高储能密度铁电聚合物纳米复合材料研究进展

沈忠慧; 江彦达; 李宝文; 张鑫

doi:10.7498/aps.69.20201209

摘要

介电电容器具有超高功率密度、低损耗以及高工作电压等优点, 是广泛应用于电子电力系统的关键储能器件. 铁电聚合物是发展高储能密度电介质薄膜材料的理想选择, 而基于铁电聚合物的纳米复合材料则兼具了聚合物的高击穿场强、柔性、易加工等特点以及陶瓷的高介电性能, 是近年来电介质储能材料研究的前沿与热点. 本文首先介绍了铁电聚合物材料的制备、铁电性能以及极化特性的调控方法, 随后总结了铁电聚合物纳米复合材料中纳米填料、复合结构以及界面三个关键调控策略对复合材料介电与储能性能的影响, 并探讨了基于相场方法的纳米复合材料中介电与储能特性的微观机制研究, 最后对高储能密度铁电聚合物纳米复合材料现存问题以及未来发展方向进行了总结与展望.

关键词:

Abstract

Electrostatic capacitors based on dielectrics delivering an ultrahigh power density, low loss and high operating voltage, are widely used in energy storage devices for modern electronic and electrical systems. Dielectric polymers, especially ferroelectric polymers, are preferable for an energy storage medium in film capacitors due to their superiority in ultrahigh breakdown strength, low mass density, flexibility, and easy fabrication process. Ferroelectric polymer nanocomposites combining the advantageous properties of ferroelectric polymer matrix and high dielectric constant of ceramic fillers, show great potential applications in achieving superior energy storage performances and have aroused substantial academic interest. This review focuses on the recent research progress of high-energy-density ferroelectric polymer nanocomposites. First, the synthesis and properties of PVDF-based ferroelectric polymers are introduced. Second, the effects of nanofillers, composite structures and interfaces on the dielectric and energy storage properties of ferroelectric polymer nanocomposites are summarized. Third, the underline mechanism of dielectric and energy storage behaviors in ferroelectric nanocomposites are discussed in the aspect of phase-field simulation. Last, the existing challenges and future directions of ferroelectric polymer nanocomposites with high energy storage density are summarized and prospected.

Keywords:

作者及机构信息

1.
武汉理工大学, 材料复合新技术国家重点实验室, 智能材料与器件研究中心, 武汉　430070

2.
武汉理工大学材料科学与工程国际化示范学院, 武汉　430070

通信作者: 张鑫, zhang-xin@whut.edu.cn

基金项目: 国家自然科学基金(批准号: 51802237, 52072280, 41180991)、中国科学技术协会青年人才托举工程(批准号: 2018QNRC001)和中央高校基本科研业务费(批准号: 193201002, 183101005, 182401004)资助的课题

Authors and contacts

1.
Center of Smart Materials and Devices, State Key Laboratory of Advanced Technology for Materials Synthesis and Processing, Wuhan University of Technology, Wuhan 430070, China

2.
International School of Materials Science and Engineering, Wuhan University of Technology, Wuhan 430070, China

Corresponding author: Zhang Xin, zhang-xin@whut.edu.cn

Funds: Project supported by the National Natural Science Foundation of China (Grant Nos. 51802237, 52072280, 41180991), the Young Elite Scientists Sponsorship Program by CAST, China (Grant No. 2018QNRC001), and the Fundamental Research Fund for the Central Universities, China (Grant Nos. 193201002, 183101005, 182401004)

