冲击压缩下金属钯的结构相变

刘泽涛; 陈博; 令伟栋; 包南云; 康冬冬; 戴佳钰

doi:10.7498/aps.71.20211511

摘要

钯作为典型高压标定材料, 研究其在极端条件下的结构变化以及热力学性质具有广泛需求并充满了挑战, 特别是冲击加载下钯的固-固相变过程研究仍然匮乏. 本文基于嵌入原子势, 使用经典分子动力学方法从原子角度揭示了冲击载荷加载下钯的结构相变路径, 在0—375 GPa的压力区间观察到一系列复杂的结构转变特征, 从初始的面心立方(FCC)结构, 至带密排六方(HCP)结构的层错体心立方(BCC)结构, 直至完全熔化. 在沿$ \langle100\rangle $晶向冲击下, 在70.0 GPa发现了FCC-BCC相变过程, 远低于之前研究中静高压的结果. 此外, 还发现了冲击方向依赖的相变点, 在沿着$ \langle110\rangle $及$ \langle111 \rangle $晶向冲击时FCC-BCC相变压力分别增加至135.8和165.4 GPa, 同时相比完美晶体, 引入缺陷会使FCC-BCC相变压强值有20—30 GPa的增幅, 并通过势能分布的分析予以验证. 本文发现冲击加载下钯的FCC-BCC相变压力大大降低的特殊现象, 为钯在高压实验等极端条件下的应用提供了新的理论认识.

关键词:

Abstract

For palladium (Pd) as a typical high-pressure standard material, studying its structural changes and thermodynamic properties under extreme conditions is widely demanded and challenging. Particularly, the solid-solid phase transition process of Pd under shock loading is understood still scarcely. In this paper, using the classical molecular dynamics simulations with embedded atom method (EAM) based on the interatomic potential, we investigate the phase transition of single crystal Pd from atomic scale under shock loading. A series of structural features is observed in a pressure range of 0–375 GPa, revealing that the structure feature transforms from the initial face-centered cubic (FCC) structure to the stacking faults body-centered cubic (BCC) structure with hexagonal close-packed (HCP) structure, and finally complete melting. Under shock loading of $ \left\langle {100} \right\rangle $ oriented bulk Pd, we find the transformation to BCC structure can take place almost at 70.0 GPa, which is much lower than the previous static calculation result. In addition, we find that the phase transition depends on the direction initially impacting crystal. Under impacting along the $ \left\langle {110} \right\rangle $ direction and the $ \left\langle {111} \right\rangle $ direction, the FCC-BCC phase transition pressures increase to 135.8 GPa and 165.4 GPa, respectively. Also, the introduction of defects will increase the phase transition pressure of FCC-BCC by 20–30 GPa in comparison with perfect crystals, which is verified by the distribution of the potential energy. An interesting phenomenon that FCC-BCC transition pressure of Pd decreases under shock loading is found in this work, which provides a new theoretical insight into the application of high pressure experiments in the future.

Keywords:

作者及机构信息

国防科技大学物理系, 长沙　410073

通信作者: 陈博, chenbochain@nudt.edu.cn ; 戴佳钰, jydai@nudt.edu.cn

基金项目: 国家自然科学基金(批准号: 11774429, 12104507)、NSAF联合基金(批准号: U1830206)、国家重点研发计划(批准号: 2017YFA0403200)和中国博士后科学基金(批准号: 2019M664024)资助的课题.

Authors and contacts

Department of Physics, National University of Defense Technology, Changsha 410073, China

Corresponding author: Chen Bo, chenbochain@nudt.edu.cn ; Dai Jia-Yu, jydai@nudt.edu.cn

Funds: Project supported by the National Natural Science Foundation of China (Grant Nos. 11774429, 12104507), the NSAF Joint Fund, China (Grant No. U1830206), the National Key R&D Program of China (Grant No. 2017YFA0403200), and the China Postdoctoral Science Foundation (Grant No. 2019M664024).

