Effects of organic molecule adsorption and substrate on electronic structure of germanene

Xiao Mei-Xia; Leng Hao; Song Hai-Yang; Wang Lei; Yao Ting-Zhen; He Cheng

doi:10.7498/aps.70.20201657

Abstract

The development potential of germanene-based integrated electronics originates from its high carrier mobility and compatibility with the existing silicon-based and germanium-based semiconductor industry. However, the small band gap energy band (Dirac point) of germanene greatly impedes its application. Thus, it is necessary to open a sizeable band gap without reducing the carrier mobility for the application in logic circuits. In this study, the effects of organic molecule (benzene or hexafluorobenzene) adsorption and substrate on the atomic structures and electronic properties of germanene under an external electric field are investigated by using density functional theory calculations with van der Waals correction. For benzene/germanene and hexafluorobenzene/germanene systems, four different adsorption sites are considered, with the center of the organic molecules lying directly atop the upper or lower Ge atoms of germanene, in the Ge-Ge bridge center, and on the central hollow ring. Meanwhile, different molecular orientations at each adsorption site are also considered. Thus, there are eight high-symmetry adsorption configurations of the systems, respectively. According to the adsorption energy, we can determine the most stable atomic structures of the above systems. The results show that the organic molecule adsorption can induce the larger buckling height in germanene. Both the adsorption energy and interlayer distance indicate that there is no chemical bond between the organic molecules and germanene. Mulliken population analysis shows that a charge redistribution in the two sublattices in germanene exists since benzene is an electron donor molecule and hexafluorobenzene is an electron acceptor molecule. As a result, the benzene/germanene system exhibits a relatively large band gap (0.036 eV), while hexafluorobenzene/germanene system displays a small band gap (0.005 eV). Under external electric field, germanene with organic molecule adsorption can exhibit a wide range of linear tunable band gaps, which is merely determined by the strength of electric field regardless of its direction. The charge transfer among organic molecules and two sublattices in germanene gradually rises with the increasing the strength of electric field, resulting in the electron density around the sublattices in germanene unequally distributed. Thus, according to the tight-binding model, a larger band gap at the K-point is opened. When germanane (fully hydrogenated germanene HGeH) substrate is applied, the band gaps further widen, where the band gap of benzene/ germanene/germanane system can increase to 0.152 eV, and that of hexafluorobenzene/germanene/germanane system can reach 0.105 eV. The sizable band gap in germanene is created due to the symmetry of two sublattices in germanene destroyed by the dual effects of organic molecule adsorption and substrate. Note that both of organic molecules and substrate are found to non-covalently functionalize the germanene. As the strength of the negative electric field increases, the band gaps can be further modulated effectively. Surprisingly, the band gaps of the above systems can be closed, and reopened under a critical electric field. These features are attributed to the build-in electric field due to the interlayer charge transfer of the systems, which breaks the equivalence between the two sublattices of germanene. More importantly, the high carrier mobility in germanene is still retained to a large extent. These results provide effective and reversible routes to engineering the band gap of germanene for the applications of germanene to field-effect transistor and other nanoelectronic devices.

Keywords:

Authors and contacts

1.
College of Materials Science and Engineering, Xi’an Shiyou University, Xi’an 710065, China
2.
State Key Laboratory for Mechanical Behavior of Materials, Xi’an Jiaotong University, Xi’an 710049, China

Corresponding author: Xiao Mei-Xia, mxxiao@xsyu.edu.cn ; He Cheng, hecheng@xjtu.edu.cn

Funds: Project supported by the Young Scientists Fund of the National Natural Science Foundation of China (Grant No. 51801155) and the Provincial Superiority Discipline of Materials Science and Engineering of Xi’an Shiyou University, China (Grant No. YS37020203)

