Research progress of Cu<sub>2</sub>Se thin film thermoelectric properties

Yang Liang-Liang; Qin Yuan-Hao; Wei Jiang-Tao; Song Pei-Shuai; Zhang Ming-Liang; Yang Fu-Hua; Wang Xiao-Dong

doi:10.7498/aps.70.20201677

Abstract

Thermoelectric (TE) materials can directly realize the mutual conversion between heat and electricity, and it is an environmentally friendly functional material. At present, the thermoelectric conversion efficiencies of thermoelectric materials are low, which seriously restricts the large-scale application of thermoelectric devices. Therefore, finding new materials with better thermoelectric properties or improving the thermoelectric properties of traditional thermoelectric materials has become the subject of thermoelectric research. Thin film materials, compared with bulk materials, possess both the two-dimensional macroscopic properties and one-dimensional nanostructure characteristics, which makes it much easier to study the relationships between physical mechanisms and properties. Besides, thin film are also suitable for the preparation of wearable electronic devices. This article summarizes five different preparation methods of Cu₂Se thin films, i.e. electrochemical deposition, thermal evaporation, spin coating, sputtering, and pulsed laser deposition. In addition, combing with typical examples, the characterization methods of the film are summarized, and the influence mechanism of each parameter on the thermoelectric performance from electrical conductivity, Seebeck coefficient and thermal conductivity is discussed. Finally, the hot application direction of Cu₂Se thin film thermoelectrics is also introduced.

Keywords:

Authors and contacts

1.
Engineering Research Center for Semiconductor Integrated Technology, Institute of Semiconductors, Chinese Academy of Sciences, Beijing 100083, China
2.
College of Microelectronics and Research Center of Materials and Optoelectronics, University of Chinese Academy of Sciences, Beijing 100049, China
3.
Beijing Institute of Quantum Information Science, Beijing 100193, China
4.
Beijing Semiconductor Micro/Nano Integrated Engineering Technology Research Center, Beijing 100083, China

Corresponding author: Wang Xiao-Dong, xdwang@semi.ac.cn

Funds: Project supported by the National Key Research and Development Program of China (Grant Nos. 2019YFB1503602, 2018YFB1107502), the Pilot B Program of the Chinese Academy of Sciences, China (Grant No. XDB43020500) and Development Program of Scientific Research Instruments and Equipment of the Chinese Academy of Sciences, China (Grant No. GJJSTD20200006)

