柠檬酸掺杂的MgB2超导体钉扎机理的研究

孙辉辉 杨烨 王磊 Cheng C. H. 冯勇 赵勇

引用本文:
Citation:

柠檬酸掺杂的MgB2超导体钉扎机理的研究

孙辉辉, 杨烨, 王磊, Cheng C. H., 冯勇, 赵勇

Evidence of δl pinning induced by citric acid doping in MgB2 superconductor

Sun Hui-Hui, Yang Ye, Wang Lei, Cheng C. H., Feng Yong, Zhao Yong
PDF
导出引用
  • 本文研究了柠檬酸掺杂的MgB2超导材料的Jc-B行为及其钉扎机理.在纯MgB2多晶样品中,δTc钉扎起主要作用,而在掺杂的样品中,则是δl钉扎和δTc钉扎共同作用,并且δl钉扎机理占主要作用,其贡献比重随着掺杂量的增加而增加.从Jc-B行为和钉扎行为的分析都可以得到
    The critical current density (Jc) and flux-pinning mechanism of MgB2 doped with citric acid (C6H8O7) from 0 to 30wt% have been investigated in detail by magnetic and resistive measurements. The temperature dependence of critical current density,Jc(T),at particular field within the single vortex regime was analyzed. δTc pinning mechanism was found to be the only important pinning mechanism in pure MgB2 samples,while δl pinning is dominant with little effect of δTc pinning for citric acid doped samples. It was observed that the contribution of δl pinning enhances with the increasing doping level of critic acid,and it was also found that MgB2 doped with 15wt% critic acid shows the best performance in Jc-B behavior.
    • 基金项目: 国家自然科学基金(批准号: 50588201,50672078,50872116),高等学校博士学科点专项科研基金(批准号:200806130023),国家重点基础研究发展计划(973)项目(批准号:2007CB616906),澳大利亚研究委员会基金(批准号:DP0559872,DP0881739),西南交通大学生博士创新基金,西南交通大学科技发展基金,西南交通大学科技创新基金资助的课题.
    [1]

    [1]Nagamatsu J,Nakagawa N,Muranaka T,Zenitani Y,Akimitsu J 2001 Nature 410 63

    [2]

    [2]Tan M Q,Tao X M 2001 Acta Phys. Sin. 50 1193 (in Chinese) [谭明秋、陶向明 2001 物理学报 50 1193]

    [3]

    [3]Yang D S,Wu B M,Li B,Zheng W H,Li S Y,Chen X H,Cao L Z 2003 Acta Phys. Sin. 52 2015 (in Chinese) [杨东升、吴柏枚、李波、郑卫华、李世燕、陈仙辉、曹烈兆 2003 物理学报 52 2015]

    [4]

    [4]Yang H S,Yu M,Li S Y,Li P C,Chai Y S,Zhang L,Chen X H,Cao L Z 2001 Acta Phys. Sin. 50 1197 (in Chinese) [杨宏顺、余旻、李世燕、李鹏程、柴一晟、章良、陈先辉、曹烈兆 2001 物理学报 50 1197]

    [5]

    [5]Shang X F,Tao X M,Chen W B,Chen H X,Wang M,Tan M Q 2008 Acta Phys. Sin. 57 5838 (in Chinese) [尚学府、陶向明、陈文斌、陈会贤、王淼、谭明秋 2008 物理学报 57 5838]

    [6]

    [6]Shi L B,Ren J Y,Zhang F Y,Zhang G H,Yu Z Q 2007 Acta Phys. Sin. 56 5353 (in Chinese) [史力斌、任骏原、张凤云、张国华、余增强 2007 物理学报 56 5353]

    [7]

    [7]Feng W J,Xia T D,Liu T Z,Zhao W J,Wei Z Q 2005 Chin. Phys. 14 2325

    [8]

    [8]Chen R H,Zhu M Y,Li Y,Li W X,Jin H M,Dou S X 2006 Acta Phys. Sin. 55 4878 (in Chinese) [陈荣华、朱明原、李瑛、李文献、金红明、窦士学 2006 物理学报 55 4878]

    [9]

    [9]Zhang X P,Ma Y W,Gao Z S,Yu Z G,K.Watanabe,Wen H H 2006 Acta Phys. Sin. 55 4873 (in Chinese) [张现平、马衍伟、高召顺、禹争光、K.Watanabe、闻海虎 2006 物理学报 55 4873]

    [10]

    ]Dou S X,Soltanian S,Horvat J,Wang X L,Zhou S H,Lonescu M,Liu H K 2002 Appl. Phys. Lett. 81 3419

