铝基银纳米阵列制备及其紫外-可见-近红外光吸收特性

梁玲玲; 赵艳; 冯超

doi:10.7498/aps.69.20191522

摘要

基于阳极氧化铝模板, 采用真空蒸镀技术, 制备了高度有序的周期性银纳米球阵列. 阵列几何结构参数调控实验发现, 通过控制蒸镀厚度, 可实现对阵列中银纳米球尺寸(直径)和间距的有效调控, 进而有效实现对紫外-可见-近红外各波段吸收峰位和峰宽的调制. 吸收光谱测试显示, 该纳米阵列在紫外、可见和近红外波段都具有明显的电磁波吸收特性. 时域有限差分理论模拟结合实验分析不同波段光吸收特性的物理机制, 紫外超窄强吸收为银、铝介电环境非对称诱发的法诺共振, 可见波段吸收源自于银纳米粒子局域表面等离子体共振, 近红外波段强吸收为银纳米球阵列表面晶格共振所激发.

关键词:

Abstract

In this paper, the highly ordered periodic silver nanosphere arrays are fabricated by vacuum evaporation based on anodic aluminum oxide (AAO) template. The diameter and spacing of silver nanosphere in the arrays are adjusted just by controlling the thickness of evaporation. Furthermore, this can effectively modulate the absorption peaks and bandwidths in ultraviolet-visible-near-infrared regions. The measurement results of absorption spectra show that the nano-arrays have obvious electromagnetic wave absorption characteristics in the ultraviolet, visible and near-infrared bands. The finite-difference time-domain theoretical simulation combined with experiments is used to analyze the physical mechanism of light absorption characteristics in different wavebands. The ultraviolet strong absorption is due to the Fano resonance induced by asymmetric dielectric environment of silver and aluminum; the visible absorption originates from local surface plasmon resonance of silver nanoparticles; the near-infrared strong absorption is attributed to the surface lattice resonance of silver nanosphere arrays.

Keywords:

作者及机构信息

1.
北京工业大学激光工程研究院, 北京　100124

2.
北京工业大学应用数理学院, 北京　100124

3.
跨尺度激光成型制造技术教育部重点实验室, 北京　100124

4.
北京市激光应用技术工程技术研究中心, 北京　100124

通信作者: 赵艳, zhaoyan@bjut.edu.cn ; 冯超, fengchaoholy@bjut.edu.cn

基金项目: 国家级-国家自然科学基金面上项目(51475014)

Authors and contacts

1.
Institute of Laser Engineering, Beijing University of Technology, Beijing 100124, China

2.
Institute of Applied Mathematics and Physics, Beijing University of Technology, Beijing 100124, China

3.
Key Laboratory of Trans-scale Laser Manufacturing Technology, Ministry of Education, Beijing 100124, China

4.
Beijing Engineering Research Center of Laser Technology, Beijing 100124, China

Corresponding author: Zhao Yan, zhaoyan@bjut.edu.cn ; Feng Chao, fengchaoholy@bjut.edu.cn

