Formation mechanism of face-centered cubic phase in impact process of single crystal iron along [101] direction

Ma Tong; Xie Hong-Xian

doi:10.7498/aps.69.20191877

Abstract

The impact phase transformation of body-centered-cubic iron is one of the hotspots in current research. Many studies demonstrated that when iron is impacted along the [100] direction, body-centered-cubic phase will transform into hexagonal close-packed phase; while when it is impacted along the [101] direction, a certain amount of face-centered-cubic phase will also appear besides hexagonal close-packed phase. The transformation from body-centered-cubic to hexagonal close-packed phase has been clarified, however, the transformation from body-centered-cubic to face-centered-cubic phase still needs further exploring. In the present work, molecular dynamics simulation is used to study the phase transformation of body-centered-cubic iron impacted along the [101] direction. The results show that the body-centered-cubic phase will transform into a close-packed structure including hexagonal close-packed phase and face-centered-cubic phase). The formation mechanism of face-centered-cubic phase is as follow. In the loading process, single crystal iron suddenly contracts along the [101] and $ [\bar101] $ directions, and expands along the [010] direction, leading to the transformation from body-centered-cubic phase to face-centered-cubic phase. The formation mechanism of hexagonal close-packed phase can be divided into two stages: first, (101) plane is compressed into close-packed plane, then hexagonal close-packed phase is obtained by the relative sliding of adjacent close-packed planes. To further investigate the formation mechanism of the close packed structure, the effect of stress state on the phase transformation of body-centered-cubic iron is further studied. Under one-dimensional (along the [101] direction) or two-dimensional loading (along [101] and $ [\bar101] $ directions), the body-centered-cubic iron transforms into face-centered-cubic iron. In the loading process the lattice constants along the three dimensions are monitored. When the transformation from body-centered-cubic phase to face-centered-cubic phase finishes, the ratio of lattice constants along three directions is 1∶1∶1.31 under one-dimensional loading; while the ratio of lattice constants is 1∶1∶1 under two-dimensional loading. Obviously, the body-centered-cubic phase transforms into distorted face-centered-cubic phase under one-dimensional loading. Under two-dimensional (along the [101] and [010] direction) and three-dimensional loading (along the [101], [010] and $ [\bar101] $ direction), the body-centered-cubic phase transforms into hexagonal close-packed phase. Gibbs free energy value for each of BCC, HCP and FCC phase is calculated. The calculation results show that the BCC phase is stable under low pressure, while the HCP and FCC phase are stable under high pressure. Finally, based on Gibbs free energy and the effect of stress state on the phase transformation, the phase transformation mechanism of body-centered-cubic iron under [101] impaction is investigated, and a reasonable explanation for the phase transformation is obtained.

Keywords:

Authors and contacts

School of Mechanical Engineering, Hebei University of Technology, Tianjin 300401, China

