Control of surface structures and functionalities in perovskite-type ferroelectric oxides and their potential applications

Pei Ming-Hui; Tian Yu; Zhang Jin-Xing

doi:10.7498/aps.69.20200884

Abstract

Over the past decades, exploration and artificial control of the surface and interfacial structure of the materials have played an important role in chemical catalyzing, energy conversion, information storage and medical field, and thus the finding of suitable materials with controllable surface/interface properties has attracted intense interest in recent years. Perovskite-type ferroelectric oxides are considered to be one of the most promising functional materials due to their intrinsic, non-volatile, reversible spontaneous polarization and controllable polar surface with high charge density. The investigating of the interaction between polarization and surface structure of perovskite-type ferroelectric oxide is very important for understanding the surface (interface) energy conversion, regulating the adsorption and desorption on the surface, controlling interfacial chemical reaction, and designing stable low-power electronic devices. In this paper, we summarize the theoretical mechanism and potential applications of the surface structures and functionality in perovskite-type ferroelectric oxide from three aspects. Firstly, we describe the inseparable relationship between the stabilized ferroelectric phase and surface structure of ferroelectric material, and illustrate the formation mechanism of complex surface structure of perovskite-type ferroelectric oxide. In order to reduce the surface energy to stabilize the polar surface of the material, perovskite-type ferroelectric oxide always needs to absorb foreign charged particles, change the stoichiometry and conduct electron orbital hybridization or surface relaxation, etc., which will cause the complexity of the surface structure of ferroelectric. Secondly, we outline the influence of ferroelectric polarization on the surface structure of ferroelectric and the behavior of changing ferroelectric polarization by controlling surface structure through adjusting the external environment, which provides an important basis for the subsequent regulation of the surface performance and functionality of perovskite-type ferroelectric oxide. Finally, we introduce the utilization of the controllable physical and chemical properties of ferroelectric surface (interface) into large area and into nanoscale (nanodomain), which has bright application prospects in many frontier fields, including non-volatile memory system, cell proliferation, microfluidic control system, catalysis, optical device and photodetector and so on. Furthermore, considering the limitations of current scientific research about the ferroelectric surface, we put forward the prospects for the future development of the ferroelectric material in the areas of information storage, controllable chemical reactions and new energy conversion.

Keywords:

Authors and contacts

1.
Department of Physics, Beijing Normal University, Beijing 100875, China
2.
School of Basic Medical Sciences, Air Force Medical University, Xi’an 710032, China

Corresponding author: Tian Yu, yutian@mail.bnu.edu.cn ; Zhang Jin-Xing, jxzhang@bnu.edu.cn

Funds: Project supported by the National Natural Science Foundation of China (Grant No. 11974052) and the Natural Science Foundation of Beijing, China (Grant No. Z190008)

