Phase-composition design of high-hardness and high-electric-conductivity Cu-Ni-Si Alloy

Li Dong-Mei; Han Jing-Yu; Dong Chuang

doi:10.7498/aps.68.20190593

Abstract

Cu-Ni-Si alloy has good electrical conductivity, thermal conductivity, high strength, and high hardness, and is widely used in electronic components and other fields. When the compositions of the Cu-Ni-Si alloy are designed, the determination of the phase component is critical. In this work, the composition of Cu-Ni-Si alloy is designed according to the "precipitation phase" by cluster-plus-glum-atom model. Following the cluster selection criteria, the δ-Ni₂Si, γ-Ni₅Si₂ and β-Ni₃Si phase clusters are determined, respectively, and the corresponding cluster formulas are [Ni-Ni₈Si₅]Ni,[Si-Ni₁₀]Si₃, and [Si-Ni₁₂]Si₃. the compositions of a series of Cu-Ni-Si alloys are designed according to the different precipitated phases of δ-Ni₂Si, γ-Ni₅Si₂, and β-Ni₃Si each with Cu atom content being 93.75%, 95%, 95.8%, 96.7% and 97.5%, respectively. The alloy raw material is melted into alloy ingot in an argon-filled vacuum arc furnace. The ingots undergoes solid-solution at 950 ° C for 1 hour and water quenching then aging treatment at 450 ° C for 4 hour and water quenching. The conductivity and Vickers hardness of the alloy are tested by conductivity meter and hardness meter, respectively. The microstructure of the alloy is characterized by x-ray diffraction (XRD), scanning electron microscopy (SEM), and transmission electron microscopy (TEM). In general, the electrical conductivity of Cu-Ni-Si is the main consideration in the design of alloy composition, the content values of matrix Cu atoms are in the ranges of 90%-95.63% and 95.63%-97.5% respectively, the precipitated phases are designed according to δ-Ni₂Si and γ-Ni₅Si₂ respectively; the content of matrix Cu atoms is over 97.5%, it can be designed according to any phase of δ-Ni₂Si, γ-Ni₅Si₂ and β-Ni₃Si, with no difference in electrical conductivity among them. If the strength of the alloy is the main factor in the composition design, the content values of Cu atoms in the matrix are in the ranges of 90% — 93.93%, 93.93% — 94.34%, 94.34%— 95.63%, and 95.63%—96.12% respectively, according to the composition intervals the precipitated phases are designed as δ-Ni₂Si, γ-Ni₅Si₂, β-Ni₃Si, and γ-Ni₅Si₂, respectively. Once the content of Cu in the matrix is greater than 96.12%, the precipitated phase can be designed according to any of the phases of δ-Ni₂Si, γ-Ni₅Si₂ and β-Ni₃Si.

Keywords:

Cu–Ni–Si alloy /
cluster plus glue atom /
precipitation phase composition design /
high hardness /
electrical conductivity

Authors and contacts

1.
Key Laboratory of Materials Modification by Laser, Iron, and Electron Beams (Ministry of Education), School of Materials Science and Engineering, Dalian University of Technology, Dalian 116024, China
2.
Inner Mongolia University For Nationalities, Tongliao 028000, China

Corresponding author: Dong Chuang, dong@dlut.edu.cn

Funds: Project supported by The National Natural Science Foundation of China (Grant No. 11674045)