FullText HTML : translate this paragraph

References

[1]	Lu P, Liu H, Yuan X, Xu F, Shi X, Zhao K, Qiu W, Zhang W, Chen L 2015 J. Mater. Chem. A 3 6901 Google Scholar
[2]	Hussain R A, Hussain I 2020 Solid State Sci. 100 106101 Google Scholar
[3]	Malekar V P, Gangawane S A, Fulari V J 2020 Mater. Today Proc. 23 202 Google Scholar
[4]	Sharma K, Sharma D K, Kumar V 2020 Optik 206 164376 Google Scholar
[5]	Li Y, Fan P, Zheng Z, Luo J, Liang G, Guo S 2016 J. Alloy. Compd. 658 880 Google Scholar
[6]	Wei J J, Yang L L, Ma Z, Song P S, Zhang M L, Ma J, Yang F H, Wang X D 2020 J. Mater. Sci. 55 12642 Google Scholar
[7]	Biswas K, He J, Blum I D, Wu C I, Hogan T P, Seidman D N, Dravid V P, Kanatzidis M G 2012 Nature 489 414 Google Scholar
[8]	Harman T C, Taylor P J, Walsh M P, LaForge B E 2002 Science 297 2229 Google Scholar
[9]	Pammi S V N, Jella V, Choi J S, Yoon S G 2017 J. Mater. Chem. C 5 763 Google Scholar
[10]	Lv Y, Chen J, Zheng R K, Shi X, Song J, Zhang T, Li X, Chen L 2015 Ceram. Int. 41 7439 Google Scholar
[11]	Ma Z, Liu Y, Deng L, Zhang M, Zhang S, Ma J, Song P, Liu Q, Ji A, Yang F, Wang X 2018 Nanomaterials 8 77 Google Scholar
[12]	Chen X, Dai W, Wu T, Luo W, Yang J, Jiang W, Wang L 2018 Coatings 8 244 Google Scholar
[13]	Hicks L D, Dresselhaus M S 1993 Phys. Rev. B Condens Matter 47 12727 Google Scholar
[14]	Dresselhaus M S, Dresselhaus G, Sun X, Zhang Z, Cronin S B, Koga T 1999 Phys. Solid State 41 679 Google Scholar
[15]	Venkatasubramanian R, Siivola E, Colpitts T, O'Quinn B J N 2001 Nature 413 597 Google Scholar
[16]	Zhou Y, Matsubara I, Shin W, Izu N, Murayama N 2004 J. Appl. Phys. 95 625 Google Scholar
[17]	Hochbaum A I, Chen R, Delgado R D, Liang W, Garnett E C, Najarian M, Majumdar A, Yang P 2008 Nature 451 163 Google Scholar
[18]	Zheng X J, Zhu L, Zhou Y H, Zhang Q 2005 Appl. Phys. Lett. 87 2229
[19]	Mehdizadeh D A, Zebarjadi M, He J, Tritt T M 2015 Mater. Sci. Eng. R 97 1 Google Scholar
[20]	Hinterleitner B, Knapp I, Poneder M, Shi Y, Müller H, Eguchi G, Eisenmenger S C, Stöger P M, Kakefuda Y, Kawamoto N, Guo Q, Baba T, Mori T, Ullah S, Chen X Q, Bauer E 2019 Nature 576 85 Google Scholar
[21]	Wang C, Xia K, Wang H, Liang X, Yin Z, Zhang Y 2019 Adv. Mater. 31 1801072 Google Scholar
[22]	Zhao W Y, Zhang Q J, Sun Z G, Zhu W T, Wei P, Fang W B, Tian Y, Nie X L, Li P 2019 J. Inorg. Mater. 34 6
[23]	Gahtori B, Bathula S, Tyagi K, Jayasimhadri M, Srivastava A K, Singh S, Budhani R C, Dhar A 2015 Nano Energy 13 36 Google Scholar
[24]	Zhao K, Liu K, Yue Z, Wang Y, Song Q, Li J, Guan M, Xu Q, Qiu P, Zhu H, Chen L, Shi X 2019 Adv. Mater. 190 3480
[25]	Byeon D, Sobota R, Delime Codrin K, Choi S, Hirata K, Adachi M, Kiyama M, Matsuura T, Yamamoto Y, Matsunami M, Takeuchi T 2019 Nat. Commun. 10 72 Google Scholar
[26]	Byeon D, Sobota R, Singh S, Ghodke S, Choi S, Kubo N, Adachi M, Yamamoto Y, Matsunami M, Takeuchi T 2020 J. Electron. Mater. 49 2855 Google Scholar
[27]	Chen H Y, Shi X, Chen L D, Chou P F 2019 J. Inorg. Mater. 34 1041
[28]	Kim J H, Oh S, Sohn W H, Rhyee J S, Park S D, Kang H, Ahn D 2015 Acta Mater. 100 32 Google Scholar
[29]	Tak J Y, Nam W H, Lee C, Kim S, Lim Y S, Ko K, Lee S, Seo W S, Cho H K, Shim J H, Park C H 2018 Chem. Mat. 30 3276 Google Scholar
[30]	Liu W, Shi X, Hong M, Yang L, Moshwan R, Chen Z G, Zou J 2018 J. Mater. Chem. C 6 13225
[31]	Sun Y, Xi L, Yang J, Wu L, Shi X, Chen L, Snyder J, Yang J, Zhang W 2017 J. Mater. Chem. A 5 5098 Google Scholar
[32]	Olvera A A, Moroz N A, Sahoo P, Ren P, Bailey T P, Page A A, Uher C, Poudeu P F P 2017 Energy & Environ. Sci. 10 1668
[33]	R. D. Heyding 1966 Can. J. Chem. 44 1233 Google Scholar
[34]	Namsani S, Auluck S, Singh J K 2017 Appl. Phys. Lett. 111 163903 Google Scholar
[35]	Eikeland E, Blichfeld A B, Borup K A, Zhao K, Overgaard J, Shi X, Chen L, Iversen B B 2017 Iucrj 4 476 Google Scholar
[36]	Bailey T P, Hui S, Xie H, Olvera A, Poudeu P F P, Tang X, Uher C 2016 J. Mater. Chem. A 4 17225 Google Scholar
[37]	Yang L, Chen Z G, Han G, Hong M, Zou Y, Zou J 2015 Nano Energy 16 367 Google Scholar
[38]	Kim H, Ballikaya S, Chi H, Ahn J P, Ahn K, Uher C, Kaviany M 2015 Acta Mater. 86 247 Google Scholar
[39]	Ballikaya S, Chi H, Salvador J R, Uher C 2013 J. Mater. Chem. A 1 12478 Google Scholar
[40]	Lin Z, Hollar C, Kang J S, Yin A, Wang Y, Shiu H Y, Huang Y, Hu Y, Zhang Y, Duan X 2017 Adv. Mater. 29 1606662 Google Scholar
[41]	Ghosh A, Kulsi C, Banerjee D, Mondal A 2016 Appl. Surf. Sci. 369 525 Google Scholar
[42]	Liu T C, Hu Y, Chang W B 2014 Mater. Sci. Eng. B 180 33 Google Scholar
[43]	Rajesh D, Chandrakanth R R, Sunandana 2013 J. Apple. Phys. 4 65
[44]	Mansour B A, Zawawi I K E L, Elsayed A H E, Hameed T A 2018 J. Alloy. Comp. 740 1125 Google Scholar
[45]	Emslie A G, Bonner F T, Peck L G 1958 J. Appl. Phys. 29 858 Google Scholar
[46]	王东, 刘红缨, 贺军辉, 刘林林 2012 影像科学与光化学 30 91 Google Scholar Wang D, Liu H Y, He J H, Liu L L, 2012 Imaging Sci. Photochem. 30 91 Google Scholar
