Structure and luminescence properties of Li2Gd4(MoO4)7:Sm3+ orange-red phosphor for solid-state lighting

Lu Jing-Wen; Zhao Jin; Zhang Yong-Chun; Tu Ru-Ting; Liu Fu-Ni; Leng Zhi-Hua

doi:10.7498/aps.73.20241017

Abstract

White LEDs have the broad application prospect and market demand, while the red phosphor can greatly affect the color temperature and color rendering index of the modulated white light. In this work, a series of Li₂Gd_4–x Sm_x(MoO₄)₇ (x = 0.01–0.13) phosphors is prepared by the high-temperature solid phase method. The successful doping of Sm³⁺ into Li₂Gd₄(MoO₄)₇ is confirmed by X-ray diffractometry (XRD) and does not lead to any change in crystal structure. The samples are detected by scanning electron microscope (SEM) to have irregular blocky structures with particle size less than 20 μm. The existence of Li, Gd, Mo, O and Sm elements in the phosphor is confirmed by energy dispersive X-ray spectroscopy (EDS). The observation of X-ray photoelectron spectroscopy (XPS) shows that the activators are successfully doped into materials. Under 406 nm excitation, the emission peaks of the samples are located at 563, 598, 645 and 706 nm respectively, which are caused by the 4f-4f transition of Sm³⁺, and the strongest emission peak comes from ⁴G_5/2→⁶H_9/2 transition. It is found that optimal concentration of Sm³⁺ is 0.07. With the increase of Sm³⁺ concentration, the fluorescence lifetime decreases gradually. The temperature-dependent emission of phosphor is also studied. The emission intensity at 473 K is still 79% of that at 298 K, indicating that the sample has excellent heat resistance. The CIE chromaticity diagram shows the luminescence of the prepared phosphor is located in the orange-red region and the color purity is high (99%). Moreover, a white LED is fabricated using the optical doped phosphor, which has CIE coordinates of (0.3788, 0.3134) that are located in the circle of white light. Research shows that the Li₂Gd₄(MoO₄)₇:Sm³⁺ phosphor is a promising orange-red phosphor for white LEDs.

Keywords:

Authors and contacts

1.
College of Science, Xi’an University of Architecture and Technology, Xi’an 710055, China
2.
School of Chemistry and Chemical Engineering, Xi’an University of Architecture and Technology, Xi’an 710055, China

Corresponding author: Zhao Jin, zhaojin@xauat.edu.cn

Funds: Project supported by the National Natural Science Foundation of China (Grant No. 11804265), the Key Science and Technology Innovation Team of Shaanxi Province, China (Grant No. 2022TD-30), and the Natural Science Basic Research Program of Shaanxi Province, China (Grant No. 2024JC-YBMS-384).

