旋涂方式对有机发光显示屏发光均匀性及性能的影响

刘南柳; 艾娜; 胡典钢; 余树福; 彭俊彪; 曹镛; 王坚

doi:10.7498/aps.60.087805

摘要

采用旋转涂布法制备空穴传输层聚二氧乙基噻吩/聚对苯乙烯磺酸过程中,设置高低转速相结合的方式,调转基片方向实施二次旋涂干燥成膜,有效改善了材料因基片开口设计而引起的单双行薄膜厚度不均匀现象. 由于增加了功能层薄膜的均匀性,从而改善了显示屏的整体发光均匀性与发光效率. 改进工艺后制备的绿光显示屏电流效率提高了近40%,并得到了电流效率达1.25 cd/A的96×64的3.81 cm全彩高分子发光点阵显示屏,发光亮度提高了近25%.

关键词:

Abstract

By improving the spin-coating process during the deposition of hole transport layer poly(3,4-ethylenedioxythiophene)-poly(styrene-sulfonate)(PEDOT:PSS), high efficient monochrome passive-matrix organic light-emitting display is fabricated. The PEDOT:PSS film is spin-coated with a two-step spin-coating process, in which the substrate is turned 180° during the spin-coating, forcing the piled-up materials to move reversely. By introducing the second spin-coating step, the film thickness difference between single and double lines significantly reduces, leading to a more uniform light emission and a larger fill factor for the 3.81 cm monochrome polymer light-emitting diode display. Green light-emitting display with a peak current efficiency of 17 cd/A is successfully fabricated, and the efficiency is improved by 40 percent compared with that made by traditional spin-coating method. A 3.81 cm 96×64 full color display with a current efficiency of 1.25 cd/A is also successfully made.

Keywords:

作者及机构信息

1.
华南理工大学高分子光电材料与器件研究所,广州 510640

基金项目: 国家高新技术研究发展计划(批准号:2008AA03A311)、国家重点基础研究发展计划(批准号:2009CB623604)和中央高等学校基本科研基金 (批准号:20092M0111)资助的课题.

Authors and contacts

1.
Institute of Polymer Optoelectronic Material and Devices, South China University of Technology, Guangzhou 510640, China

