二维过渡金属硫属化合物相变方法的研究进展

张浩哲; 徐春燕; 南海燕; 肖少庆; 顾晓峰

doi:10.7498/aps.69.20200965

摘要

近些年来, 二维过渡金属硫属化合物因其具有独特的原子结构和能带特征而备受关注. 过渡金属硫属化合物不仅存在稳定相, 也存在一些亚稳相, 这些亚稳相因其独特的电学和光学特性逐渐成为研究的热点. 为了获得这些亚稳相, 一种能够使过渡金属硫属化合物在两种晶相之间可控相变的方法必不可少. 本文首先对过渡金属硫属化合物的电学、力学和光学特性进行了总结, 然后介绍了其不同的晶相结构特征, 接着列举了目前报道的过渡金属硫属化合物的八种相变方法: 化学气相沉积法、掺杂法、分子插层法、应力法、高温热处理法、激光引导法、等离子体处理法以及电场引导法, 并且介绍了各自的研究进展, 最后对本文涉及的相变方法进行了总结并列举了这些方法迄今为止所存在的一些问题. 该文详细阐述了过渡金属硫属化合物的相变方法, 为未来过渡金属硫属化合物的相变研究提供了一个很好的参考方向.

关键词:

Abstract

Following traditional semiconductors such as silicon and GaAs, in recent years the two-dimensional materials have attracted attention in the field of optoelectronic devices, thermoelectric devices and energy storage and conversion due to their many peculiar properties. However, the normal two-dimensional materials such as graphene, cannot be well used in the field of optoelectronics due to the lack of a band gap, and the black phosphorus is also greatly limited in practical applications due to its instability in the air. The two-dimensional transition metal dichalcogenides have attracted more attention due to the different atomic structures, adjustable energy band and excellent photoelectric properties. There are different crystal phases in transition metal dichalcogenides, some of which are stable in the ground state, and others are instable. Different phases exhibit different characteristics, some of which have semiconductor properties and others have like metal in property. These stable and metastable phases of transition metal dichalcogenides can be transformed into each other under some conditions. In order to obtain these metastable phases, thereby modulating their photoelectric performance and improving the mobility of the devices, it is essential to obtain a phase transition method that enables the crystal phase transition of the transition metal dichalcogenides. In this article, first of all, we summarize the different crystal structures of transition metal dichalcogenides and their electrical, mechanical, and optical properties. Next, the eight phase transition methods of transition metal dichalcogenides are listed, these being chemical vapor deposition, doping, ion intercalation, strain, high temperature thermal treatment, laser inducing, plasma treatment, and electric field inducing. After that, the research progress of these phase transition methods and their advantages and disadvantages are introduced. Finally, we sum up all the phase transition methods mentioned in this article and then list some of the problems that have not been solved so far. This review elaborates all of the presently existing different phase transition methods of transition metal dichalcogenides in detail, which provides a good reference for studying the phase transition of transition metal dichalcogenides in the future, the electrical performance regulated by different phases, and the applications of memory devices and electrode manufacturing.

Keywords:

two-dimensional transition metal dichalcogenides /
crystal structure /
phase transition method

作者及机构信息

江南大学电子工程系, 物联网技术应用教育部工程研究中心, 无锡　214122

通信作者: 南海燕, jnanhaiyan@jiangnan.edu.cn

基金项目: 国家自然科学基金(批准号: 11704159)、江苏省自然科学基金(批准号: BK20170167)、中国博士后科学基金(批准号: 2018M642154)和江苏省博士后基金(批准号: 2018K057B)资助的课题

Authors and contacts

Engineering Research Center of IOT Technology Applications (Ministry of Education), Department of Electronic Engineering, Jiangnan University, Wuxi 214122, China

Corresponding author: Nan Hai-Yan, jnanhaiyan@jiangnan.edu.cn

Funds: Project supported by the National Natural Science Foundation of China (Grant No. 11704159), the Natural Science Foundation of Jiangsu Province, China (Grant No. BK20170167), the China Postdoctoral Science Foundation (Grant No. 2018M642154), and the Postdoctoral Foundation of Jiangsu Province, China (Grant No. 2018K057B)