文章全文 : translate this paragraph

参考文献

[1]	Wang S Q, Xu L P, Wen Y Q, Du H W, Wang S T, Zhang X J 2013 Nanoscale 5 4284 Google Scholar
[2]	Shipway A N, Katz E, Willner I 2000 ChemPhysChem 1 18 Google Scholar
[3]	Prakash J, Harris R A, Swart H C 2016 Int. Rev. Phys. Chem. 35 353 Google Scholar
[4]	Fuku K, Hayashi R, Takakura S, Kamegawa T, Mori K, Yamashita H 2013 Angew. Chem. Int. Ed. 52 7446 Google Scholar
[5]	Yan B, Yang X X, Fang J Y, Huang Y D, Qin H, Qin S Q 2015 Chin. Phys. B 24 15203 Google Scholar
[6]	张喆, 柳倩, 祁志美 2013 物理学报 62 060703 Google Scholar Zhang Z, Liu Q, Qi Z M 2013 Acta Phys. Sin. 62 060703 Google Scholar
[7]	Offermans P, Schaafsma M C, Rodriguez S R K, Zhang Y C, Crego-Calama M, Brongersma S H, Rivas J G 2015 ACS Nano 5 5151
[8]	Ren K, Yin P, Zhou Y, Cao X, Dong C, Cui L, Liu H, Du X 2017 Small 13 1700867 Google Scholar
[9]	Mi Y, Wen L Y, Xu R, Wang Z J, Cao D W, Fang Y G, Lei Y 2016 Adv. Energy Mater. 6 1501496 Google Scholar
[10]	叶松, 王向贤, 侯宜栋, 张志友, 杜惊雷 2014 物理学报 65 087802 Google Scholar Ye S, Wang X, Hou Y D, Zhang Z Y, Du J L 2014 Acta Phys. Sin. 65 087802 Google Scholar
[11]	Zhang J, Dong L, Yu S H 2015 Sci. Bull. 60 785 Google Scholar
[12]	Khan Y, Li A R, Chang L, Li L D 2018 Sens. Actuator, B 255 1298 Google Scholar
[13]	Xiong B, Zhou R, Hao J R, Jia Y H, He Y, Yeung E S 2013 Nat. Commun. 4 1708 Google Scholar
[14]	Jung H Y, Yeo I S, Kim T U, Ki H C, Gu H B 2018 Appl. Surf. Sci. 432 266 Google Scholar
[15]	Wu K, Li T, Schmidt M S, Rindzevicius T, Boisen A, Ndoni S 2018 Adv. Funct. Mater. 28 1704818 Google Scholar
[16]	Zhan Z B, Xu R, Mi Y, Zhao H P, Lei Y 2015 ACS Nano 9 4583 Google Scholar
[17]	Ji N, Ruan W D, Li Z S, Wang C X, Yang Z, Zhao B 2013 J. Raman Spectrosc. 44 1 Google Scholar
[18]	King N S, Liu L F, Yang X, Cerjan B, Everitt H O, Nordlander P, Halas N J 2015 ACS Nano 9 10628 Google Scholar
[19]	Zhan Z B, Xu R, Zheng X Z, Fu Q, Wu M H, Lei Y 2016 Nanotechnol. 27 445301 Google Scholar
[20]	Minamimoto H, Oikawa S, Hayashi T, Shibazaki A, Li X W, Murakoshi K 2018 J. Phys. Chem. C 122 14162 Google Scholar
[21]	Zhang C, Wu K, Ling B, Li X F 2016 J. Photonics Energy 6 042502 Google Scholar
[22]	González-Rubio G, Díaz-Núñez P, Rivera A, Prada A, Tardajos G, González-Izquierdo J, Bañares L, Llombart P, Macdowell L G, Palafox M A, Liz-Marzán L M, Peña-Rodríguez O, Guerrero-Martínez A 2017 Science 358 640 Google Scholar
[23]	Wang L C, Liu Z Q, Yi X Y, Zhang Y Y, Li H J, Li G M, Wang G H 2016 J. Appl. Phys. 119 1685 Google Scholar
[24]	Gromov D G, Pavlova L M, Savitsky A I, Trifonov A Y 2015 Appl. Phys. A 118 1297 Google Scholar
[25]	Liu Z H, Ye J 2016 Nanoscale 8 17665 Google Scholar
[26]	Marimuthu A, Zhang J W, Linic S 2013 Science 339 1590 Google Scholar
[27]	Ji N, Ruan W D, Wang C X, Lu C, Zhao B 2009 Langmuir 25 11869 Google Scholar
[28]	Zhang S P, Bao K, Halas N J, Xu H X, Nordlander P 2011 Nano Lett. 11 1657 Google Scholar
[29]	屈炜, 李静 2017 新技术新工艺 5 15 Google Scholar Qu W, Li J 2017 New Technol. New Process 5 15 Google Scholar
[30]	Zhan Y H, Lei D Y, Li X F, Maier S A 2014 Nanoscale 6 4705 Google Scholar
[31]	张佳, 牧凯军, 王俊俏, 范春珍, 梁二军 2017 光散射学报 29 1007 Google Scholar Zhang J, Mu K J, Wang J X, Fan C Z, Liang E J 2017 J. Light Scatt. 29 1007 Google Scholar
[32]	Knight M W, Wu Y P, Lassiter J B, Nordlander P, Halas N J 2009 Nano Lett. 9 2188 Google Scholar
[33]	Wu Y P, Nordlander P 2010 J. Phys. Chem. C 114 7302 Google Scholar
[34]	Benjamin G, Olivier Martin J F 2011 ACS Nano 5 8999 Google Scholar
[35]	Wang M S, Krasnok A, Zhang T Y, Scarabelli L, Liu H, Wu Z L, Luis M, Marzán L, Terrones M, Alù A, Zheng Y B 2018 Adv. Mater. 3 1705779 Google Scholar
[36]	Sherry L J, Chang S H, Schatz G C, Van Duyne R P, Wiley B J, Xia Y 2005 Nano Lett. 5 2034 Google Scholar
[37]	Yin J, Zang Y S, Xu B B, Li S P, Kang J Y, Fang Y Y, Wu Z H, Li J 2014 Nanoscale 6 3934 Google Scholar
[38]	Catchpole K R, Polman A 2008 Opt. Express 16 21793 Google Scholar
[39]	黄昕乾, 姚若河 2018 真空科学与技术学报 38 791 Google Scholar Huang X Q, Yao R H 2018 Chin. J. Vacuum Sci. Technol. 38 791 Google Scholar
[40]	Cristiano M, Christoph H, Luis G P J, Judith L, Agustín M, Luis M, Liz M 2018 ACS Nano 12 8531 Google Scholar

