Effect of Ti content on preparation and properties of TiB<sub>2</sub>-SiC-Ti materials

He Xiao-Xun; Li Bing-Sheng; Liu Rui; Zhang Tong-Min; Cao Xing-Zhong; Chen Li-Ming; Xu Shuai

doi:10.7498/aps.71.20220530

Abstract

Since the 21st century, low atomic number material coating has been considered as one of methods for treating the first wall of controllable thermonuclear fusion device . The TiB₂ material with high melting point, high hardness, low coefficient of thermal expansion, excellent wear resistance and low atomic number has entered into people’s field of vision. Single TiB₂ is difficult to sinter and process into other products. Therefore, adding ceramic and metal additives to TiB₂ matrix material to effectively improve the mechanical properties and processability of the material has become a research hotspot. On the basis of the existing researches of TiB₂-SiC, in the present work the metal Ti powder is added as the second additive to improve the properties of TiB₂ composite. The TiB₂ and SiC are mixed at a mass ratio of 2 to 3, then two kinds of TiB₂-SiC-Ti materials with different amounts of Ti content are prepared by spark plasma sintering (SPS) technology. The materials are irradiated by a He⁺ beam with energy of 60 keV and ion fluence of 2 × 10¹⁷ ions/cm² at room temperature. The material is heat-treated at 1500 ℃ before and also after irradiation. The performances of prepared samples, the effect of irradiation on materials and the results of high temperature heat treatment are characterized by energy dispersive spectroscopy, Raman spectrum, grazing angle x-ray diffraction spectrum, Vickers hardness, wear resistance test, and scanning electron microscope. The results show that the surface morphology and toughness of TiB₂-SiC-Ti material with 3% Ti mass fraction are poor as shown in SEM images. The wear resistance test indicates that the material surface is seriously worn and the wear resistance is poor. The X-ray diffraction spectrum and Raman spectra show that the material is oxidized seriously at 1500 ℃, which is likely to be the cause of the poor compactness of materials. Raman spectra, Grazing angle X-ray diffraction spectrum and some Vickers hardness data before and after irradiation indicate that the material with low Ti content possess better crystal structure and weaker irradiation hardening. In conclusion, the TiB₂-SiC-Ti material with 3% Ti mass fraction exhibits lower density, poorer wear resistance and lower hardness, while the material with lower Ti mass fraction is more resistant to irradiation than the material with 6% Ti mass fraction at room temperature.

Keywords:

Authors and contacts

1.
State Key Laboratory of Environment-Friendly Energy Materials, Southwest University of Science and Technology, Mianyang 621010, China
2.
Institute of Solid State Physics, Chinese Academy of Sciences, Hefei 230000, China
3.
Institute of Modern Physics, Chinese Academy of Sciences, Lanzhou 730000, China
4.
Institute of High Energy Physics, Chinese Academy of Sciences, Beijing 100049, China
5.
School of Materials Science and Engineering, Southwest University of Science and Technology, Mianyang 621010, China

Corresponding author: Li Bing-Sheng, libingshengmvp@163.com

Funds: Project supported by the National Natural Science Foundation of China (Grant No. 12075194).

