Progress of ARPES study on topological semimetals

Deng Tao; Yang Hai-Feng; Zhang Jing; Li Yi-Wei; Yang Le-Xian; Liu Zhong-Kai; Chen Yu-Lin

doi:10.7498/aps.68.20191544

Abstract

Topological semimetal, known as a type of topological quantum materials without energy gap, has attracted lots of research interests due to its unique physical properties such as novel quasiparticles, giant magnetoresistance and large carrier mobility. Topological semimetal can be further classified into topological Dirac semimetal, topological Weyl semimetal, topological nodal-line semimetal and topological semimetals with " new fermions”. The high-resolution angle-resolved photoemission spectroscopy (ARPES) has emerged as a powerful experimental technique to directly visualize the electronic structure and identify the characteristic topological electronic states in topological semimetals. Here we would briefly introduce the ARPES technique and review some of the recent progress of ARPES study on the electronic structures of typical topological semimetals. We would focus mostly on the physics origin and ARPES signature of topological electronic structures and hope the readers would find it interesting and useful in the understanding of this material class which both is important in physics and has promising application potentials.

Keywords:

topological semimetal /
electronic structure /
quantum materials /
angle-resolved photoemission spectroscopy

Authors and contacts

1.
CAS Center for Excellence in Superconducting Electronics (CENSE), State Key Laboratory of Functional Materials for Informatics, Shanghai Institute of Microsystem and Information Technology (SIMIT), Chinese Academy of Sciences, Shanghai 200050, China
2.
University of Chinese Academy of Sciences, Beijing 100049, China
3.
School of Physical Science and Technology, ShanghaiTech University, ShanghaiTech Laboratory for Topological Physics, Shanghai 201210, China
4.
Department of Physics, University of Oxford, Oxford OX1 3PU, United Kingdom
5.
Department of Physics, Tsinghua University, Beijing 100084, China

Corresponding author: Liu Zhong-Kai, liuzhk@shanghaitech.edu.cn ; Chen Yu-Lin, yulin.chen@physics.ox.ac.uk

Funds: Project supported by the National Key Technologies Research and Development program of the Ministry of Science and Technology of China (Grant Nos.2017YFA0305400, 2017YFA0304600) and the National Natural Science Foundation of China (Grant Nos. 11774190, 11674229)

