In掺杂ZnO薄膜的制备及其白光发射机理

李世帅 张仲 黄金昭 冯秀鹏 刘如喜

引用本文:
Citation:

In掺杂ZnO薄膜的制备及其白光发射机理

李世帅, 张仲, 黄金昭, 冯秀鹏, 刘如喜

Preparation and mechanism of In-doped ZnO emitting white-light

Li Shi-Shuai, Zhang Zhong, Huang Jin-Zhao, Feng Xiu-Peng, Liu Ru-Xi
PDF
导出引用
  • 采用溶胶-凝胶法在Si衬底上制备了本征ZnO薄膜和In:(Zn+In)分别为5%,8%,10%的ZnO薄膜,对薄膜的晶相结构和光电性质进行了表征并在CIE-XYZ表色系统中计算了不同样品的色品坐标.结果表明:In掺入后ZnO薄膜的择优生长方向由(002)面变为(101)面且面间距变小,当In掺杂量为5%时,In原子完全替代Zn原子;薄膜的电阻率随In含量的增加出现先抑后扬的趋势;随着In的掺入光谱的紫外发射峰红移,并在670 nm左右出现一个新的峰值;In:(Zn+In)为5%样品具有白光发射特性.从第一
    Pure ZnO films and In/ZnO films are prepared by sol-gel process on Si substrates.The ratio of In/(Zn+In) are 5%, 8% and 10% separately. Crystal phase structures and photoelectric properties of these films are characterized and these chromaticity coordinates of different samples are also calculated in a CIE-XYZ color system. The results show that preferred growth direction of ZnO film changes from (002) plane to (001) plane and interplanar distance becomes shorter. When doping amount of In is 5%, Zn atoms are replaced by In atoms. Resistivity of the film first decreases and the increases with the increase of the amount of In. Ultraviolet emission peak of spectrum has a redshift; a new peak emerges at 670nm with the increase of In. The sample of 5% emits white-light.The band structures of pure and 5% doping content of film are calculated based on first principles.The mechanism of emitting white-light is discussed from the view point of additional energy level.
    • 基金项目: 山东省自然科学基金(批准号:Y2007G14),山东省科学技术发展计划项目(批准号:2009GG2003028,2010G0020423),济南大学博士基金(批准号:XBS0845),北京交通大学发光与光信息技术教育部重点实验室开放基金(批准号:2010LOI01)和济南大学科研基金(批准号:XKY1029)资助的课题.
    [1]

    Fan X M, Lian J S, Guo Z X 2005 Appl. Surf. Sci. 239 176

    [2]

    Zou J, Zhou S M, Xia C T 2005 J. Crys. Grow. 280 185

    [3]

    Huang J Z, Li S S, Feng X P 2010 Acta Phys.Sin. 59 5839 (in Chinese) [黄金昭、李世帅、冯秀鹏 2010 物理学报 59 5839]

    [4]

    Zhou X, Wang S Q, Lian G J, Xiong G C 2006 Chin. Phys. 15 199

    [5]

    Liu Z W, Gu J F, Fu W J, Sun C W, Li Y, Zhang Q Y 2006 Acta Phys. Sin. 55 5479 (in Chinese) [刘志文、谷建峰、付伟佳、孙成伟、李 勇、张庆瑜 2006 物理学报 55 5479]

    [6]

    Liu R B, Pan A L, Wang F F, Zou B S 2007 Chin. Phys. 16 1129

    [7]

    Gao L, Zhang J M 2009 Chin. Phys. B 18 4536

    [8]

    Lu S C, Song G L, Xiao Z Y, Zhang J H, Huang S H 2002 Chinese Journal of Luminescence 23 306 (in Chinese) [吕树臣、宋国立、肖芝雁、张家骅、黄世华 2002 发光学报 23 306]

    [9]

    Hao Y 2005 Optoelectronic Technology & Information 18 65 (in Chinese) [郝 云 2005 光电子技术与信息 18 65]

    [10]