FullText HTML : translate this paragraph

References

[1]	Stacey Jr W M, Abdou M A, Bertoncini P J, Bolta C C, Brooks J N, Evans K, Fasolo J A, Jung J C, Kustom R L, Maroni A, Mattas R F, Monich J S, Moretti A, Mills F E, Misra B, Norem J H, Patten J S, Praeg W F, Smelser P, Smith D L, Stevens H C, Turner L, Wang S T, Youngdahl C K 1976 Proceedings of the Second Topical Meeting on “The Technology of Controlled Nuclear Fusion” Richland, 1976 p21
[2]	Kaminsky M 1976 Proceedings of the Second Topical Meeting on “The Technology of Controlled Nuclear Fusion” Richland, 1976 p169
[3]	Rossing T D, Das S K, Kaminsky M 1977 J. Vac. Sci. Technol. 14 550 Google Scholar
[4]	Mattox D M 1978 First Wall Coating Workshop Report Sandia Laboratories, Albuquerque, 1978 p1
[5]	Boutard J L, Alamo A, Lindau R, Rieth M 2008 CR. Phys. 9 287 Google Scholar
[6]	Zhao G L, Huang C Z, Liu H L, Zou B, Zhu H T, Wang J 2014 Mater. Sci. Eng. A 606 108 Google Scholar
[7]	Bhattacharya A, Parish C M, Koyanagi T, Petrie C M, King D, Hilmas G, Fahrenholtz W G, Zinkle S J, Katoh Y 2019 Acta Mater. 165 26 Google Scholar
[8]	Istgaldi H, Nayebi B, Ahmadi Z, Shahi P, Asl M S 2020 Ceram. Int. 46 23155 Google Scholar
[9]	Konigshofer R, Furnsinn S, Steinkellner P 2005 Int. J. Refract. Met. H. 23 350 Google Scholar
[10]	Murthy T S R C, Balasubramaniam R, Basu B, Suri A K, Mungole M N 2006 J. Eur. Ceram. Soc. 26 187 Google Scholar
[11]	Asl M S, Kakroudi M G, Kondolaji R A, Nasiri H 2015 Ceram. Int. 41 5843 Google Scholar
[12]	Germi M D, Mahaseni Z H, Ahmadi Z, Asl M S 2018 Mater. Charact. 145 225 Google Scholar
[13]	Namini A S, Motallebzadeh A, Nayebi B, Asl M S, Azadbeh M 2019 Mater. Chem. Phys. 223 789 Google Scholar
[14]	Mahaseni Z H, Germi M D, Ahmadi Z, Asl M S 2018 Ceram. Int. 44 13367 Google Scholar
[15]	Nguyen V H, Asl M S, Mahaseni Z H, Germi M D, Delbari S A, Le Q V, Ahmadi Z, Shokouhimehr M, Namini A S, Mohammadi M 2020 Ceram. Int. 46 25341 Google Scholar
[16]	Ahmadi Z, Nayebi B, Asl M S, Farahbakhsh I, Balak Z 2018 Ceram. Int. 44 11431 Google Scholar
[17]	Zou B, Huang C Z, Song J P, Liu Z Y, Liu L, Zhao Y 2012 Mater. Sci. Eng. A 540 235 Google Scholar
[18]	Song J P, Huang C Z, Lv M, Zou B, Wang S Y, Wang J, An J 2014 Mater. Sci. Eng. A 605 137 Google Scholar
[19]	Chlup Z, Baca L, Halasova M, Neubauer E, Hadraba H, Stelzer N, Roupcova P 2015 J. Eur. Ceram. Soc. 35 2745 Google Scholar
[20]	Zhang Z H, Shen X B, Wang F C, Lee S K, Fan Q B, Cao M S 2012 Scripta Mater. 66 167 Google Scholar
[21]	Mukhopadhyay A, Raju G B, Basu B, Suri A K 2009 J. Eur. Ceram. Soc. 29 505 Google Scholar
[22]	Asl M S, Namini A S, Kakroudi M G 2016 Ceram. Int. 42 5375 Google Scholar
[23]	Murthy T S R C, Subramanian C, Fotedar R K, Gonal M R, Sengupta P, Kumar S, Suri A K 2009 Int. J. Refract. Met. H. 27 629 Google Scholar
[24]	Li M, Zhou X B, Yang H, Du S Y, Huang Q 2018 Scripta Mater. 143 149 Google Scholar
[25]	He Q L, Tian S, Xie J J, Xiang C L, Wang H, Wang W M, Fu Z Y 2020 J. Eur. Ceram. Soc. 40 2862 Google Scholar
[26]	Kovalcikova A, Tatarko P, Sedlak R, Medved D, Chlup Z, Mudra E, Dusza J 2020 J. Eur. Ceram. Soc. 40 4860 Google Scholar
[27]	Singlard M, Tessier-Doyen N, Chevallier G, Oriol S, Fiore G, Vieille B, Estournes C, Vardelle M, Rossignol S 2018 Ceram. Int. 44 22357 Google Scholar