[47]	Mitzi D B, Kosbar L L, Murray C E, Copel M, Afzali A 2004 Nature 428 299 Google Scholar
[48]	Mitzi D B, Copel M, Murray C E 2006 Adv. Mater. 18 2448 Google Scholar
[49]	Sheng J, Han K L, Hong T, Choi W H, Park J S 2018 J. Semicond. 39 011008 Google Scholar
[50]	Mihi A, Ocana M, Miguez H 2006 Adv. Mater. 18 2244 Google Scholar
[51]	Zhang T, Yao G, Pan T, Lu Q 2020 J. Semicond. 41 041602 Google Scholar
[52]	Lee H, Lee B P, Messersmith P B 2007 Nature 448 338 Google Scholar
[53]	Lee J H, Oh J Y, Kim D M 1999 J. Mater. Sci.-Mater. Med. 10 629 Google Scholar
[54]	Scimeca M R, Yang F, Zaia E, Chen N, Zhao P, Gordon M P, Forster J D, Liu Y S, Guo J, Urban J J, Sahu A 2019 ACS Appl. Energy Mater. 2 1517 Google Scholar
[55]	Day T W, Weldert K S, Zeier W G, Chen B R, Moffitt S L, Weis U, Jochum K P, Panthoefer M, Bedzyk M J, Snyder G J, Tremel W 2015 Chem. Mater. 27 7018 Google Scholar
[56]	Zeng Y, Liang G, Fan P, Xie Y, Fan B, Hu J, Zheng Z, Zhang X, Luo J, Zhang D 2017 J. Mater. Sci.-Mater. Electron. 28 13763 Google Scholar
[57]	Shen S, Zhu W, Deng Y, Zhao H, Peng Y, Wang C 2017 Appl. Surf. Sci. 414 197 Google Scholar
[58]	Kim H J, Kim K C, Choi W C, Kim J S, Kim Y H, Kim S I, Park C 2012 J. Nanosci. Nanotechnol. 12 3629 Google Scholar
[59]	Yuan D, Zhi Wei Z 2015 J. Inorg. Mater. 30 1 Google Scholar
[60]	Perez Taborda J A, Vera L, Caballero Calero O, Lopez E O, Romero J J, Stroppa D G, Briones F, Martin Gonzalez M 2017 Adv. Mater. Technol. 2 7
[61]	Lv Y H, Chen J K, Doebeli M, Li Y L, Shi X, Chen L D 2015 J. Inorg. Mater. 30 1115 Google Scholar
[62]	Yang L, Wei J, Ma Z, Song P, Ma J, Zhao Y, Huang Z, Zhang M, Yang F, Wang X 2019 Nanomaterials 9 12
[63]	Liu H, Yuan X, Lu P, Shi X, Xu F, He Y, Tang Y, Bai S, Zhang W, Chen L, Lin Y, Shi L, Lin H, Gao X, Zhang X, Chi H, Uher C 2013 Adv. Mater. 25 6607 Google Scholar
[64]	Hu Q, Zhu Z, Zhang Y, Li X J, Song H, Zhang Y 2018 J. Mater. Chem. A 6 23417 Google Scholar
[65]	Zhong B, Zhang Y, Li W, Chen Z, Cui J, Li W, Xie Y, Hao Q, He Q 2014 Appl. Phys. Lett. 105 123902 Google Scholar
[66]	Cui J, Liu X, Zhang X, Li Y, Deng Y 2011 J. Appl. Phys. 110 023708 Google Scholar
[67]	Boukai A I, Bunimovich Y, Tahir Kheli J, Yu J K, Goddard W A, 3 rd, Heath J R 2008 Nature 451 168 Google Scholar
[68]	Bhuse V M, Hankare P P, Garadkar K M, Khomane A S 2003 Mater. Chem. Phys. 80 82 Google Scholar
[69]	Pathan H M, Lokhande C D, Amalnerkar D P, Seth T 2003 Appl. Surf. Sci. 211 48 Google Scholar
[70]	Dhanam M, Manoj P K, Prabhu R R 2005 J. Cryst. Growth 280 425 Google Scholar
[71]	Hu Y, Afzaal M, Malik M A, O’Brien P 2006 J. Cryst. Growth 297 61 Google Scholar
[72]	Hiramatsu H, Koizumi I, Kim K B, Yanagi H, Kamiya T, Hirano M, Matsunami N, Hosono H 2008 J. Appl. Phys. 104 113723 Google Scholar
[73]	Yang M, Shen Z, Liu X, Wang W 2016 J. Electron. Mater. 45 1974 Google Scholar
[74]	Romero J J, Perez Taborda J A, Briones F, Martín González M S 2016 12^th European Conference on Thermoelectrics, Madrid, Spain, September 24–26, 2014
[75]	Liu K, Jing M, Zhang L, Li J, Shi L 2018 Integr. Ferroelectr. 189 71 Google Scholar
[76]	Forster J D, Lynch J J, Coates N E, Liu J, Jang H, Zaia E, Gordon M P, Szybowski M, Sahu A, Cahill D G, Urban J J 2017 Sci. Rep. 7 2765 Google Scholar
[77]	Lu Y, Ding Y, Qiu Y, Cai K, Yao Q, Song H, Tong L, He J, Chen L 2019 ACS Appl. Mater. Interfaces 11 12819 Google Scholar
[78]	邓元, 张义政, 王瑶, 高洪利 2014 航空学报 35 2733 Deng Y, Zhang Y Z, Wang Y, Gao H L 2014 Acta Aeronaut. Astronaut. Sin. 35 2733
[79]	Jin Q, Jiang S, Zhao Y, Wang D, Qiu J, Tang D M, Tan J, Sun D M, Hou P X, Chen X Q, Tai K, Gao N, Liu C, Cheng H M, Jiang X 2019 Nat. Mater. 18 62 Google Scholar
[80]	Bahk J H, Fang H, Yazawa K, Shakouri A 2015 J. Mater. Chem. C 3 10362 Google Scholar
[81]	Liu X, Long Y Z, Liao L, Duan X, Fan Z 2012 ACS Nano 6 1888 Google Scholar
[82]	Lu Y, Qiu Y, Jiang Q, Cai K, Du Y, Song H, Gao M, Huang C, He J, Hu D 2018 ACS Appl. Mater. Interfaces 10 42310 Google Scholar
[83]	Du Y, Shen S Z, Cai K, Casey P S 2012 Prog. Polym. Sci. 37 820 Google Scholar
[84]	Fan Z, Razavi H, Do J W, Moriwaki A, Ergen O, Chueh Y L, Leu P W, Ho J C, Takahashi T, Reichertz L A, Neale S, Yu K, Wu M, Ager J W, Javey A 2009 Nat. Mater. 8 648 Google Scholar
[85]	He Y, Wang X, Gao Y, Hou Y, Wan Q 2018 J. Semicond. 39 011005 Google Scholar
[86]	Lu Y, Qiu Y, Cai K, Ding Y, Wang M, Jiang C, Yao Q, Huang C, Chen L, He J 2020 Energy. Environ. Sci. 13 1240 Google Scholar
[87]	Zhao K, Blichfeld A B, Chen H, Song Q, Zhang T, Zhu C, Ren D, Hanus R, Qiu P, Iversen B B, Xu F, Snyder G J, Shi X, Chen L 2017 Chem. Mat. 29 6367 Google Scholar
[88]	Finefrock S W, Zhu X, Sun Y, Wu Y 2015 Nanoscale 7 5598 Google Scholar
[89]	Im H, Moon H G, Lee J S, Chung I Y, Kang T J, Kim Y H 2015 Nano Res. 7 443
[90]	Kim S J, Lee H E, Choi H, Kim Y, We J H, Shin J S, Lee K J, Cho B J 2016 ACS Nano 10 10851 Google Scholar

