Effect of manganese doping on ferroelectric and piezoelectric properties of KNbO3 and (K0.5Na0.5)NbO3 lead-free ceramics

Xu Ze; Lou Lu-Yao; Zhao Chun-Lin; Tang Hao-Cheng; Liu Yi-Xuan; Li Zhao; Qi Xiao-Mei; Zhang Bo-Ping; Li Jing-Feng; Gong Wen; Wang Ke

doi:10.7498/aps.69.20200277

Abstract

Potassium sodium niobate ((K_0.5Na_0.5)NbO₃)-based lead-free piezoelectric ceramics are excellent ferroelectric materials and have been demonstrated to have many practical applications. Recent studies have revealed that chemical doping plays a crucial role in optimizing the electromechanical coupling properties of (K_0.5Na_0.5)NbO₃-based piezoelectric ceramics. In this paper, MnO₂ is doped into potassium niobate (KNbO₃) and (K_0.5Na_0.5)NbO₃ piezoelectric ceramics prepared by the conventional solid-state reaction method. The influences of doped Mn cation on KNbO₃ and (K_0.5Na_0.5)NbO₃ piezoelectric ceramics including microstructure and macroscopic electrical properties are systematically investigated. The doping effects of Mn cation on the KNbO₃ and (K_0.5Na_0.5)NbO₃ piezoelectric ceramics are significantly different from each other. For the Mn-doped KNbO₃ piezoelectric ceramics, the sizes of ferroelectric domains are reduced. Meanwhile, the diffused orthorhombic-tetragonal phase transition is observed, which is accompanied by reducing dielectric loss and Curie temperature, and broadening vibration peaks in Raman spectrum. It is known that the oxygen vacancy can be formed to compensate for the charges created by the acceptor doping of Mn into the B site of perovskite, and thus forming a defect dipole with the acceptor center. From the ferroelectric measurement, a double hysteresis loop (P-E curve) and a recoverable electric-field-induced strain due to the formation of defect dipole are observed. On the contrary, for the Mn-doped (K_0.5Na_0.5)NbO₃ piezoelectric ceramics, the sizes of ferroelectric domains are not reduced. Meanwhile, the Curie temperature and vibration peaks in Raman spectrum are not changed. A rectangular hysteresis loop (P-E curve) and an unrecoverable electric-field-induced strain are observed in the ferroelectric measurement. The difference between these systems might originate from the greater ionic disorder and lattice distortion in (K_0.5Na_0.5)NbO₃ piezoelectric ceramics. The difference in ionic radius between Na⁺ and K⁺ can affect the migration and distribution of oxygen vacancies, which makes it difficult to form stable defect dipoles in the Mn-doped (K_0.5Na_0.5)NbO₃ piezoelectric ceramics. The results will serve as an important reference for preparing high-performance (K_0.5Na_0.5)NbO₃-based piezoelectric ceramics via chemical doping.

Keywords:

Authors and contacts

1.
State Key Laboratory of New Ceramics and Fine Processing, School of Materials Science and Engineering, Tsinghua University, Beijing 100084, China
2.
School of Materials Science and Engineering, University of Science and Technology Beijing, Beijing 100083, China
3.
Advanced Ceramic Materials & Devices Research Center, Yangtze Delta Region Institute of Tsinghua University, Zhejiang, Jiaxing 314006, China

Corresponding author: Zhang Bo-Ping, bpzhang@ustb.edu.cn ; Gong Wen, gongwen@tsinghua-zj.edu.cn ; Wang Ke, wang-ke@tsinghua.edu.cn