文章全文 : translate this paragraph

参考文献

[1]	Novoselov K S, Jiang D, Schedin F, Booth T J, Khotkevich V V, Morozov S V, Geim A K 2005 Proc. Natl. Acad. Sci. U. S. A. 102 10451 Google Scholar
[2]	Allen M J, Tung V C, Kaner R B 2010 Chem. Rev. 110 132 Google Scholar
[3]	Fukuoka S, Taen T, Osada T 2015 J. Phys. Soc. Jpn. 84 121004 Google Scholar
[4]	Li P, Zhang D Z, Liu J J, Chang H Y, Sun Y, Yin N L 2015 ACS Appl. Mater. Interfaces 7 24396 Google Scholar
[5]	Xu M S, Liang T, Shi M M, Chen H Z 2013 Chem. Rev. 113 3766 Google Scholar
[6]	Xie L, Liao M Z, Wang S P, Yu H, Du L J, Tang J, Zhao J, Zhang J, Chen P, Lu X B, Wang G L, Xie G B, Yang R, Shi D X, Zhang G Y 2017 Adv. Mater. 29 1702522 Google Scholar
[7]	Liu H, Neal A T, Ye P D 2012 ACS Nano 6 8563 Google Scholar
[8]	Zhang F, Appenzeller J 2015 Nano Lett. 15 301 Google Scholar
[9]	Kappera R, Voiry D, Yalcin S E, Branch B, Gupta G, Mohite A D, Chhowalla M 2014 Nat. Mater. 13 1128 Google Scholar
[10]	Kuc A, Heine T 2015 Chem. Soc. Rev. 44 2603 Google Scholar
[11]	Zhang F, Zhang H R, Krylyuk S, Milligan C A, Zhu Y Q, Zemlyanov D Y, Bendersky L A, Burton B P, Davydov A V, Appenzeller J 2019 Nat. Mater. 18 55 Google Scholar
[12]	Splendiani A, Sun L, Zhang Y B, Li T S, Kim J, Chim C Y, Galli G, Wang F 2010 Nano Lett. 10 1271 Google Scholar
[13]	苏向英 2017 低维过渡金属硫属化合物的电子性质及调控 (北京: 电子工业出版社) 第3页 Su X Y 2017 Electronic Properties and Control of Low-dimensional Transition Metal Chalcogenides (Beijing: Publishing House of Electronics Industry) p3 (in Chinese)
[14]	Radisavljevic B, Radenovic A, Brivio J, Giacometti V, Kis A 2011 Nat. Nanotechnol. 6 147 Google Scholar
[15]	Zhang Y J, Ye J T, Matsuhashi Y, Iwasa Y 2012 Nano Lett. 12 1136 Google Scholar
[16]	Agnihotri P, Dhakras P, Lee J U 2016 Nano Lett. 16 4355 Google Scholar
[17]	Lee Y T, Kang J H, Kwak K, Ahn J, Choi H T, Ju B K, Shokouh S H, Im S, Park M C, Hwang D K 2018 ACS Photonics 5 4745 Google Scholar
[18]	Bertolazzi S, Brivio J, Kis A 2011 ACS Nano 5 9703 Google Scholar
[19]	Castellanos-Gomez A, Poot M, Steele G A, van der Zant H S J, Agrait N, Rubio-Bollinger G 2012 Adv. Mater. 24 772 Google Scholar
[20]	周愈之 2018 物理学报 67 218102 Google Scholar Zhou Y Z 2018 Acta Phys. Sin. 67 218102 Google Scholar
[21]	Park J C, Yun S J, Kim H, Park J H, Chae S H, An S J, Kim J G, Kim S M, Kim K K, Lee Y H 2015 ACS Nano 9 6548 Google Scholar
[22]	Zhou L, Xu K, Zubair A, Liao A D, Fang W J, Ouyang F P, Lee Y H, Ueno K, Saito R, Palacios T, Kong J, Dresselhaus M S 2015 J. Am. Chem. Soc. 137 11892 Google Scholar
[23]	Naylor C H, Parkin W M, Ping J L, Gao Z L, Zhou Y R, Kim Y, Streller F, Carpick R W, Rappe A M, Drndic M, Kikkawa J M, Johnson A T C 2016 Nano Lett 16 4297 Google Scholar
[24]	Yang L, Zhang W F, Li J, Cheng S, Xie Z J, Chang H X 2017 ACS Nano 11 1964 Google Scholar
[25]	Zhu X K, Li A L, Wu D, Zhu P, Xiang H Y, Liu S, Sun J, Ouyang F P, Zhou Y, Xiong X 2019 J. Mater. Chem. C 7 10598 Google Scholar
[26]	Huang W J, G an, L, Li H Q, Ma Y, Zhai T Y 2018 Chem. – Eur. J. 24 15678 Google Scholar
[27]	Liu L N, Wu J X, Wu L Y, Ye M, Liu X Z, Wang Q, Hou S Y, Lu P F, Sun L F, Zheng J Y, Xing L, Gu L, Jiang X W, Xie L M, Jiao L Y 2018 Nat. Mater. 17 1108 Google Scholar
[28]	Wang Z Q, Shen Y H, Ito Y, Zheng Y Z, Du J, Fujita T, Hirata A, Tang Z, Chen M W 2018 ACS Nano 12 1571 Google Scholar
[29]	Wang Z, Sun J, Wang H L, Lei Y M, Xie Y, Wang G F, Zhao Y, Li X B, Xu H, Yang X B, Feng L P, Ma X H 2020 Appl. Surf. Sci. 504 144371 Google Scholar
[30]	Feng Q L, Mao N N, Wu J X, Xu H, Wang C M, Zhang J, Xie L M 2015 ACS Nano 9 7450 Google Scholar
[31]	Feng Q L, Zhu Y M, Hong J H, Zhang M, Duan W J, Mao N N, Wu J X, Xu H, Dong F L, Lin F, Jin C H, Wang C M, Zhang J, Xie L M 2014 Adv. Mater. 26 2648 Google Scholar
[32]	Tongay S, Narang D S, Kang J, Fan W, Ko C H, Luce A V, Wang K X, Suh J, Patel K D, Pathak V M, Li J B, Wu J Q 2014 Appl. Phys. Lett. 104 012101 Google Scholar
[33]	Li H L, Duan X D, Wu X P, Zhuang X J, Zhou H, Zhang Q L, Zhu X L, Hu W, Ren P Y, Guo P F, Ma L, Fan X P, Wang X X, Xu J Y, Pan A L, Duan X F 2014 J. Am. Chem. Soc. 136 3756 Google Scholar
[34]	Li H L, Zhang Q L, Duan X D, Wu X P, Fan X P, Zhu X L, Zhuang X J, Hu W, Zhou H, Pan A L, Duan X F 2015 J. Am. Chem. Soc. 137 5284 Google Scholar
[35]	Chen Y F, Dumcenco D O, Zhu Y M, Zhang X, Mao N N, Feng Q L, Zhang M, Zhang J, Tan P H, Huang Y S, Xie L M 2014 Nanoscale 6 2833 Google Scholar
[36]	Liu H F, Antwi K K A, Chua S, Chi D Z 2014 Nanoscale 6 624 Google Scholar
[37]	Chen Y F, Xi J Y, Dumcenco D O, Liu Z, Suenaga K, Wang D, Shuai Z G, Huang Y S, Xie L M 2013 ACS Nano 7 4610 Google Scholar
[38]	Liu S J, Huang L, Wu K D, Wei Z M, Huang B J, Meng X Q, Tongay S, Liu J, Li J B, Chen H D 2016 Appl. Phys. Lett. 109 112102 Google Scholar
[39]	Lin Y C, Dumcenco D O, Komsa H P, Niimi Y, Krasheninnikov A V, Huang Y S, Suenaga K 2014 Adv. Mater. 26 2857 Google Scholar
[40]	Zandalazini C I, Albanesi E A 2019 J. Magn. Magn. Mater. 484 146 Google Scholar
[41]	Fan S W, Yang L, Gao G Y 2019 Phys. Lett. A 383 3138 Google Scholar
[42]	Laroussi A, Berber M, Mokaddem A, Doumi B, Abid H, Boudali A 2019 Acta Phys. Pol. A 135 451 Google Scholar
[43]	Duerloo K N, Reed E J 2016 ACS Nano 10 289 Google Scholar
[44]	Kumar A, Strachan A, Onofrio N 2019 J. Appl. Phys. 125 204303 Google Scholar
