJ/(kA·m^–1)	(BH )_max/(kJ·m^–3)
TDK^[23]	日本	FB13B	475	340	380	44.0
TDK^[23]		FB14H	470	355	430	43.1
日立金属^[31]		NMF-15	480	342	382	44.0
横店东磁^[27]	中国	DM4748	460	328	368	41.5
北矿磁材^[28]		BMS-9.3	420	318	398	33.5
江益磁材^[29]		JPM-12B	450	310	350	38.2
龙磁科技^[30]		SM13N	450	278	298	38.1

DownLoad: CSV

表 2 磁铅石型铁氧体AFe₁₂O₁₉中A和Fe晶位的相对磁矩方向

Table 2. Relative magnetic moment orientations of A and Fe sites in AFe₁₂O₁₉.

元素	Wyckoff晶位	氧配位数	晶位形状	磁矩方向
A	2d	12	—	—
Fe	2a	6	八面体	↑
	2b	5	双锥体	↑
	4f₁	4	四面体	↓
	4f₂	6	八面体	↓
	12k	6	八面体	↑

DownLoad: CSV

表 3 各国研究者用不同测量方法关于La-Co SrM中Co占据晶位的研究结论(●: 肯定或很可能; ▲: 可能, 但值得怀疑)

Table 3. Conclusions of researchers from various countries on the occupation of crystalline sites by Co in La-Co SrM using different measurements (●: certain or very likely; ▲: possible, but doubtful).

样品	作者和年份	国家	检测方法	Co²⁺占位
样品	作者和年份	国家	检测方法	2a	2b	4f₁	4f₂	12k
多晶	Pieper等, 2002^[100]	澳大利亚	⁵⁷Fe-NMR			●	●
	Pieper等, 2002^[101]	澳大利亚	⁵⁷Fe, ¹³⁹La和 ⁵⁹Co-NMR			▲	●
	Moral等, 2002^[102]	法国	⁵⁷Fe-Mössbauer, Raman	●			●
	Le Breton等, 2002^[103]	法国	⁵⁷Fe-Mössbauer	●	▲		●
	Wiesinger等, 2002^[104]	澳大利亚	⁵⁷Fe-Mössbauer, ⁵⁷Fe和⁵⁹Co-NMR	●		▲	●
	Lechevallier等, 2003^[97]	法国	⁵⁷Fe-Mössbauer	●			●
	Lechevallier等, 2004^[105]	法国	⁵⁷Fe-Mössbauer	●			●
	Choi等, 2006^[106]	韩国	⁵⁷Fe-Mössbauer		●		●	●
	Kobayashi等, 2011^[107]	日本	Neutron Diffraction, EXAFS, XMCD	●		●		●
	Kouřil, 2013^[109]	捷克	⁵⁷Fe-NMR	●	▲	●	▲	▲
	Wu等, 2015^[110]	中国	Raman, XPS	●		●		●
	Ohtsuka等, 2016^[111]	日本	TEM-EDXS	●		●		●
	Mahadevan等, 2020^[112]	印度	⁵⁷Fe-Mössbauer, Raman	●	●		●
单晶	Nagasawa等, 2016^[113]	日本	⁵⁷Fe-Mössbauer			▲	▲
	Oura等, 2018^[114]		⁵⁷Fe-Mössbauer, XES	●		●
	Sakai等, 2018^[115]		⁵⁷Fe和⁵⁹Co-NMR	●		●		●
	Nakamura等, 2019^[116]		⁵⁹Co-NMR	●		●		●
	Nagasawa等, 2020^[117]		外场作用下的⁵⁷Fe-Mössbauer			●

DownLoad: CSV

表 4 (Na/Ca-)La-Co替代SrM系列样品在5 K下的磁各向异性场H_A

Table 4. Magnetic anisotropy field H_A at 5 K for (Na/Ca-)La-Co substituted SrM series samples.

样品	制备方法	替代浓度		5 K时的磁各向异性场 H_A/kOe
样品	制备方法	x	y	5 K时的磁各向异性场 H_A/kOe
Sr_1–xLa_xFe_12–yCo_yO₁₉^[140]	Na₂O助熔剂法生长的单晶	0	0	17.50
		0.055	0.032	17.22
		0.139	0.077	19.46
		0.242	0.108	18.62
		0.289	0.152	21.57
		0.367	0.212	24.36
		0.511	0.161	22.17
		0.472	0.266	25.57
Sr_1–xLa_xFe_12–yCo_yO₁₉^[142]	高氧压移动溶剂浮区法生长的单晶	0.2	0.2	21.77
Sr_1–xLa_xFe_12–yCo_yO₁₉^[142]	高氧压移动溶剂浮区法生长的单晶	0.4	0.4	27.96
Sr_1–xLa_xFe_12–yCo_yO₁₉^[143]	高氧压固相反应法合成的多晶	0.21	0.21	21.18
		0.30	0.30	21.76
		0.39	0.39	24.41
		0.41	0.41	27.06
		0.72	0.72	34.12
		0.93	0.93	42.35
		1.00	1.00	56.76
Ca_13–n–xLa_xFe_n–yCo_yO₁₉ (n = 11.87—11.93, 根据不同Co替代量而改变)^[144]	CaO助熔剂法生长的单晶	0.52	0.07	15.26
		0.52	0.10	17.35
		0.56	0.17	23.15
		0.48	0.16	25.65
		0.59	0.27	28.31
		0.37	0.17	26.89
		0.56	0.36	31.54
Na_axLa_xFe_n–yCo_yO₁₉ (a = 0.25—0.41, n = 11.84—11.97, 根据不同Co 替代量而改变)^[145]	Na₂O助熔剂法生长的单晶	0.82	0.12	25.72
		0.79	0.21	25.61
		0.83	0.31	29.61

DownLoad: CSV

表 5 通过中子衍射和Rietveld分析得到7个候选模型, 显示了Co的占据晶位^[107]

Table 5. Seven candidate models obtained by neutron diffraction and Ritveld analysis showing Co occupied sites^[107].

