Ti, N共掺杂4H-SiC复合增强缓冲层生长及其对PiN二极管正向性能稳定性的改善

李传纲; 鞠涛; 张立国; 李杨; 张璇; 秦娟; 张宝顺; 张泽洪

doi:10.7498/aps.70.20200921

摘要

“双极型退化”现象严重阻碍了4H-SiC双极型器件如PiN二极管等的产品化, 其微观机理是电子-空穴复合条件下层错由基面位错处的扩展. 为遏制“双极型退化”现象, 不仅要消除漂移层中的基面位错, 还需要通过生长复合增强缓冲层的方法阻止少子空穴到达含高密度基面位错片段的外延层/衬底界面. 本文采用钛、氮共掺杂的方式进行缓冲层的生长, 通过钛掺杂进一步降低缓冲层中的少子寿命. 首先确定了钛掺杂浓度和钛源摩尔流量之间的定量关系, 在此基础上制备了含钛、氮共掺杂缓冲层结构的4H-SiC PiN二极管, 并在正向电流密度100 A/cm²的条件下保持10 min, 测量其正向压降随时间的变化. 与无缓冲层结构、仅含高浓度氮掺杂缓冲层结构的4H-SiC PiN二极管相比, 含钛、氮共掺杂缓冲层的二极管的正向压降稳定性得到了明显改善.

关键词:

Abstract

“Bipolar degradation” phenomenon has severely impeded the development of 4H-SiC bipolar devices. Their defect mechanism is the expansion of Shockley-type stacking faults from basal plane dislocations under the condition of electron-hole recombination. To suppress the “bipolar degradation” phenomenon, not only do the basal plane dislocations in the 4H-SiC drift layer need eliminating, but also a recombination-enhancing buffer layer is required to prevent the minority carriers of holes from reaching the epilayer/substrate interface where high-density basal plane dislocation segments exist. In this paper, Ti and N co-doped 4H-SiC buffer layers are grown to further shorten the minority carrier lifetime. Firstly, the dependence of Ti doping concentration on TiCl₄ flow rate in 4H-SiC epilayers is determined by using single-dilution gas line and double-dilution gas line. Then the p⁺ layer and p⁺⁺ layer in PiN diode are obtained by aluminum ion implantation at room temperature and 500 ℃ followed by high temperature activation annealing. Finally, 4H-SiC PiN diodes with a Ti, N co-doped buffer layer are fabricated and tested with a forward current density of 100 A/cm² for 10 min. Comparing with the PiN diodes without a buffer layer and with a buffer layer only doped with high concentration of nitrogen, the forward voltage drop stability of those diodes with a 2 μm-thick Ti, N co-doped buffer layer (Ti: 3.70 × 10¹⁵ cm^–3 and N: 1.01 × 10¹⁹ cm^–3) is greatly improved.

Keywords:

作者及机构信息

1.
上海大学材料科学与工程学院, 上海　200444

2.
中国科学院苏州纳米技术与纳米仿生研究所, 苏州　215123

通信作者: 秦娟, juan_qin@staff.shu.edu.cn ; 张宝顺, bszhang2006@sinano.ac.cn ;

基金项目: 国家自然科学基金青年科学基金(批准号: 61804166)资助的课题

Authors and contacts

1.
School of Materials Science and Engineering, Shanghai University, Shanghai 200444, China

2.
Suzhou Institute of Nano-Tech and Nano-Bionics, Chinese Academy of Sciences, Suzhou 215123, China

Corresponding author: Qin Juan, juan_qin@staff.shu.edu.cn ; Zhang Bao-Shun, bszhang2006@sinano.ac.cn ;

Funds: Project supported by the Young Scientists Fund of the National Natural Science Foundation of China (Grant No. 61804166)