[45]	Wang J Z, Yang T, Zhang Z D, Yang L 2018 Appl. Phys. Lett. 112 213104 Google Scholar
[46]	Young J, Reinecke T L 2017 Phys. Chem. Chem. Phys. 19 31874 Google Scholar
[47]	Huang H H, Fan X F, Singh D J, Zheng W T 2018 Phys. Chem. Chem. Phys. 20 26986 Google Scholar
[48]	Chen M W, Zhu L G, Chen Q F, Miao N H, Si C, Zhou J, Sun Z M 2020 J. Mater. Chem. C 8 721 Google Scholar
[49]	Koski K J, Wessells C D, Reed B W, Cha J J, Kong D S, Cui Y 2012 J. Am. Chem. Soc. 134 13773 Google Scholar
[50]	Gong Y J, Yuan H T, Wu C L, et al. 2018 Nat. Nanotechnol. 13 294 Google Scholar
[51]	Meng Y S, Elena Arroyo-de Dompablo M 2009 Energy Environ. Sci. 2 589 Google Scholar
[52]	Zhang Z X, Yang M Y, Zhao N, Wang L, Li Y Y 2019 Phys. Chem. Chem. Phys. 21 23441 Google Scholar
[53]	Py M A, Haering R R 1983 Can. J. Phys. 61 76 Google Scholar
[54]	Kan M, Wang J Y, Li X W, Zhang S H, Li Y W, Kawazoe Y, Sun Q, Jena P 2014 J. Phys. Chem. C 118 1515 Google Scholar
[55]	Tan S J R, Abdelwahab I, Ding Z J, Zhao X X, Yang T S, Loke G Z J, Lin H, Verzhbitskiy I, Poh S M, Xu H, Nai C T, Zhou W, Eda G, Jia B H, Loh K P 2017 J. Am. Chem. Soc. 139 2504 Google Scholar
[56]	Xia J, Wang J, Chao D L, Chen Z, Liu Z, Kuo J L, Yan J X, Shen Z X 2017 Nanoscale 9 7533 Google Scholar
[57]	Sun L F, Yan X X, Zheng J Y, Yu H D, Lu Z X, Gao S P, Liu L N, Pan X Q, Wang D, Wang Z G, Wang P, Jiao L Y 2018 Nano Lett. 18 3435 Google Scholar
[58]	Eshete Y A, Ling N, Kim S, Kim D, Hwang G, Cho S, Yang H 2019 Adv. Funct. Mater. 29 1904504 Google Scholar
[59]	Leng K, Chen Z X, Zhao X X, Tang W, Tian B B, Nai C T, Zhou W, Loh K P 2016 ACS Nano 10 9208 Google Scholar
[60]	Tan C L, Zhao W, Chaturvedi A, Fei Z, Zeng Z Y, Chen J Z, Huang Y, Ercius P, Luo Z M, Qi X Y, Chen B, Lai Z C, Li B, Zhang X, Yang J, Zong Y, Jin C H, Zheng H M, Kloc C, Zhang H 2016 Small 12 1866 Google Scholar
[61]	Wang X F, Shen X, Wang Z X, Yu R C, Chen L Q 2014 ACS Nano 8 11394 Google Scholar
[62]	Koley S, Basu S 2020 J. Magn. Magn. Mater. 499 166294 Google Scholar
[63]	Li P, Jeong J Y, Jin B J, Zhang K, Park J H 2020 Energy Storage Mater. 25 687 Google Scholar
[64]	Island J O, Kuc A, Diependaal E H, Bratschitsch R, van der Zant H S J, Heine T, Castellanos-Gomez A 2016 Nanoscale 8 2589 Google Scholar
[65]	Duerloo K N, Li Y, Reed E J 2014 Nat. Commun. 5 4214 Google Scholar
[66]	Song S, Keum D H, Cho S, Perello D, Kim Y, Lee Y H 2016 Nano Letters 16 188 Google Scholar
[67]	Huang H H, Fan X F, Singh D J, Chen H, Jiang Q, Zheng W T 2016 Phys. Chem. Chem. Phys. 18 4086 Google Scholar
[68]	Fan X F, Singh D J, Jiang Q, Zheng W T 2016 Phys. Chem. Chem. Phys. 18 12080 Google Scholar
[69]	Tang Q 2018 J. Mater. Chem. C 6 9561 Google Scholar
[70]	Johari P, Shenoy V B 2012 ACS Nano 6 5449 Google Scholar
[71]	Apte A, Kochat V, Rajak P, et al. 2018 ACS Nano 12 3468 Google Scholar
[72]	Keum D H, Cho S, Kim J H, et al. 2015 Nat. Phys. 11 482 Google Scholar
[73]	Wang Z Y, Sun Y Y, Abdelwahab I, et al. 2018 ACS Nano 12 12619 Google Scholar
[74]	Yin X M, Tang C S, Wu D, et al. 2019 Adv. Sci. 6 1802093 Google Scholar
[75]	Sung J H, Heo H, Si S, Kim Y H, Noh H R, Song K, Kim J, Lee C S, Seo S Y, Kim D H, Kim H K, Yeom H W, Kim T H, Choi S Y, Kim J S, Jo M H 2017 Nat. Nanotechnol. 12 1064 Google Scholar
[76]	Nakata Y, Sugawara K, Shimizu R, Okada Y, Han P, Hitosugi T, Ueno K, Sato T, Takahashi T 2016 NPG Asia Mater. 8 e231 Google Scholar
[77]	Chen J C, Feng Z H, Fan S Q, et al. 2017 ACS Appl. Mater. Interfaces 9 30107 Google Scholar
[78]	Cho S, Kim S, Kim J H, Zhao J, Seok J, Keum D H, Baik J, Choe D H, Chang K J, Suenaga K, Kim S W, Lee Y H, Yang H 2015 Science 349 625 Google Scholar
[79]	Yu Y F, Nam G H, He Q Y, et al. 2018 Nat. Chem. 10 638 Google Scholar
[80]	Chen Z R, Nan H Y, Liu Z, Wang X Y, Gu X F, Xiao S Q 2019 J. Raman Spectrosc. 50 755 Google Scholar
[81]	Si C, Choe D, Xie W Y, Wang H, Sun Z M, Bang J, Zhang S B 2019 Nano Lett. 19 3612 Google Scholar
[82]	Azcatl A, Qin X Y, Prakash A, et al. 2016 Nano Lett. 16 5437 Google Scholar
[83]	Cheng C C, Lu A Y, Tseng C C, Yang X L, Hedhili M N, Chen M C, Wei K H, Li L J 2016 Nano Energy 30 846 Google Scholar
[84]	O’Brien M, Lee K, Morrish R, Berner N C, McEvoy N, Wolden C A, Duesberg G S 2014 Chem. Phys. Lett. 615 6 Google Scholar
[85]	Jin J C, Zhang D P, Qin X N, Yang Y, Huang Y, Guan H, He Q C, Fan P, Lv W Z 2019 Nanomaterials 9 102 Google Scholar
[86]	Zhu J, Wang Z, Yu H 2017 J. Am. Chem. Soc. 139 10216 Google Scholar
[87]	Shawkat M S, Gil J, Han S S, et al. 2020 ACS Appl. Mater. Interfaces 12 14341 Google Scholar
[88]	Nan H Y, Jiang J, Xiao S Q, et al. 2018 Nanotechnology 30 034004 Google Scholar
[89]	Taniguchi K, Matsumoto A, Shimotani H, Takagi H 2012 Appl, . Phys. Lett. 101 042603 Google Scholar
[90]	Ye J T, Zhang Y J, Akashi R, Bahramy M S, Arita R, Iwasa Y 2012 Science 338 1193 Google Scholar
[91]	何学侠, 刘富才, 曾庆圣, 刘政 2015 化学学报 73 924 Google Scholar He X X, Liu F C, Zeng Q S, Liu Z 2015 Acta Chim. Sin. 73 924 Google Scholar
[92]	Li Y, Duerloo K A N, Wauson K, Reed E J 2016 Nat. Commun. 7 10671 Google Scholar
[93]	Wang Y, Xiao J, Zhu H 2017 Nature 550 487 Google Scholar
[94]	Bischoff F, Auwarter W, Barth J V, Schiffrin A, Fuhrer M, Weber B 2017 Chem. Mater. 29 9907 Google Scholar