Cited By

图 1 Cu₂Se高温β相晶体结构^[34]　(a)在8c和32f间隙位置显示有铜原子的晶胞; (b)沿着立方[$1\bar{1} 0$]方向的晶体结构的投影平面表示

Figure 1. Cu₂Se high temperature β- phase crystal structure^[34] (a) Unit cell where the 8c and 32f interstitial positions are shown with Cu atoms; (b) projected plane representation of the crystal structure along the cubic [$1\bar{1} 0$] direction.

DownLoad: Full-Size Img PowerPoint

图 2 (a)电镀沉积生长机制示意图; (b) Cu₂Se薄膜的XRD图案; (c) Cu₂Se薄膜的场发射扫描电子显微镜(FESEM)图像; (d) ITO基板上Cu₂Se薄膜的AFM 3D图像^[41]

Figure 2. (a) Schematic diagram of Galvanic Deposition mechanism; (b) XRD pattern of Cu₂Se thin film; (c) FESEM image of Cu₂Se thin film; (d) AFM 3D image of Cu₂Se film on ITO substrate^[41].

DownLoad: Full-Size Img PowerPoint

图 3 (a)溶解在硫醇胺中的Cu_2–xSe溶液; (b) 旋涂和退火后, 玻璃上的Cu₂Se薄膜; (c) (d) Cu_2–xSe薄膜样品浸泡前的SEM图像; (d) Cu_2–xSe薄膜样品浸泡后的SEM图像; (e) 旋涂制备的Cu_2–xSe样品的XRD图谱^[54]

Figure 3. (a) Cu_2–x Se solution dissolved in thiolamine; (b) after spin coating and annealing, the Cu₂Se film on the glass; (c) SEM image of Cu_2–xSe thin film sample before soaking; (d) SEM image of Cu_2–xSe thin film sample after soaking; (e) XRD pattern of Cu_2–xSe sample prepared by spin coating^[54].

DownLoad: Full-Size Img PowerPoint

图 4 (a) Al₂O₃基板上沉积的Cu₂Se薄膜的照片; (b) 在573 K下退火的薄膜能量色散X射线光谱(EDS); (c) Al₂O₃基材上薄膜的横截面SEM分析; (d) 薄膜中纳米晶体的TEM分析, 其中虚线突出了晶界, 插图是TEM图像的相应FFT^[40]

Figure 4. (a) Photograph of Cu₂Se thin film deposited on Al₂O₃ substrate; (b) energy dispersive X-ray spectroscopy (EDS) of thin film annealed at 573 K; (c) cross-sectional SEM analysis of thin film on Al₂O₃ substrate; (d) TEM analysis of nanocrystals in the thin film, the dotted line highlights the grain boundaries, the inset is the corresponding FFT of the TEM image.^[40]

DownLoad: Full-Size Img PowerPoint

图 5 (a) 脉冲混合反应磁控溅射(PHRMS)沉积系统; (b) 从标称成分分别为Cu/Se = 1, 2, 2.4, 3.6, 5和9的薄膜上获得的掠入射同步辐射X射线衍射图^[60]

Figure 5. (a) Pulse hybrid reactive magnetron sputtering (PHRMS) deposition system; (b) grazing incident synchrotron radiation X Ray diffraction pattern obtained from a film with a nominal composition of Cu/Se = 1, 2, 2.4, 3.6, 5 and 9^[60].

DownLoad: Full-Size Img PowerPoint

图 6 具有不同铜/硒比的薄膜的SEM图像^[60]　(a) Cu/Se = 1; (b) Cu/Se = 2; (c) Cu/Se = 2.4; (d) Cu/Se = 3.6; (e) Cu/Se = 5; (f) Cu/Se = 9

Figure 6. SEM images of films with different copper/selenium ratios^[60] (a) Cu/Se = 1; (b) Cu/Se = 2; (c) Cu/Se = 2.4; (d) Cu/Se = 3.6; (e) Cu/Se = 5; (f) Cu/Se = 9.

DownLoad: Full-Size Img PowerPoint

图 7 (a)由各种Cu_2+xSe靶沉积的Cu_2–ySe膜中的XRD图案; (b) 根据布拉格定律计算的(001)面的晶面晶体间距(c); (c) Cu₂Se膜的截面HRTEM图像; (d) (e)不同Cu_2–xSe靶沉积的Cu_2–ySe膜的FESEM图像, (d) x = 0.1, (d) x = 0.3 ^[10]

Figure 7. (a) XRD patterns in Cu_2–y Se films deposited from various Cu_2+x Se targets; (b) (001) plane crystal spacing (c) calculated according to Bragg's law; (c) HRTEM image of the cross-section of Cu₂Se film; (d)(e) FESEM images of Cu_2–ySe films deposited on different Cu_2–x Se targets, (d) x = 0.1, (e) x = 0.3 ^[10]

DownLoad: Full-Size Img PowerPoint

图 8 (a)在不同温度下退火的Cu₂Se薄膜中的室温载流子浓度; (b)电导率对薄膜中载流子浓度的依赖性; (c)塞贝克系数对薄膜中载流子浓度的依赖性; (d) (e) 柔性塑料基板上Cu₂Se薄膜的热电性能; (f)沉积在聚酰亚胺基板上的薄膜的电导率σ, (g)塞贝克系数S, (h) 功率因数PF = σS² ^[40]

Figure 8. (a) Room temperature carrier concentration in Cu₂Se thin films annealed at different temperatures; (b) dependence of conductivity on carrier concentration in thin films; (c) dependence of Seebeck coefficient on carrier concentration in film; (d)(e) thermoelectric properties of Cu₂Se film on flexible plastic substrate, (f) conductivity σ of the film deposited on polyimide substrate, (g) Seebeck coefficient S, (h) power factor PF = σS² ^[40].

DownLoad: Full-Size Img PowerPoint

图 9 (a) Cu₂Se/PEDOT: PSS复合膜的输出电压与温度梯度的关系; (b) 在不同温差下的输出电压和功率与电流的关系; (c) 设备的数码照片; (d) 由于手臂和周围环境之间的温差而产生的4.5 mV电压的照片; (e) 将茶水倒入500 mL烧杯中直至液位到达设备下边缘时产生的15.4 mV电压的照片, d部分和e部分的插图是红外热像图^[77]

Figure 9. (a) Cu₂Se/PEDOT: Relationship between the output voltage of the PSS composite film and the temperature gradient; (b) relationship between output voltage and power and current under different temperature differences; (c) digital photos of the device; (d) photo of the 4.5 mV voltage generated due to the temperature difference between the arm and the surrounding environment; (e) pour the tea water into a 500 mL beaker until the liquid level reaches the bottom edge of the device at 15.4 mV voltage, where Illustrations in the (d) and (e) parts are infrared thermal images^[77]

DownLoad: Full-Size Img PowerPoint

表 1 近年来Cu₂Se薄膜热电性能研究进展

Table 1. Research progress of Cu₂Se thin film thermoelectric properties in recent years.