FullText HTML : translate this paragraph

References

[1]	Gholami M, Vesely J, Altenberger I, Kuhn H A, Janecek M, Wollmann M, Wagner L 2017 J. Alloys Compd. 696 201 Google Scholar
[2]	Li D M, Jiang B B, Li X N, Wang Qing, Dong C 2019 Acta Metall. Sinica DOI:10.11900/0412.1961.2019.00080
[3]	Corson M G 1927 Aime. Trans. 43 5
[4]	Corson M G 1927 Iron Age 119 421
[5]	Okamoto M 1939 The II. Report. J. Jpn. Inst. Met. 3 336 Google Scholar
[6]	Okamoto M 1939 The II. Report. J. Jpn. Inst. Met. 3 365 Google Scholar
[7]	Robertson W D, Grenier E G, Nole V F 1961 Trans.: Met. Soc. Aime 221 503
[8]	Lei Q, Lia Z, Wang M P, Zhang L, Gong S, Xiao Z, Pan Z Y 2011 J. Alloys Compd. 509 3617 Google Scholar
[9]	Li D M, Wang Q, Jiang B B, Li X N, Zhou W L, Dong C, Wang H, Chen Q X 2017 PNSI 27 467 DOI:10.1016/j.pnsc.2017.06.006
[10]	Lockyer S A, Noble F W 1994 J. Mater. Sci. 29 218 Google Scholar
[11]	Futatsuka R 1997 J. Jpn. Copper Brass Res. Assoc. 36 25
[12]	Zhao D M, Dong Q M, Liu P, Kang B X, Huang J L, Jin Z H 2003 Mater. Chem. Phys. 79 81 Google Scholar
[13]	Yamamoto Y, Sasaki G, Odasin M 1999 J. Jpn Copper Brass Res. Assoc 38 204
[14]	Ryu H J, Baik H K, Hong S H 2000 J. Mater. Sci. 35 3641 Google Scholar
[15]	Zhao D M, Dong Q M, Liu P, Kang B X, Huang J L, Jin Z H 2003 Mater. Sci. Eng. A 361 93 Google Scholar
[16]	Kim Y G, Seong T Y, Han J H 1986 J. Mater. Sci. 21 1357 Google Scholar
[17]	Dong C, Wang Q, Qiang J B, Wang Y M, Jiang N, Han G, Li Y H, Wu J, Xia J H 2007 J. Phys. D: Appl. Phys. 40 273 Google Scholar
[18]	董闯, 董丹丹, 王清 2018 金属学报 54 293 Google Scholar Dong C, Dong D D, Wang Q 2018 Acta Metall. Sin. 54 293 Google Scholar
[19]	Pang C, Wang Q, Zhang R Q, Li Q, Dai X, Dong C, Liaw P K 2015 Mater. Sci. Eng., A 626 369 Google Scholar
[20]	Wang Q, Ji C J, Wang Y M, Qiang J B, Dong C 2013 Metall. Mater. Trans. A 44 1872 Google Scholar
[21]	郝传璞, 王清, 马仁涛, 王英敏, 羌建兵, 董闯 2011 物理学报 60 116101 Google Scholar Hao C P, Wang Q, Ma R T, Wang Y M, Qiang J B, Dong C 2011 Acta Phys. Sin. 60 116101 Google Scholar
[22]	Wang Z R, Qiang J B, Wang Y M, Wang Q, Dong D D, Dong C 2016 Acta Mater. 111 366 Google Scholar
[23]	姜贝贝, 王清, 董闯 2017 物理学报 66 026100 Jiang B B, Wang Q, Dong C 2017 Acta Phys. Sin. 66 026100
[24]	Hong H L, Wang Q, Dong C, Liaw P K 2014 Sci. Rep. 4 7065 DOI:10.1038/srep07065
[25]	Takeuchi A, Inoue A 2005 Mater. Trans. 46 2817 Google Scholar
[26]	Qian S N, Dong C, Liu T Y, Qin Y, Wang Q, Wu Y J, Gu L D, Zou J X, Heng X W, Peng L M, Zeng X Q 2018 J. Mater. Sci. Technol. 34 1132 Google Scholar
[27]	Villars P 1997 Perason’s Handbook Copyright Materials (Park, OH:ASM Interational) pp1−2886
[28]	陈季香, 羌建兵, 王清, 董闯 2012 物理学报 61 046102 Google Scholar Chen J X, Qiang J B, Wang Q, Dong C 2012 Acta Phys. Sin. 61 046102 Google Scholar
[29]	王清 2005博士学位论文 (大连: 大连理工大学) Wang Q 2005 Ph. D. Dissertation (Dalian: Dalian University of Technology) (in Chinese)
[30]	Luo L J, Jiang W, Wang Q, Wang Y M, Han G, Dong C 2010 Philos. Mag. 90 3961 Google Scholar
[31]	Hu T, Chen J H, Liu J Z, Liu Z R, Wu C L 2013 Acta Mater. 61 1210 Google Scholar
[32]	Hu J, Shi Y N, Sauvage X, Sha G, Lu K 2017 Science 355 1292 Google Scholar

Cited By

图 1 基体Cu中立方八面体团簇

Figure 1. Cubooctahedral cluster in Cu matrix.

DownLoad: Full-Size Img PowerPoint

图 2 δ-Ni₂Si团簇的三种构型

Figure 2. Three configurations of δ-Ni₂Si cluster

DownLoad: Full-Size Img PowerPoint

图 3 δ-Ni₂Si相中分别以Ni¹, Ni², Si¹为心部原子的团簇径向原子密度

Figure 3. Radial atomic density around 3 different sites Ni¹, Ni² and Si¹ in the δ-Ni₂Si phase.

DownLoad: Full-Size Img PowerPoint

图 4 γ-Ni₅Si₂团簇的十三种构型

Figure 4. Thirteen configurations of γ-Ni₅Si₂ cluster

DownLoad: Full-Size Img PowerPoint

图 5 γ-Ni₅Si₂晶体相中分别以Ni¹, Ni², Si¹, Ni³, Ni⁴, Si², Si³, Si⁴, Si⁵, Ni⁵, Ni⁶, Ni⁷, Ni⁸为心的团簇径向原子分布

Figure 5. Radial atomic density around 13 different sites Ni¹, Ni², Si¹, Ni³, Ni⁴, Si², Si³, Si⁴, Si⁵, Ni⁵, Ni⁶, Ni⁷, Ni⁸ and Ni⁸ in the γ-Ni₅Si₂ phase.