施引文献

图 1 TMD稳定性及半导体特性的总结^[5]

Fig. 1. Summarize of the stability and semiconductor properties of TMD^[5].

下载: 全尺寸图片幻灯片

图 2 不同相TMD的基本结构图

Fig. 2. Basic structure diagram of TMDs different phases.

下载: 全尺寸图片幻灯片

图 3 TMD的相变方法

Fig. 3. Phase transition methods of TMDs.

下载: 全尺寸图片幻灯片

图 4 TMD的CVD法相变　(a) 通过CVD生长出1T' MoTe₂的示意图^[21]; (b), (c)大面积多层MoTe₂的CVD过程中金属-半导体-金属相演化与前驱体的碲化速度的关系^[24]; (d), (e) CVD法获得多层1T'-2H MoTe₂横向同质结^[25]; (f) 三元TMD的CVD法驱动2H到1T' 相变示意图^[29]

Fig. 4. TMD phase transition induced by CVD method: (a) Schematic diagram of 1T' MoTe₂ grown by CVD^[21]; (b), (c) relationship between metal-semiconductor-metal phase evolution and telluride velocity of precursor during the CVD process of large-area multilayer MoTe₂^[24]; (d), (e) multilayer 1T' -2H MoTe₂ transverse homogeneous junction was obtained by CVD^[25]; (f) schematic diagram of ternary TMD 2H-1T' phase transition driven by the CVD method^[29].

下载: 全尺寸图片幻灯片

图 5 通过掺杂/合金化诱导TMD相变　(a), (b) MoTe₂掺杂部分非金属元素后发生的相位改变^[46]; (c), (d) MoS₂掺杂Cu引发2H-1T' 相的改变^[47]; (e) 过渡金属掺入MoSe₂, MoTe₂和WTe₂形成合金的相位稳定性^[48]

Fig. 5. TMD phase transition induced by doping/alloying: (a), (b) The phase transition of MoTe₂ after doping part of nonmetallic elements^[46]; (c), (d) the 2H-1T' phase transition of MoS₂ induced by doping Cu^[47]; (e) the phase stability of the alloy was obtained by mixing the transition metal with MoSe₂, MoTe₂ and WTe₂^[48].

下载: 全尺寸图片幻灯片

图 6 分子插层和应力诱导TMD相变　(a) MoS₂相变难度与其层数的关系^[57]; (b) 电化学法诱导三元TMD相变示意图; (c) 相变前后三元TMD的STEM图像和XPS光谱; (d) 1T三元层状TMD的电学特性^[60]; (e) 机械拉伸诱导MoTe₂由2H-1T' 的转变^[65]; (f) 在空位与拉伸条件下MoX₂ TMD的相位稳定性^[69]; (g) 三元TMD通过拉伸引发不可逆相变^[71]

Fig. 6. TMD phase transition induced by intercalation and strain: (a) The relationship between the phase transition difficulty of MoS₂ and the number of layers^[57]; (b) schematic diagram of ternary TMD phase transition induced by electrochemical method; (c) STEM image and XPS spectrum of ternary TMD before and after phase transition; (d) electrical properties of 1T ternary layered TMD^[60]; (e) mechanical tensile induced 2H-1T' transformation of MoTe₂^[65]; (f) phase stability of MoX₂ TMD under vacancy and stretch conditions^[69]; (g) irreversible phase transition of ternary TMD induced by stretching^[71].

下载: 全尺寸图片幻灯片

图 7 高温热处理、激光、等离子体诱导TMD相变　(a) MoTe₂相变程度与温度及Te浓度的关系^[72]; (b) 块状1T-TaS₂的1T-2H相变示意图^[73]; (c) NbSe₂上1T和2H相的选择性合成^[76]; (d) 激光灼烧诱导相变示意图^[78]; (e) 激光引导MoTe₂诱导相变的原理图^[81]; (f) Ar等离子体引发MoS₂相变的光学特性^[86]; (g) 温和等离子体诱导MoTe₂相变原理图; (h) 2H和1T' MoTe₂的转移特性曲线^[88]

Fig. 7. TMDs phase transition induced by thermal, laser and plasma treatment: (a) The relationship between MoTe₂ phase transition and temperature and Te concentration^[72]; (b) schematic diagram of 1T-2H phase transition on the bulk 1T-TaS₂^[73]; (c) selective synthesis of 1T and 2H phases on NbSe₂^[76]; (d) schematic diagram of the phase transition by laser irradiation^[78]; (e) schematic diagram of laser-induced MoTe₂ phase transition^[81]; (f) optical properties of MoS₂ phase transition induced by Ar plasma^[86]; (g) schematic diagram of MoTe₂ phase transition induced by soft plasma; (h) transfer characteristic curves of 2H and 1T' MoTe₂^[88].