模型	2a	2b	4f₁	4f₂	12k
1	—	—	1.00	—	—
2	—	—	—	—	1.00
3	0.35	—	0.65	—	—
4	0.31	—	—	—	0.69
5	—	—	0.88	0.12	—
6	—	—	0.47	—	0.53
7	0.22	—	0.38	—	0.40

DownLoad: CSV

表 6 Co²⁺和Co³⁺的高、低自旋值, 其中给出了八面体、四面体和双锥体对称的低自旋值, 而其中具有$ {{\mathrm{e}}}_{{\mathrm{g}}}^{4}{{\mathrm{t}}}_{2{\mathrm{g}}}^{3} $构型的四面体Co²⁺只有S = 3/2的单自旋态

Table 6. High and low spin values of Co²⁺ and Co³⁺. The low spin values of octahedral, tetrahedral and bipyramidal symmetries are given, where the tetrahedron Co²⁺ with $ {{\mathrm{e}}}_{{\mathrm{g}}}^{4}{{\mathrm{t}}}_{2{\mathrm{g}}}^{3} $ configuration has only S = 3/2 single spin states.

类别	高自旋	低自旋
类别	高自旋	八面体	四面体	双锥体
Co²⁺(d⁷)	3/2	1/2	—	1/2
Co³⁺(d⁶)	2	0	1	1

DownLoad: CSV

表 7 Sr_1–xLa_xFe_12–yCo_yO₁₉ (x = 0.289, y = 0.152)的⁵⁹Co共振^[155]

Table 7. ⁵⁹Co resonances of Sr_1–xLa_xFe_12–yCo_yO₁₉ (x = 0.289, y = 0.152)^[155].

记号	中心频率/MHz	局域场大小/T	相对丰度
S1	86	8.6	0.73
S2	307	30.6	0.16
S3	386	38.5	0.11
S4	529	52.7	＜0.002

