He+辐照对Ga0.94Mn0.06As薄膜铁磁性的改善

丁斌峰 相凤华 王立明 王洪涛

引用本文:
Citation:

He+辐照对Ga0.94Mn0.06As薄膜铁磁性的改善

丁斌峰, 相凤华, 王立明, 王洪涛

Amending the ferromagnetic properties of Ga0.94Mn0.06As films by He+ irradiation

Ding Bin-Feng, Xiang Feng-Hua, Wang Li-Ming, Wang Hong-Tao
PDF
导出引用
  • 离子辐照半导体可以很好的改善半导体材料的磁学性质.用He+ 辐照Ga0.94Mn0.06As薄膜,可以较方便的调制Ga0.94Mn0.06As 薄膜中产生铁磁性载体的浓度.由于空穴居间而导致Ga0.94Mn0.06As薄膜的铁磁性, 可以通过He+的辐照来得到改善,其结果是Ga0.94Mn0.06As薄膜的矫顽力可以增加3倍多. 当He+辐照流强增加时, 居里温度和沿着样品面外磁化难轴方向的饱和磁场都减小了. 被辐照的Ga0.94Mn0.06As薄膜的电学性质和结构特征显示, He+辐照Ga0.94Mn0.06As薄膜可以有控制地改善它的铁磁性, 其结果源于He+辐照Ga0.94Mn0.06As薄膜所诱导产生电缺陷对空穴的补偿, 而不是He+辐照改变了Ga0.94Mn0.06As薄膜的结构.
    Ion irradiation of semiconductors is a well understood method to tune the carrier concentration in a controlled manner. We show that the ferromagnetism in Ga0.94Mn0.06As films, known to be hole-mediated, can be modified by He ion irradiation. The coercivity can be increased by more than three times. The magnetization, Curie temperature and the saturation field along the out-of-plane hard axis all decrease as the fluence increases. The electrical and structural characterization of the irradiated Ga0.94Mn0.06As layers indicates that the controlled amending of magnetism results from a compensation of holes by generated electrical defects and not from a structural modification.
    • 基金项目: 国家自然科学基金(批准号: 50802041, 50872050), 国家重点基础研究发展计划(973)项目(批准号: 2011CB832923)和廊坊师范学院重点项目(批准号: LSZZ201101)资助的课题.
    • Funds: Project supported by the National Natural Science Foundation of China (Grant Nos.10875004, 11005005), and the National Basic Research Program of China (Grant No. 2010CB832904).
    [1]

    Fassbender, McCord J 2008 J. Magn. Magn. Mater. 320 579

    [2]

    Chappert C, Bernas H, Ferré J, Kottler V, Jamet J P, Chen Y, Cambril E, Devolder T, Rousseaux F, Mathet V, Launois H 1998 Science 280 1919

    [3]

    Matsukura F, Ohno H, Shen A, Sugawara Y 1998 Phys. Rev. B 57 R2037

    [4]

    Xu Z F, Liu L L, Zhao Y T, Chen L, Zhu J, Wang Y Y, Xiao G Q 2008 Acta Phys. Sin. 57 3833 (in Chinese) [徐忠锋,刘丽莉,赵永涛, 陈亮,朱键,王瑜玉, 肖国青 2008 物理学报 57 3833]]

    [5]

    Ma Y G, He G W, Hu G, Chen Y, Duan X F 2001 Acta Phys. Sin. 51 620 (in Chinese) [马余刚, 何国伟, 胡岗, 陈一, 段晓峰 2002 物理学报 100 620]

    [6]

    Dietl T, Ohno H 2001 Physica E 9 185

    [7]

    Jungwirth T, Sinova J, Mašek J, Kučra J, MacDonald A H 2006 Rev. Mod. Phys. 78 809

    [8]

    Yamanouchi M, Chiba D, Matsukura F, Ohno H 2004 Nature 428 539

    [9]

    Hümpfner S, Sawicki M, Pappert K,Wenisch J, Brunner K, Gould C, Schmidt G, Dietl T, Molenkamp L W 2007 Appl. Phys. Lett. 90 102102

    [10]

    Wunderlich J, Irvine A C, Zemen J, Holy V, Rushforth A W, De Ranieri E, Rana U, Vyborny K, Sinova J, Foxon C T, Campion R P, Williams D A, Gallagher B L, Jungwirth T 2007 Phys. Rev. B 76 054424

