强流脉冲电子束辐照诱发金属纯镍中的空位簇缺陷

邹慧 荆洪阳 王志平 关庆丰

引用本文:
Citation:

强流脉冲电子束辐照诱发金属纯镍中的空位簇缺陷

邹慧, 荆洪阳, 王志平, 关庆丰

The vacancy defect clusters in polycrystalline pure nickle induced by high-current pulsed electron beam

Zou Hui, Jing Hong-Yang, Wamg Zhi-Ping, Guan Qing-Feng
PDF
导出引用
  • 利用强流脉冲电子束(high-current pulsed electron beam,HCPEB)技术对多晶纯Ni进行了辐照处理,采用透射电子显微镜详细分析了辐照诱发的缺陷结构.HCPEB辐照后,纯镍表层积聚了幅值极大的残余应力,沿{111}晶面形成了稠密的位错墙及孪晶结构,另外还形成了大量的包括位错圈、堆垛层错四面体(SFT)及孔洞在内的空位簇缺陷.SFT缺陷的数量远高于其他空位簇缺陷,其周围区域位错密度很低.孔洞缺陷主要出现在SFT密集区域.HCPEB瞬间的加热和冷却诱发的幅值极大的应力和极高的应变
    High-current pulsed electron beam (HCPEB) technique is employed to irradiate the samples of polycrystalline pure nickel. The microstructures of the irradiated surface layers are investigated by using transmission electron microscopy (TEM). After HCPEB irradiation, very high value of residual stress is induced in the irradiated surface layer, which leads to the formation of dense dislocation walls and twins. Furthermore, a larger number of vacancy defect clusters including dislocation loops, stacking fault tetrahedra (SFT) and voids are also formed. Among three vacancy defect clusters, the number of SFT is much more than that of two other vacancy defect clusters. The lower dislocation density near the regions with dense SFT is observed and voids are likely to be present in these regions. It suggests that the stress with very high value and strain rate induced by rapid heating and cooling due to HCPEB irradiation could cause the shifting of the whole atomic plane synchronously.
    • 基金项目: 国家自然科学基金(批准号:50671042)和江苏大学基金(批准号:07JDG032)资助的课题.
    [1]

    Feng D 2000 Metallogrphy Physics (Vol.1) (Beijing: Science Press) p226 (in Chinese) [冯 端 2000 金属物理学 (第一卷)(北京: 科学出版社) 第226页]

    [2]

    Kiritani M 1997 Mater. Chem. Phys. 50 133

    [3]

    Guan Q F, Pan L, Zou H, Zou G T 2004 J. Mater. Sci. 39 6349

    [4]

    Guan Q F, Chen B, Zhang Q Y, Dong C, Zou G T 2008 Acta Phys. Sin. 57 392 (in Chinese) [关庆丰、 陈 波、 张庆瑜、 董 闯、 邹广田 2008 物理学报 58 392]

    [5]

    Guan Q F, Cheng D Q, Qiu D H, Zhu J, Wang X T, Cheng X W 2009 Acta Phys. Sin. 58 4846 (in Chinese) [关庆丰、 程笃庆、 邱冬华、 朱 健、 王雪涛、 程秀围 2009 物理学报 58 4846]

    [6]

    Guan Q F, Wang S Q, Cui X H, Zhang Q Y, Dong C 2007 ISIJ Int. 47 1375

    [7]

    Proskurovsky D I, Rotshtein V P, Ozur G E, Markov A B, Nazarov D S 1998 J. Vac. Sci. Technol. A 16 2480

    [8]

    Li Y S, Tao N R, Lu K 2008 Acta Mater. 56 230

    [9]

    Kibey S, Liu J B, Johnson D D 2007 Acta Mater. 55 6843

    [10]

    Cheng X W, Guan Q F, Fan X H, Chen B 2010 Chin. Phys. B 19 016103

    [11]

    Kiritani M, Yoshiie T, Kojima S 1994 J. Nucl. Mater. 192 212

    [12]

    Mansur L K 1978 J. Nucl. Sci. Technol. 40 5

    [13]

    Singh B N, Zinkle S J 1993 J. Nucl. Mater 206 212

    [14]

    Niwase K, Phillipp F, Sigle W, Seeger A 1999 J. Nucl. Mater 271-272 261

    [15]

    Mukouda I, Shimomura Y 1999 J. Nucl. Mater 271-272 230

    [16]

    Shimonmura Y, Mukouda I, Kiritani M, Kojima S, Garner F A 1997 J. Nucl. Mater. 212-125 352

    [17]

