The sintered Nd25.5Dy6.5Co13FebalM1.05B0.98 magnet (Co13 magnet) and Nd30Dy1.5Co0.5FebalM1.05B0.98 magnet (35SH magnet) are prepared by strip casting, hydrogen decrepitation, jet milling, orienting compression, sintering and annealling. The maximum energy product (BH)max and coercivity Hcj of Co13 magnet at room temperature are 30.88 MGOe and 19.01 kOe, which are lower than those of 35SH magnet. By adding Co and Dy, the remanence temperature coefficient α , curie temperature TC, and max operating temperature TW significantly increase form –0.136%/℃ to –0.065%/℃ (25–180 ℃), 310 ℃ to 454 ℃, and 160 ℃ to 200 ℃ respectively. Mechanical property test and fracture analysis show that owing to the high content of Co in the magnet, the proportion of cleavage fracture in the main phase grains increases, and the bending strength Rbb decreases compared with the Rbb of 35SH magnet, which is nearly twice that of 2∶17 type Sm-Co magnet. The reason for Rbb decreasing might be that Co element preferentially replaces Fe in the 2∶14∶1 main phase, which leads the lattice to be distorted and the grain strength of the main phase to decrease. The microstructure analysis shows that there exists a high Co region in the grain boundary phase of Co13 magnet, and its composition is close to (Nd,Dy)(Fe,Co)3, which might be one of the reasons for coercivity Hcj decreasing.
-
Keywords:
- sintered Nd-Fe-B /
- temperature stability /
- maximum operating temperature /
- mechanical Properties
[1] Brown D, Ma B M, Chen Z M 2002 J. Magn. Magn. Mater. 248 432
[2] Nakamura H, Hirota K, Shimao M, Minowa T, Honshima M 2005 IEEE. T. Magn. 41 3844
Google Scholar
[3] 朱明刚, 孙旭, 刘荣辉, 徐会兵 2020 中国工程科学 22 37
Google Scholar
Zhu M G, Sun X, Liu R H, Xu H B 2020 Strateg. Study CAE 22 37
Google Scholar
[4] Hono K, Sepehri-Amin H 2012 Scripta Mater. 67 530
Google Scholar
[5] Coey J 2020 Engineering 6 118
[6] Matsuura Y 2006 J. Magn. Magn. Mater. 303 344
Google Scholar
[7] Givord D, Li H S, Moreau J M 1984 Solid State Commun. 50 497
Google Scholar
[8] Hu Z H, Cheng X H, Zhu M G, Li W, Lian F Z 2008 Rare Metals 27 358
Google Scholar
[9] Gutfleisch O, Willard M A, Brück E, Chen C H, Sankar S G, Liu J P 2011 Adv. Mater. 23 821
Google Scholar
[10] Kronmüller H, Goll D 2002 Scripta Mater. 47 545
Google Scholar
[11] Machida H, Fujiwara T, Kamada R, Morimoto Y, Takezawa M 2017 AIP Adv. 7 056223
Google Scholar
[12] 孙威 2015 博士学位论文(北京: 钢铁研究总院)
Sun W 2015 Ph. D. Dissertation (Beijing: Central Iron & Steel Research Institute) (in Chinese)
[13] 周寿增, 郭灿杰, 呼琴, 李春和 1988 北京钢铁学院学报 10 317
Google Scholar
Zhou S Z, Guo C J, Hu Q, Li C H 1988 J. Beijing Univ. Iron Steel Tech. 10 317
Google Scholar
[14] ARAI S, SHIBATA T 1985 IEEE T. Magn. 21 1952
Google Scholar
[15] Kronmuller H 1987 Phys. Status Solidi B 144 385
[16] Li L, Dong S Z, Han R, Song K K, Li D, Zhu M G, Li W, Sun W 2019 J. Rare Earth 37 628
Google Scholar
[17] Sagawa M, Hirosawa S, Tokuhara K, Yamamoto H, Fujimura S 1987 J. Appl. Phys. 61 3559
Google Scholar
[18] Hirosawa S, Matsuura Y, Yamamoto H, Fujimura S, Sagawa M 1986 J. Appl. Phys. 59 873
Google Scholar
[19] Ma B M, Narasimhan, K, Hurt J 1986 IEEE. T. Magn. 22 1081
Google Scholar