FullText HTML : translate this paragraph

References

[1]	黄立, 杜世萱, 高鸿钧 2018 物理 47 173 Google Scholar Huang L, Du S X, Gao H J 2018 Physics 47 173 Google Scholar
[2]	Li L F, Lu S Z, Pan J B, Qin Z H, Wang Y Q, Wang Y L, Cao G Y, Du S X, Gao H J 2014 Adv. Mater. 26 4820 Google Scholar
[3]	Dávila M E, Xian L, Cahangirov S, Rubio A, Lay Le G 2014 New J. Phys. 16 095002 Google Scholar
[4]	Derivaz M, Dentel D, Stephan R, Hanf M C, Mehdaoui A, Sonnet P, Pirri C 2015 Nano Lett. 15 2510 Google Scholar
[5]	Qin Z H, Pan J B, Lu S Z, Shao Y, Wang Y L, Du S X, Gao H J, Cao G Y 2017 Adv. Mater. 29 1606046 Google Scholar
[6]	武红, 李峰 2016 物理学报 65 096801 Google Scholar Wu H, Li F 2016 Acta Phys. Sin. 65 096801 Google Scholar
[7]	Liu C C, Feng W X, Yao Y G 2011 Phys. Rev. Lett. 107 076802 Google Scholar
[8]	Wang T H, Zhu Y F, Jiang Q 2013 J. Phys. Chem. C 117 12873 Google Scholar
[9]	Zhu Y F, Dai Q Q, Zhao M, Jiang Q 2013 Sci. Rep. 3 1524 Google Scholar
[10]	Garcia J C, de Lima D B, Assali L V C, Justo J F 2011 J. Phys. Chem. C 115 13242 Google Scholar
[11]	Gao N, Zheng W T, Jiang Q 2012 Phys. Chem. Chem. Phys. 14 257 Google Scholar
[12]	Wang R, Xu M S, Pi X D 2015 Chin. Phys. B 24 086807 Google Scholar
[13]	Gao J F, Zhang J F, Liu H S, Zhang Q F, Zhao J J 2013 Nanoscale 5 9785 Google Scholar
[14]	Li S, Wu Y F, Tu Y, Wang Y, Jiang T, Liu W, Zhao Y 2015 Sci. Rep. 5 7881 Google Scholar
[15]	Liu H S, Feng H F, Du Y, Chen J, Wu K H, Zhao J J 2016 2D Mater. 3 025034 Google Scholar
[16]	Hu T, Gerber I C 2013 J. Phys. Chem. C 117 2411 Google Scholar
[17]	Wang Y P, Ji W X, Zhang C W, Li S S, Li F, Li P, Ren M J, Chen X L, Yuan M, Wang P J 2016 Mater. Chem. Phys. 173 379 Google Scholar
[18]	Chen Q, Hu H, Chen X J, Wang J L 2011 Appl. Phys. Lett. 98 053102 Google Scholar
[19]	Zhang Y B, Tang T T, Girit C, Hao Z, Martin M C, Zettl A, Crommie M F, Shen Y R, Wang F 2009 Nature 459 820 Google Scholar
[20]	Ni Z, Liu Q H, Tang K C, Zheng J X, Zhou J, Qin R, Gao Z X, Yu P, Lu J 2012 Nano Lett. 12 113 Google Scholar
[21]	Liu G, Luo W W, Wang X, Lei X L, Xu B, Ouyang C Y, Liu S B 2018 J. Mater. Chem. C 6 5937 Google Scholar
[22]	Zhang D, Lou W K, Miao M S, Zhang S C, Chang K 2013 Phys. Rev. Lett. 111 156402 Google Scholar
[23]	张弦, 郭志新, 曹觉先, 肖思国, 丁建文 2015 物理学报 64 186101 Google Scholar Zhang X, Guo Z X, Cao J X, Xiao S G, Ding J W 2015 Acta Phys. Sin. 64 186101 Google Scholar
[24]	Li X D, Wu S Q, Zhou S, Zhu Z Z 2014 Nanoscale Res. Lett. 9 110 Google Scholar
