钴磷族化合物BaT2P2和BaT2As2(T=Co, Rh, Ir) 的电子结构

钱玉敏; 徐刚

doi:10.7498/aps.60.067101

摘要

基于密度泛函理论(DFT)在广义梯度(GGA)下计算了钴磷族化合物BaT2P2和BaT2As2(T=Co, Rh, Ir)的电子结构.研究发现在BaCo2P2和BaCo2As2中,由于范霍夫畸点位于费米面附近使得费米能级处的态密度非常高,从而导致由斯通纳机理引起的巡游铁磁不稳定性.在从Co到

关键词:

We study the electronic structure of cobalt pnictides: BaT2P2 and BaT2As2 (T=Co, Rh, Ir) by the density functional theory within generalized gradient approximation, and find that the ferromagnetisms in BaCo2As2 and BaCo2P2 are due mostly to the high density of states (Van-Hove singularity) at Fermi level, which induce Stoner ferromagnetism. In these compounds, from Co-3d to Rh-4d, then to Ir-5d, the d-d bonding and the d-p bonding in the TX4(X=P, As) layers are strengthened. As a result, the antibonding d-d states are pushed away from the Fermi level, and the ferromagnetisms are suppressed in Rh and Ir compounds. The evolutions and the detailed electronic structures of these compounds are studied and compared, and spin orbital coupling interaction is negligible.

Keywords:

作者及机构信息

钱玉敏,
徐刚

1.
北京凝聚态物理国家实验室,中国科学院物理研究所,北京 100190

基金项目: 国家自然科学基金(批准号:90921004)资助的课题.

Authors and contacts

1.
Beijing National Laboratory for Condensed Matter Physics, Institute of Physics, Chinese Academy of Sciences, Beijing 100190, China

参考文献

[1]	Kamihara Y, Watanabe T, Hirano M, Hosono H 2008 J. Am. Chem. Soc. 130 3296
[2]	Chen G F, Li Z, Li G, Zhou J, Wu D, Dong J, Hu W Z, Zheng P, Chen Z J, Yuan H Q, Singleton J, Luo J L, Wang N L 2008 Phys. Rev. Lett. 101 057007
[3]	Zhu X, Yang H, Fang L, Mu G, Wen H H 2008 Supercond. Sci. Technol. 21 105001
[4]	Rotter M, Tegel M, Johrendt D, Schellenberg I, Hermes W, Pottgen R 2008 Phys. Rev. B 78 020503(R)
[5]	Rotter M, Tegel M, Johrendt D 2008 Phys. Rev. Lett. 101 107006
[6]	Wang X C, Liu Q Q, Lü Y X, Gao W B, Yang L X, Yu R C, Li F Y, Jin C Q 2008 Solid State Commun. 148 538
[7]	Hsu F C, Luo J Y, Yeh K W, Chen T K, Huang T W, Wu P M, Lee Y C, Huang Y L, Chu Y Y, Yan D C, Wu M K 2008 Proc. Natl. Acad. Sci. USA 105 14262