施引文献

图 1 AAO纳米碗阵列和Ag纳米球阵列制备过程示意图　(a) 高纯铝片; (b) AAO纳米管阵列; (c) AAO纳米碗阵列; (d) Ag纳米颗粒; (e) Ag纳米球阵列

Fig. 1. Schematic diagram of the preparation procedure for fabricating patterned aluminum templates and Ag nanosphere arrays: (a) Purity aluminum; (b) AAO nanotube arrays after the first anodization; (c) AAO nanobowl arrays after the removal of the porous alumina layer; (d) Ag nanoparticles; (e) Ag nanosphere arrays.

下载: 全尺寸图片幻灯片

图 2 真空蒸镀实验仪器示意图

Fig. 2. Schematic diagram of vacuum evaporation apparatus.

下载: 全尺寸图片幻灯片

图 3 FDTD Solutions仿真模型　(a) x-y视图; (b) x-z视图

Fig. 3. View of simulation model in FDTD Solution (a) x-y; (b) x-z.

下载: 全尺寸图片幻灯片

图 4 (a) AAO纳米碗阵列SEM图; (b) Ag纳米球周期性阵列SEM图

Fig. 4. SEM images of the (a) AAO nanobowl arrays and (b) periodic arrays of Ag nanospheres.

下载: 全尺寸图片幻灯片

图 5 不同粒径(D) Ag纳米球周期性阵列/不同厚度(T) Ag膜的SEM图 (a)−(n)及相应的粒径分布直方图(i)−(x)　(a) D = 73.5 nm; (b) D = 78.2 nm; (c) D = 83.2 nm; (d) D = 85.5 nm; (e) D = 87.7 nm; (f) D = 90.1 nm; (g) D = 91.3 nm; (h) D = 91.7 nm; (i) D = 93.1 nm; (j) D = 94.2 nm; (k) T = 17.5; (l) T =18.2 nm; (m) T = 19.0 nm; (n) T = 19.7 nm

Fig. 5. (a)−(n) SEM images of Ag nanosphere arrays/Ag film and (i)−(x) their related size distribution histograms: (a) D = 73.5 nm; (b) D = 78.2 nm; (c) D = 83.2 nm; (d) D = 85.5 nm; (e) D = 87.7 nm; (f) D = 90.1 nm; (g) D = 91.3 nm; (h) D = 91.7 nm; (i) D = 93.1 nm; (j) D = 94.2 nm; (k) T = 17.5 nm; (l) T = 18.2 nm; (m) T = 19.0 nm; (n) T = 19.7 nm.

下载: 全尺寸图片幻灯片

图 6 (a) 沉积在AAO纳米碗上不同粒径Ag纳米球阵列UV-vis-NIR实验所得吸收光谱; (b) 不同衬底制备的银复合结构的吸收光谱

Fig. 6. Experimental UV-vis-NIR absorption spectra of (a) Ag nanosphere arrays deposited on AAO-nanobowl with different sizes; (b) silver composite structure fabricated on different substrates.

