对于提拉法合成的BiVO4单晶进行了X射线衍射分析。室温下该晶体属于单斜晶系,空间群为B2/b,z=4,晶胞参数为:a=7.247?,b=5.096?,c=11.702?,γ=134.18°。进行了二维、三维帕特逊分析和三维电子密度计算。全矩阵最小二乘法修正给出335个独立反射的R=0.067,Rw=0.058。经吸收和次级消光校正后,R=0.058。Bi和V原子各占据一套4e特殊点系,O原子占据两套一般点系。V3+是四配位,形成规则的VO4四面体。Bi3+是八配位,形成畸变Bi-O十二面体。BiVO4在Tc温度上下空间群各为I41/a和I2/b(或B2/b)。由四方到单斜相变没有正交中间变体。相变显然是由Bi-O多面体孤对畸变所驱动。Bi3+和V5+沿c轴上下交替位移,这就显示单斜BiVO4具有层状结构的特征。这一特征由光学观察得到证实。该晶体在垂直干c轴的方向极易开裂而产生平坦的解理面。选取具有胞状结构圆盘形晶体、自然解理晶片和粉末晶粒三种试样进行了光学观察,并研究了晶体透过率与波长关系。A single-crystal X-ray diffraction analysis has been performed on fergusonite BiVO4 synthesized by pulling method. At room temperature the crystal belongs to monoclinic system, with space group B2/b, z = 4, and cell parameters a = 7.247?, b=5.096?, c = 11.702? and r =134.18o. The structure has been analysed by two and three-dimensional Patterson procedure, and calculated through three-dimensional electron density. A full-matrix, least square refinement gave R=0.067, Rw =0.058 for 335 independent reflections. An absorption and secondary extinction correction gave final R = 0.058. The Bi and V atoms occupy a respective set of 4e special positions and the O atoms two sets of general positions. The oxygen atoms take part in four-fold coordinations around vanadium in the sense that they form regular VO4 tetrahedra. The structure also shows eight-fold oxygen coordinations around bismuth and form distorted Bi-O dodecahedron. The space groups for temperatures above and below Tc are found to be I41/a and 12/b (or B2/b) respectivelv. The phase transition from tetragonal to monoclinic does skip over a possible intermediate orthorhombic modification. The phase transition is apparently driven by a lone-pair distortion of the Bi-O polyhedron. Bi3+ and V5+ displace alternatively up and down along the c axis, resulting in a layer-like Character for monoclinic BiVO4 The character has been proved by optical observations. The BiVO4 crystal cleaves easily to give smooth (cleavage) faces parallel to plane perpendicular to the c axis.Three kinds of samples, i.e crystals with cell-like structure and disc shape, crystal ribbon with natural cleavage and powder crystal grain, were used for optical observation, and the relationship between the transmittance of BiVO4 and optical wave-length was studied.
计量
- 文章访问数: 13897
- PDF下载量: 7028
- 被引次数: 0