[28]	Zou B, Ji W B, Huang C Z, Xu K T, Li S S 2014 Int. J. Refract. Met. H. 47 1 Google Scholar
[29]	Cai X Q, Wang D P, Wang Y, Yang Z W 2021 J. Manuf. Processes 64 1349 Google Scholar
[30]	Wang Y, Liu Q, Zhang B, Zhang H Q, Jin Y C, Zhong Z X, Ye J, Ren Y H, Ye F, Wang W 2021 Ceram. Int. 47 10665 Google Scholar
[31]	Song B, Yang W, Liu X M, Chen H Y, Akhlaghi M 2021 Ceram. Int. 47 29174 Google Scholar
[32]	Zhao B, Zhao Y Q, Hou Z M, Luo Y Y, Zhang W, Zhang P X, Wu J P 2018 Fusion Eng. Des. 137 405 Google Scholar
[33]	Vajdi M, Moghanlou F S, Ahmadi Z, Motallebzadeh A, Asl M S 2019 Ceram. Int. 45 8333 Google Scholar
[34]	Tatarko P, Grasso S, Kovalcikova A, Medved D, Dlouhy I, Reece M J 2020 J. Eur. Ceram. Soc. 40 1111 Google Scholar
[35]	Iltis X, Lefebvre F, Lemaignan C 1995 J. Nucl. Mater. 224 109 Google Scholar
[36]	Garner A, Baxter F, Frankel P, Topping M, Harte A, Slater T, Tejland P, Romero J, Darby E, Cole-Baker A, Gass M, Preuss M 2018 Zirconium in the Nuclear Industry: 18 th International Symposium West Conshohocken, 2018 p491
[37]	Wang J, Ren D L, Chen L L, Man G A, Zhang H Y, Zhang H P, Luo L H, Li W P, Pan Y B, Gao P F, Zhu Y B, Wang Z G 2020 J. Nucl. Mater. 539 152275 Google Scholar
[38]	Bhattacharya A, Parish C M, Koyanagi T, Petrie C M, King D, Hilmas G, Fahrenholtz W G, Zinkle S J, Katoh Y 2019 Acta Materialia 165 26
[39]	Golanski G, Purzynska H 2022 Int. J. Pres. Ves. Pip. 195 104574 Google Scholar
[40]	Paul B, Kishor J, Karthik A, Murthy T S R C, Sunil S 2022 Int. J. Refract. Met. H. 103 105752 Google Scholar
[41]	Guo W C, He Q L, Wang A Y, Tian T, Liu C, Hu L X, Wang H, Wang W M, Fu Z Y 2021 J. Mater. Res. Technol. 15 6700 Google Scholar
[42]	Rafaja D, Valvoda V, Perry A J, Treglio J R 1997 Surf. Coat. Tech. 92 135 Google Scholar
[43]	Lu X R, Shu X Y, Wang L, Shao D D, Zhang H B, Zhang K B, Xie Y 2019 J. Alloys Compd. 771 973 Google Scholar
[44]	Agarwal S, Chen Q, Koyanagi T, Zhao Y, Zinkle S J, Weber W J 2019 J. Nucl. Mater. 526 151778 Google Scholar
[45]	Lopez-Honorato E, Meadows P J, Shatwell R A, Xiao P 2010 Carbon 48 881
[46]	Baca L, Stelzer N 2008 J. Eur. Ceram. Soc. 28 907 Google Scholar
[47]	Buixaderas E, Anghel E M, Atkinson I, Simon P, Bratan V, Petrescu S 2015 Ceram. Int. 41 2680 Google Scholar
[48]	Ohsaka T, Izumi F, Fujiki Y 1978 J. Raman Spectrosc. 7 321 Google Scholar
[49]	Bezrodna T, Gavrilko T, Puchkovska G, Shimanovska V, Baran J, Marchewka M 2002 J. Mol. Struct. 614 315 Google Scholar
[50]	Santara B, Giri P K, Imakita K, Fujii M 2014 J. Phys. D Appl. Phys. 47 215302 Google Scholar
[51]	Hernandez A, Barrios M L, Sanchez M L 2019 Mater. Today 13 446
[52]	Zheng G M, Zhao J, Zhou Y H 2012 Wear 290 41
[53]	Wang R D, Li P, Li B S, Hu L J, Huang F, Huang Q 2022 Corros. Sci. 201 110301 Google Scholar
[54]	Wang H, Ren F, Tang J, Qin W J, Hu L L, Dong L, Yang B, Cai G X, Jiang C Z 2018 Acta Mater. 144 691 Google Scholar
[55]	Zhang W, Chen L, Xu C G, Lu W Y, Wang Y J, Ouyang J H, Zhou Y 2021 J. Mater. Sci. Technol. 72 23 Google Scholar
[56]	Wang Y, Liu Q, Zhang B, Zhang H Q, Jin Y C, Zhong Z X, Ye J, Ren Y H, Ye F, Wang W 2021 Ceramics International 47 10665