下载: 全尺寸图片幻灯片

图 8 电场引导TMD相变　(a) MoTe₂相变与门控电压的关系; (b) TaSe₂电场相变示意图及其相变与门控电压的关系^[92]; (c) 静电掺杂诱导MoTe₂相变原理图; (d) MoTe₂相变过程拉曼光谱及其相变程度与栅极电压的关系^[93]; (e) STM尖端电压脉冲诱导NbSe₂的相变^[94]; (f) 施加电场对Mo_1–_xW_xTe₂的2H-2H_d相变^[11]

Fig. 8. TMDs phase transition induced by electric-field: (a) Relationship between MoTe₂ phase transition and gate voltage; (b) schematic diagram of TaSe₂ electric-field phase transition and its relationship with gate voltage^[92]; (c) schematic diagram of electrostatic doping induced MoTe₂ phase transition; (d) Raman spectrum of MoTe₂ phase transition and relationship between the phase transition and gate voltage^[93]; (e) phase transition of NbSe₂ induced by voltage pulses with an STM tip^[94]; (f) the 2H-2H_d phase transition of Mo_1–_xW_xTe₂ by applying electric field^[11].

下载: 全尺寸图片幻灯片

表 1 TMD的相变方法及其特点

Table 1. Phase transition methods of TMDs and their properties.

相变方法	特点
相变方法	优点	不足
化学气相沉积	可以通过改变温度、气流量以及源粉成分来实现不同相的选择性生长或相变, 操作简单	该方法受环境因素影响较大, 产物不稳定
掺杂/合金化	通过对TMD引入其他原子使其完成半导体到半金属的转变, 生成产物性质稳定, 不易变质	原有材料本身的化学性质容易发生改变, 一些原有的良好性能受到破坏
分子插层	将离解出的原子或离子嵌入对象TMD材料双层之间的空隙从而达到相变的目的, 该方法因其操作简单, 现已成为TMD的常用相变方法	相变产物中可能包含插层原子或离子
应力	通过机械拉伸可以实现薄层TMD的相变, 这种相变通常不可逆, 所以可以保持产物的稳定性	过度引入应力可能使材料开裂或变形
高温热处理	提高温度来实现TMD的相变, 是最为直接的相变方法, 操作容易	相变产物在长时间室温条件下可以恢复为原来的晶相
激光引导	使用激光照射TMD样品来实现其相变, 相变产物稳定, 不易恢复为原来的晶相, 有着广阔的应用前景	相变往往具有不可逆性, 且激光功率过大容易损坏样品
等离子体处理	通过低温等离子体处理TMD材料实现其相变, 可实现大范围简易相位调控, 研究前景广阔	相变产物不稳定, 高温下晶相容易恢复
电场引导	通过电场直接在TMD器件上实现相变, 避免了相变后的 TMD在制作器件时恢复为原来的晶相, 这种相变通常可逆, 在电子器件制造上有着广泛的应用	局限于电学器件制造, 很难在其他方面有所应用, 另外实验所需环境较为苛刻

