电荷媒介的磁电耦合: 从铁电场效应到电荷序铁电体

安明; 董帅

doi:10.7498/aps.69.20201193

摘要

磁电耦合效应是百年铁电领域中新兴的科学话题和前沿难点. 包含两种及以上铁性序的多铁性材料则是追求本征强磁电耦合的理想体系, 其展现了丰富的物理性质, 蕴含着很高的应用潜力. 作为关联电子大家庭的一个分支, 多铁性材料体系也涉及电荷、自旋、轨道, 以及晶格多重自由度. 但过往的磁电耦合研究对自旋与晶格自由度关注最多, 却往往忽略了其中的电荷自由度. 实际上, 电荷自由度可以在磁电耦合中扮演重要的媒介作用. 本文将介绍异质结中的铁电场效应和单相多铁性材料中的电荷序所涉及的磁电耦合物理机制, 以及回顾作者近年来在此方向上的若干尝试, 希望能为本领域的研究者提供一些参考.

关键词:

多铁性 /
磁电耦合 /
场效应 /
电荷序

Abstract

Magnetoelectricity is an emerging topic and a frontier issue of the field of ferroelectricity. Multiferroics containing more than one ferroic order is an ideal system to pursuit intrinsic and robust magnetoelectric coupling, which holds rich physics and great potential applications. As a branch of the correlated electron family, multiferroic also has multiple degrees of freedom, including the charge, spin, orbital, and lattice. Among them, the charge degree of freedom has been mostly overlooked in the past researches and actually it may play an important role in magnetoelectricity. In this topical review, the charge-mediated magnetoelectricity is introduced, including the ferroelectric field effect in heterostructures and the charge ordering in single-phase multiferroics. The physical mechanisms will be revealed, together with several examples we given in recent years. We hope that this topical review can provide a reference for the researches in this vigorous filed.

Keywords:

作者及机构信息

安明,
董帅

东南大学物理学院, 南京　211189

通信作者: 董帅, sdong@seu.edu.cn

基金项目: 国家自然科学基金(批准号:11834002, 11674055)资助的课题

Authors and contacts

An Ming,
Dong Shuai

School of Physics, Southeast University, Nanjing 211189, China

Corresponding author: Dong Shuai, sdong@seu.edu.cn

Funds: Project supported by the National Natural Science Foundation of China (Grant Nos. 11834002, 11674055)