Methods	Film	Cu/Se	Crystallite size/mm	S/μV·K^–1	σ/ ×10³ S/m	κ/ W·(m·K)^–1	PF/ mW·(m·K²) ^–1	ZT	Ref.
Chemical deposition	600	1.8	38		18				[68]
	330	2.125			1				[69]
	403	1.96	37.039		17.8				[70]
	1700	1.81			8.13 × 10³				[71]
Pulsed laser deposition	40	1.7	< 10		450				[72]
	234			57	130		619		[10]
				60	10		350		[61]
Electrochemial deposition	90—100	1.92—1.89			0.14—0.22				[42]
		1.78	40—50	80	27	0.77	173	0.07	[41]
		2.191	34	56			130		[73]
Sputtering deposition		1—3	1000	10—100	100				[74]
		3—10	100	> 100	1
	48—131	1.777		37.3	1.4—4.9				[5]
	600—850	1—9	25—84	100	100	0.8 ± 0.1	110	0.4	[60]
Spin coating process			300—500		44.603				[75]
	62.6	1.9—1.995		200—250	25	0.62	653	0.34	[54]
	50—100			80	100	0.4—1.4		0.14	[76]
	55	1.79 ± 0.06	10			1.3—1.5	620		[40]
Simple mechanical pressing	10000—50000	1.743		14.3	557.82	0.79	111.84	0.04	[9]
Wet-chemical process	8000	1.98		50.8	104.7	0.25—0.3	270.3	0.3	[77]