文章全文 : translate this paragraph

参考文献

[1]	Lendenmann H, Dahlquist F, Johansson N, Soderholm R, Nilsson P A, Bergman J P, Skytt P 2001 Mater. Sci. Forum. 353–356 727 Google Scholar
[2]	Skowronski M, Liu J Q, Vetter W M, Dudley M, Hallin C, Lendenmann H 2002 J. Appl. Phys. 92 4699 Google Scholar
[3]	Caldwell J D, Stahlbush R E, Ancona M G, Glembocki O J, Hobart K D 2010 J. Appl. Phys. 108 044503 Google Scholar
[4]	Maeda K, Hirano R, Sato Y, Tajima M 2012 Mater. Sci. Forum. 725 35 Google Scholar
[5]	Ha S, Mieszkowski P, Skowronski M, Rowland L B 2002 J. Cryst. Growth 244 257 Google Scholar
[6]	Tsuchida H, Kamata I, Miyazawa T, Ito M, Zhang X, Nagano M 2018 Mater. Sci. Semicond. Process. 78 2 Google Scholar
[7]	Tanaka A, Matsuhata H, Kawabata N, Mori D, Inoue K, Ryo M, Fujimoto T, Tawara T, Miyazato M, Miyajima M, Fukuda K, Ohtsuki A, Tomohisa T, Tsuchida H, Yonezawa Y, Kimoto T 2016 J. Appl. Phys. 119 095711 Google Scholar
[8]	Sumakeris J J, Bergman P, Das M K, Hallin C, Hull B A, Janzen E, Lendenmann H, O’Loughlin M J, Paisley M J, Ha S Y, Skowronski M, Palmour J W, Carter Jr C H 2006 Mater. Sci. Forum. 527-529 141 Google Scholar
[9]	Hori T, Danno K, Kimoto T 2007 J. Cryst. Growth. 306 297 Google Scholar
[10]	Stahlbush R E, VanMil B L, Myers Ward R L, Lew K K, Gaskill D K, Eddy Jr C R 2009 Appl. Phys. Lett. 94 041916 Google Scholar
[11]	Mahadik N A, Stahlbush R E, Ancona M G, Lmhoff E A, Hobart K D, Myers-Ward R L, Eddy Jr C R, Gaskill D K, Kub F J 2012 Appl. Phys. Lett. 100 042102 Google Scholar
[12]	Tawara T, Miyazawa T, Ryo M, Miyazato M, Fujimoto T, Takenaka K, Matsunaga S, Miyajima M, Otsuki A, Yonezawa Y, Kato T, Okumura H, Kimoto T, Tsuchida H 2016 J. Appl. Phys. 120 115101 Google Scholar
[13]	Miyazawa T, Tawara T, Tsuchida H 2017 Mater. Sci. Forum. 897 67 Google Scholar
[14]	Miyazawa T, Tawara T, Takanashi R, Tsuchida H 2016 Appl. Phys. Express 9 111301 Google Scholar
[15]	Murata K, Tawara T, Yang A, Takanashi R, Miyazawa T, Tsuchida H 2019 J. Appl. Phys. 126 045711 Google Scholar
[16]	Tawara T, Miyazawa T, Ryo M, Miyazato M, Fujimoto T, Takenaka K, Matsunaga S, Miyajima M, Otsuki A, Yonezawa Y, Kato T, Okumura H, Kimoto T, Tsuchida H 2017 Mater. Sci. Forum. 897 419 Google Scholar
[17]	Dalibor T, Pensl G, Matsunami H, Kimoto T, Choyke W J, Schoner A, Nordell N 1997 Phys. Status Solidi A 162 199 Google Scholar
[18]	Hobgood H M, Glass R C, Augustine G, Hopkins R H, Jenny J, Skowronski M, Mitchel W C, Roth M 1995 Appl. Phys. Lett. 66 1364 Google Scholar
[19]	Dalibor T, Pensl G, Nordell N, Schoner A 1997 Phys. Rev. B 55 13618 Google Scholar
[20]	Maier K, Muller H D, Schneider J 1992 Mater. Sci. Forum. 83–87 1183 Google Scholar

施引文献

图 1 (a) 4H-SiC CVD外延设备示意图; Ti掺杂(b)单稀释和(c)双稀释管路示意图

Fig. 1. Schematics of (a) the CVD reactor for 4H-SiC epitaxial growth, (b) single-dilution pipe and (c) double-dilution pipe of TiCl₄ gas delivery.