DownLoad: CSV

[1]	Went J, Rathenau G, Gorter E, Van Oosterhout G 1952 Phy. Rev. 86 424 Google Scholar
[2]	Went J J, Rathenau G W, Gorter E W, Oosterhout G W V 1952 Philips Tech. Rev. 13 194
[3]	Granados-Miralles C, Jenuš P 2021 J. Phys. D Appl. Phys. 54 303001 Google Scholar
[4]	Coey J M D 2002 J. Magn. Magn. Mater. 248 441 Google Scholar
[5]	Pullar R C 2012 Prog. Mater. Sci. 57 1191 Google Scholar
[6]	Gutfleisch O, Willard M A, Bruck E, Chen C H, Sankar S G, Liu J P 2011 Adv. Mater. 23 821 Google Scholar
[7]	de Julian Fernandez C, Sangregorio C, de la Figuera J, Belec B, Makovec D, Quesada A 2020 J. Phys. D Appl. Phys. 54 153001 Google Scholar
[8]	Bollero A, Rial J, Villanueva M, Golasinski K M, Seoane A, Almunia J, Altimira R 2017 ACS Sustain. Chem. Eng. 5 3243 Google Scholar
[9]	Iida K, Minachi Y, Masuzawa K, Kawakami M, Nishio H, Taguchi H 1999 J. Magn. Soc. Jpn. 23 1093 Google Scholar
[10]	Coey J M 2014 J. Phys. Condens. Matter 26 064211 Google Scholar
[11]	Cochardt A 1966 J. Appl. Phys. 37 1112 Google Scholar
[12]	Taguchi H 1998 KONA Powder Part. J. 16 116 Google Scholar
[13]	Goldman A 2006 Modern Ferrite Technology (New York: Springer Science & Business Media
[14]	Went J 1952 Philips Tech. Rev. 13 361
[15]	Stuijts A, Rathenau G, Weber G 1954 Philips Tech. Rev. 16 209
[16]	Deshpande U S 2003 IEEE International Electric Machines and Drives Conference IEMDC'03 Madison, WI, USA, June 1-4, 2003 p509
[17]	Chen C H, Yi P 2014 Proceedings of 2014 International Conference on NdFeB Magnets: Supply Chain, Critical Properties, & Applications Ningbo, China, March 2−5, 2014 p126
[18]	Tech-Mag T https://www.tdk.com/en/tech-mag/ferrite02/012#section3 [2021-12-3]
[19]	Coey J M D 2020 Engineering 6 119 Google Scholar
[20]	Bollero A, Palmero E M 2022 Modern Permanent Magnets Chapter 3-Recent Advances in Hard-Ferrite Magnets ( Woodhead Publishing
[21]	TDK https://product.tdk.com/en/system/files?file=dam/doc/product/magnet/magnet/ferrite/datasheets/magnet_fb_summary_en.pdf [2021-12-3]
[22]	Hitachi Metals L http://www.hitachi-metals.co.jp/e/products/auto/el/p03_01_g.html [2021-12-3]
[23]	TDK Ferrite Magnets Catalog https://product.tdk.com/en/products/magnet/magnet/ferrite/index.html [2021-12-3]
[24]	翁兴园 2021 新材料产业 4 32 Google Scholar Weng X Y 2021 Adv. Mater. Indus. 4 32 Google Scholar
[25]	华经产业研究 https://baijiahao.baidu.com/s?id=1749074365467103880&wfr=spider&for=pc [2023-2-13]
[26]	陈羽峰, 徐斌 2022 磁性材料及器件 54 108 Google Scholar Chen Y F, Xu B 2022 J. Mag. Mater. Dev. 54 108 Google Scholar
[27]	横店东磁磁性产品 http://www.chinadmegc.com/product/1.html [2024-1-28]
[28]	北矿磁材科技有限公司-烧结永磁铁氧体磁粉(BGRIMM Magnetic Materials & Technology Co. , Ltd) http://www.magmat.com/cpysc/yctytcf/index.htm [2022-11-15]
[29]	江益磁材湿式异方性铁氧体永磁产品结构http://www.jpmf.com.cn/displayproduct.html?id=3806471777899840 [2022-11-15]
[30]	安徽龙磁科技股份有限公司永磁铁氧体磁性能牌号表https://www.sinomagtech.com/cpzx/yctyt/ [2024-1-28]
[31]	Hitachi catalogue http://www.hitachi-metals.co.jp/e/products/auto/el/p03_05.html [2022-11-15]
[32]	翁兴园 2013 新材料产业 4 31 Google Scholar Weng X Y 2013 Adv. Mater. Indus. 4 31 Google Scholar
[33]	Smit B J, Wijn H P 1959 Ferrites, Philips Technical Library (The Netherlands: Eindhoven
[34]	Aminoff G 1925 Geologiska Fö reningen i Stockholm Fö rhandlingar 47 283 Google Scholar
[35]	Adelsköld V 1938 Arkiv. Kemi. Min. Geol. 12a 1
[36]	Harris V G, Geiler A, Chen Y, Yoon S D, Wu M, Yang A, Chen Z, He P, Parimi P V, Zuo X, Patton C E, Abe M, Acher O, Vittoria C 2009 J. Magn. Magn. Mater. 321 2035 Google Scholar
[37]	Kojima H 1982 Handb. Ferromagn. Mater. 3 305 Google Scholar