DownLoad: CSV

[1]	Lu P, Liu H, Yuan X, Xu F, Shi X, Zhao K, Qiu W, Zhang W, Chen L 2015 J. Mater. Chem. A 3 6901 Google Scholar
[2]	Hussain R A, Hussain I 2020 Solid State Sci. 100 106101 Google Scholar
[3]	Malekar V P, Gangawane S A, Fulari V J 2020 Mater. Today Proc. 23 202 Google Scholar
[4]	Sharma K, Sharma D K, Kumar V 2020 Optik 206 164376 Google Scholar
[5]	Li Y, Fan P, Zheng Z, Luo J, Liang G, Guo S 2016 J. Alloy. Compd. 658 880 Google Scholar
[6]	Wei J J, Yang L L, Ma Z, Song P S, Zhang M L, Ma J, Yang F H, Wang X D 2020 J. Mater. Sci. 55 12642 Google Scholar
[7]	Biswas K, He J, Blum I D, Wu C I, Hogan T P, Seidman D N, Dravid V P, Kanatzidis M G 2012 Nature 489 414 Google Scholar
[8]	Harman T C, Taylor P J, Walsh M P, LaForge B E 2002 Science 297 2229 Google Scholar
[9]	Pammi S V N, Jella V, Choi J S, Yoon S G 2017 J. Mater. Chem. C 5 763 Google Scholar
[10]	Lv Y, Chen J, Zheng R K, Shi X, Song J, Zhang T, Li X, Chen L 2015 Ceram. Int. 41 7439 Google Scholar
[11]	Ma Z, Liu Y, Deng L, Zhang M, Zhang S, Ma J, Song P, Liu Q, Ji A, Yang F, Wang X 2018 Nanomaterials 8 77 Google Scholar
[12]	Chen X, Dai W, Wu T, Luo W, Yang J, Jiang W, Wang L 2018 Coatings 8 244 Google Scholar
[13]	Hicks L D, Dresselhaus M S 1993 Phys. Rev. B Condens Matter 47 12727 Google Scholar
[14]	Dresselhaus M S, Dresselhaus G, Sun X, Zhang Z, Cronin S B, Koga T 1999 Phys. Solid State 41 679 Google Scholar
[15]	Venkatasubramanian R, Siivola E, Colpitts T, O'Quinn B J N 2001 Nature 413 597 Google Scholar
[16]	Zhou Y, Matsubara I, Shin W, Izu N, Murayama N 2004 J. Appl. Phys. 95 625 Google Scholar
[17]	Hochbaum A I, Chen R, Delgado R D, Liang W, Garnett E C, Najarian M, Majumdar A, Yang P 2008 Nature 451 163 Google Scholar
[18]	Zheng X J, Zhu L, Zhou Y H, Zhang Q 2005 Appl. Phys. Lett. 87 2229
[19]	Mehdizadeh D A, Zebarjadi M, He J, Tritt T M 2015 Mater. Sci. Eng. R 97 1 Google Scholar
[20]	Hinterleitner B, Knapp I, Poneder M, Shi Y, Müller H, Eguchi G, Eisenmenger S C, Stöger P M, Kakefuda Y, Kawamoto N, Guo Q, Baba T, Mori T, Ullah S, Chen X Q, Bauer E 2019 Nature 576 85 Google Scholar
[21]	Wang C, Xia K, Wang H, Liang X, Yin Z, Zhang Y 2019 Adv. Mater. 31 1801072 Google Scholar
[22]	Zhao W Y, Zhang Q J, Sun Z G, Zhu W T, Wei P, Fang W B, Tian Y, Nie X L, Li P 2019 J. Inorg. Mater. 34 6
[23]	Gahtori B, Bathula S, Tyagi K, Jayasimhadri M, Srivastava A K, Singh S, Budhani R C, Dhar A 2015 Nano Energy 13 36 Google Scholar
[24]	Zhao K, Liu K, Yue Z, Wang Y, Song Q, Li J, Guan M, Xu Q, Qiu P, Zhu H, Chen L, Shi X 2019 Adv. Mater. 190 3480
[25]	Byeon D, Sobota R, Delime Codrin K, Choi S, Hirata K, Adachi M, Kiyama M, Matsuura T, Yamamoto Y, Matsunami M, Takeuchi T 2019 Nat. Commun. 10 72 Google Scholar
[26]	Byeon D, Sobota R, Singh S, Ghodke S, Choi S, Kubo N, Adachi M, Yamamoto Y, Matsunami M, Takeuchi T 2020 J. Electron. Mater. 49 2855 Google Scholar
[27]	Chen H Y, Shi X, Chen L D, Chou P F 2019 J. Inorg. Mater. 34 1041
[28]	Kim J H, Oh S, Sohn W H, Rhyee J S, Park S D, Kang H, Ahn D 2015 Acta Mater. 100 32 Google Scholar
[29]	Tak J Y, Nam W H, Lee C, Kim S, Lim Y S, Ko K, Lee S, Seo W S, Cho H K, Shim J H, Park C H 2018 Chem. Mat. 30 3276 Google Scholar
[30]	Liu W, Shi X, Hong M, Yang L, Moshwan R, Chen Z G, Zou J 2018 J. Mater. Chem. C 6 13225
[31]	Sun Y, Xi L, Yang J, Wu L, Shi X, Chen L, Snyder J, Yang J, Zhang W 2017 J. Mater. Chem. A 5 5098 Google Scholar
[32]	Olvera A A, Moroz N A, Sahoo P, Ren P, Bailey T P, Page A A, Uher C, Poudeu P F P 2017 Energy & Environ. Sci. 10 1668
[33]	R. D. Heyding 1966 Can. J. Chem. 44 1233 Google Scholar
[34]	Namsani S, Auluck S, Singh J K 2017 Appl. Phys. Lett. 111 163903 Google Scholar
[35]	Eikeland E, Blichfeld A B, Borup K A, Zhao K, Overgaard J, Shi X, Chen L, Iversen B B 2017 Iucrj 4 476 Google Scholar
[36]	Bailey T P, Hui S, Xie H, Olvera A, Poudeu P F P, Tang X, Uher C 2016 J. Mater. Chem. A 4 17225 Google Scholar
[37]	Yang L, Chen Z G, Han G, Hong M, Zou Y, Zou J 2015 Nano Energy 16 367 Google Scholar
[38]	Kim H, Ballikaya S, Chi H, Ahn J P, Ahn K, Uher C, Kaviany M 2015 Acta Mater. 86 247 Google Scholar
[39]	Ballikaya S, Chi H, Salvador J R, Uher C 2013 J. Mater. Chem. A 1 12478 Google Scholar
[40]	Lin Z, Hollar C, Kang J S, Yin A, Wang Y, Shiu H Y, Huang Y, Hu Y, Zhang Y, Duan X 2017 Adv. Mater. 29 1606662 Google Scholar
[41]	Ghosh A, Kulsi C, Banerjee D, Mondal A 2016 Appl. Surf. Sci. 369 525 Google Scholar
[42]	Liu T C, Hu Y, Chang W B 2014 Mater. Sci. Eng. B 180 33 Google Scholar
[43]	Rajesh D, Chandrakanth R R, Sunandana 2013 J. Apple. Phys. 4 65
[44]	Mansour B A, Zawawi I K E L, Elsayed A H E, Hameed T A 2018 J. Alloy. Comp. 740 1125 Google Scholar
[45]	Emslie A G, Bonner F T, Peck L G 1958 J. Appl. Phys. 29 858 Google Scholar
[46]	王东, 刘红缨, 贺军辉, 刘林林 2012 影像科学与光化学 30 91 Google Scholar Wang D, Liu H Y, He J H, Liu L L, 2012 Imaging Sci. Photochem. 30 91 Google Scholar