FullText HTML : translate this paragraph

References

[1]	Valasek J 1920 Phys. Rev. 17 475 Google Scholar
[2]	Setter N, Damjanovic D, Eng L, Fox G, Gevorgian S, Hong S, Kingon A, Kohlstedt H, Park N Y, Stephenson G B, Stolitchnov I, Taganstev A K, Taylor D V, Yamada T, Streiffer S 2006 J. Appl. Phys. 100 051606 Google Scholar
[3]	Auciello O, Scott J F, Ramesh R 1998 Phys. Today 51 22 Google Scholar
[4]	Dawber M, Rabe K M, Scott J F 2005 Rev. Mod. Phys. 77 1083 Google Scholar
[5]	Li Y J, Wang J J, Ye J C, et al. 2015 Adv. Funct. Mater. 25 3405 Google Scholar
[6]	Ishiwata S, Taguchi Y, Murakawa H, Onose Y, Tokura Y 2008 Science 319 1643 Google Scholar
[7]	Li D, Zhao M H, Garra J, Kolpak A M, Rappe A M, Bonnell D A, Vohs J M 2008 Nat. Mater. 7 473 Google Scholar
[8]	Song J, Kim T L, Lee J, et al. 2018 Nano Res. 11 642 Google Scholar
[9]	Grilli S, Coppola S, Nasti G, Vespini V, Gentile G, Ambrogi V, Carfagna C, Ferraro P 2014 Rsc Adv. 4 2851 Google Scholar
[10]	Liu Y, Zhang X, Cao C, et al. 2017 Adv. Funct. Mater. 27 1703771 Google Scholar
[11]	Kakekhani A, Ismail-Beigi S 2015 ACS Catal. 5 4537 Google Scholar
[12]	Guo J, Liu Y, Lin Y, Tian Y, Zhang J, Gong T, Cheng T, Huang W, Zhang X 2019 Nanoscale 11 20868 Google Scholar
[13]	Goniakowski J, Finocchi F, Noguera C 2007 Reps. Prog. Phys. 71 016501 Google Scholar
[14]	Damjanovic D 1998 Reps. Prog. Phys. 61 1267 Google Scholar
[15]	Noguera C 2000 J. Phys.: Condens. Matter 12 R367 Google Scholar
[16]	Garrity K, Kakekhani A, Kolpak A, Ismail-Beigi S 2013 Phys. Rev. B 88 045401 Google Scholar
[17]	Spanier J E, Kolpak A M, Urban J J, Grinberg I, Ouyang L, Yun W S, Rappe A M, Park H 2006 Nano Lett. 6 735 Google Scholar
[18]	Jia C L, Urban K 2004 Science 303 2001 Google Scholar
[19]	Ebensperger C, Meyer B 2011 Phys. Status Solidi B 248 2229 Google Scholar
[20]	Munkholm A, Streiffer S K, Ramana Murty M V, et al. 2002 Phys. Rev. Lett. 88 016101 Google Scholar
[21]	Kakekhani A, Ismail-Beigi S, Altman E I 2016 Surf. Sci. 650 302 Google Scholar
[22]	Kalinin S V, Johnson C Y, Bonnell D A 2002 J. Appl. Phys. 91 3816 Google Scholar
[23]	Apostol N G, Stoflea L E, Lungu G A, Tache C A, Popescu D G, Pintilie L, Teodorescu C M 2013 Mater. Sci. Eng. B 178 1317 Google Scholar
[24]	Fong D D, Kolpak A M, Eastman J A, et al. 2006 Phys. Rev. Lett. 96 127601 Google Scholar
[25]	Gao P, Liu H J, Huang Y L, et al. 2016 Nat. Commun. 7 11318 Google Scholar
[26]	Tian Y, Wei L, Zhang Q, Huang H, Zhang Y, Zhou H, Ma F, Gu L, Meng S, Chen L Q, Nan C W, Zhang J 2018 Nat. Commun. 9 3809 Google Scholar
[27]	Kalinin S V, Bonnell D A 2001 Phys. Rev. B 63 125411 Google Scholar
[28]	Ying X, Haitao Y 2014 Chem. Res. Chin. Univ. 30 794 Google Scholar
[29]	Zhu L, Yao K L, Liu Z L, Zhang D H 2009 Phys. Lett. A 373 2374 Google Scholar
[30]	Song C, Gao J, Liu J, Yang Y, Tian C, Hong J, Weng H, Zhang J 2020 ACS Appl. Mater. Interfaces 12 4150 Google Scholar
[31]	Dai J Q, Xu J W, Zhu J H 2017 Appl. Surf. Sci. 392 135 Google Scholar
[32]	Yun Y, Kampschulte L, Li M, Liao D, Altman E I 2007 J. Phys. Chem. C 111 13951 Google Scholar