    [11]

    ]Zhou S H,Pan A V,Qin M J,Liu H K,Dou S X 2003 Physica C 387 321

    [12]

    ]Yamamoto A,Shimoyama J,Ueda S,Iwayama I,Horii S,Kishio K2005 Supercond. Sci. Technol. 18 1323

    [13]

    ]Cheng C H,Yang Y,Munroe P,Zhao Y 2007 Supercond. Sci. Technol. 20 296

    [14]

    ]Qin M J,Wang X L,Liu H K,Dou S X 2002 Phys. Rev. B 65 132508

    [15]

    ]Wang X L,Zeng R,Kim J H,Liu L,Dou S X 2008 Phys. Rev. B 77 174501

    [16]

    ]Ghorbani S R,Wang X L,Dou S X,Lee S,Hossain M S A 2008 Phys. Rev. B 78 184502

    [17]

    ]Kang W N,Kim H J,Choi E M,Lee S L 2002 Phys. Rev. B 65 64512

    [18]

    ]Takenobu T,Ito T,Chi D H,Prassides K,Iwasa Y 2001 Phys. Rev. B 64 134513

    [19]

    ]Avdeev M,Jorgensen J D,Ribeiro R A,Bud’ko S L,Canfield P C 2003 Physica C 387 301

    [20]

    ]Wang X L,Yao Q W,Horvat J,Qin M J,Dou S X 2004 Supercond. Sci. Technol. 17 L21

    [21]

    ]Wilke R H T,Budko S L,Canfield P C,Finnemore D K 2004 Phys. Rev. Lett. 92 217003

    [22]

    ]Blatter G,Feigelman M V,Geshkenbein V B,Larkin A I,Vinokur V M 1994 Rev. Mod. Phys. 66 1125

    [23]

    ]Wen H H,Schnack H G,Griessen R,Dam B,Rector J 1995 Physica C 241 353

    [24]

    ]Yeoh W K,Dou S X 2007 Physica C 456 170

    [25]

    ]Zeng R,Lu L,Wang J L,Horvat J,Li W X,Shi D Q,Dou S X,Tomsic M,Rindfleisch M 2007 Supercond. Sci. Technol. 20 L43

    [26]

    ]Kazakov S M,Puzniak R,Rogacki K,Mironov A V,Zhigadlo N D,Jun J,Soltmann C,Batlogg B,Karpinski J 2005 Phys. Rev. B 71 024533

    [27]

    ]Rowell J M 2003 Supercond. Sci. Technol. 16 R17

    [28]

    ]Mickelson W,Cumings J,Han W Q,Zettl A 2002 Phys. Rev. B 65 052505

  • [1]

    [1]Nagamatsu J,Nakagawa N,Muranaka T,Zenitani Y,Akimitsu J 2001 Nature 410 63

    [2]

    [2]Tan M Q,Tao X M 2001 Acta Phys. Sin. 50 1193 (in Chinese) [谭明秋、陶向明 2001 物理学报 50 1193]

    [3]

    [3]Yang D S,Wu B M,Li B,Zheng W H,Li S Y,Chen X H,Cao L Z 2003 Acta Phys. Sin. 52 2015 (in Chinese) [杨东升、吴柏枚、李波、郑卫华、李世燕、陈仙辉、曹烈兆 2003 物理学报 52 2015]

    [4]

    [4]Yang H S,Yu M,Li S Y,Li P C,Chai Y S,Zhang L,Chen X H,Cao L Z 2001 Acta Phys. Sin. 50 1197 (in Chinese) [杨宏顺、余旻、李世燕、李鹏程、柴一晟、章良、陈先辉、曹烈兆 2001 物理学报 50 1197]

    [5]

    [5]Shang X F,Tao X M,Chen W B,Chen H X,Wang M,Tan M Q 2008 Acta Phys. Sin. 57 5838 (in Chinese) [尚学府、陶向明、陈文斌、陈会贤、王淼、谭明秋 2008 物理学报 57 5838]

    [6]

    [6]Shi L B,Ren J Y,Zhang F Y,Zhang G H,Yu Z Q 2007 Acta Phys. Sin. 56 5353 (in Chinese) [史力斌、任骏原、张凤云、张国华、余增强 2007 物理学报 56 5353]

    [7]

    [7]Feng W J,Xia T D,Liu T Z,Zhao W J,Wei Z Q 2005 Chin. Phys. 14 2325

    [8]