DownLoad: Full-Size Img PowerPoint

图 6 β-Ni₃Si团簇的两种构型

Figure 6. Two configurations of β-Ni₃Si cluster

DownLoad: Full-Size Img PowerPoint

图 7 Ni/Si(at.%)分别为 (a) 2, (b) 2.5和(c) 3在C_Cu分别为 93.75%, 95%, 95.83%, 96.7%和97.5% 每一成分点处的合金XRD谱图

Figure 7. XRD patterns of the alloys when C_Cu is 93.75%, 95%, 95.83%, 96.7% and 97.5%, and the Ni/Si (at.%) is (a) 2, (b) 2.5 and (c) 3 in each composition point, respectively.

DownLoad: Full-Size Img PowerPoint

图 8 合金的微观形貌. C_Cu为 93.75% 时Ni/Si 分别为(a) 2, (b) 2.5和(c) 3及C_Cu为96.7% 时Ni/Si 分别为(d) 2, (e) 2.5或(f) 3

Figure 8. The microstructure of the alloys. The Ni/Si is (a) 2, (b) 2.5 and (c) 3 when C_Cu is 93.75% and Ni/Si is (a) 2, (b) 2.5 and (c) 3 when C_Cu is 96.7%, respectively.

DownLoad: Full-Size Img PowerPoint

图 9 Cu_96.7Ni_2.36Si_0.94 样品的(a)明场像和(b)选区衍射图***图(b)(123)中，2上面也有横杠***

Figure 9. (a) Bright-field micrographs and (b) selected area diffraction patterns of the Cu_96.7Ni_2.36Si_0.94 sample.

DownLoad: Full-Size Img PowerPoint

图 10 (a) Ni/Si分别为2, 2.5, 3时, 维氏硬度和导电性随C_Cu的变化; 三元相图中 (b) 导电性和(c)维氏硬度随Cu, Ni和Si元素的原子分数的变化***图(a)和(b)中均应为%IACS***

Figure 10. (a) Ni/Si is 2, 2.5 and 3 respectively, the variation of vickers hardness and electrical conductivity as increase C_Cu; the variation of (b) electrical conductivity and (c) vickers hardness as atomic percent of Cu,Ni and Si in ternary phase diagram.

DownLoad: Full-Size Img PowerPoint

表 1 δ-Ni₂Si相中以3种占位原子为心的径向原子分布

Table 1. Radial atomic distributions around 3 different sites in the δ-Ni₂Si phase.

心部原子	壳层原子数目	壳层原子种类	壳层原子与心部原子的距离r/nm	径向原子密度ρ/nm^-3	团簇	团簇构型
Ni¹	1	Si¹	0.20823	52.909	Ni₉Si₄	图2(a)
	2	Si¹	0.22614	82.615
	1	Si¹	0.23232	95.245
	2	Ni²	0.25359	102.526
	1	Ni²	0.26231	105.871
	1	Ni²	0.26268	118.602
	2	Ni¹	0.27021	133.174
	2	Ni²	0.27132	155.464
	1	Si¹	0.29611	128.795
Ni²	2	Si¹	0.24629	47.964	Ni₉Si₅	图2(b)
	2	Si¹	0.24872	77.619
	1	Si¹	0.24972	92.092
	2	Ni¹	0.25359	117.172
	2	Ni²	0.25818	138.792
	1	Ni¹	0.26231	145.573
	1	Ni¹	0.26268	158.136
	2	Ni¹	0.27132	167.423
	1	Si¹	0.32162	107.695
	2	Ni²	0.34426	93.668
Si¹	1	Ni¹	0.20823	52.909	SiNi₉	图2(c)
	2	Ni¹	0.22614	82.615
	1	Ni¹	0.23232	95.245
	2	Ni²	0.24629	111.915
	2	Ni²	0.24872	139.715
	1	Ni²	0.24972	153.381
	1	Ni¹	0.29611	101.196
	2	Si¹	0.31484	99.496
	1	Ni²	0.32162	100.515
	2	Si¹	0.34056	96.754

DownLoad: CSV

表 2 γ-Ni₅Si₂ 相中以13种占位原子为心的径向原子分布

Table 2. Radial atomic distributions around 13 different sites in the γ-Ni₅Si₂ phase.