[47]	Mitzi D B, Kosbar L L, Murray C E, Copel M, Afzali A 2004 Nature 428 299 Google Scholar
[48]	Mitzi D B, Copel M, Murray C E 2006 Adv. Mater. 18 2448 Google Scholar
[49]	Sheng J, Han K L, Hong T, Choi W H, Park J S 2018 J. Semicond. 39 011008 Google Scholar
[50]	Mihi A, Ocana M, Miguez H 2006 Adv. Mater. 18 2244 Google Scholar
[51]	Zhang T, Yao G, Pan T, Lu Q 2020 J. Semicond. 41 041602 Google Scholar
[52]	Lee H, Lee B P, Messersmith P B 2007 Nature 448 338 Google Scholar
[53]	Lee J H, Oh J Y, Kim D M 1999 J. Mater. Sci.-Mater. Med. 10 629 Google Scholar
[54]	Scimeca M R, Yang F, Zaia E, Chen N, Zhao P, Gordon M P, Forster J D, Liu Y S, Guo J, Urban J J, Sahu A 2019 ACS Appl. Energy Mater. 2 1517 Google Scholar
[55]	Day T W, Weldert K S, Zeier W G, Chen B R, Moffitt S L, Weis U, Jochum K P, Panthoefer M, Bedzyk M J, Snyder G J, Tremel W 2015 Chem. Mater. 27 7018 Google Scholar
[56]	Zeng Y, Liang G, Fan P, Xie Y, Fan B, Hu J, Zheng Z, Zhang X, Luo J, Zhang D 2017 J. Mater. Sci.-Mater. Electron. 28 13763 Google Scholar
[57]	Shen S, Zhu W, Deng Y, Zhao H, Peng Y, Wang C 2017 Appl. Surf. Sci. 414 197 Google Scholar
[58]	Kim H J, Kim K C, Choi W C, Kim J S, Kim Y H, Kim S I, Park C 2012 J. Nanosci. Nanotechnol. 12 3629 Google Scholar
[59]	Yuan D, Zhi Wei Z 2015 J. Inorg. Mater. 30 1 Google Scholar
[60]	Perez Taborda J A, Vera L, Caballero Calero O, Lopez E O, Romero J J, Stroppa D G, Briones F, Martin Gonzalez M 2017 Adv. Mater. Technol. 2 7
[61]	Lv Y H, Chen J K, Doebeli M, Li Y L, Shi X, Chen L D 2015 J. Inorg. Mater. 30 1115 Google Scholar
[62]	Yang L, Wei J, Ma Z, Song P, Ma J, Zhao Y, Huang Z, Zhang M, Yang F, Wang X 2019 Nanomaterials 9 12
[63]	Liu H, Yuan X, Lu P, Shi X, Xu F, He Y, Tang Y, Bai S, Zhang W, Chen L, Lin Y, Shi L, Lin H, Gao X, Zhang X, Chi H, Uher C 2013 Adv. Mater. 25 6607 Google Scholar
[64]	Hu Q, Zhu Z, Zhang Y, Li X J, Song H, Zhang Y 2018 J. Mater. Chem. A 6 23417 Google Scholar
[65]	Zhong B, Zhang Y, Li W, Chen Z, Cui J, Li W, Xie Y, Hao Q, He Q 2014 Appl. Phys. Lett. 105 123902 Google Scholar
[66]	Cui J, Liu X, Zhang X, Li Y, Deng Y 2011 J. Appl. Phys. 110 023708 Google Scholar
[67]	Boukai A I, Bunimovich Y, Tahir Kheli J, Yu J K, Goddard W A, 3 rd, Heath J R 2008 Nature 451 168 Google Scholar
[68]	Bhuse V M, Hankare P P, Garadkar K M, Khomane A S 2003 Mater. Chem. Phys. 80 82 Google Scholar
[69]	Pathan H M, Lokhande C D, Amalnerkar D P, Seth T 2003 Appl. Surf. Sci. 211 48 Google Scholar
[70]	Dhanam M, Manoj P K, Prabhu R R 2005 J. Cryst. Growth 280 425 Google Scholar
[71]	Hu Y, Afzaal M, Malik M A, O’Brien P 2006 J. Cryst. Growth 297 61 Google Scholar
[72]	Hiramatsu H, Koizumi I, Kim K B, Yanagi H, Kamiya T, Hirano M, Matsunami N, Hosono H 2008 J. Appl. Phys. 104 113723 Google Scholar
[73]	Yang M, Shen Z, Liu X, Wang W 2016 J. Electron. Mater. 45 1974 Google Scholar
[74]	Romero J J, Perez Taborda J A, Briones F, Martín González M S 2016 12^th European Conference on Thermoelectrics, Madrid, Spain, September 24–26, 2014
[75]	Liu K, Jing M, Zhang L, Li J, Shi L 2018 Integr. Ferroelectr. 189 71 Google Scholar
[76]	Forster J D, Lynch J J, Coates N E, Liu J, Jang H, Zaia E, Gordon M P, Szybowski M, Sahu A, Cahill D G, Urban J J 2017 Sci. Rep. 7 2765 Google Scholar
[77]	Lu Y, Ding Y, Qiu Y, Cai K, Yao Q, Song H, Tong L, He J, Chen L 2019 ACS Appl. Mater. Interfaces 11 12819 Google Scholar
[78]	邓元, 张义政, 王瑶, 高洪利 2014 航空学报 35 2733 Deng Y, Zhang Y Z, Wang Y, Gao H L 2014 Acta Aeronaut. Astronaut. Sin. 35 2733
[79]	Jin Q, Jiang S, Zhao Y, Wang D, Qiu J, Tang D M, Tan J, Sun D M, Hou P X, Chen X Q, Tai K, Gao N, Liu C, Cheng H M, Jiang X 2019 Nat. Mater. 18 62 Google Scholar
[80]	Bahk J H, Fang H, Yazawa K, Shakouri A 2015 J. Mater. Chem. C 3 10362 Google Scholar
[81]	Liu X, Long Y Z, Liao L, Duan X, Fan Z 2012 ACS Nano 6 1888 Google Scholar
[82]	Lu Y, Qiu Y, Jiang Q, Cai K, Du Y, Song H, Gao M, Huang C, He J, Hu D 2018 ACS Appl. Mater. Interfaces 10 42310 Google Scholar
[83]	Du Y, Shen S Z, Cai K, Casey P S 2012 Prog. Polym. Sci. 37 820 Google Scholar
[84]	Fan Z, Razavi H, Do J W, Moriwaki A, Ergen O, Chueh Y L, Leu P W, Ho J C, Takahashi T, Reichertz L A, Neale S, Yu K, Wu M, Ager J W, Javey A 2009 Nat. Mater. 8 648 Google Scholar
[85]	He Y, Wang X, Gao Y, Hou Y, Wan Q 2018 J. Semicond. 39 011005 Google Scholar
[86]	Lu Y, Qiu Y, Cai K, Ding Y, Wang M, Jiang C, Yao Q, Huang C, Chen L, He J 2020 Energy. Environ. Sci. 13 1240 Google Scholar
[87]	Zhao K, Blichfeld A B, Chen H, Song Q, Zhang T, Zhu C, Ren D, Hanus R, Qiu P, Iversen B B, Xu F, Snyder G J, Shi X, Chen L 2017 Chem. Mat. 29 6367 Google Scholar
[88]	Finefrock S W, Zhu X, Sun Y, Wu Y 2015 Nanoscale 7 5598 Google Scholar
[89]	Im H, Moon H G, Lee J S, Chung I Y, Kang T J, Kim Y H 2015 Nano Res. 7 443
[90]	Kim S J, Lee H E, Choi H, Kim Y, We J H, Shin J S, Lee K J, Cho B J 2016 ACS Nano 10 10851 Google Scholar