FullText HTML : translate this paragraph

References

[1]	Wang K, Malič B, Wu J 2018 MRS Bull. 43 607 Google Scholar
[2]	Thong H C, Zhao C, Zhou Z, Wu C F, Liu Y X, Du Z Z, Li J F, Gong W, Wang K 2019 Mater. Today 29 37 Google Scholar
[3]	吴金根, 高翔宇, 陈建国, 王春明, 张树君, 董蜀湘 2018 物理学报 67 207701 Google Scholar Wu J G, Gao X Y, Chen J G, Wang C M, Zhang S J, Dong S X 2018 Acta Phys. Sin. 67 207701 Google Scholar
[4]	刘涛, 丁爱丽, 何夕云, 郑鑫森, 仇萍荪, 程文秀 2007 无机材料学报 22 469 Google Scholar Liu T, Ding A L, He X Y, Zheng X S, Qiu P S, Cheng W X 2007 J. Inorg. Mater. 22 469 Google Scholar
[5]	Saito Y, Takao H, Tani T, Nonoyama T, Takatori K, Homma T, Nagaya T, Nakamura M 2004 Nature 432 84 Google Scholar
[6]	Koruza J, Bell A J, Frömling T, Webber K G, Wang K, Rödel J 2018 J. Materiomics 4 13 Google Scholar
[7]	Liu Q, Zhang Y, Gao J, Zhou Z, Yang D, Lee K Y, Studer A, Hinterstein M, Wang K, Zhang X, Li L, Li J F 2020 Natl. Sci. Rev. 7 355 Google Scholar
[8]	Zhang J, Pan Z, Guo F F, Liu W C, Ning H, Chen Y B, Lu M H, Yang B, Chen J, Zhang S T, Xing X, Rödel J, Cao W, Chen Y F 2015 Nat. Commun. 6 1 Google Scholar
[9]	Wang Y, Luo C, Wang S, Chen C, Yuan G, Luo H, Viehland D 2020 Adv. Electron. Mater. 6 1900949 Google Scholar
[10]	Wu J, Xiao D, Zhu J 2015 Chem. Rev. 115 2559 Google Scholar
[11]	Mgbemere H E, Herber R P, Schneider G A 2009 J. Eur. Ceram. Soc. 29 1729 Google Scholar
[12]	Cheng X, Wu J, Lou X, Wang X, Wang X, Xiao D, Zhu J 2014 ACS Appl. Mater. Inter. 6 750 Google Scholar
[13]	Hao J, Li W, Zhai J, Chen H 2019 Mat. Sci. Eng. R 135 1 Google Scholar
[14]	Wang K, Yao F Z, Jo W, Gobeljic D, Shvartsman V V, Lupascu D C, Li J F, Rödel J 2013 Adv. Funct. Mater. 23 4079 Google Scholar
[15]	Yao F Z, Wang K, Jo W, Webber K G, Comyn T P, Ding J X, Xu B, Cheng L Q, Zheng M P, Hou Y D, Li J F 2016 Adv. Funct. Mater. 26 1217 Google Scholar
[16]	Zheng T, Wu J, Xiao D, Zhu J 2018 Prog. Mater. Sci. 98 552 Google Scholar
[17]	Tao H, Wu H, Liu Y, Zhang Y, Wu J, Li F, Lü X, Zhao C, Xiao D, Zhu J, Pennycook S J 2019 J. Am. Chem. Soc. 141 13987 Google Scholar
[18]	Zhang M H, Wang K, Du Y J, Dai G, Sun W, Li G, Hu D, Thong H C, Zhao C, Xi X Q, Yue Z X, Li J F 2017 J. Am. Chem. Soc. 139 3889 Google Scholar
[19]	王轲, 沈宗洋, 张波萍, 李敬锋 2014 无机材料学报 29 13 Google Scholar Wang K, Shen Z Y, Zhang B P, Li J F 2014 J. Inorg. Mater. 29 13 Google Scholar
[20]	Hollenstein E, Davis M, Damjanovic D, Setter N 2005 Appl. Phys. Lett. 87 182905 Google Scholar
[21]	Birol H, Damjanovic D, Setter N 2005 J. Am. Ceram. Soc. 88 1754 Google Scholar
[22]	Kim D H, Joung M R, Seo I T, Hur J, Kim J H, Kim B Y, Lee H J, Nahm S 2014 J. Eur. Ceram. Soc. 34 4193 Google Scholar