    [11]

    Pearton S J 1990 Mater. Sci. Rep. 4 313

    [12]

    Deenapanray P N K, Gao Q, Jagadish C 2003 J. Appl. Phys. 93 9123

    [13]

    Dietl T, Ohno H, Matsukura F, Cibert J, Ferr D 2000 Science 287 1019

    [14]

    Thevenard L,Mauguin O, Largeau L, Theys B, Lema?itre A 2005 Appl. Phys. Lett. 87 182506

    [15]

    Thevenard L, Largeau L, Mauguin O, Lema?itre A, Khazen Kh, Bardeleben H J 2007 Phys. Rev. B 75 195218

    [16]

    Van Esch A, Van Bockstal L, De Boeck J, Verbanck G, Steenbergen A S,Wellmann P J, Grietens B, Bogaerts R, Herlach F, Borghs G 1997 Phys. Rev. B 56 13103

    [17]

    Yoon I T, Kang T W, Kim K H, Kim D J 2005 J. Appl. Phys. 97 063902

    [18]

    Oiwa A, Katsumoto S, Endo A, Hirasawa M, Iye Y, Ohno H, Matsukura F, Shen A, Sugawara Y 1997 Solid State Commun. 103 209

    [19]

    Omiya T, Matsukura F, Dietl T, Ohno Y, Sakon T, Motokawa M, Ohno H 2000 Physica E 7 976

    [20]

    Wang K Y, Edmonds K W, Campion R P, Zhao L X, Foxon C T, Gallagher B L 2005 Phys. Rev. B 72 085201

    [21]

    Iye Y, Oiwa A, Endo A, Katsumoto S,Matsukura F, Shen A, Ohno H, Munekata H 1999 Mater. Sci. Eng. B 63 88

    [22]

    Edmonds K W, Campion R P, Wang K -Y, Neumann A C, Gallagher B L, Foxon C T, Main P C 2003 J. Appl. Phys. 93 6787

    [23]

    Ziegler J F, Biersack J P, Littmark U 1985 The Stopping, Range of Ions in Solids, Pergamon, New York

    [24]

    Carmeli I, Bloom F, Gwinn E G, Kreutz T C, Scoby C, Gossard A C 2006 Appl. Phys. Lett. 89 112508

    [25]

    Kreutz T C, Artzi R, Gwinn E G, Naaman R, Pizem H, Sukenik C N 2003 Appl. Phys. Lett. 83 4211-3

    [26]

    Wang B, Zhao YW, Dong Z Y, Deng A H,Miao S S, Yang J 2007 Acta Phys. Sin. 56 1603 (in Chinese) [王博, 赵有文, 董志远, 邓爱红, 苗杉杉, 杨 俊 2007 物理学报 56 1603]

  • [1]

    Fassbender, McCord J 2008 J. Magn. Magn. Mater. 320 579

    [2]

    Chappert C, Bernas H, Ferré J, Kottler V, Jamet J P, Chen Y, Cambril E, Devolder T, Rousseaux F, Mathet V, Launois H 1998 Science 280 1919

    [3]

    Matsukura F, Ohno H, Shen A, Sugawara Y 1998 Phys. Rev. B 57 R2037

    [4]

    Xu Z F, Liu L L, Zhao Y T, Chen L, Zhu J, Wang Y Y, Xiao G Q 2008 Acta Phys. Sin. 57 3833 (in Chinese) [徐忠锋,刘丽莉,赵永涛, 陈亮,朱键,王瑜玉, 肖国青 2008 物理学报 57 3833]]

    [5]

    Ma Y G, He G W, Hu G, Chen Y, Duan X F 2001 Acta Phys. Sin. 51 620 (in Chinese) [马余刚, 何国伟, 胡岗, 陈一, 段晓峰 2002 物理学报 100 620]

    [6]

    Dietl T, Ohno H 2001 Physica E 9 185

    [7]

    Jungwirth T, Sinova J, Mašek J, Kučra J, MacDonald A H 2006 Rev. Mod. Phys. 78 809

    [8]

    Yamanouchi M, Chiba D, Matsukura F, Ohno H 2004 Nature 428 539

    [9]

    Hümpfner S, Sawicki M, Pappert K,Wenisch J, Brunner K, Gould C, Schmidt G, Dietl T, Molenkamp L W 2007 Appl. Phys. Lett. 90 102102

    [10]