心部原子	壳层原子数目	壳层原子种类	壳层原子与心部原子的距离r/nm	径向原子密度ρ/nm^–3	团簇	团簇构型
Ni¹	3	Si⁵	0.23282	113.557	Ni₇Si₅	图4(a)
	6	Ni⁸	0.25853	138.229
	2	Si¹	0.26156	160.177
	6	Ni⁷	0.32954	120.138
	6	Ni⁴	0.39376	93.896
	6	Ni⁶	0.42716	91.935
	3	Si⁵	0.43428	96.236
	6	Ni⁸	0.45646	97.946
	6	Si²	0.47401	100.921
	2	Ni²	0.49734	91.258
Ni²	1	Ni²	0.23332	37.61	Ni₈Si₄	图4(b)
	1	Si¹	0.23578	54.668
	3	Si⁴	0.2421	100.995
	3	Ni⁶	0.24757	141.671
	3	Ni⁵	0.25331	176.342
	3	Ni⁵	0.34555	86.834
	3	Ni⁷	0.34582	103.957
	3	Ni³	0.38621	87.072
	3	Si³	0.4174	78.829
	3	Ni⁶	0.41824	88.149
	3	Ni⁵	0.42043	96.421
	3	Ni³	0.43617	94.99
Ni³	3	Si⁴	0.24409	65.696	Ni₁₀Si₄	图4(c)
	1	Si²	0.24965	76.755
	3	Ni⁵	0.25453	115.879
	3	Ni⁶	0.26112	147.572
	3	Ni⁵	0.26706	175.563
	1	Si³	0.36558	73.329
	3	Ni⁷	0.37339	82.588
	3	Ni²	0.38621	87.072
	3	Ni⁶	0.41335	81.169
	3	Ni⁵	0.42222	85.68
Ni⁴	3	Si⁵	0.23225	76.265	Ni₁₀Si₄	图4(d)
	1	Si³	0.25456	72.399
	3	Ni⁸	0.25532	114.807
	3	Ni⁷	0.25574	157.083
	3	Ni⁸	0.27402	162.522
	1	Si²	0.35821	77.949
	3	Ni⁶	0.37974	78.514
	3	Ni¹	0.39376	82.159
	3	Ni⁷	0.39797	90.948
	3	Ni⁸	0.41739	88.689
Ni⁵	1	Si⁴	0.23142	38.544	Ni₈Si₃	图4(e)
	1	Si³	0.23246	57.044
	1	Si⁴	0.24177	67.606
	1	Ni⁶	0.25071	75.786
	1	Ni⁶	0.25316	88.328
	1	Ni²	0.25331	102.866
	1	Ni⁵	0.25375	116.951
	1	Ni³	0.26706	137.942
	1	Ni⁶	0.28031	130.136
	2	Ni⁵	0.29349	132.276
Ni⁶	1	Si²	0.22997	39.278	Ni₉Si₄	图4(f)
	1	Si¹	0.23889	52.56
	1	Si⁴	0.2445	65.366
	1	Ni²	0.24757	78.706
	1	Si³	0.24916	92.651
	1	Ni⁵	0.25071	103.499
	1	Ni⁵	0.25316	117.77
	1	Ni⁸	0.25429	130.733
	1	Ni⁷	0.25495	144.134
	1	Ni⁷	0.26059	148.474
	1	Ni³	0.26112	160.988
	1	Ni⁷	0.26728	162.621
Ni⁷	1	Si³	0.22567	41.566	Ni₉Si₄	图4(g)
	1	Si¹	0.22958	59.218
	1	Si⁵	0.23849	70.434
	1	Si²	0.24038	85.982