[23]	Du H, Li Z, Tang F, Qu S, Pei Z, Zhou W 2006 Mat. Sci. Eng. B 131 83 Google Scholar
[24]	Lin D, Kwok K W, Chan H L W 2008 J. Alloys Compd. 461 273 Google Scholar
[25]	Wu L, Zhang J L, Wang C L, Li J C 2008 J. Appl. Phys. 103 084116 Google Scholar
[26]	Standards Committee of the IEEE Ultrasonics, Ferroelectrics, and Frequency Control Society 1988 IEEE Standard on Piezoelectricity (New York: IEEE) ANSI/IEEE Std. 176-1987
[27]	Thong H C, Xu Z, Zhao C, Lou L Y, Chen S, Zuo S Q, Li J F, Wang K 2019 J. Am. Ceram. Soc. 102 836 Google Scholar
[28]	Camargo J, Espinosa P A, Zabotto F, Ramajo L, Castro M 2020 J. Alloys Compd. 826 154129 Google Scholar
[29]	李睿 2015 物理学报 64 167303 Google Scholar Li R 2015 Acta Phys. Sin. 64 167303 Google Scholar
[30]	贺连星, 李承恩 2000 无机材料学报 15 293 Google Scholar He L X, Li C E 2000 J. Inorg. Mater. 15 293 Google Scholar
[31]	Kamiya T, Suzuki T, Tsurumi T, Daimon M 1992 Jpn. J. Appl. Phys. 31 3058 Google Scholar
[32]	Yao F Z, Zhang M H, Wang K, Zhou J J, Chen F, Xu B, Li F, Shen Y, Zhang Q H, Gu L, Zhang X W, Li J F 2018 ACS Appl. Mater. Inter. 10 37298 Google Scholar
[33]	Cheng L Q, Wang K, Yu Q, Li J F 2014 J. Mater. Chem. C 2 1519 Google Scholar
[34]	Shen Z X, Hu Z P, Chong T C, Beh C Y, Tang S H, Kuok M H 1995 Phys. Rev. B 52 3976
[35]	Sundarakannan B, Kakimoto K, Ohsato H 2004 Ferroelectrics 302 175 Google Scholar
[36]	路朋献, 许德合, 马秋花, 王改民, 侯永改, 周文俊, 栗政新 2007 红外与毫米波学报 26 69 Google Scholar Lu P X, Xu D H, Ma Q H, Wang G M, Hou Y G, Zhou W J, Li Z X 2007 J. Infrared Millm. W. 26 69 Google Scholar
[37]	Wang Z, Gu H, Hu Y, Yang K, Hu M, Zhou D, Guan J 2010 Cryst. Eng. Comm. 12 3157 Google Scholar
[38]	Li J F, Wang K, Zhu F Y, Cheng L Q, Yao F Z 2013 J. Am. Ceram. Soc. 96 3677 Google Scholar
[39]	刘霄, 徐小敏, 杜慧玲 2018 无机材料学报 33 683 Google Scholar Liu X, Xu X M, Du H L 2018 J. Inorg. Mater. 33 683 Google Scholar
[40]	Lee D, Jeon B C, Baek S H, Yang J S, Kim T H, Kim Y S, Yoon J G, Eom C B, Noh T W 2012 Adv. Mater. 24 6490 Google Scholar
[41]	Ren X 2004 Nat. Mater. 3 91 Google Scholar
[42]	Feng Z, Ren X 2007 Appl. Phys. Lett. 91 032904 Google Scholar
[43]	Voas B K, Usher T M, Liu X, Li S, Jones J L, Tan X, Cooper V R, Beckman S P 2014 Phys. Rev. B 90 024105 Google Scholar
[44]	Steiner S, Seo I T, Ren P, Li M, Keeble D J, Frömling T 2019 J. Am. Ceram. Soc. 102 5295 Google Scholar
[45]	Herber R P, Schneider G A, Wagner S, Hoffmann M J 2007 Appl. Phys. Lett. 90 252905 Google Scholar
[46]	Nakamura K, Tokiwa T, Kawamura Y 2002 J. Appl. Phys. 91 9272 Google Scholar
[47]	Qin Y, Zhang J, Yao W, Wang C, Zhang S 2015 J. Am. Ceram. Soc. 98 1027 Google Scholar