文章全文 : translate this paragraph

参考文献

[1]	Graziani F, Desjarlais M P, Redmer R, Trickey S B 2014 Frontiers and Challenges in Warm Dense Matter (Vol. 1) (Switzerland: Springer) pp1–3
[2]	Moses E I, Boyd R N, Remington B A, Keane C J, Al-Ayat R 2009 Phys. Plasmas 16 041006 Google Scholar
[3]	Mitchell A C, Nellis W J, Moriarty J A, Heinle R A, Holmes N C, Tipton R E, Repp G W 1991 J. Appl. Phys. 69 2981 Google Scholar
[4]	Nagao H, Nakamura K J, Kondo K, Ozaki N, Takamatsu K, Ono T, Shiota T, Ichinose D, Tanaka K A, Wakabayashi K 2006 Phys. Plasmas 13 052705 Google Scholar
[5]	Yokoo M, Kawai N, Nakamura K G, Kondo K I 2008 Appl. Phys. Lett. 92 051901 Google Scholar
[6]	Nellis W J, Weir S T, Mitchell A C 1996 Science 273 936 Google Scholar
[7]	Weir S T, Mitchell A C, Nellis W J 1996 Phys. Rev. Lett. 76 1860 Google Scholar
[8]	Hartley N J, Brown S, Cowan T E, Cunningham E, Döppner T, Falcone R W, Fletcher L B, Frydrych S, Galtier E, Gamboa E J 2019 Sci. Rep. 9 1
[9]	Briggs R, Coppari F, Gorman M G, Smith R F, Tracy S J, Coleman A L, Fernandez-Panella A, Millot M, Eggert J H, Fratanduono D E 2019 Phys. Rev. Lett. 123 045701 Google Scholar
[10]	Sharma S M, Turneaure S J, Winey J M, Li Y, Rigg P, Schuman A, Sinclair N, Toyoda Y, Wang X, Weir N, Zhang J, Gupta Y M 2019 Phys. Rev. Lett. 123 045702 Google Scholar
[11]	Li Q J, Liu B B 2016 Chin. Phys. B 25 076107 Google Scholar
[12]	Guo Y L, Wei J H, Liu X, Ke X Z, Jiao Z Y 2021 Chin. Phys. B 30 016101 Google Scholar
[13]	Lu M Y, Huang Y P, Tian F B, Li D, Duan D F, Zhou Q, Cui T 2020 Chin. Phys. B 29 053104 Google Scholar
[14]	Hesse R W 2007 Jewelry-Making Through History: an Encyclopedia (Westport: Greenwood Publishing Group) p146
[15]	Colon P, Pradelle-Plasse N, Galland J 2003 Dent. Mater. 19 232 Google Scholar
[16]	Harper C A 1997 Passive Electronic Component Handbook. McGraw-Hill Professional (New York: McGraw-Hill) pp580
[17]	Fleischmann M, Pons S, Hawkins M 1989 J. Electroanal. Chem. 261 301 Google Scholar
[18]	Mutschele T, Kirchheim R 1987 Scr. Mater. 21 1351101
[19]	Pundt A, Sachs C, Winter M, Reetz M T, Fritsch D, Kirchheim R 1999 J. Alloys Compd. 293-295 480
[20]	Bonivardi A L, Baltanas M A 1994 React. Kinet. Catal. Lett. 52 95
[21]	Eastman J A, Thompson L J, Kestel B J 1993 Phys. Rev. 48 84 Google Scholar
[22]	Foiles S M, Adams J B 1989 Phys. Rev. B 40 9
[23]	Foiles S M, Baskes M I, Daw M S 1986 Phys. Rev. B 33 7983 Google Scholar
