等离子体增强化学气相沉积法制备含氢类金刚石膜的紫外Raman光谱和X射线光电子能谱研究

杨发展; 沈丽如; 王世庆; 唐德礼; 金凡亚; 刘海峰

doi:10.7498/aps.62.017802

摘要

利用脉冲辉光放电的方法, 在硅片上采用不同的沉积工艺制备了含氢类金刚石膜层, 并采用Raman光谱和X射线光电子能谱(XPS)对膜层进行表征. 用Raman光谱仪在波长为325 nm的紫外光源的激励下观察膜层的键结构. 紫外Raman光谱对含氢类金刚石膜是非常有用的, 它能有效避免可见光Raman光谱测量时的荧光干扰, 清晰地得到膜层的D峰和G峰. 同时利用XPS分析得到膜层的 sp3键含量, 并与Raman光谱所得数据进行比较. 通过Raman光谱和XPS分析可以发现, 在紫外光源的激励下, 膜层的G峰峰位向高频移方向移动, G峰峰位、I(D)/I(G), G峰半高宽和sp3键含量之间存在一定的关系.

关键词:

Abstract

The hydrogenous diamond-like carbon (DLC) films deposited on Si substrates using pulsed glow discharge method are investigated using Raman spectroscopy and X-ray photoelectron spectroscopy method. The UV Raman spectrum for excitation wavelength is 325 nm. UV Raman is particularly useful for hydrogenous DLC, as it gives clear measurements in the D and G peak spectral region even for highly hydrogenated samples, for which the visible Raman spectra are overshadowed by photoluminescence. The sp3 bonding of hydrogenous DLC film can be effectively studied by X-ray photoelectron spectroscopy method, and the data from the X-ray photoelectron spectroscopy method are compared with Raman results. It is found that G peak shows a shift to ward a higher wave under UV excitation. For the G peak, I(D)/I(G), G-FWHM and sp3, there exists a relationship among them.

Keywords:

作者及机构信息

1.
核工业西南物理研究院, 成都 610041;

2.
成都理工大学工程技术学院, 乐山 614000

基金项目: 国家自然科学基金(批准号: 10975050)资助的课题.

Authors and contacts

1.
Southwestern Insititute of Physics, Chengdu 610041, China;

2.
The Enginering and Technical College of University, Leshan 614000, China

Funds: Project supported by the National Natural Science Foundation of China (Grant No. 10975050).

参考文献

[1]	Wang Y J, Li H X, Ji L, Liu X H, Wu Y X, Zhou H D, Chen J M 2012 Acta Phys. Sin. 61 056103 (in Chinese) [王永军, 李红轩, 吉利, 刘晓红, 吴艳霞, 周惠娣, 陈建敏 2012 物理学报 61 056103]
[2]	Lifshitz Y 1999 Diamond Rel. Mater. 8 1659
[3]	Morshed M M, Cameron D C, McNamara B P, Hashmi M S J 2005 J. Mater. Process. Technol. 169 222
[4]	Hauert R 2003 Diamond Relat. Mater. 12 589
[5]	Casiraghi C, Robertson J, Ferrari A C 2006 Materials Today 1-2 10
[6]	Zhao D C, Ren N, Ma Z J, Qiu J W, Xiao G J, Wu S H 2008 Acta Phys. Sin. 57 1935 (in Chinese) [赵栋才, 任妮, 马占吉, 邱家稳, 肖更竭, 武生虎 2008 物理学报 57 1935]
[7]	Zhou B, Wang L, Mehta N 2006 J. Micromech. Microeng. 16 7
[8]	Dearnaley G, Arps J H 2005 Surf. Coat. Technol. 200 7
[9]	Tomcik B 2002 Diamond Relat. Mater. 11 1409
[10]	Vercammen K, Meneve J, Dekempeneer E 1999 Surf. Coat. Technol. 121-121 11
[11]	Staryga E, Bak G W, Dluzniewski M 2004 Vacuum 74 2
[12]	Dai Y F, Jiang M F, Yang Y S, Zhou Y 2011 Acta Phys. Sin. 60 118101 (in Chinese) [戴永丰, 江美福, 杨亦赏, 周杨 2011 物理学报 60 118101]
[13]	Small J P, Shi L, Kim P 2003 Solid State Commun. 127 181
[14]	Occelli F, Loubeyre P, Letoullec R 2003 Nat. Mater. 2 151
[15]	Pichler T, Kuzmany H, Katura H, Achiba Y 2001 Phys. Rev. B63 140301
[16]	Jacob W, Moller W 1993 Appl. Phys. Lett. 63 1771
[17]	Robertson J 2002 Mater. Sci. Eng. R37 129
[18]	Ferrari A C, Robertson J 2001 Phys. Rev. B 64 075414
[19]	Chu P K, Li L H 2006 Mater. Chem. Phys. 96 253
[20]	Cheng Y H, Tay B K, Lau S P, Shi X, Qiao X L, Chen J G, Wu Y P, Xie C S 2001 Appl. Phys. A 73 341
[21]	Chen M W 2008 M. S. Dissertation (Xiamen: Xiamen University) (in Chinese) [刘明文 2008 硕士学位论文 (厦门: 厦门大学)]
[22]	Quaeyhaegens C, Knuyt G 1995 Thin Solid Films 258 170
[23]	Hatada R, Baba K 1999 Nuclear Instruments and Methods in Physics Research Section B: Beam Interactions with Materials and Atoms 148 655
[24]	Donnelly K, Dowling D P, McConnell M L, Flood R V 1999 Diamond Relat. Mater. 8 538