Cited By

图 1 SRIM 模拟60 keV, 2 × 10¹⁷ ions/cm² He⁺ 辐照TiB₂-SiC-Ti复合材料得到的损伤深度分布及He原子浓度深度分布图

Figure 1. The depth distribution of damage and concentration of He atoms calculated with SRIM for TiB₂-SiC-Ti irradiated with 60 keV He⁺ ions to a fluence of 2 × 10¹⁷ ions/cm²

DownLoad: Full-Size Img PowerPoint

图 2 (a) TiB₂-SiC-Ti(Ti的质量分数为3%)样品和 (b) TiB₂-SiC-Ti(Ti的质量分数为6%)样品的能量色散X射线光谱图

Figure 2. Energy dispersion X-ray spectroscopy of TiB₂-SiC-Ti ((the mass fraction of Ti is 3%)) samples (a) and TiB₂-SiC-Ti (the mass fraction of Ti is 6%) samples (b).

DownLoad: Full-Size Img PowerPoint

图 3 制备态、辐照前1500 ℃热处理、室温下氦离子辐照和辐照后1500 ℃退火4种条件下TiB₂-SiC-Ti(Ti的质量分数为3%)样品(a)和TiB₂-SiC-Ti(Ti的质量分数为6%)样品(b)的拉曼光谱

Figure 3. Raman spectra of TiB₂-SiC-Ti (the mass fraction of Ti is 3%) (a) and TiB₂-SiC-Ti (the mass fraction of Ti is 6%) (b) under four conditions: Original state, heat treatment at 1500 ℃ before irradiation, irradiation with 60 keV to a fluence of 2 × 10¹⁷ ions/cm² at room temperature followed by annealing at 1500 ℃.