	1	Ni⁸	0.24588	96.408
	1	Ni⁸	0.25044	106.443
	1	Ni⁶	0.25495	115.307
	1	Ni⁴	0.25574	128.522
	1	Ni⁵	0.26021	135.569
	1	Ni⁶	0.26059	148.474
	1	Ni⁶	0.26728	150.111
	1	Ni⁸	0.27224	153.893
Ni⁸	1	Si⁵	0.23059	38.962	Ni₉Si₄	图4(h)
	1	Si⁵	0.24054	51.486
	1	Ni⁸	0.2457	64.413
	1	Ni⁷	0.24588	80.34
	1	Si²	0.24656	95.613
	1	Ni⁷	0.25044	106.443
	1	Ni⁶	0.25429	116.207
	1	Ni⁴	0.25531	129.173
	1	Ni¹	0.25853	138.229
Ni⁸	1	Si¹	0.27197	130.605	Ni₉Si₄	图4(h)
	1	Ni⁷	0.27224	142.055
	1	Ni⁴	0.27402	150.913
Si¹	3	Ni⁷	0.22958	78.957	SiNi₁₁	图4(i)
	1	Ni²	0.23578	91.113
	3	Ni⁶	0.23889	140.161
	1	Ni¹	0.26156	120.132
	3	Ni⁸	0.27197	142.479
	3	Ni⁵	0.34489	87.334
	3	Si⁵	0.35017	100.131
	3	Si²	0.38543	87.602
	3	Si³	0.39237	94.898
	3	Si⁴	0.41136	92.647
Si²	3	Ni⁶	0.22997	78.556	SiNi₁₀	图4(j)
	3	Ni⁷	0.24038	120.375
	3	Ni⁸	0.24656	159.354
	1	Ni³	0.24965	168.861
	3	Ni⁵	0.33462	89.249
	3	Si⁵	0.35153	93.475
	1	Ni⁴	0.35821	93.539
	3	Si¹	0.38543	87.602
	3	Si³	0.38982	96.772
	3	Si⁴	0.40727	95.466
Si³	3	Ni⁷	0.22567	83.132	SiNi₁₀	图4(k)
	3	Ni⁵	0.23246	133.102
	3	Ni⁶	0.24916	154.418
	1	Ni⁴	0.25456	159.277
	3	Ni⁸	0.33473	89.161
	3	Si⁴	0.35895	87.797
	1	Ni³	0.36558	87.995
	3	Si²	0.38982	84.676
	3	Si¹	0.39237	94.898
	3	Si⁵	0.40056	100.344
Si⁴	2	Ni⁵	0.23142	57.816	SiNi₁₀	图4(l)
	2	Ni⁵	0.24177	84.507
	2	Ni²	0.2421	117.827
	2	Ni³	0.24409	147.817
	2	Ni⁶	0.2445	179.758
	2	Ni⁵	0.29512	120.803
	2	Si³	0.35895	77.468
	2	Si⁴	0.36743	81.857
	4	Si⁴	0.39431	81.816
	2	Si²	0.40727	81.323
Si⁵	2	Ni⁸	0.23059	58.364	SiNi₉	图4(m)
	2	Ni⁴	0.23225	95.331
	1	Ni¹	0.23282	113.559
	2	Ni⁷	0.23849	140.868
	2	Ni⁸	0.24054	171.621
	2	Ni⁸	0.28808	119.887
	2	Si¹	0.35017	77.879
	2	Si²	0.35153	76.979
	4	Si⁵	0.37643	80.603
	2	Si³	0.40056	74.329