下载: 全尺寸图片幻灯片

图 2 (a) 含Ti, N共掺杂缓冲层结构的SiC PiN二极管结构示意图; (b) TRIM模拟的Al注入浓度箱型分布

Fig. 2. (a) Schematic of the cross-sectional structure of a 4H-SiC PiN diode with Ti and N co-doped buffer layer; (b) box-profile of Al concentration by TRIM simulation.

下载: 全尺寸图片幻灯片

图 3 Ti掺杂浓度随TiCl₄摩尔流量的变化

Fig. 3. Relationship between Ti doping concentration and TiCl₄ mole flow rate.

下载: 全尺寸图片幻灯片

图 4 Ti, N共掺杂4H-SiC缓冲层表面形貌(N_d = 1.01 × 10¹⁹ cm^–3)　(a) Ti掺杂浓度为3.70 × 10¹⁵ cm^–3; (b) Ti掺杂浓度为3.71 × 10¹⁶ cm^–3

Fig. 4. Optical microscope images of the Ti and N co-doped 4H-SiC buffer layer surface with Ti doping concentrations of (a) 3.70 × 10¹⁵ cm^–3 and (b) 3.71 × 10¹⁶ cm^–3. Both with N_d = 1.01 × 10¹⁹ cm^–3.

下载: 全尺寸图片幻灯片

图 5 无缓冲层、仅含高浓度N掺杂缓冲层、含Ti和N共掺杂缓冲层的4H-SiC PiN二极管的正向特性　(a), (c), (e)在100 A/cm²电流密度下10 min, 正向压降随时间的变化; (b), (d), (f)正向偏置前后正向电流-电压曲线的对比

Fig. 5. (a), (c), (e) Change of forward voltage drop vs. time and (b), (d), (f) comparison between the forward I-V characteristics before and after being biased for 10 min at a current density of 100 A/cm² for 4H-SiC PiN diodes without a buffer layer, with a highly N-doped buffer layer, and with a Ti and N co-doped buffer layer.

下载: 全尺寸图片幻灯片

表 1 Ti掺杂实验参数

Table 1. Experimental parameters of Ti doping.

稀释管路	MFC1	MFC2	MFC3	TiCl₄掺杂摩尔流量
稀释管路	/sccm	/slm	/sccm	/(mol·min^–1)
单稀释	1.25	9.800	—	7.25 × 10^–7
	5	9.800	—	2.90 × 10^–6
	50	9.800	—	2.90 × 10^–5
双稀释	50	0.100	5	8.95 × 10^–7
	50	0.075	5	1.14 × 10^–6
	50	0.040	5	1.62 × 10^–6