    Wunderlich J, Irvine A C, Zemen J, Holy V, Rushforth A W, De Ranieri E, Rana U, Vyborny K, Sinova J, Foxon C T, Campion R P, Williams D A, Gallagher B L, Jungwirth T 2007 Phys. Rev. B 76 054424

    [11]

    Pearton S J 1990 Mater. Sci. Rep. 4 313

    [12]

    Deenapanray P N K, Gao Q, Jagadish C 2003 J. Appl. Phys. 93 9123

    [13]

    Dietl T, Ohno H, Matsukura F, Cibert J, Ferr D 2000 Science 287 1019

    [14]

    Thevenard L,Mauguin O, Largeau L, Theys B, Lema?itre A 2005 Appl. Phys. Lett. 87 182506

    [15]

    Thevenard L, Largeau L, Mauguin O, Lema?itre A, Khazen Kh, Bardeleben H J 2007 Phys. Rev. B 75 195218

    [16]

    Van Esch A, Van Bockstal L, De Boeck J, Verbanck G, Steenbergen A S,Wellmann P J, Grietens B, Bogaerts R, Herlach F, Borghs G 1997 Phys. Rev. B 56 13103

    [17]

    Yoon I T, Kang T W, Kim K H, Kim D J 2005 J. Appl. Phys. 97 063902

    [18]

    Oiwa A, Katsumoto S, Endo A, Hirasawa M, Iye Y, Ohno H, Matsukura F, Shen A, Sugawara Y 1997 Solid State Commun. 103 209

    [19]

    Omiya T, Matsukura F, Dietl T, Ohno Y, Sakon T, Motokawa M, Ohno H 2000 Physica E 7 976

    [20]

    Wang K Y, Edmonds K W, Campion R P, Zhao L X, Foxon C T, Gallagher B L 2005 Phys. Rev. B 72 085201

    [21]

    Iye Y, Oiwa A, Endo A, Katsumoto S,Matsukura F, Shen A, Ohno H, Munekata H 1999 Mater. Sci. Eng. B 63 88

    [22]

    Edmonds K W, Campion R P, Wang K -Y, Neumann A C, Gallagher B L, Foxon C T, Main P C 2003 J. Appl. Phys. 93 6787

    [23]

    Ziegler J F, Biersack J P, Littmark U 1985 The Stopping, Range of Ions in Solids, Pergamon, New York

    [24]

    Carmeli I, Bloom F, Gwinn E G, Kreutz T C, Scoby C, Gossard A C 2006 Appl. Phys. Lett. 89 112508

    [25]

    Kreutz T C, Artzi R, Gwinn E G, Naaman R, Pizem H, Sukenik C N 2003 Appl. Phys. Lett. 83 4211-3

    [26]

    Wang B, Zhao YW, Dong Z Y, Deng A H,Miao S S, Yang J 2007 Acta Phys. Sin. 56 1603 (in Chinese) [王博, 赵有文, 董志远, 邓爱红, 苗杉杉, 杨 俊 2007 物理学报 56 1603]