下载: 导出CSV

[1]	Novoselov K S, Jiang D, Schedin F, Booth T J, Khotkevich V V, Morozov S V, Geim A K 2005 Proc. Natl. Acad. Sci. U. S. A. 102 10451 Google Scholar
[2]	Allen M J, Tung V C, Kaner R B 2010 Chem. Rev. 110 132 Google Scholar
[3]	Fukuoka S, Taen T, Osada T 2015 J. Phys. Soc. Jpn. 84 121004 Google Scholar
[4]	Li P, Zhang D Z, Liu J J, Chang H Y, Sun Y, Yin N L 2015 ACS Appl. Mater. Interfaces 7 24396 Google Scholar
[5]	Xu M S, Liang T, Shi M M, Chen H Z 2013 Chem. Rev. 113 3766 Google Scholar
[6]	Xie L, Liao M Z, Wang S P, Yu H, Du L J, Tang J, Zhao J, Zhang J, Chen P, Lu X B, Wang G L, Xie G B, Yang R, Shi D X, Zhang G Y 2017 Adv. Mater. 29 1702522 Google Scholar
[7]	Liu H, Neal A T, Ye P D 2012 ACS Nano 6 8563 Google Scholar
[8]	Zhang F, Appenzeller J 2015 Nano Lett. 15 301 Google Scholar
[9]	Kappera R, Voiry D, Yalcin S E, Branch B, Gupta G, Mohite A D, Chhowalla M 2014 Nat. Mater. 13 1128 Google Scholar
[10]	Kuc A, Heine T 2015 Chem. Soc. Rev. 44 2603 Google Scholar
[11]	Zhang F, Zhang H R, Krylyuk S, Milligan C A, Zhu Y Q, Zemlyanov D Y, Bendersky L A, Burton B P, Davydov A V, Appenzeller J 2019 Nat. Mater. 18 55 Google Scholar
[12]	Splendiani A, Sun L, Zhang Y B, Li T S, Kim J, Chim C Y, Galli G, Wang F 2010 Nano Lett. 10 1271 Google Scholar
[13]	苏向英 2017 低维过渡金属硫属化合物的电子性质及调控 (北京: 电子工业出版社) 第3页 Su X Y 2017 Electronic Properties and Control of Low-dimensional Transition Metal Chalcogenides (Beijing: Publishing House of Electronics Industry) p3 (in Chinese)
[14]	Radisavljevic B, Radenovic A, Brivio J, Giacometti V, Kis A 2011 Nat. Nanotechnol. 6 147 Google Scholar
[15]	Zhang Y J, Ye J T, Matsuhashi Y, Iwasa Y 2012 Nano Lett. 12 1136 Google Scholar
[16]	Agnihotri P, Dhakras P, Lee J U 2016 Nano Lett. 16 4355 Google Scholar
[17]	Lee Y T, Kang J H, Kwak K, Ahn J, Choi H T, Ju B K, Shokouh S H, Im S, Park M C, Hwang D K 2018 ACS Photonics 5 4745 Google Scholar
[18]	Bertolazzi S, Brivio J, Kis A 2011 ACS Nano 5 9703 Google Scholar
[19]	Castellanos-Gomez A, Poot M, Steele G A, van der Zant H S J, Agrait N, Rubio-Bollinger G 2012 Adv. Mater. 24 772 Google Scholar
[20]	周愈之 2018 物理学报 67 218102 Google Scholar Zhou Y Z 2018 Acta Phys. Sin. 67 218102 Google Scholar
[21]	Park J C, Yun S J, Kim H, Park J H, Chae S H, An S J, Kim J G, Kim S M, Kim K K, Lee Y H 2015 ACS Nano 9 6548 Google Scholar
[22]	Zhou L, Xu K, Zubair A, Liao A D, Fang W J, Ouyang F P, Lee Y H, Ueno K, Saito R, Palacios T, Kong J, Dresselhaus M S 2015 J. Am. Chem. Soc. 137 11892 Google Scholar
[23]	Naylor C H, Parkin W M, Ping J L, Gao Z L, Zhou Y R, Kim Y, Streller F, Carpick R W, Rappe A M, Drndic M, Kikkawa J M, Johnson A T C 2016 Nano Lett 16 4297 Google Scholar
[24]	Yang L, Zhang W F, Li J, Cheng S, Xie Z J, Chang H X 2017 ACS Nano 11 1964 Google Scholar
[25]	Zhu X K, Li A L, Wu D, Zhu P, Xiang H Y, Liu S, Sun J, Ouyang F P, Zhou Y, Xiong X 2019 J. Mater. Chem. C 7 10598 Google Scholar
[26]	Huang W J, G an, L, Li H Q, Ma Y, Zhai T Y 2018 Chem. – Eur. J. 24 15678 Google Scholar
[27]	Liu L N, Wu J X, Wu L Y, Ye M, Liu X Z, Wang Q, Hou S Y, Lu P F, Sun L F, Zheng J Y, Xing L, Gu L, Jiang X W, Xie L M, Jiao L Y 2018 Nat. Mater. 17 1108 Google Scholar
[28]	Wang Z Q, Shen Y H, Ito Y, Zheng Y Z, Du J, Fujita T, Hirata A, Tang Z, Chen M W 2018 ACS Nano 12 1571 Google Scholar
[29]	Wang Z, Sun J, Wang H L, Lei Y M, Xie Y, Wang G F, Zhao Y, Li X B, Xu H, Yang X B, Feng L P, Ma X H 2020 Appl. Surf. Sci. 504 144371 Google Scholar
[30]	Feng Q L, Mao N N, Wu J X, Xu H, Wang C M, Zhang J, Xie L M 2015 ACS Nano 9 7450 Google Scholar
[31]	Feng Q L, Zhu Y M, Hong J H, Zhang M, Duan W J, Mao N N, Wu J X, Xu H, Dong F L, Lin F, Jin C H, Wang C M, Zhang J, Xie L M 2014 Adv. Mater. 26 2648 Google Scholar
[32]	Tongay S, Narang D S, Kang J, Fan W, Ko C H, Luce A V, Wang K X, Suh J, Patel K D, Pathak V M, Li J B, Wu J Q 2014 Appl. Phys. Lett. 104 012101 Google Scholar
[33]	Li H L, Duan X D, Wu X P, Zhuang X J, Zhou H, Zhang Q L, Zhu X L, Hu W, Ren P Y, Guo P F, Ma L, Fan X P, Wang X X, Xu J Y, Pan A L, Duan X F 2014 J. Am. Chem. Soc. 136 3756 Google Scholar
[34]	Li H L, Zhang Q L, Duan X D, Wu X P, Fan X P, Zhu X L, Zhuang X J, Hu W, Zhou H, Pan A L, Duan X F 2015 J. Am. Chem. Soc. 137 5284 Google Scholar
[35]	Chen Y F, Dumcenco D O, Zhu Y M, Zhang X, Mao N N, Feng Q L, Zhang M, Zhang J, Tan P H, Huang Y S, Xie L M 2014 Nanoscale 6 2833 Google Scholar
[36]	Liu H F, Antwi K K A, Chua S, Chi D Z 2014 Nanoscale 6 624 Google Scholar
[37]	Chen Y F, Xi J Y, Dumcenco D O, Liu Z, Suenaga K, Wang D, Shuai Z G, Huang Y S, Xie L M 2013 ACS Nano 7 4610 Google Scholar
[38]	Liu S J, Huang L, Wu K D, Wei Z M, Huang B J, Meng X Q, Tongay S, Liu J, Li J B, Chen H D 2016 Appl. Phys. Lett. 109 112102 Google Scholar
[39]	Lin Y C, Dumcenco D O, Komsa H P, Niimi Y, Krasheninnikov A V, Huang Y S, Suenaga K 2014 Adv. Mater. 26 2857 Google Scholar
[40]	Zandalazini C I, Albanesi E A 2019 J. Magn. Magn. Mater. 484 146 Google Scholar
[41]	Fan S W, Yang L, Gao G Y 2019 Phys. Lett. A 383 3138 Google Scholar
[42]	Laroussi A, Berber M, Mokaddem A, Doumi B, Abid H, Boudali A 2019 Acta Phys. Pol. A 135 451 Google Scholar
[43]	Duerloo K N, Reed E J 2016 ACS Nano 10 289 Google Scholar
[44]	Kumar A, Strachan A, Onofrio N 2019 J. Appl. Phys. 125 204303 Google Scholar