文章全文 : translate this paragraph

参考文献

[1]	Li Q, Chen L, Gadinski M R, Zhang S H, Zhang G Z, Li H U, Iagodkine E, Haque A, Chen L Q, Jackson T N, Wang Q 2015 Nature 523 576 Google Scholar
[2]	Prateek, Thakur V K, Gupta R K 2016 Chem. Rev. 116 4260 Google Scholar
[3]	成桑, 李雨抒, 梁家杰, 李琦 2020 高分子学报 51 469 Google Scholar Chen S, Li Y S, Liang J J, Li Q 2020 Acta Polym. Sin. 51 469 Google Scholar
[4]	Barshaw E J, White J, Chait M J, Cornette J B, Rabuffi M 2007 IEEE Trans. Magn. 43 223 Google Scholar
[5]	Chen Q, Shen Y, Zhang S, Zhang Q M 2015 Annu. Rev. Mater. Res. 45 433 Google Scholar
[6]	Laihonen S J, Gafvert U, Schutte T, Gedde U 2007 IEEE Trans. Dielectr. Electr. Insul. 14 275 Google Scholar
[7]	Rabuffi M, Picci G 2002 IEEE Trans. Plasma Sci. 30 1939 Google Scholar
[8]	Kawa H 1969 Jpn. J. Appl. Phys. 8 975 Google Scholar
[9]	Lovinger A J 1983 Science 220 1115 Google Scholar
[10]	Martins P, Lopes A C, Lanceros-Mendez S 2014 Prog. Polym. Sci. 39 683 Google Scholar
[11]	Zhu L, Wang Q 2012 Macromolecules 45 2937 Google Scholar
[12]	Cheng Z Y, Zhang Q M, Bateman F B 2002 J. Appl. Phys. 92 6749 Google Scholar
[13]	Bharti V, Zhang Q M 2001 Phys. Rev. B 63 184103 Google Scholar
[14]	Li Z, Arbatti M D, Cheng Z Y 2004 Macromolecules 37 79 Google Scholar
[15]	Forsythe J S, Hill D 2000 Prog. Polym. Sci. 25 101 Google Scholar
[16]	Chu B, Zhou X, Neese B, Zhang Q M, Bauer F 2006 IEEE Trans. Dielectr. Electr. Insul. 13 1162 Google Scholar
[17]	Xu H, Cheng Z Y, Olson D, Mai T, Zhang Q M, Kavarnos G 2001 Appl. Phys. Lett. 78 2360 Google Scholar
[18]	Chu B, Zhou X, Ren K, Neese B, Lin M, Wang Q, Bauer F, Zhang Q M 2006 Science 313 334 Google Scholar
[19]	Zhou X, Chu B, Neese B, Lin M, Zhang Q 2007 IEEE Trans. Dielectr. Electr. Insul. 14 1133 Google Scholar
[20]	Zhou X, Zhao X, Suo Z, Zou C, Runt J, Liu S, Zhang S H, Zhang Q M 2009 Appl. Phys. Lett. 94 162901 Google Scholar
[21]	Guan F, Yang L, Wang J, Guan B, Han K, Wang Q, Zhu L 2011 Adv. Funct. Mater. 21 3176 Google Scholar
[22]	Guan F X, Wang J, Yang L Y, Tseng J K, Han K, Wang Q, Zhu L 2011 Macromolecules 44 2190 Google Scholar
[23]	Terzic I, Meereboer N L, Acuautla M, Portale G, Loos K 2019 Nat. Commun. 10 601 Google Scholar
[24]	Li J, Tan S, Ding S, Li H, Yang L, Zhang Z 2012 J. Mater. Chem. 22 23468 Google Scholar
[25]	Bornand V, Vacher C, Collet A, Papet P 2009 Mater. Chem. Phys. 117 169 Google Scholar
[26]	Kim E J, Kim K A, Yoon S M 2016 J. Phys. D: Appl. Phys. 49 075105 Google Scholar
[27]	Okabe Y, Murakami H, Osaka N, Saito H, Inoue T 2010 Polymer 51 1494 Google Scholar
[28]	Aid S, Eddhahak A, Khelladi S, Ortega Z, Chaabani S, Tcharkhtchi A 2019 Polym. Test. 73 222 Google Scholar
[29]	Zhang X, Shen Y, Shen Z H, Jiang J Y, Chen L Q, Nan C W 2016 ACS Appl. Mater. Interfaces 8 27236 Google Scholar
[30]	Meng N, Ren X, Santagiuliana G, Ventura L, Bilotti E 2019 Nat. Commun. 10 4535 Google Scholar
[31]	Yu K, Niu Y, Zhou Y, Bai Y, Wang H 2013 J. Am. Ceram. Soc. 96 2519 Google Scholar
[32]	Hao Y, Wang X, Bi K, Zhang J, Li L 2017 Nano Energy 31 49 Google Scholar
[33]	Thakur Y, Zhang T, Iacob C, Yang T, Bernholc J, Chen L Q, Runt J, Zhang Q M 2017 Nanoscale 9 10992 Google Scholar
[34]	Zhang T, Chen X, Thakur Y, Lu B, Zhang Q Y, Runt J, Zhang Q M 2020 Sci. Adv. 6 eaax6622 Google Scholar