施引文献

[1]	Wang Y J, Li H X, Ji L, Liu X H, Wu Y X, Zhou H D, Chen J M 2012 Acta Phys. Sin. 61 056103 (in Chinese) [王永军, 李红轩, 吉利, 刘晓红, 吴艳霞, 周惠娣, 陈建敏 2012 物理学报 61 056103]
[2]	Lifshitz Y 1999 Diamond Rel. Mater. 8 1659
[3]	Morshed M M, Cameron D C, McNamara B P, Hashmi M S J 2005 J. Mater. Process. Technol. 169 222
[4]	Hauert R 2003 Diamond Relat. Mater. 12 589
[5]	Casiraghi C, Robertson J, Ferrari A C 2006 Materials Today 1-2 10
[6]	Zhao D C, Ren N, Ma Z J, Qiu J W, Xiao G J, Wu S H 2008 Acta Phys. Sin. 57 1935 (in Chinese) [赵栋才, 任妮, 马占吉, 邱家稳, 肖更竭, 武生虎 2008 物理学报 57 1935]
[7]	Zhou B, Wang L, Mehta N 2006 J. Micromech. Microeng. 16 7
[8]	Dearnaley G, Arps J H 2005 Surf. Coat. Technol. 200 7
[9]	Tomcik B 2002 Diamond Relat. Mater. 11 1409
[10]	Vercammen K, Meneve J, Dekempeneer E 1999 Surf. Coat. Technol. 121-121 11
[11]	Staryga E, Bak G W, Dluzniewski M 2004 Vacuum 74 2
[12]	Dai Y F, Jiang M F, Yang Y S, Zhou Y 2011 Acta Phys. Sin. 60 118101 (in Chinese) [戴永丰, 江美福, 杨亦赏, 周杨 2011 物理学报 60 118101]
[13]	Small J P, Shi L, Kim P 2003 Solid State Commun. 127 181
[14]	Occelli F, Loubeyre P, Letoullec R 2003 Nat. Mater. 2 151
[15]	Pichler T, Kuzmany H, Katura H, Achiba Y 2001 Phys. Rev. B63 140301
[16]	Jacob W, Moller W 1993 Appl. Phys. Lett. 63 1771
[17]	Robertson J 2002 Mater. Sci. Eng. R37 129
[18]	Ferrari A C, Robertson J 2001 Phys. Rev. B 64 075414
[19]	Chu P K, Li L H 2006 Mater. Chem. Phys. 96 253
[20]	Cheng Y H, Tay B K, Lau S P, Shi X, Qiao X L, Chen J G, Wu Y P, Xie C S 2001 Appl. Phys. A 73 341
[21]	Chen M W 2008 M. S. Dissertation (Xiamen: Xiamen University) (in Chinese) [刘明文 2008 硕士学位论文 (厦门: 厦门大学)]
[22]	Quaeyhaegens C, Knuyt G 1995 Thin Solid Films 258 170
[23]	Hatada R, Baba K 1999 Nuclear Instruments and Methods in Physics Research Section B: Beam Interactions with Materials and Atoms 148 655
[24]	Donnelly K, Dowling D P, McConnell M L, Flood R V 1999 Diamond Relat. Mater. 8 538