FullText HTML : translate this paragraph

References

[1]	Klitzing K V, Dorda G, Popper M, et al. 1980 Phys. Rev. Lett. 45 494 Google Scholar
[2]	Thouless D J, et al. 1982 Phys. Rev. Lett. 49 405
[3]	Tusi D C, Stormer H L, Gossard A C, et al. 1982 Phys. Rev. Lett. 48 1559 Google Scholar
[4]	Wen X G 1989 Phys. Rev. B 40 7387
[5]	Wen X G 1990 Int. J. Mod. Phys. B 4 239 Google Scholar
[6]	Bernevig B A, Hughes T L, Zhang S C, et al. 2006 Science 314 1757 Google Scholar
[7]	Fu L, Kane C L 2007 Phys. Rev. B 76 045302 Google Scholar
[8]	Moore J E, Balents L 2007 Phys. Rev. B 75 121306 Google Scholar
[9]	Hsieh D, Qian D, Wray L, et al. 2008 Nature 452 970 Google Scholar
[10]	Chen Y L, Analytis J G, Chu J H, et al. 2009 Science 325 178 Google Scholar
[11]	Wan X G, Turner A M, Vishwanath A, et al. 2011 Phys. Rev. B 83 205101 Google Scholar
[12]	Wang Z J, Sun Y, Chen X Q, et al. 2012 Phys. Rev. B 85 195320 Google Scholar
[13]	Young S M, Zaheer S, Teo J C Y, et al. 2012 Phys. Rev. Lett. 108 140405 Google Scholar
[14]	Dirac P A M 1928 Proc. R. Soc. A 117 610 Google Scholar
[15]	Weyl H 1929 Proc. Natl. Acad. Sci. U.S.A. 15 323 Google Scholar
[16]	Borisenko S, Gibson Q, Evtushinsky D, et al. 2014 Phys. Rev. Lett. 113 027603 Google Scholar
[17]	Liu Z K, Jiang J, Zhou B, et al. 2014 Nat. Mater. 13 677 Google Scholar
[18]	Liu Z K, Zhou B, Zhang Y, et al. 2014 Science 343 864 Google Scholar
[19]	Neupane M, Xu S Y, Sankar R, et al. 2014 Nat. Commun. 5 3786 Google Scholar
[20]	Xu S Y, Belopolski I, Alidoust N, et al. 2015 Science 349 6248
[21]	Damascelli A, Hussain Z, Shen Z X 2003 Rev. Mod. Phys. 75 473 Google Scholar
[22]	Chen Y L 2012 Front. Phys. 7 175
[23]	Penn D R 1987 Phys. Rev. B 35 482 Google Scholar
[24]	Powell C J, Jablonski A, Tilinin I S, et al. 1999 J. Electron. Spectrosc. Relat. Phenom. 98-99
[25]	Clark D T, Thomas H R 1977 J. Polym. Sci., Part A: Polym. Chem. 15 2843 Google Scholar
[26]	Nicholson A J C 1970 Appl. Opt. 9 1155 Google Scholar
[27]	Elder F R, Gurewitsch A M, Langmuir R V, et al. 1947 Phys. Rev. 71 829
[28]	Huffman R E, Tanaka Y, Larrabee J C 1963 Appl. Opt. 2 617 Google Scholar
[29]	Carmignani N 2016 Touschek Lifetime Studies and Optimization of the European Synchrotron Radiation Facility 1
[30]	Xu S Y, Liu C, Kushwaha S K, et al. 2015 Science 347 294 Google Scholar
[31]	Liang A J, Chen C Y, Wang Z J, et al. 2016 Chin. Phys. B 25 077101 Google Scholar
[32]	Yi H M, Wang Z J, Chen C Y, et al. 2014 Sci. Rep. 4 6106
[33]	Wang Z J, Weng H M, Wu Q S, et al. 2013 Phys. Rev. B 88 125427 Google Scholar
[34]	Wu M, Zheng G L, Chu W W, et al. 2018 Phys. Rev. B 98 161110 Google Scholar
[35]	Zhang C, Zhang Y, Yuan X, et al. 2019 Nature 565 331 Google Scholar
[36]	Zhang K N, Yan M Z, Zhang H X, et al. 2017 Phys. Rev. B 96 125102 Google Scholar
[37]	Li Y W, Xia Y Y Y, Ekahana S A, et al. 2017 Phys. Rev. Mater. 1 074202 Google Scholar
[38]	Yan M Z, Huang H Q, Zhang K N, et al. 2017 Nat. Commun. 8 257 Google Scholar
[39]	Bahramy M S, Clark O J, Yang B J, et al. 2017 Nat. Mater. 17 21
[40]	Noh H J, Jeong J, Cho E J, et al. 2017 Phys. Rev. Lett. 119 016401 Google Scholar
[41]	Fei F C, Bo X Y, Wang R, et al. 2017 Phys. Rev. B 96 041201 Google Scholar
[42]	Xiao R C, Gong P L, Wu Q S, et al. 2017 Phys. Rev. B 96 075101 Google Scholar
[43]	Tang P Z, Zhou Q, Xu G, et al. 2016 Nat. Phys. 12 1100 Google Scholar
[44]	Emmanouilidou E, Cao H B, Tang P Z, et al. 2017 Phys. Rev. B 96 224405 Google Scholar
[45]	Kang M G, Ye L D, Fang S A, et al. 2019 arXiv: 1906.02167
[46]	Lin Z Y, Wang C Z, Wang P D, et al. 2019 arXiv: 1906.05755
[47]	Soh J R, Juan F, Vergniory M G, et al. 2019 arXiv: 1901.10022 v
[48]	Ma J Z, Nie S M, Yi C J, et al. 2019 Sci. Adv. 5 eaaw4718 Google Scholar
[49]	Su H, Gong B C, Shi W J, et al. 2019 arXiv: 1903.12532
[50]	Hua G Y, Nie S M, Song Z D, et al. 2018 Phys. Rev. B 98 201116 Google Scholar
[51]	Xu G, Weng H M, Wang Z J, et al. 2011 Phys. Rev. Lett. 107 186806 Google Scholar
[52]	Lv B Q, Weng H M, Fu B B, et al. 2015 Phys. Rev. X 5 031013
[53]	Lv B Q, et al. 2015 Phys. Rev. Lett. 115 217601; 2015 Nat. Phys. 11 724 Google Scholar
[54]	Yang L X, Liu Z K, Sun Y, et al. 2015 Nat. Phys. 11 728
[55]	Liu Z K, Yang L X, Sun Y, et al. 2016 Nat. Mater. 15 27 Google Scholar
[56]	Weng H M, Fang C, Fang Z, et al. 2015 Phys. Rev. X 5 011029
[57]	Xu S Y, Belopolski I, Sanchez D S, et al. 2015 Sci. Adv. 1 e1501092 Google Scholar
[58]	Xu S Y, Belopolski I, Sanchez D S, et al. 2015 arXiv: 1509.07465
[59]	Xu S Y, Alidoust N, Belopolski I, et al. 2015 Nat. Phys. 11 748 Google Scholar
[60]	Kuroda K,Tomita T, Suzuki M T, et al. 2017 Nat. Mater. 16 1090 Google Scholar
[61]	Liu D F, Liang A J, Liu E K, et al. 2019 Science 365 1282 Google Scholar
[62]	Morali Noam, Batabyal Rajib, Nag P K, et al. 2019 Science 365 1286 Google Scholar
[63]	Soluyanov A A, Gresch D, Wang Z J, et al. 2015 Nature 527 495 Google Scholar
[64]	Sun Y, Wu S C, Ali M N, et al. 2015 Phys. Rev. B 92 161107 Google Scholar
[65]	Wang Z J, Gresch D, Soluyanov A A, et al. 2016 Phys. Rev. Lett. 117 056805 Google Scholar
[66]	Tamai A, Wu Q S, Cucchi I, et al. 2016 Phys. Rev. X 6 031021
[67]	Deng K, Wan G L, Deng P, et al. 2016 Nat. Phys. 12 1105 Google Scholar
[68]	Jiang J, Liu Z K, Sun Y, et al. 2017 Nat. Commun. 8 13973 Google Scholar
[69]	Huang L, McCormick T M, Ochi M, et al. 2016 Nat. Mater. 15 1155 Google Scholar
[70]	Rüßmann P, Weber A P, Glott F, et al. 2018 Phys. Rev. B 97 075106 Google Scholar
[71]	Wang Z J, Alexandradinata A, Robert J C 2016 Nature 532 189 Google Scholar
[72]	Xu N, Wang Z J, Weber A P, et al. 2016 arXiv: 1604.02116
[73]	Berger A N, Andrade E, Kerelsky A, et al. 2018 npj Quantum Mater. 3 2 Google Scholar
[74]	Yao M Y, Xu N,Wu Q S, et al. 2019 Phys. Rev. Lett. 122 176402 Google Scholar
[75]	Liang A J, Huang J W, Nie S M, et al. 2016 arXiv: 1604.01706
[76]	Sakano M, Bahramy M S, Tsuji H, et al. 2017 Phys. Rev. B 95 121101 Google Scholar
[77]	Wan G L, Yao W, Zhang K N, et al. 2017 arXiv: 1710.00350
[78]	Weber A P, Rüßmann P, Xu N, et al. 2018 Phys. Rev. Lett. 121 156401 Google Scholar
[79]	Chang T R, Xu S Y, Chang G Q, et al. 2016 Nat. Commun. 7 10639 Google Scholar
[80]	Belopolski I, Xu S Y, Ishida Y, et al. 2016 Phys. Rev. B 94 085127 Google Scholar
[81]	Pletikosić I, Ali M N, Fedorov A V, et al. 2014 Phys. Rev. Lett. 113 216601 Google Scholar
[82]	Jiang J, Tang F, Pan X C, et al. 2015 Phys. Rev. Lett. 115 166601 Google Scholar
[83]	Wu Y, Jo N H, Ochi M, et al. 2015 Phys. Rev. Lett. 115 166602 Google Scholar
[84]	Xu S Y, Alidoust N, Chang G Q, et al. 2017 Sci. Adv. 3 e1603266 Google Scholar
[85]	Belopolski I, Yu P, Sanchez D S, et al. 2017 Nat. Commun. 8 942 Google Scholar
[86]	Koepernik K, Kasinathan D, Efremov D V, et al. 2016 Phys. Rev. B 93 201101 Google Scholar
[87]	Haubold E, Koepernik K, Efremov D, et al. 2017 Phys. Rev. B 95 241108 Google Scholar
[88]	Heikkilä T T, Volovik G E 2015 New J. Phys. 17 093019 Google Scholar
[89]	Winkler G W, Wu Q S, Troyer M, et al. 2016 Phys. Rev. Lett. 117 076403 Google Scholar
[90]	Hyart T, Heikkilä T T 2016 Phys. Rev. B 93 235147 Google Scholar
[91]	Weng H M, Fang C, Fang Z, et al. 2016 Phys. Rev. B 93 241202 Google Scholar
[92]	Bradlyn B, Cano J, Wang Z J, et al. 2016 Science 353 558
[93]	Zhu Z M, Winkler G W, Wu Q S, et al. 2016 Phys. Rev. X 6 031003
[94]	Weng H M, Fang C, Fang Z, et al. 2016 Phys. Rev. B 94 165201 Google Scholar
[95]	Chang G Q, Xu S Y, Huang S M, et al. 2017 Sci. Rep. 7 1688 Google Scholar
[96]	Lv B Q, Feng Z L, Xu Q N, et al. 2017 Nature 546 627 Google Scholar
[97]	Rao Z C, Li H, Zhang T T, et al. 2019 Nature 567 496 Google Scholar
[98]	Sanchez D S, Belopolski I, Cochran T A, et al. 2019 Nature 567 500 Google Scholar
[99]	Schröter N B M, Pei D, Vergniory M G, et al. 2019 Nat. Phys. 15 759 Google Scholar
[100]	Lv B Q, Feng Z L, Zhao J Z, et al. 2019 Phys. Rev. B 99 241104 Google Scholar
[101]	Fang C, Weng H M, Dai X, et al. 2016 Chin. Phys. B 25 117106 Google Scholar
[102]	Burkov A A, Hook M D, Balents L, et al. 2011 Phys. Rev. B 84 235126 Google Scholar
[103]	Feng B J, Fu B T, Kasamatsu S, et al. 2017 Nat. Commun. 8 1007 Google Scholar
[104]	Lian J L, Yu L X, Liang Q F, et al. 2019 npj Comput. Mater. 10 1
[105]	Bian G, Chang T R, Sankar R, et al. 2016 Nat. Commun. 7 10556 Google Scholar
[106]	Wu Y, Wang L L, Mun E, et al. 2016 Nat. Phys. 12 667 Google Scholar
[107]	Wu Y, Jo N H, Wang L L, et al. 2019 Phys. Rev. B 99 161113(R)Google Scholar
[108]	Neupane M, Belopolski I, Hosen M M, et al. 2016 Phys. Rev. B 93 201104 Google Scholar
[109]	Takane D, Wang Z W, Souma S, et al. 2016 Phys. Rev. B 94 121108 Google Scholar
[110]	Chen C, Xu X, Jiang J, et al. 2017 Phys. Rev. B 95 125126 Google Scholar
[111]	Hosen M M, Dimitri K, Belopolski I, et al. 2017 Phys. Rev. B 95 161101 Google Scholar
[112]	Xu X, Jiang J, Shi W J, et al. 2019 Phys. Rev. B 99 195106 Google Scholar
[113]	Ekahana S A, Wu S C, Jiang J, et al. 2017 New J. Phys. 19 065007 Google Scholar
[114]	Li R H, Ma H, Cheng X Y, et al. 2016 Phys. Rev. Lett. 117 096401 Google Scholar
[115]	Xu Q N, Song Z D, Nie S M, et al. 2015 Phys. Rev. B 92 205310 Google Scholar
[116]	Fu B B, Yi C J, Zhang T T, et al. 2019 Sci. Adv. 645 eaau6459
[117]	Belopolski I, Manna K, Sanchez D S, et al. 2019 Science 365 1278 Google Scholar
[118]	Takane D, Souma S, Nakayama K, et al. 2018 Phys. Rev. B 98 041105(R)Google Scholar
[119]	Liu Z H, Lou R, Guo P J, et al. 2018 Phys. Rev. X 8 031044
[120]	Yi C J, Lv B Q, Wu Q S, et al. 2018 Phys. Rev. B 97 201107(R)Google Scholar
[121]	Lou R, Guo P J, Li M, et al. 2018 npj Quantum Mater. 43 1
[122]	Yang H F, Yang L X, Liu Z K, et al. 2019 Nat. Commun. 10 3478 Google Scholar
[123]	Tang S J, Zhang C F, Wong D, et al. 2017 Nat. Phys. 13 684
[124]	Šmejkal L, Železný J, Sinova J, et al. 2017 Phys. Rev. Lett. 118 106402 Google Scholar
[125]	Sun Yan, Wu S C, Yan B H, et al. 2015 Phys. Rev. B 92 115428 Google Scholar
[126]	Qian X F, Liu J W, Fu L, et al. 2014 Science 346 1344 Google Scholar
[127]	Wu S F, Fatemi V, Gibson Q D, et al. 2018 Science 359 76 Google Scholar