DownLoad: Full-Size Img PowerPoint

图 4 TiB₂-SiC-Ti(Ti的质量分数为3%)和TiB₂-SiC-Ti(Ti的质量分数为6%)烧结样品的X射线衍射图谱

Figure 4. X-ray diffraction patterns of TiB₂-SiC-Ti (the mass fraction of Ti is 3%) and TiB₂-SiC-Ti (the mass fraction of Ti is 6%).

DownLoad: Full-Size Img PowerPoint

图 5 0.5°入射角下TiB₂-SiC-Ti(Ti的质量分数为3%)　(a) 和TiB₂-SiC-Ti(Ti的质量分数为6%) (b) 样品的X射线衍射图谱, 包括原始状态、室温下60 keV, 2 × 10¹⁷ ions/cm² He⁺ 辐照以及辐照后1500 ℃退火3种条件

Figure 5. Grazing angle X-ray diffraction patterns of TiB₂-SiC-Ti (the mass fraction of Ti is 3%) (a) and TiB₂-SiC-Ti (the mass fraction of Ti is 6%) (b) at 0.5° incident angle, including the as-grown, 60 keV, 2 × 10¹⁷ions/cm² irradiation at room temperature followed by annealing at 1500 ℃

DownLoad: Full-Size Img PowerPoint

图 6 维氏硬度测试的实测硬度图　(a) TiB₂-SiC-Ti(Ti的质量分数为3%); (b) 2 × 10¹⁷ ions/cm² He⁺室温辐照的TiB₂-SiC-Ti(Ti的质量分数为3%); (c) TiB₂-SiC-Ti(Ti的质量分数为6%); (d) 2 × 10¹⁷ ions/cm² He⁺ 室温辐照的TiB₂-SiC-Ti(Ti的质量分数为6%)

Figure 6. Measured hardness diagram of Vickers hardness test: (a) TiB₂-SiC-Ti(the mass fraction of Ti is 3%); (b) TiB₂-SiC-Ti(the mass fraction of Ti is 3%) irradiated with He⁺ to a fluence of 2 × 10¹⁷ ions/cm² at room temperature; (c) TiB₂-SiC-Ti (the mass fraction of Ti is 6%); (d) TiB₂-SiC-Ti (the mass fraction of Ti is 6%) irradiated with He⁺ to a fluence of 2 × 10¹⁷ ions/cm² at room temperature.

DownLoad: Full-Size Img PowerPoint

图 7 原始样品的SEM图像　(a) TiB₂-SiC-Ti (Ti的质量分数为3%); (b) TiB₂-SiC-Ti (Ti的质量分数为6%)

Figure 7. Scanning electron microscope images of original sample: (a) TiB₂-SiC-Ti (the mass fraction of Ti is 3%); (b) TiB₂-SiC-Ti (the mass fraction of Ti is 6%).

DownLoad: Full-Size Img PowerPoint

图 8 维氏硬度测试后压痕处的SEM图像　(a), (c), (e) TiB₂-SiC-Ti(Ti的质量分数为3%); (b), (d), (f) TiB₂-SiC-Ti(Ti的质量分数为6%)

Figure 8. Scanning electron microscope image of indentation after Vickers hardness test: (a), (c), (e) TiB₂-SiC-Ti (the mass fraction of Ti is 3%); (b), (d), (f) TiB₂-SiC-Ti (the mass fraction of Ti is 6%).

DownLoad: Full-Size Img PowerPoint

图 9 样品的摩擦系数-时间曲线　(a) TiB₂-SiC-Ti(Ti的质量分数为3%); (b) TiB₂-SiC-Ti(Ti的质量分数为6%)

Figure 9. The friction coefficient-time curves of the samples: (a) TiB₂-SiC-%Ti (the mass fraction of Ti is 3%); (b) TiB₂- SiC-Ti (the mass fraction of Ti is 6%).

DownLoad: Full-Size Img PowerPoint

图 10 样品的磨损位置二维特征线轮廓　(a) TiB₂-SiC-Ti(Ti的质量分数为3%); (b) TiB₂-SiC-Ti(Ti的质量分数为6%)

Figure 10. Two-dimensional characteristic line profiles of wear locations of samples: (a) TiB₂-SiC-%Ti (the mass fraction of Ti is 3%); (b) TiB₂-SiC-Ti (the mass fraction of Ti is 6%).

DownLoad: Full-Size Img PowerPoint

图 11 样品的磨损位置三维形貌　(a) TiB₂-SiC-Ti(Ti的质量分数为3%); (b) TiB₂-SiC-Ti(Ti的质量分数为6%)

Figure 11. Three-dimensional morphologies of wear position of samples: (a) TiB₂-SiC-Ti (the mass fraction of Ti is 3%); (b) TiB₂- SiC-Ti (the mass fraction of Ti is 6%).

DownLoad: Full-Size Img PowerPoint

表 1 TiB₂-SiC-Ti复合材料中各物质的拉曼峰

Table 1. Raman peaks of various substances in TiB₂-SiC-Ti composites.