下载: 导出CSV

[1]	Lendenmann H, Dahlquist F, Johansson N, Soderholm R, Nilsson P A, Bergman J P, Skytt P 2001 Mater. Sci. Forum. 353–356 727 Google Scholar
[2]	Skowronski M, Liu J Q, Vetter W M, Dudley M, Hallin C, Lendenmann H 2002 J. Appl. Phys. 92 4699 Google Scholar
[3]	Caldwell J D, Stahlbush R E, Ancona M G, Glembocki O J, Hobart K D 2010 J. Appl. Phys. 108 044503 Google Scholar
[4]	Maeda K, Hirano R, Sato Y, Tajima M 2012 Mater. Sci. Forum. 725 35 Google Scholar
[5]	Ha S, Mieszkowski P, Skowronski M, Rowland L B 2002 J. Cryst. Growth 244 257 Google Scholar
[6]	Tsuchida H, Kamata I, Miyazawa T, Ito M, Zhang X, Nagano M 2018 Mater. Sci. Semicond. Process. 78 2 Google Scholar
[7]	Tanaka A, Matsuhata H, Kawabata N, Mori D, Inoue K, Ryo M, Fujimoto T, Tawara T, Miyazato M, Miyajima M, Fukuda K, Ohtsuki A, Tomohisa T, Tsuchida H, Yonezawa Y, Kimoto T 2016 J. Appl. Phys. 119 095711 Google Scholar
[8]	Sumakeris J J, Bergman P, Das M K, Hallin C, Hull B A, Janzen E, Lendenmann H, O’Loughlin M J, Paisley M J, Ha S Y, Skowronski M, Palmour J W, Carter Jr C H 2006 Mater. Sci. Forum. 527-529 141 Google Scholar
[9]	Hori T, Danno K, Kimoto T 2007 J. Cryst. Growth. 306 297 Google Scholar
[10]	Stahlbush R E, VanMil B L, Myers Ward R L, Lew K K, Gaskill D K, Eddy Jr C R 2009 Appl. Phys. Lett. 94 041916 Google Scholar
[11]	Mahadik N A, Stahlbush R E, Ancona M G, Lmhoff E A, Hobart K D, Myers-Ward R L, Eddy Jr C R, Gaskill D K, Kub F J 2012 Appl. Phys. Lett. 100 042102 Google Scholar
[12]	Tawara T, Miyazawa T, Ryo M, Miyazato M, Fujimoto T, Takenaka K, Matsunaga S, Miyajima M, Otsuki A, Yonezawa Y, Kato T, Okumura H, Kimoto T, Tsuchida H 2016 J. Appl. Phys. 120 115101 Google Scholar
[13]	Miyazawa T, Tawara T, Tsuchida H 2017 Mater. Sci. Forum. 897 67 Google Scholar
[14]	Miyazawa T, Tawara T, Takanashi R, Tsuchida H 2016 Appl. Phys. Express 9 111301 Google Scholar
[15]	Murata K, Tawara T, Yang A, Takanashi R, Miyazawa T, Tsuchida H 2019 J. Appl. Phys. 126 045711 Google Scholar
[16]	Tawara T, Miyazawa T, Ryo M, Miyazato M, Fujimoto T, Takenaka K, Matsunaga S, Miyajima M, Otsuki A, Yonezawa Y, Kato T, Okumura H, Kimoto T, Tsuchida H 2017 Mater. Sci. Forum. 897 419 Google Scholar
[17]	Dalibor T, Pensl G, Matsunami H, Kimoto T, Choyke W J, Schoner A, Nordell N 1997 Phys. Status Solidi A 162 199 Google Scholar
[18]	Hobgood H M, Glass R C, Augustine G, Hopkins R H, Jenny J, Skowronski M, Mitchel W C, Roth M 1995 Appl. Phys. Lett. 66 1364 Google Scholar
[19]	Dalibor T, Pensl G, Nordell N, Schoner A 1997 Phys. Rev. B 55 13618 Google Scholar
[20]	Maier K, Muller H D, Schneider J 1992 Mater. Sci. Forum. 83–87 1183 Google Scholar