[38]	Kreisel J, Vincent H, Tasset F, Paté M, Ganne J P 2001 J. Magn. Magn. Mater. 224 17 Google Scholar
[39]	Townes W, Fang J, Perrotta A 1967 Z. Krist. -Cryst. Mater. 125 437 Google Scholar
[40]	Braun P B 1957 Philips Res. Rep. 12 491
[41]	Bilovol V, Martínez-García R 2015 J. Phy. Chem. Solids 86 131 Google Scholar
[42]	Harris V G 2012 IEEE T. Magn. 48 1075 Google Scholar
[43]	Cullity B D, Graham C D 2011 Introduction to Magnetic Materials (Hoboken: John Wiley & Sons
[44]	Jahn L, Müller H G 1969 Phys. Status Solidi B 35 723 Google Scholar
[45]	Coey J M 2010 Magnetism and Magnetic Materials (Cambridge: Cambridge University Press
[46]	Stäblein H 1982 Handb. Ferromagn. Mater. 3 441 Google Scholar
[47]	Cui J, Kramer M, Zhou L, Liu F, Gabay A, Hadjipanayis G, Balasubramanian B, Sellmyer D 2018 Acta Mater. 158 118 Google Scholar
[48]	Selvaraj S, Gandhi U, Berchmans L J, Mangalanathan U 2021 Mater. Tech. 36 36 Google Scholar
[49]	Waki T 2022 J. Jpn. Soc. Powder Powder Metall. 69 149 (in Japanese Google Scholar
[50]	Mahmood S H, Abu-Aljarayesh I 2016 Hexaferrite Permanent Magnetic Materials (Materials Research Forum LLC
[51]	Lisjak D, Mertelj A 2018 Prog. Mater. Sci. 95 286 Google Scholar
[52]	任延英, 李雅宁, 柳洪盛, 徐楠, 郭坤, 徐朝辉, 陈鑫, 高峻峰 2024 物理学报 73 066104 Google Scholar Ren Y Y, Li Y N, Liu H S, Xu N, Guo K, Xu Z H, Chen X, Gao J F 2024 Acta Phys. Sin. 73 066104 Google Scholar
[53]	Rhein F, Helbig T, Neu V, Krispin M, Gutfleisch O 2018 Acta Mater. 146 85 Google Scholar
[54]	Trukhanov A V, Kostishyn V G, Panina L V, Jabarov S H, Korovushkin V V, Trukhanov S V, Trukhanova E L 2017 Ceram. Int. 43 12822 Google Scholar
[55]	Trukhanov S V, Trukhanov A V, Turchenko V A, Kostishyn V G, Panina L V, Kazakevich I S, Balagurov A M 2016 J. Alloy Compd. 689 383 Google Scholar
[56]	Li J, Hong Y, He S, Li W K, Bai H, Xia Y H, Sun G A, Zhou Z X 2022 J. Adv. Ceram. 11 263 Google Scholar
[57]	Nguyen H H, Jeong W H, Phan T L, Lee B W, Yang D S, Tran N, Dang N T 2021 J. Magn. Magn. Mater. 537 168195 Google Scholar
[58]	Albanese G, Deriu A 1979 Ceram. Int. 5 3 Google Scholar
[59]	Dionne G F 2009 Magnetic Oxides (New York: Springer
[60]	Summergrad R N, Banks E 1957 J. Phys. Chem. Solids 2 312 Google Scholar
[61]	Le Roux D, Vincent H, Joubert J C, Vallet-Regi M 1988 Mater. Res. Bull. 23 299 Google Scholar
[62]	Ogata Y, Kubota Y, Takami T, Tokunaga M, Shinokara T 1999 IEEE T. Magn. 35 3334 Google Scholar
[63]	Tenaud P, Morel A, Kools F, Le Breton J M, Lechevallier L 2004 J. Alloy Compd. 370 331 Google Scholar
[64]	Kools F, Morel A, Grössinger R, Le Breton J M, Tenaud P 2002 J. Magn. Magn. Mater. 242-245 1270 Google Scholar
[65]	Nishio H, Minachi Y, Yamamoto H 2009 IEEE T. Magn. 45 5281 Google Scholar
[66]	Kikuchi T, Nakamura T, Yamasaki T, Nakanishi M, Fujii T, Takada J, Ikeda Y 2010 J. Magn. Magn. Mater. 322 2381 Google Scholar
[67]	Nishio H, Yamamoto H 2011 IEEE T. Magn. 47 3641 Google Scholar
[68]	Kobayashi Y, Hosokawa S, Oda E, Toyota S 2008 J. Jpn. Soc. Powder Powder Metall. 55 541 Google Scholar
[69]	Du Y B, Liu Y, Lian L X, Du J 2019 J. Magn. Magn. Mater. 469 189 Google Scholar
[70]	Chen Z, Wang F, Yan S, Nie Y, Feng Z, Chen Y, Harris V G, Zhang S 2014 J. Am. Ceram. Soc. 97 1873 Google Scholar
[71]	Chen Z, Wang F, Yan S, Feng Z 2014 Mat. Sci. Eng. B 182 69 Google Scholar
[72]	Zhu D, Geng Z, Liu R S, Zhou X, Jia L, Hu G, Wang Q, Li B 2020 Rare Metals 39 89 Google Scholar
[73]	Li X, Yang W G, Bao D X, Meng X D, Lou B Y 2013 J. Magn. Magn. Mater. 329 1 Google Scholar
[74]	Huang X, Liu X S, Yang Y J, Huang K, Niu X F, Jin D L, Gao S, Ma Y Q, Huang F, Lv F R, Feng S J 2015 J. Magn. Magn. Mater. 378 424 Google Scholar
