电脉冲对多晶La0.7Ca0.3MnO3比热的影响

吴子华 谢华清

引用本文:
Citation:

电脉冲对多晶La0.7Ca0.3MnO3比热的影响

吴子华, 谢华清

The effect of electric pulses on the specific heat of polycrystalline La0.7Ca0.3MnO3

Wu Zhi-Hua, Xie Hua-Qing
PDF
导出引用
  • 对电脉冲诱导的不同电阻态下La0.7Ca0.3MnO3样品的比热进行了研究.实验结果表明,电脉冲导致La0.7Ca0.3MnO3样品比热随电阻状态发生可逆变化.比热随电阻状态的减小而减小.低温比热拟合及不同电阻状态下的比热差与温度关系说明,声子对比热的贡献不随电阻状态变化,磁性和载流子对比热的贡献是导致La0.7Ca0.3MnO3样品比热变化的原因.电脉冲诱导O离子沿一维扩展性缺陷的电化学迁移,导致材料中局部区域的O离子浓度发生变化.O离子浓度的变化导致载流子浓度的变化,同时载流子浓度的变化将使得低温下磁性耦合强度发生变化,从而导致比热发生变化.
    The specific heat of polycrystalline La0.7Ca0.3MnO3 at different resistance states induced by electric pulses was studied. It was found that the specific heat decreases with decreasing resistance, and the change is reversible. The reversible change of specific heat was shown to be mainly due to the ferromagnetic-spin-waves component and charge carriers component by fitting the specific heat data. These results indicate that the electric pulses modulated the magnetic configuration of LCMO at low temperature, which would result in large variation in magnetization and specific heat associated with ferromagnetic-spin-waves.
    • 基金项目: 上海市教育委员会和上海市教育发展基金会优秀青年科学基金(批准号: EGD08012)和曙光计划(批准号: 07SG56)、上海市高校特聘教师“东方学者”岗位计划和国家自然科学基金(批准号: 50876058)资助的课题.
    [1]

    [1]Liu S Q, Wu N J, Lgnatiev A 2000 Appl. Phys. Lett. 76 2749

    [2]

    [2]Ahn K H, Lookman T, Bishop A R 2004 Nature 428 401

    [3]

    [3]Nagaev E L 1996 Phys. Lett. A 218 367

    [4]

    [4]Li Q, Wang Z G, Liu S, Xing Z W, Liu M 2007 Acta Phys. Sin. 56 1637 (in Chinese) [李倩、王之国、刘甦、刑仲文、刘楣 2007 物理学报 56 1637]

    [5]

    [5]Tulina N A, Sirotkin V V 2004 Physica C 400 105

    [6]

    [6]Szot K, Speier W, Bihlmayer G, Waser R 2006 Nat. Mater. 5 312

    [7]

    [7]Baikalov A, Wang Y Q, Shen B, Lorenz B, Tsui S, Sun Y Y, Xue Y Y 2003 Appl. Phys. Lett. 83 957

    [8]

    [8]Nian Y B, Strozier J, Wu N J, Chen X, Ignatiev A 2007 Phys. Rev. Lett. 98 146403

    [9]

    [9]Ziese M, Bollero A, Panagiotopoulos I, Moutis N 2005 Phys. Rev. B 72 024453

    [10]

    ]Long Y Z, Zheng P, Zhang Z M, Wei Z X, Wan M X, Chen Z J, Wang N L 2002 Acta Phys. Sin. 51 2090 (in Chinese) [龙云泽、郑萍、张志明、魏志祥、万梅香、陈兆甲、王楠林 2002物理学报 51 2090]

    [11]

    ]Ghivelder L, Abrego C I, Gusmao M A, Alonso J A, Cohen L F 1999 Phys. Rev.B 60 12184

    [12]

    ]Luo J L, Zhang J, Chen Z J, Bai H Y, Wang Y P, Meng J B, Jin D, Ren Z A, 2001 Chin. Phys. Lett. 18 820

    [13]

    ]Xu J, Luo J L, Chen Z J, Long Y Z, Bai H Y, Wan M X, Wang W L 2003 Acta Phys. Sin. 52 947 (in Chinese) [许杰、雒建林、陈兆甲、龙云泽、白海洋、万梅香、王万录 2003 物理学报 52 947]

    [14]

    ]Woodfield B F, Wilson M L, Byers J M 1997 Phys. Rev. Lett. 78 3201

    [15]