    Guo H H, Lin Z H, Feng Z F, Lin L L, Zhou J Z 2009 J. Phys. Chem. C 113 12546

    [11]

    Guo C F, Ding X, Xu Y 2010 Journal of the American Ceramic Society 93 1708

    [12]

    Zhang J M, Zhao D L, Shen Z M 2010 High Performance Ceramics 6 434

    [13]

    Cao Y, Miao L, Tanemura S 2006 J. Appl. Phys. 45 623

    [14]

    Chris G, Vande W 2001 Physica B 308 310

    [15]

    Ravindra S, Mahesh K, Sudhir C 2007 J. Mater. Sci. 42 4675

    [16]

    Kim S, Wan I L, Hwang S K, Chongmu L 2007 J. Mater. Sci. 42 4845

    [17]

    Lyudmila N D, Lyudmila L T U, Yurn M J 2008 Mater. Sci. 43 2143

    [18]

    Lidia A, Gregorio B, Michele P J 2008 Phys. Chem. C 112 4049

    [19]

    Zhao Y, Fu Y J 2010 Acta Phys. Sin. 59 2679 (in Chinese) [赵 艳、蒋毅坚 2010 物理学报 59 2679]

    [20]

    Li S T, Cheng P F, Zhao L, Li J Y 2009 Acta Phys.Sin. 58 523 (in Chinese)[李盛涛、成鹏飞、赵 雷、李建英 2009 物理学报 58 523]

    [21]

    Li S S, Feng X P, Hang J J, Zhang Z, Tao Y Y 2010 Journal of Functional Materials 41 113[李世帅、冯秀鹏、黄金昭、张 仲、陶冶微 2010 功能材料 41 113]

    [22]

    Fu Z X, Guo C X, Lin B X 1998 Chin. Phys. Lett. 15 457

    [23]

    Seung Y B, Hyun C C, Chan W N, Jeunghee P 2005 Appl. Phys. Lett. 86 033102

    [24]

    Jie J S, Wang G Z, Han X H, Yu Q X, Liao Y, Li G P, Hou J G 2004 Chem. Phys. Lett. 387 466

    [25]

    Xu J, Huang S P, Wang Z S 2009 Solid State Commun. 149 527

  • [1]

    Fan X M, Lian J S, Guo Z X 2005 Appl. Surf. Sci. 239 176

    [2]

    Zou J, Zhou S M, Xia C T 2005 J. Crys. Grow. 280 185

    [3]

    Huang J Z, Li S S, Feng X P 2010 Acta Phys.Sin. 59 5839 (in Chinese) [黄金昭、李世帅、冯秀鹏 2010 物理学报 59 5839]

    [4]

    Zhou X, Wang S Q, Lian G J, Xiong G C 2006 Chin. Phys. 15 199

    [5]

    Liu Z W, Gu J F, Fu W J, Sun C W, Li Y, Zhang Q Y 2006 Acta Phys. Sin. 55 5479 (in Chinese) [刘志文、谷建峰、付伟佳、孙成伟、李 勇、张庆瑜 2006 物理学报 55 5479]

    [6]

    Liu R B, Pan A L, Wang F F, Zou B S 2007 Chin. Phys. 16 1129

    [7]

    Gao L, Zhang J M 2009 Chin. Phys. B 18 4536

    [8]

    Lu S C, Song G L, Xiao Z Y, Zhang J H, Huang S H 2002 Chinese Journal of Luminescence 23 306 (in Chinese) [吕树臣、宋国立、肖芝雁、张家骅、黄世华 2002 发光学报 23 306]

    [9]

    Hao Y 2005 Optoelectronic Technology & Information 18 65 (in Chinese) [郝 云 2005 光电子技术与信息 18 65]

    [10]

    Guo H H, Lin Z H, Feng Z F, Lin L L, Zhou J Z 2009 J. Phys. Chem. C 113 12546

    [11]

    Guo C F, Ding X, Xu Y 2010 Journal of the American Ceramic Society 93 1708

    [12]