Cited By

图 1 (a)光电子能谱实验原理示意图; (b)光电子非弹性平均自由程与能量关系图; (c)光电效应过程的能量关系图示; (d) ARPES测量不同k_z等能面示意图

Figure 1. (a) Illustration of a photoemission experiment; (b) curve of electric IMFP vs energy; (c) energetics of the photoemission process; (d) illustration different FSs measured by ARPES under different photon energies due to the k_z dispersion in k-space of a 3D Fermi Surface.

DownLoad: Full-Size Img PowerPoint

图 2 上海光源中同步辐射束线BL03U搭载的空间分辨角分辨光电子能谱实验工作站图

Figure 2. A picture of the synchrotron-based nano-ARPES workstation in SSRF BL03U.

DownLoad: Full-Size Img PowerPoint

图 3 (a)三维狄拉克费米子在能-动量四维空间示意图及其在不同三维能-动量子空间的投影; (b) Na₃Bi的晶体结构示意图; (c) Na₃Bi的第一布里渊区示意图; (d)在三维动量空间中的实验测量费米面(上半图)及其在表面布里渊区的投影(下半图) (e) (f)狄拉克点处沿k^D_y–k^D_x和k^D_y–k^D_z方向的三维光电子谱图

Figure 3. (a) Illustration of a 3D Dirac Fermion in 4D energy-momentum space and its projection onto different 3D subspace; (b) the crystal structure of Na₃Bi; (c) 1^st Brillouin zone of Na₃Bi; (d) measured Fermi surface map across the whole 3D BZ (top panel) and its projection on the surface BZ (bottom panel) on pristine surfaces. 3D intensity plot of the photoemission spectra (e) along the k^D_y–k^D_x direction and (f) along the k^D_y–k^D_z direction at the Dirac point.

DownLoad: Full-Size Img PowerPoint

图 4 (a)沿(100)解理的Na₃Bi费米面示意图; (b) ARPES实验测得的费米面图像; (c)图(b)中沿α方向切出的能谱; (d)费米弧的理论自旋织构图; (e)沿$\bar A - {{\bar \Gamma }} - {{\bar X}}$方向的能带结构图; (f) k_y = 0时图(c)对应的$\bar K - \bar \varGamma - \bar K$方向理论计算投影能谱

Figure 4. (a) Schematic of Fermi surface in Na₃Bi cleaved along (100) direction; (b) Fermi surface measured by ARPES experiment; (c) spectrum cut along α from (b); (d) theoretical calculated spin texture of Fermi arcs; (e) band structure along $\bar A - \bar \varGamma - \bar K$; (f) calculated $\bar K - \bar \varGamma - \bar K$ projected bands corresponding to (c) when k_y = 0.

DownLoad: Full-Size Img PowerPoint

图 5 第二类狄拉克锥的三维示意图　(a)投影在k_x–k_y–E空间上的第二类狄拉克锥简图; (b) PtSe₂中k_x–k_y面内切过第二类体狄拉克点的三维色散能谱图(光能24 eV), 狄拉克点由紫色箭头指出; (c)放大的图(b)中ARPES等能面堆叠图; (d)投影在k_y–k_z–E空间上的第二类狄拉克锥简图; (e)三维k_z依赖的色散能谱图(光能18—33 eV); (f)放大的图(e)中ARPES等能面堆叠图

Figure 5. 3D visualization of type-II Dirac cone: (a) Schematic of type-II Dirac cone projected on k_x-k_y-E space; (b) 3D ARPES map (hν = 24 eV) which slices through the type-II BDP (pointed out by magenta arrow); (c) zoomed-in ARPES constant energy contours (CECs) of Fig.(b); (d) schematic of type-II Dirac cone projected on k_x–k_z–E space; (e) 3D k_z-dependent map (hν = 18–33 eV); (f) zoomed-in ARPES CECs of Fig. (e).

DownLoad: Full-Size Img PowerPoint

图 6 (a) PdTe₂型材料的晶体结构(及其俯视图)和(b)第一布里渊区(蓝色所示为(001)表面布里渊区); (c)忽略杂化和(d)考虑杂化时晶体场产生的能级随k_z动量变化的演化, A₁与E产生的能级在绿点处出现受保护的交界点; (e)沿Γ-A-Γ方向的ARPES能谱(横轴为光能80−132 eV对应的k_z区间), 黄线为理论计算的能带; (f)沿表面布里渊区$\bar M - \bar \varGamma - \bar M$方向的ARPES能谱(光能27 eV), 小图为24 eV时的局部放大图; (g)理论计算的表面布里渊区能带投影图

Figure 6. (a) Crystal structure (with its top view) and (b) 1^st Brillouin zone (with surface BZ marked in blue) of PtTe₂; (c) (d) evolution of crystal-field-derived levels with the out-of-plane k_z momentum when hybridization is (c)neglected or (d)included, showing a protected crossing of the A₁ and E-derived levels; (e) ARPES spectrum along Γ-A-Γ direction (k_z corresponding to hv = 80−132 eV) with calculated bands (yellow lines) attached; (f) ARPES spectrum along $\bar M - \bar \varGamma - \bar M$ direction (hv = 27 eV); (g) calculated energy bands projected on surface Brillouin zone.