    ]Zhang J, Luo J L, Bai H Y,Chen Z J, Lin D H, Che G C, Ren Z A, Zhao Z X, Jin D 2002 Acta Phys. Sin. 51 6540 (in Chinese) [张杰、雒建林、白海洋、陈兆甲、林德华、车广灿、任治安、赵忠贤、金铎 2002 物理学报 51 6540]

    [16]

    ]Li R W, Wang Z H, Chen X, Shen B G 1999 Acta Phys. Sin. 48 S105 (in Chinese) [ 李润伟、王志宏、陈新、沈保根 1999 物理学报 48 S105]

  • [1]

    [1]Liu S Q, Wu N J, Lgnatiev A 2000 Appl. Phys. Lett. 76 2749

    [2]

    [2]Ahn K H, Lookman T, Bishop A R 2004 Nature 428 401

    [3]

    [3]Nagaev E L 1996 Phys. Lett. A 218 367

    [4]

    [4]Li Q, Wang Z G, Liu S, Xing Z W, Liu M 2007 Acta Phys. Sin. 56 1637 (in Chinese) [李倩、王之国、刘甦、刑仲文、刘楣 2007 物理学报 56 1637]

    [5]

    [5]Tulina N A, Sirotkin V V 2004 Physica C 400 105

    [6]

    [6]Szot K, Speier W, Bihlmayer G, Waser R 2006 Nat. Mater. 5 312

    [7]

    [7]Baikalov A, Wang Y Q, Shen B, Lorenz B, Tsui S, Sun Y Y, Xue Y Y 2003 Appl. Phys. Lett. 83 957

    [8]

    [8]Nian Y B, Strozier J, Wu N J, Chen X, Ignatiev A 2007 Phys. Rev. Lett. 98 146403

    [9]

    [9]Ziese M, Bollero A, Panagiotopoulos I, Moutis N 2005 Phys. Rev. B 72 024453

    [10]

    ]Long Y Z, Zheng P, Zhang Z M, Wei Z X, Wan M X, Chen Z J, Wang N L 2002 Acta Phys. Sin. 51 2090 (in Chinese) [龙云泽、郑萍、张志明、魏志祥、万梅香、陈兆甲、王楠林 2002物理学报 51 2090]

    [11]

    ]Ghivelder L, Abrego C I, Gusmao M A, Alonso J A, Cohen L F 1999 Phys. Rev.B 60 12184

    [12]

    ]Luo J L, Zhang J, Chen Z J, Bai H Y, Wang Y P, Meng J B, Jin D, Ren Z A, 2001 Chin. Phys. Lett. 18 820

    [13]

    ]Xu J, Luo J L, Chen Z J, Long Y Z, Bai H Y, Wan M X, Wang W L 2003 Acta Phys. Sin. 52 947 (in Chinese) [许杰、雒建林、陈兆甲、龙云泽、白海洋、万梅香、王万录 2003 物理学报 52 947]

    [14]

    ]Woodfield B F, Wilson M L, Byers J M 1997 Phys. Rev. Lett. 78 3201

    [15]

    ]Zhang J, Luo J L, Bai H Y,Chen Z J, Lin D H, Che G C, Ren Z A, Zhao Z X, Jin D 2002 Acta Phys. Sin. 51 6540 (in Chinese) [张杰、雒建林、白海洋、陈兆甲、林德华、车广灿、任治安、赵忠贤、金铎 2002 物理学报 51 6540]

    [16]

    ]Li R W, Wang Z H, Chen X, Shen B G 1999 Acta Phys. Sin. 48 S105 (in Chinese) [ 李润伟、王志宏、陈新、沈保根 1999 物理学报 48 S105]