[8]	Liu S, Li B, Wang W, Wang J, Liu M 2010 Acta Phys. Sin. 59 4245 (in Chinese) [刘甦、李斌、王玮、汪军、刘楣 2010 物理学报 59 4245] 〖9] Yang S, You W L, Gu S J, Lin H Q 2009 Chin. Phys. B 18 2545
[9]	Li Z C, Zhou F 2010 Chin. Phys. B 19
[10]	Hamlin J J, Baumbach R E, Zocco D A, Sayles T A, Maple M B 2008 J. Phys. Condens. Matter 20 365220
[11]	Dong J, Zhang H J, Xu G, Li Z, Li G, Hu W Z, Wu D, Chen G F, Dai X, Luo J L, Fang Z, Wang N L 2008 Europhys. Lett. 83 27006
[12]	Cruz C de la, Huang Q, Lynn J W, Li J Y, Ratcliff W, Zarestky J L, Mook H A, Chen G F, Luo J L, Wang N L, Dai P C 2008 Nature 453 899
[13]	Kofu M, Qiu Y, Bao W, Lee S H, Chang S, Wu T, Wu G, Chen X H 2009 New J. Phys. 11 055001
[14]	Takumi W, Hiroshi Y, Toshio K, Yoichi K, Hidenori H, Masahiro H, Hideo H 2007 Inorg. Chem. 46 7719
[15]	Takumi W, Hiroshi Y, Yoichi K, Toshio K, Masahiro H, Hideo H 2008 J. Solid State Chem. 181 2117
[16]	Li Z, Chen G F, Dong J, Li G, Hu W Z, Wu D, Su S, Zheng P, Xiang T, Wang N L, Luo J L 2008 Phys. Rev. B 78 R060504
[17]	Ronning F, Kurita N, Bauer E D, Scott B L, Park T, Klimczuk T, Movshovich R, Thompson J D 2008 J. Phys. Condens. Matter. 20 342203
[18]	Takashi M, Hiroshi Y, Toshio K, Yoichi K, Masahiro H, Hideo H 2008 Solid State Commun. 147 111
[19]	Hiroshi Y, Ryuto K, Toshio K, Yoichi K, Masahiro H, Tetsuya N, Hitoshi O, Hideo H 2008 Phys. Rev. B 77 224431
[20]	Sefat A S, Singh D J, Jin R, McGuire M A, Sales B C, Mandrus D 2009 Phys. Rev. B 79 024512
[21]	Yogesh S, Lee Y, Nandi S, Kreyssig A, Ellern A, Das S, Nath R, Harmon B N, Goldman A I, Johnston D C 2008 Phys. Rev. B 78 104512
[22]	Daigorou H, Tomohiro T, Ryuji H, Hiroko A K, Hidenori T 2009 J. Phys. Soc. Jpn. 78 023706
[23]	Berry N, Capan C, Seyfarth G, Bianchi A D, Ziller J, Fisk Z 2009 Phys. Rev. B 79 180502(R)
[24]	Fang Z, Terakura K 2002 J. Phys. Condens. Matter. 14 3001
[25]	Perdew J, Burke K, Ernzerhof M 1996 Phys. Rev. Lett. 77 3865
[26]	Wang G T, Qian Y M, Xu G, Dai X, Fang Z 2010 Phys. Rev. Lett. 104 047002
[27]	Shein I R, Ivanovskii A L 2009 JETP Lett. 89 357
[28]	Johrendt D, Felser C, Jepsen O, Andersen O K, Mewis A, Rouxel J 1997 J. Solid State Chem. 130 254