[24]	Liu Z L, Yang J H, Cai L C, Jing F Q, Alfѐ D 2011 Phys. Rev. B 83 144113 Google Scholar
[25]	Errandonea D 2013 Phys. Rev. B 87 054108 Google Scholar
[26]	Jeong J W, Chang K 1999 J. Phys. Condens. Matter 11 3799 Google Scholar
[27]	Liu Z L, Zhang X L, Cai L C 2015 J. Chem. Phys. 11 637
[28]	Zheng Z Y, Zhao J J 2016 Chin. Phys. B 25 076202 Google Scholar
[29]	孙小伟, 褚衍东, 刘子江, 刘玉孝, 王成伟, 刘维民 2005 物理学报 54 5830 Google Scholar Sun X W, Zhe Y D, Liu Z J, Liu Y X, Wang C W, Liu W M 2005 Acta Phys. Sin. 54 5830 Google Scholar
[30]	段芳莉, 王家序, 雒建斌, 温诗铸 2007 物理学报 56 6552 Google Scholar Duan F L, Wang J X, Luo J B, Weng S Z 2007 Acta Phys. Sin. 56 6552 Google Scholar
[31]	邵建立, 王裴, 秦承森, 周洪强 2007 物理学报 56 5389 Google Scholar Shao J L, Wang F, Qing C S, Zhou H Q 2007 Acta Phys. Sin. 56 5389 Google Scholar
[32]	周化光, 林鑫, 王猛, 黄卫东 2013 物理学报 62 056803 Google Scholar Zhou H G, Lin X, Wang M, Huang W D 2013 Acta Phys. Sin. 62 056803 Google Scholar
[33]	Plimpton S J 1995 J. Comput. Phys. 117 1 Google Scholar
[34]	Reed E J, Fried L E, Joannopoulos J D 2003 Phys. Rev. Lett. 90 235503 Google Scholar
[35]	Stukowski A 2009 Modell. Simul. Mater. Sci. Eng. 18 015012
[36]	韦昭召, 马骁, 柯常波, 张新平 2020 物理学报 69 136102 Google Scholar Wei Z Z, Ma X, Ke C B, Zhang X P 2020 Acta Phys. Sin. 69 136102 Google Scholar
[37]	Kien P H 2014 Int. Scholarly Res. Not. 2014 253627
[38]	Sun H Y, Kang D D, Hou Y, Dai J Y 2017 Matter Radiat. at Extremes 2 287 Google Scholar
[39]	Neogi A, Mitra N 2017 Sci. Rep. 7 1 Google Scholar
[40]	Honeycutt J D, Andersen H C 1987 J. Phys. Chem. 91 4950 Google Scholar
[41]	Schiøtz J, Tolla F D D, Jacobsen K W 1998 Nature 391 561 Google Scholar
[42]	Stukowski A 2012 Model. Simul. Mater. Sci. Eng. 20 045021 Google Scholar
[43]	Faken D, Jónsson H 1994 Comput. Mater. Sci. 2 279 Google Scholar
[44]	Tsuzuki H, Branicio P, Rino J 2007 Comput. Phys. Commun. 177 518 Google Scholar
[45]	Zeng Q Y, Dai J Y 2020 Sci. China Phys. Mech. Astron. 63 263011 Google Scholar
[46]	Walsh J M, Rice M H, Mcqueen R G, Yarger F L 1957 Phys. Rev. 108 196 Google Scholar
[47]	Marsh S P 1979 Los Alamos Shock Hugoniot Data (Berkeley: University of California Press)
[48]	Thiel M V 1997 Compendium of Shock Wave Data (Livermore: Lawrence Livermore National Laboratory) Report UCRL 50108
[49]	Mcqueen R G, Marsh, S P, Taylor J W, Fritz J N, Carter W J 1970 The Equation of State of Solids from Shock Wave Studies (New York: Academic) pp348–350

