5 at%Yb3+: YNbO4 的提拉法晶体生长和光谱特性

周鹏宇; 张庆礼; 杨华军; 宁凯杰; 孙敦陆; 罗建乔; 殷绍唐

doi:10.7498/aps.61.228103

摘要

用提拉法生长了新型激光晶体5 at% Yb3+:YNbO4, 测量了它的吸收和光致发光光谱, 计算了它的吸收和发射截面, 并对其激光性能进行了评估. Yb3+:YNbO4的吸收半峰全宽为17 nm, 吸收峰位于933, 955, 974和1003 nm, 相应的吸收截面分别为0.731020, 1.8510-20, 0.8610-20和0.4410-20 cm2; 最大吸收截面值为Yb3+:YAG的两倍. 光致发光谱的发射带的中心位置处于1020 nm附近, 相应的半高宽为41 nm, 是Yb3+:YAG的3倍; Yb3+:YNbO4在955, 974, 1005, 1021和1030 nm处都有着较大的发射截面, 截面值分别为0.6910-20, 0.8610-20, 1.8110-20, 1.1110-20和0.5710-20 cm2, 最大发射截面值与Yb3+:YAG相当. Yb3+:YNbO4晶体的宽发射带有利于实现相应波长的超短脉冲和可调谐激光输出, 表明它是在这些领域非常有希望的全固态工作物质.

关键词:

Yb3+:YNbO4 /
晶体生长 /
光谱性质

Abstract

5 at%Yb3+:YNbO4 crystal is grown by Czochralski(CZ) method. Its transmission and emission spectra are measured. The absorption peaks are located at 933, 955, 974 and 1003 nm with their corresponding absorbtion cross section values 0.7310-20, 1.8510-20, 0.8610-20 and 0.4410-20 cm2; and the FWHM of 955 nm absorbtion peak is 17 nm. Its emission band centered at 1020 nm with the FWHM is 41 nm, which is over three times that of Yb3+:YAG crystal. The emission cross section values of 955, 974, 1005, 1021 and 1030 nm peaks are calculated to be 0.6910-20, 0.8610-20, 1.8110-20, 1.1110-20 and 0.5710-20 cm2, respectively, and the biggest one is comparable to that of Yb3+:YAG crystal. The laser parameters of 5 at% Yb3+:YNbO4 crystal are evaluated and the results suggest that it is a potential all-solid-state pumped laser crystal in tunable and ultrafast lasers field.

Keywords:

作者及机构信息

1.
中科院安徽光学精密机械研究所安徽省光子器件与材料重点实验室, 合肥 230031;

2.
中国科学院研究生院, 北京 100049

基金项目: 国家自然科学基金(批准号: 90922003, 50772112, 50872135, 50932005)和中科院知识创新项目(批准号: YYYJ-1002)资助的课题.

Authors and contacts

1.
The Key Laboratory of Photonic Devices and Materials, Anhui Institute of Optics and Fine Mechanics, Chinese Academy of Sciences, Hefei 230031, China;

2.
Graduate University of Chinese Academy of Sciences, Beijing 100049, China

Funds: Project supported by the National Natural Science Foundation of China (Grant Nos. 90922003, 50772112, 50872135, 50932005), and the Knowledge Innovation Program of the Chinese Academy of Sciences (Grant No.YYYJ-1002).