[45]	Wang J Z, Yang T, Zhang Z D, Yang L 2018 Appl. Phys. Lett. 112 213104 Google Scholar
[46]	Young J, Reinecke T L 2017 Phys. Chem. Chem. Phys. 19 31874 Google Scholar
[47]	Huang H H, Fan X F, Singh D J, Zheng W T 2018 Phys. Chem. Chem. Phys. 20 26986 Google Scholar
[48]	Chen M W, Zhu L G, Chen Q F, Miao N H, Si C, Zhou J, Sun Z M 2020 J. Mater. Chem. C 8 721 Google Scholar
[49]	Koski K J, Wessells C D, Reed B W, Cha J J, Kong D S, Cui Y 2012 J. Am. Chem. Soc. 134 13773 Google Scholar
[50]	Gong Y J, Yuan H T, Wu C L, et al. 2018 Nat. Nanotechnol. 13 294 Google Scholar
[51]	Meng Y S, Elena Arroyo-de Dompablo M 2009 Energy Environ. Sci. 2 589 Google Scholar
[52]	Zhang Z X, Yang M Y, Zhao N, Wang L, Li Y Y 2019 Phys. Chem. Chem. Phys. 21 23441 Google Scholar
[53]	Py M A, Haering R R 1983 Can. J. Phys. 61 76 Google Scholar
[54]	Kan M, Wang J Y, Li X W, Zhang S H, Li Y W, Kawazoe Y, Sun Q, Jena P 2014 J. Phys. Chem. C 118 1515 Google Scholar
[55]	Tan S J R, Abdelwahab I, Ding Z J, Zhao X X, Yang T S, Loke G Z J, Lin H, Verzhbitskiy I, Poh S M, Xu H, Nai C T, Zhou W, Eda G, Jia B H, Loh K P 2017 J. Am. Chem. Soc. 139 2504 Google Scholar
[56]	Xia J, Wang J, Chao D L, Chen Z, Liu Z, Kuo J L, Yan J X, Shen Z X 2017 Nanoscale 9 7533 Google Scholar
[57]	Sun L F, Yan X X, Zheng J Y, Yu H D, Lu Z X, Gao S P, Liu L N, Pan X Q, Wang D, Wang Z G, Wang P, Jiao L Y 2018 Nano Lett. 18 3435 Google Scholar
[58]	Eshete Y A, Ling N, Kim S, Kim D, Hwang G, Cho S, Yang H 2019 Adv. Funct. Mater. 29 1904504 Google Scholar
[59]	Leng K, Chen Z X, Zhao X X, Tang W, Tian B B, Nai C T, Zhou W, Loh K P 2016 ACS Nano 10 9208 Google Scholar
[60]	Tan C L, Zhao W, Chaturvedi A, Fei Z, Zeng Z Y, Chen J Z, Huang Y, Ercius P, Luo Z M, Qi X Y, Chen B, Lai Z C, Li B, Zhang X, Yang J, Zong Y, Jin C H, Zheng H M, Kloc C, Zhang H 2016 Small 12 1866 Google Scholar
[61]	Wang X F, Shen X, Wang Z X, Yu R C, Chen L Q 2014 ACS Nano 8 11394 Google Scholar
[62]	Koley S, Basu S 2020 J. Magn. Magn. Mater. 499 166294 Google Scholar
[63]	Li P, Jeong J Y, Jin B J, Zhang K, Park J H 2020 Energy Storage Mater. 25 687 Google Scholar
[64]	Island J O, Kuc A, Diependaal E H, Bratschitsch R, van der Zant H S J, Heine T, Castellanos-Gomez A 2016 Nanoscale 8 2589 Google Scholar
[65]	Duerloo K N, Li Y, Reed E J 2014 Nat. Commun. 5 4214 Google Scholar
[66]	Song S, Keum D H, Cho S, Perello D, Kim Y, Lee Y H 2016 Nano Letters 16 188 Google Scholar
[67]	Huang H H, Fan X F, Singh D J, Chen H, Jiang Q, Zheng W T 2016 Phys. Chem. Chem. Phys. 18 4086 Google Scholar
[68]	Fan X F, Singh D J, Jiang Q, Zheng W T 2016 Phys. Chem. Chem. Phys. 18 12080 Google Scholar
[69]	Tang Q 2018 J. Mater. Chem. C 6 9561 Google Scholar
[70]	Johari P, Shenoy V B 2012 ACS Nano 6 5449 Google Scholar
[71]	Apte A, Kochat V, Rajak P, et al. 2018 ACS Nano 12 3468 Google Scholar
[72]	Keum D H, Cho S, Kim J H, et al. 2015 Nat. Phys. 11 482 Google Scholar
[73]	Wang Z Y, Sun Y Y, Abdelwahab I, et al. 2018 ACS Nano 12 12619 Google Scholar
[74]	Yin X M, Tang C S, Wu D, et al. 2019 Adv. Sci. 6 1802093 Google Scholar
[75]	Sung J H, Heo H, Si S, Kim Y H, Noh H R, Song K, Kim J, Lee C S, Seo S Y, Kim D H, Kim H K, Yeom H W, Kim T H, Choi S Y, Kim J S, Jo M H 2017 Nat. Nanotechnol. 12 1064 Google Scholar
[76]	Nakata Y, Sugawara K, Shimizu R, Okada Y, Han P, Hitosugi T, Ueno K, Sato T, Takahashi T 2016 NPG Asia Mater. 8 e231 Google Scholar
[77]	Chen J C, Feng Z H, Fan S Q, et al. 2017 ACS Appl. Mater. Interfaces 9 30107 Google Scholar
[78]	Cho S, Kim S, Kim J H, Zhao J, Seok J, Keum D H, Baik J, Choe D H, Chang K J, Suenaga K, Kim S W, Lee Y H, Yang H 2015 Science 349 625 Google Scholar
[79]	Yu Y F, Nam G H, He Q Y, et al. 2018 Nat. Chem. 10 638 Google Scholar
[80]	Chen Z R, Nan H Y, Liu Z, Wang X Y, Gu X F, Xiao S Q 2019 J. Raman Spectrosc. 50 755 Google Scholar
[81]	Si C, Choe D, Xie W Y, Wang H, Sun Z M, Bang J, Zhang S B 2019 Nano Lett. 19 3612 Google Scholar
[82]	Azcatl A, Qin X Y, Prakash A, et al. 2016 Nano Lett. 16 5437 Google Scholar
[83]	Cheng C C, Lu A Y, Tseng C C, Yang X L, Hedhili M N, Chen M C, Wei K H, Li L J 2016 Nano Energy 30 846 Google Scholar
[84]	O’Brien M, Lee K, Morrish R, Berner N C, McEvoy N, Wolden C A, Duesberg G S 2014 Chem. Phys. Lett. 615 6 Google Scholar
[85]	Jin J C, Zhang D P, Qin X N, Yang Y, Huang Y, Guan H, He Q C, Fan P, Lv W Z 2019 Nanomaterials 9 102 Google Scholar
[86]	Zhu J, Wang Z, Yu H 2017 J. Am. Chem. Soc. 139 10216 Google Scholar
[87]	Shawkat M S, Gil J, Han S S, et al. 2020 ACS Appl. Mater. Interfaces 12 14341 Google Scholar
[88]	Nan H Y, Jiang J, Xiao S Q, et al. 2018 Nanotechnology 30 034004 Google Scholar
[89]	Taniguchi K, Matsumoto A, Shimotani H, Takagi H 2012 Appl, . Phys. Lett. 101 042603 Google Scholar
[90]	Ye J T, Zhang Y J, Akashi R, Bahramy M S, Arita R, Iwasa Y 2012 Science 338 1193 Google Scholar
[91]	何学侠, 刘富才, 曾庆圣, 刘政 2015 化学学报 73 924 Google Scholar He X X, Liu F C, Zeng Q S, Liu Z 2015 Acta Chim. Sin. 73 924 Google Scholar
[92]	Li Y, Duerloo K A N, Wauson K, Reed E J 2016 Nat. Commun. 7 10671 Google Scholar
[93]	Wang Y, Xiao J, Zhu H 2017 Nature 550 487 Google Scholar
[94]	Bischoff F, Auwarter W, Barth J V, Schiffrin A, Fuhrer M, Weber B 2017 Chem. Mater. 29 9907 Google Scholar