    Shimonmura Y, Guinan M W,Diaz T 1993 J. Nucl. Mater. 205 374

    [18]

    Silcox J, Hirsch P B 1959 Philos. Mag. 4 72

    [19]

    Qiu D H, Cheng D Q, Guan Q F, Zou G T 2009 Chin. J. High Pressure Phys. 5 23 (in Chinese) [邱冬华、 程笃庆、 关庆丰、 邹广田 2009 高压物理学报 5 23]

    [20]

    Kiritani M 2003 Mater. Sci. Eng. A 350 1

  • [1]

    Feng D 2000 Metallogrphy Physics (Vol.1) (Beijing: Science Press) p226 (in Chinese) [冯 端 2000 金属物理学 (第一卷)(北京: 科学出版社) 第226页]

    [2]

    Kiritani M 1997 Mater. Chem. Phys. 50 133

    [3]

    Guan Q F, Pan L, Zou H, Zou G T 2004 J. Mater. Sci. 39 6349

    [4]

    Guan Q F, Chen B, Zhang Q Y, Dong C, Zou G T 2008 Acta Phys. Sin. 57 392 (in Chinese) [关庆丰、 陈 波、 张庆瑜、 董 闯、 邹广田 2008 物理学报 58 392]

    [5]

    Guan Q F, Cheng D Q, Qiu D H, Zhu J, Wang X T, Cheng X W 2009 Acta Phys. Sin. 58 4846 (in Chinese) [关庆丰、 程笃庆、 邱冬华、 朱 健、 王雪涛、 程秀围 2009 物理学报 58 4846]

    [6]

    Guan Q F, Wang S Q, Cui X H, Zhang Q Y, Dong C 2007 ISIJ Int. 47 1375

    [7]

    Proskurovsky D I, Rotshtein V P, Ozur G E, Markov A B, Nazarov D S 1998 J. Vac. Sci. Technol. A 16 2480

    [8]

    Li Y S, Tao N R, Lu K 2008 Acta Mater. 56 230

    [9]

    Kibey S, Liu J B, Johnson D D 2007 Acta Mater. 55 6843

    [10]

    Cheng X W, Guan Q F, Fan X H, Chen B 2010 Chin. Phys. B 19 016103

    [11]

    Kiritani M, Yoshiie T, Kojima S 1994 J. Nucl. Mater. 192 212

    [12]

    Mansur L K 1978 J. Nucl. Sci. Technol. 40 5

    [13]

    Singh B N, Zinkle S J 1993 J. Nucl. Mater 206 212

    [14]

    Niwase K, Phillipp F, Sigle W, Seeger A 1999 J. Nucl. Mater 271-272 261

    [15]

    Mukouda I, Shimomura Y 1999 J. Nucl. Mater 271-272 230

    [16]

    Shimonmura Y, Mukouda I, Kiritani M, Kojima S, Garner F A 1997 J. Nucl. Mater. 212-125 352

    [17]

    Shimonmura Y, Guinan M W,Diaz T 1993 J. Nucl. Mater. 205 374

    [18]

    Silcox J, Hirsch P B 1959 Philos. Mag. 4 72

    [19]

    Qiu D H, Cheng D Q, Guan Q F, Zou G T 2009 Chin. J. High Pressure Phys. 5 23 (in Chinese) [邱冬华、 程笃庆、 关庆丰、 邹广田 2009 高压物理学报 5 23]

    [20]