Corresponding author: Xie Hong-Xian, hongxianxie@hebut.edu.cn

FullText HTML : translate this paragraph

References

[1]	Bancroft D, Peterson E L, Minshall S 1956 J. Appl. Phys. 27 291 Google Scholar
[2]	Wang F M, Ingalls R 1998 Phys. Rev. B 57 5647 Google Scholar
[3]	Kalantar D H, Belak J F, Collins G W, Colvin J D, Davies H M, Eggert J H, Germann T C, Hawreliak J, Holian B L, Kadau K, Lomdahl P S, Lorenzana H E, Meyers M A, Rosolankova K, Schneider M S, Sheppard J, Stölken J S, Wark J S 2005 Phys. Rev. Lett. 95 075502 Google Scholar
[4]	Hawreliak J, Colvin J D, Eggert J H, Kalantar D H, Lorenzana H E, Stölken J S 2006 Phys. Rev. B 74 184107 Google Scholar
[5]	Yaakobi B, Boehly T R, Meyerhofer D D, Collins T J B, Remington B A, Allen P G, Pollaine S M, Lorenzana H E, Eggert J H 2005 Phys. Rev. Lett. 95 075501 Google Scholar
[6]	Hawreliak J A, El-Dasher B, Lorenzana H, Kimminau G, Higginbotham A, Nagler B, Vinko S M, Murphy W J, Whitcher T, Wark J S, Rothman S, Park N 2011 Phys. Rev. B 83 144114 Google Scholar
[7]	Kadau K, Germann T C, Lomdahl P S, Holian B L 2002 Science 296 1681 Google Scholar
[8]	Kadau K, Germann T C, Lomdahl P S, Holian B L 2005 Phys. Rev. B 72 064120 Google Scholar
[9]	Kadau K, Germann T C, Lomdahl P S, Albers R C, Wark J S, Higginbotham A, Holian B L 2007 Phys. Rev. Lett. 98 135701 Google Scholar
[10]	马文, 经福谦, 张亚林, 祝文军 2011 物理学报 60 066404 Google Scholar Ma W, Jing F Q, Zhang Y L, Zhu W J 2011 Acta Phys. Sin. 60 066404 Google Scholar
[11]	Wang B T, Shao J L, Zhang G C, Li W D, Zhang P 2009 J. Phys. Condens. Matter 21 495702 Google Scholar
[12]	Gunkelmann N, Bringa E M, Tramontina D R, Ruestes C J, Suggit M J, Higginbotham A, Wark J S, Urbassek H M 2014 Phys. Rev. B 89 140102 Google Scholar
[13]	Shao J L, Wang P, Zhang F G, He A M 2018 J. Phys. Condens. Matter 30 255401 Google Scholar
[14]	Shao J L, Wang P, Zhang F G, He A M 2018 Sci. Rep. 8 7650 Google Scholar
[15]	Plimpton S 1995 J. Comput. Phys. 117 1 Google Scholar
[16]	Chamati H, Papanicolaou N I, Mishin Y, Papaconstantopoulos D A 2006 Surf. Sci. 600 1793 Google Scholar
[17]	Holian B L, Lomdahl P S 1998 Science 280 2085 Google Scholar
[18]	邵建立, 王裴, 秦承森, 周洪强 2008 物理学报 57 1254 Google Scholar Shao J L, Wang P, Qin C S, Zhou H Q 2008 Acta Phys. Sin. 57 1254 Google Scholar