物质	峰的位置/cm^–1	振动模式
TiB₂	275, 418	声子振动
TiO₂	227	二阶散射峰
	446	平面外振动
	610	Ti-O拉伸振动
SiO₂	708	Si-O拉伸振动
SiC	794, 958	Si-C伸缩振动
C	1345, 1590	面内伸缩振动

DownLoad: CSV

表 2 TiO₂位于610 cm^–1处的峰的有效面积

Table 2. The effective area of TiO₂ peak at 610 cm^–1.

材料	条件	有效面积	面积增加率/%
TiB₂-SiC-Ti (Ti的质量分数为3%)	1500 ℃热处理	35209	442
TiB₂-SiC-Ti (Ti的质量分数为3%)	辐照后1500 ℃退火	190919	442
TiB₂-SiC-Ti (Ti的质量分数为6%)	1500 ℃热处理	48570	131
TiB₂-SiC-Ti (Ti的质量分数为6%)	辐照后1500 ℃退火	112214	131

DownLoad: CSV

表 3 两种Ti含量、相同TiB₂晶面指数处的峰强和半高宽

Table 3. Peak intensity and FWHM of samples at the same TiB₂ crystal plane index.

晶面指数		(001)	(100)	(101)	(002)	(201)	(112)
TiB₂-SiC-Ti (Ti的质量分数为3%)	峰高	696	1624	2708	244	280	240
TiB₂-SiC-Ti (Ti的质量分数为3%)	半高宽	0.163	0.244	0.211	0.287	0.332	0.342
TiB₂-SiC-Ti (Ti的质量分数为6%)	峰高	715	1623	2870	295	290	266
TiB₂-SiC-Ti (Ti的质量分数为6%)	半高宽	0.159	0.210	0.211	0.251	0.315	0.334

DownLoad: CSV

表 4 1 kgf载荷下的维氏硬度值

Table 4. Vickers hardness value under 1 kgf load.

样品	HV	误差	硬度变化/%
TiB₂-SiC-Ti (Ti的质量分数为3%)	290.104	± 0.03	6.9
TiB₂-SiC-Ti (Ti的质量分数为3%) (辐照)	311.489	± 1.22	6.9
TiB₂-SiC-Ti (Ti的质量分数为6%)	344.824	± 17.80	9.2
TiB₂-SiC-Ti (Ti的质量分数为6%) (辐照)	379.775	± 0.62	9.2