[75]	Yang Y J, Wang F H, Shao J X, Huang D H, Liu X X, Feng S J, Wen C E 2015 J. Magn. Magn. Mater. 384 64 Google Scholar
[76]	Kang Y M, Moon K S 2015 Ceram. Int. 41 12828 Google Scholar
[77]	Lotgering F K 1974 J. Phys. Chem. Solids 35 1633 Google Scholar
[78]	Deschamps A, Bertaut F 1957 Compt. Rend. 244 3069
[79]	Wang J F, Ponton C B, Harris I R 2001 J. Magn. Magn. Mater. 234 233 Google Scholar
[80]	Lechevallier L, Le Breton J M, Wang J F, Harris I R 2004 J. Magn. Magn. Mater. 269 192 Google Scholar
[81]	Wang J F, Ponton C B, Grössinger R, Harris I R 2004 J. Alloys Compd. 369 170 Google Scholar
[82]	Sharma P, Verma A, Sidhu R K, Pandey O P 2003 J. Alloys Compd. 361 257 Google Scholar
[83]	Grossinger R, Kupferling M, Tellez Blanco J C, Wiesinger G, Muller M, Hilscher G, Pieper M W, Wang J F, Harris I R 2003 IEEE T. Magn. 39 2911 Google Scholar
[84]	Mocuta H, Lechevallier L, Le Breton J M, Wang J F, Harris I R 2004 J. Alloys Compd. 364 48 Google Scholar
[85]	Wang J F, Ponton C B, Harris I R 2005 J. Alloys Compd. 403 104 Google Scholar
[86]	Ounnunkad S 2006 Solid State Commun. 138 472 Google Scholar
[87]	Litsardakis G, Manolakis I, Efthimiadis K 2007 J. Alloys Compd. 427 194 Google Scholar
[88]	Lechevallier L, Le Breton J M, Morel A, Tenaud P 2008 J. Phys. Condens. Mat. 20 175203 Google Scholar
[89]	Seifert D, Töpfer J, Stadelbauer M, Grössinger R, Le Breton J M 2011 J. Am. Ceram. Soc. 94 2109 Google Scholar
[90]	Waki T, Inoue G, Tabata Y, Nakamura H 2020 IEEE T. Magn. 56 6702304 Google Scholar
[91]	Lucchini E, Slokar G 1980 J. Magn. Magn. Mater. 21 93 Google Scholar
[92]	Blanco A M, Gonzalez C 1991 J. Phys. D Appl. Phys. 24 612 Google Scholar
[93]	Lechevallier L, Le Breton J M, Morel A, Tenaud P 2007 J. Magn. Magn. Mater. 316 e109 Google Scholar
[94]	Chlan V, Kouřil K, Uličná K, Štěpánková H, Töpfer J, Seifert D 2015 Phys. Rev. B 92 125125 Google Scholar
[95]	Sauer C, Köbler U, Zinn W, Stäblein H 1978 J. Phys. Chem. Solids 39 1197 Google Scholar
[96]	Le Breton J M, Seifert D, Töpfer J, Lechevallier L 2015 Physica B 470 33 Google Scholar
[97]	Lechevallier L, Le Breton J M, Teillet J, Morel A, Kools F, Tenaud P 2003 Physica B 327 135 Google Scholar
[98]	Graetsch H, Leckebusch R, Sahl K, Haberey F, Rosenberg M S 1984 IEEE T. Magn. 20 495 Google Scholar
[99]	Lee H B, Chun S H, Shin K W, Jeon B G, Chai Y S, Kim K H, Schefer J, Chang H, Yun S N, Joung T Y, Chung J H 2012 Phys. Rev. B 86 094435 Google Scholar
[100]	Pieper M W, Morel A, Kools F 2002 J. Magn. Magn. Mater. 242-245 1408 Google Scholar
[101]	Pieper M W, Kools F, Morel A 2002 Phys. Rev. B 65 184402 Google Scholar
[102]	Morel A, Le Breton J M, Kreisel J, Wiesinger G, Kools F, Tenaud P 2002 J. Magn. Magn. Mater. 242-245 1405 Google Scholar
[103]	Le Breton J M, Teillet J, Wiesinger G, Morel A, Kools F, Tenaud P 2002 IEEE T. Magn. 38 2952 Google Scholar
[104]	Wiesinger G, Mller M, Grssinger R, Pieper M, Morel A, Kools F, Tenaud P, Le Breton J M, Kreisel J 2002 Phys. Status Solidi A 189 499 Google Scholar
[105]	Lechevallier L, Le Breton J M, Wang J F, Harris I R 2004 J. Phys. Condens. Mat. 16 5359 Google Scholar
[106]	Choi D H, Lee S W, Shim I B, Kim C S 2006 J. Magn. Magn. Mater. 304 e243 Google Scholar
[107]	Kobayashi Y, Oda E, Nishiuchi T, Nakagawa T 2011 J. Ceram. Soc. Jpn. 119 285 Google Scholar
[108]	Langhof N, Göbbels M 2009 J. Solid State Chem. 182 2725 Google Scholar
[109]	Kouřil K 2013 Ph. D. Dissertation (Prague: Charles University
[110]	Wu C J, Yu Z, Yang Y, Sun K, Guo R D, Jiang X N, Lan Z W 2015 J. Appl. Phys. 118 103907 Google Scholar