Cited By

图 1 KN, KN-Mn, KNN和KNN-Mn陶瓷XRD图谱

Figure 1. XRD patterns of KN, KN-Mn, KNN, and KNN-Mn ceramics.

DownLoad: Full-Size Img PowerPoint

图 2 经热腐蚀的表面SEM形貌图　(a) KN陶瓷; (b) KN-Mn陶瓷; (c) KNN陶瓷; (d) KNN-Mn陶瓷

Figure 2. SEM images of the thermally etched surface: (a) KN, (b) KN-Mn, (c) KNN, (d) KNN-Mn ceramics.

DownLoad: Full-Size Img PowerPoint

图 3 (a)−(d)纵向压电响应模式(VPFM)、(e)−(h)横向压电响应模式(LPFM)下测试的未极化KN, KN-Mn, KNN, KNN-Mn陶瓷的铁电畴形貌图

Figure 3. Domain images of unpoled KN, KN-Mn, KNN, KNN-Mn ceramics tested in (a)−(d) vertical piezoresponse force microscopy (VPFM) and (e)−(h) lateral piezoresponse force microscopy (LPFM).

DownLoad: Full-Size Img PowerPoint

图 4 X波段ESR谱图　(a) KN-Mn陶瓷; (b) KNN-Mn陶瓷

Figure 4. X-band ESR spectra: (a) KN-Mn ceramics; (b) KNN-Mn ceramics.

DownLoad: Full-Size Img PowerPoint

图 5 (a) KN, KN-Mn, KNN和KNN-Mn陶瓷的拉曼散射光谱图; (b) NbO₆八面体三种内部振动模的示意图, 其中V₁和V₂为拉伸振动模、V₅为弯曲振动模

Figure 5. (a) Raman spectra of KN, KN-Mn, KNN, KNN-Mn ceramics; (b) schematic illustration of three internal vibrational modes of NbO₆ octahedra. V₁ and V₂ are stretching modes, and V₅ is bending mode.

DownLoad: Full-Size Img PowerPoint

图 6 陶瓷的相对介电常数和介电损耗随温度的变化　(a) KN, KN-Mn陶瓷; (b) KNN, KNN-Mn陶瓷

Figure 6. Temperature dependence of dielectric permittivity and dielectric loss of unpoled for ceramics: (a) KN, KN-Mn ceramics; (b) KNN, KNN-Mn ceramics.

DownLoad: Full-Size Img PowerPoint

图 7 (a) KN, (b) KN-Mn, (e) KNN, (f) KNN-Mn陶瓷的电滞回线; (c) KN, (d) KN-Mn, (g) KNN, (h) KNN-Mn陶瓷的双极场致应变曲线

Figure 7. Polarization hysteresis loops of (a) KN, (b) KN-Mn, (e) KNN, (f) KNN-Mn ceramics; bipolar piezoelectric strain curves of (c) KN, (d) KN-Mn, (g) KNN, (h) KNN-Mn ceramics.

DownLoad: Full-Size Img PowerPoint

表 1 KN, KN-Mn, KNN和KNN-Mn陶瓷的相对密度、压电性能和介电性能

Table 1. Relative density, piezoelectric and dielectric properties of KN, KN-Mn, KNN, and KNN-Mn ceramics.

d₃₃/pC·N^–1 Relative density/% k_p Q_m θ_max/(°) tanδ ε_r (1 kHz)

KN 90 92.0 0.26 177 66 0.042 576
KN-Mn 83 95.1 0.27 185 77 0.015 526
KNN 115 94.9 0.29 85 64 0.060 393
KNN-Mn 109 94.3 0.32 330 83 0.024 355

