木文用X射线粉末衍射法配合差热分析法,确证了金属间化合物DyNi4的存在,发现了一种新的金属间化合物Dy4Ni17,并作出了这个二元系合金相图。此合金系中共存在着十种金属间化合物,它们是:Dy3Ni,Dy3Ni2,DyNi,DyNi2,DyNi3,Dy2Ni7,DyNi4The dysprosium-nickel phase diagram has been completed by X-rays in conjunction with differential thermal analysis. The intermetallic compound DyNi4 was detected, and the new intermetallic compound Dy4Ni17 was observed.In this system there exist ten intermetallic compounds: Dy3Ni,Dy3Ni2,DyNi,DyNi2,DyNi3,Dy2Ni7,DyNi4,Dy4Ni17,DyNi5, and Dy2Ni17. The intermetallic compounds DyNi and DyNi5 melt congruently at 1248℃and 1387℃, and the intermetallic compounds Dy3NiDy3Ni2,DyNi2,DyNi3,Dy2Ni7,DyNi4,Dy4Ni17 and Dy2Ni17 are formed by eight peritectic reactions at 762℃, 928℃, 1258℃, 1283℃, 1307℃, 1336℃, 1352℃ and 1321℃, respectively. Three eutectic reactions occur: at 31 at% Ni and 693℃, 56 at% Ni and 1173℃, 93 at% Ni and 1279℃. Neither Dy in Ni nor Ni in Dy shows any detectable solid solubility.
计量
- 文章访问数: 5034
- PDF下载量: 480
- 被引次数: 0
Dy-Ni二元系合金相图
- 收稿日期: 1981-06-15
- 刊出日期: 2005-07-27
摘要: 木文用X射线粉末衍射法配合差热分析法,确证了金属间化合物DyNi4的存在,发现了一种新的金属间化合物Dy4Ni17,并作出了这个二元系合金相图。此合金系中共存在着十种金属间化合物,它们是:Dy3Ni,Dy3Ni2,DyNi,DyNi2,DyNi3,Dy2Ni7,DyNi4
English Abstract
PHASE DIAGRAM OF THE ALLOYS IN Dy-Ni BINARY SYSTEM
- Received Date:
15 June 1981
- Published Online:
27 July 2005
Abstract: The dysprosium-nickel phase diagram has been completed by X-rays in conjunction with differential thermal analysis. The intermetallic compound DyNi4 was detected, and the new intermetallic compound Dy4Ni17 was observed.In this system there exist ten intermetallic compounds: Dy3Ni,Dy3Ni2,DyNi,DyNi2,DyNi3,Dy2Ni7,DyNi4,Dy4Ni17,DyNi5, and Dy2Ni17. The intermetallic compounds DyNi and DyNi5 melt congruently at 1248℃and 1387℃, and the intermetallic compounds Dy3NiDy3Ni2,DyNi2,DyNi3,Dy2Ni7,DyNi4,Dy4Ni17 and Dy2Ni17 are formed by eight peritectic reactions at 762℃, 928℃, 1258℃, 1283℃, 1307℃, 1336℃, 1352℃ and 1321℃, respectively. Three eutectic reactions occur: at 31 at% Ni and 693℃, 56 at% Ni and 1173℃, 93 at% Ni and 1279℃. Neither Dy in Ni nor Ni in Dy shows any detectable solid solubility.