简化共沉淀法制备CaCu3Ti4O12陶瓷及其介电性能研究

贾然 顾访 吴珍华 赵学童 李建英

引用本文:
Citation:

简化共沉淀法制备CaCu3Ti4O12陶瓷及其介电性能研究

贾然, 顾访, 吴珍华, 赵学童, 李建英

Dielectric properties of CaCu3Ti4O12 ceramics prepared by a simplified coprecipitation method

Jia Ran, Gu Fang, Wu Zhen-Hua, Zhao Xue-Tong, Li Jian-Ying
PDF
导出引用
  • 具有巨介电常数的CaCu3Ti4O12陶瓷是一种理想的高储能密度电容器材料. 本文以草酸为沉淀剂、以乙酸铵为调节pH值的定量缓冲剂, 获得制备CaCu3Ti4O12陶瓷的简化共沉淀法.确定了pH=3.0为制备前驱粉料的 最佳反应条件.通过显微分析和介电性能测量,发现在1040℃-1100℃ 范围内,随着烧结温度的提高,陶瓷的晶粒尺寸增大,非线性系数上升,电位梯度和介电损耗下降, 1100℃烧结的试样tanδ 最低达到0.04.认为CaCu3Ti4O12 陶瓷介电损耗包含直流电导分量、低频松弛损耗和高频松弛损耗.低频松弛活化能为0.51 eV, 对应于晶界处的Maxwell-Wagner松弛极化;高频松弛过程活化能为0.10 eV, 对应晶粒内部的氧空位缺陷.烧结温度的升高导致晶界电阻下降.
    Precursor powder of CaCu3Ti4O12 is prepared by a simplified coprecipitation process, in which an optimum reaction condition with ammonium acetate is used as buffer solution and pH=3.0 is proved by X-ray diffraction and scanning electron microscope. The CaCu3Ti4O12 ceramics samples are prepared by sintering the calcined powder at different temperatures (1040℃-1100℃). It is found that higher sintering temperature of CaCu3Ti4O12 ceramics will lead to lager grain size, higher dielectric constant and lower dielectric loss. The dielectric loss of CaCu3Ti4O12 ceramics is suggested to be due to DC electric conductivity, low-frequency relaxation loss and high-frequency relaxation loss. The low-frequency and high-frequency relaxations are related to grain boundary and oxygen vacancy defects respectively.
    • 基金项目: 国家自然科学基金(批准号: 50977071, 50972118, 51177121)资助的课题.
    • Funds: Project supported by the National Natural Science Foundation of China (Grant Nos. 50977071, 50972118, 51177121).
    [1]

    Subramanian M A, Dong L, Duan N, Reisner B A, Sleight A W 2000 Solid State Chem. 151 323

    [2]

    Ramirez A P, Subramanian M A, Gardel M, Blumberg G, Li D, Vogt T, Shapiro S M 2000 Solid State Commun. 151 217

    [3]

    Subramanian M A, Sleight A W 2002 Solid State Sci. 4 347

    [4]

    He L X, Neaton J B, Cohen M H, Vanderbilt D, Homes C C 2002 Phys. Rev. B 65 214112

    [5]

    He L X, Neaton J B, Vanderbilt D, Choen M H 2003 Phys. Rev. B 67 012103

    [6]

    Cohen M H, Neaton J B, He L X, Vanderbilt D 2003 J. Appl. Phys. 94 3299

    [7]

    Zhang L, Tang Z 2004 Phys. Rev. B 70 174306

    [8]

    Tselev A, Brooks C M, Anlage S M, Zheng H, Riba L S, Ramesh R, Subramanian M A 2004 Phys. Rev. B 70 144101

    [9]

    Chiodelli G, Massarotti V, Capsoni D, Bini M, Azzoni C B, Mozzati M C, Lupotto P 2004 Solid State Commun. 132 241

    [10]

    Fang L, Shen M, Cao W 2004 J. Appl. Phys. 95 6483

    [11]

    Homes C C, Vogt T, Shapiro S M, Wakimoto S, Subramanian M A, Ramirez A P 2003 Phys. Rev. B 67 092106

    [12]

    Chen L, Chen C L, Lin Y, Chen Y B, Chen X H, Bontchev R P, Park C Y, Jacobson A J 2003 Appl. Phys. Lett. 82 2317

    [13]

    Fang T T, Liu C P 2005 Chem. Mater. 17 5167

    [14]

    Fang T T, Shiau H K 2004 J. Am. Ceram. Soc. 87 2072

    [15]

    Fu D S, Taniguchi H, Taniyama T, Itoh M, Koshihara S Y 2008 Chem. Mater. 20 1694

    [16]

    Yang C H, Zhou X L, Xu G, Han G R, Weng W J, Du P Y 2006 J. Chin. Ceram. Soc. 34 753 (in Chinese) [杨昌辉, 周小莉, 徐刚, 韩高荣, 翁文剑, 杜丕一 2006 硅酸盐学报 34 753]

    [17]

    Guillemet-Fritscha S, Lebeyb T, Boulosa M, Duranda B 2006 J. Eur. Ceram. Soc. 26 1245