下载: 全尺寸图片幻灯片

图 7 (a) UV-Vis波段不同粒径Ag纳米球阵列实验所得吸收光谱和(b) FDTD模拟吸收光谱

Fig. 7. UV-Vis absorption spectra of Ag nanosphere arrays with different sizes: (a) Experimental results; (b) FDTD simulation results

下载: 全尺寸图片幻灯片

图 8 (a)紫外波段Ag纳米颗粒实验测得吸收光谱(黑色虚线), 以及根据(3)式拟合得到的吸收光谱(红色); (b) Ag纳米球阵列在437 nm波长下x-y平面(z = 0)的极化电场分布

Fig. 8. (a) UV absorption spectra of Ag nanosphere arrays (black dashed line is experimental results; red line corresponds to σ_t obtained by fitting the Eq. (3); (b) polarized field distributions on the x-y plane (z = 0) of the Ag nano-sphere array excited 437 nm.

下载: 全尺寸图片幻灯片

图 9 (a) NIR波段不同粒径Ag纳米球阵列实验所得吸收光谱和(b) FDTD理论模拟吸收光谱

Fig. 9. NIR absorption spectra of Ag nanosphere arrays with different sizes: (a) Experimental results; (b) FDTD simulation results.

下载: 全尺寸图片幻灯片

[1]	Wang S Q, Xu L P, Wen Y Q, Du H W, Wang S T, Zhang X J 2013 Nanoscale 5 4284 Google Scholar
[2]	Shipway A N, Katz E, Willner I 2000 ChemPhysChem 1 18 Google Scholar
[3]	Prakash J, Harris R A, Swart H C 2016 Int. Rev. Phys. Chem. 35 353 Google Scholar
[4]	Fuku K, Hayashi R, Takakura S, Kamegawa T, Mori K, Yamashita H 2013 Angew. Chem. Int. Ed. 52 7446 Google Scholar
[5]	Yan B, Yang X X, Fang J Y, Huang Y D, Qin H, Qin S Q 2015 Chin. Phys. B 24 15203 Google Scholar
[6]	张喆, 柳倩, 祁志美 2013 物理学报 62 060703 Google Scholar Zhang Z, Liu Q, Qi Z M 2013 Acta Phys. Sin. 62 060703 Google Scholar
[7]	Offermans P, Schaafsma M C, Rodriguez S R K, Zhang Y C, Crego-Calama M, Brongersma S H, Rivas J G 2015 ACS Nano 5 5151
[8]	Ren K, Yin P, Zhou Y, Cao X, Dong C, Cui L, Liu H, Du X 2017 Small 13 1700867 Google Scholar
[9]	Mi Y, Wen L Y, Xu R, Wang Z J, Cao D W, Fang Y G, Lei Y 2016 Adv. Energy Mater. 6 1501496 Google Scholar
[10]	叶松, 王向贤, 侯宜栋, 张志友, 杜惊雷 2014 物理学报 65 087802 Google Scholar Ye S, Wang X, Hou Y D, Zhang Z Y, Du J L 2014 Acta Phys. Sin. 65 087802 Google Scholar
[11]	Zhang J, Dong L, Yu S H 2015 Sci. Bull. 60 785 Google Scholar
[12]	Khan Y, Li A R, Chang L, Li L D 2018 Sens. Actuator, B 255 1298 Google Scholar
[13]	Xiong B, Zhou R, Hao J R, Jia Y H, He Y, Yeung E S 2013 Nat. Commun. 4 1708 Google Scholar
[14]	Jung H Y, Yeo I S, Kim T U, Ki H C, Gu H B 2018 Appl. Surf. Sci. 432 266 Google Scholar
[15]	Wu K, Li T, Schmidt M S, Rindzevicius T, Boisen A, Ndoni S 2018 Adv. Funct. Mater. 28 1704818 Google Scholar
[16]	Zhan Z B, Xu R, Mi Y, Zhao H P, Lei Y 2015 ACS Nano 9 4583 Google Scholar
[17]	Ji N, Ruan W D, Li Z S, Wang C X, Yang Z, Zhao B 2013 J. Raman Spectrosc. 44 1 Google Scholar