DownLoad: Full-Size Img PowerPoint

图 7 (a) TaAs的晶体结构; (b)有自旋极化费米弧的外尔半金属电子结构图示(红色和蓝色分别代表不同的手性. 为清晰起见, 图中只画出了顶面和底面的表面态); (c)理论计算的第一布里渊区中外尔费米子及费米弧位置及其(ii)俯视图, (iii)为费米能级处k_y–k_z面上(k_x = 0)光电子强度谱的等能面能谱, 绿线为k_y–k_z面上的布里渊区边线; (d)ARPES实验(光能36 eV)所得的k_x–k_y费米面; (e)选取闭合路径计算能带穿越费米面数目的示意图, 紫色及蓝色圆点代表能带穿越$\bar \varGamma - \bar X - \bar M - \bar \varGamma $和$\bar \varGamma - \bar Y - \bar M - \bar \varGamma $闭合回路的位置; (f)费米面上W1外尔点附近理论计算的局部放大图; (g)理论计算的费米面上表面态自旋织构(白色箭头为面内自旋极化方向); (h)沿图(g)中C1, C2在P_z方向的角分辨自旋极化情况

Figure 7. (a) Crystal structure of TaAs; (b) schematic of a WSM electronic structure with spin-polarized Fermi arcs connecting projections of two bulk Weyl nodes (The red and blue colors represent opposite chirality. For clarity, only surface states on the top and bottom surfaces are indicated); (c) (i) calculated position of Weyl Fermions and Fermi arcs in 1^st BZ with its (ii) top view; (iii) shows the photoemission intensity plot at E_F in the k_y–k_z plane at k_x = 0 (The green lines represent the BZ structure in the k_y–k_z plane.); (d) Fermi surface measured by ARPES experiment (hv = 36 eV); (e) illustration of band numbers crossing an arbitrary k loop. Blue and magenta circles indicate the locations where the bands cross the enclosed k loop $\bar \varGamma - \bar X - \bar M - \bar \varGamma $ and $\bar \varGamma - \bar Y - \bar M - \bar \varGamma $ at E_F, respectively. (f) zoomed-in experimental and theoretical Fermi surface near W1 Weyl point (spin polarizations of Fermi arc marked by red arrows); (g) theoretical spin texture of surface states on Fermi surface (spin polarization indicated by white arrows); (h) angle-resolved spin polarizations along C1, C2 (marked in Fig. (g) with white lines) in the z direction.

DownLoad: Full-Size Img PowerPoint

图 8 软X射线ARPES下TaAs中体外尔锥和外尔点观测图　(a) k_z穿过外尔点W1时候采得的费米面及其理论简图; (b) (i)沿图(a)中cut1, cut2方向切出的角分辨光电子能谱图; (c) k_z穿过外尔点W2时候采得的费米面及沿cut3方向切出的能谱; 过外尔点W1, W2均可看到线性色散外尔锥

Figure 8. Observation of bulk Weyl cones and Weyl nodes in TaAs using SX-ARPES: (a) Measured and first principles calculated k_x-k_y Fermi surface maps at the k_z value that corresponds to the W1 Weyl nodes; (b) ARPES spectra cut along (i)cut1 and (ii)cut2 from Fig. (a); (c) measured k_x-k_y Fermi surface maps at the k_z value that corresponds to the W2 Weyl nodes as well as the spectrum cut along cut3. Linearly dispersive Weyl cones of both W1 and W2 can be observed.

DownLoad: Full-Size Img PowerPoint

图 9 (a) TaAs家族中不同自旋轨道耦合强度材料中手性相反外尔点的位置演化图; (b)—(d)高分辨ARPES测量的NbP, TaP和TaAs的(i)勺状费米面以及(ii) (iii)沿C1, C2红虚线方向的能谱; (ΔK₁和ΔK₂分布代表外尔点、费米弧的分离程度); (e)统计得到的ΔK₁和ΔK₂随三种不同材料自旋轨道耦合强度变化图像

Figure 9. (a) Illustration of the separation of Weyl points (with opposite chirality, marked as WP+ and WP–) in different materials of TaAs family with increasing spin-orbital coupling effect; (b)–(d) high-resolution ARPES measurements on the (i) spoon-like FS and (ii, iii) associated band dispersions indicated by the red dotted lines for NbP, TaP and TaAs, respectively (ΔK₁ and ΔK₂ represent the separation between the Weyl points and Fermi arcs, respectively.); (e) summary of the extracted ΔK₁ and ΔK₂ from the three compounds, plotted against the SOC strength

DownLoad: Full-Size Img PowerPoint

图 10 磁性Weyl半金属Co₃Sn₂S₂　(a)磁性Weyl半金属及其丰富的近邻量子态; (b)时间反演破缺使狄拉克费米子(DP)劈裂产生一对手性相反的外尔费米子(WP)示意图; (c) Co₃Sn₂S₂晶体结构及(d)动量空间中(001)面外尔点和费米弧表面态分布示意图; (e)费米弧表面态所形成费米面的理论计算(i)和实验结果(ii)比较以及费米弧表面态能带色散的理论计算(iii)和实验结果(iv)比较; (f)费米面上的Weyl点(i)及其能带(ii)的三维演示; (ii)中过Weyl点的线性色散为(i)中灰色平面位置所切取, 红色的叠加曲线是理论计算结果

Figure 10. Magnetic Weyl semimetal Co₃Sn₂S₂: (a) Exotic neighboring states of the magnetic WSM can be achieved by tuning parameters such as magnetism, thickness, and electron correlation; (b) illustration of DP splitting (into one pair or two Weyl points) caused by time reversal symmetry broken in simplest magnetic WSMs. Magenta and green color of the Weyl points represent positive (+) and negative (–) chirality, respectively; the arrows illustrate the Berry curvature. k: momentum; s: spin; WP: Weyl point; IS: inversion symmetry; (c) crystal structure of Co₃Sn₂S₂ and (d) schematic of the bulk and surface Brillouin zones along the (001) surface of Co₃Sn₂S₂, with the Weyl points marked and connected by SFAs (yellow line segments); (e) comparison of the calculated (i) FS, (iii) band dispersion from both bulk and surface states and the corresponding experimental data of (ii) FS, (iv) band dispersion at 124 eV; (f) (i) 3D ARPES spectra intensity plot measured with Weyl points emerge (marked by green arrows). (ii) The band measured at 10 K, cutting from (i) with grey surface, shows a linear dispersion across the Weyl point, agreeing well with the calculations (red curves overlaid).

DownLoad: Full-Size Img PowerPoint

图 11 (a)第二类外尔费米子在动量空间中示意图; (b) T_d-MoTe₂的晶体结构及其(c)第一布里渊区示意图; (d)理论计算的W1和W2外尔费米子及费米弧在等能面上的位置; (e) (i)温度30 K下沿$\bar \varGamma - \bar X$方向的光能依赖ARPES谱以及(ii)k_x-k_y面上的E_F处等能面谱图, (iii)在k_y ≈ 0.05 Å^–1处沿P_x, P_y和P_z方向的光能依赖自旋极化情况(表示电子口袋和空穴口袋的EPs和HPs以及费米弧等由α, β, γ, δ等虚线指出); (f)k_x–k_y面内W1和W2外尔点附近的实验费米面图像及理论计算能带投影图; (g)利用泵浦-探测技术测得的过外尔点ARPES谱图及其对应的理论计算结果

Figure 11. (a) Schematic illustration of type-II Weyl Fermions in the momentum space; (b) crystal structure and (c) 1^st Brillouin zone of T_d-MoTe₂; (d) calculated W1 and W2 Weyl Fermions and Fermi arcs on CECs; (e) (i) photon-energy dependent ARPES data (T = 30 K) plot along $\bar \varGamma - \bar X$ at E_F as well as Fermi surface in the k_x–k_y plane, together with (iii) spin polarization measured at k_y ≈ 0.05 Å^–1 with photon-energy variation for P_x, P_y and P_z, respectively. EPs, HPs are short for electron pockets and hole pockets, small Fermi arcs are pointed out by α, β, γ, δ dashed lines; (f) measured and calculated Fermi surface around W1 and W2 in k_x–k_y plane; (g) pump-probe ARPES sprectrum cut through WP as well as the corresponding band structure calculation.