DownLoad: CSV

表 3 β-Ni₃Si相中以不同原子为心的径向原子分布

Table 3. Radial atomic distributions around 2 different sites in the β-Ni₃Si phase.

心部原子	壳层原子数	壳层原子种类	壳层原子与心部原子的距离r/nm	径向原子密度ρ/ nm⁻³	团簇	团簇构型
Ni¹	4	Si¹	0.24791	203.795	Ni₉Si₄	图6(a)
Ni¹	8	Ni¹	0.24791	203.795	Ni₉Si₄	图6(a)
Si¹	12	Ni¹	0.24791	203.795	SiNi₁₂	图6(b)

DownLoad: CSV

表 4 Cu-Ni-Si-M (M = Fe or null)系列合金的Ni/Si(原子比)、团簇成分式、成分(原子分数)、维氏硬度(kgf/mm²)和导电率(%IACS)

Table 4. Ni/Si(at.%), Cluster formula, Composition(at.%), Vickers Hardness (kgf/mm²) and Electrical conductivity(%IACS) of Cu-Ni-Si-M (M = Fe or null) alloys.

Ni/Si (at.%)	cluster formulas	composition wt.% /at.%	Vickers Hardness kgf·mm^–2	Electrical Conductivity /%IACS
2	[(Fe_1/15Ni_9/15Si_5/15)Cu₁₂]Cu₃	95.18Cu3.52Ni0.93Si0.37Fe (Cu_93.75Ni_3.75Si_2.08Fe_0.42)	258	35
	([(Ni_10/15Si_5/15)Cu₁₂]Cu₃)₄+([CuCu₁₂]Cu₃)	96.14Cu3.11Ni0.75Si (Cu₉₅Ni_3.33Si_1.67)	161	51
	([(Ni_10/15Si_5/15)Cu₁₂]Cu₃)₂+([CuCu₁₂]Cu₃)	96.79Cu2.59Ni0.62Si (Cu_95.83Ni_2.78Si_1.39)	189	35
	{[(Ni_10/15Si_5/15)_1.0602Cu₁₂]Cu₃}_0.996 +{[CuCu₁₂]Cu₃}	97.4Cu2.1Ni0.5Si (Cu_96.7Ni_2.2Si_1.1)	191	40
	([(Ni_10/15Si_5/15)Cu₁₂]Cu₃)₂+([CuCu₁₂]Cu₃)₃	98.08Cu1.55Ni0.37Si (Cu_97.5Ni_1.67Si_0.83)	172	48
2.5	[(Fe_1/14Ni_9/14Si_4/14)Cu₁₂]Cu₃	95.04Cu3.75Ni0.8Si0.41Fe (Cu_93.75Ni_4.01Si_1.79Fe_0.45)	262	32.5
	([(Ni_10/14Si_4/14)Cu₁₂]Cu₃)₄+([CuCu₁₂]Cu₃)	96.03Cu3.33Ni0.64Si (Cu₉₅Ni_3.57Si_1.43)	201	41
	([(Ni_10/14Si_4/14)Cu₁₂]Cu₃)₂+([CuCu₁₂]Cu₃)	96.69Cu2.78Ni0.53Si (Cu_95.83Ni_2.98Si_1.19)	201	38
	{([(Ni_10/14Si_4/14) _1.0602Cu₁₂]Cu₃)}_{0.996 +}([CuCu₁₂]Cu₃)	97.39Cu2.2Ni0.41Si (Cu_96.7Ni_2.36Si_0.94)	168	41
	([Ni_10/14Si_4/14)Cu₁₂]Cu₃)₂+([CuCu₁₂]Cu₃)₃	98.02Cu1.66Ni0.32Si (Cu_97.5Ni_1.79Si_0.71)	176	48
3	([(Fe_1/16Ni_11/16Si_4/16)Cu₁₂]Cu₃)	94.93Cu4.02Ni0.7Si0.35Fe (Cu_93.75Ni_4.3Si_1.56Fe_0.39)	241	30
	([(Ni_12/16Si_4/16)Cu₁₂]Cu₃)₄+([CuCu₁₂]Cu₃)	95.94Cu3.5Ni0.56Si (Cu₉₅Ni_3.75Si_1.25)	225	33
	([(Ni_12/16Si_4/16)Cu₁₂]Cu₃)₂+([CuCu₁₂]Cu₃)	96.63Cu2.91Ni0.46Si (Cu_95.83Ni_3.13Si_1.04)	191	36
	{([(Ni_12/16Si_4/16)_1.0602Cu₁₂]Cu₃)}_0.996 + ([CuCu₁₂]Cu₃)	97.33Cu2.31Ni0.36Si (Cu_96.7Ni_2.47Si_0.83)	160	39
	([(Ni_12/16Si_4/16)Cu₁₂]Cu₃)₂+([CuCu₁₂]Cu₃)₃	97.98Cu1.74Ni0.28Si (Cu_97.5Ni_1.87Si_0.63)	171	47