[25]	Ye H, Hu F F, Tang H Y, Yang L W, Chen X P, Wang L G, Zhang G Q 2018 Phys. Chem. Chem. Phys. 20 16067 Google Scholar
[26]	Fan Y C, Liu X B, Wang J R, Ai H Q, Zhao M W 2018 Phys. Chem. Chem. Phys. 20 11369 Google Scholar
[27]	Gao N, Lu G Y, Wen Z, Jiang Q 2017 J. Mater. Chem. C 5 627 Google Scholar
[28]	Zhou S, Zhao J 2016 J. Phys. Chem. C 120 21691 Google Scholar
[29]	Delley B 1990 J. Chem. Phys. 92 508 Google Scholar
[30]	Delley B 2000 J. Chem. Phys. 113 7756 Google Scholar
[31]	Perdew J P, Burke K, Ernzerhof M 1996 Phys. Rev. Lett. 77 3865 Google Scholar
[32]	Koelling D D, Hartreermon B N 1977 J. Phys. C 10 3107 Google Scholar
[33]	Monkhorst H J, Pack J D 1976 Phys. Rev. B 13 5188 Google Scholar
[34]	Grimme S 2006 J. Comput. Chem. 27 1787 Google Scholar
[35]	Li S, Wu Y F, Liu W, Zhao Y H 2014 Chem. Phys. Lett. 609 161 Google Scholar
[36]	Xie X Q, Ao Z M, Su D W, Zhang J Q, Wang G X 2015 Adv. Funct. Mater. 25 1393 Google Scholar
[37]	陈庆玲, 戴振宏, 刘兆庆, 安玉凤, 刘悦林 2016 物理学报 65 136101 Google Scholar Chen Q L, Dai Z H, Liu Z Q, An Y F, Liu Y L 2016 Acta Phys. Sin. 65 136101 Google Scholar
[38]	Shen T, Ren J C, Liu X, Li S, Liu W 2019 J. Am. Chem. Soc. 141 3110 Google Scholar
[39]	He C, Han F S, Zhang J H, Zhang W X 2020 J. Mater. Chem. C 8 6923 Google Scholar
[40]	Rubio-Pereda P, Takeuchi N 2015 J. Phys. Chem. C 119 27995 Google Scholar
[41]	Su G R, Yang S, Jiang Y D, Li J T, Ren J C, Liu W 2019 Prog. Surf. Sci. 4 100561 Google Scholar
[42]	Gao W, Chen Y, Li B, Liu S P, Liu X, Jiang Q 2020 Nat. Commun. 11 1196 Google Scholar
[43]	Ye J P, Liu G, Han Y, Luo W W, Sun B Z, Lei X L, Xu B, Ouyang C Y, Zhang H L 2019 Phys. Chem. Chem. Phys. 21 20287 Google Scholar
[44]	Ye X S, Shao Z G, Zhao H B, Yang L, Wang C L 2014 RSC Adv. 4 21216 Google Scholar
[45]	Quhe R, Fei R, Liu Q H, Zheng J X, Li H, Xu C Y, Ni Z Y, Wang Y Y, Yu D P, Gao Z X, Lu J 2012 Sci. Rep. 2 853 Google Scholar
[46]	Yan J A, Gao S P, Stein R, Coard G 2015 Phys. Rev. B 91 245403 Google Scholar
[47]	陈艳珊, 刘兴斌 2013 低温与特气 31 33 Google Scholar Chen Y S, Liu X B 2013 Low Temp. Spec. Gases 31 33 Google Scholar
[48]	Amamou W, Odenthal P M, Bushong E J, O’hara D J, Luo Y K, Baren J V, Pinchuck I, Wu Y, Ahmed A S, Katoch J, Bockrath M W 2015 2D Mater. 2 035012 Google Scholar
[49]	Jiang S S, Bianco E, Goldberger J E 2014 J. Mater. Chem. C 2 3185 Google Scholar
[50]	Bianco E, Butler S, Jiang S S, Restrepo O D, Windl W F, Goldberger J E 2013 ACS Nano 7 4414 Google Scholar