[1]	Yang Shi-Guan, Lin Xin, He Jun-Song, Zhai Li-Jun, Cheng Lin, Lü Ming Hao, Liu Hong-Xia, Zhang Yan, Sun Zhi-Gang. Study of parallel models for thermoelectric properties of double-layer thermoelectric thin films. Acta Physica Sinica, 2023, 72(22): 228401. doi: 10.7498/aps.72.20231259
[2]	Zheng Jian-Jun, Zhang Li-Ping. Monolayer Cu₂X (X=S, Se): excellent thermoelectric material with low lattice thermal conductivity. Acta Physica Sinica, 2023, 0(0): 0-0. doi: 10.7498/aps.72.20220015
[3]	Zheng Jian-Jun, Zhang Li-Ping. Thermoelectric properties of monolayer Cu₂X. Acta Physica Sinica, 2023, 72(8): 086301. doi: 10.7498/aps.72.20222015
[4]	Ma Yun-Peng, Zhuang Hua-Lu, Li Jing-Feng, Li Qian. Strain-enhanced thermoelectric properties of Nb-doped SrTiO₃ thin films. Acta Physica Sinica, 2023, 72(9): 096803. doi: 10.7498/aps.72.20222301
[5]	Chen Shang-Feng, Sun Nai-Kun, Zhang Xian-Min, Wang Kai, Li Wu, Han Yan, Wu Li-Jun, Dai Qin. Preparation and thermoelectric properties of Mn₃As₂-doped Cd₃As₂ nanostructures. Acta Physica Sinica, 2022, 71(18): 187201. doi: 10.7498/aps.71.20220584
[6]	Xu Jing, He Zi-Min, Yang Wen-Long, Wu Rong, Lai Xiao-Fang, Jian Ji-Kang. Preparation and thermoelectric properties of layered Bi_1–xSb_xSe nanocrystalline films. Acta Physica Sinica, 2022, 71(19): 197301. doi: 10.7498/aps.71.20220834
[7]	Nie Xiao-Lei, Yu Hao-Cheng, Zhu Wan-Ting, Sang Xia-Han, Wei Ping, Zhao Wen-Yu. Design, fabrication and performance evaluation of graphene/Bi_0.5Sb_1.5Te₃ flexible thermoelectric films and in-plane heat dissipation devices. Acta Physica Sinica, 2022, 71(15): 157301. doi: 10.7498/aps.71.20220358
[8]	Chen Yun-Fei, Wei Feng, Wang He, Zhao Wei-Yun, Deng Yuan. Structural control for high performance Bi₂Te_3–xSe_x thermoelectric thin films. Acta Physica Sinica, 2021, 70(20): 207303. doi: 10.7498/aps.70.20211090
[9]	Zou Ping, Lü Dan, Xu Gui-Ying. Microstructure and thermoelectric property of (Bi_1–xTb_x)₂(Te_0.9Se_0.1)₃ fabricated by high pressure sintering technique. Acta Physica Sinica, 2020, 69(5): 057201. doi: 10.7498/aps.69.20191561
[10]	Wang Jiao, Liu Shao-Hui, Zhou Meng, Hao Hao-Shan. Effects of ascorbic acid post-treatment on thermoelectric properties of poly (3, 4-ethylenedioxythiophene) thin films by a vapor phase polymerization. Acta Physica Sinica, 2020, 69(14): 147201. doi: 10.7498/aps.69.20200431
[11]	Zhang Hua, Chen Shao-Ping, Long Yang, Fan Wen-Hao, Wang Wen-Xian, Meng Qing-Sen. Thermoelectric transport mechanism of Mg2Si0.4Sn0.6-yBiy prepared by low-temperature microwave reaction. Acta Physica Sinica, 2015, 64(24): 247302. doi: 10.7498/aps.64.247302
[12]	Liu Ran, Gao Lin-Jie, Li Long-Jiang, Zhai Sheng-Jun, Wang Jiang-Long, Fu Guang-Sheng, Wang Shu-Fang. High temperature thermoelectric performance of Ca2+ doped CdO ceramics. Acta Physica Sinica, 2015, 64(21): 218101. doi: 10.7498/aps.64.218101
[13]	Huo Feng-Ping, Wu Rong-Gui, Xu Gui-Ying, Niu Si-Tong. Thermoelectric properties of (AgSbTe2)100-x (GeTe)x fabricated by hot pressing method. Acta Physica Sinica, 2012, 61(8): 087202. doi: 10.7498/aps.61.087202
[14]	Tang Xin-Feng, Du Bao-Li, Xu Jing-Jing, Yan Yong-Gao. Synthesis and thermoelectric properties of nonstoichiometric AgSbTe2+ x compounds. Acta Physica Sinica, 2011, 60(1): 018403. doi: 10.7498/aps.60.018403
[15]	Fan Ping, Cai Zhao-Kun, Zheng Zhuang-Hao, Zhang Dong-Ping, Cai Xing-Min, Chen Tian-Bao. Fabrication and characterization of Bi-Sb-Te based thin film thermoelectric generator prepared by ion beam sputtering deposition. Acta Physica Sinica, 2011, 60(9): 098402. doi: 10.7498/aps.60.098402
[16]	Fan Ping, Zheng Zhuang-Hao, Liang Guang-Xing, Zhang Dong-Ping, Cai Xing-Min. Preparation and characterization of Sb2Te3 thermoelectric thin films by ion beam sputtering. Acta Physica Sinica, 2010, 59(2): 1243-1247. doi: 10.7498/aps.59.1243
[17]	Xiong Fei, Zhang Hui, Li Hong-Shan, Zhang Peng-Xiang, Jiang Zui-Min. Influence of annealing oxygen pressure on the laser-induced thermoelectric voltage effect in YBa2Cu3O7-x thin films. Acta Physica Sinica, 2008, 57(8): 5237-5243. doi: 10.7498/aps.57.5237
[18]	Chen Xiao-Yang, Xu Xiang-Fan, Hu Rong-Xing, Ren Zhi, Xu Zhu-An, Cao Guang-Han. Synthesis and thermopower measurement of LixNayCoO2. Acta Physica Sinica, 2007, 56(3): 1627-1631. doi: 10.7498/aps.56.1627
[19]	Li Jin-Hua, Yuan Ning-Yi, H L W Chan, Lin Cheng-Lu. . Acta Physica Sinica, 2002, 51(8): 1788-1792. doi: 10.7498/aps.51.1788
[20]	CHEN JI-SHU. THEORY OF THIN PYROELECTRIC FILM DETECTORS. Acta Physica Sinica, 1974, 23(6): 51-58. doi: 10.7498/aps.23.51

Catalog

Vol. 70, Issue 7 - 2021-04-05

Metrics

Abstract views: 11066
PDF Downloads: 363
Cited By: 0

姓名
邮箱
手机号码
标题
留言内容
验证码

Search

Article

留言板

Research progress of Cu₂Se thin film thermoelectric properties

Abstract

Authors and contacts

Corresponding author: Wang Xiao-Dong, xdwang@semi.ac.cn

FullText HTML : translate this paragraph

References

Cited By

Catalog

Metrics

Authors

Referees

About Journal

About

Search

Article

留言板

Research progress of Cu2Se thin film thermoelectric properties

Abstract

Authors and contacts

Corresponding author: Wang Xiao-Dong, xdwang@semi.ac.cn

FullText HTML : translate this paragraph

References

Cited By

Catalog

Metrics

Publishing process

Authors

Referees

About Journal

About

Research progress of Cu₂Se thin film thermoelectric properties