DownLoad: CSV

[1]	Wang K, Malič B, Wu J 2018 MRS Bull. 43 607 Google Scholar
[2]	Thong H C, Zhao C, Zhou Z, Wu C F, Liu Y X, Du Z Z, Li J F, Gong W, Wang K 2019 Mater. Today 29 37 Google Scholar
[3]	吴金根, 高翔宇, 陈建国, 王春明, 张树君, 董蜀湘 2018 物理学报 67 207701 Google Scholar Wu J G, Gao X Y, Chen J G, Wang C M, Zhang S J, Dong S X 2018 Acta Phys. Sin. 67 207701 Google Scholar
[4]	刘涛, 丁爱丽, 何夕云, 郑鑫森, 仇萍荪, 程文秀 2007 无机材料学报 22 469 Google Scholar Liu T, Ding A L, He X Y, Zheng X S, Qiu P S, Cheng W X 2007 J. Inorg. Mater. 22 469 Google Scholar
[5]	Saito Y, Takao H, Tani T, Nonoyama T, Takatori K, Homma T, Nagaya T, Nakamura M 2004 Nature 432 84 Google Scholar
[6]	Koruza J, Bell A J, Frömling T, Webber K G, Wang K, Rödel J 2018 J. Materiomics 4 13 Google Scholar
[7]	Liu Q, Zhang Y, Gao J, Zhou Z, Yang D, Lee K Y, Studer A, Hinterstein M, Wang K, Zhang X, Li L, Li J F 2020 Natl. Sci. Rev. 7 355 Google Scholar
[8]	Zhang J, Pan Z, Guo F F, Liu W C, Ning H, Chen Y B, Lu M H, Yang B, Chen J, Zhang S T, Xing X, Rödel J, Cao W, Chen Y F 2015 Nat. Commun. 6 1 Google Scholar
[9]	Wang Y, Luo C, Wang S, Chen C, Yuan G, Luo H, Viehland D 2020 Adv. Electron. Mater. 6 1900949 Google Scholar
[10]	Wu J, Xiao D, Zhu J 2015 Chem. Rev. 115 2559 Google Scholar
[11]	Mgbemere H E, Herber R P, Schneider G A 2009 J. Eur. Ceram. Soc. 29 1729 Google Scholar
[12]	Cheng X, Wu J, Lou X, Wang X, Wang X, Xiao D, Zhu J 2014 ACS Appl. Mater. Inter. 6 750 Google Scholar
[13]	Hao J, Li W, Zhai J, Chen H 2019 Mat. Sci. Eng. R 135 1 Google Scholar
[14]	Wang K, Yao F Z, Jo W, Gobeljic D, Shvartsman V V, Lupascu D C, Li J F, Rödel J 2013 Adv. Funct. Mater. 23 4079 Google Scholar
[15]	Yao F Z, Wang K, Jo W, Webber K G, Comyn T P, Ding J X, Xu B, Cheng L Q, Zheng M P, Hou Y D, Li J F 2016 Adv. Funct. Mater. 26 1217 Google Scholar
[16]	Zheng T, Wu J, Xiao D, Zhu J 2018 Prog. Mater. Sci. 98 552 Google Scholar
[17]	Tao H, Wu H, Liu Y, Zhang Y, Wu J, Li F, Lü X, Zhao C, Xiao D, Zhu J, Pennycook S J 2019 J. Am. Chem. Soc. 141 13987 Google Scholar
[18]	Zhang M H, Wang K, Du Y J, Dai G, Sun W, Li G, Hu D, Thong H C, Zhao C, Xi X Q, Yue Z X, Li J F 2017 J. Am. Chem. Soc. 139 3889 Google Scholar
[19]	王轲, 沈宗洋, 张波萍, 李敬锋 2014 无机材料学报 29 13 Google Scholar Wang K, Shen Z Y, Zhang B P, Li J F 2014 J. Inorg. Mater. 29 13 Google Scholar
[20]	Hollenstein E, Davis M, Damjanovic D, Setter N 2005 Appl. Phys. Lett. 87 182905 Google Scholar
[21]	Birol H, Damjanovic D, Setter N 2005 J. Am. Ceram. Soc. 88 1754 Google Scholar
[22]	Kim D H, Joung M R, Seo I T, Hur J, Kim J H, Kim B Y, Lee H J, Nahm S 2014 J. Eur. Ceram. Soc. 34 4193 Google Scholar