Cited By

图 1 有机分子吸附在2 × 2锗烯超晶胞表面的八种吸附构型示意图(粉色球和蓝色球分别表示锗烯中上层锗原子和下层锗原子, 灰色球表示C原子, 而白色球表示H原子或F原子)

Figure 1. Schematic view of the eight adsorption configurations of the organic molecules adsorbed on the 2 × 2 supercell of germanene, where the pink balls represent the upper Ge atoms of the germanene, the blue balls represent the lower Ge atoms of the germanene, the gray balls represent the C atom, and the white balls represent the H or F atoms.

DownLoad: Full-Size Img PowerPoint

图 2 (a) T-1构型的苯/锗烯体系的俯视图和主视图. (b) T-4构型的六氟苯/锗烯体系的俯视图和主视图. 粉色球和蓝色球分别表示锗烯上层和下层Ge原子, 灰色球表示C原子, 白色球和黄色球分别表示H原子和F原子; E_ex表示垂直于锗烯的外电场强度, 从锗原子指向有机分子方向的电场为正电场, 反之为负电场. (c) T-1构型的苯/锗烯体系的能带结构图和部分态密度(PDOS)图. (d) T-4构型的六氟苯/锗烯体系的能带结构图和部分态密度图

Figure 2. (a) Top and side views of the benzene/germanene systems with T-1 configuration. (b) The top and side views of the hexafluorobenzene/germanene systems with T-4 configuration. The pink and blue balls represent the upper and lower Ge atoms of the germanene, respectively. The gray balls represent the C atom. The white and yellow balls represent the H and F atoms, respectively. External electric field E_ex perpendicular to the germanene is applied along the upward direction (defined as positive “+”, i.e., the electric field direction is from the germanene to the organic molecules at positive electric field) or the downward direction (defined as negative “–”). (c) Band structure and partial density of states (PDOS) of benzene/germanene with T-1 configuration. (d) Band structure and PDOS of hexafluobenzene/germanene with T-4 configuration.

DownLoad: Full-Size Img PowerPoint

图 3 (a) T-1构型的苯/锗烯体系和(b) T-4构型的六氟苯/锗烯体系的带隙E_g随外电场强度E_ex的变化图, 插图a—d分别显示了两种体系在负电场和正电场作用下具有最大带隙时的能带结构, e和f分别显示了两种体系在临界外电场下具有零带隙时的能带结构图

Figure 3. Band gaps E_g of (a) benzene/germanene system with T-1 configuration and (b) hexafluorobenzene/germanene system with T-4 configuration as a function of the strength of the external electric field. The inserts a–d show the band structures of both systems with the maximum band gap under negative and positive electric field, while e and f show the band structure of both systems with the zero-gap under the critical external electric field.

DownLoad: Full-Size Img PowerPoint

图 4 (a) T-1构型的苯/锗烯体系和(b) T-4构型的六氟苯/锗烯体系电荷转移量Q随外电场强度E_ex变化关系图

Figure 4. Charge transfer Q of (a) benzene/germanene system with T-1 configuration and (b) hexafluorobenzene/germanene system with T-4 configuration as a function of the strength of external electric field E_ex.

DownLoad: Full-Size Img PowerPoint

图 5 (a) T-1构型的苯/锗烯体系和(b) T-4构型的六氟苯/锗烯体系的内电场强度E_in与外电场强度E_ex变化关系图

Figure 5. Strength of internal electric field E_in of (a) benzene/germanene system with T-1 configuration and (b) hexafluorobenzene/germanene system with T-4 configuration as a function of the strength of external electric field E_ex.

DownLoad: Full-Size Img PowerPoint

图 6 (a)苯/锗烯/HGeH体系的俯视图和主视图. (b)六氟苯/锗烯/HGeH体系的俯视图和主视图, 其中粉色球和蓝色球表示锗烯上层和下层Ge原子, 灰色球表示C原子, 白色球和黄色球表示有机分子中H原子和F原子, 橙色球和黑色球表示HGeH上层H原子和下层H原子, 绿色球和红色球表示HGeH上层和下层Ge原子; E_ex表示垂直于锗烯的外电场, 从HGeH指向有机分子方向的电场为正电场, 反之为负电场. (c)苯/锗烯/HGeH体系的能带结构图和部分态密度(PDOS)图. (d)六氟苯/锗烯/HGeH体系的能带结构图和部分态密度图

Figure 6. (a) Top and side views of the benzene/germanene/HGeH system. (b) Top and side views of the hexafluorobenzene/germanene/HGeH systems. The pink and blue balls represent the upper and lower Ge atoms of the germanene, respectively. The gray balls represent the C atom. The white and yellow balls represent the H or F atoms of organic molecules. The orange and black balls represent the upper and lower H atoms of HGeH. The green and red balls represent the upper and lower Ge atoms of HGeH, respectively. External electric field E_ex perpendicular to the germanene is applied along the upward direction (defined as positive “+”, i.e., the electric field direction is from the HGeH to the organic molecules at positive electric field) or the downward direction (defined as negative “–”). (c) Band structure and PDOS of benzene/germanene/HGeH. (d) Band structure and PDOS of hexafluobenzene/germanene/HGeH.