文章全文 : translate this paragraph

参考文献

[1]	Hill N A 2000 J. Phys. Chem. B 104 6694 Google Scholar
[2]	Wang J, Neaton J B, Zheng H, et al. 2003 Science 299 1719 Google Scholar
[3]	Kimura T, Goto T, Shintani H, Ishizaka K, Arima T, Tokura Y 2003 Nature 426 55 Google Scholar
[4]	Dong S, Liu J M, Cheong S W, Ren Z F 2015 Adv. Phys. 64 519 Google Scholar
[5]	Ramesh R, Spaldin N A 2007 Nat. Mater. 6 21 Google Scholar
[6]	Dong S, Xiang H J, Dagotto E 2019 Natl. Sci. Rev. 6 629 Google Scholar
[7]	徐萌, 晏建民, 徐志学, 郭磊, 郑仁奎, 李晓光 2018 物理学报 67 157506 Google Scholar Xu M, Yan J M, Xu Z X, Guo L, Zheng R K, Li X G 2018 Acta. Phys. Sin. 67 157506 Google Scholar
[8]	宋骁, 高兴森, 刘俊明 2018 物理学报 67 157512 Google Scholar Song X, Gao X S, Liu J M 2018 Acta Phys. Sin. 67 157512 Google Scholar
[9]	胡婷, 阚二军 2018 物理学报 67 157701 Google Scholar Hu T, Kan E J 2018 Acta Phys. Sin. 67 157701 Google Scholar
[10]	Spaldin N A, Ramesh R 2019 Nat. Mater. 18 203 Google Scholar
[11]	Dong S, Dagotto E 2013 Phys. Rev. B 88 140404(R)Google Scholar
[12]	Duan C G, Jaswal S S, Tsymbal E Y 2006 Phys. Rev. Lett. 97 047201 Google Scholar
[13]	Duan C G, Velev J P, Sabirianov R F, Zhu Z Q, Chu J H, Jaswal S S, Tsymbal E Y 2008 Phys. Rev. Lett. 101 137201 Google Scholar
[14]	Rondinelli J M, Stengel M, Spaldin N A 2008 Nat. Nano. 3 46 Google Scholar
[15]	Yang P, Zhu J S, Lee J Y, Lee H Y 2011 Trans. Nonferrous Met. Soc. China 21 s92 Google Scholar
[16]	Radaelli G, Petti D, Plekhanov E, Fina I, Torelli P, Salles B R, Cantoni M, Rinaldi C, Gutiérrez D, Panaccione G, Varela M, Picozzi S, Fontcuberta J, Bertacco R 2014 Nat. Commun. 5 3404 Google Scholar
[17]	Chen H H, Ismail-Beigi S 2012 Phys. Rev. B 86 024433 Google Scholar
[18]	Vaz C A F, Walker F J, Ahn C H, Ismail-Beigi S 2015 J. Phys.: Condens. Matter 27 123001 Google Scholar
[19]	Burton J D, Tsymbal E Y 2009 Phys. Rev. B 80 174406 Google Scholar
[20]	Molegraaf H J A, Hoffman J, Vaz C A F, Gariglio S, Marel D V D, Ahn C H, Triscone J M 2009 Adv. Mater. 21 3470 Google Scholar
[21]	Vaz C A F, Hoffman J, Segal Y, Reiner J W, Grober R D, Zhang Z, Ahn C H, Walker F J 2010 Phys. Rev. Lett. 104 127202 Google Scholar
[22]	Vaz C A F, Hoffman J, Segal Y, Marshall M S J, Reiner J W, Zhang Z, Grober R D, Walker F J, Ahn C H 2011 J. Appl. Phys. 109 07D905 Google Scholar
[23]	Lu H, George T A, Wang Y, Ketsman I, Burton J D, Bark C W, Ryu S, Kim D J, Wang J, Binek C, Dowben P A, Sokolov A, Eom C B, Tsymbal E Y, Gruverman A 2012 Appl. Phys. Lett. 100 232904 Google Scholar
[24]	Jiang L, Choi W S, Jeen H, Egami T, Lee H N 2012 Appl. Phys. Lett. 101 042902 Google Scholar