[35]	Huang X, Sun B, Zhu Y, Li S, Jiang P 2019 Prog. Mater. Sci. 100 187 Google Scholar
[36]	Zhang H, Marwat M A, Xie B, Ashtar M, Ye Z G 2019 ACS Appl. Mater. Interfaces 12 1 Google Scholar
[37]	Tang H X, Lin Y R, Sodano H A 2012 Adv. Energy Mater. 2 469 Google Scholar
[38]	Wang G, Huang X, Jiang P 2015 ACS Appl. Mater. Interfaces 7 18017 Google Scholar
[39]	Zhang X, Jiang J Y, Shen Z H, Dan Z K, Shen Y 2018 Adv. Mater. 30 1707269 Google Scholar
[40]	Li H, Ai D, Ren L L, Yao B, Han Z B, Shen Z H, Wang J J, Chen L Q, Wang Q 2019 Adv. Mater. 31 1900875 Google Scholar
[41]	Bao Z W, Hou C M, Shen Z H, Sun H Y, Zhang G Q, Luo Z, Dai Z Z, Wang C M, Chen X W, Li L B, Yin Y W, Shen Y, Li X G 2020 Adv. Mater. 32 1907227 Google Scholar
[42]	Jiang Y D, Zhang X, Shen Z H, Li X H, Yan J J, Li B W, Nan C W 2020 Adv. Funct. Mater. 30 1906112 Google Scholar
[43]	Jiang J Y, Shen Z H, Cai X K, Qian Z K, Dan Z K, Lin Y H, Liu B L, Nan C W, C, Chen L Q, Shen Y 2019 Adv. Energy Mater. 9 1803411 Google Scholar
[44]	Luo S B, Yu J Y, Yu S H, Sun R, Cao L Q, Liao W H, Wong C P 2019 Adv. Energy Mater. 9 1803204 Google Scholar
[45]	Wang Y F, Chen J, Li Y, Niu Y J, Wang Q, Wang H 2019 J. Mater. Chem. 7 2965 Google Scholar
[46]	Wang Y F, Cui J, Yuan Q B, Niu Y J, Bai Y Y, Wang H 2015 Adv. Mater. 27 6658 Google Scholar
[47]	Liu F H, Li Q, Cui J, Li Z Y, Yang G, Liu Y, Dong L J, Xiong C X, Wang H, Wang Q 2017 Adv. Funct. Mater. 27 1606292 Google Scholar
[48]	Jiang J Y, Shen Z H, Qian J F, Dan Z K, Guo M F, He Y, Lin Y H, Nan C W, Chen L Q, Shen Y 2019 Nano Energy 62 220 Google Scholar
[49]	Lewis T J 2005 J. Phys. D: Appl. Phys. 38 202 Google Scholar
[50]	Tanaka T, Kozako M, Fuse N, Ohki Y 2005 IEEE Trans. Dielectr. Electr. Insul. 12 669 Google Scholar
[51]	Peng S M, Yang X, Yang Y, Wang S J, Zhou Y, Hu J, Li Q, He J L 2019 Adv. Mater. 31 e1807722 Google Scholar
[52]	Borgani R, Pallon L K H, Hedenqvist M S, Gedde U W, Haviland D B 2016 Nano Lett. 16 5934 Google Scholar
[53]	Zhang X, Li B-W, Dong L J, Liu H X, Chen W, Shen Y, Nan C W 2018 Adv. Mater. Interfaces 5 1800096 Google Scholar
[54]	Pourrahimi A M, Olsson R T, Hedenqvist M S 2018 Adv. Mater. 30 1703624 Google Scholar
[55]	Huang X Y, Jiang P K 2015 Adv. Mater. 27 546 Google Scholar
[56]	Xie L, Huang X, Yang K, Li S T, Jiang P K 2014 J. Mater. Chem. 2 5244 Google Scholar
[57]	Zhang T, Guo M F, Jiang J Y, Zhang X Y, Lin Y H, Nan C W, Shen Y 2019 RSC Adv. 9 35990 Google Scholar
[58]	Zhang X, Shen Y, Xu B, Zhang Q H, Gu L, Jiang J Y, Ma J, Lin Y H, Nan C W 2016 Adv. Mater. 28 2055 Google Scholar
[59]	Pan Z B, Zhai J W, Shen B 2017 J. Mater. Chem. A 5 15217 Google Scholar
[60]	Chen L Q 2008 J. Am. Ceram. Soc. 91 1835 Google Scholar
[61]	Wang J J, Wang B, Chen L Q 2019 Annu. Rev. Mater. Res. 49 127 Google Scholar
[62]	Wang Y U, Tan D Q 2011 J. Appl. Phys. 109 104102 Google Scholar
[63]	Wang Y U, Tan D Q, Krahn J 2011 J. Appl. Phys. 110 034115
[64]	Shen Z H, Wang J J, Lin Y H, Nan C W, Chen L Q, Shen Y 2018 Adv. Mater. 30 1704380 Google Scholar
[65]	Shen Z H, Wang J J, Jiang J Y, Huang S X, Lin Y H, Nan C W, Chen L Q, Shen Y 2019 Nat. Commun. 10 1843 Google Scholar
[66]	Shen Z H, Shen Y, Cheng X X, Lin H X, Chen L Q, Nan C W 2020 J. Materiomics 6 573 Google Scholar
[67]	Shen Z H, Wang J J, Zhang X, Lin Y H, Nan C W, Chen L Q, Shen Y 2017 Appl. Phys. Lett. 111 092901 Google Scholar