    Kiritani M 2003 Mater. Sci. Eng. A 350 1

  • [1] 朱琪, 王升涛, 赵福祺, 潘昊. 层错四面体对单晶铜层裂行为影响的分子动力学研究. 物理学报, 2020, 69(3): 036201. doi: 10.7498/aps.69.20191425
    [2] 胡远超, 曹兴忠, 李玉晓, 张鹏, 靳硕学, 卢二阳, 于润升, 魏龙, 王宝义. 慢正电子束流技术在金属/合金微观缺陷研究中的应用. 物理学报, 2015, 64(24): 247804. doi: 10.7498/aps.64.247804
    [3] 蔡杰, 季乐, 杨盛志, 张在强, 刘世超, 李艳, 王晓彤, 关庆丰. 强流脉冲电子束作用下金属锆的微观结构与应力状态. 物理学报, 2013, 62(15): 156106. doi: 10.7498/aps.62.156106
    [4] 季乐, 杨盛志, 蔡杰, 李艳, 王晓彤, 张在强, 侯秀丽, 关庆丰. 强流脉冲电子束辐照诱发纯钼表面的损伤效应及结构缺陷. 物理学报, 2013, 62(23): 236103. doi: 10.7498/aps.62.236103
    [5] 李艳, 蔡杰, 吕鹏, 邹阳, 万明珍, 彭冬晋, 顾倩倩, 关庆丰. 强流脉冲电子束诱发纯钛表面的微观结构及应力状态. 物理学报, 2012, 61(5): 056105. doi: 10.7498/aps.61.056105
    [6] 关庆丰, 顾倩倩, 李艳, 邱冬华, 彭冬晋, 王雪涛. 强流脉冲电子束作用下金属纯Cu的微观结构状态变形结构. 物理学报, 2011, 60(8): 086106. doi: 10.7498/aps.60.086106
    [7] 王雪涛, 关庆丰, 邱冬华, 程秀围, 李艳, 彭冬晋, 顾倩倩. 强流脉冲电子束作用下金属纯Cu的微观结构状态——空位簇缺陷及表面微孔结构. 物理学报, 2010, 59(10): 7252-7257. doi: 10.7498/aps.59.7252
    [8] 方步青, 卢果, 张广财, 许爱国, 李英骏. 铜晶体中类层错四面体的结构及其演化. 物理学报, 2009, 58(7): 4862-4871. doi: 10.7498/aps.58.4862
    [9] 程笃庆, 关庆丰, 朱健, 邱东华, 程秀围, 王雪涛. 强流脉冲电子束诱发纯镍表层纳米结构的形成机制. 物理学报, 2009, 58(10): 7300-7306. doi: 10.7498/aps.58.7300
    [10] 关庆丰, 程笃庆, 邱冬华, 朱健, 王雪涛, 程秀围. 强流脉冲电子束辐照诱发多晶纯铝中的空位缺陷簇结构. 物理学报, 2009, 58(7): 4846-4852. doi: 10.7498/aps.58.4846
    [11] 檀满林, 朱嘉琦, 张化宇, 朱振业, 韩杰才. 硼掺杂对四面体非晶碳膜电导性能的影响. 物理学报, 2008, 57(10): 6551-6556. doi: 10.7498/aps.57.6551
    [12] 廖庆亮, 张 跃, 夏连胜, 齐俊杰, 黄运华, 邓战强, 高战军, 曹佳伟. 丝网印刷制备碳纳米管阴极的强流脉冲发射特性研究. 物理学报, 2008, 57(4): 2328-2333. doi: 10.7498/aps.57.2328
    [13] 范鲜红, 陈 波, 关庆丰. 质子辐照对纯铝薄膜微观结构的影响. 物理学报, 2008, 57(3): 1829-1833. doi: 10.7498/aps.57.1829
    [14] 关庆丰, 陈 波, 张庆瑜, 董 闯, 邹广田. 强流脉冲电子束辐照下单晶铝中的堆垛层错四面体. 物理学报, 2008, 57(1): 392-397. doi: 10.7498/aps.57.392
    [15] 关庆丰, 安春香, 秦 颖, 邹建新, 郝胜志, 张庆瑜, 董 闯, 邹广田. 强流脉冲电子束应力诱发的微观结构. 物理学报, 2005, 54(8): 3927-3934. doi: 10.7498/aps.54.3927
    [16] 秦 颖, 王晓钢, 董 闯, 郝胜智, 刘 悦, 邹建新, 吴爱民, 关庆丰. 强流脉冲电子束诱发温度场及表面熔坑的形成. 物理学报, 2003, 52(12): 3043-3048. doi: 10.7498/aps.52.3043
    [17] 彭栋梁, 王天民, 童志深. 形变充氢多晶纯钴中缺陷的正电子湮没研究. 物理学报, 1992, 41(7): 1106-1110. doi: 10.7498/aps.41.1106
    [18] 王淑英, 季国坤, 侯耀永, 李理. 用正电子湮没技术研究纯镍多晶体疲劳过程中的晶体缺陷. 物理学报, 1985, 34(12): 1627-1633. doi: 10.7498/aps.34.1627
    [19] 江兴流, 陈克凡, 朴禹伯. 新型毫微秒强流脉冲电子束和离子束发生装置. 物理学报, 1983, 32(10): 1344-1348. doi: 10.7498/aps.32.1344
    [20] 李家璘, 陈良辰, 沈主同. 双级四压砧(四面体)静态超高压技术. 物理学报, 1975, 24(4): 301-306. doi: 10.7498/aps.24.301
计量
  • 文章访问数:  7297
  • PDF下载量:  805
  • 被引次数: 0
出版历程
  • 收稿日期:  2009-11-08
  • 修回日期:  2010-03-12
  • 刊出日期:  2010-09-15

/

返回文章
返回