[111]	Ohtsuka M, Muto S, Tatsumi K, Kobayashi Y, Kawata T 2016 Microscopy 65 127 Google Scholar
[112]	Mahadevan S, Sathe V, Raghavendra Reddy V, Sharma P 2020 IEEE T. Magn. 56 1800106 Google Scholar
[113]	Nagasawa N, Ikeda S, Shimoda A, Waki T, Tabata Y, Nakamura H, Kobayashi H 2016 Hyperfine Interact. 237 39 Google Scholar
[114]	Oura M, Nagasawa N, Ikeda S, Shimoda A, Waki T, Tabata Y, Nakamura H, Hiraoka N, Kobayashi H 2018 J. Appl. Phys. 123 033907 Google Scholar
[115]	Sakai H, Hattori T, Tokunaga Y, Kambe S, Ueda H, Tanioku Y, Michioka C, Yoshimura K, Takao K, Shimoda A, Waki T, Tabata Y, Nakamura H 2018 Phys. Rev. B 98 064403 Google Scholar
[116]	Nakamura H, Waki T, Tabata Y, Mény C 2019 J. Phys. Mater. 2 015007 Google Scholar
[117]	Nagasawa N, Oura M, Ikeda S, Waki T, Tabata Y, Nakamura H, Kobayashi H 2020 J. Appl. Phys. 128 133901 Google Scholar
[118]	Balbashov A M, Egorov S K 1981 J. Cryst. Growth 52 498 Google Scholar
[119]	Morishita H, Amano A, Ueda H, Michioka C, Yoshimura K 2014 J. Jpn. Soc. Powder Powder Metall. 61 S64 Google Scholar
[120]	Gambino R J, Leonhard F 1961 J. Am. Ceram. Soc. 44 221 Google Scholar
[121]	Shirk B T, Buessem W R 1969 J. Appl. Phys. 40 1294 Google Scholar
[122]	Goto Y, Takahashi K 1972 J. Ceram. Soc. Jpn. 80 358 Google Scholar
[123]	Obradors X, Solans X, Collomb A, Samaras D, Rodriguez J, Pernet M, Font-Altaba M 1988 J. Solid State Chem. 72 218 Google Scholar
[124]	Vinnik D A, Tarasova A Y, Zherebtsov D A, Gudkova S A, Galimov D M, Zhivulin V E, Trofimov E A, Nemrava S, Perov N S, Isaenko L I, Niewa R 2017 Materials 10 578 Google Scholar
[125]	Vinnik D A, Gudkova S A, Zherebtsov D A, Trofimov E A, Mashkovtseva L S, Trukhanov A V, Trukhanov S V, Nemrava S, Blaschkowski B, Niewa R 2019 J. Magn. Magn. Mater. 470 97 Google Scholar
[126]	Vincent H, Sugg B, Lefez V, Bochu B, Boursier D, Chaudouet P 1991 J. Magn. Magn. Mater. 101 170 Google Scholar
[127]	Takaoka H, Suito H 1994 J. Cryst. Growth 137 493 Google Scholar
[128]	Eraky M R, Beslepkin A A, Kuntsevich S P 2003 Mater. Lett. 57 3427 Google Scholar
[129]	Jalli J, Yang-Ki H, Sung-Hoon G, Seok B, Jaejin L, Sur J C, Abo G S, Lyle A, Sung-Ik L, Hwachol L, Mewes T 2008 IEEE T. Magn. 44 2978 Google Scholar
[130]	Pavlova S G, Balbashov A M, Rybina L N 2012 J. Cryst. Growth 351 161 Google Scholar
[131]	Vinnik D A, Zherebtsov D A, Mashkovtseva L S, Nemrava S, Semisalova A S, Galimov D M, Gudkova S A, Chumanov I V, Isaenko L I, Niewa R 2015 J. Alloys Compd. 628 480 Google Scholar
[132]	Shlyk L, Vinnik D A, Zherebtsov D A, Hu Z, Kuo C Y, Chang C F, Lin H J, Yang L Y, Semisalova A S, Perov N S, Langer T, Pöttgen R, Nemrava S, Niewa R 2015 Solid State Sci. 50 23 Google Scholar
[133]	Vinnik D A, Tarasova A Y, Zherebtsov D A, et al. 2015 Ceram. Int. 41 9172 Google Scholar
[134]	Vinnik D A, Zherebtsov D A, Mashkovtseva L S, et al. 2015 Mater. Chem. Phys. 155 99 Google Scholar
[135]	Vinnik D A, Semisalova A S, Mashkovtseva L S, Yakushechkina A K, Nemrava S, Gudkova S A, Zherebtsov D A, Perov N S, Isaenko L I, Niewa R 2015 Mater. Chem. Phys. 163 416 Google Scholar
[136]	Gudkova S A, Vinnik D A, Zhivulin V E, et al. 2019 J. Magn. Magn. Mater. 470 101 Google Scholar
[137]	Hassner M, Vinnik D A, Niewa R 2020 Materials 13 858 Google Scholar
[138]	Vinnik D A, Prosvirin I P, Zhivulin V E, et al. 2020 J. Alloys Compd. 844 156036 Google Scholar
[139]	Zhivulin V E, Trofimov E A, Zaitseva O V, Zherebtsov D A, Uchaev D A, Vinnik D A 2020 Crystals 10 264 Google Scholar
[140]	Shimoda A, Takao K, Uji K, Waki T, Tabata Y, Nakamura H 2016 J. Solid State Chem. 239 153 Google Scholar