    [18]

    Marchin L, Guillemet-Fritsch S, Durand B 2007 Prog. Solid State Chem. 36 151

    [19]

    Yang Y, Li S T 2010 J. Inorg. Mater. 25 835 (in Chinese) [杨雁, 李盛涛 2010 无机材料学报 25 835]

    [20]

    Sinclair D C, Adams T B, Morrison F D, West A R 2002 Appl. Phys. Lett. 80 2153

    [21]

    Zang G Z, Zhang J L, Zheng P, Wang J F, Wang C L 2005 J. Phys. D: Appl. Phys. 38 1824

    [22]

    Morrison F D, Sinclair D C, West A R 2001 J. Am. Ceram. Soc. 84 531

    [23]

    Li W, Schwartz R W 2007 Phys. Rev. B 75 012104

    [24]

    Li J Y, Zhao X T, Li S T, Alim M A 2010 J. Appl. Phys. 108 104104

    [25]

    Li J Y, Xu T W, Li S T, Jin H Y, Li W 2010 J. Alloys Compd. 506 L1

  • [1]

    Subramanian M A, Dong L, Duan N, Reisner B A, Sleight A W 2000 Solid State Chem. 151 323

    [2]

    Ramirez A P, Subramanian M A, Gardel M, Blumberg G, Li D, Vogt T, Shapiro S M 2000 Solid State Commun. 151 217

    [3]

    Subramanian M A, Sleight A W 2002 Solid State Sci. 4 347

    [4]

    He L X, Neaton J B, Cohen M H, Vanderbilt D, Homes C C 2002 Phys. Rev. B 65 214112

    [5]

    He L X, Neaton J B, Vanderbilt D, Choen M H 2003 Phys. Rev. B 67 012103

    [6]

    Cohen M H, Neaton J B, He L X, Vanderbilt D 2003 J. Appl. Phys. 94 3299

    [7]

    Zhang L, Tang Z 2004 Phys. Rev. B 70 174306

    [8]

    Tselev A, Brooks C M, Anlage S M, Zheng H, Riba L S, Ramesh R, Subramanian M A 2004 Phys. Rev. B 70 144101

    [9]

    Chiodelli G, Massarotti V, Capsoni D, Bini M, Azzoni C B, Mozzati M C, Lupotto P 2004 Solid State Commun. 132 241

    [10]

    Fang L, Shen M, Cao W 2004 J. Appl. Phys. 95 6483

    [11]

    Homes C C, Vogt T, Shapiro S M, Wakimoto S, Subramanian M A, Ramirez A P 2003 Phys. Rev. B 67 092106

    [12]

    Chen L, Chen C L, Lin Y, Chen Y B, Chen X H, Bontchev R P, Park C Y, Jacobson A J 2003 Appl. Phys. Lett. 82 2317

    [13]

    Fang T T, Liu C P 2005 Chem. Mater. 17 5167

    [14]

    Fang T T, Shiau H K 2004 J. Am. Ceram. Soc. 87 2072

    [15]

    Fu D S, Taniguchi H, Taniyama T, Itoh M, Koshihara S Y 2008 Chem. Mater. 20 1694

    [16]

    Yang C H, Zhou X L, Xu G, Han G R, Weng W J, Du P Y 2006 J. Chin. Ceram. Soc. 34 753 (in Chinese) [杨昌辉, 周小莉, 徐刚, 韩高荣, 翁文剑, 杜丕一 2006 硅酸盐学报 34 753]

    [17]

    Guillemet-Fritscha S, Lebeyb T, Boulosa M, Duranda B 2006 J. Eur. Ceram. Soc. 26 1245

    [18]

    Marchin L, Guillemet-Fritsch S, Durand B 2007 Prog. Solid State Chem. 36 151

    [19]

    Yang Y, Li S T 2010 J. Inorg. Mater. 25 835 (in Chinese) [杨雁, 李盛涛 2010 无机材料学报 25 835]

    [20]

    Sinclair D C, Adams T B, Morrison F D, West A R 2002 Appl. Phys. Lett. 80 2153

    [21]

    Zang G Z, Zhang J L, Zheng P, Wang J F, Wang C L 2005 J. Phys. D: Appl. Phys. 38 1824

    [22]

    Morrison F D, Sinclair D C, West A R 2001 J. Am. Ceram. Soc. 84 531

    [23]

    Li W, Schwartz R W 2007 Phys. Rev. B 75 012104

    [24]

    Li J Y, Zhao X T, Li S T, Alim M A 2010 J. Appl. Phys. 108 104104

    [25]