施引文献

图 1 D-E曲线示意图

Fig. 1. Schematic illustration of electric displacement (D)-electric field (E) loop.

下载: 全尺寸图片幻灯片

图 2 (a) PVDF晶体链构象示意图^[10]; (b) 沿c轴观察的PVDF晶体四个不同相的单胞^[11]

Fig. 2. (a) Schematic chain conformations^[10]; (b) unit cells of PVDF crystals with four different phases viewed along c-axis^[11].

下载: 全尺寸图片幻灯片

图 3 D-E曲线示意图(阴影区域代表释放的能量密度)　(a) 铁电; (b) 弛豫铁电; (c) 反铁电

Fig. 3. Schematic D-E hysteresis loops for (a) normal ferroelectric; (b) relaxor ferroelectric; (c) antiferroelectric behaviors. The shaded areas represent the released energy density.

下载: 全尺寸图片幻灯片

图 4 (a) PVDF和P(VDF-CTFE)-g-PS接枝共聚物的极化机制示意图; (b) P(VDF-CTFE)和P(VDF-CTFE)-g-PS接枝共聚物的D-E曲线^[21]; (c) PVDF的压折工艺图解; (d) 压折和拉伸PVDF薄膜储能性能的比较^[30]

Fig. 4. (a) Schematic models of polarization mechanisms for PVDF and P(VDF-CTFE)-g-PS; (b) D-E loops for the hot-pressed and stretched films of P(VDF-CTFE) and P(VDF-CTFE)-g-PS graft copolymers^[21]; (c) schematic demonstration of pressed-and-folding technique for PVDF; (d) a comparison of electric energy storage properties of pressed-and-folded and stretched films^[30].

下载: 全尺寸图片幻灯片

图 5 (a) PEI中超细纳米颗粒的体积分数与介电常数的关系^[33]; (b) 不同取向的纳米纤维填料对介电常数的影响^[37]; (c) 不同维度的Al₂O₃与c-BCB复合后的击穿场强与温度稳定性^[40]; (d) PVDF/Ca₂Nb₃O₁₀复合材料的击穿场强和储能密度^[41]

Fig. 5. (a) Relationship between volume fraction of ultrafine nanoparticles and dielectric constant in PEI^[33]; (b) influence of nanofiber fillers with different orientations on dielectric constant^[37]; (c) breakdown field strength and temperature stability of Al₂O₃ with different dimensions and c-BCB composites^[40]; (d) breakdown field strength and energy storage density of PVDF/Ca₂Nb₃O₁₀ composites^[41].

下载: 全尺寸图片幻灯片

图 6 (a) P(VDF-HFP)/BaTiO₃复合材料中不同梯度分布的示意图^[42]; (b) BNNS和BZT填料互穿结构的示意图^[43]; (c) BN和BT共混填料的制备过程和电镜图^[44]

Fig. 6. (a) Schematic diagram of different gradient distributions in P(VDF-HFP)/BaTiO₃ composites^[42]; (b) schematic diagram of interpenetrating structure of BNNS and BZT fillers^[43]; (c) preparation process and electron micrograph of BN and BT blend filler^[44].

下载: 全尺寸图片幻灯片

图 7 (a) 三明治结构复合薄膜的示意图和断面电镜图^[46]; (b) 分别掺有BNNS和BST的叠层结构示意图和电镜图^[47]; (c) 多层复合材料的制备流程图和示意图^[48]

Fig. 7. (a) Schematic diagram and sectional electron microscope of sandwich composite film^[46]; (b) schematic diagram and electron micrograph of laminated structure doped with BNNS and BST respectively^[47]; (c) preparation flow chart and schematic diagram of multilayer composite materials^[48].