[1]	陆益敏, 汪雨洁, 徐曼曼, 王海, 奚琳. 磁场辅助激光生长类金刚石膜的微结构及光学性能. 物理学报, 2024, 73(10): 108101. doi: 10.7498/aps.73.20240145
[2]	李刘合, 刘红涛, 罗辑, 许亿. 带状真空电弧磁过滤器等离子体分布特性及制备类金刚石膜研究. 物理学报, 2016, 65(6): 065202. doi: 10.7498/aps.65.065202
[3]	刘明, 曹世勋, 袁淑娟, 康保娟, 鲁波, 张金仓. Pr掺杂DyFeO3体系的自旋重取向相变、晶格畸变与Raman光谱研究. 物理学报, 2013, 62(14): 147601. doi: 10.7498/aps.62.147601
[4]	刘天元, 孙成林, 里佐威, 周密. Raman光谱方法研究三氯甲烷与苯分子间的 C/H相互作用. 物理学报, 2012, 61(10): 107801. doi: 10.7498/aps.61.107801
[5]	房超, 刘马林. 包覆燃料颗粒碳化硅层的Raman光谱研究. 物理学报, 2012, 61(9): 097802. doi: 10.7498/aps.61.097802
[6]	王静, 刘贵昌, 李红玲, 侯保荣. 铜基类金刚石膜功能梯度材料作为散热材料的研究. 物理学报, 2012, 61(5): 058102. doi: 10.7498/aps.61.058102
[7]	赵栋才, 任妮, 马占吉, 邱家稳, 肖更竭, 武生虎. 掺硅类金刚石膜的制备与力学性能研究. 物理学报, 2008, 57(3): 1935-1940. doi: 10.7498/aps.57.1935
[8]	马国佳, 刘喜亮, 张华芳, 武洪臣, 彭丽平, 蒋艳莉. 乙炔气体流量对纳米TiC类金刚石复合膜的化学结构及力学性能影响. 物理学报, 2007, 56(4): 2377-2381. doi: 10.7498/aps.56.2377
[9]	刘燕燕, E. Bauer-Grosse, 张庆瑜. 一氧化碳合成金刚石薄膜的形貌和结构分析. 物理学报, 2007, 56(11): 6572-6579. doi: 10.7498/aps.56.6572
[10]	王静, 刘贵昌, 汲大鹏, 徐军, 邓新禄. 铜上采用过渡层沉积类金刚石薄膜的研究. 物理学报, 2006, 55(7): 3748-3755. doi: 10.7498/aps.55.3748
[11]	刘艳红, 张家良, 王卫国, 李建, 刘东平, 马腾才. CH4或CH4+Ar介质阻挡放电中的离子能量和类金刚石膜制备. 物理学报, 2006, 55(3): 1458-1463. doi: 10.7498/aps.55.1458
[12]	李之杰, 潘正瑛, 朱靖, 魏启, 王月霞, 臧亮坤, 周亮, 刘提将. 离子束辅助沉积对类金刚石膜结构影响的计算机模拟. 物理学报, 2005, 54(5): 2233-2238. doi: 10.7498/aps.54.2233
[13]	彭鸿雁, 周传胜, 赵立新, 金曾孙, 张冰, 陈宝玲, 陈玉强, 李敏君. 激光功率密度对类金刚石膜结构性能的影响. 物理学报, 2005, 54(9): 4294-4299. doi: 10.7498/aps.54.4294
[14]	杨武保, 范松华, 张谷令, 马培宁, 张守忠, 杜健. 非平衡磁控溅射法类金刚石薄膜的制备及分析. 物理学报, 2005, 54(10): 4944-4948. doi: 10.7498/aps.54.4944
[15]	蔡炜颖, 李志锋, 陆卫, 李守荣, 梁平治. Si微电阻桥温度分布与热传导特性的显微Raman光谱研究. 物理学报, 2003, 52(11): 2923-2928. doi: 10.7498/aps.52.2923
[16]	杨武保, 范松华, 刘赤子, 张谷令, 王久丽, 杨思泽. 脉冲高能量密度等离子体法类金刚石膜的制备及分析. 物理学报, 2003, 52(1): 140-144. doi: 10.7498/aps.52.140
[17]	张海燕, 陈可心, 朱燕娟, 陈易明, 何艳阳, 伍春燕, 王金华, 刘颂豪. CO2连续激光蒸发制备单壁碳纳米管及其Raman光谱的研究. 物理学报, 2002, 51(2): 444-448. doi: 10.7498/aps.51.444
[18]	卢贵武, 夏海瑞, 孟宪林, 刘雪松, 杨卫兵. 掺Nd锆石类激光晶体的Raman光谱研究. 物理学报, 2002, 51(2): 424-429. doi: 10.7498/aps.51.424
[19]	梁二军, 晁明举. 激光诱导多孔硅晶格畸变的Raman光谱和光致发光谱研究. 物理学报, 2001, 50(11): 2241-2246. doi: 10.7498/aps.50.2241
[20]	李刘合, 张海泉, 崔旭明, 张彦华, 夏立芳, 马欣新, 孙跃. X射线光电子能谱辅助Raman光谱分析类金刚石碳膜的结构细节. 物理学报, 2001, 50(8): 1549-1554. doi: 10.7498/aps.50.1549

计量

文章访问数: 7134
PDF下载量: 938
被引次数: 0

姓名
邮箱
手机号码
标题
留言内容
验证码

搜索

留言板