[19]	崔新林, 李英骏, 祝文军, 祁美兰, 王海燕, 贺红亮, 刘建军 2009 高压物理学报 23 37 Google Scholar Cui X L, Li Y J, Zhu W J, Qi M L, Wang H Y, He H L, Liu J J 2009 Chin. J. High Pressure Phys. 23 37 Google Scholar
[20]	何安民, 邵建立, 秦承森, 王裴 2009 物理学报 58 5667 Google Scholar He A M, Shao J L, Qin C S, Wang P 2009 Acta Phys. Sin. 58 5667 Google Scholar
[21]	Stukowski A 2012 Modell. Simul. Mater. Sci. Eng. 20 045021 Google Scholar
[22]	Stukowski A 2010 Modell Simull. Mater. Sci. Eng. 18 015012 Google Scholar
[23]	Smith R F, Eggert J H, Swift D C, Wang J, Duffy T S, Braun D G, Rudd R E, Reisman D B, Davis J P, Knudson M D, Collins G W 2013 J. Appl. Phys. 114 223507 Google Scholar
[24]	Amadou N, Resseguier T D, Brambrink E, Vinci T, Mounaix A B, Huser G, Morard G, Guyot F, Miyanishi K, Ozaki N, Kodama R, Koenig M 2016 Phys. Rev. B 93 214108 Google Scholar
[25]	Gunkelmann N, Tramontina D R, Bringa E M, Urbassek H M 2014 New J. Phys. 16 093032 Google Scholar
[26]	Amadou N, de Resseguier T, Dragon A, Brambrink E 2018 Phys. Rev. B 98 024104 Google Scholar
[27]	邵建立, 秦承森, 王裴 2008 金属学报 44 1085 Google Scholar Shao J L, Qin C S, Wang P 2008 Acta Metall. Sin. 44 1085 Google Scholar
[28]	Dewaele A, Denoual C, Anzellini S, Occelli F, Mezouar M, Cordier P, Merkel S, Véron M, Rausch E 2015 Phys. Rev. B 91 174105 Google Scholar
[29]	Xie H X, Yu T, Fang W, Yin F X, Khan D F 2016 Chin. Phys. B 25 126201 Google Scholar
[30]	Cui X L, Zhu W J, He H L, Deng X L, Li Y J 2008 Phys. Rev. B 78 024115 Google Scholar
[31]	贺红亮, 祝文军, 邓小良, 李英骏, 崔新林 2006 物理学报 55 5545 Google Scholar He H L, Zhu W J, Deng X L, Li Y J, Cui X L 2006 Acta Phys. Sin. 55 5545 Google Scholar
[32]	崔新林, 祝文军, 贺红亮, 邓小良, 李英骏 2007 高压物理学报 21 433 Google Scholar Cui X L, Zhu W J, He H L, Deng X L, Li Y J 2007 Chin. J. High Pressure Phys. 21 433 Google Scholar
[33]	Dremov V V, Ionov G V, Sapozhnikov F A, Smirnov N A, Karavaev A V, Vorobyova M A, Ryzhkov M V 2015 EPJ Web Conf. 94 04023 Google Scholar
[34]	Djohari H, Milstein F, Maroudas D 2009 Phys. Rev. B 79 174109 Google Scholar
[35]	Wang S J, Sui M L, Chen Y T, Lu Q H, Ma E, Pei X Y, Li Q Z, Hu H B 2013 Sci. Rep. 3 1086 Google Scholar
[36]	Guo Y F, Wang Y S, Zhao D L, Wu W P 2007 Acta Mater. 55 6634 Google Scholar