DownLoad: Full-Size Img PowerPoint

图 12 MoP的晶体结构及动量空间Γ—A方向能带结构图示　(a) MoP的三维晶体结构及(b) M_z方向(黄色面)俯视图; (c)体布里渊区和投影的(001)表面布里渊区; (d)不考虑及(e)考虑自旋轨道耦合时沿Γ—A方向的理论能带结构. 交叉点处的黑点表示三重简并点. 颜色混合标注的曲线表示双重简并能带, 纯色曲线表示非简并带

Figure 12. Crystal structure and band structure of MoP along the Γ–A line in the momentum space: (a) Three-dimensional crystal structure of MoP and (b) the top view of the lattice showing the C₃_Z rotation symmetry with respect to molybdenum (brown spheres) or phosphorous (green spheres) and the M_y mirror plane (horizontal red line); (c) bulk Brillouin zone and the projected (001) surface Brillouin zone; (d) (e) calculated band structures along Γ–A (d) without and (e) with SOC. The black spots at the crossing points indicate the triply degenerate points. The curves with mixed colors represent doubly degenerate bands, curves with pure color represent non-degenerate bands.

DownLoad: Full-Size Img PowerPoint

图 13 拓扑简并点TP1附近的电子结构　 (a)—(c)沿C1, C2, C3方向((i)—(iii))的ARPES及其能带曲率谱图与理论计算能带色散; (d) C1, C2, C3方向在体布里渊区中的位置示意图; (e)沿C1演化的TP1点附近能带分布三维色散图. C1能谱由(100)解理面采得而C2, C3由(001)解理面采得

Figure 13. Electronic structure near TP1. (a)-(c) (i) ARPES, (ii) curvature intensity plots and (iii)calculated band structure along (a) C1, (b) C2 and (c) C3; (C1, C2, C3 are blue and green lines indicated in (d)) (e) 3D plot of the band dispersions along C1 near TP1. Spectrum along C1 is recorded on the (100) cleavage surface; those along C2 and C3 are obtained on the (001) cleavage surface.

DownLoad: Full-Size Img PowerPoint

图 14 (a)四种费米子的能带示意图; (b)外尔半金属(上)与CoSi(下)中连接手性相反费米子投影的费米弧图示; (c) CoSi的晶体结构及(d)第一布里渊区示意图; (e)三维动量空间中手性边界态与费米弧示意图; (f), (g)理论计算和实验得出的CoSi费米面结果; (h)沿图(g)中Loop1和Loop2所示切出的k_//面内能谱

Figure 14. (a)Schematics of the band structures of a Weyl Fermion, a Dirac Fermion, a spin-1 Fermion and a charge-2 Fermion; (b) schematics of the Fermi arcs connecting the projections of Fermions with opposite chiralities for Weyl semimetals(up) and CoSi (down); (c) crystal structure and (d) 1^st Brillouin zone of CoSi; (e) diagram of chiral edge states and Fermi arcs in 3D momentum space; (f), (g) theoretical and experimental results of Fermi surface in CoSi; (h) in-plane (along k_//) spectra cut along Loop1 and Loop2 in Fig. (g).

DownLoad: Full-Size Img PowerPoint

图 15 (a)狄拉克点与节点线图示; (b) MSiS(M = Zr/Hf)材料的晶体结构和(c)第一布里渊区(及(001)表面布里渊区)示意图; (d) ZrSiS中光能436 eV下(k_z = 0)测得的三维能谱图, 展示了的节点环能带结构; (e)沿k_z方向演化的狄拉克节点线图示及对应的从Γ-X-Γ到Z-R-Z的ARPES能谱; (f)理论计算和实验得出的ZrSiS费米面(i) (iii)表面态及(ii) (iv)纯体态结果; (g) Co₂MnGa中的鼓面表面态图示

Figure 15. (a) Schematic illustration of Dirac node and Dirac nodal line in the momentum space; (b) crystal structure and (c) 1^st Brillouin zone (together with surface BZ) of MSiS (M = Zr/Hf); (d) 3D intensity plot of spectra measured in ZrSiS with hv = 436 eV, showing the band structure of the nodal ring when k_z = 0; (e) schematic of the band structure hosting a Dirac nodal line along k_z direction as well as corresponding ARPES spectra from Γ-X-Γ to Z-R-Z; (f) calculated and measured Fermi surface of ZrSiS with surface and bulk states respectively; (g) schematic of topological drumhead surface states in Co₂MnGa.

DownLoad: Full-Size Img PowerPoint

图 16 (a) ZrSiS的布里渊区局部放大图; (b)节面附近任意k_x-k_y面上的节线能带劈裂图示; (c)理论计算的R—A, L—H, X—M方向上的节点线能带色散; (d)沿图(a)中C1—C6方向的ARPES能谱, 红色箭头所指为劈裂前后的对应能带

Figure 16. (a) Zoomed-in Brillouin zone of ZrSiS; (b) Schematic plot of the band splitting of nodal line in an arbitrary k_x-k_y plane near the nodal surface; (c) calculated nodal line dispersion along R–A, L–H and X–M direction; (d) ARPES spectra along C1–C6 cuts in Fig. (a), with nodal lines before and after spliting pointed out by red arrows.

DownLoad: Full-Size Img PowerPoint

图 17 (a)四种节线形成的拓扑结构; (b)三维动量空间中TiB₂的理论计算体态费米面图示; (c)节点链结构在A-Γ-J面上的投影; (d) TiB₂的晶格结构示意图; (e)节点链结构在Γ-M-K面上的俯视投影; (f) ARPES实验80 eV下测得的费米面图; (g)光能依赖ARPES实验测得的节点链结构

Figure 17. (a) Schematics of four topological configurations formed by nodal lines; (b) calculated bulk FSs in the 3D BZ and the (c) projected calculation on the A-Γ-J surface, respectively; (d) crystal structure of TiB₂; (e) top view projection on Γ-M-K surface of the nodal chain calculation. (f) Fermi surface measured using ARPES at 80 eV; (g) nodal chain measured using hv-dependent ARPES experiment.

DownLoad: Full-Size Img PowerPoint

图 18 原位表面钾原子修饰诱发的拓扑Lifshitz转变 (a)和(b)分别是解离的NbAs的(001)面和钾原子修饰的电子能带结构. (i)到(iv)分别是实验测得的费米面、$\bar X$点附近费米面的能带计算和实验测量、费米弧连接成对外尔点的示意图. Trivial SS指平庸的表面态, SFAs指费米弧表面态, WP指外尔点.

Figure 18. Topological Lifshitz transition induced by in-situ potassium decoration: (a) and (b) are band structures of the pristine and in-situ potassium-decorated NbAs (001) surface, respectively. (i) - (iv): Measured Fermi surface, calculated and measured Fermi surface patch around $\bar X$ point, schematic illustration of the Fermi arc connectivity to projections of pairs of Weyl points. Trivial SS is short for trivial surface states, SFAs is short for surface Fermi arcs, and WP is short for Weyl point.