[1]	李腾, 邱文婷, 龚深. 基于相场方法的多孔合金马氏体相变模拟. 物理学报, 2023, 72(14): 148102. doi: 10.7498/aps.72.20230212
[2]	王铄, 王文辉, 吕俊鹏, 倪振华. 化学气相沉积法制备大面积二维材料薄膜: 方法与机制. 物理学报, 2021, 70(2): 026802. doi: 10.7498/aps.70.20201398
[3]	方云团, 王张鑫, 范尔盼, 李小雪, 王洪金. 基于结构反转二维光子晶体的拓扑相变及拓扑边界态的构建. 物理学报, 2020, 69(18): 184101. doi: 10.7498/aps.69.20200415
[4]	刘慧莹, 王树申, 林恒福. 单层haeckelites结构Ⅲ族金属硫族化合物MX (M = Al, Ga, In; X = S, Se, Te). 物理学报, 2020, 69(14): 146802. doi: 10.7498/aps.69.20191955
[5]	罗雄, 孟威威, 陈国旭佳, 管晓溪, 贾双凤, 郑赫, 王建波. 二维Nb₂SiTe₄基化合物稳定性、电子结构和光学性质的第一性原理研究. 物理学报, 2020, 69(19): 197102. doi: 10.7498/aps.69.20200848
[6]	马嵩松, 舒天宇, 朱家旗, 李锴, 吴惠桢. Ⅳ-Ⅵ族化合物半导体异质结二维电子气研究进展. 物理学报, 2019, 68(16): 166801. doi: 10.7498/aps.68.20191074
[7]	高英俊, 罗志荣, 黄创高, 卢强华, 林葵. 晶体相场方法研究二维六角相向正方相结构转变. 物理学报, 2013, 62(5): 050507. doi: 10.7498/aps.62.050507
[8]	计时鸣, 翁晓星, 谭大鹏. 基于水平集方法二维模型的软性磨粒两相流流场特性分析方法. 物理学报, 2012, 61(1): 010205. doi: 10.7498/aps.61.010205
[9]	张贺, 骆军, 朱航天, 刘泉林, 梁敬魁, 饶光辉. Cu掺杂AgSbTe2化合物的相稳定、晶体结构及热电性能. 物理学报, 2012, 61(8): 086101. doi: 10.7498/aps.61.086101
[10]	宋庆功, 姜恩永, 裴海林, 康建海, 郭英. 插层化合物LixTiS2中Li离子-空位二维有序结构稳定性的第一性原理研究. 物理学报, 2007, 56(8): 4817-4822. doi: 10.7498/aps.56.4817
[11]	张立刚, 陈静, 朱伯铨, 李亚伟, 汪汝武, 李云宝, 张国宏, 李钰. NaZn13型结构LaFe13－xAlxCy化合物的磁熵变与磁相变的研究. 物理学报, 2006, 55(10): 5506-5510. doi: 10.7498/aps.55.5506
[12]	白锁柱, 姚斌, 郑大方, 邢国忠, 苏文辉. 新型BCN化合物的结构表征和相转变. 物理学报, 2006, 55(11): 5740-5744. doi: 10.7498/aps.55.5740
[13]	郭光华, 张海贝. 化合物HoMn6Sn6的磁晶各向异性及自旋重取向相变研究. 物理学报, 2005, 54(12): 5879-5883. doi: 10.7498/aps.54.5879
[14]	王文全, 闫羽, 王向群, 王学凤, 苏峰, 金汉民. Gd3Co29-xCrx新相化合物的结构与磁性. 物理学报, 2003, 52(3): 647-651. doi: 10.7498/aps.52.647
[15]	赵代平, 荆涛, 柳百成. 相场方法模拟铝合金三维枝晶生长. 物理学报, 2003, 52(7): 1737-1742. doi: 10.7498/aps.52.1737
[16]	胡社军, 特古斯, 魏兴钊, 张雷, 曾德长, 刘正义, F.R.deBoer, K.H.J.Buschow. Ho2(Co,Si)17化合物的结构与磁晶各向异性. 物理学报, 2000, 49(2): 355-360. doi: 10.7498/aps.49.355
[17]	傅正民, 李震武, 李文秀. 新化合物——Sr2CaMoO6的相变与晶体结构. 物理学报, 1992, 41(6): 937-947. doi: 10.7498/aps.41.937
[18]	段文晖, 顾秉林, 朱嘉麟. 硫族化合物半导体CdSe,CdTe和SnSe的电子结构. 物理学报, 1990, 39(3): 437-445. doi: 10.7498/aps.39.437
[19]	杨桂林, 徐游, 卢德林, 翟宏如. 稀土化合物RX的晶场参数分析. 物理学报, 1986, 35(9): 1142-1147. doi: 10.7498/aps.35.1142
[20]	徐建华, 谢雷鸣, 徐永年. NiSi2化合物的电子结构. 物理学报, 1984, 33(10): 1480-1484. doi: 10.7498/aps.33.1480

计量

文章访问数: 14337
PDF下载量: 571
被引次数: 0

姓名
邮箱
手机号码
标题
留言内容
验证码

搜索

留言板