Cited By

图 1 BCC铁冲击初始模型

Figure 1. Initial model of BCC iron impact.

DownLoad: Full-Size Img PowerPoint

图 2 单晶铁沿[101]方向的冲击压缩过程(冲击速度为1.05 km/s)　(a) 冲击过程中不同时刻模型中的压应力; (b) 8 ps时刻的模型, 图中蓝色、红色分别代表BCC和HCP相, 绿色代表FCC相或者HCP相的层错

Figure 2. The simulation of a single crystal iron model which was impacted along [101] crystal direction (the impact speed was 1.05 km/s): (a) The stress in the impacted sample at different times; (b) the impacted sample at 8 ps. Blue and red parts represent BCC and HCP phase, respectively; green part represents FCC or stacking fault of HCP phase.

DownLoad: Full-Size Img PowerPoint

图 3 冲击后模型向X轴((101)面)的投影(蓝球、红球和绿球分别代表位于BCC相、HCP相和FCC相(或HCP相中的层错)中的铁原子)

Figure 3. The atoms’ configuration on the (101) plane after impaction (blue, red and green balls represent the iron atoms in BCC phase, HCP phase and FCC phase (or stacking fault of HCP), respectively.

DownLoad: Full-Size Img PowerPoint

图 4 BCC铁沿[101]晶向冲击条件下HCP和FCC相的形成机制　(a) 一个结构单元的BCC-HCP相变机制; (b) (101)面的原子运动规律(黄色箭头代表(101)面原子收缩方向, 黑色箭头代表(101)面相对滑移方向(1—6号原子和7—9号原子分别对应(a)中的第一层和第二层原子面; u为(101)面相对滑移距离.); (c) 原子间距离随冲击时间的变化; (d) BCC-FCC相变机制(为了方便观察, 将结构单元中的面心原子设置为黄色); (e) 晶格常数随冲击时间的变化

Figure 4. The formation mechanisms of HCP and FCC phase under impact of BCC iron along [101] direction: (a) The BCC-HCP phase transition mechanism of a structural unit; (b) the atomic motion of (101) plane (yellow arrow represents the contraction direction of (101) plane, and black arrow represents the relative sliding direction of (101) plane (atoms 1—6 and 7—9 correspond to the first and second atomic planes in (a) respectively; u is the relative sliding distance of (101) plane); (c) the change of atomic distance with impact time; (d) BCC-FCC phase transition mechanism (set the face center atom in the structural unit to yellow for easy observation); (e) the change of lattice constant with impact time.