DownLoad: Full-Size Img PowerPoint

图 19 单层WTe₂的量子自旋霍尔绝缘体态　(a) WTe₂单晶的沿着$\bar Y - \bar G - \bar Y$方向的能带色散; (b) WTe₂单层薄膜的能带色散. 导带和价带形成45 meV的带隙; (c)在单层薄膜上的边界和体态的隧道扫描显微镜微分电导谱的对比: 边界上出现了边界态

Figure 19. (a) Band dispersion of WTe₂ crystals along $\bar Y - \bar G - \bar Y$ direction, showing multiple band crossings at E_F; (b) band dispersion of monolayer WTe₂ film (A bandgap of 45 meV is clearly revealed); (c) representative STM dI/dV spectra taken at the edge (orange) and in the bulk (purple), respectively.

DownLoad: Full-Size Img PowerPoint

[1]	Klitzing K V, Dorda G, Popper M, et al. 1980 Phys. Rev. Lett. 45 494 Google Scholar
[2]	Thouless D J, et al. 1982 Phys. Rev. Lett. 49 405
[3]	Tusi D C, Stormer H L, Gossard A C, et al. 1982 Phys. Rev. Lett. 48 1559 Google Scholar
[4]	Wen X G 1989 Phys. Rev. B 40 7387
[5]	Wen X G 1990 Int. J. Mod. Phys. B 4 239 Google Scholar
[6]	Bernevig B A, Hughes T L, Zhang S C, et al. 2006 Science 314 1757 Google Scholar
[7]	Fu L, Kane C L 2007 Phys. Rev. B 76 045302 Google Scholar
[8]	Moore J E, Balents L 2007 Phys. Rev. B 75 121306 Google Scholar
[9]	Hsieh D, Qian D, Wray L, et al. 2008 Nature 452 970 Google Scholar
[10]	Chen Y L, Analytis J G, Chu J H, et al. 2009 Science 325 178 Google Scholar
[11]	Wan X G, Turner A M, Vishwanath A, et al. 2011 Phys. Rev. B 83 205101 Google Scholar
[12]	Wang Z J, Sun Y, Chen X Q, et al. 2012 Phys. Rev. B 85 195320 Google Scholar
[13]	Young S M, Zaheer S, Teo J C Y, et al. 2012 Phys. Rev. Lett. 108 140405 Google Scholar
[14]	Dirac P A M 1928 Proc. R. Soc. A 117 610 Google Scholar
[15]	Weyl H 1929 Proc. Natl. Acad. Sci. U.S.A. 15 323 Google Scholar
[16]	Borisenko S, Gibson Q, Evtushinsky D, et al. 2014 Phys. Rev. Lett. 113 027603 Google Scholar
[17]	Liu Z K, Jiang J, Zhou B, et al. 2014 Nat. Mater. 13 677 Google Scholar
[18]	Liu Z K, Zhou B, Zhang Y, et al. 2014 Science 343 864 Google Scholar
[19]	Neupane M, Xu S Y, Sankar R, et al. 2014 Nat. Commun. 5 3786 Google Scholar
[20]	Xu S Y, Belopolski I, Alidoust N, et al. 2015 Science 349 6248
[21]	Damascelli A, Hussain Z, Shen Z X 2003 Rev. Mod. Phys. 75 473 Google Scholar
[22]	Chen Y L 2012 Front. Phys. 7 175
[23]	Penn D R 1987 Phys. Rev. B 35 482 Google Scholar
[24]	Powell C J, Jablonski A, Tilinin I S, et al. 1999 J. Electron. Spectrosc. Relat. Phenom. 98-99
[25]	Clark D T, Thomas H R 1977 J. Polym. Sci., Part A: Polym. Chem. 15 2843 Google Scholar
[26]	Nicholson A J C 1970 Appl. Opt. 9 1155 Google Scholar
[27]	Elder F R, Gurewitsch A M, Langmuir R V, et al. 1947 Phys. Rev. 71 829
[28]	Huffman R E, Tanaka Y, Larrabee J C 1963 Appl. Opt. 2 617 Google Scholar
[29]	Carmignani N 2016 Touschek Lifetime Studies and Optimization of the European Synchrotron Radiation Facility 1
[30]	Xu S Y, Liu C, Kushwaha S K, et al. 2015 Science 347 294 Google Scholar
[31]	Liang A J, Chen C Y, Wang Z J, et al. 2016 Chin. Phys. B 25 077101 Google Scholar
[32]	Yi H M, Wang Z J, Chen C Y, et al. 2014 Sci. Rep. 4 6106
[33]	Wang Z J, Weng H M, Wu Q S, et al. 2013 Phys. Rev. B 88 125427 Google Scholar
[34]	Wu M, Zheng G L, Chu W W, et al. 2018 Phys. Rev. B 98 161110 Google Scholar
[35]	Zhang C, Zhang Y, Yuan X, et al. 2019 Nature 565 331 Google Scholar
[36]	Zhang K N, Yan M Z, Zhang H X, et al. 2017 Phys. Rev. B 96 125102 Google Scholar
[37]	Li Y W, Xia Y Y Y, Ekahana S A, et al. 2017 Phys. Rev. Mater. 1 074202 Google Scholar
[38]	Yan M Z, Huang H Q, Zhang K N, et al. 2017 Nat. Commun. 8 257 Google Scholar
[39]	Bahramy M S, Clark O J, Yang B J, et al. 2017 Nat. Mater. 17 21
[40]	Noh H J, Jeong J, Cho E J, et al. 2017 Phys. Rev. Lett. 119 016401 Google Scholar
[41]	Fei F C, Bo X Y, Wang R, et al. 2017 Phys. Rev. B 96 041201 Google Scholar
[42]	Xiao R C, Gong P L, Wu Q S, et al. 2017 Phys. Rev. B 96 075101 Google Scholar
[43]	Tang P Z, Zhou Q, Xu G, et al. 2016 Nat. Phys. 12 1100 Google Scholar
[44]	Emmanouilidou E, Cao H B, Tang P Z, et al. 2017 Phys. Rev. B 96 224405 Google Scholar
[45]	Kang M G, Ye L D, Fang S A, et al. 2019 arXiv: 1906.02167
[46]	Lin Z Y, Wang C Z, Wang P D, et al. 2019 arXiv: 1906.05755
[47]	Soh J R, Juan F, Vergniory M G, et al. 2019 arXiv: 1901.10022 v
[48]	Ma J Z, Nie S M, Yi C J, et al. 2019 Sci. Adv. 5 eaaw4718 Google Scholar
[49]	Su H, Gong B C, Shi W J, et al. 2019 arXiv: 1903.12532
[50]	Hua G Y, Nie S M, Song Z D, et al. 2018 Phys. Rev. B 98 201116 Google Scholar
[51]	Xu G, Weng H M, Wang Z J, et al. 2011 Phys. Rev. Lett. 107 186806 Google Scholar
[52]	Lv B Q, Weng H M, Fu B B, et al. 2015 Phys. Rev. X 5 031013
[53]	Lv B Q, et al. 2015 Phys. Rev. Lett. 115 217601; 2015 Nat. Phys. 11 724 Google Scholar
[54]	Yang L X, Liu Z K, Sun Y, et al. 2015 Nat. Phys. 11 728
[55]	Liu Z K, Yang L X, Sun Y, et al. 2016 Nat. Mater. 15 27 Google Scholar
[56]	Weng H M, Fang C, Fang Z, et al. 2015 Phys. Rev. X 5 011029
[57]	Xu S Y, Belopolski I, Sanchez D S, et al. 2015 Sci. Adv. 1 e1501092 Google Scholar
[58]	Xu S Y, Belopolski I, Sanchez D S, et al. 2015 arXiv: 1509.07465
[59]	Xu S Y, Alidoust N, Belopolski I, et al. 2015 Nat. Phys. 11 748 Google Scholar
[60]	Kuroda K,Tomita T, Suzuki M T, et al. 2017 Nat. Mater. 16 1090 Google Scholar
[61]	Liu D F, Liang A J, Liu E K, et al. 2019 Science 365 1282 Google Scholar
[62]	Morali Noam, Batabyal Rajib, Nag P K, et al. 2019 Science 365 1286 Google Scholar