[18]	King N S, Liu L F, Yang X, Cerjan B, Everitt H O, Nordlander P, Halas N J 2015 ACS Nano 9 10628 Google Scholar
[19]	Zhan Z B, Xu R, Zheng X Z, Fu Q, Wu M H, Lei Y 2016 Nanotechnol. 27 445301 Google Scholar
[20]	Minamimoto H, Oikawa S, Hayashi T, Shibazaki A, Li X W, Murakoshi K 2018 J. Phys. Chem. C 122 14162 Google Scholar
[21]	Zhang C, Wu K, Ling B, Li X F 2016 J. Photonics Energy 6 042502 Google Scholar
[22]	González-Rubio G, Díaz-Núñez P, Rivera A, Prada A, Tardajos G, González-Izquierdo J, Bañares L, Llombart P, Macdowell L G, Palafox M A, Liz-Marzán L M, Peña-Rodríguez O, Guerrero-Martínez A 2017 Science 358 640 Google Scholar
[23]	Wang L C, Liu Z Q, Yi X Y, Zhang Y Y, Li H J, Li G M, Wang G H 2016 J. Appl. Phys. 119 1685 Google Scholar
[24]	Gromov D G, Pavlova L M, Savitsky A I, Trifonov A Y 2015 Appl. Phys. A 118 1297 Google Scholar
[25]	Liu Z H, Ye J 2016 Nanoscale 8 17665 Google Scholar
[26]	Marimuthu A, Zhang J W, Linic S 2013 Science 339 1590 Google Scholar
[27]	Ji N, Ruan W D, Wang C X, Lu C, Zhao B 2009 Langmuir 25 11869 Google Scholar
[28]	Zhang S P, Bao K, Halas N J, Xu H X, Nordlander P 2011 Nano Lett. 11 1657 Google Scholar
[29]	屈炜, 李静 2017 新技术新工艺 5 15 Google Scholar Qu W, Li J 2017 New Technol. New Process 5 15 Google Scholar
[30]	Zhan Y H, Lei D Y, Li X F, Maier S A 2014 Nanoscale 6 4705 Google Scholar
[31]	张佳, 牧凯军, 王俊俏, 范春珍, 梁二军 2017 光散射学报 29 1007 Google Scholar Zhang J, Mu K J, Wang J X, Fan C Z, Liang E J 2017 J. Light Scatt. 29 1007 Google Scholar
[32]	Knight M W, Wu Y P, Lassiter J B, Nordlander P, Halas N J 2009 Nano Lett. 9 2188 Google Scholar
[33]	Wu Y P, Nordlander P 2010 J. Phys. Chem. C 114 7302 Google Scholar
[34]	Benjamin G, Olivier Martin J F 2011 ACS Nano 5 8999 Google Scholar
[35]	Wang M S, Krasnok A, Zhang T Y, Scarabelli L, Liu H, Wu Z L, Luis M, Marzán L, Terrones M, Alù A, Zheng Y B 2018 Adv. Mater. 3 1705779 Google Scholar
[36]	Sherry L J, Chang S H, Schatz G C, Van Duyne R P, Wiley B J, Xia Y 2005 Nano Lett. 5 2034 Google Scholar
[37]	Yin J, Zang Y S, Xu B B, Li S P, Kang J Y, Fang Y Y, Wu Z H, Li J 2014 Nanoscale 6 3934 Google Scholar
[38]	Catchpole K R, Polman A 2008 Opt. Express 16 21793 Google Scholar
[39]	黄昕乾, 姚若河 2018 真空科学与技术学报 38 791 Google Scholar Huang X Q, Yao R H 2018 Chin. J. Vacuum Sci. Technol. 38 791 Google Scholar
[40]	Cristiano M, Christoph H, Luis G P J, Judith L, Agustín M, Luis M, Liz M 2018 ACS Nano 12 8531 Google Scholar

计量

文章访问数: 9646
PDF下载量: 115
被引次数: 0

姓名
邮箱
手机号码
标题
留言内容
验证码

搜索

留言板

铝基银纳米阵列制备及其紫外-可见-近红外光吸收特性