    [8]Chen R H,Zhu M Y,Li Y,Li W X,Jin H M,Dou S X 2006 Acta Phys. Sin. 55 4878 (in Chinese) [陈荣华、朱明原、李瑛、李文献、金红明、窦士学 2006 物理学报 55 4878]

    [9]

    [9]Zhang X P,Ma Y W,Gao Z S,Yu Z G,K.Watanabe,Wen H H 2006 Acta Phys. Sin. 55 4873 (in Chinese) [张现平、马衍伟、高召顺、禹争光、K.Watanabe、闻海虎 2006 物理学报 55 4873]

    [10]

    ]Dou S X,Soltanian S,Horvat J,Wang X L,Zhou S H,Lonescu M,Liu H K 2002 Appl. Phys. Lett. 81 3419

    [11]

    ]Zhou S H,Pan A V,Qin M J,Liu H K,Dou S X 2003 Physica C 387 321

    [12]

    ]Yamamoto A,Shimoyama J,Ueda S,Iwayama I,Horii S,Kishio K2005 Supercond. Sci. Technol. 18 1323

    [13]

    ]Cheng C H,Yang Y,Munroe P,Zhao Y 2007 Supercond. Sci. Technol. 20 296

    [14]

    ]Qin M J,Wang X L,Liu H K,Dou S X 2002 Phys. Rev. B 65 132508

    [15]

    ]Wang X L,Zeng R,Kim J H,Liu L,Dou S X 2008 Phys. Rev. B 77 174501

    [16]

    ]Ghorbani S R,Wang X L,Dou S X,Lee S,Hossain M S A 2008 Phys. Rev. B 78 184502

    [17]

    ]Kang W N,Kim H J,Choi E M,Lee S L 2002 Phys. Rev. B 65 64512

    [18]

    ]Takenobu T,Ito T,Chi D H,Prassides K,Iwasa Y 2001 Phys. Rev. B 64 134513

    [19]

    ]Avdeev M,Jorgensen J D,Ribeiro R A,Bud’ko S L,Canfield P C 2003 Physica C 387 301

    [20]

    ]Wang X L,Yao Q W,Horvat J,Qin M J,Dou S X 2004 Supercond. Sci. Technol. 17 L21

    [21]

    ]Wilke R H T,Budko S L,Canfield P C,Finnemore D K 2004 Phys. Rev. Lett. 92 217003

    [22]

    ]Blatter G,Feigelman M V,Geshkenbein V B,Larkin A I,Vinokur V M 1994 Rev. Mod. Phys. 66 1125

    [23]

    ]Wen H H,Schnack H G,Griessen R,Dam B,Rector J 1995 Physica C 241 353

    [24]

    ]Yeoh W K,Dou S X 2007 Physica C 456 170

    [25]

    ]Zeng R,Lu L,Wang J L,Horvat J,Li W X,Shi D Q,Dou S X,Tomsic M,Rindfleisch M 2007 Supercond. Sci. Technol. 20 L43

    [26]

    ]Kazakov S M,Puzniak R,Rogacki K,Mironov A V,Zhigadlo N D,Jun J,Soltmann C,Batlogg B,Karpinski J 2005 Phys. Rev. B 71 024533

    [27]

    ]Rowell J M 2003 Supercond. Sci. Technol. 16 R17

    [28]