FullText HTML : translate this paragraph

References

[1]	Li X H, Ding J N, Tang Z, Lin X Y, Dong H, Wu A H, Jiang L W 2024 Ceram. Int. 50 20 Google Scholar
[2]	Wang L, Zhang Y, Gao D, Sha X, Chen X, Zhang Y, Zhang J, Zhang X, Cao Y, Wang Y, Li X, Xu S, Yu H, Chen B J 2024 Results Phys. 56 107238 Google Scholar
[3]	王国静 2021 硕士学位论文 (保定: 河北大学) Wang G J 2021 M. S. Thesis (Baoding: Hebei University
[4]	王新瑞 2020 硕士学位论文(哈尔滨: 哈尔滨工业大学) Wang X R 2020 M. S. Thesis (Harbin: Harbin Institute of technology
[5]	王贵民 2021 硕士学位论文(南京: 南京邮电大学) Wang G M 2021 M. S. Thesis (Nanjing: Nanjing university of posts and telecommunications
[6]	Cao R P, Tu Y F, Chen T, Li L, Lan B, Liu R, Luo Z Y, Yi X H 2023 J. Optics-UK. 52 1278 Google Scholar
[7]	Dalal H, Kumar M, Kaushik S, Sehrawat P, Sheoran M, Sehrawat N, Malik R K 2023 J. Electron. Mater. 52 2780 Google Scholar
[8]	Xiao Z L, Ye J T, Wu B K, Wang F Z, Li J H, Zhang B H, Liu W Z, Han L, You W X 2022 Appl. Phys. A 128 1 Google Scholar
[9]	Chauhan V, Dixit P, Pandey P C 2021 J. Rare Earth 39 1336 Google Scholar
[10]	陆逸, 许英朝, 孟宪国, 鹿晨东, 杨伟斌, 吴盼盼, 刘月 2024 中国稀土学报 42 216 Lu Y, Xu Y C, Meng X G, Lu C D, Yang W B, Wu P P, Liu Y 2024 J. Rare Earth 42 216
[11]	Wang C W, Peng L X, Qin F, Kou M, Wang Y D, Xu L L, Zhang Z G 2024 Opt. Mater. 154 115741
[12]	Zhao J X, Zhang Y, Wang T A, Guan L, Dong G Y, Liu Z Y, Fu N, Wang F H, Li X, 2023 Ceram. Int. 49 29505 Google Scholar
[13]	杨伟斌, 熊飞兵, 杨寅, 周琼, 谢岚驰, 凌爽, 罗新 2022 发光学报 43 879 Google Scholar Yang W B, Xiong F B, Yang Y, Zhou Q, Xie L C, Ling S, Luo X 2022 Chin. J. Lumin. 43 879 Google Scholar
[14]	任艳东, 吕树臣 2011 物理学报 60 087804 Google Scholar Ren Y D, Lv S C, 2011 Acta Phys. Sin. 60 087804 Google Scholar
[15]	赵聪, 孟庆裕, 孙文军 2015 物理学报 64 107803 Google Scholar Zhao C, Meng Q Y, Sun W J 2015 Acta Phys. Sin. 64 107803 Google Scholar
[16]	Ju Z H, Wei R P, Ma J X, Pang C R, Liu W S 2010 J. Alloys Compds. 507 133 Google Scholar
[17]	Yang R Q, Li J, Xie X J, Lian J J, Wang C Y, Li C L, Su H R, Zou Z Q, Xie S A, Yu R J 2024 J. Lumin. 267 120366 Google Scholar
[18]	关丽, 魏伟, 刘超, 郭树青, 李旭, 杨志平 2013 硅酸盐学报 41 62 Google Scholar Guan L, Wei W, Liu Chao, Guo S Q, Li X, Yang Z P 2013 J. Chin. Ceram. Soc. 41 62 Google Scholar
[19]	韩建伟, 林林, 童玉清, 羊富强, 曹林, 刘行仁 2012 稀土 33 50 Han J W, Lin L, Tong Y Q, Yang F Q, Cao L, Liu X R 2012 Chin. Rare Earths 33 50
[20]	Yu Z M, Luo Z Y, Liu X R, Pun E Y B, Lin H 2019 Opt. Mater. 93 76 Google Scholar
[21]	骆志杨 2020 硕士学位论文(大连: 大连工业大学) Luo Z Y 2020 M. S. Thesis (Dalian: Dalian Polytechnic University
[22]	Chen J Q, Chen J Y, Zhang W N, Xu S J, Chen L P, Guo H 2023 Ceram. Int. 49 16252 Google Scholar
[23]	Jiang K Z, Zhou C, Li W H, Su H R, He D M, Chen X Y, Zhang D, Xie S A, Yu R J 2024 J. Alloys Compds. 980 173518 Google Scholar