[33]	Yun Y, Altman E I 2007 J. Am. Chem. Soc. 129 15684 Google Scholar
[34]	Kolpak A M, Grinberg I, Rappe A M 2007 Phys. Rev. Lett. 98 166101 Google Scholar
[35]	Ferris R, Yellen B, Zauscher S 2012 Small 8 28 Google Scholar
[36]	Israelachvili J N 2011 Intermolecular and Surface Forces (San Diego: Academic Press) pp293–294
[37]	Ferris R J, Lin S, Therezien M, Yellen B B, Zauscher S 2013 ACS Appl. Mater. Interfaces 5 2610 Google Scholar
[38]	Nishino R, Kozuka Y, Kagawa F, Uchida M, Kawasaki M 2018 Appl. Phys. Lett. 113 143501 Google Scholar
[39]	Shin J, Nascimento V B, Geneste G, Rundgren J, Plummer E W, Dkhil B, Kalinin S V, Baddorf A P 2009 Nano Lett. 9 3720 Google Scholar
[40]	Wang R V, Fong D D, Jiang F, et al. 2009 Phys. Rev. Lett. 102 047601 Google Scholar
[41]	Jiang B, Bai Y, Chu W Y, Shi S Q, Qiao L J, Su Y J 2008 Appl. Surf. Sci. 254 5594 Google Scholar
[42]	Sun X, Su Y J, Li X, Gao K W, Qiao L J 2012 J. Appl. Phys. 111 094110 Google Scholar
[43]	Li X, Bai Y, Wang B C, Su Y J 2015 J. Appl. Phys. 118 094104 Google Scholar
[44]	Lee H, Kim T H, Patzner J, Lu H, Lee J, Zhou H, Chang W, Mahanthappa M, Tsymbal E Y, Gruverman A, Eom C B 2016 Nano Lett. 16 2400 Google Scholar
[45]	Du H, Lin X, Xu Z, Chu D 2015 J. Mater. Sci. 50 5641 Google Scholar
[46]	Ito M, Matsubara Y, Kozuka Y, et al. 2014 Appl. Phys. Lett. 104 222101 Google Scholar
[47]	Reiss B D, Bai G R, Auciello O, Ocola L E, Firestone M A 2006 Appl. Phys. Lett. 88 083903 Google Scholar
[48]	Hong J, Kim B S, Char K, Hammond P T 2011 Biomacromolecules 12 2975 Google Scholar
[49]	Yu Y, Wang X 2018 Adv. Mater. 30 1800154 Google Scholar
[50]	Chen F, Huang H, Guo L, Zhang Y, Ma T 2019 Angew. Chem. Int. Ed. 58 10061 Google Scholar
[51]	Cui Y, Briscoe J, Dunn S 2013 Chem. Mater. 25 4215 Google Scholar
[52]	Giocondi J L, Rohrer G S 2001 J. Phys. Chem. B 105 8275 Google Scholar
[53]	Bhardwaj A, Burbure N V, Gamalski A, Rohrer G S 2010 Chem. Mater. 22 3527 Google Scholar
[54]	Tan C, Wang J, Zhong X, Jiang J, Zhang X, Ding Y 2017 Mater. Des. 129 186 Google Scholar
[55]	Jones P M, Dunn S 2007 Nanotechnology 18 185702 Google Scholar
[56]	Sun Y, Nemanich R J 2011 J. Appl. Phys. 109 104302 Google Scholar
[57]	Ullah R, Pei M, Wu J, et al. 2020 ACS Appl. Energy Mater. 3 4149 Google Scholar
[58]	Wang X, Yang D, Zhang H M, Song C, Wang J, Tan G, Zheng R, Dong S, Cheong S W, Zhang J 2019 Phys. Rev. B 99 054106 Google Scholar
[59]	Medford A J, Vojvodic A, Hummelshøj J S, Voss J, Abild-Pedersen F, Studt F, Bligaard T, Nilsson A, Nørskov J K 2015 J. Catal. 328 36 Google Scholar
[60]	Ostrovskii I V, Nadtochiy A B 2005 Appl. Phys. Lett. 86 222902 Google Scholar
[61]	Kalinin S V, Bonnell D A, Alvarez T, Lei X, Hu Z, Shao R, Ferris J H 2004 Adv. Mater. 16 795 Google Scholar
[62]	Christophis C, Cavalcanti-Adam E A, Hanke M, et al. 2013 Biointerphases 8 27 Google Scholar
[63]	Li D, Bonnell D A 2008 Annu. Rev. Mater. Res. 38 351 Google Scholar
[64]	Chen X, Karpinski P, Shvedov V, et al. 2015 Appl. Phys. Lett. 107 141102 Google Scholar
[65]	Shur V Y, Lobov A I, Shur A G, et al. 2005 Appl. Phys. Lett. 87 022905 Google Scholar