[20] Li W, Jiang L, Wang D, Sun T D, Zhu J H 1986 J. Alloys Compd. 126 95
[21] Kablov E N, Petrakov A F, Piskorskii V P, Valeev V A, Nazarova N V 2007 Met. Sci. Heat Treat. 49 159
Google Scholar
[22] 蒋建华, 曾振鹏 1999 稀有金属材料与工程 28 144
Google Scholar
Jiang J H, Zeng Z P 1999 Rare Metals Eng. 28 144
Google Scholar
[23] Li W, Li A H, Wang H J, Pan W, Chang H W 2009 J. Appl. Phys. 105 07A703
Google Scholar
[24] Wang H J, Li A H, Li W 2006 J. Magn. Magn. Mater. 307 268
Google Scholar
[25] Wang H J, Li a H, Li W 2007 Intermetallics 15 985
[26] XB/T 507—2009 2: 17 Type Samarium Uobalt Uermanent Uagnetic Material (in Chinese) [XB/T 507—2009 2: 17型钐钴永磁材料]
[27] GYB-2 2016 钢铁研究总院
GYB-2 2016 Central Iron & Steel Research Institute (in Chinese)
[28] GB/T 13560 2017 烧结钕铁硼永磁材料
GB/T 13560—2017 Sintered Neodymium Iron Boron Permanent Magnets (in Chinese)
[29] Wu Y Y, Skokov K, Schfer L, Maccari F, Aubert A, Xu H, Wu H C, Jiang C B, Gutfleisch O 2022 Acta Mater. 235 118062
Google Scholar
[30] Popov A G, Kolodkin D A, Gaviko V S, Vasilenko D Y, Shitov A V 2018 Met. Sci. Heat Treat. 60 528
Google Scholar
-
图 1 样品在不同温度下的退磁曲线和剩磁温度系数随温度区间的变化 (a) Co13的退磁曲线; (b) 35SH的退磁曲线; (c) Sm2Co17的退磁曲线; (d)剩磁温度系数随温度的变化
Figure 1. Demagnetization curve and remanence temperature coefficient of samples at different temperatures: (a) Demagnetization curve of Co13 magnet; (b) demagnetization curve of 35SH magnet; (c) demagnetization curve of Sm2Co17 magnet; (d) remanence temperature coefficient.
图 2 磁性能随温度变化曲线和DTG曲线 (a)Br随温度变化曲线; (b) Hcj随温度变化曲线; (c) (BH)max随温度变化曲线; (d) DTG曲线
Figure 2. Magnetic properties at different temperatures and DTG curve: (a) Br at different temperatures; (b) Hcj at different temperatures; (c) (BH)max at different temperatures; (d) DTG curve.
图 3 样品的不可逆磁通损失随温度变化曲线
Figure 3. Irreversible magnetic flux loss versus temperature.
图 4 两种磁体的背散射形貌图 (a) Co13磁体; (b) 35SH磁体
Figure 4. Backscattering topography of two magnets: (a) Co13 magnet; (b) 35SH magnet.
图 5 两种磁体的背散射形貌和元素面扫图 (a) Co13磁体; (b) 35SH磁体
Figure 5. Backscattering morphology and element mapping scan of two magnets: (a) Co13 magnet; (b) 35SH magnet.
图 6 磁体的力学性能和密度 (a)力学性能对比; (b)密度对比
Figure 6. Mechanical properties and density of magnets: (a) Comparison of mechanical properties; (b) comparison of density.
图 7 磁体抗弯样品断口形貌图 (a) Co13磁体; (b) 35SH磁体; (c) Sm2Co17磁体
Figure 7. Fracture morphology of bending sample: (a) Co13 magnet; (b) 35SH magnet;(c)Sm2Co17 magnet.
表 1 样品在不同温度区间内的剩磁温度系数α(%·℃–1)
Table 1. Remanence temperature coefficient α in different temperature ranges(%·℃–1).
Sample Temperature ranges/℃ 25—40 25—60 25—80 25—100 25—120 25—140 25—160 25—180 Co13 –0.027 –0.036 –0.044 –0.048 –0.053 –0.057 –0.061 –0.065 35SH –0.081 –0.102 –0.107 –0.110 –0.117 –0.123 –0.129 –0.136 Sm2Co17 –0.006 –0.020 –0.029 –0.032 –0.034 –0.036 –0.038 –0.038 
DownLoad: CSV
表 2 两种磁体在不同位置的Nd/Dy/Fe/Co元素含量(%)
Table 2. Nd/Dy/Fe/Co element content of two magnets at different positions(%).
Samples Positions Elements content Nd Dy Co Fe Co13 1 89.75 2.13 0.98 7.13 2 39.52 6.77 19.37 34.34 3 21.51 6.02 13.06 59.41 35SH 4 20.50 1.16 0.69 77.65 5 79.20 0.90 0.52 19.38
DownLoad: CSV
表 3 磁体的抗弯强度、抗压强度和显微硬度
Table 3. Bending strength, compressive strength and Vickers hardness of magnets.