[24]	Fan M H, Liu S, Yang K, Guo J, Wang J X, Wang X H, Liu Q, Wei B 2020 Ceram. Int. 46 6926 Google Scholar
[25]	Cao R P, Wang X T, Jiao Y M, Ouyang X, Guo S L, Liu P, Ao H, Cao C Y 2019 J. Lumin. 212 23 Google Scholar
[26]	Ogugua S N, Shaat S K K, Swart H C, Kroon R E, Ntwaeaborwa O M 2019 J. Alloys Compds. 775 950 Google Scholar
[27]	樊霞霞, 高志翔, 屈文山, 田翠锋, 李建刚, 李伟, 董丽娟, 石云龙 2022 无机化学学报 38 1016 Google Scholar Fan X X, Gao Z X, Qu W S, Tian C F, Li J G, Li W, Dong L J, Shi Y L 2022 Inorg. Chim. 38 1016 Google Scholar
[28]	Kumar I, Gathania A K 2022 J. Mater. Sci. Mater. El. 33 328 Google Scholar
[29]	Sun G H, Chen Q L 2023 J. Alloys Compds. 936 168263 Google Scholar
[30]	Zhao C C, Yin X, Huang F Q, Hang Y 2011 J. Solid State Chem. 184 3190 Google Scholar
[31]	Li H, Li L, Zhao W, Zhou X, Hua Y 2023 Mater. Today Chem. 32 101661 Google Scholar
[32]	Ji C Y, Huang Z, Tian X Y 2020 J. Alloys Compds. 825 154176 Google Scholar
[33]	Liu H K, Nie K, Zhang Y Y, Mei L F, Deyneko D V, Ma X X 2023 J. Rare Earth 41 1288 Google Scholar
[34]	阿依努热木·吐尔逊, 王磊, 苏比伊努尔·吉力力, 艾尔肯·斯地克 2022 激光与光电子学进展 59 329 Ayinuremu T, Wang L, Subiyinuer J, Aierken S 2022 Prog. Laser Optoelectron. 59 329
[35]	Yang Y, Pan H, Guan L, Wang D W, Zhao J X, Yang J F, Yang Z P, Li X 2020 J. Mater. Res. Technol. 9 3847 Google Scholar
[36]	Liu Y Y, Shi W, Liao D L, Yang X Y, Gao J, Ma Z J, Guo J, Gong N, Liu L, Chang M X, Deng B, Yu R J 2021 J. Am. Ceram. Soc. 104 5966 Google Scholar
[37]	Tang Z, Sun Z G, Zheng Y Q, Chen G J, Li X H, Jiang L W 2023 Ceram. Int. 49 10064 Google Scholar
[38]	张恒, 陈伟, 姜锋, 朱德生 2023 稀土 44 28 Zhang H, Chen W, Jiang F, Zhu D S 2023 Chin. Rare Earths. 44 28
[39]	Wang J X, Guo J, Lv Q Y, Ma Z J, Feng X Y, Lu Y H, Gao J, Chen W S, Deng B, Yu R J 2022 J. Lumin. 241 118459 Google Scholar
[40]	Mu Y X, Yao J H, Wan X M, Mao X J, Luo L H 2022 J. Alloys Compd. 909 164801 Google Scholar
[41]	Xue J P, Song M J, Noh H M, Park S H, Lee B R, Kim J H, Jeong J H 2020 J. Alloys Compds. 817 152705 Google Scholar
[42]	Han B J, Ren J, Teng P P, Zhu J B, Shen Y, Li Z A, Zhu X L, Yang X H 2022 Ceram. Int. 48 971 Google Scholar
[43]	Zhang Z C, Ran W G, Wang F K, Jiang H X, Yan T J 2024 Ceram. Int. 50 5614 Google Scholar
[44]	Huo X X, Wang Z J, Tao C J, Zhang N, Wang D W, Zhao J X, Yang Z P, Li P L 2022 J. Alloys Compds. 902 163823 Google Scholar
[45]	Du H Y, Zhu G, Li Z W, Li S S, He M, Bi Z H, Xin S Y 2023 Spectrochim. Acta A 302 123134 Google Scholar
[46]	Chen J X, He D M, Wang W X, Li S L, Zou Z Q, Liu J H, Wang Y, Chen X Y, Zheng L L, Xie S A, Yu R J 2024 J. Lumin. 265 120252 Google Scholar
[47]	Cui R R, Guo X, Deng C Y 2020 J. Lumin. 224 117233 Google Scholar
[48]	Wu G D, Xue J Q, Li X Y, Bi Q, Sheng M J, Leng Z H 2023 Ceram. Int. 49 10615 Google Scholar