    ]Mickelson W,Cumings J,Han W Q,Zettl A 2002 Phys. Rev. B 65 052505

  • [1] 果辰, 蔡欣炜, 罗文浩, 黄子耕, 冯庆荣, 甘子钊. 原位电阻测试分析Mg(BH4)2制备MgB2的成相过程. 物理学报, 2021, 70(19): 197401. doi: 10.7498/aps.70.20210620
    [2] 王松, 王星云, 周章渝, 杨发顺, 杨健, 傅兴华. 硼膜制备工艺、微观结构及其在硼化镁超导约瑟夫森结中的应用. 物理学报, 2016, 65(1): 017401. doi: 10.7498/aps.65.017401
    [3] 王春雷, 易晓磊, 姚超, 张谦君, 林鹤, 张现平, 王栋樑, 马衍伟. Ba1-xKxFe2As2单晶(Tc=38.5K)磁通钉扎力与钉扎机理研究. 物理学报, 2015, 64(11): 117401. doi: 10.7498/aps.64.117401
    [4] 王银博, 薛驰, 冯庆荣. 钛离子辐照对MgB2超导薄膜的载流能力和磁通钉扎能力的影响. 物理学报, 2012, 61(19): 197401. doi: 10.7498/aps.61.197401
    [5] 韩晓琴, 蒋利娟, 刘玉芳. MgB和MgB2(1A1)的结构与解析势能函数. 物理学报, 2010, 59(7): 4542-4546. doi: 10.7498/aps.59.4542
    [6] 阮文, 胡强林, 谢安东, 余晓光, 罗文浪, 朱正和. 基态MgB2分子的结构与分析势能函数. 物理学报, 2009, 58(12): 8188-8193. doi: 10.7498/aps.58.8188
    [7] 陈荣华, 朱明原, 李 瑛, 李文献, 金红明, 窦士学. 脉冲磁场处理对碳纳米管掺杂MgB2线材临界电流密度的影响. 物理学报, 2006, 55(9): 4878-4882. doi: 10.7498/aps.55.4878
    [8] 杨东升, 吴柏枚, 李 波, 郑卫华, 李世燕, 樊 荣, 陈仙辉, 曹烈兆. 双能隙超导体MgB2的热导. 物理学报, 2003, 52(3): 683-686. doi: 10.7498/aps.52.683
    [9] 杨东升, 吴柏枚, 李 波, 郑卫华, 李世燕, 陈仙辉, 曹烈兆. MgB2混合态热导率的反常增强. 物理学报, 2003, 52(8): 2015-2019. doi: 10.7498/aps.52.2015
    [10] 吴柏枚, 李 波, 杨东升, 郑卫华, 李世燕, 曹烈兆, 陈仙辉. 新型超导体MgB2和MgCNi3热、电输运性质研究. 物理学报, 2003, 52(12): 3150-3154. doi: 10.7498/aps.52.3150
    [11] 张杰, 雒建林, 白海洋, 陈兆甲, 林德华, 车广灿, 任治安, 赵忠贤, 金铎. 常压和高压合成MgB2的低温比热及两个超导能隙研究. 物理学报, 2002, 51(2): 342-346. doi: 10.7498/aps.51.342
    [12] 王智河, 曹效文, 陈敬林, 李可斌. YBa2Cu3O7-δ外延薄膜的有效钉扎势. 物理学报, 1998, 47(10): 1720-1726. doi: 10.7498/aps.47.1720
    [13] 曾朝阳, 丁世英, 邱里, 姚希贤, 杨宏川, 傅耀先, 蔡传兵. 高Jc熔融织构YBa2Cu3Oy块材的磁性质与钉扎机制. 物理学报, 1995, 44(3): 460-470. doi: 10.7498/aps.44.460
    [14] 胡刚进, 方明虎, 李钟贤, 曾兴斌, 陈南松, 焦正宽, 张其瑞, 张贻瞳, 金新, 姚希贤. YBa2Cu3Oy中氧缺位的磁通钉扎效应. 物理学报, 1993, 42(10): 1669-1673. doi: 10.7498/aps.42.1669
    [15] 金新, 张贻瞳, 陆瑞熙, 姚希贤, 刘奉生, 牟慧麟, 吴晓祖, 周廉. Yba2Cu3O7-δ不可逆线与钉扎势的关联. 物理学报, 1992, 41(1): 123-127. doi: 10.7498/aps.41.123
    [16] 丁世英, 史可信, 曾朝阳, 余正, 施智祥, 邱里. Tl2Ba2Ca2Cu3Oy超导体磁通钉扎能的分布. 物理学报, 1991, 40(6): 985-989. doi: 10.7498/aps.40.985
    [17] 金新, 张贻瞳, 鹿牧, 张长贵, 颜涌, 于杨, 沈剑沧, 姚希贤. (BiPb)-Sr-Ca-Cu-O2223相高Tc超导体磁通钉扎与蠕动. 物理学报, 1991, 40(4): 630-633. doi: 10.7498/aps.40.630
    [18] 丁世英, 施智祥, 颜家烈, 余正, 史可信, 童红武, 邱里. Tl2Ba2Ca2Cu3Oy超导体低场钉扎力的性质. 物理学报, 1990, 39(12): 1999-2004. doi: 10.7498/aps.39.1999
    [19] 丁世英, 余正, 史可信. 非理想平面散射中心的磁通钉扎. 物理学报, 1987, 36(12): 1635-1639. doi: 10.7498/aps.36.1635
    [20] 蔡学榆, 尹道乐, 李传义. A-15超导材料的高场钉扎机制. 物理学报, 1983, 32(9): 1183-1186. doi: 10.7498/aps.32.1183
计量
  • 文章访问数:  6865
  • PDF下载量:  527
  • 被引次数: 0
出版历程
  • 收稿日期:  2009-07-15
  • 修回日期:  2009-09-08
  • 刊出日期:  2010-05-15

/

返回文章
返回