Cited By

图 1 利用钙钛矿型铁电氧化物独特表面性质的相关应用, E代表电场, P代表极化

Figure 1. Related applications utilizing the unique surface properties of perovskite-type ferroelectric oxides, E represents electric field, P represents polarization.

DownLoad: Full-Size Img PowerPoint

图 2 (a) 束缚电荷引起的退极化场, E代表电场, P代表极化^[21]; (b) 极化向外导致铁电体表面处能带向下弯曲; (c) 极化向内导致铁电体表面处能带向上弯曲, E_CBM代表导带底的能量, E_VBM代表价带顶的能量, E_F代表费米能^[23]; PZT薄膜的正极性表面(d)、负极性表面(e)和面内畴区域(f)的阳离子和阴离子之间的位移图^[25]; (g) BWO (113)表面原子分辨率的STM图; (h) BWO薄膜从体态表面到边缘态的dI/dV曲线的演变^[30]

Figure 2. (a) Depolarization field caused by bound charge, E represents electric field, P represents polarization^[21]; (b) the downward band bend at an ideal ferroelectric surface with outward (↑) polarization; (c) the upward band bend at an ideal ferroelectric surface with inward (↓) polarization, E_CBM represents the energy of the conduction band minimum, E_VBM the energy of the valence band maximum, E_F Fermi energy^[23]; vector maps of the displacement between the cation and anion columns of positively poled surface (d), negatively poled surface (e) and the domain with the in-plane polarization (f) about PZT thin films^[25]; (g) atomic resolution STM image of BWO (113) surface; (h) evolution of dI/dV curves of BWO thin film when approaching from the terrace to the edge^[30].

DownLoad: Full-Size Img PowerPoint

图 3 (a) LNO的正极性和负极性表面对异丙醇脱附的数据比较^[32]; (b) LNO的正极性和负极性表面对乙酸、异丙醇和十二烷脱附的β/T_P²-T_P图^[33]; (c) 电解质溶液中极化向内的铁电薄膜上方的双电层结构和对应电势的示意图; (d) 带负电荷的探针与极化向内或向外的铁电薄膜之间的双电层结构和相互作用力^[37]; 极化向外(e) 和向内(f) 的BFO表面分别吸附 H⁺ (e) 和 OH^– (f) 后极化翻转的示意图^[26]

Figure 3. (a) Comparison of 2-propanol desorption from positively and negatively poled LNO^[32]; (b) plots of β/T_P² versus T_P for desorption of acetic acid, 2-propanol and dodecane from positively and negatively poled LNO^[33]; (c) schematic of the electric double layer structure above an inward-polarized ferroelectric thin film in an electrolyte solution and a corresponding sketch of the potential; (d) the electric double layer structure and interaction force between a negatively charged probe and a ferroelectric thin film with inward or outward polarization^[37]; schematic diagrams show BFO polarizations are switched from outward/inward to inward/outward after surfaces adsorbed H⁺ (e) or OH^– (f), respectively^[26].

DownLoad: Full-Size Img PowerPoint

图 4 (a) 钙钛矿型铁电氧化物与液体界面形成离子梯度^[35]; (b) 双电层晶体管示意图^[46]; 示意图展示了钙钛矿型铁电氧化物表面电荷诱导的pH梯度(c)、极性大分子的高度变化(d), 以及利用铁电材料的表面电场控制溶液中带电粒子的流动方向(e) ^[35]; (f) 带正电的纳米膜植入体表面与带负电的内源性骨缺损壁之间形成内建电场^[10]

Figure 4. (a) Ionic gradient is formed in the interface between perovskite-type ferroelectric oxides and liquid^[35]; (b) a schematic of the electric double-layer transistor^[46]; schematic diagrams show pH gradients (c) and macromolecular height change (d) are induced by surface charges of perovskite-type ferroelectric oxides; and (e) the flow direction of charged particles in solution is controlled by the surface electric field of ferroelectric materials^[35]; (f) a built-in electric field is formed between the electropositive nanofilm implant surface and electronegative endogenous bone defect wall^[10].

DownLoad: Full-Size Img PowerPoint

图 5 极化向外(a)或极化向内(b)的BTO与Ag⁺还原电位、Pb²⁺氧化电位的能带结构图, E_V代表价带顶的能量, E_C代表导带底的能量, E_F代表费米能, P代表极化^[53]; (c)和(d) 分别展示了BWO(001)中带不同电荷畴壁的水分解示意图^[57]; (e) 计算模拟通过动态翻转PTO的铁电极化可以实现将一氧化氮合成为氮气和氧气的过程示意图; (f) 铁电极化调控分子与表面相互作用的示意图^[11]

Figure 5. Energy band structure of BTO with outward (a) or inward (b) polarization and Ag⁺ reduction potential, Pb²⁺ oxidation potential, respectively, E_V is the valence band edge, E_C the conduction band edge, E_F the Fermi level, P polarization^[53]; (c) and (d) show the schematics of water splitting mechanism of different charged domain walls in BWO (001), respectively^[57]; (e) simulation shows the decomposition process of nitric oxide into nitrogen and oxygen can be realized by dynamically switching ferroelectric polarization of PTO; (f) schematic of molecule-surface interaction controlled by ferroelectric polarization^[11].