参考文献

[1]	Pope M, Kallmann H P, Mangnante P 1963 J. Chem. Phys. 38 2042
[2]	[邹建华、兰林峰、徐瑞霞、杨伟、彭俊彪 2010 物理学报 59 1275]
[3]	Tang C W, Van Slyke S A 1987 Appl. Phys. Lett. 51 913
[4]	Niu Q L, Shao Y X, Xu W, Wang L, Han S H, Liu N L, Peng J B, Cao Y, Wang J 2008 Org. Electron. 9 95
[5]	Stephen F R 2004 Nature 428 911
[6]	Yimsiri P, Mackley M R 2007 Thin Solid Films 515 3787
[7]	Pschenitzka F, Sturm J C 1999 Appl. Phys. Lett. 74 1913
[8]	Pardo D A, Jabbour G E, Peyghambarian N 2000 Adv. Mater. 12 1249
[9]	Chang S C, Bharathan J, Yang Y, Helgeson R, Wudl F, Ramey M B, Reynolds J R 1998 Appl. Phys. Lett. 73 2561
[10]	van der Vaart N C, Lifka H, Budzelaar F P M, Rubingh J E J M, Hoppenbrouwers J J L, Dijksman J F, Verbeek R G F A, van Woudenberg R, Vossen F J, Hiddink M G H, Rosink J J W M, Bernards T N M, Giraldo A, Young N D, Fish D A, Childs M J, Steer W A, Lee D, George D S 2005 J. Soc. Inform. Display 13 9
[11]	Braun D, Heeger A J 1991 Appl. Phys. Lett. 58 1982
[12]	Gustafsson G, Cao Y, Treacy G M, Klavetter F, Colaneri N, Heeger A J 1992 Nature 357 477
[13]	Chang Y G, Nam S H, Kim N K, Kook Y H, Kim J, Yoo S S, Kim C D, Kang I, Chung I J 2008 Soc. Inform. Display 39 637
[14]	Hamer J W, Cok R S, Parrett G J, Winters D, Primerano B 2009 Soc. Inform. Display 40 947
[15]	Partridge R H 1983 Polymer 24 748
[16]	Burroughes J H, Bradleyd D D C, Brown A R, Marks R N, Mackay K, Friend R H, Burns P L, Holmes A B 1990 Nature 347 539
[17]	Charlie M, Anzlowar M, Innocenzo J, Kolosov D, Lehr W, O’Regan M, Sant P, Stainer M, Sysavat S, Venkatesh S 2003 Soc. Inform. Display 34 1191
[18]	Rahul G, Andrew I, Natarajan S, Franky S 2004 Soc. Inform. Display 35 1281
[19]	Saafir A K, Chung J, Joo I, Huh J, Rhee J, Park S, Choi B, Ko C, Koh B, Jung J, Choi J, Kim N, Chung K 2005 Soc. Inform. Display 36 968
[20]	Hou L T, Hou Q, Peng J B,Cao Y 2005 Acta Phys. Sin. 54 5377 (in Chinese) [侯林涛、侯琼、彭俊彪、曹镛 2005 物理学报 54 5377]
[21]	Huang W B, Peng J B 2007 Acta Phys. Sin. 56 2974(in Chinese) [黄文波、彭俊彪 2007 物理学报 56 2974]
[22]	Okutani S, Kamiura N, Sano H, Sawatani T, Fujita D, Takehara T, Sunohara K, Kobayashi M 2007 Soc. Inform. Display 38 173
[23]	Zou J H, Tao H, Wu H B, Peng J B 2009 Acta Phys. Sin. 58 1224 (in Chinese) [邹建华、陶洪、吴宏斌、彭俊彪 2009 物理学报 58 1224 Zou J H, Lan L F, Xu R X, Yang W, Peng J B 2010 Acta Phys. Sin. 59 1275 (in Chinese)
[24]	Ogi T, Modesto-Lopez L B, Iskandar F, Okuyama K 2007 Colloids Surf. A 297 71
[25]	Li Y Y, Wu H B, Zou J H, Ying L, Yang W, Cao Y 2009 Org. Electron. 10 901
[26]	Hou Q, Zhou Q M, Zhang Y, Yang W, Yang R Q, Cao Y 2004 Macromolecules 37 6299