[25]	Yi D, Liu J, Okamoto S, Jagannatha S, Chen Y C, Yu P, Chu Y H, Arenholz E, Ramesh R 2013 Phys. Rev. Lett. 111 127601 Google Scholar
[26]	Dong S, Zhang X T, Yu R, Liu J M, Dagotto E 2011 Phys. Rev. B 84 155117 Google Scholar
[27]	Ma X, Kumar A, Dussan S, Zhai H, Fang F, Zhao H B, Scott J F, Katiyar R S, Lüpke G 2014 Appl. Phys. Lett. 104 132905 Google Scholar
[28]	Weng Y K, Lin L F, Dagotto E, Dong S 2016 Phys. Rev. Lett. 117 037601 Google Scholar
[29]	Bhattacharya A, May S J, Velthuis S G E, Warusawithana M, Zhai X, Jiang B, Zuo J M, Fitzsimmons M R, Bader S D, Eckstein J N 2008 Phys. Rev. Lett. 100 257203 Google Scholar
[30]	Dong S, Yu R, Yunoki S, Alvarez G, Liu J M, Dagotto E 2008 Phys. Rev. B 78 201102(R)Google Scholar
[31]	Gibert M, Zubko P, Scherwitzl R, Íñiguez J, Triscone J M 2012 Nature Mater. 11 195 Google Scholar
[32]	Brink J V D, Khomskii D I 2008 J. Phys.: Condens. Matter 20 434217 Google Scholar
[33]	Ikeda N, Ohsumi H, Ohwada K, Ishii K, Inami T, Kakurai K, Murakami Y, Yoshii K, Mori S, Horibe Y, Kitô H 2005 Nature 436 1136 Google Scholar
[34]	Nagano A, Naka M, Nasu J, Ishihara S 2007 Phys. Rev. Lett. 99 217202 Google Scholar
[35]	Alexe M, Ziese M, Hesse D, Esquinazi P, Yamauchi K, Fukushima T, Picozzi S, Gösel U 2009 Adv. Mater. 21 4452 Google Scholar
[36]	Efremov D V, van den Brink J, Khomskii D I 2004 Nat. Mater. 3 853 Google Scholar
[37]	Giovannetti G, Kumar S, van den Brink J, Picozzi S 2009 Phys. Rev. Lett. 103 037601 Google Scholar
[38]	Portier J, Tressaud A, De Pape R, Hagenmuller P 1970 J. Solid State Chem. 2 269 Google Scholar
[39]	Lin L F, Xu Q R, Zhang Y, Zhang J J, Liang Y P, Dong S 2017 Phys. Rev. Mater. 1 071401(R)Google Scholar
[40]	Wu S W, Cybart S A, Yu P, Rossell M D, Zhang J X, Ramesh R, Dynes R C 2010 Nat. Mater. 9 756 Google Scholar
[41]	Yu P, Lee J S, Okamoto S, Rossell M D, Huijben M, Yang C H, He Q, Zhang J X, Yang S Y, Lee M J, Ramasse Q M, Erni R, Chu Y H, Arena D A, Kao C C, Martin L, Ramesh R 2010 Phys. Rev. Lett. 105 027201 Google Scholar
[42]	Weisheit M, Fähler S, Marty A, Souche Y, Poinsignon C, Givord D 2007 Science 315 349 Google Scholar
[43]	Eerenstein W, Wiora M, Prieto J L, Scott J F, Mathur N D 2007 Nat. Mater. 6 348 Google Scholar
[44]	Lebeugle D, Mougin A, Viret M, Colson D, Ranno L 2009 Phys. Rev. Lett. 103 257601 Google Scholar
[45]	Tsymbal E Y, Kohlstedt H 2006 Science 313 181 Google Scholar
[46]	Garcia V, Bibes M 2014 Nat. Commun. 5 4289 Google Scholar
[47]	Chen A, Wen Y, Fang B, Zhao Y L, Zhang Q, Chang Y S, Li P S, Wu H, Huang H L, Lu Y L, Zeng Z M, Cai J W, Han X F, Wu T, Zhang X X, Zhao Y G 2019 Nat. Commun. 10 243 Google Scholar