下载: 全尺寸图片幻灯片

图 8 (a) GMA功能化PVDF-HFP的流程图^[56]; (b) PTFEMA, PHFBMA和PDFHM原位聚合的示意图和电镜图^[57]; (c) BaTiO₃@TiO₂多级结构的电镜图^[58]; (d) BaTiO₃@TiO₂@Al₂O₃同轴纤维的电镜图和示意图^[59]

Fig. 8. (a) Flow chart of GMA functionalized PVDF-HFP^[56]; (b) schematic diagram and electron micrograph of in-situ polymerization of PTFEMA, PHFBMA and PDFHM^[57]; (c) electron micrograph of BaTiO₂@TiO₂ multilevel structure^[58]; (d) electron micrograph and schematic diagram of BaTiO₃@TiO₂@Al₂O₃ coaxial fiber^[59].

下载: 全尺寸图片幻灯片

图 9 (a) 颗粒填料取向分布与介电常数的关系^[62]; (b) 多物理场协同击穿的路径演化及能量分布^[65]; (c) 不同填料种类的体积分数与击穿场强的关系^[64]; (d) 空间电荷分布的示意图^[67]

Fig. 9. (a) Relationship between orientation distribution of particulate filler and dielectric constant^[62]; (b) path evolution and energy distribution of multi-physical field cooperative breakdown^[65]; (c) the relationship between the volume fraction of different fillers and the breakdown field strength^[64]; (d) schematic diagram of space charge distribution^[67].