    Li J Y, Xu T W, Li S T, Jin H Y, Li W 2010 J. Alloys Compd. 506 L1

  • [1] 赵学童, 廖瑞金, 李建英, 王飞鹏. 直流老化对CaCu3Ti4O12陶瓷介电性能的影响. 物理学报, 2015, 64(12): 127701. doi: 10.7498/aps.64.127701
    [2] 成鹏飞, 王辉, 李盛涛. CaCu3Ti4O12陶瓷的介电特性与弛豫机理. 物理学报, 2013, 62(5): 057701. doi: 10.7498/aps.62.057701
    [3] 毛金伟, 吕树臣, 曲秀荣, 何冬丽, 孟庆裕. 发光二极管用红色荧光粉Sr0.8-xBaxEu0.2WO4的制备和性质研究. 物理学报, 2013, 62(3): 037803. doi: 10.7498/aps.62.037803
    [4] 李盛涛, 王辉, 林春江, 李建英. CaCu3Ti4O12 陶瓷介电模量响应特性的研究. 物理学报, 2013, 62(8): 087701. doi: 10.7498/aps.62.087701
    [5] 王辉, 林春江, 李盛涛, 李建英. CaCu3Ti4O12 陶瓷松弛损耗机理研究. 物理学报, 2013, 62(8): 087702. doi: 10.7498/aps.62.087702
    [6] 桑士晶, 吕树臣, 曲秀荣, 杨晓旭, 张丽丽. 纳米晶ZrO2:Eu3+-Bi3+的制备及Bi3+敏化Eu3+特征发射的研究. 物理学报, 2012, 61(22): 227801. doi: 10.7498/aps.61.227801
    [7] 杨昌平, 李旻奕, 宋学平, 肖海波, 徐玲芳. 氧含量对CaCu3Ti4O12巨介电常数和介电过程的影响. 物理学报, 2012, 61(19): 197702. doi: 10.7498/aps.61.197702
    [8] 郭琳娜, 王育华. 共沉淀法制备Y2SiO5∶Er3+ ,Yb3+ ,Tm3+及其上转换发光性能研究. 物理学报, 2011, 60(2): 027803. doi: 10.7498/aps.60.027803
    [9] 唐红霞, 吕树臣. 发光二极管用红色荧光粉SrMoO4:Eu3+的制备和发射性质. 物理学报, 2011, 60(3): 037805. doi: 10.7498/aps.60.037805
    [10] 曹蕾, 刘鹏, 周剑平, 王亚娟, 苏丽娜, 刘成. CaCu3Ti4O12-MgTiO3陶瓷的介电性能与I-V非线性特征. 物理学报, 2011, 60(3): 037701. doi: 10.7498/aps.60.037701
    [11] 罗晓婧, 杨昌平, 宋学平, 徐玲芳. 巨介电常数氧化物CaCu3Ti4O12的介电和阻抗特性. 物理学报, 2010, 59(5): 3516-3522. doi: 10.7498/aps.59.3516
    [12] 姚长达, 巩江峰, 耿芳芳, 高虹, 徐云玲, 张爱梅, 唐春梅, 朱卫华. 常温常压下BiMnO3纳米粉末的制备与物性分析. 物理学报, 2010, 59(8): 5332-5337. doi: 10.7498/aps.59.5332
    [13] 杨雁, 李盛涛. CaCu3Ti4O12陶瓷的微观结构及直流导电特性. 物理学报, 2009, 58(9): 6376-6380. doi: 10.7498/aps.58.6376
    [14] 严国清, 谢凯旋, 莫仲荣, 路忠林, 邹文琴, 王申, 岳凤娟, 吴镝, 张凤鸣, 都有为. 共沉淀法制备Co掺杂ZnO的室温铁磁性的研究. 物理学报, 2009, 58(2): 1237-1241. doi: 10.7498/aps.58.1237
    [15] 慕春红, 刘 鹏, 贺 颖, 张 丹, 孟 玲, 边小兵. Fe掺杂CaCu3Ti4O12陶瓷的介电性能与弛豫特性研究. 物理学报, 2008, 57(4): 2432-2437. doi: 10.7498/aps.57.2432
    [16] 刘 鹏, 贺 颖, 李 俊, 朱刚强, 边小兵. 添加Nb对CaCu3Ti4O12陶瓷介电性能的影响. 物理学报, 2007, 56(9): 5489-5493. doi: 10.7498/aps.56.5489
    [17] 邵守福, 郑 鹏, 张家良, 钮效鵾, 王春雷, 钟维烈. CaCu3Ti4O12陶瓷的微观结构和电学性能. 物理学报, 2006, 55(12): 6661-6666. doi: 10.7498/aps.55.6661
    [18] 周小莉, 杜丕一. 磁控溅射法制备的CaCu3Ti4O12薄膜. 物理学报, 2005, 54(4): 1809-1813. doi: 10.7498/aps.54.1809
    [19] 李发伸, 王 涛, 王 颖. H2O2氧化法制备Fe3O4纳米颗粒及与共沉淀法制备该样品的比较. 物理学报, 2005, 54(7): 3100-3105. doi: 10.7498/aps.54.3100
    [20] 赵彦立, 焦正宽, 曹光旱. CaCu3Ti4O12块材和薄膜的巨介电常数. 物理学报, 2003, 52(6): 1500-1504. doi: 10.7498/aps.52.1500
计量
  • 文章访问数:  5514
  • PDF下载量:  493
  • 被引次数: 0
出版历程
  • 收稿日期:  2012-01-12
  • 修回日期:  2012-05-17
  • 刊出日期:  2012-10-05

/

返回文章
返回