Cited By

图 1 样品的物相分析与结构　(a) Li₂Gd₄(MoO₄)₇:x Sm³⁺ (x = 0.01, 0.07, 0.13)的XRD图谱; (b) Li₂Gd₄(MoO₄)₇的晶体结构

Figure 1. Phase analysis and structrue of samples: (a) XRD patterns of Li₂Gd₄(MoO₄)₇:x Sm³⁺ (x = 0.01, 0.07, 0.13); (b) crystal structure of Li₂Gd₄(MoO₄)₇.

DownLoad: Full-Size Img PowerPoint

图 2 Li₂Gd₄(MoO₄)₇:0.07Sm³⁺荧光粉的形貌分析　(a) SEM图; (b)—(g)各元素分布图和EDS能谱图

Figure 2. Morphology analysis of Li₂Gd₄(MoO₄)₇:0.07Sm³⁺: (a) SEM image; (b)–(g) distribution of elements and EDS energy spectrum.

DownLoad: Full-Size Img PowerPoint

图 3 (a) Li₂Gd₄(MoO₄)₇:0.07Sm³⁺荧光粉XPS全谱; (b)—(f) Li 1s, Gd 4d, Mo 3d, O 1s和Sm 3d核心级频谱

Figure 3. (a) Full XPS spectrum of Li₂Gd₄(MoO₄)₇:0.07Sm³⁺ phosphor; (b)–(f) Li 1s, Gd 4d, Mo 3d, O 1s and Sm 3d core-level spectra.

DownLoad: Full-Size Img PowerPoint

图 4 Li₂Gd₄(MoO₄)₇:x Sm³⁺ (x = 0.01—0.13)样品的荧光光谱　(a) 激发光谱; (b) 发射光谱

Figure 4. Fluorescence spectra of Li₂Gd₄(MoO₄)₇:x Sm³⁺ (x = 0.01–0.13) samples: (a) Excitation spectra; (b) emission spectra.

DownLoad: Full-Size Img PowerPoint

图 5 (a) Li₂Gd₄(MoO₄)₇:x Sm³⁺ (x = 0.01—0.13)的发射光谱; (b) 发射强度与Sm³⁺掺杂浓度的关系图; (c) lg(I/x)与lg(x)的关系曲线; (d) Sm³⁺的掺杂浓度与598, 645 nm处发射峰积分面积关系图

Figure 5. (a) Emission spectra of Li₂Gd₄(MoO₄)₇:x Sm³⁺ (x = 0.01–0.13); (b) the relationship between emission intensity and Sm³⁺ doping concentration; (c) lg(I/x)-lg(x); (d) the relationship between the concentration of Sm³⁺ and the emission integral intensity at 598 nm and 645 nm.

DownLoad: Full-Size Img PowerPoint

图 6 荧光衰减曲线和发光机理　(a) Li₂Gd₄(MoO₄)₇:x Sm³⁺ (x = 0.01—0.13)系列样品在645 nm处的寿命衰减曲线(λ_ex = 406 nm); (b) Sm³⁺的能级跃迁图

Figure 6. Fluorescence attenuation curves and luminescence mechanism: (a) Lifetime decay curves of Li₂Gd₄(MoO₄)₇:x Sm³⁺ (x = 0.01–0.13) at 645 nm (λ_ex = 406 nm); (b) energy level transition diagram of Sm³⁺.

DownLoad: Full-Size Img PowerPoint

图 7 (a) Li₂Gd₄(MoO₄)₇:0.07Sm³⁺荧光粉在不同温度下的发光光谱; (b) 样品在298—448 K范围内的热行为映射图; (c) 归一化发光强度随温度的变化; (d) $\ln[(I_0/I) - 1]$与10000/T关系

Figure 7. (a) Luminescence spectra of Li₂Gd₄(MoO₄)₇:0.07Sm³⁺ phosphor at different temperatures; (b) the thermal behavior mapping diagram of sample in the range of 298–448 K; (c) the normalized luminescence intensity varies with temperature; (d) the relationship between $\ln[(I_0/I) -1] $ of phosphor and 10000/T.

DownLoad: Full-Size Img PowerPoint

图 8 (a) Li₂Gd₄(MoO₄)₇:x Sm³⁺ (x = 0.01—0.13)荧光粉在406 nm激发下的色坐标图; (b) Li₂Gd₄(MoO₄)₇:x Sm³⁺ (x = 0.01—0.13)的色度坐标x, y点线图

Figure 8. (a) Color coordinates of Li₂Gd₄(MoO₄)₇:x Sm³⁺ (x = 0.01–0.13) excited at 406 nm; (b) the chromaticity coordinates x, y point plot of Li₂Gd₄(MoO₄)₇:x Sm³⁺ (x = 0.01–0.13).

DownLoad: Full-Size Img PowerPoint

图 9 (a) Li₂Gd₄(MoO₄)₇:0.07Sm³⁺的内量子效率和放大图; (b)白光LED装置的色坐标、电致发光光谱及照片

Figure 9. (a) Internal quantum efficiency of Li₂Gd₄(MoO₄)₇:0.07Sm³⁺ and enlarged profile; (b) the color coordinates, electroluminescence spectrum and LED image of the fabricated w-LED.

DownLoad: Full-Size Img PowerPoint

表 1 Li₂Gd₄(MoO₄)₇:x Sm³⁺ (x = 0.01—0.13)的CIE色度坐标及色纯度

Table 1. The CIE coordinates and color purity of Li₂Gd₄(MoO₄)₇:x Sm³⁺ (x = 0.01—0.13).