下载: 全尺寸图片幻灯片

[1]	Li Q, Chen L, Gadinski M R, Zhang S H, Zhang G Z, Li H U, Iagodkine E, Haque A, Chen L Q, Jackson T N, Wang Q 2015 Nature 523 576 Google Scholar
[2]	Prateek, Thakur V K, Gupta R K 2016 Chem. Rev. 116 4260 Google Scholar
[3]	成桑, 李雨抒, 梁家杰, 李琦 2020 高分子学报 51 469 Google Scholar Chen S, Li Y S, Liang J J, Li Q 2020 Acta Polym. Sin. 51 469 Google Scholar
[4]	Barshaw E J, White J, Chait M J, Cornette J B, Rabuffi M 2007 IEEE Trans. Magn. 43 223 Google Scholar
[5]	Chen Q, Shen Y, Zhang S, Zhang Q M 2015 Annu. Rev. Mater. Res. 45 433 Google Scholar
[6]	Laihonen S J, Gafvert U, Schutte T, Gedde U 2007 IEEE Trans. Dielectr. Electr. Insul. 14 275 Google Scholar
[7]	Rabuffi M, Picci G 2002 IEEE Trans. Plasma Sci. 30 1939 Google Scholar
[8]	Kawa H 1969 Jpn. J. Appl. Phys. 8 975 Google Scholar
[9]	Lovinger A J 1983 Science 220 1115 Google Scholar
[10]	Martins P, Lopes A C, Lanceros-Mendez S 2014 Prog. Polym. Sci. 39 683 Google Scholar
[11]	Zhu L, Wang Q 2012 Macromolecules 45 2937 Google Scholar
[12]	Cheng Z Y, Zhang Q M, Bateman F B 2002 J. Appl. Phys. 92 6749 Google Scholar
[13]	Bharti V, Zhang Q M 2001 Phys. Rev. B 63 184103 Google Scholar
[14]	Li Z, Arbatti M D, Cheng Z Y 2004 Macromolecules 37 79 Google Scholar
[15]	Forsythe J S, Hill D 2000 Prog. Polym. Sci. 25 101 Google Scholar
[16]	Chu B, Zhou X, Neese B, Zhang Q M, Bauer F 2006 IEEE Trans. Dielectr. Electr. Insul. 13 1162 Google Scholar
[17]	Xu H, Cheng Z Y, Olson D, Mai T, Zhang Q M, Kavarnos G 2001 Appl. Phys. Lett. 78 2360 Google Scholar
[18]	Chu B, Zhou X, Ren K, Neese B, Lin M, Wang Q, Bauer F, Zhang Q M 2006 Science 313 334 Google Scholar
[19]	Zhou X, Chu B, Neese B, Lin M, Zhang Q 2007 IEEE Trans. Dielectr. Electr. Insul. 14 1133 Google Scholar
[20]	Zhou X, Zhao X, Suo Z, Zou C, Runt J, Liu S, Zhang S H, Zhang Q M 2009 Appl. Phys. Lett. 94 162901 Google Scholar
[21]	Guan F, Yang L, Wang J, Guan B, Han K, Wang Q, Zhu L 2011 Adv. Funct. Mater. 21 3176 Google Scholar
[22]	Guan F X, Wang J, Yang L Y, Tseng J K, Han K, Wang Q, Zhu L 2011 Macromolecules 44 2190 Google Scholar
[23]	Terzic I, Meereboer N L, Acuautla M, Portale G, Loos K 2019 Nat. Commun. 10 601 Google Scholar
[24]	Li J, Tan S, Ding S, Li H, Yang L, Zhang Z 2012 J. Mater. Chem. 22 23468 Google Scholar
[25]	Bornand V, Vacher C, Collet A, Papet P 2009 Mater. Chem. Phys. 117 169 Google Scholar
[26]	Kim E J, Kim K A, Yoon S M 2016 J. Phys. D: Appl. Phys. 49 075105 Google Scholar
[27]	Okabe Y, Murakami H, Osaka N, Saito H, Inoue T 2010 Polymer 51 1494 Google Scholar
[28]	Aid S, Eddhahak A, Khelladi S, Ortega Z, Chaabani S, Tcharkhtchi A 2019 Polym. Test. 73 222 Google Scholar
[29]	Zhang X, Shen Y, Shen Z H, Jiang J Y, Chen L Q, Nan C W 2016 ACS Appl. Mater. Interfaces 8 27236 Google Scholar
[30]	Meng N, Ren X, Santagiuliana G, Ventura L, Bilotti E 2019 Nat. Commun. 10 4535 Google Scholar
[31]	Yu K, Niu Y, Zhou Y, Bai Y, Wang H 2013 J. Am. Ceram. Soc. 96 2519 Google Scholar
[32]	Hao Y, Wang X, Bi K, Zhang J, Li L 2017 Nano Energy 31 49 Google Scholar
[33]	Thakur Y, Zhang T, Iacob C, Yang T, Bernholc J, Chen L Q, Runt J, Zhang Q M 2017 Nanoscale 9 10992 Google Scholar
[34]	Zhang T, Chen X, Thakur Y, Lu B, Zhang Q Y, Runt J, Zhang Q M 2020 Sci. Adv. 6 eaax6622 Google Scholar
[35]	Huang X, Sun B, Zhu Y, Li S, Jiang P 2019 Prog. Mater. Sci. 100 187 Google Scholar