施引文献

图 1 理论计算得到的雨贡纽P-V曲线与冲击实验数据的比较

Fig. 1. Hugoniot P-V curves compared with the shock experimental data and theoretical results.

下载: 全尺寸图片幻灯片

图 2 (a)沿$\left\langle {100} \right\rangle $晶向冲击后不同结构特征的钯的原子分数与纵向应力的关系; (b)不同结构特征随纵向应力变化的可视化表示; (c)温度与纵向应力的关系, 其中红色点线图为刘中利等^[24]冲击熔化的分子动力学模拟数据

Fig. 2. (a) Fraction of atoms with different structural features versus longitudinal stress along the crystallographic direction $\left\langle {100} \right\rangle $; (b) visual representation of the variation of different structural features with longitudinal stress; (c) temperature versus longitudinal stress, the red dotted line plot shows the MD simulation data of Liu et al.^[24] shock melting.

下载: 全尺寸图片幻灯片

图 3 沿不同晶向冲击后的结果　(a) $\left\langle {100} \right\rangle $晶向; (b) $\left\langle {110} \right\rangle $晶向; (c) $\left\langle {100} \right\rangle $晶向. 其中实线表示冲击速度在5.0—7.8 km/s范围内结构的RDF图像, 点划线表示与之对应的配位数曲线, 黑色虚线位置指向初始状态下的第一峰的位置

Fig. 3. Results along different crystallographic directions: (a) $\left\langle {100} \right\rangle $; (b) $\left\langle {110} \right\rangle $; (c) $\left\langle {111} \right\rangle $. The solid lines indicate radial distribution functions of deformed micro-structure shocked at a range of shock velocity of 5.0–7.8 km/s. The dotted lines indicate the coordination number curves that correspond to the RDF, and the dashed lines points to the position of the first peak in the initial state.

下载: 全尺寸图片幻灯片

图 4 利用a-CNA方法得到的沿不同晶向冲击的不同结构比例随压强的变化　(a) $\left\langle {110} \right\rangle $晶向; (b) $\left\langle {111} \right\rangle $晶向

Fig. 4. Fraction of atoms with different structural versus compressing stress along different crystallographic directions obtained by a-CNA: (a) $\left\langle {110} \right\rangle $; (b) $\left\langle {111} \right\rangle $.

下载: 全尺寸图片幻灯片

图 5 (a)不同缺陷率的晶体结构在冲击压缩后温度与压力的关系; (b), (c), (d)分别表示冲击压缩下含不同缺陷率体系的原子类别占比随冲击压强的变化

Fig. 5. (a) Comparison of Hugoniot P-T curve among crystal structures with different porosities defects; (b), (c), (d) comparison of phase transition processes of atoms of system with variation porosities defects under shock compression.

下载: 全尺寸图片幻灯片

图 6 (a)完美晶体与含缺陷晶体在冲击前后的势能差值分布图; (b)不同体系中势能差值的概率分布曲线

Fig. 6. (a) Distribution diagram of potential energy difference between perfect crystal and defective crystal before and after compression; (b) probability distribution curves of potential energy differences in perfect crystal and defective crystal.