DownLoad: Full-Size Img PowerPoint

图 6 (a) 基于铁电畴调谐的石墨烯等离子体光电探测器的自驱动微型光谱仪的吸收特性, 目标光谱范围从5—20 μm^[12]; (b) 扫描探针显微镜观察到的具有周期性畴结构的PZT薄膜上的Ag光沉积^[61]; (c) BFO薄膜暴露在酸性溶液(pH = 3)后的铁电极化翻转为向内, 暴露在纯水溶液后极化翻转为向外; (d) 将BFO暴露在不同pH值的水溶液中, 印刷和消除铁电极化的原理图^[26]

Figure 6. (a) The absorption characteristics of a self-driven micro-spectrometer based on the graphene plasmonic photodetector tuned by ferroelectric domains, the target spectrum ranges from 5 to 20 μm^[12]; (b) Ag photodeposition on the PZT thin film with periodic domain structure observed by scanning probe microscopy^[61]; (c) the ferroelectric polarization of BFO thin film is switched to inward after being exposed to acidic solution (pH = 3) and then outward after being exposed to Milli-Q water; (d) the schematic of printing and erasing the ferroelectric polarization by exposing the BFO to aqueous solution with different pH value^[26].

DownLoad: Full-Size Img PowerPoint

[1]	Valasek J 1920 Phys. Rev. 17 475 Google Scholar
[2]	Setter N, Damjanovic D, Eng L, Fox G, Gevorgian S, Hong S, Kingon A, Kohlstedt H, Park N Y, Stephenson G B, Stolitchnov I, Taganstev A K, Taylor D V, Yamada T, Streiffer S 2006 J. Appl. Phys. 100 051606 Google Scholar
[3]	Auciello O, Scott J F, Ramesh R 1998 Phys. Today 51 22 Google Scholar
[4]	Dawber M, Rabe K M, Scott J F 2005 Rev. Mod. Phys. 77 1083 Google Scholar
[5]	Li Y J, Wang J J, Ye J C, et al. 2015 Adv. Funct. Mater. 25 3405 Google Scholar
[6]	Ishiwata S, Taguchi Y, Murakawa H, Onose Y, Tokura Y 2008 Science 319 1643 Google Scholar
[7]	Li D, Zhao M H, Garra J, Kolpak A M, Rappe A M, Bonnell D A, Vohs J M 2008 Nat. Mater. 7 473 Google Scholar
[8]	Song J, Kim T L, Lee J, et al. 2018 Nano Res. 11 642 Google Scholar
[9]	Grilli S, Coppola S, Nasti G, Vespini V, Gentile G, Ambrogi V, Carfagna C, Ferraro P 2014 Rsc Adv. 4 2851 Google Scholar
[10]	Liu Y, Zhang X, Cao C, et al. 2017 Adv. Funct. Mater. 27 1703771 Google Scholar
[11]	Kakekhani A, Ismail-Beigi S 2015 ACS Catal. 5 4537 Google Scholar
[12]	Guo J, Liu Y, Lin Y, Tian Y, Zhang J, Gong T, Cheng T, Huang W, Zhang X 2019 Nanoscale 11 20868 Google Scholar
[13]	Goniakowski J, Finocchi F, Noguera C 2007 Reps. Prog. Phys. 71 016501 Google Scholar
[14]	Damjanovic D 1998 Reps. Prog. Phys. 61 1267 Google Scholar
[15]	Noguera C 2000 J. Phys.: Condens. Matter 12 R367 Google Scholar