参考文献

[1]	Qiu H W, Mao Y L, Dong J, Deng P Z, Xu J, Chen W 2002 Chinese J. Quant. Electron. 19 1 (in Chinese) [邱宏伟, 毛艳丽, 董俊, 邓佩珍, 徐军, 陈伟 2002 量子电子学报 19 1]
[2]	Zhang Q L, Xiao J Z, Sun D L, Wang A H, Yin S T 2004 Specrosc. Spect. Anal. 24 1157 (in Chinese) [张庆礼, 肖敬忠, 孙敦陆, 王爱华, 殷绍唐 2004 光谱学与光谱分析 24 1157]
[3]	Wang X D, Zhao Z W, Xu X D, Song P X, Jiang B X, Xu J, Deng P Z 2006 Acta Phys. Sin. 55 4558 (in Chinese) [王晓丹, 赵志伟, 晓东, 宋平新, 姜本学, 徐军, 邓佩珍 2006 物理学报 55 4558]
[4]	Zhang H J, Jiang M H 2008 J. Inorg. Mater. 23 417 (in Chinese) [张怀金, 蒋民华 2008 无机材料学报 23 417]
[5]	Zhang Q L, Zhou W L, Liu W P, Ding L H, Luo J Q, Yin S T, Jiang H H 2010 Acta Opt. Sin. 30 849 (in Chinese) [张庆礼, 周文龙, 刘文鹏, 丁丽华, 罗建乔, 殷绍唐, 江海河 2010 光学学报 30 849]
[6]	Ding L H, Zhang Q L, Zhou W L, Liu W P, Yin S T 2009 The Pacific Rim Conference on Lasers and Electro-Optics, ShangHai, China, 2009 pp2
[7]	Gaume R, Haumesser P H, Viana B, Vivien D, Ferrand B, Aka G 2002 Opt. Mater. 19 81
[8]	Yan C, Zhao G, Zhang L, Xu J, Liang X Y, Juan D, Li W X, Pan H F, Ding L G, Zeng H P 2006 Solid State Commun. 137 451
[9]	Xue Y C, Wang Q Y, Chai L, Liu Q W, Zhao G J, Su L B, Xu X D, Xu J 2006 Acta Phys. Sin. 55 457 (in Chinese) [薛迎红, 王清月, 柴路, 刘庆文, 赵广军, 苏良碧, 徐晓东, 徐军 2006 物理学报 55 457]
[10]	Jacquemet M, Jacquemet C, Janel N, Druon F, Balembois F 2005 Appl. Phys. B 80 171
[11]	Sych A M, Golub A M 1977 Russian Chem. Rev. 46 417
[12]	Choi S H, Anoop G, Suh D W, Kim K P, Lee H J, Yoo J S 2012 J. Rare Earths 30 205
[13]	Lee E Y, Kim Y J 2010 Thin Solid Films 518 E72
[14]	Nazarov M, Kim Y J, Lee E Y, Min K I, Jeong M S, Lee S W, Noh D Y 2010 J. App. Phys. 107 103104
[15]	Zhou Y, Ma Q, Lu M, Qiu M, Zhang A 2008 J. Phys. Chem. C 112 19901
[16]	Xiao X Z, Yan B 2008 J. Alloys Compd. 456 447
[17]	Xiao X Z, Yan B 2005 J. Non-cryst. Solids 351 3634
[18]	Trunov V K, Efremov V A, Velikodnyi Y A, Averina I M 1981 Kristallografiya 26 67
[19]	Zhang Q L, Yin S T, Wang Z B, Sun D L, Wan S M 2007 J. Synth. Cryst. l36 111 (in Chinese) [张庆礼, 殷绍唐, 王召兵, 孙敦陆, 万松明 2007 人工晶体学报 l36 111]
[20]	Chénais S, Duron F, Balembos F, Georges P, Brenier A, Boulon G 2003 Opt. Mater. 22 99
[21]	Gschneidner K A Jr., LeRoy E 1996 Handbook on the Physics and Chemistry of Rear Earths (Vol. 23) (Elsevier Science B. V.) p267
[22]	Payne S A, Chase L L, Smith L K 1992 IEEE. Quant. Electron. 28 2619
[23]	Zhang H W, Yang Q H, Xu J, Su L B 2007 Acta Photonica Sin. 36 286 (in Chinese) [张红伟, 杨秋红, 徐军, 苏良碧 2007 光子学报 36 286]
[24]	Song P X, Zhao Z W, Xu X D, Den P Z, Xu J 2005 Chinese J. Lasers 32 1433 (in Chinese) [宋平新, 赵志伟, 徐晓东, 邓佩珍, 徐军 2005 中国激光 32 1433]
[25]	DeLoach L D, Payne S A, Smith L K, Kway W L, Krupke W F 1994 J. Opt. Soc. Am. B 11 269
[26]	Boulon G, Collombet A, Brenier A, Cohen-Adad Marie-Thor.se, Yoshikawa A, Kheirreddine Lebbou, Lee J H, Fukuda T 2001 Adv. Funct. Mater. 11 263