[23]	Du H, Li Z, Tang F, Qu S, Pei Z, Zhou W 2006 Mat. Sci. Eng. B 131 83 Google Scholar
[24]	Lin D, Kwok K W, Chan H L W 2008 J. Alloys Compd. 461 273 Google Scholar
[25]	Wu L, Zhang J L, Wang C L, Li J C 2008 J. Appl. Phys. 103 084116 Google Scholar
[26]	Standards Committee of the IEEE Ultrasonics, Ferroelectrics, and Frequency Control Society 1988 IEEE Standard on Piezoelectricity (New York: IEEE) ANSI/IEEE Std. 176-1987
[27]	Thong H C, Xu Z, Zhao C, Lou L Y, Chen S, Zuo S Q, Li J F, Wang K 2019 J. Am. Ceram. Soc. 102 836 Google Scholar
[28]	Camargo J, Espinosa P A, Zabotto F, Ramajo L, Castro M 2020 J. Alloys Compd. 826 154129 Google Scholar
[29]	李睿 2015 物理学报 64 167303 Google Scholar Li R 2015 Acta Phys. Sin. 64 167303 Google Scholar
[30]	贺连星, 李承恩 2000 无机材料学报 15 293 Google Scholar He L X, Li C E 2000 J. Inorg. Mater. 15 293 Google Scholar
[31]	Kamiya T, Suzuki T, Tsurumi T, Daimon M 1992 Jpn. J. Appl. Phys. 31 3058 Google Scholar
[32]	Yao F Z, Zhang M H, Wang K, Zhou J J, Chen F, Xu B, Li F, Shen Y, Zhang Q H, Gu L, Zhang X W, Li J F 2018 ACS Appl. Mater. Inter. 10 37298 Google Scholar
[33]	Cheng L Q, Wang K, Yu Q, Li J F 2014 J. Mater. Chem. C 2 1519 Google Scholar
[34]	Shen Z X, Hu Z P, Chong T C, Beh C Y, Tang S H, Kuok M H 1995 Phys. Rev. B 52 3976
[35]	Sundarakannan B, Kakimoto K, Ohsato H 2004 Ferroelectrics 302 175 Google Scholar
[36]	路朋献, 许德合, 马秋花, 王改民, 侯永改, 周文俊, 栗政新 2007 红外与毫米波学报 26 69 Google Scholar Lu P X, Xu D H, Ma Q H, Wang G M, Hou Y G, Zhou W J, Li Z X 2007 J. Infrared Millm. W. 26 69 Google Scholar
[37]	Wang Z, Gu H, Hu Y, Yang K, Hu M, Zhou D, Guan J 2010 Cryst. Eng. Comm. 12 3157 Google Scholar
[38]	Li J F, Wang K, Zhu F Y, Cheng L Q, Yao F Z 2013 J. Am. Ceram. Soc. 96 3677 Google Scholar
[39]	刘霄, 徐小敏, 杜慧玲 2018 无机材料学报 33 683 Google Scholar Liu X, Xu X M, Du H L 2018 J. Inorg. Mater. 33 683 Google Scholar
[40]	Lee D, Jeon B C, Baek S H, Yang J S, Kim T H, Kim Y S, Yoon J G, Eom C B, Noh T W 2012 Adv. Mater. 24 6490 Google Scholar
[41]	Ren X 2004 Nat. Mater. 3 91 Google Scholar
[42]	Feng Z, Ren X 2007 Appl. Phys. Lett. 91 032904 Google Scholar
[43]	Voas B K, Usher T M, Liu X, Li S, Jones J L, Tan X, Cooper V R, Beckman S P 2014 Phys. Rev. B 90 024105 Google Scholar
[44]	Steiner S, Seo I T, Ren P, Li M, Keeble D J, Frömling T 2019 J. Am. Ceram. Soc. 102 5295 Google Scholar
[45]	Herber R P, Schneider G A, Wagner S, Hoffmann M J 2007 Appl. Phys. Lett. 90 252905 Google Scholar
[46]	Nakamura K, Tokiwa T, Kawamura Y 2002 J. Appl. Phys. 91 9272 Google Scholar
[47]	Qin Y, Zhang J, Yao W, Wang C, Zhang S 2015 J. Am. Ceram. Soc. 98 1027 Google Scholar