DownLoad: Full-Size Img PowerPoint

图 7 (a)苯/锗烯/HGeH体系和(b)六氟苯/锗烯/HGeH体系的带隙E_g随外电场强度E_ex的变化关系图, 其中插图显示了两个体系具有最大带隙时的能带结构

Figure 7. Band gaps E_g of (a) benzene/germanene/HGeH system and (b) hexafluorobenzene/germanene/HGeH system as a function of the strength of the external electric field E_ex. The inserts show the band structures of both systems with the maximum band gaps.

DownLoad: Full-Size Img PowerPoint

图 8 (a)苯/锗烯/HGeH体系和(b)六氟苯/锗烯/HGeH体系的电荷转移量Q随外电场强度E_ex变化关系图

Figure 8. Charge transfer Q of (a) benzene/germanene/HGeH system and (b) hexafluorobenzene/germanene/HGeH system as a function of the strength of external electric field E_ex.

DownLoad: Full-Size Img PowerPoint

表 1 苯/锗烯体系和六氟苯/锗烯体系的八种高对称吸附构型的吸附能E_ad、吸附距离H、翘曲高度d和带隙E_g

Table 1. Adsorption energy E_ad, adsorption distance H, buckling height d and band gap E_g of eight highly symmetric adsorption configurations of benzene/germanene and hexafluobenzene/germanene systems.

八种构型		T-1	T-2	T-3	T-4	H-1	H-2	B-1	B-2
苯/锗烯	E_ad/eV	0.676	0.662	0.605	0.617	0.525	0.522	0.640	0.638
	H/Å	3.060	3.063	3.146	3.090	3.352	3.445	2.977	3.060
	d/Å	0.804	0.795	0.741	0.739	0.720	0.720	0.793	0.783
	E_g/eV	0.036	0.035	0.041	0.039	0.009	0.010	0.044	0.044
六氟苯/锗烯	E_ad/eV	0.593	0.588	0.589	0.656	0.521	0.569	0.647	0.631
	H/Å	3.005	3.160	3.020	2.970	3.114	3.141	2.982	3.054
	d/Å	0.780	0.786	0.732	0.763	0.765	0.781	0.762	0.776
	E_g/eV	0.014	0.022	0.039	0.005	0.006	0.018	0.016	0.035