施引文献

[1]	Pope M, Kallmann H P, Mangnante P 1963 J. Chem. Phys. 38 2042
[2]	[邹建华、兰林峰、徐瑞霞、杨伟、彭俊彪 2010 物理学报 59 1275]
[3]	Tang C W, Van Slyke S A 1987 Appl. Phys. Lett. 51 913
[4]	Niu Q L, Shao Y X, Xu W, Wang L, Han S H, Liu N L, Peng J B, Cao Y, Wang J 2008 Org. Electron. 9 95
[5]	Stephen F R 2004 Nature 428 911
[6]	Yimsiri P, Mackley M R 2007 Thin Solid Films 515 3787
[7]	Pschenitzka F, Sturm J C 1999 Appl. Phys. Lett. 74 1913
[8]	Pardo D A, Jabbour G E, Peyghambarian N 2000 Adv. Mater. 12 1249
[9]	Chang S C, Bharathan J, Yang Y, Helgeson R, Wudl F, Ramey M B, Reynolds J R 1998 Appl. Phys. Lett. 73 2561
[10]	van der Vaart N C, Lifka H, Budzelaar F P M, Rubingh J E J M, Hoppenbrouwers J J L, Dijksman J F, Verbeek R G F A, van Woudenberg R, Vossen F J, Hiddink M G H, Rosink J J W M, Bernards T N M, Giraldo A, Young N D, Fish D A, Childs M J, Steer W A, Lee D, George D S 2005 J. Soc. Inform. Display 13 9
[11]	Braun D, Heeger A J 1991 Appl. Phys. Lett. 58 1982
[12]	Gustafsson G, Cao Y, Treacy G M, Klavetter F, Colaneri N, Heeger A J 1992 Nature 357 477
[13]	Chang Y G, Nam S H, Kim N K, Kook Y H, Kim J, Yoo S S, Kim C D, Kang I, Chung I J 2008 Soc. Inform. Display 39 637
[14]	Hamer J W, Cok R S, Parrett G J, Winters D, Primerano B 2009 Soc. Inform. Display 40 947
[15]	Partridge R H 1983 Polymer 24 748
[16]	Burroughes J H, Bradleyd D D C, Brown A R, Marks R N, Mackay K, Friend R H, Burns P L, Holmes A B 1990 Nature 347 539
[17]	Charlie M, Anzlowar M, Innocenzo J, Kolosov D, Lehr W, O’Regan M, Sant P, Stainer M, Sysavat S, Venkatesh S 2003 Soc. Inform. Display 34 1191
[18]	Rahul G, Andrew I, Natarajan S, Franky S 2004 Soc. Inform. Display 35 1281
[19]	Saafir A K, Chung J, Joo I, Huh J, Rhee J, Park S, Choi B, Ko C, Koh B, Jung J, Choi J, Kim N, Chung K 2005 Soc. Inform. Display 36 968
[20]	Hou L T, Hou Q, Peng J B,Cao Y 2005 Acta Phys. Sin. 54 5377 (in Chinese) [侯林涛、侯琼、彭俊彪、曹镛 2005 物理学报 54 5377]
[21]	Huang W B, Peng J B 2007 Acta Phys. Sin. 56 2974(in Chinese) [黄文波、彭俊彪 2007 物理学报 56 2974]
[22]	Okutani S, Kamiura N, Sano H, Sawatani T, Fujita D, Takehara T, Sunohara K, Kobayashi M 2007 Soc. Inform. Display 38 173
[23]	Zou J H, Tao H, Wu H B, Peng J B 2009 Acta Phys. Sin. 58 1224 (in Chinese) [邹建华、陶洪、吴宏斌、彭俊彪 2009 物理学报 58 1224 Zou J H, Lan L F, Xu R X, Yang W, Peng J B 2010 Acta Phys. Sin. 59 1275 (in Chinese)
[24]	Ogi T, Modesto-Lopez L B, Iskandar F, Okuyama K 2007 Colloids Surf. A 297 71
[25]	Li Y Y, Wu H B, Zou J H, Ying L, Yang W, Cao Y 2009 Org. Electron. 10 901
[26]	Hou Q, Zhou Q M, Zhang Y, Yang W, Yang R Q, Cao Y 2004 Macromolecules 37 6299