  • [1] 但敏, 陈伦江, 贺岩斌, 吕兴旺, 万俊豪, 张虹, 张珂嘉, 杨莹, 金凡亚. H+离子辐照Y0.5Gd0.5Ba2Cu3O7-δ超导层中的缺陷演化. 物理学报, 2023, 0(0): 0-0. doi: 10.7498/aps.72.20221612
    [2] 祝鑫强, 王剑, 朱璨, 罗丰, 陈树权, 徐佳辉, 徐峰, 王嘉赋, 张艳, 孙志刚. Co3Sn2S2单晶的磁性和电-热输运性能. 物理学报, 2023, 72(17): 177102. doi: 10.7498/aps.72.20230621
    [3] 但敏, 陈伦江, 贺岩斌, 吕兴旺, 万俊豪, 张虹, 张珂嘉, 杨莹, 金凡亚. H+离子辐照Y0.5Gd0.5Ba2Cu3O7–δ超导层中的缺陷演化. 物理学报, 2022, 71(23): 237401. doi: 10.7498/aps.71.20221612
    [4] 郑翠红, 杨剑, 谢国锋, 周五星, 欧阳滔. 离子辐照对磷烯热导率的影响及其机制分析. 物理学报, 2022, 71(5): 056101. doi: 10.7498/aps.71.20211857
    [5] 郑翠红, 杨剑, 谢国锋, 周五星, 欧阳滔. 离子辐照对磷烯热导率的影响及其机制分析. 物理学报, 2021, (): . doi: 10.7498/aps.70.20211857
    [6] 何斌, 何雄, 刘国强, 朱璨, 王嘉赋, 孙志刚. SnSe2的忆阻及磁阻效应. 物理学报, 2020, 69(11): 117301. doi: 10.7498/aps.69.20200160
    [7] 李明阳, 张雷敏, 吕沙沙, 李正操. 离子辐照和氧化对IG-110核级石墨中的点缺陷的影响. 物理学报, 2019, 68(12): 128102. doi: 10.7498/aps.68.20190371
    [8] 卞西磊, 王刚. 非晶合金的离子辐照效应. 物理学报, 2017, 66(17): 178101. doi: 10.7498/aps.66.178101
    [9] 谢玲玲, 陈水源, 刘凤金, 张建敏, 林应斌, 黄志高. Zn0.97Cr0.03O的PLD制备及其铁磁性. 物理学报, 2014, 63(7): 077102. doi: 10.7498/aps.63.077102
    [10] 赵翠莲, 甄聪棉, 马丽, 潘成福, 侯登录. Ge纳米结构的形貌与铁磁性研究. 物理学报, 2013, 62(3): 037502. doi: 10.7498/aps.62.037502
    [11] 肖振林, 史力斌. 利用第一性原理研究Ni掺杂ZnO铁磁性起源. 物理学报, 2011, 60(2): 027502. doi: 10.7498/aps.60.027502
    [12] 林竹, 郭志友, 毕艳军, 董玉成. Cu掺杂的AlN铁磁性和光学性质的第一性原理研究. 物理学报, 2009, 58(3): 1917-1923. doi: 10.7498/aps.58.1917
    [13] 徐忠锋, 刘丽莉, 赵永涛, 陈亮, 朱键, 王瑜玉, 肖国青. 不同能量的高电荷态Ar12+离子辐照对Au纳米颗粒尺寸的影响. 物理学报, 2009, 58(6): 3833-3838. doi: 10.7498/aps.58.3833
    [14] 刘妍妍, 刘发民, 石 霞, 丁 芃, 周传仓. 钙钛矿型纳米BaFeO3的制备、结构表征及铁磁性研究. 物理学报, 2008, 57(11): 7274-7278. doi: 10.7498/aps.57.7274
    [15] 王叶安, 秦福文, 吴东江, 吴爱民, 徐 茵, 顾 彪. 基于电子回旋共振-等离子体增强金属有机物化学气相沉积技术生长GaMnN稀磁半导体的研究. 物理学报, 2008, 57(1): 508-513. doi: 10.7498/aps.57.508
    [16] 王敬平, 孟 健. 磁场下合成Fe3O4粉体的隧道磁阻. 物理学报, 2008, 57(2): 1197-1201. doi: 10.7498/aps.57.1197
    [17] 覃怀莉, 薛建明, 赖江南, 王建勇, 苗 琦, 张伟明, 马 磊, 颜 莎, 赵渭江, 顾红雅, 王宇钢. 拟南芥胚的不同区域对MeV离子辐照的响应. 物理学报, 2006, 55(11): 5991-5995. doi: 10.7498/aps.55.5991
    [18] 孙友梅, 刘 杰, 张崇宏, 王志光, 金运范, 段敬来, 宋 银. 快重离子辐照聚酰亚胺潜径迹的电子能损效应. 物理学报, 2005, 54(11): 5269-5273. doi: 10.7498/aps.54.5269
    [19] 匡安龙, 刘兴翀, 路忠林, 任尚坤, 刘存业, 张凤鸣, 都有为. 稀释磁性半导体Sn1-xMnxO2的室温铁磁性. 物理学报, 2005, 54(6): 2934-2937. doi: 10.7498/aps.54.2934
    [20] 郭忠诚, 郑萍, 王楠林, 陈兆甲, Y. MAENO, Z. Q. MAO. Sr2RuO4正常态的c方向的磁阻的研究. 物理学报, 2001, 50(9): 1824-1828. doi: 10.7498/aps.50.1824
计量
  • 文章访问数:  5753
  • PDF下载量:  315
  • 被引次数: 0
出版历程
  • 收稿日期:  2011-08-19
  • 修回日期:  2011-10-21
  • 刊出日期:  2012-02-05

/

返回文章
返回