施引文献

图 1 铁电场效应示意图(箭头表示铁电极化的方向)　(a) 极化向上时, 界面处吸引空穴; (b) 极化向下时, 界面处吸引电子; 即极化翻转导致界面处局域电荷重新分布^[11]

Fig. 1. Sketch of ferroelectric-field effect: (a) When the ferroelectric polarization (as denoted by assows) is upward, holes are attracted at the interface; (b) in contrast, electrons will gather at the interface when the polarization is reversed ^[11].

下载: 全尺寸图片幻灯片

图 2 (a) La_1–xA_xMnO₃/BaTiO₃ (001)异质结结构示意图, 界面处La_1–xA_xMnO₃ (LAMO)(虚线框区域)随着BaTiO₃ (BTO)极化方向(黑色箭头所示)翻转, 从铁磁态转变为A型反铁磁态; (b) 界面处锰氧化物的局域态密度随着BaTiO₃极化方向翻转而变化(极化指向界面时, 蓝色虚线表示; 极化背离界面时, 红色实线)^[19]

Fig. 2. (a) Interfacial magnetic transition induced by charge redistribution at the La_1–xA_xMnO₃/BaTiO₃ interface. Specifically, the local moments of Mn (denoted by small arrows) close to the interface change from parallel to antiparallel as the polarization of BaTiO₃ (denoted by large arrows) is reversed; (b) the spin-resolved local density of states of the interfacial La_0.5A_0.5MnO₃ varies with the ferroelectric field direction of BaTiO₃, shifting downwards (blue dashed line) or upwards (red solid line) as the polarization pointing to or away from the interface, respectively^[19].