DownLoad: CSV

[1]	Gholami M, Vesely J, Altenberger I, Kuhn H A, Janecek M, Wollmann M, Wagner L 2017 J. Alloys Compd. 696 201 Google Scholar
[2]	Li D M, Jiang B B, Li X N, Wang Qing, Dong C 2019 Acta Metall. Sinica DOI:10.11900/0412.1961.2019.00080
[3]	Corson M G 1927 Aime. Trans. 43 5
[4]	Corson M G 1927 Iron Age 119 421
[5]	Okamoto M 1939 The II. Report. J. Jpn. Inst. Met. 3 336 Google Scholar
[6]	Okamoto M 1939 The II. Report. J. Jpn. Inst. Met. 3 365 Google Scholar
[7]	Robertson W D, Grenier E G, Nole V F 1961 Trans.: Met. Soc. Aime 221 503
[8]	Lei Q, Lia Z, Wang M P, Zhang L, Gong S, Xiao Z, Pan Z Y 2011 J. Alloys Compd. 509 3617 Google Scholar
[9]	Li D M, Wang Q, Jiang B B, Li X N, Zhou W L, Dong C, Wang H, Chen Q X 2017 PNSI 27 467 DOI:10.1016/j.pnsc.2017.06.006
[10]	Lockyer S A, Noble F W 1994 J. Mater. Sci. 29 218 Google Scholar
[11]	Futatsuka R 1997 J. Jpn. Copper Brass Res. Assoc. 36 25
[12]	Zhao D M, Dong Q M, Liu P, Kang B X, Huang J L, Jin Z H 2003 Mater. Chem. Phys. 79 81 Google Scholar
[13]	Yamamoto Y, Sasaki G, Odasin M 1999 J. Jpn Copper Brass Res. Assoc 38 204
[14]	Ryu H J, Baik H K, Hong S H 2000 J. Mater. Sci. 35 3641 Google Scholar
[15]	Zhao D M, Dong Q M, Liu P, Kang B X, Huang J L, Jin Z H 2003 Mater. Sci. Eng. A 361 93 Google Scholar
[16]	Kim Y G, Seong T Y, Han J H 1986 J. Mater. Sci. 21 1357 Google Scholar
[17]	Dong C, Wang Q, Qiang J B, Wang Y M, Jiang N, Han G, Li Y H, Wu J, Xia J H 2007 J. Phys. D: Appl. Phys. 40 273 Google Scholar
[18]	董闯, 董丹丹, 王清 2018 金属学报 54 293 Google Scholar Dong C, Dong D D, Wang Q 2018 Acta Metall. Sin. 54 293 Google Scholar
[19]	Pang C, Wang Q, Zhang R Q, Li Q, Dai X, Dong C, Liaw P K 2015 Mater. Sci. Eng., A 626 369 Google Scholar
[20]	Wang Q, Ji C J, Wang Y M, Qiang J B, Dong C 2013 Metall. Mater. Trans. A 44 1872 Google Scholar
[21]	郝传璞, 王清, 马仁涛, 王英敏, 羌建兵, 董闯 2011 物理学报 60 116101 Google Scholar Hao C P, Wang Q, Ma R T, Wang Y M, Qiang J B, Dong C 2011 Acta Phys. Sin. 60 116101 Google Scholar
[22]	Wang Z R, Qiang J B, Wang Y M, Wang Q, Dong D D, Dong C 2016 Acta Mater. 111 366 Google Scholar
[23]	姜贝贝, 王清, 董闯 2017 物理学报 66 026100 Jiang B B, Wang Q, Dong C 2017 Acta Phys. Sin. 66 026100
[24]	Hong H L, Wang Q, Dong C, Liaw P K 2014 Sci. Rep. 4 7065 DOI:10.1038/srep07065
[25]	Takeuchi A, Inoue A 2005 Mater. Trans. 46 2817 Google Scholar
[26]	Qian S N, Dong C, Liu T Y, Qin Y, Wang Q, Wu Y J, Gu L D, Zou J X, Heng X W, Peng L M, Zeng X Q 2018 J. Mater. Sci. Technol. 34 1132 Google Scholar
[27]	Villars P 1997 Perason’s Handbook Copyright Materials (Park, OH:ASM Interational) pp1−2886
[28]	陈季香, 羌建兵, 王清, 董闯 2012 物理学报 61 046102 Google Scholar Chen J X, Qiang J B, Wang Q, Dong C 2012 Acta Phys. Sin. 61 046102 Google Scholar
[29]	王清 2005博士学位论文 (大连: 大连理工大学) Wang Q 2005 Ph. D. Dissertation (Dalian: Dalian University of Technology) (in Chinese)
[30]	Luo L J, Jiang W, Wang Q, Wang Y M, Han G, Dong C 2010 Philos. Mag. 90 3961 Google Scholar
[31]	Hu T, Chen J H, Liu J Z, Liu Z R, Wu C L 2013 Acta Mater. 61 1210 Google Scholar
[32]	Hu J, Shi Y N, Sauvage X, Sha G, Lu K 2017 Science 355 1292 Google Scholar