施引文献

[1]	Qiu H W, Mao Y L, Dong J, Deng P Z, Xu J, Chen W 2002 Chinese J. Quant. Electron. 19 1 (in Chinese) [邱宏伟, 毛艳丽, 董俊, 邓佩珍, 徐军, 陈伟 2002 量子电子学报 19 1]
[2]	Zhang Q L, Xiao J Z, Sun D L, Wang A H, Yin S T 2004 Specrosc. Spect. Anal. 24 1157 (in Chinese) [张庆礼, 肖敬忠, 孙敦陆, 王爱华, 殷绍唐 2004 光谱学与光谱分析 24 1157]
[3]	Wang X D, Zhao Z W, Xu X D, Song P X, Jiang B X, Xu J, Deng P Z 2006 Acta Phys. Sin. 55 4558 (in Chinese) [王晓丹, 赵志伟, 晓东, 宋平新, 姜本学, 徐军, 邓佩珍 2006 物理学报 55 4558]
[4]	Zhang H J, Jiang M H 2008 J. Inorg. Mater. 23 417 (in Chinese) [张怀金, 蒋民华 2008 无机材料学报 23 417]
[5]	Zhang Q L, Zhou W L, Liu W P, Ding L H, Luo J Q, Yin S T, Jiang H H 2010 Acta Opt. Sin. 30 849 (in Chinese) [张庆礼, 周文龙, 刘文鹏, 丁丽华, 罗建乔, 殷绍唐, 江海河 2010 光学学报 30 849]
[6]	Ding L H, Zhang Q L, Zhou W L, Liu W P, Yin S T 2009 The Pacific Rim Conference on Lasers and Electro-Optics, ShangHai, China, 2009 pp2
[7]	Gaume R, Haumesser P H, Viana B, Vivien D, Ferrand B, Aka G 2002 Opt. Mater. 19 81
[8]	Yan C, Zhao G, Zhang L, Xu J, Liang X Y, Juan D, Li W X, Pan H F, Ding L G, Zeng H P 2006 Solid State Commun. 137 451
[9]	Xue Y C, Wang Q Y, Chai L, Liu Q W, Zhao G J, Su L B, Xu X D, Xu J 2006 Acta Phys. Sin. 55 457 (in Chinese) [薛迎红, 王清月, 柴路, 刘庆文, 赵广军, 苏良碧, 徐晓东, 徐军 2006 物理学报 55 457]
[10]	Jacquemet M, Jacquemet C, Janel N, Druon F, Balembois F 2005 Appl. Phys. B 80 171
[11]	Sych A M, Golub A M 1977 Russian Chem. Rev. 46 417
[12]	Choi S H, Anoop G, Suh D W, Kim K P, Lee H J, Yoo J S 2012 J. Rare Earths 30 205
[13]	Lee E Y, Kim Y J 2010 Thin Solid Films 518 E72
[14]	Nazarov M, Kim Y J, Lee E Y, Min K I, Jeong M S, Lee S W, Noh D Y 2010 J. App. Phys. 107 103104
[15]	Zhou Y, Ma Q, Lu M, Qiu M, Zhang A 2008 J. Phys. Chem. C 112 19901
[16]	Xiao X Z, Yan B 2008 J. Alloys Compd. 456 447
[17]	Xiao X Z, Yan B 2005 J. Non-cryst. Solids 351 3634
[18]	Trunov V K, Efremov V A, Velikodnyi Y A, Averina I M 1981 Kristallografiya 26 67
[19]	Zhang Q L, Yin S T, Wang Z B, Sun D L, Wan S M 2007 J. Synth. Cryst. l36 111 (in Chinese) [张庆礼, 殷绍唐, 王召兵, 孙敦陆, 万松明 2007 人工晶体学报 l36 111]
[20]	Chénais S, Duron F, Balembos F, Georges P, Brenier A, Boulon G 2003 Opt. Mater. 22 99
[21]	Gschneidner K A Jr., LeRoy E 1996 Handbook on the Physics and Chemistry of Rear Earths (Vol. 23) (Elsevier Science B. V.) p267
[22]	Payne S A, Chase L L, Smith L K 1992 IEEE. Quant. Electron. 28 2619
[23]	Zhang H W, Yang Q H, Xu J, Su L B 2007 Acta Photonica Sin. 36 286 (in Chinese) [张红伟, 杨秋红, 徐军, 苏良碧 2007 光子学报 36 286]
[24]	Song P X, Zhao Z W, Xu X D, Den P Z, Xu J 2005 Chinese J. Lasers 32 1433 (in Chinese) [宋平新, 赵志伟, 徐晓东, 邓佩珍, 徐军 2005 中国激光 32 1433]
[25]	DeLoach L D, Payne S A, Smith L K, Kway W L, Krupke W F 1994 J. Opt. Soc. Am. B 11 269
[26]	Boulon G, Collombet A, Brenier A, Cohen-Adad Marie-Thor.se, Yoshikawa A, Kheirreddine Lebbou, Lee J H, Fukuda T 2001 Adv. Funct. Mater. 11 263