Concentration of Sm³⁺	CIE coordinates (x, y)	Color purity/%
x = 0.01	(0.6311, 0.3682)	99.77
x = 0.03	(0.6314, 0.3679)	99.86
x = 0.05	(0.6315, 0.3678)	99.89
x = 0.07	(0.6315, 0.3679)	99.89
x = 0.09	(0.6318, 0.3676)	99.98
x = 0.11	(0.6313, 0.3680)	99.83
x = 0.01	(0.6312, 0.3681)	99.80

DownLoad: CSV

[1]	Li X H, Ding J N, Tang Z, Lin X Y, Dong H, Wu A H, Jiang L W 2024 Ceram. Int. 50 20 Google Scholar
[2]	Wang L, Zhang Y, Gao D, Sha X, Chen X, Zhang Y, Zhang J, Zhang X, Cao Y, Wang Y, Li X, Xu S, Yu H, Chen B J 2024 Results Phys. 56 107238 Google Scholar
[3]	王国静 2021 硕士学位论文 (保定: 河北大学) Wang G J 2021 M. S. Thesis (Baoding: Hebei University
[4]	王新瑞 2020 硕士学位论文(哈尔滨: 哈尔滨工业大学) Wang X R 2020 M. S. Thesis (Harbin: Harbin Institute of technology
[5]	王贵民 2021 硕士学位论文(南京: 南京邮电大学) Wang G M 2021 M. S. Thesis (Nanjing: Nanjing university of posts and telecommunications
[6]	Cao R P, Tu Y F, Chen T, Li L, Lan B, Liu R, Luo Z Y, Yi X H 2023 J. Optics-UK. 52 1278 Google Scholar
[7]	Dalal H, Kumar M, Kaushik S, Sehrawat P, Sheoran M, Sehrawat N, Malik R K 2023 J. Electron. Mater. 52 2780 Google Scholar
[8]	Xiao Z L, Ye J T, Wu B K, Wang F Z, Li J H, Zhang B H, Liu W Z, Han L, You W X 2022 Appl. Phys. A 128 1 Google Scholar
[9]	Chauhan V, Dixit P, Pandey P C 2021 J. Rare Earth 39 1336 Google Scholar
[10]	陆逸, 许英朝, 孟宪国, 鹿晨东, 杨伟斌, 吴盼盼, 刘月 2024 中国稀土学报 42 216 Lu Y, Xu Y C, Meng X G, Lu C D, Yang W B, Wu P P, Liu Y 2024 J. Rare Earth 42 216
[11]	Wang C W, Peng L X, Qin F, Kou M, Wang Y D, Xu L L, Zhang Z G 2024 Opt. Mater. 154 115741
[12]	Zhao J X, Zhang Y, Wang T A, Guan L, Dong G Y, Liu Z Y, Fu N, Wang F H, Li X, 2023 Ceram. Int. 49 29505 Google Scholar
[13]	杨伟斌, 熊飞兵, 杨寅, 周琼, 谢岚驰, 凌爽, 罗新 2022 发光学报 43 879 Google Scholar Yang W B, Xiong F B, Yang Y, Zhou Q, Xie L C, Ling S, Luo X 2022 Chin. J. Lumin. 43 879 Google Scholar
[14]	任艳东, 吕树臣 2011 物理学报 60 087804 Google Scholar Ren Y D, Lv S C, 2011 Acta Phys. Sin. 60 087804 Google Scholar
[15]	赵聪, 孟庆裕, 孙文军 2015 物理学报 64 107803 Google Scholar Zhao C, Meng Q Y, Sun W J 2015 Acta Phys. Sin. 64 107803 Google Scholar
[16]	Ju Z H, Wei R P, Ma J X, Pang C R, Liu W S 2010 J. Alloys Compds. 507 133 Google Scholar
[17]	Yang R Q, Li J, Xie X J, Lian J J, Wang C Y, Li C L, Su H R, Zou Z Q, Xie S A, Yu R J 2024 J. Lumin. 267 120366 Google Scholar
[18]	关丽, 魏伟, 刘超, 郭树青, 李旭, 杨志平 2013 硅酸盐学报 41 62 Google Scholar Guan L, Wei W, Liu Chao, Guo S Q, Li X, Yang Z P 2013 J. Chin. Ceram. Soc. 41 62 Google Scholar
[19]	韩建伟, 林林, 童玉清, 羊富强, 曹林, 刘行仁 2012 稀土 33 50 Han J W, Lin L, Tong Y Q, Yang F Q, Cao L, Liu X R 2012 Chin. Rare Earths 33 50
[20]	Yu Z M, Luo Z Y, Liu X R, Pun E Y B, Lin H 2019 Opt. Mater. 93 76 Google Scholar
[21]	骆志杨 2020 硕士学位论文(大连: 大连工业大学) Luo Z Y 2020 M. S. Thesis (Dalian: Dalian Polytechnic University
[22]	Chen J Q, Chen J Y, Zhang W N, Xu S J, Chen L P, Guo H 2023 Ceram. Int. 49 16252 Google Scholar