[141]	Liu R S, Wang L C, Xu Z, Qin C, Li Z, Yu X, Liu D, Gong H, Zhao T Y, Sun J, Hu F, Shen B G 2022 Mater. Today Commun. 32 103996 Google Scholar
[142]	Ueda H, Tanioku Y, Michioka C, Yoshimura K 2017 Phys. Rev. B 95 224421 Google Scholar
[143]	Waki T, Okazaki S, Tabata Y, Kato M, Hirota K, Nakamura H 2018 Mater. Res. Bull. 104 87 Google Scholar
[144]	Waki T, Uji K, Tabata Y, Nakamura H 2019 J Solid State Chem. 270 366 Google Scholar
[145]	Waki T, Takao K, Tabata Y, Nakamura H 2020 J. Solid State Chem. 282 121071 Google Scholar
[146]	Waki T, Hani K, Tabata Y, Nakamura H 2023 Mater. Trans. 64 564 Google Scholar
[147]	Küpferling M, Novák P, Knížek K, Pieper M W, Grössinger R, Wiesinger G, Reissner M 2005 J. Appl. Phys. 97 10 Google Scholar
[148]	Küpferling M, Grössinger R, Pieper M W, et al. 2006 Phys. Rev. B 73 144408 Google Scholar
[149]	Komabuchi M, Urushihara D, Kimata Y, Okabe M, Asaka T, Fukuda K 2019 Phys. Rev. B 100 094406 Google Scholar
[150]	Komabuchi M, Urushihara D, Kimata Y, Okabe M, Asaka T, Fukuda K, Nakano K, Yamamoto K 2020 J. Magn. Magn. Mater. 498 166115 Google Scholar
[151]	Liu R S, Wang L C, Yu X, Xu Z, Gong H, Zhao T Y, Hu F, Shen B G 2023 Ceram. Int. 49 1888 Google Scholar
[152]	Williams J M, Adetunji J, Gregori M 2000 J. Magn. Magn. Mater. 220 124 Google Scholar
[153]	Kobayashi Y, Oda E, Nakagawa T, Nishiuchi T 2016 J. Jpn. Soc. Powder Powder Metall. 63 101 Google Scholar
[154]	Kobayashi Y, Oda E, Kawata T, Nakagawa T 2017 Hitachi Metal Tech. Rev. 33 34 (in Japanese
[155]	Nakamura H, Shimoda A, Waki T, Tabata Y, Meny C 2016 J. Phys. Condens Mat. 28 346002 Google Scholar
[156]	Nishikubo T, Motizuki K 1962 J. Phys. Soc. Jpn. 17 871 Google Scholar
[157]	Tsuda T, Okada K, Yasuoka H 1974 J. Phys. Soc. Jpn. 37 1713 Google Scholar
[158]	Jung H, Lee S J, Song M, Lee S, Lee H J, Kim D H, Kang J S, Zhang C L, Cheong S W 2009 New J. Phys. 11 043008 Google Scholar
[159]	Miyatani K, Kohn K, Kamimura H, Iida S 1966 J. Phys. Soc. Jpn. 21 464 Google Scholar
[160]	Itoh M, Nawata Y, Kiyama T, Akahoshi D, Fujiwara N, Ueda Y 2003 Physica B 329 751 Google Scholar
[161]	Ghoshray A, Bandyopadhyay B, Ghoshray K, Morchshakov V, Bärner K, Troyanchuk I O, Nakamura H, Kohara T, Liu G Y, Rao G H 2004 Phys. Rev. B 69 064424 Google Scholar
[162]	Julien M H, de Vaulx C, Mayaffre H, et al. 2008 Phys. Rev. Let. 100 096405 Google Scholar
[163]	Park J, Hong Y K, Lee W, Choi B C, Choi C J 2016 IEEE Magn. Lett. 7 5500403 Google Scholar
[164]	Dixit V, Kim S G, Park J, Hong Y K 2017 AIP Adv. 7 115209 Google Scholar
[165]	Hui Y J, Cheng W M, Lin G Q, Miao X S 2014 IEEE T. Magn. 50 2800904 Google Scholar
[166]	Hou Y H, Chen X, Guo X L, Li W, Huang Y L, Tao X M 2021 J. Magn. Magn. Mater. 538 168257 Google Scholar
[167]	Ravindran P, Delin A, James P, Johansson B, Wills J, Ahuja R, Eriksson O 1999 Phys. Rev. B 59 15680 Google Scholar
[168]	Feng M, Shao B, Wu J, Zuo X 2013 J. Appl. Phys. 113 17D909 Google Scholar
[169]	Ahn K, Ryu B, Korolev D, Jae Kang Y 2013 Appl. Phys. Lett. 103 242417 Google Scholar
[170]	Halilov S, Perlov A Y, Oppeneer P, Yaresko A, Antonov V 1998 Phys. Rev. B 57 9557 Google Scholar
[171]	Wang G Y, Yang K, Ma Y Z H, Liu L, Lu D, Zhou Y X, Wu H 2023 Chin. Phys. Lett. 40 077301 Google Scholar
[172]	蒋有为 2020 硕士学位论文 (成都: 电子科技大学) Jiang Y W 2020 M. S. Thesis (Chengdu: University of Electronic Science and Technology of China
[173]	Inoue J, Onoda H, Yanagihara H 2020 J. Phys. D Appl. Phys. 53 195003 Google Scholar
[174]	Inoue J, Nakamura H, Yanagihara H 2019 T. Magn. Soc. Jpn. (Special Issues) 3 12 Google Scholar
[175]	Silva L M, da Silva R B, Silva R L, et al. 2022 Ceram. Int. 48 23224 Google Scholar