[16]	Garrity K, Kakekhani A, Kolpak A, Ismail-Beigi S 2013 Phys. Rev. B 88 045401 Google Scholar
[17]	Spanier J E, Kolpak A M, Urban J J, Grinberg I, Ouyang L, Yun W S, Rappe A M, Park H 2006 Nano Lett. 6 735 Google Scholar
[18]	Jia C L, Urban K 2004 Science 303 2001 Google Scholar
[19]	Ebensperger C, Meyer B 2011 Phys. Status Solidi B 248 2229 Google Scholar
[20]	Munkholm A, Streiffer S K, Ramana Murty M V, et al. 2002 Phys. Rev. Lett. 88 016101 Google Scholar
[21]	Kakekhani A, Ismail-Beigi S, Altman E I 2016 Surf. Sci. 650 302 Google Scholar
[22]	Kalinin S V, Johnson C Y, Bonnell D A 2002 J. Appl. Phys. 91 3816 Google Scholar
[23]	Apostol N G, Stoflea L E, Lungu G A, Tache C A, Popescu D G, Pintilie L, Teodorescu C M 2013 Mater. Sci. Eng. B 178 1317 Google Scholar
[24]	Fong D D, Kolpak A M, Eastman J A, et al. 2006 Phys. Rev. Lett. 96 127601 Google Scholar
[25]	Gao P, Liu H J, Huang Y L, et al. 2016 Nat. Commun. 7 11318 Google Scholar
[26]	Tian Y, Wei L, Zhang Q, Huang H, Zhang Y, Zhou H, Ma F, Gu L, Meng S, Chen L Q, Nan C W, Zhang J 2018 Nat. Commun. 9 3809 Google Scholar
[27]	Kalinin S V, Bonnell D A 2001 Phys. Rev. B 63 125411 Google Scholar
[28]	Ying X, Haitao Y 2014 Chem. Res. Chin. Univ. 30 794 Google Scholar
[29]	Zhu L, Yao K L, Liu Z L, Zhang D H 2009 Phys. Lett. A 373 2374 Google Scholar
[30]	Song C, Gao J, Liu J, Yang Y, Tian C, Hong J, Weng H, Zhang J 2020 ACS Appl. Mater. Interfaces 12 4150 Google Scholar
[31]	Dai J Q, Xu J W, Zhu J H 2017 Appl. Surf. Sci. 392 135 Google Scholar
[32]	Yun Y, Kampschulte L, Li M, Liao D, Altman E I 2007 J. Phys. Chem. C 111 13951 Google Scholar
[33]	Yun Y, Altman E I 2007 J. Am. Chem. Soc. 129 15684 Google Scholar
[34]	Kolpak A M, Grinberg I, Rappe A M 2007 Phys. Rev. Lett. 98 166101 Google Scholar
[35]	Ferris R, Yellen B, Zauscher S 2012 Small 8 28 Google Scholar
[36]	Israelachvili J N 2011 Intermolecular and Surface Forces (San Diego: Academic Press) pp293–294
[37]	Ferris R J, Lin S, Therezien M, Yellen B B, Zauscher S 2013 ACS Appl. Mater. Interfaces 5 2610 Google Scholar
[38]	Nishino R, Kozuka Y, Kagawa F, Uchida M, Kawasaki M 2018 Appl. Phys. Lett. 113 143501 Google Scholar
[39]	Shin J, Nascimento V B, Geneste G, Rundgren J, Plummer E W, Dkhil B, Kalinin S V, Baddorf A P 2009 Nano Lett. 9 3720 Google Scholar
[40]	Wang R V, Fong D D, Jiang F, et al. 2009 Phys. Rev. Lett. 102 047601 Google Scholar