施引文献

[1]	Kamihara Y, Watanabe T, Hirano M, Hosono H 2008 J. Am. Chem. Soc. 130 3296
[2]	Chen G F, Li Z, Li G, Zhou J, Wu D, Dong J, Hu W Z, Zheng P, Chen Z J, Yuan H Q, Singleton J, Luo J L, Wang N L 2008 Phys. Rev. Lett. 101 057007
[3]	Zhu X, Yang H, Fang L, Mu G, Wen H H 2008 Supercond. Sci. Technol. 21 105001
[4]	Rotter M, Tegel M, Johrendt D, Schellenberg I, Hermes W, Pottgen R 2008 Phys. Rev. B 78 020503(R)
[5]	Rotter M, Tegel M, Johrendt D 2008 Phys. Rev. Lett. 101 107006
[6]	Wang X C, Liu Q Q, Lü Y X, Gao W B, Yang L X, Yu R C, Li F Y, Jin C Q 2008 Solid State Commun. 148 538
[7]	Hsu F C, Luo J Y, Yeh K W, Chen T K, Huang T W, Wu P M, Lee Y C, Huang Y L, Chu Y Y, Yan D C, Wu M K 2008 Proc. Natl. Acad. Sci. USA 105 14262
[8]	Liu S, Li B, Wang W, Wang J, Liu M 2010 Acta Phys. Sin. 59 4245 (in Chinese) [刘甦、李斌、王玮、汪军、刘楣 2010 物理学报 59 4245] 〖9] Yang S, You W L, Gu S J, Lin H Q 2009 Chin. Phys. B 18 2545
[9]	Li Z C, Zhou F 2010 Chin. Phys. B 19
[10]	Hamlin J J, Baumbach R E, Zocco D A, Sayles T A, Maple M B 2008 J. Phys. Condens. Matter 20 365220
[11]	Dong J, Zhang H J, Xu G, Li Z, Li G, Hu W Z, Wu D, Chen G F, Dai X, Luo J L, Fang Z, Wang N L 2008 Europhys. Lett. 83 27006
[12]	Cruz C de la, Huang Q, Lynn J W, Li J Y, Ratcliff W, Zarestky J L, Mook H A, Chen G F, Luo J L, Wang N L, Dai P C 2008 Nature 453 899
[13]	Kofu M, Qiu Y, Bao W, Lee S H, Chang S, Wu T, Wu G, Chen X H 2009 New J. Phys. 11 055001
[14]	Takumi W, Hiroshi Y, Toshio K, Yoichi K, Hidenori H, Masahiro H, Hideo H 2007 Inorg. Chem. 46 7719
[15]	Takumi W, Hiroshi Y, Yoichi K, Toshio K, Masahiro H, Hideo H 2008 J. Solid State Chem. 181 2117
[16]	Li Z, Chen G F, Dong J, Li G, Hu W Z, Wu D, Su S, Zheng P, Xiang T, Wang N L, Luo J L 2008 Phys. Rev. B 78 R060504
[17]	Ronning F, Kurita N, Bauer E D, Scott B L, Park T, Klimczuk T, Movshovich R, Thompson J D 2008 J. Phys. Condens. Matter. 20 342203
[18]	Takashi M, Hiroshi Y, Toshio K, Yoichi K, Masahiro H, Hideo H 2008 Solid State Commun. 147 111
[19]	Hiroshi Y, Ryuto K, Toshio K, Yoichi K, Masahiro H, Tetsuya N, Hitoshi O, Hideo H 2008 Phys. Rev. B 77 224431
[20]	Sefat A S, Singh D J, Jin R, McGuire M A, Sales B C, Mandrus D 2009 Phys. Rev. B 79 024512
[21]	Yogesh S, Lee Y, Nandi S, Kreyssig A, Ellern A, Das S, Nath R, Harmon B N, Goldman A I, Johnston D C 2008 Phys. Rev. B 78 104512
[22]	Daigorou H, Tomohiro T, Ryuji H, Hiroko A K, Hidenori T 2009 J. Phys. Soc. Jpn. 78 023706
[23]	Berry N, Capan C, Seyfarth G, Bianchi A D, Ziller J, Fisk Z 2009 Phys. Rev. B 79 180502(R)
[24]	Fang Z, Terakura K 2002 J. Phys. Condens. Matter. 14 3001
[25]	Perdew J, Burke K, Ernzerhof M 1996 Phys. Rev. Lett. 77 3865
[26]	Wang G T, Qian Y M, Xu G, Dai X, Fang Z 2010 Phys. Rev. Lett. 104 047002
[27]	Shein I R, Ivanovskii A L 2009 JETP Lett. 89 357
[28]	Johrendt D, Felser C, Jepsen O, Andersen O K, Mewis A, Rouxel J 1997 J. Solid State Chem. 130 254