[1]	Jiang Fu-Shi, Wang Wei-Hua, Li Hong-Ming, Wang Qing, Dong Chuang. First-principles calculations of Ni-Al-Cr alloys using cluster-plus-glue-atom model. Acta Physica Sinica, 2022, 71(20): 207101. doi: 10.7498/aps.71.20221036
[2]	Bao Kuo, Ma Shuai-Ling, Xu Chun-Hong, Cui Tian. Design of ultra-hard multifunctional transition metal compounds. Acta Physica Sinica, 2017, 66(3): 036104. doi: 10.7498/aps.66.036104
[3]	Wang Tong, Hu Xiao-Gang, Wu Ai-Min, Lin Guo-Qiang, Yu Xue-Wen, Dong Chuang. Explanation of Cr-C eutectic points using the cluster-plus-glue-atom model. Acta Physica Sinica, 2017, 66(9): 092101. doi: 10.7498/aps.66.092101
[4]	Jiang Bei-Bei, Wang Qing, Dong Chuang. A cluster-formula composition design approach based on the local short-range order in solid solution structure. Acta Physica Sinica, 2017, 66(2): 026102. doi: 10.7498/aps.66.026102
[5]	Hong Hai-Lian, Dong Chuang, Wang Qing, Zhang Yu, Geng Yao-Xiang. Cluster-plus-glue-atom model of FCC solid solutions and composition explanation of typical industrial alloys. Acta Physica Sinica, 2016, 65(3): 036101. doi: 10.7498/aps.65.036101
[6]	Yang Jian-Qun, Li Xing-Ji, Ma Guo-Liang, Liu Chao-Ming, Zou Meng-Nan. Effect of 170 keV proton irradiation on structure and electrical conductivity of multi-walled carbon nanotubes film. Acta Physica Sinica, 2015, 64(13): 136401. doi: 10.7498/aps.64.136401
[7]	Li Xiao-Na, Zheng Yue-Hong, Li Zhen, Wang Miao, Zhang Kun, Dong Chuang. High temperature oxidation resistance of cluster model designed alloys Cu-Cu12-[Mx/(12+x)Ni12/(12+x)]5 (M=Si, Cr, Cr+Fe). Acta Physica Sinica, 2014, 63(2): 028102. doi: 10.7498/aps.63.028102
[8]	Han Jun, Zhang Peng, Gong Hai-Bo, Yang Xiao-Peng, Qiu Zhi-Wen, Zi Min, Cao Bing-Qiang. Influence of the growth conditions on the transparent conductive properties of ZnO：Al thin films grown by pulsed laser deposition. Acta Physica Sinica, 2013, 62(21): 216102. doi: 10.7498/aps.62.216102
[9]	Wu Yong-Sheng, Wang Bing. Preparation and physical properties of (BEDT-TTF)[FeBr4] crystal. Acta Physica Sinica, 2012, 61(5): 056104. doi: 10.7498/aps.61.056104
[10]	Hao Chuan-Pu, Wang Qing, Ma Ren-Tao, Wang Ying-Min, Qiang Jian-Bing, Dong Chuang. Cluster-plus-glue-atom model in bcc solid solution alloys. Acta Physica Sinica, 2011, 60(11): 116101. doi: 10.7498/aps.60.116101
[11]	Ri Chung-Ho, Li Lin, Zhu Lin. First-principles study of the electronic structure and electric conductivity in W-type hexagonal ferrite BaFe18O27. Acta Physica Sinica, 2011, 60(10): 107102. doi: 10.7498/aps.60.107102
[12]	Li Ke, Dong Rui-Xin, Ban Ge, Han Hong-Wen, Su Wei, Yan Xun-Ling. The effect of nickel ions on structure and conductivity of DNA. Acta Physica Sinica, 2009, 58(9): 6477-6481. doi: 10.7498/aps.58.6477
[13]	Meng Xian-Lan, Gao Xu-Tuan, Qu Zhen, Kang Da-Wei, Liu De-Sheng, Xie Shi-Jie. Effects of interfacial couplings on charge transport properties of DNA molecule. Acta Physica Sinica, 2008, 57(8): 5316-5322. doi: 10.7498/aps.57.5316
[14]	Wang Qi, Zhao Hua-Bo, Zhang Zhao-Hui. Conductance enhancement phenomenon of graphene ribbons on highly oriented pyrolytic graphite surfaces studied by scanning probe microscopy. Acta Physica Sinica, 2008, 57(5): 3059-3063. doi: 10.7498/aps.57.3059
[15]	LU YA-FENG, WU XIAO-ZU, LI QING-YUN, ZHOU LIAN, XIN MIAN-RONG, LUO CHANG-XUN. SUPERCONDUCTIVITY OF RICH-Ca,Cu Bi(Pb)-Sr- Ca-Cu-O SYSTEM. Acta Physica Sinica, 1992, 41(7): 1157-1161. doi: 10.7498/aps.41.1157
[16]	XU ZHU-AN, OUYANG SONG, FANG MING-HU, WANG JING-SONG, ZHANG SHI-YONG, SHEN MING, ZHANG QI-RUI. SUPERCONDUCTIVITY IN Y1-xCaxBa2Cu3-xMxO7-δ (M=Fe, Ni) SYSTEMS. Acta Physica Sinica, 1992, 41(9): 1510-1516. doi: 10.7498/aps.41.1510
[17]	CHEN SHI-MIN, SUN JI-XIN. ELECTRONIC STRUCTURE AND SUPERCONDUCTIVITY OF Nd-(Ce)-Cu-O. Acta Physica Sinica, 1990, 39(12): 1994-1998. doi: 10.7498/aps.39.1994
[18]	WU BAI-MEI, CHEN ZHAO-JIA. THE ELECTRON STRUCTURE, MAGNETISM AND SUPERCONDUCTIVITY OF AMORPHOUS Nb-Ni ALLOYS. Acta Physica Sinica, 1988, 37(1): 29-35. doi: 10.7498/aps.37.29
[19]	Chen Xi-chen, Guan Wei-yan, Yi Sun-sheng, Wang Zu-lun, Lin Ying. A STUDY ON THE SUPERCONDUCTIVITY OF FAST QUENCHED Al-Si-Ge ALLOY. Acta Physica Sinica, 1983, 32(4): 446-459. doi: 10.7498/aps.32.446
[20]	GUAN WEI-YAN, CHEN XI-SHEN, WANG ZU-LUN, YI SUN-SHENG, LIN YING. A STUDY OF THE SUPER-CONDUCTIVITY OF FAST QUENCHED Al-Si ALLOY. Acta Physica Sinica, 1982, 31(4): 485-502. doi: 10.7498/aps.31.485

Catalog

Vol. 68, Issue 19 - 2019-10-05

Metrics

Abstract views: 12193
PDF Downloads: 108
Cited By: 0

姓名
邮箱
手机号码
标题
留言内容
验证码

Search

Article

留言板