[41]	Jiang B, Bai Y, Chu W Y, Shi S Q, Qiao L J, Su Y J 2008 Appl. Surf. Sci. 254 5594 Google Scholar
[42]	Sun X, Su Y J, Li X, Gao K W, Qiao L J 2012 J. Appl. Phys. 111 094110 Google Scholar
[43]	Li X, Bai Y, Wang B C, Su Y J 2015 J. Appl. Phys. 118 094104 Google Scholar
[44]	Lee H, Kim T H, Patzner J, Lu H, Lee J, Zhou H, Chang W, Mahanthappa M, Tsymbal E Y, Gruverman A, Eom C B 2016 Nano Lett. 16 2400 Google Scholar
[45]	Du H, Lin X, Xu Z, Chu D 2015 J. Mater. Sci. 50 5641 Google Scholar
[46]	Ito M, Matsubara Y, Kozuka Y, et al. 2014 Appl. Phys. Lett. 104 222101 Google Scholar
[47]	Reiss B D, Bai G R, Auciello O, Ocola L E, Firestone M A 2006 Appl. Phys. Lett. 88 083903 Google Scholar
[48]	Hong J, Kim B S, Char K, Hammond P T 2011 Biomacromolecules 12 2975 Google Scholar
[49]	Yu Y, Wang X 2018 Adv. Mater. 30 1800154 Google Scholar
[50]	Chen F, Huang H, Guo L, Zhang Y, Ma T 2019 Angew. Chem. Int. Ed. 58 10061 Google Scholar
[51]	Cui Y, Briscoe J, Dunn S 2013 Chem. Mater. 25 4215 Google Scholar
[52]	Giocondi J L, Rohrer G S 2001 J. Phys. Chem. B 105 8275 Google Scholar
[53]	Bhardwaj A, Burbure N V, Gamalski A, Rohrer G S 2010 Chem. Mater. 22 3527 Google Scholar
[54]	Tan C, Wang J, Zhong X, Jiang J, Zhang X, Ding Y 2017 Mater. Des. 129 186 Google Scholar
[55]	Jones P M, Dunn S 2007 Nanotechnology 18 185702 Google Scholar
[56]	Sun Y, Nemanich R J 2011 J. Appl. Phys. 109 104302 Google Scholar
[57]	Ullah R, Pei M, Wu J, et al. 2020 ACS Appl. Energy Mater. 3 4149 Google Scholar
[58]	Wang X, Yang D, Zhang H M, Song C, Wang J, Tan G, Zheng R, Dong S, Cheong S W, Zhang J 2019 Phys. Rev. B 99 054106 Google Scholar
[59]	Medford A J, Vojvodic A, Hummelshøj J S, Voss J, Abild-Pedersen F, Studt F, Bligaard T, Nilsson A, Nørskov J K 2015 J. Catal. 328 36 Google Scholar
[60]	Ostrovskii I V, Nadtochiy A B 2005 Appl. Phys. Lett. 86 222902 Google Scholar
[61]	Kalinin S V, Bonnell D A, Alvarez T, Lei X, Hu Z, Shao R, Ferris J H 2004 Adv. Mater. 16 795 Google Scholar
[62]	Christophis C, Cavalcanti-Adam E A, Hanke M, et al. 2013 Biointerphases 8 27 Google Scholar
[63]	Li D, Bonnell D A 2008 Annu. Rev. Mater. Res. 38 351 Google Scholar
[64]	Chen X, Karpinski P, Shvedov V, et al. 2015 Appl. Phys. Lett. 107 141102 Google Scholar
[65]	Shur V Y, Lobov A I, Shur A G, et al. 2005 Appl. Phys. Lett. 87 022905 Google Scholar