下载: 全尺寸图片幻灯片

图 3 (a) 100 K时PbZr_0.2Ti_0.8O₃不同极化方向下La_0.8Sr_0.2MnO₃在面内[100]方向上测得的磁滞回线; (b)异质结界面处受极化翻转调制的自旋结构示意图(黑色箭头, Mn离子自旋方向; n, 界面开始的Mn离子层数^[20]); (c) 100 K时受外电场调控的磁响应曲线^[21]; (d) BiFeO₃/La_0.5Ca_0.5MnO₃界面电荷密度及自旋结构示意图^[25]

Fig. 3. (a) Magnetic hysteresis curves of La_0.8Sr_0.2MnO₃ along [100] direction taken at 100 K as the PbZr_0.2Ti_0.8O₃ polariztion points down into (black dots) or away from (red hollow diamonds) the interface; (b) sketch of the spin configurations of interfacial Mn for the two polarization states of PbZr_0.2Ti_0.8O₃. The schematic change of Mn and O orbital states are shown along with the layer-resolved magnetic moment. The spin orientation of Mn are denoted by arrows^[20]; (c) magnetoelectric hysteresis curve taken at 100 K which is obviously manipulated by the external electric field^[21]; (d) sketch of the interfacial charge distribution and spin structure of BiFeO₃/La_0.5Ca_0.5MnO₃ (denoed by arrows with different size)^[25].

下载: 全尺寸图片幻灯片

图 4 (a)铁电-锰氧化物异质结模型模拟结果: 铁电极化(灰色区域)调节界面处静电势(线)和Mn上e_g电子密度分布(点线); (b)铁电调控磁性相图: 从铁磁基态出发, 加大铁电极化(Q, 负值代表极化方向背离界面), 可以诱发界面反铁磁相(如CE1, Cx1)^[26]

Fig. 4. (a) Schematic of the interfacial electrostatic potential (lines without dots) and the corresponding curve of Mns’ e_g charge density (line with dots), with the original density (dashed lines) for reference. The typical polarization cases (left: Q = –0.4, right: Q = 0.4) are shown for better illustration. The sandwiched ferroelectric gate and its polarization are also drafted. (b) Ferroelectric field dependent ground-state phase diagram for the interfacial layers. In addition to the intrinsic ferromangentic phase, there are many antiferromagnetic orders (such as CE1 and Cx1)^[26].

下载: 全尺寸图片幻灯片

图 5 (a) 锰氧化物-铁电BaTiO₃超晶格结构示意图(黄色小球代表三价稀土金属元素和二价碱土金属元素的混合; Ba, Mn, Ti, O分别用绿色、紫色、蓝绿色和红色表示; +P和–P箭头代表铁电极化方向; 绿色箭头代表(铁磁相)自旋; 紫色箭头代表(亚铁磁相)自旋); (b) 不同MnO₂层中Mn的e_g电荷密度(用紫色球体大小区分)以及相应静电势(黑色横线)示意图^[11]

Fig. 5. (a) The superlattice structure composed of manganite and ferroelectric titanate. The Ba, O, Ti, Mn, and the mixture of trivalent and divalent cations are denoted by green, red, cyan, purple, and yellow balls. The n/p-type interfaces have been marked. The magnetic order of manganite can be switched from ferromagnetic to ferrimagnetic as the polarization of titanate changes from –P (left) to +P (right); (b) the layer-resolved e_g density (spheres) and electrostatic potential (bars) modulated by n/p-type interfaces (bricks) and –P/+P polarizations (arrows)^[11].