[36]	Zhang H, Marwat M A, Xie B, Ashtar M, Ye Z G 2019 ACS Appl. Mater. Interfaces 12 1 Google Scholar
[37]	Tang H X, Lin Y R, Sodano H A 2012 Adv. Energy Mater. 2 469 Google Scholar
[38]	Wang G, Huang X, Jiang P 2015 ACS Appl. Mater. Interfaces 7 18017 Google Scholar
[39]	Zhang X, Jiang J Y, Shen Z H, Dan Z K, Shen Y 2018 Adv. Mater. 30 1707269 Google Scholar
[40]	Li H, Ai D, Ren L L, Yao B, Han Z B, Shen Z H, Wang J J, Chen L Q, Wang Q 2019 Adv. Mater. 31 1900875 Google Scholar
[41]	Bao Z W, Hou C M, Shen Z H, Sun H Y, Zhang G Q, Luo Z, Dai Z Z, Wang C M, Chen X W, Li L B, Yin Y W, Shen Y, Li X G 2020 Adv. Mater. 32 1907227 Google Scholar
[42]	Jiang Y D, Zhang X, Shen Z H, Li X H, Yan J J, Li B W, Nan C W 2020 Adv. Funct. Mater. 30 1906112 Google Scholar
[43]	Jiang J Y, Shen Z H, Cai X K, Qian Z K, Dan Z K, Lin Y H, Liu B L, Nan C W, C, Chen L Q, Shen Y 2019 Adv. Energy Mater. 9 1803411 Google Scholar
[44]	Luo S B, Yu J Y, Yu S H, Sun R, Cao L Q, Liao W H, Wong C P 2019 Adv. Energy Mater. 9 1803204 Google Scholar
[45]	Wang Y F, Chen J, Li Y, Niu Y J, Wang Q, Wang H 2019 J. Mater. Chem. 7 2965 Google Scholar
[46]	Wang Y F, Cui J, Yuan Q B, Niu Y J, Bai Y Y, Wang H 2015 Adv. Mater. 27 6658 Google Scholar
[47]	Liu F H, Li Q, Cui J, Li Z Y, Yang G, Liu Y, Dong L J, Xiong C X, Wang H, Wang Q 2017 Adv. Funct. Mater. 27 1606292 Google Scholar
[48]	Jiang J Y, Shen Z H, Qian J F, Dan Z K, Guo M F, He Y, Lin Y H, Nan C W, Chen L Q, Shen Y 2019 Nano Energy 62 220 Google Scholar
[49]	Lewis T J 2005 J. Phys. D: Appl. Phys. 38 202 Google Scholar
[50]	Tanaka T, Kozako M, Fuse N, Ohki Y 2005 IEEE Trans. Dielectr. Electr. Insul. 12 669 Google Scholar
[51]	Peng S M, Yang X, Yang Y, Wang S J, Zhou Y, Hu J, Li Q, He J L 2019 Adv. Mater. 31 e1807722 Google Scholar
[52]	Borgani R, Pallon L K H, Hedenqvist M S, Gedde U W, Haviland D B 2016 Nano Lett. 16 5934 Google Scholar
[53]	Zhang X, Li B-W, Dong L J, Liu H X, Chen W, Shen Y, Nan C W 2018 Adv. Mater. Interfaces 5 1800096 Google Scholar
[54]	Pourrahimi A M, Olsson R T, Hedenqvist M S 2018 Adv. Mater. 30 1703624 Google Scholar
[55]	Huang X Y, Jiang P K 2015 Adv. Mater. 27 546 Google Scholar
[56]	Xie L, Huang X, Yang K, Li S T, Jiang P K 2014 J. Mater. Chem. 2 5244 Google Scholar
[57]	Zhang T, Guo M F, Jiang J Y, Zhang X Y, Lin Y H, Nan C W, Shen Y 2019 RSC Adv. 9 35990 Google Scholar
[58]	Zhang X, Shen Y, Xu B, Zhang Q H, Gu L, Jiang J Y, Ma J, Lin Y H, Nan C W 2016 Adv. Mater. 28 2055 Google Scholar
[59]	Pan Z B, Zhai J W, Shen B 2017 J. Mater. Chem. A 5 15217 Google Scholar
[60]	Chen L Q 2008 J. Am. Ceram. Soc. 91 1835 Google Scholar
[61]	Wang J J, Wang B, Chen L Q 2019 Annu. Rev. Mater. Res. 49 127 Google Scholar
[62]	Wang Y U, Tan D Q 2011 J. Appl. Phys. 109 104102 Google Scholar
[63]	Wang Y U, Tan D Q, Krahn J 2011 J. Appl. Phys. 110 034115
[64]	Shen Z H, Wang J J, Lin Y H, Nan C W, Chen L Q, Shen Y 2018 Adv. Mater. 30 1704380 Google Scholar
[65]	Shen Z H, Wang J J, Jiang J Y, Huang S X, Lin Y H, Nan C W, Chen L Q, Shen Y 2019 Nat. Commun. 10 1843 Google Scholar
[66]	Shen Z H, Shen Y, Cheng X X, Lin H X, Chen L Q, Nan C W 2020 J. Materiomics 6 573 Google Scholar
[67]	Shen Z H, Wang J J, Zhang X, Lin Y H, Nan C W, Chen L Q, Shen Y 2017 Appl. Phys. Lett. 111 092901 Google Scholar