DownLoad: CSV

[1]	Stacey Jr W M, Abdou M A, Bertoncini P J, Bolta C C, Brooks J N, Evans K, Fasolo J A, Jung J C, Kustom R L, Maroni A, Mattas R F, Monich J S, Moretti A, Mills F E, Misra B, Norem J H, Patten J S, Praeg W F, Smelser P, Smith D L, Stevens H C, Turner L, Wang S T, Youngdahl C K 1976 Proceedings of the Second Topical Meeting on “The Technology of Controlled Nuclear Fusion” Richland, 1976 p21
[2]	Kaminsky M 1976 Proceedings of the Second Topical Meeting on “The Technology of Controlled Nuclear Fusion” Richland, 1976 p169
[3]	Rossing T D, Das S K, Kaminsky M 1977 J. Vac. Sci. Technol. 14 550 Google Scholar
[4]	Mattox D M 1978 First Wall Coating Workshop Report Sandia Laboratories, Albuquerque, 1978 p1
[5]	Boutard J L, Alamo A, Lindau R, Rieth M 2008 CR. Phys. 9 287 Google Scholar
[6]	Zhao G L, Huang C Z, Liu H L, Zou B, Zhu H T, Wang J 2014 Mater. Sci. Eng. A 606 108 Google Scholar
[7]	Bhattacharya A, Parish C M, Koyanagi T, Petrie C M, King D, Hilmas G, Fahrenholtz W G, Zinkle S J, Katoh Y 2019 Acta Mater. 165 26 Google Scholar
[8]	Istgaldi H, Nayebi B, Ahmadi Z, Shahi P, Asl M S 2020 Ceram. Int. 46 23155 Google Scholar
[9]	Konigshofer R, Furnsinn S, Steinkellner P 2005 Int. J. Refract. Met. H. 23 350 Google Scholar
[10]	Murthy T S R C, Balasubramaniam R, Basu B, Suri A K, Mungole M N 2006 J. Eur. Ceram. Soc. 26 187 Google Scholar
[11]	Asl M S, Kakroudi M G, Kondolaji R A, Nasiri H 2015 Ceram. Int. 41 5843 Google Scholar
[12]	Germi M D, Mahaseni Z H, Ahmadi Z, Asl M S 2018 Mater. Charact. 145 225 Google Scholar
[13]	Namini A S, Motallebzadeh A, Nayebi B, Asl M S, Azadbeh M 2019 Mater. Chem. Phys. 223 789 Google Scholar
[14]	Mahaseni Z H, Germi M D, Ahmadi Z, Asl M S 2018 Ceram. Int. 44 13367 Google Scholar
[15]	Nguyen V H, Asl M S, Mahaseni Z H, Germi M D, Delbari S A, Le Q V, Ahmadi Z, Shokouhimehr M, Namini A S, Mohammadi M 2020 Ceram. Int. 46 25341 Google Scholar
[16]	Ahmadi Z, Nayebi B, Asl M S, Farahbakhsh I, Balak Z 2018 Ceram. Int. 44 11431 Google Scholar
[17]	Zou B, Huang C Z, Song J P, Liu Z Y, Liu L, Zhao Y 2012 Mater. Sci. Eng. A 540 235 Google Scholar
[18]	Song J P, Huang C Z, Lv M, Zou B, Wang S Y, Wang J, An J 2014 Mater. Sci. Eng. A 605 137 Google Scholar
[19]	Chlup Z, Baca L, Halasova M, Neubauer E, Hadraba H, Stelzer N, Roupcova P 2015 J. Eur. Ceram. Soc. 35 2745 Google Scholar
[20]	Zhang Z H, Shen X B, Wang F C, Lee S K, Fan Q B, Cao M S 2012 Scripta Mater. 66 167 Google Scholar
[21]	Mukhopadhyay A, Raju G B, Basu B, Suri A K 2009 J. Eur. Ceram. Soc. 29 505 Google Scholar
[22]	Asl M S, Namini A S, Kakroudi M G 2016 Ceram. Int. 42 5375 Google Scholar
[23]	Murthy T S R C, Subramanian C, Fotedar R K, Gonal M R, Sengupta P, Kumar S, Suri A K 2009 Int. J. Refract. Met. H. 27 629 Google Scholar
[24]	Li M, Zhou X B, Yang H, Du S Y, Huang Q 2018 Scripta Mater. 143 149 Google Scholar
[25]	He Q L, Tian S, Xie J J, Xiang C L, Wang H, Wang W M, Fu Z Y 2020 J. Eur. Ceram. Soc. 40 2862 Google Scholar
[26]	Kovalcikova A, Tatarko P, Sedlak R, Medved D, Chlup Z, Mudra E, Dusza J 2020 J. Eur. Ceram. Soc. 40 4860 Google Scholar
[27]	Singlard M, Tessier-Doyen N, Chevallier G, Oriol S, Fiore G, Vieille B, Estournes C, Vardelle M, Rossignol S 2018 Ceram. Int. 44 22357 Google Scholar
[28]	Zou B, Ji W B, Huang C Z, Xu K T, Li S S 2014 Int. J. Refract. Met. H. 47 1 Google Scholar
[29]	Cai X Q, Wang D P, Wang Y, Yang Z W 2021 J. Manuf. Processes 64 1349 Google Scholar
[30]	Wang Y, Liu Q, Zhang B, Zhang H Q, Jin Y C, Zhong Z X, Ye J, Ren Y H, Ye F, Wang W 2021 Ceram. Int. 47 10665 Google Scholar
[31]	Song B, Yang W, Liu X M, Chen H Y, Akhlaghi M 2021 Ceram. Int. 47 29174 Google Scholar
[32]	Zhao B, Zhao Y Q, Hou Z M, Luo Y Y, Zhang W, Zhang P X, Wu J P 2018 Fusion Eng. Des. 137 405 Google Scholar
[33]	Vajdi M, Moghanlou F S, Ahmadi Z, Motallebzadeh A, Asl M S 2019 Ceram. Int. 45 8333 Google Scholar
[34]	Tatarko P, Grasso S, Kovalcikova A, Medved D, Dlouhy I, Reece M J 2020 J. Eur. Ceram. Soc. 40 1111 Google Scholar
[35]	Iltis X, Lefebvre F, Lemaignan C 1995 J. Nucl. Mater. 224 109 Google Scholar
[36]	Garner A, Baxter F, Frankel P, Topping M, Harte A, Slater T, Tejland P, Romero J, Darby E, Cole-Baker A, Gass M, Preuss M 2018 Zirconium in the Nuclear Industry: 18 th International Symposium West Conshohocken, 2018 p491
[37]	Wang J, Ren D L, Chen L L, Man G A, Zhang H Y, Zhang H P, Luo L H, Li W P, Pan Y B, Gao P F, Zhu Y B, Wang Z G 2020 J. Nucl. Mater. 539 152275 Google Scholar
[38]	Bhattacharya A, Parish C M, Koyanagi T, Petrie C M, King D, Hilmas G, Fahrenholtz W G, Zinkle S J, Katoh Y 2019 Acta Materialia 165 26
[39]	Golanski G, Purzynska H 2022 Int. J. Pres. Ves. Pip. 195 104574 Google Scholar
[40]	Paul B, Kishor J, Karthik A, Murthy T S R C, Sunil S 2022 Int. J. Refract. Met. H. 103 105752 Google Scholar
[41]	Guo W C, He Q L, Wang A Y, Tian T, Liu C, Hu L X, Wang H, Wang W M, Fu Z Y 2021 J. Mater. Res. Technol. 15 6700 Google Scholar
[42]	Rafaja D, Valvoda V, Perry A J, Treglio J R 1997 Surf. Coat. Tech. 92 135 Google Scholar
[43]	Lu X R, Shu X Y, Wang L, Shao D D, Zhang H B, Zhang K B, Xie Y 2019 J. Alloys Compd. 771 973 Google Scholar
[44]	Agarwal S, Chen Q, Koyanagi T, Zhao Y, Zinkle S J, Weber W J 2019 J. Nucl. Mater. 526 151778 Google Scholar
[45]	Lopez-Honorato E, Meadows P J, Shatwell R A, Xiao P 2010 Carbon 48 881
[46]	Baca L, Stelzer N 2008 J. Eur. Ceram. Soc. 28 907 Google Scholar
[47]	Buixaderas E, Anghel E M, Atkinson I, Simon P, Bratan V, Petrescu S 2015 Ceram. Int. 41 2680 Google Scholar
[48]	Ohsaka T, Izumi F, Fujiki Y 1978 J. Raman Spectrosc. 7 321 Google Scholar
[49]	Bezrodna T, Gavrilko T, Puchkovska G, Shimanovska V, Baran J, Marchewka M 2002 J. Mol. Struct. 614 315 Google Scholar
[50]	Santara B, Giri P K, Imakita K, Fujii M 2014 J. Phys. D Appl. Phys. 47 215302 Google Scholar
[51]	Hernandez A, Barrios M L, Sanchez M L 2019 Mater. Today 13 446
[52]	Zheng G M, Zhao J, Zhou Y H 2012 Wear 290 41
[53]	Wang R D, Li P, Li B S, Hu L J, Huang F, Huang Q 2022 Corros. Sci. 201 110301 Google Scholar
[54]	Wang H, Ren F, Tang J, Qin W J, Hu L L, Dong L, Yang B, Cai G X, Jiang C Z 2018 Acta Mater. 144 691 Google Scholar
[55]	Zhang W, Chen L, Xu C G, Lu W Y, Wang Y J, Ouyang J H, Zhou Y 2021 J. Mater. Sci. Technol. 72 23 Google Scholar
[56]	Wang Y, Liu Q, Zhang B, Zhang H Q, Jin Y C, Zhong Z X, Ye J, Ren Y H, Ye F, Wang W 2021 Ceramics International 47 10665