[23]	Jiang K Z, Zhou C, Li W H, Su H R, He D M, Chen X Y, Zhang D, Xie S A, Yu R J 2024 J. Alloys Compds. 980 173518 Google Scholar
[24]	Fan M H, Liu S, Yang K, Guo J, Wang J X, Wang X H, Liu Q, Wei B 2020 Ceram. Int. 46 6926 Google Scholar
[25]	Cao R P, Wang X T, Jiao Y M, Ouyang X, Guo S L, Liu P, Ao H, Cao C Y 2019 J. Lumin. 212 23 Google Scholar
[26]	Ogugua S N, Shaat S K K, Swart H C, Kroon R E, Ntwaeaborwa O M 2019 J. Alloys Compds. 775 950 Google Scholar
[27]	樊霞霞, 高志翔, 屈文山, 田翠锋, 李建刚, 李伟, 董丽娟, 石云龙 2022 无机化学学报 38 1016 Google Scholar Fan X X, Gao Z X, Qu W S, Tian C F, Li J G, Li W, Dong L J, Shi Y L 2022 Inorg. Chim. 38 1016 Google Scholar
[28]	Kumar I, Gathania A K 2022 J. Mater. Sci. Mater. El. 33 328 Google Scholar
[29]	Sun G H, Chen Q L 2023 J. Alloys Compds. 936 168263 Google Scholar
[30]	Zhao C C, Yin X, Huang F Q, Hang Y 2011 J. Solid State Chem. 184 3190 Google Scholar
[31]	Li H, Li L, Zhao W, Zhou X, Hua Y 2023 Mater. Today Chem. 32 101661 Google Scholar
[32]	Ji C Y, Huang Z, Tian X Y 2020 J. Alloys Compds. 825 154176 Google Scholar
[33]	Liu H K, Nie K, Zhang Y Y, Mei L F, Deyneko D V, Ma X X 2023 J. Rare Earth 41 1288 Google Scholar
[34]	阿依努热木·吐尔逊, 王磊, 苏比伊努尔·吉力力, 艾尔肯·斯地克 2022 激光与光电子学进展 59 329 Ayinuremu T, Wang L, Subiyinuer J, Aierken S 2022 Prog. Laser Optoelectron. 59 329
[35]	Yang Y, Pan H, Guan L, Wang D W, Zhao J X, Yang J F, Yang Z P, Li X 2020 J. Mater. Res. Technol. 9 3847 Google Scholar
[36]	Liu Y Y, Shi W, Liao D L, Yang X Y, Gao J, Ma Z J, Guo J, Gong N, Liu L, Chang M X, Deng B, Yu R J 2021 J. Am. Ceram. Soc. 104 5966 Google Scholar
[37]	Tang Z, Sun Z G, Zheng Y Q, Chen G J, Li X H, Jiang L W 2023 Ceram. Int. 49 10064 Google Scholar
[38]	张恒, 陈伟, 姜锋, 朱德生 2023 稀土 44 28 Zhang H, Chen W, Jiang F, Zhu D S 2023 Chin. Rare Earths. 44 28
[39]	Wang J X, Guo J, Lv Q Y, Ma Z J, Feng X Y, Lu Y H, Gao J, Chen W S, Deng B, Yu R J 2022 J. Lumin. 241 118459 Google Scholar
[40]	Mu Y X, Yao J H, Wan X M, Mao X J, Luo L H 2022 J. Alloys Compd. 909 164801 Google Scholar
[41]	Xue J P, Song M J, Noh H M, Park S H, Lee B R, Kim J H, Jeong J H 2020 J. Alloys Compds. 817 152705 Google Scholar
[42]	Han B J, Ren J, Teng P P, Zhu J B, Shen Y, Li Z A, Zhu X L, Yang X H 2022 Ceram. Int. 48 971 Google Scholar
[43]	Zhang Z C, Ran W G, Wang F K, Jiang H X, Yan T J 2024 Ceram. Int. 50 5614 Google Scholar
[44]	Huo X X, Wang Z J, Tao C J, Zhang N, Wang D W, Zhao J X, Yang Z P, Li P L 2022 J. Alloys Compds. 902 163823 Google Scholar
[45]	Du H Y, Zhu G, Li Z W, Li S S, He M, Bi Z H, Xin S Y 2023 Spectrochim. Acta A 302 123134 Google Scholar
[46]	Chen J X, He D M, Wang W X, Li S L, Zou Z Q, Liu J H, Wang Y, Chen X Y, Zheng L L, Xie S A, Yu R J 2024 J. Lumin. 265 120252 Google Scholar
[47]	Cui R R, Guo X, Deng C Y 2020 J. Lumin. 224 117233 Google Scholar
[48]	Wu G D, Xue J Q, Li X Y, Bi Q, Sheng M J, Leng Z H 2023 Ceram. Int. 49 10615 Google Scholar