  • [1] 刘金明, 翟薇, 周凯, 耿德路, 魏炳波. 三元(Co0.5Cu0.5)100-xSnx合金的热物理性质与液固相变机理. 物理学报, 2016, 65(22): 228101. doi: 10.7498/aps.65.228101
    [2] 邵宗乾, 陈金望, 李玉奇, 潘孝胤. 限制在一维谐振势下的三维自由电子气的一些热力学性质. 物理学报, 2014, 63(24): 240502. doi: 10.7498/aps.63.240502
    [3] 石大为, 吴美玲, 杨昌平, 任春林, 肖海波, 王开鹰. Pr0.7Ca0.3MnO3陶瓷晶界势垒的交流特性. 物理学报, 2013, 62(2): 026201. doi: 10.7498/aps.62.026201
    [4] 刘雅洁. 直接利用磁场和温度精确确定磁性材料La0.67Ca0.33MnO3和Pr0.7Sr0.3MnO3的电阻率. 物理学报, 2013, 62(1): 017601. doi: 10.7498/aps.62.017601
    [5] 饶中浩, 汪双凤, 张艳来, 彭飞飞, 蔡颂恒. 相变材料热物理性质的分子动力学模拟. 物理学报, 2013, 62(5): 056601. doi: 10.7498/aps.62.056601
    [6] 王仲伟, 张建, 李红维, 董春颖, 赵晶, 赵旭, 陈伟. Ti/Pr0.7Ca0.3MnO3/La0.67Sr0.33MnO3/Pt异质结电致电阻效应的改善. 物理学报, 2011, 60(11): 117306. doi: 10.7498/aps.60.117306
    [7] 姚文静, 王楠. Ni-15%Mo合金熔体热物理性质的Monte Carlo模拟. 物理学报, 2009, 58(6): 4053-4058. doi: 10.7498/aps.58.4053
    [8] 吴延昭, 谢宁, 刘建静, 焦永芳. 单壁碳纳米管声子谱及比热计算. 物理学报, 2009, 58(11): 7787-7791. doi: 10.7498/aps.58.7787
    [9] 陈乐, 王海鹏, 魏炳波. 液态三元Ni-Cu-Fe合金比热的实验与计算研究. 物理学报, 2009, 58(1): 384-389. doi: 10.7498/aps.58.384
    [10] 梁 维, 肖 杨, 丁建文. 石墨带的晶格动力学研究. 物理学报, 2008, 57(6): 3714-3719. doi: 10.7498/aps.57.3714
    [11] 李 政, 雒建林. 非中心对称超导体Mg10±δIr19B16?δ的超导电性研究. 物理学报, 2008, 57(7): 4508-4511. doi: 10.7498/aps.57.4508
    [12] 严资杰, 袁 孝, 徐业彬, 高国棉, 陈长乐. 室温下Pr0.7Ca0.3MnO3薄膜的瞬态光响应特性. 物理学报, 2007, 56(10): 6080-6083. doi: 10.7498/aps.56.6080
    [13] 郭焕银, 刘 宁, 蔡之让, 张裕恒. Mn位W掺杂对La0.3Ca0.7MnO3体系磁结构的影响. 物理学报, 2006, 55(2): 865-872. doi: 10.7498/aps.55.865
    [14] 杨 弘, 陈 民. 深过冷液态Ni2TiAl合金热物理性质的分子动力学模拟. 物理学报, 2006, 55(5): 2418-2421. doi: 10.7498/aps.55.2418
    [15] 王世奇, 连贵君, 熊光成. La0.7Ca0.3MnO3和CeO2混合块状样品电输运性质及使用分形迭代电阻网络模型的计算模拟. 物理学报, 2005, 54(8): 3815-3821. doi: 10.7498/aps.54.3815
    [16] 程金光, 隋 郁, 千正男, 刘志国, 黄喜强, 苗继鹏, 吕 喆, 王先杰, 苏文辉. 单晶NdMnO3的比热研究. 物理学报, 2005, 54(9): 4359-4364. doi: 10.7498/aps.54.4359
    [17] 胡小华, 陈兆甲, 雒建林, 王玉鹏, 白海洋, 金 铎. Cu掺杂对Kondo绝缘体CeNiSn低温比热的影响. 物理学报, 2000, 49(10): 2109-2112. doi: 10.7498/aps.49.2109
    [18] 金志强, 覃红侠, 章建荣, 王敦辉, 都有为. 机械合金化La0.7Ca0.3MnO3的晶化动力学及磁电阻研究. 物理学报, 1999, 48(13): 230-235. doi: 10.7498/aps.48.230
    [19] 秦晓岿, 石兢, 陈鸿, 田明亮, 田德诚. K0.3MoO3和Tl0.3MoO3派尔斯相变临界行为的比热研究. 物理学报, 1996, 45(6): 1033-1038. doi: 10.7498/aps.45.1033
    [20] 郑国光, 刘体汉, 管惟炎. Nb3Sn正常-超导转变时的比热反常. 物理学报, 1965, 21(4): 817-823. doi: 10.7498/aps.21.817
计量
  • 文章访问数:  7869
  • PDF下载量:  1040
  • 被引次数: 0
出版历程
  • 收稿日期:  2009-07-03
  • 修回日期:  2009-08-07
  • 刊出日期:  2010-02-05

/

返回文章
返回