[1]	张硕鑫, 刘士余, 严达利, 余浅, 任海涛, 于彬, 李德军. Ta_1–xHf_xC和Ta_1–xZr_xC固溶体的结构稳定性和力学性质的第一性原理研究. 物理学报, 2021, 70(11): 117102. doi: 10.7498/aps.70.20210191
[2]	邢海英, 郑智健, 张子涵, 吴文静, 郭志英. 应力调控BlueP/X Te₂ (X = Mo, W)范德瓦耳斯异质结电子结构及光学性质理论研究. 物理学报, 2021, 70(6): 067101. doi: 10.7498/aps.70.20201728
[3]	林洪斌, 林春, 陈越, 钟克华, 张健敏, 许桂贵, 黄志高. 第一性原理研究Mg掺杂对LiCoO₂正极材料结构稳定性及其电子结构的影响. 物理学报, 2021, 70(13): 138201. doi: 10.7498/aps.70.20210064
[4]	刘娜, 危阳, 马新国, 祝林, 徐国旺, 楚亮, 黄楚云. 钙钛矿APbI3结构稳定性及光电性质的理论研究. 物理学报, 2017, 66(5): 057103. doi: 10.7498/aps.66.057103
[5]	马振宁, 周全, 汪青杰, 王逊, 王磊. Mg-Y-Cu合金长周期有序相热力学稳定性及其电子结构的第一性原理研究. 物理学报, 2016, 65(23): 236101. doi: 10.7498/aps.65.236101
[6]	贺艳斌, 贾建峰, 武海顺. N2H4在NiFe(111)合金表面吸附稳定性和电子结构的第一性原理研究. 物理学报, 2015, 64(20): 203101. doi: 10.7498/aps.64.203101
[7]	马振宁, 蒋敏, 王磊. Mg-Y-Zn合金三元金属间化合物的电子结构及其相稳定性的第一性原理研究. 物理学报, 2015, 64(18): 187102. doi: 10.7498/aps.64.187102
[8]	王转玉, 康伟丽, 贾建峰, 武海顺. Ti2Bn(n=1–10)团簇的结构与稳定性:基于从头算的研究. 物理学报, 2014, 63(23): 233102. doi: 10.7498/aps.63.233102
[9]	杨建辉, 陈言星, 吴丽慧, 韦世豪. MC与Mn+1ACn稳定性与电子特征的第一性原理研究. 物理学报, 2014, 63(23): 237301. doi: 10.7498/aps.63.237301
[10]	周树兰, 赵显, 江向平, 韩晓东. 立方相Na1/2Bi1/2TiO3和K1/2Bi1/2TiO3的电子结构和结构不稳定性的第一性原理比较研究. 物理学报, 2014, 63(16): 167101. doi: 10.7498/aps.63.167101
[11]	唐春梅, 郭微, 朱卫华, 刘明熠, 张爱梅, 巩江峰, 王辉. 内掺过渡金属非典型富勒烯M@C22(M=Sc, Ti, V, Cr, Mn, Fe, Co, Ni) 几何结构、电子结构、稳定性和磁性的密度泛函研究. 物理学报, 2012, 61(2): 026101. doi: 10.7498/aps.61.026101
[12]	宋健, 李锋, 邓开明, 肖传云, 阚二军, 陆瑞锋, 吴海平. 单层硅Si6H4Ph2的稳定性和电子结构密度泛函研究. 物理学报, 2012, 61(24): 246801. doi: 10.7498/aps.61.246801
[13]	濮春英, 唐鑫, 吕海峰, 张庆瑜. 掺Cd氧化锌的电子结构及相结构稳定性的第一性原理研究. 物理学报, 2011, 60(3): 037101. doi: 10.7498/aps.60.037101
[14]	高潭华, 吴顺情, 胡春华, 朱梓忠. 二维BC2 N薄片的结构稳定性和电子性质. 物理学报, 2011, 60(12): 127305. doi: 10.7498/aps.60.127305
[15]	潘洪哲, 徐明, 陈丽, 孙媛媛, 王永龙. 单层正三角锯齿型石墨烯量子点的电子结构和磁性. 物理学报, 2010, 59(9): 6443-6449. doi: 10.7498/aps.59.6443
[16]	汪志刚, 张杨, 文玉华, 朱梓忠. ZnO原子链的结构稳定性和电子性质的第一性原理研究. 物理学报, 2010, 59(3): 2051-2056. doi: 10.7498/aps.59.2051
[17]	王松有, 段国玉, 邱建红, 贾瑜, 陈良尧. 闪锌矿结构的PtN:一种不稳定的过渡金属氮化物. 物理学报, 2006, 55(4): 1979-1982. doi: 10.7498/aps.55.1979
[18]	沈汉鑫, 蔡娜丽, 文玉华, 朱梓忠. Nb原子链的结构稳定性和电子性质. 物理学报, 2005, 54(11): 5362-5366. doi: 10.7498/aps.54.5362
[19]	贾　瑜, 杨仕娥, 马丙现, 李新建, 胡　行. 稳定的GaAs (2 5 1 1)高密勒指数表面的电子结构. 物理学报, 2004, 53(10): 3515-3520. doi: 10.7498/aps.53.3515
[20]	王立民, 罗莹, 马本堃. 双量子点分子的电子结构. 物理学报, 2001, 50(2): 278-286. doi: 10.7498/aps.50.278

计量

文章访问数: 6988
PDF下载量: 1690
被引次数: 0

姓名
邮箱
手机号码
标题
留言内容
验证码

搜索

留言板