下载: 全尺寸图片幻灯片

[1]	Graziani F, Desjarlais M P, Redmer R, Trickey S B 2014 Frontiers and Challenges in Warm Dense Matter (Vol. 1) (Switzerland: Springer) pp1–3
[2]	Moses E I, Boyd R N, Remington B A, Keane C J, Al-Ayat R 2009 Phys. Plasmas 16 041006 Google Scholar
[3]	Mitchell A C, Nellis W J, Moriarty J A, Heinle R A, Holmes N C, Tipton R E, Repp G W 1991 J. Appl. Phys. 69 2981 Google Scholar
[4]	Nagao H, Nakamura K J, Kondo K, Ozaki N, Takamatsu K, Ono T, Shiota T, Ichinose D, Tanaka K A, Wakabayashi K 2006 Phys. Plasmas 13 052705 Google Scholar
[5]	Yokoo M, Kawai N, Nakamura K G, Kondo K I 2008 Appl. Phys. Lett. 92 051901 Google Scholar
[6]	Nellis W J, Weir S T, Mitchell A C 1996 Science 273 936 Google Scholar
[7]	Weir S T, Mitchell A C, Nellis W J 1996 Phys. Rev. Lett. 76 1860 Google Scholar
[8]	Hartley N J, Brown S, Cowan T E, Cunningham E, Döppner T, Falcone R W, Fletcher L B, Frydrych S, Galtier E, Gamboa E J 2019 Sci. Rep. 9 1
[9]	Briggs R, Coppari F, Gorman M G, Smith R F, Tracy S J, Coleman A L, Fernandez-Panella A, Millot M, Eggert J H, Fratanduono D E 2019 Phys. Rev. Lett. 123 045701 Google Scholar
[10]	Sharma S M, Turneaure S J, Winey J M, Li Y, Rigg P, Schuman A, Sinclair N, Toyoda Y, Wang X, Weir N, Zhang J, Gupta Y M 2019 Phys. Rev. Lett. 123 045702 Google Scholar
[11]	Li Q J, Liu B B 2016 Chin. Phys. B 25 076107 Google Scholar
[12]	Guo Y L, Wei J H, Liu X, Ke X Z, Jiao Z Y 2021 Chin. Phys. B 30 016101 Google Scholar
[13]	Lu M Y, Huang Y P, Tian F B, Li D, Duan D F, Zhou Q, Cui T 2020 Chin. Phys. B 29 053104 Google Scholar
[14]	Hesse R W 2007 Jewelry-Making Through History: an Encyclopedia (Westport: Greenwood Publishing Group) p146
[15]	Colon P, Pradelle-Plasse N, Galland J 2003 Dent. Mater. 19 232 Google Scholar
[16]	Harper C A 1997 Passive Electronic Component Handbook. McGraw-Hill Professional (New York: McGraw-Hill) pp580
[17]	Fleischmann M, Pons S, Hawkins M 1989 J. Electroanal. Chem. 261 301 Google Scholar
[18]	Mutschele T, Kirchheim R 1987 Scr. Mater. 21 1351101
[19]	Pundt A, Sachs C, Winter M, Reetz M T, Fritsch D, Kirchheim R 1999 J. Alloys Compd. 293-295 480
[20]	Bonivardi A L, Baltanas M A 1994 React. Kinet. Catal. Lett. 52 95
[21]	Eastman J A, Thompson L J, Kestel B J 1993 Phys. Rev. 48 84 Google Scholar
[22]	Foiles S M, Adams J B 1989 Phys. Rev. B 40 9
[23]	Foiles S M, Baskes M I, Daw M S 1986 Phys. Rev. B 33 7983 Google Scholar