下载: 全尺寸图片幻灯片

图 6 (a), (b)沿不同方向观察的立方结构中G型反铁磁序示意图, 其中绿色和红色分别代表不同自旋方向; (c)沿[111]方向构建的BiFeO₃/SrTiO₃超晶格结构示意图; (d), (e)超晶格中BiFeO₃层中电子密度空间分布示意图, 箭头分别表示极化P的方向(绿色)和净磁矩M的方向(橘色); (f)电控磁示意图: 随着极化方向的翻转, 体系净磁矩方向也相应发生翻转^[28]

Fig. 6. (a), (b) Schematic of G-type antiferromagnetic order in pseudocubic perovskite structure (as in BiFeO₃) viewed from different orientations. The antiparallel spins are distinguished by green and purple; (c) the superlattice structure of BiFeO₃/SrTiO₃ stacking along the pseudocubic [111] direction. The two Fe’s in bilayer are labeled as 1 and 2; (d), (e) spatial charge distribution for the P_up and P_down cases. The orientations of M and P are also indicated; (f) the schematic process of the electric field switch of magnetism, forming an E-M hysteresis loop^[28].

下载: 全尺寸图片幻灯片

图 7 (a)三金红石LiFe₂F₆的晶体结构(棕色球, Fe; 绿色球, Li; 银色球, F); (b), (c)在面内双轴应力(–3%)作用下LiFe₂F₆中以电荷序为媒介的磁电耦合示意图: (b) 模拟的材料铁电极化翻转过程示意图, 插图为初态、中间态和末态时Fe²⁺/Fe³⁺二聚体的示意图; (c)随铁电极化变化的净磁矩翻转过程示意图, 插图为初末态对应的价带顶部分电荷密度图(沿[110]方向)^[39]

Fig. 7. (a) Crystal structure of LiFe₂F₆, in which the Fe, Li, and F are denoted by brown, green, and silver balls, respectively; (b), (c) the sketch of charge-ordering-mediated magnetoelectricity in LiFe₂F₆ with moderate compressive strain: (b) the switch of polarization. Insert: sketch of the charge redistribution within Fe²⁺/Fe³⁺ dimer; (c) the switch of local moment. Insert: the corresponding profile of partial charge density^[39].

