研究了T*相超导体(Bi,Sr)2(Y,Ce)2Cu2Oy的成相规律,发现缓冷对T*相单相样品的制备是有利的.淬火样品的主相物质为Ce2Y2O7,完全不含T*相结构.在室温到熔化温度的范围,热分析未观察到结构相变.在240—460℃,相对每个Cu原子超导体失氧约0.1个氧.氧气中烧结并缓冷到室温的样品在30K出现零电阻现象The optimal synthesis of T* phase superconductors(Bi0.5Sr1.5)(Y,Ce)2Cu2Oy was studied in detail. Slow cooling was required for preparation of single phase T*-type compounds. After quenching,the samples contained Ce2Y2O7 as the major phase without T* structure presented. From room temperature to 1000℃ phase transition was not observed by thermal analysis. Upon slow cooling in oxygen, T*-type cuprates exhibited zero resistance at 30K.