[1]	Wei Xiao-Wei, Tao Hong, Zhao Chun-Lin, Wu Jia-Gang. Piezoelectric and electrocaloric properties of high performance potassium sodium niobate-based lead-free ceramics. Acta Physica Sinica, 2020, 69(21): 217705. doi: 10.7498/aps.69.20200540
[2]	Liu Yong, Xu Zhi-Jun, Fan Li-Qun, Yi Wen-Tao, Yan Chun-Yan, Ma Jie, Wang Kun-Peng. Preparation and properties of multi-effect potassium sodium niobate based transparent ferroelectric ceramics. Acta Physica Sinica, 2020, 69(24): 247702. doi: 10.7498/aps.69.20201317
[3]	Xing Jie, Tan Zhi, Zheng Ting, Wu Jia-Gang, Xiao Ding-Quan, Zhu Jian-Guo. Research progress of high piezoelectric activity of potassium sodium niobate based lead-free ceramics. Acta Physica Sinica, 2020, 69(12): 127707. doi: 10.7498/aps.69.20200288
[4]	Lin Jia-Qi, Li Xiao-Kang, Yang Wen-Long, Sun Hong-Guo, Xie Zhi-Bin, Xiu Han-jiang, Lei Qing-Quan. Molecular dynamics simulation study on the structure and mechanical properties of polyimide/KTa0.5Nb0.5O3 nanoparticle composites. Acta Physica Sinica, 2015, 64(12): 126202. doi: 10.7498/aps.64.126202
[5]	Liu Shi-Yu, Yu Da-Shu, Lü Yue-Kai, Li De-Jun, Cao Mao-Sheng. First-principles study of structural stability and electronic properties of tetragonal and orthorhombic as well as monoclinic K0.5Na0.5NbO3. Acta Physica Sinica, 2013, 62(17): 177102. doi: 10.7498/aps.62.177102
[6]	Wang Bin-Ke, Tian Xiao-Xia, Xu Zhuo, Qu Shao-Bo, Li Zhen-Rong. Preparation and performances of KNN-based lead-free transparent ceramics. Acta Physica Sinica, 2012, 61(19): 197703. doi: 10.7498/aps.61.197703
[7]	Zhao Jing-Bo, Du Hong-Liang, Qu Shao-Bo, Zhang Hong-Mei, Xu Zhuo. Effects of A-site equivalence and non-equivalence substitution on polarization properties of K0.5Na0.5NbO3 lead-free piezoelectric ceramics. Acta Physica Sinica, 2011, 60(10): 107701. doi: 10.7498/aps.60.107701
[8]	Ding Nan, Tang Xin-Gui, Kuang Shu-Juan, Wu Jun-Bo, Liu Qiu-Xiang, He Qin-Yu. Effect of MnO2 additive on the piezoelectric and dielectric properties of Ba(Zr, Ti)O3 ceramics. Acta Physica Sinica, 2010, 59(9): 6613-6619. doi: 10.7498/aps.59.6613
[9]	Ming Bao-Quan, Wang Jin-Feng, Zang Guo-Zhong, Wang Chun-Ming, Gai Zhi-Gang, Du Juan, Zheng Li-Mei. X-ray diffraction and phase transition analysis for (K, Na)NbO3-based lead-free piezoelectric ceramics. Acta Physica Sinica, 2008, 57(9): 5962-5967. doi: 10.7498/aps.57.5962