下载: 全尺寸图片幻灯片

[1]	Hill N A 2000 J. Phys. Chem. B 104 6694 Google Scholar
[2]	Wang J, Neaton J B, Zheng H, et al. 2003 Science 299 1719 Google Scholar
[3]	Kimura T, Goto T, Shintani H, Ishizaka K, Arima T, Tokura Y 2003 Nature 426 55 Google Scholar
[4]	Dong S, Liu J M, Cheong S W, Ren Z F 2015 Adv. Phys. 64 519 Google Scholar
[5]	Ramesh R, Spaldin N A 2007 Nat. Mater. 6 21 Google Scholar
[6]	Dong S, Xiang H J, Dagotto E 2019 Natl. Sci. Rev. 6 629 Google Scholar
[7]	徐萌, 晏建民, 徐志学, 郭磊, 郑仁奎, 李晓光 2018 物理学报 67 157506 Google Scholar Xu M, Yan J M, Xu Z X, Guo L, Zheng R K, Li X G 2018 Acta. Phys. Sin. 67 157506 Google Scholar
[8]	宋骁, 高兴森, 刘俊明 2018 物理学报 67 157512 Google Scholar Song X, Gao X S, Liu J M 2018 Acta Phys. Sin. 67 157512 Google Scholar
[9]	胡婷, 阚二军 2018 物理学报 67 157701 Google Scholar Hu T, Kan E J 2018 Acta Phys. Sin. 67 157701 Google Scholar
[10]	Spaldin N A, Ramesh R 2019 Nat. Mater. 18 203 Google Scholar
[11]	Dong S, Dagotto E 2013 Phys. Rev. B 88 140404(R)Google Scholar
[12]	Duan C G, Jaswal S S, Tsymbal E Y 2006 Phys. Rev. Lett. 97 047201 Google Scholar
[13]	Duan C G, Velev J P, Sabirianov R F, Zhu Z Q, Chu J H, Jaswal S S, Tsymbal E Y 2008 Phys. Rev. Lett. 101 137201 Google Scholar
[14]	Rondinelli J M, Stengel M, Spaldin N A 2008 Nat. Nano. 3 46 Google Scholar
[15]	Yang P, Zhu J S, Lee J Y, Lee H Y 2011 Trans. Nonferrous Met. Soc. China 21 s92 Google Scholar
[16]	Radaelli G, Petti D, Plekhanov E, Fina I, Torelli P, Salles B R, Cantoni M, Rinaldi C, Gutiérrez D, Panaccione G, Varela M, Picozzi S, Fontcuberta J, Bertacco R 2014 Nat. Commun. 5 3404 Google Scholar
[17]	Chen H H, Ismail-Beigi S 2012 Phys. Rev. B 86 024433 Google Scholar
[18]	Vaz C A F, Walker F J, Ahn C H, Ismail-Beigi S 2015 J. Phys.: Condens. Matter 27 123001 Google Scholar
[19]	Burton J D, Tsymbal E Y 2009 Phys. Rev. B 80 174406 Google Scholar
[20]	Molegraaf H J A, Hoffman J, Vaz C A F, Gariglio S, Marel D V D, Ahn C H, Triscone J M 2009 Adv. Mater. 21 3470 Google Scholar
[21]	Vaz C A F, Hoffman J, Segal Y, Reiner J W, Grober R D, Zhang Z, Ahn C H, Walker F J 2010 Phys. Rev. Lett. 104 127202 Google Scholar
[22]	Vaz C A F, Hoffman J, Segal Y, Marshall M S J, Reiner J W, Zhang Z, Grober R D, Walker F J, Ahn C H 2011 J. Appl. Phys. 109 07D905 Google Scholar
[23]	Lu H, George T A, Wang Y, Ketsman I, Burton J D, Bark C W, Ryu S, Kim D J, Wang J, Binek C, Dowben P A, Sokolov A, Eom C B, Tsymbal E Y, Gruverman A 2012 Appl. Phys. Lett. 100 232904 Google Scholar
[24]	Jiang L, Choi W S, Jeen H, Egami T, Lee H N 2012 Appl. Phys. Lett. 101 042902 Google Scholar
[25]	Yi D, Liu J, Okamoto S, Jagannatha S, Chen Y C, Yu P, Chu Y H, Arenholz E, Ramesh R 2013 Phys. Rev. Lett. 111 127601 Google Scholar
[26]	Dong S, Zhang X T, Yu R, Liu J M, Dagotto E 2011 Phys. Rev. B 84 155117 Google Scholar
[27]	Ma X, Kumar A, Dussan S, Zhai H, Fang F, Zhao H B, Scott J F, Katiyar R S, Lüpke G 2014 Appl. Phys. Lett. 104 132905 Google Scholar
[28]	Weng Y K, Lin L F, Dagotto E, Dong S 2016 Phys. Rev. Lett. 117 037601 Google Scholar
[29]	Bhattacharya A, May S J, Velthuis S G E, Warusawithana M, Zhai X, Jiang B, Zuo J M, Fitzsimmons M R, Bader S D, Eckstein J N 2008 Phys. Rev. Lett. 100 257203 Google Scholar
[30]	Dong S, Yu R, Yunoki S, Alvarez G, Liu J M, Dagotto E 2008 Phys. Rev. B 78 201102(R)Google Scholar
[31]	Gibert M, Zubko P, Scherwitzl R, Íñiguez J, Triscone J M 2012 Nature Mater. 11 195 Google Scholar
[32]	Brink J V D, Khomskii D I 2008 J. Phys.: Condens. Matter 20 434217 Google Scholar
[33]	Ikeda N, Ohsumi H, Ohwada K, Ishii K, Inami T, Kakurai K, Murakami Y, Yoshii K, Mori S, Horibe Y, Kitô H 2005 Nature 436 1136 Google Scholar
[34]	Nagano A, Naka M, Nasu J, Ishihara S 2007 Phys. Rev. Lett. 99 217202 Google Scholar
[35]	Alexe M, Ziese M, Hesse D, Esquinazi P, Yamauchi K, Fukushima T, Picozzi S, Gösel U 2009 Adv. Mater. 21 4452 Google Scholar
[36]	Efremov D V, van den Brink J, Khomskii D I 2004 Nat. Mater. 3 853 Google Scholar
[37]	Giovannetti G, Kumar S, van den Brink J, Picozzi S 2009 Phys. Rev. Lett. 103 037601 Google Scholar
[38]	Portier J, Tressaud A, De Pape R, Hagenmuller P 1970 J. Solid State Chem. 2 269 Google Scholar
[39]	Lin L F, Xu Q R, Zhang Y, Zhang J J, Liang Y P, Dong S 2017 Phys. Rev. Mater. 1 071401(R)Google Scholar
[40]	Wu S W, Cybart S A, Yu P, Rossell M D, Zhang J X, Ramesh R, Dynes R C 2010 Nat. Mater. 9 756 Google Scholar
[41]	Yu P, Lee J S, Okamoto S, Rossell M D, Huijben M, Yang C H, He Q, Zhang J X, Yang S Y, Lee M J, Ramasse Q M, Erni R, Chu Y H, Arena D A, Kao C C, Martin L, Ramesh R 2010 Phys. Rev. Lett. 105 027201 Google Scholar
[42]	Weisheit M, Fähler S, Marty A, Souche Y, Poinsignon C, Givord D 2007 Science 315 349 Google Scholar
[43]	Eerenstein W, Wiora M, Prieto J L, Scott J F, Mathur N D 2007 Nat. Mater. 6 348 Google Scholar
[44]	Lebeugle D, Mougin A, Viret M, Colson D, Ranno L 2009 Phys. Rev. Lett. 103 257601 Google Scholar
[45]	Tsymbal E Y, Kohlstedt H 2006 Science 313 181 Google Scholar
[46]	Garcia V, Bibes M 2014 Nat. Commun. 5 4289 Google Scholar
[47]	Chen A, Wen Y, Fang B, Zhao Y L, Zhang Q, Chang Y S, Li P S, Wu H, Huang H L, Lu Y L, Zeng Z M, Cai J W, Han X F, Wu T, Zhang X X, Zhao Y G 2019 Nat. Commun. 10 243 Google Scholar