    Zhang J M, Zhao D L, Shen Z M 2010 High Performance Ceramics 6 434

    [13]

    Cao Y, Miao L, Tanemura S 2006 J. Appl. Phys. 45 623

    [14]

    Chris G, Vande W 2001 Physica B 308 310

    [15]

    Ravindra S, Mahesh K, Sudhir C 2007 J. Mater. Sci. 42 4675

    [16]

    Kim S, Wan I L, Hwang S K, Chongmu L 2007 J. Mater. Sci. 42 4845

    [17]

    Lyudmila N D, Lyudmila L T U, Yurn M J 2008 Mater. Sci. 43 2143

    [18]

    Lidia A, Gregorio B, Michele P J 2008 Phys. Chem. C 112 4049

    [19]

    Zhao Y, Fu Y J 2010 Acta Phys. Sin. 59 2679 (in Chinese) [赵 艳、蒋毅坚 2010 物理学报 59 2679]

    [20]

    Li S T, Cheng P F, Zhao L, Li J Y 2009 Acta Phys.Sin. 58 523 (in Chinese)[李盛涛、成鹏飞、赵 雷、李建英 2009 物理学报 58 523]

    [21]

    Li S S, Feng X P, Hang J J, Zhang Z, Tao Y Y 2010 Journal of Functional Materials 41 113[李世帅、冯秀鹏、黄金昭、张 仲、陶冶微 2010 功能材料 41 113]

    [22]

    Fu Z X, Guo C X, Lin B X 1998 Chin. Phys. Lett. 15 457

    [23]

    Seung Y B, Hyun C C, Chan W N, Jeunghee P 2005 Appl. Phys. Lett. 86 033102

    [24]

    Jie J S, Wang G Z, Han X H, Yu Q X, Liao Y, Li G P, Hou J G 2004 Chem. Phys. Lett. 387 466

    [25]