[1]	任兴, 于宏宇, 张勇. 基于BCPO发光材料近紫外有机发光二极管的电致发光效率与稳定性. 物理学报, 2024, 73(4): 047801. doi: 10.7498/aps.73.20231301
[2]	保希, 关云霞, 李万娇, 宋家一, 陈丽佳, 徐爽, 彭柯敖, 牛连斌. 载流子阶梯效应调控有机发光二极管三线态激子的解离和散射. 物理学报, 2023, 72(21): 217101. doi: 10.7498/aps.72.20230851
[3]	成燕琴, 徐娟娟, 王有娣, 黎卓熹, 陈江山. 一种苯乙烯基喹啉衍生物的稳态和瞬态光电性质. 物理学报, 2022, 71(1): 018501. doi: 10.7498/aps.71.20211171
[4]	蒋福春, 刘瑞友, 彭冬生, 刘文, 柴广跃, 李百奎, 武红磊. 基于光谱法的发光二极管稳态热阻测量方法. 物理学报, 2021, 70(9): 098501. doi: 10.7498/aps.70.20201093
[5]	成燕琴, 徐娟娟, 王有娣, 黎卓熹, 陈江山. 一种苯乙烯基喹啉衍生物的稳态和瞬态光电性质研究. 物理学报, 2021, (): . doi: 10.7498/aps.70.20211171
[6]	邰建鹏, 郭伟玲, 李梦梅, 邓杰, 陈佳昕. GaN基微缩化发光二极管尺寸效应和阵列显示. 物理学报, 2020, 69(17): 177301. doi: 10.7498/aps.69.20200305
[7]	刘萌娇, 张新稳, 王炯, 秦雅博, 陈月花, 黄维. 非周期微纳结构增强有机发光二极管光耦合输出的研究进展. 物理学报, 2018, 67(20): 207801. doi: 10.7498/aps.67.20181209
[8]	张雅男, 王俊锋. 利用发光层梯度掺杂改善顶发射白光有机发光二极管光谱的稳定性. 物理学报, 2015, 64(9): 097801. doi: 10.7498/aps.64.097801
[9]	黄迪, 徐征, 赵谡玲. 使用PTB7作为阳极修饰层提高有机发光二极管的性能. 物理学报, 2014, 63(2): 027301. doi: 10.7498/aps.63.027301
[10]	刘佰全, 兰林锋, 邹建华, 彭俊彪. 具有新型双空穴注入层的有机发光二极管. 物理学报, 2013, 62(8): 087302. doi: 10.7498/aps.62.087302
[11]	张勇, 刘亚莉, 焦威, 陈林, 熊祖洪. 有机发光器件的磁电导效应. 物理学报, 2012, 61(11): 117106. doi: 10.7498/aps.61.117106
[12]	焦威, 雷衍连, 张巧明, 刘亚莉, 陈林, 游胤涛, 熊祖洪. 有机发光二极管的光致磁电导效应. 物理学报, 2012, 61(18): 187305. doi: 10.7498/aps.61.187305
[13]	杨洋, 陈淑芬, 谢军, 陈春燕, 邵茗, 郭旭, 黄维. 有机发光二极管光取出技术研究进展. 物理学报, 2011, 60(4): 047809. doi: 10.7498/aps.60.047809
[14]	邹建华, 兰林锋, 徐瑞霞, 杨伟, 彭俊彪. 有机薄膜晶体管驱动聚合物发光二极管研究. 物理学报, 2010, 59(2): 1275-1281. doi: 10.7498/aps.59.1275
[15]	程萍, 高峰, 陈向东, 杨继平. 偏置电场对聚对苯乙烯激发态弛豫特性的影响. 物理学报, 2010, 59(4): 2831-2835. doi: 10.7498/aps.59.2831
[16]	张勇, 刘荣, 雷衍连, 陈平, 张巧明, 熊祖洪. 基于Alq3的有机发光二极管的磁电导效应. 物理学报, 2010, 59(8): 5817-5822. doi: 10.7498/aps.59.5817
[17]	李春, 彭俊彪, 曾文进. 新型TPBI/Ag阴极结构的红色有机发光二极管. 物理学报, 2009, 58(3): 1992-1996. doi: 10.7498/aps.58.1992
[18]	张秀龙, 杨盛谊, 娄志东, 侯延冰. 有机电致发光器件的动态电学特性. 物理学报, 2007, 56(3): 1632-1636. doi: 10.7498/aps.56.1632
[19]	王军, 魏孝强, 饶海波, 成建波, 蒋亚东. 基于铱配合物材料的高效高稳定性有机发光二极管. 物理学报, 2007, 56(2): 1156-1161. doi: 10.7498/aps.56.1156
[20]	许雪梅, 彭景翠, 李宏建, 瞿述, 赵楚军, 罗小华. 有机层界面对双层有机发光二极管复合效率的影响. 物理学报, 2004, 53(1): 286-290. doi: 10.7498/aps.53.286

计量

文章访问数: 7182
PDF下载量: 752
被引次数: 0

姓名
邮箱
手机号码
标题
留言内容
验证码

搜索

留言板