[63]	Soluyanov A A, Gresch D, Wang Z J, et al. 2015 Nature 527 495 Google Scholar
[64]	Sun Y, Wu S C, Ali M N, et al. 2015 Phys. Rev. B 92 161107 Google Scholar
[65]	Wang Z J, Gresch D, Soluyanov A A, et al. 2016 Phys. Rev. Lett. 117 056805 Google Scholar
[66]	Tamai A, Wu Q S, Cucchi I, et al. 2016 Phys. Rev. X 6 031021
[67]	Deng K, Wan G L, Deng P, et al. 2016 Nat. Phys. 12 1105 Google Scholar
[68]	Jiang J, Liu Z K, Sun Y, et al. 2017 Nat. Commun. 8 13973 Google Scholar
[69]	Huang L, McCormick T M, Ochi M, et al. 2016 Nat. Mater. 15 1155 Google Scholar
[70]	Rüßmann P, Weber A P, Glott F, et al. 2018 Phys. Rev. B 97 075106 Google Scholar
[71]	Wang Z J, Alexandradinata A, Robert J C 2016 Nature 532 189 Google Scholar
[72]	Xu N, Wang Z J, Weber A P, et al. 2016 arXiv: 1604.02116
[73]	Berger A N, Andrade E, Kerelsky A, et al. 2018 npj Quantum Mater. 3 2 Google Scholar
[74]	Yao M Y, Xu N,Wu Q S, et al. 2019 Phys. Rev. Lett. 122 176402 Google Scholar
[75]	Liang A J, Huang J W, Nie S M, et al. 2016 arXiv: 1604.01706
[76]	Sakano M, Bahramy M S, Tsuji H, et al. 2017 Phys. Rev. B 95 121101 Google Scholar
[77]	Wan G L, Yao W, Zhang K N, et al. 2017 arXiv: 1710.00350
[78]	Weber A P, Rüßmann P, Xu N, et al. 2018 Phys. Rev. Lett. 121 156401 Google Scholar
[79]	Chang T R, Xu S Y, Chang G Q, et al. 2016 Nat. Commun. 7 10639 Google Scholar
[80]	Belopolski I, Xu S Y, Ishida Y, et al. 2016 Phys. Rev. B 94 085127 Google Scholar
[81]	Pletikosić I, Ali M N, Fedorov A V, et al. 2014 Phys. Rev. Lett. 113 216601 Google Scholar
[82]	Jiang J, Tang F, Pan X C, et al. 2015 Phys. Rev. Lett. 115 166601 Google Scholar
[83]	Wu Y, Jo N H, Ochi M, et al. 2015 Phys. Rev. Lett. 115 166602 Google Scholar
[84]	Xu S Y, Alidoust N, Chang G Q, et al. 2017 Sci. Adv. 3 e1603266 Google Scholar
[85]	Belopolski I, Yu P, Sanchez D S, et al. 2017 Nat. Commun. 8 942 Google Scholar
[86]	Koepernik K, Kasinathan D, Efremov D V, et al. 2016 Phys. Rev. B 93 201101 Google Scholar
[87]	Haubold E, Koepernik K, Efremov D, et al. 2017 Phys. Rev. B 95 241108 Google Scholar
[88]	Heikkilä T T, Volovik G E 2015 New J. Phys. 17 093019 Google Scholar
[89]	Winkler G W, Wu Q S, Troyer M, et al. 2016 Phys. Rev. Lett. 117 076403 Google Scholar
[90]	Hyart T, Heikkilä T T 2016 Phys. Rev. B 93 235147 Google Scholar
[91]	Weng H M, Fang C, Fang Z, et al. 2016 Phys. Rev. B 93 241202 Google Scholar
[92]	Bradlyn B, Cano J, Wang Z J, et al. 2016 Science 353 558
[93]	Zhu Z M, Winkler G W, Wu Q S, et al. 2016 Phys. Rev. X 6 031003
[94]	Weng H M, Fang C, Fang Z, et al. 2016 Phys. Rev. B 94 165201 Google Scholar
[95]	Chang G Q, Xu S Y, Huang S M, et al. 2017 Sci. Rep. 7 1688 Google Scholar
[96]	Lv B Q, Feng Z L, Xu Q N, et al. 2017 Nature 546 627 Google Scholar
[97]	Rao Z C, Li H, Zhang T T, et al. 2019 Nature 567 496 Google Scholar
[98]	Sanchez D S, Belopolski I, Cochran T A, et al. 2019 Nature 567 500 Google Scholar
[99]	Schröter N B M, Pei D, Vergniory M G, et al. 2019 Nat. Phys. 15 759 Google Scholar
[100]	Lv B Q, Feng Z L, Zhao J Z, et al. 2019 Phys. Rev. B 99 241104 Google Scholar
[101]	Fang C, Weng H M, Dai X, et al. 2016 Chin. Phys. B 25 117106 Google Scholar
[102]	Burkov A A, Hook M D, Balents L, et al. 2011 Phys. Rev. B 84 235126 Google Scholar
[103]	Feng B J, Fu B T, Kasamatsu S, et al. 2017 Nat. Commun. 8 1007 Google Scholar
[104]	Lian J L, Yu L X, Liang Q F, et al. 2019 npj Comput. Mater. 10 1
[105]	Bian G, Chang T R, Sankar R, et al. 2016 Nat. Commun. 7 10556 Google Scholar
[106]	Wu Y, Wang L L, Mun E, et al. 2016 Nat. Phys. 12 667 Google Scholar
[107]	Wu Y, Jo N H, Wang L L, et al. 2019 Phys. Rev. B 99 161113(R)Google Scholar
[108]	Neupane M, Belopolski I, Hosen M M, et al. 2016 Phys. Rev. B 93 201104 Google Scholar
[109]	Takane D, Wang Z W, Souma S, et al. 2016 Phys. Rev. B 94 121108 Google Scholar
[110]	Chen C, Xu X, Jiang J, et al. 2017 Phys. Rev. B 95 125126 Google Scholar
[111]	Hosen M M, Dimitri K, Belopolski I, et al. 2017 Phys. Rev. B 95 161101 Google Scholar
[112]	Xu X, Jiang J, Shi W J, et al. 2019 Phys. Rev. B 99 195106 Google Scholar
[113]	Ekahana S A, Wu S C, Jiang J, et al. 2017 New J. Phys. 19 065007 Google Scholar
[114]	Li R H, Ma H, Cheng X Y, et al. 2016 Phys. Rev. Lett. 117 096401 Google Scholar
[115]	Xu Q N, Song Z D, Nie S M, et al. 2015 Phys. Rev. B 92 205310 Google Scholar
[116]	Fu B B, Yi C J, Zhang T T, et al. 2019 Sci. Adv. 645 eaau6459
[117]	Belopolski I, Manna K, Sanchez D S, et al. 2019 Science 365 1278 Google Scholar
[118]	Takane D, Souma S, Nakayama K, et al. 2018 Phys. Rev. B 98 041105(R)Google Scholar
[119]	Liu Z H, Lou R, Guo P J, et al. 2018 Phys. Rev. X 8 031044
[120]	Yi C J, Lv B Q, Wu Q S, et al. 2018 Phys. Rev. B 97 201107(R)Google Scholar
[121]	Lou R, Guo P J, Li M, et al. 2018 npj Quantum Mater. 43 1
[122]	Yang H F, Yang L X, Liu Z K, et al. 2019 Nat. Commun. 10 3478 Google Scholar
[123]	Tang S J, Zhang C F, Wong D, et al. 2017 Nat. Phys. 13 684
[124]	Šmejkal L, Železný J, Sinova J, et al. 2017 Phys. Rev. Lett. 118 106402 Google Scholar
[125]	Sun Yan, Wu S C, Yan B H, et al. 2015 Phys. Rev. B 92 115428 Google Scholar
[126]	Qian X F, Liu J W, Fu L, et al. 2014 Science 346 1344 Google Scholar
[127]	Wu S F, Fatemi V, Gibson Q D, et al. 2018 Science 359 76 Google Scholar