[1]	Ruan Yuan-Dong, Zhang Zhi-Hao, Jia Jiang-Xie, Gu Yu-Ning, Zhang Shan-Duan, Cui Xu-Gao, Hong Wei, Bai Yan-Zheng, Tian Peng-Fei. Application of ultraviolet light sources in charge management systems for space gravitational wave detection. Acta Physica Sinica, 2024, 73(22): 220401. doi: 10.7498/aps.73.20241115
[2]	Luo Jie, Zhang Zi-Qiu, Xu Jun-Hao, Qin Zhao-Ting, Zhao Yuan-Shuai, He Hong, Li Guan-Nan, Tang Jian-Feng. Synthesis and luminescent properties of rare earths doped Gd₂Te₄O₁₁ tellurite phosphors. Acta Physica Sinica, 2023, 72(1): 017801. doi: 10.7498/aps.72.20221341
[3]	Lü Zhao-Cheng, Li Ying, Quan Gui-Ying, Zheng Qing-Hua, Zhou Wei-Wei, Zhao Wang. Preparation and photoluminescent properties of near-UV broadband-excited red phosphor (Gd1-xEux)6(Te1-yMoy)O12 for white-LEDs. Acta Physica Sinica, 2017, 66(11): 117801. doi: 10.7498/aps.66.117801
[4]	Liu Wen-Quan, Chao Ke-Fu, Wu Wen-Jie, Bao Fu-Quan, Zhou Bing-Qing. CaAlSiN3:Eu2+ red phosphors synthesized by atmospheric nitrogen and their luminescence properties. Acta Physica Sinica, 2016, 65(20): 207801. doi: 10.7498/aps.65.207801
[5]	Chen Qiao-Qiao, Dai Neng-Li, Liu Zi-Jun, Chu Ying-Bo, Li Jin-Yan, Yang Lü-Yun. Luminescence property of Ce3+-Tb3+-Sm3+ co-doped borosilicate glass under various ultraviolet excitations. Acta Physica Sinica, 2014, 63(7): 077803. doi: 10.7498/aps.63.077803
[6]	Ren Guo-Hao, Pei Yu, Wu Yun-Tao, Chen Xiao-Feng, Li Huan-Ying, Pan Shang-Ke. Influence of Ce doping concentration on the luminescence properties of LaCl3：Ce scintillation crystals. Acta Physica Sinica, 2014, 63(3): 037802. doi: 10.7498/aps.63.037802
[7]	Zhou Ren-Di, Huang Xue-Fei, Qi Zhi-Jian, Huang Wei-Gang. Preparation and luminescent properties of Ca2Si(O4-xNx)：Eu2+ green-emitting phosphors. Acta Physica Sinica, 2014, 63(19): 197801. doi: 10.7498/aps.63.197801
[8]	Luo Lin-Ling, Tang Ke, Zhu Da-Chuan, Han Tao, Zhao Cong. Effect of Li+ and Er3+ co-doping on the luminescence properties of Ba2SiO4：Eu. Acta Physica Sinica, 2013, 62(15): 157802. doi: 10.7498/aps.62.157802
[9]	Xu Xin-Wei, Cui Bi-Feng, Zhu Yan-Xu, Guo Wei-Ling, Li Wei-Guo. Research of dielectric photonic crystal on red LED to increase luminous flux. Acta Physica Sinica, 2012, 61(15): 154213. doi: 10.7498/aps.61.154213
[10]	Qian Ke-Yuan, Ma Jun, Fu Wei, Luo Yi. Research on scattering properties of phosphor for high power white light emitting diode based on Mie scattering theory. Acta Physica Sinica, 2012, 61(20): 204201. doi: 10.7498/aps.61.204201