[1]	Zhang Yu-Ye, Zhang Yi-Yi, Wei Wen-Chang, Su Zhi-Cheng, Lan Dan-Quan, Luo Shi-Hao. Molecular dynamics simulation of mechanical and thermal properties of nano-zinc oxide modified cellulose insulating paper. Acta Physica Sinica, 2024, 73(12): 127701. doi: 10.7498/aps.73.20240208
[2]	Guo Xi, Zuo Ya-Lu, Cui Bao-Shan, Shen Tie-Long, Sheng Yan-Bin, Xi Li. Ion irradiation modulated magnetic properties of materials and its applications. Acta Physica Sinica, 2024, 73(13): 136101. doi: 10.7498/aps.73.20240541
[3]	Xu Chi, Wan Fa-Rong. Analysis of dislocation characteristics and inside-outside contrasts in irradiated and annealed tungsten as a fusion reactor material. Acta Physica Sinica, 2023, 72(5): 056801. doi: 10.7498/aps.72.20222124
[4]	Dan Min, Chen Lun-Jiang, He Yan-Bin, Wan Jun-Hao, Zhang Hong, Zhang Ke-Jia, Yang Yin, Jin Fan-Ya. Defect Evolution in Y_0.5Gd_0.5Ba₂Cu₃O_7-_δ Layer by H Ion Irradiation. Acta Physica Sinica, 2023, 0(0): 0-0. doi: 10.7498/aps.72.20221612
[5]	Dan Min, Chen Lun-Jiang, He Yan-Bin, Lü Xing-Wang, Wan Jun-Hao, Zhang Hong, Zhang Ke-Jia, Yang Ying, Jin Fan-Ya. Defect evolution in Y_0.5Gd_0.5Ba₂Cu₃O_7–δ superconducting layer irradiated by H⁺ ions. Acta Physica Sinica, 2022, 71(23): 237401. doi: 10.7498/aps.71.20221612
[6]	Xin Yong, Bao Hong-Wei, Sun Zhi-Peng, Zhang Ji-Bin, Liu Shi-Chao, Guo Zi-Xuan, Wang Hao-Yu, Ma Fei, Li Yuan-Ming. Effects of Th doping on mechanical properties of U_1–_xTh_xO₂: An atomistic simulation. Acta Physica Sinica, 2021, 70(12): 122801. doi: 10.7498/aps.70.20202239
[7]	Li Ming-Yang, Zhang Lei-Min, Lv Shasha, Li Zheng-Cao. Effects of ion irradiation and oxidation on point defects in IG-110 nuclear grade graphite. Acta Physica Sinica, 2019, 68(12): 128102. doi: 10.7498/aps.68.20190371
[8]	Deng Shi-Jie, Zhao Yu-Hong, Hou Hua, Wen Zhi-Qin, Han Pei-De. Structural, mechanical and thermodynamic properties of Ti2AlX (X= C, N) at high pressure. Acta Physica Sinica, 2017, 66(14): 146101. doi: 10.7498/aps.66.146101
[9]	Bian Xi-Lei, Wang Gang. Ion irradiation of metallic glasses. Acta Physica Sinica, 2017, 66(17): 178101. doi: 10.7498/aps.66.178101
[10]	Li Li-Li, Zhang Xiao-Hong, Wang Yu-Long, Guo Jia-Hui, Zhang Shuang. Simulation of mechanical properties based on microstructure in polyethylene/montmorillonite nanocomposites. Acta Physica Sinica, 2016, 65(19): 196202. doi: 10.7498/aps.65.196202
[11]	Yang Duo, Zhong Ning, Shang Hai-Long, Sun Shi-Yang, Li Ge-Yang. Microstructures and mechanical properties of (Ti, N)/Al nanocomposite films by magnetron sputtering. Acta Physica Sinica, 2013, 62(3): 036801. doi: 10.7498/aps.62.036801
[12]	Wang Ying, Lu Tie-Cheng, Wang Yue-Zhong, Yue Shun-Li, Qi Jian-Qi, Pan Lei. Investigation of the electronic and mechanical properties of Al2O3-AlN solid solution by virtual crystal approximation. Acta Physica Sinica, 2012, 61(16): 167101. doi: 10.7498/aps.61.167101
[13]	Luo Qing-Hong, Lu Yong-Hao, Lou Yan-Zhi. Microstructure and mechanical properties of Ti-B-C-N nanocomposite coatings. Acta Physica Sinica, 2011, 60(8): 086802. doi: 10.7498/aps.60.086802
[14]	Liu Gui-Li, Yang Jie. Electronic theory study on high temperature oxidation mechanism of Nb-Ti-Al alloy. Acta Physica Sinica, 2010, 59(7): 4939-4944. doi: 10.7498/aps.59.4939
[15]	Yu Wei-Yang, Tang Bi-Yu, Peng Li-Ming, Ding Wen-Jiang. Electronic structure and mechanical properties of α-Mg3Sb2. Acta Physica Sinica, 2009, 58(13): 216-S223. doi: 10.7498/aps.58.216
[16]	Wang Zhen-Xia, Pan Qiang-Yan, Hu Jian-Gang, Yong Zhen-Zhong, Hu Yong-Qing, Zhu Zhi-Yuan. Synthesis of diamond nanocrystals by double ions (40Ar+,C2H+6) bombardment. Acta Physica Sinica, 2007, 56(8): 4829-4833. doi: 10.7498/aps.56.4829
[17]	Wang Li-Qun, Wang Ming-Xia, Li De-Jun, Yang Jin, Yu Da-Shu, Su Jie. Effect of N2 partial pressure on the defect properties and mechanical behaviors of nanoscale ZrN/WN multilayers. Acta Physica Sinica, 2007, 56(6): 3435-3439. doi: 10.7498/aps.56.3435
[18]	Jin Hui-Ming, Felix Adriana, Aroyave Majorri. Influence of yttrium ion-implantation on oxidation behavior of nickel and property of oxide scale at 900℃. Acta Physica Sinica, 2006, 55(11): 6157-6162. doi: 10.7498/aps.55.6157
[19]	Li Teng, Li Wei, Pan Wei, Li Xiu-Mei. Effect of microstructure on the mechanical properties of Fe45—50 Cr30—35Co20—25Mo0—4Zr0—2 alloy. Acta Physica Sinica, 2005, 54(9): 4395-4399. doi: 10.7498/aps.54.4395
[20]	Wei Lun, Mei Fang-Hua, Shao Nan, Dong Yun-Shan, Li Ge-Yang. The coherent growth and mechanical properties of non-isostructural TiN/TiB2 nanomultilayers. Acta Physica Sinica, 2005, 54(10): 4846-4851. doi: 10.7498/aps.54.4846

Catalog

Vol. 71, Issue 19 - 2022-10-05

Metrics

Abstract views: 4446
PDF Downloads: 64
Cited By: 0

姓名
邮箱
手机号码
标题
留言内容
验证码

Search

Article

留言板

Effect of Ti content on preparation and properties of TiB₂-SiC-Ti materials

Abstract

Authors and contacts

Corresponding author: Li Bing-Sheng, libingshengmvp@163.com

FullText HTML : translate this paragraph

References

Cited By

Catalog

Metrics

Authors

Referees

About Journal

About

Search

Article

留言板

Effect of Ti content on preparation and properties of TiB2-SiC-Ti materials

Abstract

Authors and contacts

Corresponding author: Li Bing-Sheng, libingshengmvp@163.com

FullText HTML : translate this paragraph

References

Cited By

Catalog

Metrics

Publishing process

Authors

Referees

About Journal

About

Effect of Ti content on preparation and properties of TiB₂-SiC-Ti materials