[1]	郭状, 欧阳峰, 卢志舟, 王梦宇, 谭庆贵, 谢成峰, 魏斌, 何兴道. 氟化镁微瓶腔光频梳光谱分析及优化. 物理学报, 2024, 0(0): 0-0. doi: 10.7498/aps.73.20231126
[2]	杨帅, 张浩, 何珂. 选区外延生长的PbTe-超导杂化纳米线: 一个可能实现拓扑量子计算的新体系. 物理学报, 2023, 72(23): 238701. doi: 10.7498/aps.72.20231603
[3]	齐刚, 黄印博, 凌菲彤, 杨佳琦, 黄俊, 杨韬, 张雷雷, 卢兴吉, 袁子豪, 曹振松. 多微管阵列结构腔-原子吸收光谱测量Rb同位素比. 物理学报, 2023, 72(5): 053201. doi: 10.7498/aps.72.20221963
[4]	钱黎明, 孙梦然, 郑改革. α相三氧化钼中各向异性双曲声子极化激元的耦合性质. 物理学报, 2023, 72(7): 077101. doi: 10.7498/aps.72.20222144
[5]	邱旭, 王林雪, 陈光平, 胡爱元, 文林. 自旋张量-动量耦合玻色-爱因斯坦凝聚的动力学性质. 物理学报, 2023, 72(18): 180304. doi: 10.7498/aps.72.20231076
[6]	蒋东镔, 张颖, 姜大朋, 朱斌, 李纲, 孙立, 黄征, 卢峰, 谢娜, 周凯南, 粟敬钦. Nd, Gd:SrF₂晶体材料在宽带放大中的光谱增益特性. 物理学报, 2023, 72(22): 224208. doi: 10.7498/aps.72.20230972
[7]	李斌, 张国峰, 陈瑞云, 秦成兵, 胡建勇, 肖连团, 贾锁堂. 单量子点光谱与激子动力学研究进展. 物理学报, 2022, 71(6): 067802. doi: 10.7498/aps.71.20212050
[8]	姚熠舟, 曹丹, 颜洁, 刘雪吟, 王建峰, 姜舟婷, 舒海波. 氧氯化铋/铯铅氯范德瓦耳斯异质结环境稳定性与光电性质的第一性原理研究. 物理学报, 2022, 71(19): 197901. doi: 10.7498/aps.71.20220544
[9]	孙颖慧, 穆丛艳, 蒋文贵, 周亮, 王荣明. 金属纳米颗粒与二维材料异质结构的界面调控和物理性质. 物理学报, 2022, 71(6): 066801. doi: 10.7498/aps.71.20211902
[10]	郭思嘉, 李昱增, 李天梓, 范喜迎, 邱春印. 二维各向异性SSH模型的拓扑性质研究. 物理学报, 2022, 71(7): 070201. doi: 10.7498/aps.71.20211967
[11]	郭厦蕾, 侯育花, 郑寿红, 黄有林, 陶小马. Ge-S/F共掺杂对Li₂MSiO₄(M = Mn, Fe)晶体结构和性能影响的理论研究. 物理学报, 2022, 71(17): 178201. doi: 10.7498/aps.71.20220473
[12]	宋谢飞, 晒旭霞, 李洁, 马新茹, 伏云昌, 曾春华. 无机非铅钙钛矿Cs₃Bi₂I₉的电子和光学性质. 物理学报, 2022, 71(1): 017101. doi: 10.7498/aps.71.20211599
[13]	邵光伟, 于瑞, 傅婷, 陈南梁, 刘向阳. 三氧化钨晶体拓扑结构生长行为及其电致变色性能. 物理学报, 2022, 71(2): 028201. doi: 10.7498/aps.71.20211555
[14]	戚炜恒, 王震, 李翔飞, 禹日成, 王焕华. 外延BaMoO₃, BaMoO₄薄膜的生长行为. 物理学报, 2022, 71(17): 178103. doi: 10.7498/aps.71.20220736
[15]	李子龙, 万源. 强关联电子体系二维相干光谱的理论研究评述. 物理学报, 2021, 70(23): 230308. doi: 10.7498/aps.70.20211556
[16]	刘尚阔, 王涛, 李坤, 曹昆, 张玺斌, 周艳, 赵建科, 姚保利. 光源光谱特性对空间相机调制传递函数检测的影响. 物理学报, 2021, 70(13): 134208. doi: 10.7498/aps.70.20201575
[17]	刘强, 何军, 王军民. 室温铯原子气室窄线宽相干布居振荡光谱. 物理学报, 2021, 70(16): 163202. doi: 10.7498/aps.70.20210405
[18]	张超江, 许洪光, 徐西玲, 郑卫军. ${\bf Ta_4C}_{ n}^{\bf -/0}$ (n = 0—4)团簇的电子结构、成键性质及稳定性. 物理学报, 2021, 70(2): 023601. doi: 10.7498/aps.70.20201351
[19]	汪静丽, 陈子玉, 陈鹤鸣. 基于Si₃N₄/SiN_x/Si₃N₄三明治结构的偏振无关1 × 2多模干涉型解复用器的设计. 物理学报, 2020, 69(5): 054206. doi: 10.7498/aps.69.20191449
[20]	杜建宾, 冯志芳, 张倩, 韩丽君, 唐延林, 李奇峰. 外电场作用下MoS₂的分子结构和电子光谱. 物理学报, 2019, 68(17): 173101. doi: 10.7498/aps.68.20190781

计量

文章访问数: 11933
PDF下载量: 630
被引次数: 0

姓名
邮箱
手机号码
标题
留言内容
验证码

搜索

留言板