DownLoad: CSV

[1]	黄立, 杜世萱, 高鸿钧 2018 物理 47 173 Google Scholar Huang L, Du S X, Gao H J 2018 Physics 47 173 Google Scholar
[2]	Li L F, Lu S Z, Pan J B, Qin Z H, Wang Y Q, Wang Y L, Cao G Y, Du S X, Gao H J 2014 Adv. Mater. 26 4820 Google Scholar
[3]	Dávila M E, Xian L, Cahangirov S, Rubio A, Lay Le G 2014 New J. Phys. 16 095002 Google Scholar
[4]	Derivaz M, Dentel D, Stephan R, Hanf M C, Mehdaoui A, Sonnet P, Pirri C 2015 Nano Lett. 15 2510 Google Scholar
[5]	Qin Z H, Pan J B, Lu S Z, Shao Y, Wang Y L, Du S X, Gao H J, Cao G Y 2017 Adv. Mater. 29 1606046 Google Scholar
[6]	武红, 李峰 2016 物理学报 65 096801 Google Scholar Wu H, Li F 2016 Acta Phys. Sin. 65 096801 Google Scholar
[7]	Liu C C, Feng W X, Yao Y G 2011 Phys. Rev. Lett. 107 076802 Google Scholar
[8]	Wang T H, Zhu Y F, Jiang Q 2013 J. Phys. Chem. C 117 12873 Google Scholar
[9]	Zhu Y F, Dai Q Q, Zhao M, Jiang Q 2013 Sci. Rep. 3 1524 Google Scholar
[10]	Garcia J C, de Lima D B, Assali L V C, Justo J F 2011 J. Phys. Chem. C 115 13242 Google Scholar
[11]	Gao N, Zheng W T, Jiang Q 2012 Phys. Chem. Chem. Phys. 14 257 Google Scholar
[12]	Wang R, Xu M S, Pi X D 2015 Chin. Phys. B 24 086807 Google Scholar
[13]	Gao J F, Zhang J F, Liu H S, Zhang Q F, Zhao J J 2013 Nanoscale 5 9785 Google Scholar
[14]	Li S, Wu Y F, Tu Y, Wang Y, Jiang T, Liu W, Zhao Y 2015 Sci. Rep. 5 7881 Google Scholar
[15]	Liu H S, Feng H F, Du Y, Chen J, Wu K H, Zhao J J 2016 2D Mater. 3 025034 Google Scholar
[16]	Hu T, Gerber I C 2013 J. Phys. Chem. C 117 2411 Google Scholar
[17]	Wang Y P, Ji W X, Zhang C W, Li S S, Li F, Li P, Ren M J, Chen X L, Yuan M, Wang P J 2016 Mater. Chem. Phys. 173 379 Google Scholar
[18]	Chen Q, Hu H, Chen X J, Wang J L 2011 Appl. Phys. Lett. 98 053102 Google Scholar
[19]	Zhang Y B, Tang T T, Girit C, Hao Z, Martin M C, Zettl A, Crommie M F, Shen Y R, Wang F 2009 Nature 459 820 Google Scholar
[20]	Ni Z, Liu Q H, Tang K C, Zheng J X, Zhou J, Qin R, Gao Z X, Yu P, Lu J 2012 Nano Lett. 12 113 Google Scholar
[21]	Liu G, Luo W W, Wang X, Lei X L, Xu B, Ouyang C Y, Liu S B 2018 J. Mater. Chem. C 6 5937 Google Scholar
[22]	Zhang D, Lou W K, Miao M S, Zhang S C, Chang K 2013 Phys. Rev. Lett. 111 156402 Google Scholar
[23]	张弦, 郭志新, 曹觉先, 肖思国, 丁建文 2015 物理学报 64 186101 Google Scholar Zhang X, Guo Z X, Cao J X, Xiao S G, Ding J W 2015 Acta Phys. Sin. 64 186101 Google Scholar
[24]	Li X D, Wu S Q, Zhou S, Zhu Z Z 2014 Nanoscale Res. Lett. 9 110 Google Scholar