[1]	Ju Hai-Lang, Xiang Ping-Ping, Wang Wei, Li Bao-He. Enhancement of perpendicular magnetic anisotropy and thermal stability in Co/Ni multilayers by MgO/Pt interfaces. Acta Physica Sinica, 2015, 64(19): 197501. doi: 10.7498/aps.64.197501
[2]	Ju Hai-Lang, Li Bao-He, Wu Zhi-Fang, Zhang Fan, Liu Shuai, Yu Guang-Hua. Perpendicular magnetic anisotropy in Co/Ni multilayers studied by anomalous Hall effect. Acta Physica Sinica, 2015, 64(9): 097501. doi: 10.7498/aps.64.097501
[3]	Hao Yan-Ming, Wang Ling-Ling, Yan Da-Li, An Li-Qun. Structure and magnetic properties of Sm2Fe17-xCrxcompound prepared by arc melting. Acta Physica Sinica, 2009, 58(10): 7222-7226. doi: 10.7498/aps.58.7222
[4]	Guo Yu-Xian, Wang Jie, Xu Peng-Shou, Li Hong-Hong, Cai Jian-Wang. Element-specific in-plane magnetic anisotropy in Co0.9Fe0.1 films. Acta Physica Sinica, 2007, 56(2): 1121-1126. doi: 10.7498/aps.56.1121
[5]	Wang Wen-Quan, Xu Shi-Feng, Xu Qin-Ying, Zhang Wen-Liang, Chen Dong-Feng. Structure and magnetic properties of (Nd1－xGdx)3 Fe27.31Ti1.69 compounds. Acta Physica Sinica, 2006, 55(7): 3531-3535. doi: 10.7498/aps.55.3531
[6]	Luo Hong-Zhi, Jia Lin, Li Yang-Xian, Meng Fan-Bin, Shen Jiang, Chen Nan-Xian, Wu Guang-Heng, Yang Fu-Ming. Structure and magnetic properties of (Nd1－xErx)3Fe25Cr4.0 compounds. Acta Physica Sinica, 2005, 54(5): 2176-2182. doi: 10.7498/aps.54.2176
[7]	Guo Guang-Hua, Zhang Hai-Bei. Magnetocrystalline anisotropy and spin-reorientation transition of intermetallic compound HoMn6Sn6. Acta Physica Sinica, 2005, 54(12): 5879-5883. doi: 10.7498/aps.54.5879
[8]	Du Jun, Sun Liang, Sheng Wen-Ting, You Biao, Lu Mu, Hu An, M. M. Corte-Real, J. Q. Xiao. In-plane ferromagnetic resonance in nano-composite Fe-R-O（R=Hf Nd Dy）films. Acta Physica Sinica, 2004, 53(7): 2352-2356. doi: 10.7498/aps.53.2352
[9]	Wang Wen-Quan, Yan Yu, Wang Xiang-Qun, Wang Xue-Feng, Jin Han-Min. Structural and magnetic properties of (Nd1-xErx)3Fe273Ti17 compounds. Acta Physica Sinica, 2003, 52(3): 641-646. doi: 10.7498/aps.52.641
[10]	Wang Wen-Quan, Yan Yu, Wang Xue-Feng, Su Feng, Wang Xiang-Qun, Jin Han-Min. Structural and magnetic properties of RCo12-xTix(R=Y and Sm) compounds. Acta Physica Sinica, 2003, 52(1): 150-155. doi: 10.7498/aps.52.150
[11]	Wang Wen-Quan, Yan Yu, Wang Xiang-Qun, Wang Xue-Feng, Su Feng, Jin Han-Min. Structural and magnetic properties of Gd3 Co29-xCrx compounds. Acta Physica Sinica, 2003, 52(3): 647-651. doi: 10.7498/aps.52.647
[12]	Liu Xian-Song, Zhong Wei, Yang Sen, Jiang Hong-Ying, Gu Ben-Xi, Du You-Wei. . Acta Physica Sinica, 2002, 51(5): 1128-1132. doi: 10.7498/aps.51.1128
[13]	Li An-Hua, Dong Sheng-Zhi, Li Wei. . Acta Physica Sinica, 2002, 51(10): 2320-2324. doi: 10.7498/aps.51.2320
[14]	Feng Quan-Yuan. . Acta Physica Sinica, 2002, 51(11): 2612-2616. doi: 10.7498/aps.51.2612
[15]	Wang Wei, Zhang Xi-Juan, Yang Cui-Hong, Cheng Hai-Ying. ＴｈｅｍａｇｎｅｔｏｃｒｙｓｔａｌｌｉｎｅａｎｉｓｏｔｒｏｐｙｏｆＥｒ3 Ｇａ5Ｏ1 2ｕｎｄｅｒｈｉｇｈｍａｇｎｅｔｉｃｆｉｅｌｄ. Acta Physica Sinica, 2002, 51(12): 2846-2848. doi: 10.7498/aps.51.2846
[16]	WANG WEN-QUAN, WANG JIAN-LI, TANG NING, BAO FU-QUAN, WU GUANG-HENG, YANG FU-MING, JIN HAN-MIN. FORMATION AND STRUCTURE OF 3∶29-TYPE GdGd3(Fe1-xCox)29-yCry COMPOUNDS. Acta Physica Sinica, 2001, 50(8): 1534-1539. doi: 10.7498/aps.50.1534
[17]	WANG WEN-QUAN, WANG JIAN-LI, TANG NING, BAO FU-QUAN, WU GUANG-HENG, YANG FU-MING, JIN HAN-MIN. Sm-Co-Ti PHASE DIAGRAM AND STRUCTURAL AND MAGNETIC PROPERTIES OF SOME SINGLE-PHASE COMPOUNDS. Acta Physica Sinica, 2001, 50(4): 752-757. doi: 10.7498/aps.50.752
[18]	. . Acta Physica Sinica, 2000, 49(2): 355-360. doi: 10.7498/aps.49.355
[19]	GUAN PENG, LIU YI-HUA, GUO YI-CHENG. INDUCED ANISOTROPY IN Co-Zr AMORPHOUS FILMS. Acta Physica Sinica, 1989, 38(12): 2029-2033. doi: 10.7498/aps.38.2029
[20]	XU YOU, YANG GUI-LIN, CAI HENG, ZHAI HONG-RU. THE MAGNET OCRYSTALLINE AN1SOTROPY OF W-TYPE HEXAGONAL FERR1TES. Acta Physica Sinica, 1985, 34(7): 901-907. doi: 10.7498/aps.34.901

Catalog

Vol. 73, Issue 12 - 2024-06-20

Metrics

Abstract views: 2178
PDF Downloads: 128