DownLoad: Full-Size Img PowerPoint

图 5 BCC铁沿[101]晶向在单轴压缩下的相变机制　(a) 压缩过程中的三个快照; (b)应力、晶格常数以及单个原子能量($ {E}_{\mathrm{t}\mathrm{o}\mathrm{t}\mathrm{a}\mathrm{l}} $)随加载时间的变化; (c) 一个结构单元的相变过程(为了方便观察, 将结构单元中的面心原子设置为黄色)

Figure 5. The transformation mechanism of BCC iron under uniaxial compression along [101] direction: (a) Three snapshots during compression (b) the variation of stress, lattice constant and energy of single atom ($ {E}_{\mathrm{t}\mathrm{o}\mathrm{t}\mathrm{a}\mathrm{l}} $) with loading time; (c) the phase transition process of a structural unit (set the face center atom in the structural unit to yellow for easy observation).

DownLoad: Full-Size Img PowerPoint

图 6 BCC铁沿[101]和$ [\bar101] $方向同时压缩下的相变机制　(a) 压缩过程中的三个快照; (b) 应力、晶格常数以及单个原子能量随加载时间的变化; (c)一个结构单元的相变过程(结构单元中的面心原子设置为黄色)

Figure 6. The phase transformation mechanism of BCC iron under simultaneous compression along [101] and $ [\bar101] $ directions: (a) Three snapshots during compression; (b) the variation of stress, lattice constant and energy of single atom with loading time; (c) the phase transition process of a structural unit (set the face center atom in the structural unit to yellow for easy observation).

DownLoad: Full-Size Img PowerPoint

图 7 沿[101]和[010]方向同时压缩下BCC铁的相变机理　(a) 压缩期间的三个快照(蓝色和红色球分别代表BCC相和HCP相的铁原子); (b) 应力、原子距离以及单个原子能量随加载时间的变化(原子距离与(c)中原子相对应); (c) BCC-HCP相变机制(黄色箭头代表(101)面原子收缩方向, 黑色箭头代表(101)面相对滑移方向)

Figure 7. The transformation mechanism of BCC iron under simultaneous compression along [101] and [010] directions: (a) Three snapshots during compression (blue and red spheres represent the iron atoms of BCC and HCP phases respectively); (b) the variation of stress, atomic distance and energy of single atom with loading time (the atomic distance corresponds to the atom in (c)); (c) BCC-HCP phase transformation process (yellow arrow represents the contraction direction of (101) plane, and black arrow represents the relative sliding direction of (101) plane).

DownLoad: Full-Size Img PowerPoint

图 8 BCC铁在三轴压缩下的相变机理　(a) 压缩过程中的三个快照(蓝色和红色的球分别代表BCC相和HCP相的铁原子); (b) 应力、原子距离以及单个原子能量随加载时间的变化(原子距离与(c)中原子相对应); (c) BCC-HCP相变机制(黄色箭头代表(101)面原子收缩方向, 黑色箭头代表(101)面相对滑移方向)

Figure 8. The phase transformation mechanism of BCC iron under triaxial compression: (a) Three snapshots during compression (blue and red spheres represent the iron atoms of BCC and HCP phases respectively); (b) the variation of stress, atomic distance and energy of single atom with loading time (the atomic distance corresponds to the atom in (c)); (c) BCC-HCP phase transformation process ( yellow arrow indicates the contraction direction of (101) plane atom, and black arrow indicates the relative sliding direction of (101) plane atom).

DownLoad: Full-Size Img PowerPoint

图 9 铁BCC, HCP 和FCC相吉布斯自由能随静水压力的变化

Figure 9. Gibbs free energies of BCC, HCP and FCC phases change with pressure.