[1]	Qi Kai, Zhu Xing-Guang, Wang Jun, Xia Guo-Dong. Heat transfer characteristics of solid-liquid interface on nanostructure surface under external electric field. Acta Physica Sinica, 2024, 73(15): 156801. doi: 10.7498/aps.73.20240698
[2]	Zheng Xu, Li Zhao, Gu Yue-Liang, Yin Shuai-Shuai, Jiang Ji-Chao, Guo Pu, Qiu Zhi-Yong, Li Xiao-Long. Surface structure of BaTiO₃ single crystal and the influence of pH value of liquid on its surface structure. Acta Physica Sinica, 2024, 73(10): 106101. doi: 10.7498/aps.73.20240084
[3]	Yuan Guo-Liang, Wang Chen-Hao, Tang Wen-Bin, Zhang Rui, Lu Xu-Bing. Structure, performance regulation and typical device applications of HfO₂-based ferroelectric films. Acta Physica Sinica, 2023, 72(9): 097703. doi: 10.7498/aps.72.20222221
[4]	Wang Yan-Bin, Liu Qian, Wang Yong, Dai Bo, Wei Xian-Hua. Effects of electrode materials and bias polarities on breakdown behaviors of oxide dielectrics and their mechanisms. Acta Physica Sinica, 2021, 70(8): 087302. doi: 10.7498/aps.70.20201262
[5]	Cui Zong-Yang, Xie Zhong-Shuai, Wang Yao-Jin, Yuan Guo-Liang, Liu Jun-Ming. Research progress and prospects of photocatalytic devices with perovskite ferroelectric semiconductors. Acta Physica Sinica, 2020, 69(12): 127706. doi: 10.7498/aps.69.20200287
[6]	Wu Mei-Xia, Li Man-Rong. Multiferroic properties of exotic double perovskite A2BB' O6. Acta Physica Sinica, 2018, 67(15): 157510. doi: 10.7498/aps.67.20180817
[7]	Zhao Guo-Dong, Yang Ya-Li, Ren Wei. Recent progress of improper ferroelectricity in perovskite oxides. Acta Physica Sinica, 2018, 67(15): 157504. doi: 10.7498/aps.67.20180936
[8]	Hu Ting, Kan Er-Jun. Research progress of low-dimensional ferroelectric materials. Acta Physica Sinica, 2018, 67(15): 157701. doi: 10.7498/aps.67.20180483
[9]	Wu Hua-Ping, Ling Huan, Zhang Zheng, Li Yan-Biao, Liang Li-Hua, Chai Guo-Zhong. Research progress on photocatalytic activity of ferroelectric materials. Acta Physica Sinica, 2017, 66(16): 167702. doi: 10.7498/aps.66.167702
[10]	Li Wen-Tao, Liang Yan, Wang Wei-Hua, Yang Fang, Guo Jian-Dong. Precise control of LaTiO3(110) film growth by molecular beam epitaxy and surface termination of the polar film. Acta Physica Sinica, 2015, 64(7): 078103. doi: 10.7498/aps.64.078103
[11]	Zheng Xiao-Qing, Yang Yang, Sun De-Yan. Atomistic characterization of a modeled binary ordered alloy solid-liquid interface. Acta Physica Sinica, 2013, 62(1): 017101. doi: 10.7498/aps.62.017101
[12]	Yi Ding, Qin Wei, Xie Shi-Jie. Investigation of polarons in perovskite manganites. Acta Physica Sinica, 2012, 61(20): 207101. doi: 10.7498/aps.61.207101
[13]	Guan Rong-Hua. The bistable state of a nematic liquid crystal cell with surface order-electricity polarization and flexoelectric polarization at saturation point. Acta Physica Sinica, 2011, 60(1): 016105. doi: 10.7498/aps.60.016105
[14]	Xiang Jun, Wang Xiao-Hui. Solid-state reaction synthesis and electrical properties of Sm0.9Sr0.1AlO3-δ perovskite oxide. Acta Physica Sinica, 2008, 57(7): 4417-4423. doi: 10.7498/aps.57.4417
[15]	Wang Fei-Peng, Xia Zhong-Fu, Qiu Xun-Lin, Shen Jun. Electrical polarization and charge dynamics of cellular polypropylene ferroelectret films. Acta Physica Sinica, 2006, 55(7): 3705-3710. doi: 10.7498/aps.55.3705
[16]	Ye Zhen-Cheng, Cai Jun, Zhang Shu-Ling, Liu Hong-Lai, Hu Ying. Studies on the density profiles of square-well chain fluid confined in a slit pore by density functional theory. Acta Physica Sinica, 2005, 54(9): 4044-4052. doi: 10.7498/aps.54.4044
[17]	JIANG YONG, LI GUANG, ZENG XIANG-YONG, YANG YING-PING, YUAN SONG-LIU, JIN SI-ZHAO. ELECTRONIC SPIN RESONANCE STUDY OF PEROVSKITE-TYPE MANGANITES. Acta Physica Sinica, 2000, 49(9): 1846-1851. doi: 10.7498/aps.49.1846
[18]	Yanag Guang-Liang, Xianyu Wen-Xu, Qian Zheng -Nan, Jin Han-Min. . Acta Physica Sinica, 2000, 49(3): 553-556. doi: 10.7498/aps.49.553
[19]	LIAN GUI-JUN, LI MEI-YA, KANG JIN-FENG, GUO JIAN-DONG, SUN YUN-FENG, XIONG GUANG-CHENG. EPITAXIAL GROWTH OF PEROVSKITE OXIDE THIN FILMS. Acta Physica Sinica, 1999, 48(10): 1917-1922. doi: 10.7498/aps.48.1917
[20]	PAN JIN-SHENG. THE SURFACE OR INTERFACE WEAK COUPLING POLARON IN POLAR CRYSTALS. Acta Physica Sinica, 1982, 31(3): 335-347. doi: 10.7498/aps.31.335

Catalog

Vol. 69, Issue 21 - 2020-11-05

Metrics

Abstract views: 13073
PDF Downloads: 527
Cited By: 0

姓名
邮箱
手机号码
标题
留言内容
验证码

Search

Article

留言板