[24]	Liu Z L, Yang J H, Cai L C, Jing F Q, Alfѐ D 2011 Phys. Rev. B 83 144113 Google Scholar
[25]	Errandonea D 2013 Phys. Rev. B 87 054108 Google Scholar
[26]	Jeong J W, Chang K 1999 J. Phys. Condens. Matter 11 3799 Google Scholar
[27]	Liu Z L, Zhang X L, Cai L C 2015 J. Chem. Phys. 11 637
[28]	Zheng Z Y, Zhao J J 2016 Chin. Phys. B 25 076202 Google Scholar
[29]	孙小伟, 褚衍东, 刘子江, 刘玉孝, 王成伟, 刘维民 2005 物理学报 54 5830 Google Scholar Sun X W, Zhe Y D, Liu Z J, Liu Y X, Wang C W, Liu W M 2005 Acta Phys. Sin. 54 5830 Google Scholar
[30]	段芳莉, 王家序, 雒建斌, 温诗铸 2007 物理学报 56 6552 Google Scholar Duan F L, Wang J X, Luo J B, Weng S Z 2007 Acta Phys. Sin. 56 6552 Google Scholar
[31]	邵建立, 王裴, 秦承森, 周洪强 2007 物理学报 56 5389 Google Scholar Shao J L, Wang F, Qing C S, Zhou H Q 2007 Acta Phys. Sin. 56 5389 Google Scholar
[32]	周化光, 林鑫, 王猛, 黄卫东 2013 物理学报 62 056803 Google Scholar Zhou H G, Lin X, Wang M, Huang W D 2013 Acta Phys. Sin. 62 056803 Google Scholar
[33]	Plimpton S J 1995 J. Comput. Phys. 117 1 Google Scholar
[34]	Reed E J, Fried L E, Joannopoulos J D 2003 Phys. Rev. Lett. 90 235503 Google Scholar
[35]	Stukowski A 2009 Modell. Simul. Mater. Sci. Eng. 18 015012
[36]	韦昭召, 马骁, 柯常波, 张新平 2020 物理学报 69 136102 Google Scholar Wei Z Z, Ma X, Ke C B, Zhang X P 2020 Acta Phys. Sin. 69 136102 Google Scholar
[37]	Kien P H 2014 Int. Scholarly Res. Not. 2014 253627
[38]	Sun H Y, Kang D D, Hou Y, Dai J Y 2017 Matter Radiat. at Extremes 2 287 Google Scholar
[39]	Neogi A, Mitra N 2017 Sci. Rep. 7 1 Google Scholar
[40]	Honeycutt J D, Andersen H C 1987 J. Phys. Chem. 91 4950 Google Scholar
[41]	Schiøtz J, Tolla F D D, Jacobsen K W 1998 Nature 391 561 Google Scholar
[42]	Stukowski A 2012 Model. Simul. Mater. Sci. Eng. 20 045021 Google Scholar
[43]	Faken D, Jónsson H 1994 Comput. Mater. Sci. 2 279 Google Scholar
[44]	Tsuzuki H, Branicio P, Rino J 2007 Comput. Phys. Commun. 177 518 Google Scholar
[45]	Zeng Q Y, Dai J Y 2020 Sci. China Phys. Mech. Astron. 63 263011 Google Scholar
[46]	Walsh J M, Rice M H, Mcqueen R G, Yarger F L 1957 Phys. Rev. 108 196 Google Scholar
[47]	Marsh S P 1979 Los Alamos Shock Hugoniot Data (Berkeley: University of California Press)
[48]	Thiel M V 1997 Compendium of Shock Wave Data (Livermore: Lawrence Livermore National Laboratory) Report UCRL 50108
[49]	Mcqueen R G, Marsh, S P, Taylor J W, Fritz J N, Carter W J 1970 The Equation of State of Solids from Shock Wave Studies (New York: Academic) pp348–350