DownLoad: Full-Size Img PowerPoint

[1]	Bancroft D, Peterson E L, Minshall S 1956 J. Appl. Phys. 27 291 Google Scholar
[2]	Wang F M, Ingalls R 1998 Phys. Rev. B 57 5647 Google Scholar
[3]	Kalantar D H, Belak J F, Collins G W, Colvin J D, Davies H M, Eggert J H, Germann T C, Hawreliak J, Holian B L, Kadau K, Lomdahl P S, Lorenzana H E, Meyers M A, Rosolankova K, Schneider M S, Sheppard J, Stölken J S, Wark J S 2005 Phys. Rev. Lett. 95 075502 Google Scholar
[4]	Hawreliak J, Colvin J D, Eggert J H, Kalantar D H, Lorenzana H E, Stölken J S 2006 Phys. Rev. B 74 184107 Google Scholar
[5]	Yaakobi B, Boehly T R, Meyerhofer D D, Collins T J B, Remington B A, Allen P G, Pollaine S M, Lorenzana H E, Eggert J H 2005 Phys. Rev. Lett. 95 075501 Google Scholar
[6]	Hawreliak J A, El-Dasher B, Lorenzana H, Kimminau G, Higginbotham A, Nagler B, Vinko S M, Murphy W J, Whitcher T, Wark J S, Rothman S, Park N 2011 Phys. Rev. B 83 144114 Google Scholar
[7]	Kadau K, Germann T C, Lomdahl P S, Holian B L 2002 Science 296 1681 Google Scholar
[8]	Kadau K, Germann T C, Lomdahl P S, Holian B L 2005 Phys. Rev. B 72 064120 Google Scholar
[9]	Kadau K, Germann T C, Lomdahl P S, Albers R C, Wark J S, Higginbotham A, Holian B L 2007 Phys. Rev. Lett. 98 135701 Google Scholar
[10]	马文, 经福谦, 张亚林, 祝文军 2011 物理学报 60 066404 Google Scholar Ma W, Jing F Q, Zhang Y L, Zhu W J 2011 Acta Phys. Sin. 60 066404 Google Scholar
[11]	Wang B T, Shao J L, Zhang G C, Li W D, Zhang P 2009 J. Phys. Condens. Matter 21 495702 Google Scholar
[12]	Gunkelmann N, Bringa E M, Tramontina D R, Ruestes C J, Suggit M J, Higginbotham A, Wark J S, Urbassek H M 2014 Phys. Rev. B 89 140102 Google Scholar
[13]	Shao J L, Wang P, Zhang F G, He A M 2018 J. Phys. Condens. Matter 30 255401 Google Scholar
[14]	Shao J L, Wang P, Zhang F G, He A M 2018 Sci. Rep. 8 7650 Google Scholar
[15]	Plimpton S 1995 J. Comput. Phys. 117 1 Google Scholar
[16]	Chamati H, Papanicolaou N I, Mishin Y, Papaconstantopoulos D A 2006 Surf. Sci. 600 1793 Google Scholar
[17]	Holian B L, Lomdahl P S 1998 Science 280 2085 Google Scholar
[18]	邵建立, 王裴, 秦承森, 周洪强 2008 物理学报 57 1254 Google Scholar Shao J L, Wang P, Qin C S, Zhou H Q 2008 Acta Phys. Sin. 57 1254 Google Scholar
[19]	崔新林, 李英骏, 祝文军, 祁美兰, 王海燕, 贺红亮, 刘建军 2009 高压物理学报 23 37 Google Scholar Cui X L, Li Y J, Zhu W J, Qi M L, Wang H Y, He H L, Liu J J 2009 Chin. J. High Pressure Phys. 23 37 Google Scholar
[20]	何安民, 邵建立, 秦承森, 王裴 2009 物理学报 58 5667 Google Scholar He A M, Shao J L, Qin C S, Wang P 2009 Acta Phys. Sin. 58 5667 Google Scholar
[21]	Stukowski A 2012 Modell. Simul. Mater. Sci. Eng. 20 045021 Google Scholar
[22]	Stukowski A 2010 Modell Simull. Mater. Sci. Eng. 18 015012 Google Scholar
[23]	Smith R F, Eggert J H, Swift D C, Wang J, Duffy T S, Braun D G, Rudd R E, Reisman D B, Davis J P, Knudson M D, Collins G W 2013 J. Appl. Phys. 114 223507 Google Scholar
[24]	Amadou N, Resseguier T D, Brambrink E, Vinci T, Mounaix A B, Huser G, Morard G, Guyot F, Miyanishi K, Ozaki N, Kodama R, Koenig M 2016 Phys. Rev. B 93 214108 Google Scholar
[25]	Gunkelmann N, Tramontina D R, Bringa E M, Urbassek H M 2014 New J. Phys. 16 093032 Google Scholar
[26]	Amadou N, de Resseguier T, Dragon A, Brambrink E 2018 Phys. Rev. B 98 024104 Google Scholar
[27]	邵建立, 秦承森, 王裴 2008 金属学报 44 1085 Google Scholar Shao J L, Qin C S, Wang P 2008 Acta Metall. Sin. 44 1085 Google Scholar
[28]	Dewaele A, Denoual C, Anzellini S, Occelli F, Mezouar M, Cordier P, Merkel S, Véron M, Rausch E 2015 Phys. Rev. B 91 174105 Google Scholar
[29]	Xie H X, Yu T, Fang W, Yin F X, Khan D F 2016 Chin. Phys. B 25 126201 Google Scholar
[30]	Cui X L, Zhu W J, He H L, Deng X L, Li Y J 2008 Phys. Rev. B 78 024115 Google Scholar
[31]	贺红亮, 祝文军, 邓小良, 李英骏, 崔新林 2006 物理学报 55 5545 Google Scholar He H L, Zhu W J, Deng X L, Li Y J, Cui X L 2006 Acta Phys. Sin. 55 5545 Google Scholar
[32]	崔新林, 祝文军, 贺红亮, 邓小良, 李英骏 2007 高压物理学报 21 433 Google Scholar Cui X L, Zhu W J, He H L, Deng X L, Li Y J 2007 Chin. J. High Pressure Phys. 21 433 Google Scholar
[33]	Dremov V V, Ionov G V, Sapozhnikov F A, Smirnov N A, Karavaev A V, Vorobyova M A, Ryzhkov M V 2015 EPJ Web Conf. 94 04023 Google Scholar
[34]	Djohari H, Milstein F, Maroudas D 2009 Phys. Rev. B 79 174109 Google Scholar
[35]	Wang S J, Sui M L, Chen Y T, Lu Q H, Ma E, Pei X Y, Li Q Z, Hu H B 2013 Sci. Rep. 3 1086 Google Scholar
[36]	Guo Y F, Wang Y S, Zhao D L, Wu W P 2007 Acta Mater. 55 6634 Google Scholar