[1]	Deng Xiang-Wen, Wu Li-Yuan, Zhao Rui, Wang Jia-Ou, Zhao Li-Na. Application and prospect of machine learning in photoelectron spectroscopy. Acta Physica Sinica, 2024, 73(21): 210701. doi: 10.7498/aps.73.20240957
[2]	Wei Zhi-Yuan, Hu Yong, Zeng Ling-Yong, Li Ze-Yu, Qiao Zhen-Hua, Luo Hui-Xia, He Jun-Feng. Angle-resolved photoemission spectroscopy of electronic structure of 1T-NbSeTe. Acta Physica Sinica, 2022, 71(12): 127901. doi: 10.7498/aps.71.20220458
[3]	Wang En, Dong Wen-Han, Zhou Hui, Liu Meng, Ji Hong-Yan, Meng Sheng, Sun Jia-Tao. Nonequilibrium states in quantum materials under time-period driving. Acta Physica Sinica, 2021, 70(13): 138101. doi: 10.7498/aps.70.20201808
[4]	Sun Hui-Min, He Qing-Lin. Physical problems and experimental progress in layered magnetic topological materials. Acta Physica Sinica, 2021, 70(12): 127302. doi: 10.7498/aps.70.20210133
[5]	Qiang Xiao-Bin, Lu Hai-Zhou. Quantum transport in topological matters under magnetic fields. Acta Physica Sinica, 2021, 70(2): 027201. doi: 10.7498/aps.70.20200914
[6]	Zhao Lin, Liu Guo-Dong, Zhou Xing-Jiang. Angle-resolved photoemission spectroscopy studies on the electronic structure and superconductivity mechanism for high temperature superconductors. Acta Physica Sinica, 2021, 70(1): 017406. doi: 10.7498/aps.70.20201913
[7]	Gu Kai-Yuan, Luo Tian-Chuang, Ge Jun, Wang Jian. Superconductivity in topological materials. Acta Physica Sinica, 2020, 69(2): 020301. doi: 10.7498/aps.69.20191627
[8]	Jiang Cong-Ying, Sun Fei, Feng Zi-Li, Liu Shi-Bing, Shi You-Guo, Zhao Ji-Min. Time-resolved ultrafast dynamics in triple degenerate topological semimetal molybdenum phosphide. Acta Physica Sinica, 2020, 69(7): 077801. doi: 10.7498/aps.69.20191816
[9]	Wang Chong, Xing Qiao-Xia, Xie Yuan-Gang, Yan Hu-Gen. Spectroscopic studies of plasmons in topological materials. Acta Physica Sinica, 2019, 68(22): 227801. doi: 10.7498/aps.68.20191098
[10]	Liu Chang, Liu Xiang-Rui. Angle resolved photoemission spectroscopy studies on three dimensional strong topological insulators and magnetic topological insulators. Acta Physica Sinica, 2019, 68(22): 227901. doi: 10.7498/aps.68.20191450
[11]	Yi Chang-Jiang, Wang Le, Feng Zi-Li, Yang Meng, Yan Da-Yu, Wang Cui-Xiang, Shi You-Guo. Research progress of single crystal growth for topological semimetals. Acta Physica Sinica, 2018, 67(12): 128102. doi: 10.7498/aps.67.20180796
[12]	Zhao Lin, Liu Guo-Dong, Zhou Xing-Jiang. Angle-resolved photoemission studies on iron based high temperature superconductors. Acta Physica Sinica, 2018, 67(20): 207413. doi: 10.7498/aps.67.20181768
[13]	Wu Qiong, Liu Jun, Dong Qian-Min, Liu Yang, Liang Pei, Shu Hai-Bo. Quantum confinement effect on electronic and optical properties of SnS. Acta Physica Sinica, 2014, 63(6): 067101. doi: 10.7498/aps.63.067101
[14]	Nie Zhao-Xiu, Wang Feng, Cheng Zhi-Mei, Wang Xin-Qiang, Lu Li-Ya, Liu Gao-Bin, Duan Zhuang-Fen. First-principles study on electronic structure and half-metallicferromagnetism of ternary compound ZnCrS. Acta Physica Sinica, 2011, 60(9): 096301. doi: 10.7498/aps.60.096301
[15]	Wang Yong-Long, Pan Hong-Zhe, Xu Ming, Chen Li, Sun Yuan-Yuan. Electronic structure and magnetism of single-layer trigonal graphene quantum dots with zigzag edges. Acta Physica Sinica, 2010, 59(9): 6443-6449. doi: 10.7498/aps.59.6443
[16]	Xu Xin-Fa, Shao Xiao-Hong. Calculation of the electronic structure of Y-doped SrTiO3. Acta Physica Sinica, 2009, 58(3): 1908-1916. doi: 10.7498/aps.58.1908
[17]	Wu Yu-Yu, Chen Shi, Gao Xin-Yu, Andrew Thye Shen Wee, Xu Peng-Shou. Synchrotron radiation angle-resolved photoelectron spectroscopy studies of 6H-SiC（0001）-6[KF（]3[KF）]×6[KF（]3[KF）] R30° surface. Acta Physica Sinica, 2009, 58(6): 4288-4294. doi: 10.7498/aps.58.4288
[18]	Zhang Wen-Hua, Mo Xiong, Wang Guo-Dong, Wang Li-Wu, Xu Fa-Qiang, Pan Hai-Bin, Shi Min-Min, Chen Hong-Zheng, Wang Mang. Study of electronic structure of 3, 4, 9, 10-perylenetetracarboxylic bisimidazole/Ag interface by photoemission. Acta Physica Sinica, 2007, 56(8): 4936-4942. doi: 10.7498/aps.56.4936
[19]	Yang Zhi-Hong, Shi Da-Ning, Luo Da-Feng. Effects of proximity coupling and substitutions for Ba-sites on the transition temperature and ARPES of high-T＿c superconductors. Acta Physica Sinica, 2004, 53(11): 3902-3908. doi: 10.7498/aps.53.3902
[20]	WANG LI-MIN, LUO YING, MA BEN-KUN. ELECTRONIC STRUCTURE OF DOUBLE QUANTUM-DOT MOLECULE. Acta Physica Sinica, 2001, 50(2): 278-286. doi: 10.7498/aps.50.278

Catalog

Vol. 68, Issue 22 - 2019-11-20

Metrics

Abstract views: 20327
PDF Downloads: 1059
Cited By: 0

姓名
邮箱
手机号码
标题
留言内容
验证码

Search

Article

留言板