[1]	常帅军, 马海伦, 李浩, 欧树基, 郭建飞, 钟鸣浩, 刘莉. 一种能够改善鲁棒性的新型4H-SiC ESD防护器件. 物理学报, 2022, 71(19): 198501. doi: 10.7498/aps.71.20220879
[2]	杜园园, 张春雷, 曹学蕾. 基于4H-SiC肖特基势垒二极管的射线探测器. 物理学报, 2016, 65(20): 207301. doi: 10.7498/aps.65.207301
[3]	贾仁需, 刘思成, 许翰迪, 陈峥涛, 汤晓燕, 杨霏, 钮应喜. 4H-SiC同质外延生长Grove模型研究. 物理学报, 2014, 63(3): 037102. doi: 10.7498/aps.63.037102
[4]	秦玉香, 刘梅, 化得燕. Ti掺杂W18O49纳米线的电子结构与NO2敏感性能的第一性原理研究. 物理学报, 2014, 63(20): 207101. doi: 10.7498/aps.63.207101
[5]	宋坤, 柴常春, 杨银堂, 张现军, 陈斌. 栅漏间表面外延层对4H-SiC功率MESFET击穿特性的改善机理与结构优化. 物理学报, 2012, 61(2): 027202. doi: 10.7498/aps.61.027202
[6]	汤晓燕, 戴小伟, 张玉明, 张义门. 套刻偏差对4H-SiC 浮动结结势垒肖特基二极管的影响研究. 物理学报, 2012, 61(8): 088501. doi: 10.7498/aps.61.088501
[7]	张林, 肖剑, 邱彦章, 程鸿亮. Ti/4H-SiC肖特基势垒二极管抗辐射特性的研究. 物理学报, 2011, 60(5): 056106. doi: 10.7498/aps.60.056106
[8]	苗瑞霞, 张玉明, 汤晓燕, 张义门. 4H-SiC中基面位错发光特性研究. 物理学报, 2011, 60(3): 037808. doi: 10.7498/aps.60.037808
[9]	程萍, 张玉明, 张义门. 退火对非故意掺杂4H-SiC外延材料386 nm和388 nm发射峰的影响. 物理学报, 2011, 60(1): 017103. doi: 10.7498/aps.60.017103
[10]	程萍, 张玉明, 张义门, 王悦湖, 郭辉. 非故意掺杂4H-SiC外延材料本征缺陷的热稳定性. 物理学报, 2010, 59(5): 3542-3546. doi: 10.7498/aps.59.3542
[11]	张林, 韩超, 马永吉, 张义门, 张玉明. Ni/4H-SiC肖特基势垒二极管的γ射线辐照效应. 物理学报, 2009, 58(4): 2737-2741. doi: 10.7498/aps.58.2737
[12]	吕红亮, 张义门, 张玉明, 车勇, 王悦湖, 陈亮. 4H-SiC 射频MESFET中陷阱参数的提取方法. 物理学报, 2008, 57(5): 2871-2874. doi: 10.7498/aps.57.2871
[13]	贾仁需, 张义门, 张玉明, 王悦湖. N型4H-SiC同质外延生长. 物理学报, 2008, 57(10): 6649-6653. doi: 10.7498/aps.57.6649
[14]	徐静平, 李春霞, 吴海平. 4H-SiC n-MOSFET的高温特性分析. 物理学报, 2005, 54(6): 2918-2923. doi: 10.7498/aps.54.2918
[15]	林洪峰, 谢二庆, 马紫微, 张军, 彭爱华, 贺德衍. 射频溅射法制备3C-SiC和4H-SiC薄膜. 物理学报, 2004, 53(8): 2780-2785. doi: 10.7498/aps.53.2780
[16]	邵军. Ti掺杂ZnTe体材料的优化光致发光光谱. 物理学报, 2003, 52(7): 1743-1747. doi: 10.7498/aps.52.1743
[17]	吕红亮, 张义门, 张玉明. 4H-SiC pn结型二极管击穿特性中隧穿效应影响的模拟研究. 物理学报, 2003, 52(10): 2541-2546. doi: 10.7498/aps.52.2541
[18]	杨林安, 张义门, 龚仁喜, 张玉明. 4H-SiC射频功率MESFET的自热效应分析. 物理学报, 2002, 51(1): 148-152. doi: 10.7498/aps.51.148
[19]	张洪涛, 徐重阳, 邹雪城, 王长安, 赵伯芳, 周雪梅, 曾祥斌. 4H-SiC纳米薄膜的微结构及其光电性质研究. 物理学报, 2002, 51(2): 304-309. doi: 10.7498/aps.51.304
[20]	徐昌发, 杨银堂, 刘莉. 4H-SiC MOSFET的温度特性研究. 物理学报, 2002, 51(5): 1113-1117. doi: 10.7498/aps.51.1113

计量

文章访问数: 7392
PDF下载量: 126
被引次数: 0

姓名
邮箱
手机号码
标题
留言内容
验证码

搜索

留言板