[1]	Zhang Xue-Yang, Hu Wang-Yu, Dai Xiong-Ying. Influence of iron anisotropy on phase transition near grain boundary under shock. Acta Physica Sinica, 2024, 73(3): 036201. doi: 10.7498/aps.73.20231081
[2]	Wang Lu-Sheng, Luo Long, Liu Hao, Yang Xin, Ding Jun, Song Kun, Lu Shi-Qing, Huang Xia. Law and mechanism of impact velocity on spalling and fracture behavior of single crystal nickel. Acta Physica Sinica, 2024, 73(16): 164601. doi: 10.7498/aps.73.20240244
[3]	Zhao Zhong-Hua, Qu Guang-Hao, Yao Jia-Chi, Min Dao-Min, Zhai Peng-Fei, Liu Jie, Li Sheng-Tao. Molecular dynamics simulation of phase transition by thermal spikes in monoclinic ZrO₂. Acta Physica Sinica, 2021, 70(13): 136101. doi: 10.7498/aps.70.20201861
[4]	Hua Ying-Xin, Liu Fu-Sheng, Geng Hua-Yun, Hao Long, Yu Ji-Dong, Tan Ye, Li Jun. Kinetics of iron α-εphase transition under thermodynamic path of multiple shock loading-unloading. Acta Physica Sinica, 2021, 70(16): 166201. doi: 10.7498/aps.70.20210089
[5]	Diwu Min-Jie, Hu Xiao-Mian. Molecular dynamics simulation of shock-induced isostructural phase transition in single crystal Ce. Acta Physica Sinica, 2020, 69(11): 116202. doi: 10.7498/aps.69.20200323
[6]	Zhu Qi, Wang Sheng-Tao, Zhao Fu-Qi, Pan Hao. Effect of stacking fault tetrahedron on spallation of irradiated Cu via molecular dynamics study. Acta Physica Sinica, 2020, 69(3): 036201. doi: 10.7498/aps.69.20191425
[7]	Li Jun, Wu Qiang, Yu Ji-Dong, Tan Ye, Yao Song-Lin, Xue Tao, Jin Ke. Orientation effect of alpha-to-epsilon phase transformation in single-crystal iron. Acta Physica Sinica, 2017, 66(14): 146201. doi: 10.7498/aps.66.146201
[8]	Jiang Zhao-Xiu, Xin Ming-Zhi, Shen Hai-Ting, Wang Yong-Gang, Nie Heng-Chang, Liu Yu-Sheng. Mechanical properties and phase transformation of porous unpoled Pb(Zr0.95Ti0.05)O3 ferroelectric ceramics under uniaxial compression. Acta Physica Sinica, 2015, 64(13): 134601. doi: 10.7498/aps.64.134601
[9]	Shao Jian-Li, Wang Pei, He An-Min, Qin Cheng-Sen. Microscopic simulation on shock-induced micro-jet ejection from metal Al surface. Acta Physica Sinica, 2012, 61(18): 184701. doi: 10.7498/aps.61.184701
[10]	Wang Jun-Guo, Liu Fu-Sheng, Li Yong-Hong, Zhang Ming-Jian, Zhang Ning-Chao, Xue Xue-Dong. The structural transition of water at quartz/water interfaces under shock compression in phase region of liquid. Acta Physica Sinica, 2012, 61(19): 196201. doi: 10.7498/aps.61.196201
[11]	Ma Wen, Zhu Wen-Jun, Zhang Ya-Lin, Jing Fu-Qian. Shock-induced phase transformation in nanocrystalline iron. Acta Physica Sinica, 2011, 60(6): 066404. doi: 10.7498/aps.60.066404
[12]	Li Yong-Hong, Liu Fu-Sheng, Cheng Xiao-Li, Zhang Ming-Jian, Xue Xue-Dong. Crystallization of water induced by fused quartz under shock compression. Acta Physica Sinica, 2011, 60(12): 126202. doi: 10.7498/aps.60.126202
[13]	Wang Zhi-Gang, Wu Liang, Zhang Yang, Wen Yu-Hua. Phase transition and coalescence behavior of fcc Fe nanoparticles: a molecular dynamics study. Acta Physica Sinica, 2011, 60(9): 096105. doi: 10.7498/aps.60.096105
[14]	Lu Zhi-Peng, Zhu Wen-Jun, Lu Tie-Cheng, Liu Shao-Jun, Cui Xin-Lin, Chen Xiang-Rong. The mechanism of structure phase transition from α Fe to ε Fe under uniaxial strain: First-principles calculations. Acta Physica Sinica, 2010, 59(6): 4303-4312. doi: 10.7498/aps.59.4303
[15]	Shao Jian-Li, He An-Min, Duan Su-Qing, Wang Pei, Qin Cheng-Sen. Atomistic simulation of the bcc—hcp transition in iron driven by uniaxial strain. Acta Physica Sinica, 2010, 59(7): 4888-4894. doi: 10.7498/aps.59.4888
[16]	Shao Jian-Li, Qin Cheng-Sen, Wang Pei. Atomistic simulation of mechanical properties of martensitic transformation under dynamic compression. Acta Physica Sinica, 2009, 58(3): 1936-1941. doi: 10.7498/aps.58.1936
[17]	Lu Zhi-Peng, Zhu Wen-Jun, Liu Shao-Jun, Lu Tie-Cheng, Chen Xiang-Rong. Structure phase transition from α to ε in Fe under non-hydrostatic pressure: an ab initio study. Acta Physica Sinica, 2009, 58(3): 2083-2089. doi: 10.7498/aps.58.2083
[18]	Shao Jian-Li, Wang Pei, Qin Cheng-Sen, Zhou Hong-Qiang. Study of nucleation of void-induced phase transformation under shock compression. Acta Physica Sinica, 2008, 57(2): 1254-1258. doi: 10.7498/aps.57.1254
[19]	Shao Jian-Li, Wang Pei, Qin Cheng-Sen, Zhou Hong-Qiang. Shock-induced phase transformations of iron studied with molecular dynamics. Acta Physica Sinica, 2007, 56(9): 5389-5393. doi: 10.7498/aps.56.5389
[20]	Cui Xin-Lin, Zhu Wen-Jun, Deng Xiao-Liang, Li Ying-Jun, He Hong-Liang. Molecular dynamic simulation of shock-induced phase transformation in single crystal iron with nano-void inclusion. Acta Physica Sinica, 2006, 55(10): 5545-5550. doi: 10.7498/aps.55.5545

Catalog

Vol. 69, Issue 13 - 2020-07-05

Metrics

Abstract views: 9846
PDF Downloads: 116
Cited By: 0

姓名
邮箱
手机号码
标题
留言内容
验证码

Search

Article

留言板