[25]	Ye H, Hu F F, Tang H Y, Yang L W, Chen X P, Wang L G, Zhang G Q 2018 Phys. Chem. Chem. Phys. 20 16067 Google Scholar
[26]	Fan Y C, Liu X B, Wang J R, Ai H Q, Zhao M W 2018 Phys. Chem. Chem. Phys. 20 11369 Google Scholar
[27]	Gao N, Lu G Y, Wen Z, Jiang Q 2017 J. Mater. Chem. C 5 627 Google Scholar
[28]	Zhou S, Zhao J 2016 J. Phys. Chem. C 120 21691 Google Scholar
[29]	Delley B 1990 J. Chem. Phys. 92 508 Google Scholar
[30]	Delley B 2000 J. Chem. Phys. 113 7756 Google Scholar
[31]	Perdew J P, Burke K, Ernzerhof M 1996 Phys. Rev. Lett. 77 3865 Google Scholar
[32]	Koelling D D, Hartreermon B N 1977 J. Phys. C 10 3107 Google Scholar
[33]	Monkhorst H J, Pack J D 1976 Phys. Rev. B 13 5188 Google Scholar
[34]	Grimme S 2006 J. Comput. Chem. 27 1787 Google Scholar
[35]	Li S, Wu Y F, Liu W, Zhao Y H 2014 Chem. Phys. Lett. 609 161 Google Scholar
[36]	Xie X Q, Ao Z M, Su D W, Zhang J Q, Wang G X 2015 Adv. Funct. Mater. 25 1393 Google Scholar
[37]	陈庆玲, 戴振宏, 刘兆庆, 安玉凤, 刘悦林 2016 物理学报 65 136101 Google Scholar Chen Q L, Dai Z H, Liu Z Q, An Y F, Liu Y L 2016 Acta Phys. Sin. 65 136101 Google Scholar
[38]	Shen T, Ren J C, Liu X, Li S, Liu W 2019 J. Am. Chem. Soc. 141 3110 Google Scholar
[39]	He C, Han F S, Zhang J H, Zhang W X 2020 J. Mater. Chem. C 8 6923 Google Scholar
[40]	Rubio-Pereda P, Takeuchi N 2015 J. Phys. Chem. C 119 27995 Google Scholar
[41]	Su G R, Yang S, Jiang Y D, Li J T, Ren J C, Liu W 2019 Prog. Surf. Sci. 4 100561 Google Scholar
[42]	Gao W, Chen Y, Li B, Liu S P, Liu X, Jiang Q 2020 Nat. Commun. 11 1196 Google Scholar
[43]	Ye J P, Liu G, Han Y, Luo W W, Sun B Z, Lei X L, Xu B, Ouyang C Y, Zhang H L 2019 Phys. Chem. Chem. Phys. 21 20287 Google Scholar
[44]	Ye X S, Shao Z G, Zhao H B, Yang L, Wang C L 2014 RSC Adv. 4 21216 Google Scholar
[45]	Quhe R, Fei R, Liu Q H, Zheng J X, Li H, Xu C Y, Ni Z Y, Wang Y Y, Yu D P, Gao Z X, Lu J 2012 Sci. Rep. 2 853 Google Scholar
[46]	Yan J A, Gao S P, Stein R, Coard G 2015 Phys. Rev. B 91 245403 Google Scholar
[47]	陈艳珊, 刘兴斌 2013 低温与特气 31 33 Google Scholar Chen Y S, Liu X B 2013 Low Temp. Spec. Gases 31 33 Google Scholar
[48]	Amamou W, Odenthal P M, Bushong E J, O’hara D J, Luo Y K, Baren J V, Pinchuck I, Wu Y, Ahmed A S, Katoch J, Bockrath M W 2015 2D Mater. 2 035012 Google Scholar
[49]	Jiang S S, Bianco E, Goldberger J E 2014 J. Mater. Chem. C 2 3185 Google Scholar
[50]	Bianco E, Butler S, Jiang S S, Restrepo O D, Windl W F, Goldberger J E 2013 ACS Nano 7 4414 Google Scholar