[1]	宋小凡, 闵道敏, 高梓巍, 王泊心, 郝予涛, 高景晖, 钟力生. 聚醚酰亚胺纳米复合电介质中指数分布陷阱电荷跳跃输运对储能性能的影响. 物理学报, 2024, 73(2): 027301. doi: 10.7498/aps.73.20230556
[2]	邓晨华, 于忠海, 王宇涛, 孔森, 周超, 杨森. Ti掺杂Nd₂Fe₁₄B/α-Fe纳米双相复合永磁体晶化动力学. 物理学报, 2023, 72(2): 027501. doi: 10.7498/aps.72.20221479
[3]	查俊伟, 查磊军, 郑明胜. 聚偏氟乙烯基复合材料储能特性优化策略. 物理学报, 2023, 72(1): 018401. doi: 10.7498/aps.72.20222012
[4]	潘鹏晖, 吉鹏飞, 林根, 董希明, 赵晋晖. 飞秒激光加工熔融石英的理论和实验研究. 物理学报, 2022, 71(24): 247901. doi: 10.7498/aps.71.20221496
[5]	徐强, 司雪, 佘维汉, 杨光敏. 超电容储能电极材料的密度泛函理论研究. 物理学报, 2021, 70(10): 107301. doi: 10.7498/aps.70.20201988
[6]	王娇, 刘少辉, 周梦, 郝好山, 翟继卫. 钛酸锶纳米纤维表面羟基化处理对聚偏氟乙烯复合材料介电性能和储能性能的影响. 物理学报, 2020, 69(21): 218101. doi: 10.7498/aps.69.20200592
[7]	王娇, 刘少辉, 陈长青, 郝好山, 翟继卫. 钛酸钡基/聚偏氟乙烯复合介质材料的界面改性与储能性能. 物理学报, 2020, 69(21): 217702. doi: 10.7498/aps.69.20201031
[8]	董久锋, 邓星磊, 牛玉娟, 潘子钊, 汪宏. 面向高温介电储能应用的聚合物基电介质材料研究进展. 物理学报, 2020, 69(21): 217701. doi: 10.7498/aps.69.20201006
[9]	高铭泽, 张沛红. 纳米SiO2/环氧树脂复合材料介电性与纳米粒子分散性关系. 物理学报, 2016, 65(24): 247802. doi: 10.7498/aps.65.247802
[10]	马国亮, 杨剑群, 李兴冀, 刘超铭, 侯春风. 电子辐照聚乙烯/碳纳米管拉伸变形机理. 物理学报, 2016, 65(17): 178104. doi: 10.7498/aps.65.178104
[11]	马国亮, 李兴冀, 杨剑群, 刘超铭, 田丰, 侯春风. 电子辐照LDPE/MWCNTs复合材料的熔融与结晶行为. 物理学报, 2016, 65(20): 208101. doi: 10.7498/aps.65.208101
[12]	冯奇, 李梦凯, 唐海通, 王晓东, 高忠民, 孟繁玲. 石墨烯/聚乙烯醇/聚偏氟乙烯基纳米复合薄膜的介电性能. 物理学报, 2016, 65(18): 188101. doi: 10.7498/aps.65.188101
[13]	李丽丽, Xia Zhen-Hai, 杨延清, 韩明. SiC纳米纤维/C/SiC复合材料拉伸行为的分子动力学研究. 物理学报, 2015, 64(11): 117101. doi: 10.7498/aps.64.117101
[14]	武峥, 周嘉仪, 曹艺, 马柯, 贾艳敏, 张以河. 电泳辅助制备伪1-3陶瓷/聚合物压电复合材料. 物理学报, 2014, 63(2): 027701. doi: 10.7498/aps.63.027701
[15]	张程宾, 程启坤, 陈永平. 分形结构纳米复合材料热导率的分子动力学模拟研究. 物理学报, 2014, 63(23): 236601. doi: 10.7498/aps.63.236601
[16]	黄丛亮, 冯妍卉, 张欣欣, 李威, 杨穆, 李静, 王戈. 介孔二氧化硅基导电聚合物复合材料热导率的实验研究. 物理学报, 2012, 61(15): 154402. doi: 10.7498/aps.61.154402
[17]	尹桂来, 李建英, 李盛涛. 利用普适介电理论对银/氧化锌复合材料介电性能的研究. 物理学报, 2009, 58(6): 4219-4224. doi: 10.7498/aps.58.4219
[18]	黄集权, 洪兰秀, 韩高荣, 翁文剑, 杜丕一. Fe-Ni-BaTiO3复合材料的介电行为及其机理研究. 物理学报, 2006, 55(7): 3664-3669. doi: 10.7498/aps.55.3664
[19]	张华, 范滇元. 组合式钕玻璃片状激光放大器增益性能的动态模拟. 物理学报, 2001, 50(12): 2375-2381. doi: 10.7498/aps.50.2375
[20]	计齐根, 都有为. 晶粒边界对Nd2Fe14B/α-Fe纳米复合材料性能的影响. 物理学报, 2000, 49(11): 2281-2286. doi: 10.7498/aps.49.2281

计量

文章访问数: 14673
PDF下载量: 685
被引次数: 0

姓名
邮箱
手机号码
标题
留言内容
验证码

搜索

留言板

高储能密度铁电聚合物纳米复合材料研究进展