    Xu J, Huang S P, Wang Z S 2009 Solid State Commun. 149 527

  • [1] 郭昭龙, 赵海新, 赵卫. 纳米ZnO-SiO2自清洁增透薄膜的制备及其性能. 物理学报, 2016, 65(6): 064206. doi: 10.7498/aps.65.064206
    [2] 贾相华, 郑友进, 尹龙承, 黄海亮, 姜宏伟, 朱瑞华. 退火温度对Cu:ZnO薄膜绿光发射的影响. 物理学报, 2014, 63(16): 166802. doi: 10.7498/aps.63.166802
    [3] 刘义, 张清, 李海金, 李勇, 刘厚通. Sr掺杂钙钛矿型氧化物Y1-xSrxCoO3的溶胶-凝胶制备及电阻率温度关系研究. 物理学报, 2013, 62(4): 047202. doi: 10.7498/aps.62.047202
    [4] 吴忠浩, 徐明, 段文倩. Fe掺杂对溶胶凝胶法制备的ZnO: Ni薄膜结构及发光特性的影响. 物理学报, 2012, 61(13): 137502. doi: 10.7498/aps.61.137502
    [5] 庄晓波, 夏海平. 用Z-扫描技术研究卟啉铜偶合TiO2/SiO2有机-无机材料的非线性吸收特性. 物理学报, 2012, 61(18): 184213. doi: 10.7498/aps.61.184213
    [6] 吴艳南, 徐明, 吴定才, 董成军, 张佩佩, 纪红萱, 何林. Co,Sn共掺ZnO薄膜结构与光致发光的研究. 物理学报, 2011, 60(7): 077505. doi: 10.7498/aps.60.077505
    [7] 杨昌虎, 马忠权, 徐飞, 赵磊, 李凤, 何波. 稀土钇、镧掺杂TiO2薄膜的拉曼谱分析. 物理学报, 2010, 59(9): 6549-6555. doi: 10.7498/aps.59.6549
    [8] 王德义, 高书霞, 李刚, 赵鸣. 溶胶-凝胶法制备Li-N双掺p型ZnO薄膜的结构、光学和电学性能. 物理学报, 2010, 59(5): 3473-3480. doi: 10.7498/aps.59.3473
    [9] 吴定才, 胡志刚, 段满益, 徐禄祥, 刘方舒, 董成军, 吴艳南, 纪红萱, 徐明. Co与Cu掺杂ZnO薄膜的制备与光致发光研究. 物理学报, 2009, 58(10): 7261-7266. doi: 10.7498/aps.58.7261
    [10] 王晓栋, 沈军, 王生钊, 张志华. 椭偏光谱法研究溶胶-凝胶TiO2薄膜的光学常数. 物理学报, 2009, 58(11): 8027-8032. doi: 10.7498/aps.58.8027
    [11] 梁丽萍, 张 磊, 盛永刚, 徐 耀, 吴 东, 孙予罕, 蒋晓东, 魏晓峰. 溶胶-凝胶ZrO2-TiO2高折射率光学膜层的抗激光损伤性能研究. 物理学报, 2007, 56(6): 3596-3601. doi: 10.7498/aps.56.3596
    [12] 兰 伟, 刘雪芹, 黄春明, 唐国梅, 杨 扬, 王印月. 溶胶凝胶旋转涂敷技术制备ZnO:In薄膜的结构特性. 物理学报, 2006, 55(2): 748-752. doi: 10.7498/aps.55.748
    [13] 梁丽萍, 徐 耀, 张 磊, 吴 东, 孙予罕, 李志宏, 吴忠华. 溶胶-凝胶方法制备ZrO2及聚合物掺杂ZrO2单层光学增反射膜. 物理学报, 2006, 55(8): 4371-4382. doi: 10.7498/aps.55.4371
    [14] 梁丽萍, 张 磊, 徐 耀, 章 斌, 吴 东, 孙予罕, 蒋晓东, 魏晓峰, 李志宏, 吴忠华. PVP掺杂-ZrO2溶胶-凝胶工艺制备多层激光高反射膜的研究. 物理学报, 2006, 55(11): 6175-6184. doi: 10.7498/aps.55.6175
    [15] 陶卫东, 董建峰, 夏海平, 白贵儒, 陆祖康. 微米手性晶粒凝胶玻璃的制备及其消偏振效应. 物理学报, 2004, 53(3): 891-894. doi: 10.7498/aps.53.891
    [16] 赵明磊, 王春雷, 王矜奉, 陈洪存, 钟维烈. 溶胶-凝胶法制备的高压电常数(Bi0.5Na0.5)1-xBaxTiO3系无铅压电陶瓷. 物理学报, 2004, 53(7): 2357-2362. doi: 10.7498/aps.53.2357
    [17] 赵明磊, 王春雷, 钟维烈, 王矜奉, 陈洪存. 溶胶-凝胶法制备Bi0.5Na0.5TiO3陶瓷及其电学特性. 物理学报, 2003, 52(1): 229-232. doi: 10.7498/aps.52.229
    [18] 何志巍, 甄聪棉, 兰 伟, 王印月. 溶胶-凝胶法制备纳米多孔SiO2薄膜. 物理学报, 2003, 52(12): 3130-3134. doi: 10.7498/aps.52.3130
    [19] 杨合情, 王喧, 张邦劳, 李永放, 张良莹, 姚熹. 溶胶-凝胶法制备的GeO2-SiO2凝胶玻璃的红光发射. 物理学报, 2002, 51(1): 178-182. doi: 10.7498/aps.51.178
    [20] 陶卫东, 夏海平, 白贵儒, 董建峰, 聂秋华. 固体手性材料的研制及其特性测试. 物理学报, 2002, 51(3): 685-689. doi: 10.7498/aps.51.685
计量
  • 文章访问数:  8767
  • PDF下载量:  631
  • 被引次数: 0
出版历程
  • 收稿日期:  2010-11-30
  • 修回日期:  2011-01-06
  • 刊出日期:  2011-09-15

/

返回文章
返回