[10]	Kang Xiang-Zhe, Ye Hui. Electro-optic properties of potassium sodium strontium barium niobate ferroelectric thin films. Acta Physica Sinica, 2006, 55(9): 4928-4933. doi: 10.7498/aps.55.4928
[11]	Zhang Li-Na, Zhao Su-Chuan, Zheng Liao-Ying, Li Guo-Rong, Yin Qing-Rui. Microstructure, dielectric and piezoelectric properties of mixed-layered Bi7Ti4NbO21 ferroelectric ceramics. Acta Physica Sinica, 2005, 54(5): 2346-2351. doi: 10.7498/aps.54.2346
[12]	Cao Xiao-Yan, Ye Hui, Deng Nian-Hui, Guo Bing, Gu Pei-Fu. Growth of highly c-axis oriented K:SBN thin films on Si(100) by the sol-gel method. Acta Physica Sinica, 2004, 53(7): 2363-2367. doi: 10.7498/aps.53.2363
[13]	Yu Tian-yan, Yu Bing-kun, Wang Qi, Wan You-bao, Pan Shou-kui. . Acta Physica Sinica, 2000, 49(3): 463-467. doi: 10.7498/aps.49.463
[14]	BIAN SHAO-PING, ZHANG JING-WEN, XU KE-BIN, JIANG QUAN-ZHONG, CHEN HUAN-CHU, SUN DA-LIANG. ANISOTROPIC DIFFRACTION IN DOPED KNSBN PHOTOREFRACTIVE CRYSTAL. Acta Physica Sinica, 1993, 42(4): 681-689. doi: 10.7498/aps.42.681
[15]	SHE WEI-LONG, LI QING-XING, YU ZHEN-XIN, GAO ZHAO-LAN, ZHANG QING-LUN, CHEN HUAN-CHU. OPTICAL DIODE EFFECT INDUCED BY USING TWO LASER BEAMS IN Mn DOPED KNSBN CRYSTAL. Acta Physica Sinica, 1992, 41(2): 342-346. doi: 10.7498/aps.41.342
[16]	ZHU DE-RUI, WANG REN, TAN JIAN-HUA, MO DANG. A STUDY ON THE GAIN COEFFICIENT OF TWO WAVE COUPLING IN DOPED KNSBN CRYSTALS. Acta Physica Sinica, 1992, 41(9): 1440-1447. doi: 10.7498/aps.41.1440
[17]	XU XIU-YING, ZHANG XING-KUI, XU ZI-RAN. IN SITU OBSERVATION OF FERRO-ELASTIC TRANSITION IN BNN CRYSTAL. Acta Physica Sinica, 1990, 39(10): 1614-1618. doi: 10.7498/aps.39.1614
[18]	FENG XI-QI, YING JI-EENG, WANG JIN-CHANG, LIU JIAN-CHENG. THE OH ABSORPTION SPECTRUM As A PROBE FOR DEFECT STRUCTURE OF LiNbO3 CRYSTAL. Acta Physica Sinica, 1988, 37(12): 2062-2067. doi: 10.7498/aps.37.2062
[19]	HU MEI-SHENG, FENG DUAN. IN SITU TEM STUDIES OF FERROELECTRIC PHASE TRANSITIONS IN Ba2NaNb5O15 AND LiTaO3. Acta Physica Sinica, 1982, 31(6): 815-819. doi: 10.7498/aps.31.815
[20]	NIOBATES RESEARCH GROUP. SINGLE CRYSTAL GROWTH OF STRONTIUM SODIUM LITHIUM NIOBATE. Acta Physica Sinica, 1979, 28(2): 229-233. doi: 10.7498/aps.28.229

Catalog

Vol. 69, Issue 12 - 2020-06-20

Metrics

Abstract views: 12976
PDF Downloads: 678
Cited By: 0

姓名
邮箱
手机号码
标题
留言内容
验证码

Search

Article

留言板

Effect of manganese doping on ferroelectric and piezoelectric properties of KNbO₃ and (K_0.5Na_0.5)NbO₃ lead-free ceramics