[1]	沈瑶. 镍基超导体中电荷序的实验研究进展. 物理学报, 2024, 73(19): 197104. doi: 10.7498/aps.73.20240898
[2]	宋凯欣, 闵书刚, 高俊奇, 张双捷, 毛智能, 沈莹, 储昭强. 磁电机械天线的阻抗特性分析. 物理学报, 2022, 71(24): 247502. doi: 10.7498/aps.71.20220591
[3]	陈诚, 卢建安, 杜微, 王伟, 毛翔宇, 陈小兵. Nd含量对Bi_6−xNd_xFe_1.4Ni_0.6Ti₃O₁₈多晶材料多铁性的影响. 物理学报, 2019, 68(3): 037701. doi: 10.7498/aps.68.20181287
[4]	刀流云, 张子涛, 肖煜同, 张明昊, 王帅, 何珺, 贾金山, 余乐军, 孙波, 熊昌民. 光电协同增强的场效应对LaAlO₃/SrTiO₃界面中持续光电导的调控. 物理学报, 2019, 68(6): 067302. doi: 10.7498/aps.68.20182204
[5]	赵润, 杨浩. 多铁性钙钛矿薄膜的氧空位调控研究进展. 物理学报, 2018, 67(15): 156101. doi: 10.7498/aps.67.20181028
[6]	刘小强, 吴淑雅, 朱晓莉, 陈湘明. Ruddlesden-Popper结构杂化非本征铁电体及其多铁性. 物理学报, 2018, 67(15): 157503. doi: 10.7498/aps.67.20180317
[7]	袁国亮, 李爽, 任申强, 刘俊明. 激发态电荷转移有机体的多铁性研究. 物理学报, 2018, 67(15): 157509. doi: 10.7498/aps.67.20180759
[8]	申见昕, 尚大山, 孙阳. 基于磁电耦合效应的基本电路元件和非易失性存储器. 物理学报, 2018, 67(12): 127501. doi: 10.7498/aps.67.20180712
[9]	黄颖妆, 齐岩, 杜安, 刘佳宏, 艾传韡, 戴海燕, 张小丽, 黄雨嫣. 复合多铁链的磁电耦合行为与外场调控. 物理学报, 2018, 67(24): 247501. doi: 10.7498/aps.67.20181561
[10]	吴枚霞, 李满荣. 异常双钙钛矿A2BB'O6氧化物的多铁性. 物理学报, 2018, 67(15): 157510. doi: 10.7498/aps.67.20180817
[11]	周龙, 王潇, 张慧敏, 申旭东, 董帅, 龙有文. 多阶有序钙钛矿多铁性材料的高压制备与物性. 物理学报, 2018, 67(15): 157505. doi: 10.7498/aps.67.20180878
[12]	殷云宇, 王潇, 邓宏芟, 周龙, 戴建洪, 龙有文. 多种有序钙钛矿结构的高压制备与特殊物性. 物理学报, 2017, 66(3): 030201. doi: 10.7498/aps.66.030201
[13]	刘恩华, 陈钊, 温晓莉, 陈长乐. 顺磁性La2/3Sr1/3MnO3层对Bi0.8Ba0.2FeO3薄膜多铁性能的影响. 物理学报, 2016, 65(11): 117701. doi: 10.7498/aps.65.117701
[14]	毛翔宇, 邹保文, 孙慧, 陈春燕, 陈小兵. Co含量对Bi6Fe2-xCoxTi3O18样品多铁性的影响. 物理学报, 2015, 64(21): 217701. doi: 10.7498/aps.64.217701
[15]	徐新河, 刘鹰, 甘月红, 刘文苗. 磁电耦合超材料本构矩阵获取方法的研究. 物理学报, 2015, 64(4): 044101. doi: 10.7498/aps.64.044101
[16]	王美娜, 李英, 王天兴, 刘国栋. 正交多铁性材料DyMnO3的磁性质研究. 物理学报, 2013, 62(22): 227101. doi: 10.7498/aps.62.227101
[17]	顾建军, 刘力虎, 岂云开, 徐芹, 张惠敏, 孙会元. 复合薄膜NiFe2 O4-BiFeO3 中的磁电耦合. 物理学报, 2011, 60(6): 067701. doi: 10.7498/aps.60.067701
[18]	马静, 施展, 林元华, 南策文. 准2-2型磁电多层复合材料的磁电性能. 物理学报, 2009, 58(8): 5852-5856. doi: 10.7498/aps.58.5852
[19]	仲崇贵, 蒋青, 方靖淮, 葛存旺. 单相ABO3型多铁材料的磁电耦合及磁电性质研究. 物理学报, 2009, 58(5): 3491-3496. doi: 10.7498/aps.58.3491
[20]	杨颖, 李启昌, 刘俊明, 刘治国. 铁电磁体Pb(Fe1/2Nb1/2)O3的磁电性能研究. 物理学报, 2005, 54(9): 4213-4216. doi: 10.7498/aps.54.4213

计量

文章访问数: 12041
PDF下载量: 690
被引次数: 0

姓名
邮箱
手机号码
标题
留言内容
验证码

搜索

留言板

电荷媒介的磁电耦合: 从铁电场效应到电荷序铁电体