10}<1120> (<a>型)滑移起主导作用; 随着塑性形变量的增加, 锥面滑移的作用增强, 且锥面{1011}<1123> (<c+a>型)滑移的作用大于柱面{1010}<1120> (<a>型)滑移, 少量的锥面{1011}<1120> (<a>型)和{1012}<1120> (<a>型)滑移也存在."/>         10}<1120> (<a> type) slip dominates; however, as the plastic strain is increased, the percentage of pyramidal {1011}<1123> (<c+a> type) slip becomes larger than that of prismatic {1010}<1120> (<a> type) slip, and the pyramidal {1011}<1120> (<a> type) slip and pyramidal {1012}<1120> (<a> type) slip may exist."/>     Zr-4合金压缩形变行为的研究
物理学报
引用检索 快速检索
物理学报  2014, Vol. 63 Issue (23): 236101     doi:10.7498/aps.63.236101
凝聚物质:结构、力学和热学性质 当期目录| 过刊浏览| 高级检索     
Zr-4合金压缩形变行为的研究
李洪佳, 孙光爱, 龚建, 陈波, 王虹, 李建, 庞蓓蓓, 张莹, 彭述明
中国工程物理研究院核物理与化学研究所, 绵阳 621999
Deformation behaviors of zircaloy-4 alloy under uniaxial compression
Li Hong-Jia, Sun Guang-Ai, Gong Jian, Chen Bo, Wang Hong, Li Jian, Pang Bei-Bei, Zhang Ying, Peng Shu-Ming
Institute of Nuclear Physics and Chemistry, China Academy of Engineering Physics, Mianyang 621999, China