[1]	Wu Hong-Fen, Feng Pan-Jun, Zhang Shuo, Liu Da-Peng, Gao Miao, Yan Xun-Wang. First-principles study of Fe atom adsorbed biphenylene monolayer. Acta Physica Sinica, 2022, 71(3): 036801. doi: 10.7498/aps.71.20211631
[2]	Zhan Zhen, Zhang Ya-Lei, Yuan Sheng-Jun. Lattice relaxation and substrate effects of graphene moiré superlattice. Acta Physica Sinica, 2022, 71(18): 187302. doi: 10.7498/aps.71.20220872
[3]	. First principles study of Fe atom adsorbed biphenylene monolayer. Acta Physica Sinica, 2021, (): . doi: 10.7498/aps.70.20211631
[4]	Xiang Yang, Zheng Jun, Li Chun-Lei, Guo Yong. Spin filter effect of germanene nanoribbon controlled by local exchange field and electric field. Acta Physica Sinica, 2019, 68(18): 187302. doi: 10.7498/aps.68.20190817
[5]	Qin Zhi-Hui. Recent progress of graphene-like germanene. Acta Physica Sinica, 2017, 66(21): 216802. doi: 10.7498/aps.66.216802
[6]	Wu Hong, Li Feng. Mechanisms on the GeH/ interactions in germanene/germanane bilayer for tuning band structures. Acta Physica Sinica, 2016, 65(9): 096801. doi: 10.7498/aps.65.096801
[7]	Gao Tan-Hua. Structural and electronic properties of hydrogenated bilayer silicene. Acta Physica Sinica, 2015, 64(7): 076801. doi: 10.7498/aps.64.076801
[8]	Zhang Xian, Guo Zhi-Xin, Cao Jue-Xian, Xiao Si-Guo, Ding Jian-Wen. Atomic and electronic structures of silicene and germanene on GaAs(111). Acta Physica Sinica, 2015, 64(18): 186101. doi: 10.7498/aps.64.186101
[9]	Liu Jun, Liang Pei, Shu Hai-Bo, Shen Tao, Xing Song, Wu Qiong. First principles study on molecule doping in MoS2 monolayer. Acta Physica Sinica, 2014, 63(11): 117101. doi: 10.7498/aps.63.117101
[10]	Wu Jiang-Bin, Zhang Xin, Tan Ping-Heng, Feng Zhi-Hong, Li Jia. Electronic structure of twisted bilayer graphene. Acta Physica Sinica, 2013, 62(15): 157302. doi: 10.7498/aps.62.157302
[11]	Wang Yong-Long, Pan Hong-Zhe, Xu Ming, Chen Li, Sun Yuan-Yuan. Electronic structure and magnetism of single-layer trigonal graphene quantum dots with zigzag edges. Acta Physica Sinica, 2010, 59(9): 6443-6449. doi: 10.7498/aps.59.6443
[12]	Huo Xin-Xia, Wang Chang, Zhang Xiu-Mei, Wang Li-Guang. Electron structure and electron conductance of fullerene C32 with Au electrodes. Acta Physica Sinica, 2010, 59(7): 4955-4960. doi: 10.7498/aps.59.4955
[13]	Jin Zi-Fei, Tong Guo-Ping, Jiang Yong-Jin. Effect of the non-nearest-neighbor hopping on the electronic structure of armchair graphene nanoribbons. Acta Physica Sinica, 2009, 58(12): 8537-8543. doi: 10.7498/aps.58.8537
[14]	Hu Hai-Xin, Zhang Zhen-Hua, Liu Xin-Hai, Qiu Ming, Ding Kai-He. Tight binding studies on the electronic structure of graphene nanoribbons. Acta Physica Sinica, 2009, 58(10): 7156-7161. doi: 10.7498/aps.58.7156
[15]	Bai Yu-Jie, Fu Shi-You, Deng Kai-Ming, Tang Chun-Mei, Chen Xuan, Tan Wei-Shi, Liu Yu-Zhen, Huang De-Cai. Density functional calculations on the geometric and electronic structures of the endohedral fullerene H2＠C60 and its dimmer. Acta Physica Sinica, 2008, 57(6): 3684-3689. doi: 10.7498/aps.57.3684
[16]	Zhang Hong-Yu, Wang Li-Guang, Zhang Xiu-Mei, Yu Ding-Wen, Li Yong. Electronic structure and conductance of fullerene C20. Acta Physica Sinica, 2008, 57(10): 6271-6276. doi: 10.7498/aps.57.6271
[17]	Ma Song-Shan, Xu Hui, Liu Xiao-Liang, Guo Ai-Min. Characteristics of the electronic structure of DNA sequence. Acta Physica Sinica, 2006, 55(6): 3170-3174. doi: 10.7498/aps.55.3170
[18]	Zhu Sheng Xiang, Li Rui, Yang Xiu Wen, Xue Chun Rong. Study on electronic structures of PuH2 with DVM. Acta Physica Sinica, 2003, 52(1): 67-71. doi: 10.7498/aps.52.67
[19]	WANG LI-MIN, LUO YING, MA BEN-KUN. ELECTRONIC STRUCTURE OF DOUBLE QUANTUM-DOT MOLECULE. Acta Physica Sinica, 2001, 50(2): 278-286. doi: 10.7498/aps.50.278
[20]	CHEN GUANG-HUA, DENG JIN-XIANG, ZHANG SHENG-JUN, SONG XUE-MEI, WANG BO, YAN HUI. INFLUENCE OF SUBSTRATES ON THE FORMATION OF c-BN THIN FILMS. Acta Physica Sinica, 2001, 50(1): 83-87. doi: 10.7498/aps.50.83

Catalog

Vol. 70, Issue 6 - 2021-03-20

Metrics

Abstract views: 6272
PDF Downloads: 83
Cited By: 0

姓名
邮箱
手机号码
标题
留言内容
验证码

Search

Article

留言板