[1]	刘泽涛, 陈博, 令伟栋, 包南云, 康冬冬, 戴佳钰. 冲击压缩下金属钯的结构相变研究. 物理学报, 2021, (): . doi: 10.7498/aps.70.20211511
[2]	陈超, 段芳莉. 氧化石墨烯褶皱行为与结构的分子模拟研究. 物理学报, 2020, 69(19): 193102. doi: 10.7498/aps.69.20200651
[3]	周边, 杨亮. 分子动力学模拟冷却速率对非晶合金结构与变形行为的影响. 物理学报, 2020, 69(11): 116101. doi: 10.7498/aps.69.20191781
[4]	孙小伟, 宋婷, 刘子江, 万桂新, 张磊, 常文利. 氟化镁高压萤石结构稳定性及热物性的数值模拟. 物理学报, 2020, 69(15): 156202. doi: 10.7498/aps.69.20200289
[5]	冯晓伟, 李俊承, 王洪波, 常敬臻. 平板冲击下氧化铝陶瓷弹性前驱波衰减的细观机理. 物理学报, 2016, 65(16): 166201. doi: 10.7498/aps.65.166201
[6]	濮春英, 王丽, 吕林霞, 于荣梅, 何朝政, 卢志文, 周大伟. NbSi2奇异高压相及其热力学性质的第一性原理研究. 物理学报, 2015, 64(8): 087103. doi: 10.7498/aps.64.087103
[7]	胡永金, 吴云沛, 刘国营, 罗时军, 何开华. ZnTe结构相变、电子结构和光学性质的研究. 物理学报, 2015, 64(22): 227802. doi: 10.7498/aps.64.227802
[8]	林家齐, 李晓康, 杨文龙, 孙洪国, 谢志滨, 修翰江, 雷清泉. 聚酰亚胺/钽铌酸钾纳米颗粒复合材料结构与机械性能分子动力学模拟. 物理学报, 2015, 64(12): 126202. doi: 10.7498/aps.64.126202
[9]	郑小青, 杨洋, 孙得彦. 模型二元有序合金固液界面结构的分子动力学研究. 物理学报, 2013, 62(1): 017101. doi: 10.7498/aps.62.017101
[10]	董垒, 王卫国. 纯铜[0 1 1]倾侧型非共格3晶界结构稳定性分子动力学模拟研究. 物理学报, 2013, 62(15): 156102. doi: 10.7498/aps.62.156102
[11]	颜笑, 辛子华, 张娇娇. 碳硅二炔结构及性质分子动力学模拟研究. 物理学报, 2013, 62(23): 238101. doi: 10.7498/aps.62.238101
[12]	徐春龙, 侯兆阳, 刘让苏. Ca70Mg30金属玻璃形成过程热力学、动力学和结构特性转变机理的模拟研究. 物理学报, 2012, 61(13): 136401. doi: 10.7498/aps.61.136401
[13]	夏冬, 王新强. 超细Pt纳米线结构和熔化行为的分子动力学模拟研究. 物理学报, 2012, 61(13): 130510. doi: 10.7498/aps.61.130510
[14]	开花, 李运超, 郭德成, 李双, 李之杰. 斜入射离子束辅助沉积对类金刚石薄膜结构影响的分子动力学模拟. 物理学报, 2009, 58(7): 4888-4894. doi: 10.7498/aps.58.4888
[15]	陈育祥, 谢国锋, 马颖, 周益春. BaTiO3晶体结构及弹性的分子动力学模拟. 物理学报, 2009, 58(6): 4085-4089. doi: 10.7498/aps.58.4085
[16]	曹莉霞, 尚家香, 张跃. 应力诱发NiAl单晶马氏体相变的分子动力学模拟. 物理学报, 2009, 58(10): 7307-7312. doi: 10.7498/aps.58.7307
[17]	马天宝, 胡元中, 王慧. 超薄类金刚石膜生长和结构特性的分子动力学模拟. 物理学报, 2006, 55(6): 2922-2927. doi: 10.7498/aps.55.2922
[18]	孙小伟, 褚衍东, 刘子江, 刘玉孝, 王成伟, 刘维民. 高温高压下闪锌矿相GaN结构和热力学特性的分子动力学研究. 物理学报, 2005, 54(12): 5830-5836. doi: 10.7498/aps.54.5830
[19]	王昶清, 贾瑜, 马丙现, 王松有, 秦臻, 王飞, 武乐可, 李新建. 不同温度下Si(001)表面各种亚稳态结构的分子动力学模拟. 物理学报, 2005, 54(9): 4313-4318. doi: 10.7498/aps.54.4313
[20]	胡林华, 戴松元, 王孔嘉. 溶胶-凝胶法制备的纳米TiO2结构相变及晶体生长动力学. 物理学报, 2003, 52(9): 2135-2139. doi: 10.7498/aps.52.2135

计量

文章访问数: 4535
PDF下载量: 110
被引次数: 0

姓名
邮箱
手机号码
标题
留言内容
验证码

搜索

留言板

冲击压缩下金属钯的结构相变