Samples Rbb/MPa Rmc/MPa HV0.5 1# 2# 3# Avg. 1# 2# 3# Avg. 1# 2# 3# Avg. Co13 162 167 159 163 800 815 814 810 665 677 661 668 35SH 210 200 206 205 841 845 849 845 625 630 611 622 Sm2Co17 92 81 83 85 891 883 901 892 640 661 654 652
DownLoad: CSV
-
[1] Brown D, Ma B M, Chen Z M 2002 J. Magn. Magn. Mater. 248 432
[2] Nakamura H, Hirota K, Shimao M, Minowa T, Honshima M 2005 IEEE. T. Magn. 41 3844
Google Scholar
[3] 朱明刚, 孙旭, 刘荣辉, 徐会兵 2020 中国工程科学 22 37
Google Scholar
Zhu M G, Sun X, Liu R H, Xu H B 2020 Strateg. Study CAE 22 37
Google Scholar
[4] Hono K, Sepehri-Amin H 2012 Scripta Mater. 67 530
Google Scholar
[5] Coey J 2020 Engineering 6 118
[6] Matsuura Y 2006 J. Magn. Magn. Mater. 303 344
Google Scholar
[7] Givord D, Li H S, Moreau J M 1984 Solid State Commun. 50 497
Google Scholar
[8] Hu Z H, Cheng X H, Zhu M G, Li W, Lian F Z 2008 Rare Metals 27 358
Google Scholar
[9] Gutfleisch O, Willard M A, Brück E, Chen C H, Sankar S G, Liu J P 2011 Adv. Mater. 23 821
Google Scholar
[10] Kronmüller H, Goll D 2002 Scripta Mater. 47 545
Google Scholar
[11] Machida H, Fujiwara T, Kamada R, Morimoto Y, Takezawa M 2017 AIP Adv. 7 056223
Google Scholar
[12] 孙威 2015 博士学位论文(北京: 钢铁研究总院)
Sun W 2015 Ph. D. Dissertation (Beijing: Central Iron & Steel Research Institute) (in Chinese)
[13] 周寿增, 郭灿杰, 呼琴, 李春和 1988 北京钢铁学院学报 10 317
Google Scholar
Zhou S Z, Guo C J, Hu Q, Li C H 1988 J. Beijing Univ. Iron Steel Tech. 10 317
Google Scholar
[14] ARAI S, SHIBATA T 1985 IEEE T. Magn. 21 1952
Google Scholar
[15] Kronmuller H 1987 Phys. Status Solidi B 144 385
[16] Li L, Dong S Z, Han R, Song K K, Li D, Zhu M G, Li W, Sun W 2019 J. Rare Earth 37 628
Google Scholar
[17] Sagawa M, Hirosawa S, Tokuhara K, Yamamoto H, Fujimura S 1987 J. Appl. Phys. 61 3559
Google Scholar
[18] Hirosawa S, Matsuura Y, Yamamoto H, Fujimura S, Sagawa M 1986 J. Appl. Phys. 59 873
Google Scholar
[19] Ma B M, Narasimhan, K, Hurt J 1986 IEEE. T. Magn. 22 1081
Google Scholar
[20] Li W, Jiang L, Wang D, Sun T D, Zhu J H 1986 J. Alloys Compd. 126 95
[21] Kablov E N, Petrakov A F, Piskorskii V P, Valeev V A, Nazarova N V 2007 Met. Sci. Heat Treat. 49 159
Google Scholar
[22] 蒋建华, 曾振鹏 1999 稀有金属材料与工程 28 144
Google Scholar
Jiang J H, Zeng Z P 1999 Rare Metals Eng. 28 144
Google Scholar
[23] Li W, Li A H, Wang H J, Pan W, Chang H W 2009 J. Appl. Phys. 105 07A703
Google Scholar
[24] Wang H J, Li A H, Li W 2006 J. Magn. Magn. Mater. 307 268
Google Scholar
[25] Wang H J, Li a H, Li W 2007 Intermetallics 15 985
[26] XB/T 507—2009 2: 17 Type Samarium Uobalt Uermanent Uagnetic Material (in Chinese) [XB/T 507—2009 2: 17型钐钴永磁材料]
[27] GYB-2 2016 钢铁研究总院
GYB-2 2016 Central Iron & Steel Research Institute (in Chinese)
[28] GB/T 13560 2017 烧结钕铁硼永磁材料
GB/T 13560—2017 Sintered Neodymium Iron Boron Permanent Magnets (in Chinese)
[29] Wu Y Y, Skokov K, Schfer L, Maccari F, Aubert A, Xu H, Wu H C, Jiang C B, Gutfleisch O 2022 Acta Mater. 235 118062
Google Scholar
[30] Popov A G, Kolodkin D A, Gaviko V S, Vasilenko D Y, Shitov A V 2018 Met. Sci. Heat Treat. 60 528
Google Scholar
DownLoad:
Catalog
Metrics
- Abstract views: 2131
- PDF Downloads: 41
- Cited By: 0