[11]	Wang Qian, Ci Zhi-Peng, Wang Yu-Hua, Zhu Ge, Wen Yan, Liu Bi-Tao, Que Mei-Dan. Preparation and luminescence properties of a red phosphor Mg5SnB2O10:Eu3+, Bi3+ for light emitting diode. Acta Physica Sinica, 2012, 61(21): 217802. doi: 10.7498/aps.61.217802
[12]	He Wei, Zhang Yue-Pin, Wang Jin-Hao, Wang Shi-Xian, Xia Hai-Ping. Luminescence properties of terbium doped oxyfluoride tellurite glasses. Acta Physica Sinica, 2011, 60(4): 042901. doi: 10.7498/aps.60.042901
[13]	Wang Bing, Li Zhi-Cong, Yao Ran, Liang Meng, Yan Fa-Wang, Wang Guo-Hong. Optimized growth of p-type AlGaN electron blocking layer in the GaN-based LED. Acta Physica Sinica, 2011, 60(1): 016108. doi: 10.7498/aps.60.016108
[14]	Yang Zhi-Ping, Ma Xin, Zhao Pan-Pan, Song Zhao-Feng. Preparation and luminescence characteristics of SrAl2B2O7:Dy3+ phosphor. Acta Physica Sinica, 2010, 59(8): 5387-5391. doi: 10.7498/aps.59.5387
[15]	Liu Yuan-Hong, Zhuang Wei-Dong, Gao Wen-Gui, Hu Yun-Sheng, He Tao, He Hua-Qiang. Effect of H3BO3 on preparation and luminescence properties of submicron green-emitting Ca3Sc2Si3O12 ∶Ce phosphor. Acta Physica Sinica, 2010, 59(11): 8200-8204. doi: 10.7498/aps.59.8200
[16]	Ding Xu, Xu Yan, Guo Chong-Feng. Luminescence characteristics of Sr2B5O9Cl: Eu2+ phosphors for white LED. Acta Physica Sinica, 2010, 59(9): 6632-6636. doi: 10.7498/aps.59.6632
[17]	Tong Jin-Gang, Wu Chun-Fang, Wang Yu-Hua, Chen Zuo-Hui. Synthesis of nanorod GdPO4:Eu3+ phosphor and its photoluminescent properties. Acta Physica Sinica, 2009, 58(1): 585-589. doi: 10.7498/aps.58.585
[18]	Zhao Xing, Fang Zhi_Liang, Mu Guo_Guang. Study on the colorimetric properties of the LED projection sources. Acta Physica Sinica, 2007, 56(5): 2537-2540. doi: 10.7498/aps.56.2537
[19]	Li Jia-Cheng, Xue Tian-Feng, Fan You-Yu, Li Shun-Guang, Hu He-Fang. Effect of introducing Ce3+ on the emission properties of Er3+/Yb3+-doped TeO2-WO3-ZnO glasses. Acta Physica Sinica, 2006, 55(2): 923-928. doi: 10.7498/aps.55.923
[20]	Yang Zhi-Ping, Liu Yu-Feng. Preparation and luminescence characteristics of Eu2+ activated Ca3SiO5 green-emitting phosphor. Acta Physica Sinica, 2006, 55(9): 4946-4950. doi: 10.7498/aps.55.4946

Catalog

Vol. 73, Issue 21 - 2024-11-05

Metrics

Abstract views: 654
PDF Downloads: 23
Cited By: 0

姓名
邮箱
手机号码
标题
留言内容
验证码

Search

Article

留言板

Structure and luminescence properties of Li₂Gd₄(MoO₄)₇:Sm³⁺ orange-red phosphor for solid-state lighting

Abstract

Authors and contacts

Corresponding author: Zhao Jin, zhaojin@xauat.edu.cn

FullText HTML : translate this paragraph

References

Cited By

Catalog

Metrics

Authors

Referees

About Journal

About

Search

Article

留言板