Effects of different compositional ratios on physical structure and optical properties of thin films during alloying of Zn<sup>2+</sup> and TiO<sub>2</sub>

Xiao Wen-Yue; Dong Xiao-Shuo; Mamatrishat Mamat; Niu Na-Na; Li Guo-Dong; Zhu Ze-Tao; Bi Jie-Hao

doi:10.7498/aps.73.20240814

Abstract

A batch of TiO₂ films with different Zn²⁺ compositions are prepared on a single crystal silicon substrate by using sol-gel method to observe the changes in optical and photocatalytic properties in the alloying process of Zn²⁺ and TiO₂. X-ray diffractometer (XRD) is used to observe the changes in the crystal structures of the films in the alloying process and to track the formation of ZnTiO₃ compounds. Scanning electron microscope (SEM) and atomic force microscope (AFM) are used to observe the phenomena of a large number of holes on the surfaces of the films due to the limited solubility of the crystal lattice for Zn²⁺ in the alloying process. X-ray photoelectron spectroscopy (XPS) and optical bandgap are used to observe the changes at a level of the electronic structure of the films in the alloying process of Zn²⁺ with TiO₂. Finally, by degrading the methylene blue solution, it is shown that a small amount of Zn²⁺ doping is completely dissolved in TiO₂, destroying the TiO₂ crystalline quality. As the compositional share of Zn²⁺ continues to increase to 15%, the limited solubility of TiO₂ for Zn²⁺ is verified in the XPS peak fitting, resulting in a large number of hole structures in the film, and the active specific surface area of the film is enhanced, while Zn²⁺ effectively traps the photogenerated e^–/h⁺. In order to continue to observe the effect of Zn²⁺ concentration on TiO₂, we increase the concentration of Zn²⁺ to 40% and observe the phenomenon in the alloying process of Zn²⁺ with TiO₂. It is shown that the appearance of the compound ZnTiO₃ can act as a complex center for e^–/h⁺ and a significant decrease in the percentage of TiO₂ leads to a gradual decrease in the photocatalytic efficiency of the films after alloying.

Keywords:

Authors and contacts

1.
School of Physics and Technology, Xinjiang University, Urumqi 830017, China
2.
School of Materials Science and Engineering, Xinjiang University, Urumqi 830017, China

Corresponding author: Mamatrishat Mamat, rxtmmt@xju.edu.cn

Funds: Project supported by the Students Innovative-Research Training Program of Xinjiang University, China (Grant No. XJU-SRT-23114).

FullText HTML : translate this paragraph

References

[1]	Lukong V T, Ukoba K, Jen T C 2022 Int. J. Adv. Manuf. Technol. 122 3525 Google Scholar
[2]	李冬冬, 王丽莉 2012 物理学报 61 034212 Google Scholar Li D D, Wang L L 2012 Acta Phys. Sin. 61 034212 Google Scholar
[3]	Chinnarani M, Suresh S, Prabu K M, Kandasamy M, Pugazhenthiran N 2024 Inorg. Chim. Acta 560 121842 Google Scholar
[4]	Sanattalab E, Gürdağ G, Sığırcı B D 2023 Biomater. Adv. 148 213365 Google Scholar
[5]	Ziental D, Goslinska B C, Mlynarczyk D T, Sobotta A G, Stanisz B, Goslinski T L 2020 Nanomaterials 10 387 Google Scholar
[6]	Zhu Z W, Chen S F, Zhang Y, Wang W 2022 Prog. Org. Coat. 173 107226 Google Scholar
[7]	Alrowaili Z A, Alsohaimi I H, Betiha M A, Essawy A A, Mousa A A, Alruwaili S F, Hassan H M A 2020 Mater. Chem. Phys. 241 122403 Google Scholar
[8]	Ike P O, Ezugwu S, Chikwenze R, Nwanya A C, Ezugwu A E, Madiba I G, Ezekoye B A, Ahmed M S, Maaza M, Ezema F I 2019 Optik 191 1 Google Scholar
[9]	Aruna S T, Vismaya A, Balaji N 2021 Mater. Manuf. Processes 36 868 Google Scholar
[10]	Mittireddi R T, Makani N H, Prajapati D, Raj A, Banerjee R, Panda E 2023 Mater. Charact. 199 112818 Google Scholar
[11]	Sun N R, Wang J W, Yao J Z, Chen H M, Deng C H 2019 Microchim. Acta 186 159 Google Scholar
[12]	Zhang Q, Li C Y 2020 Nanomaterials 10 911 Google Scholar
[13]	Kusior A, Banas J, Zajac A T, Zubrzycka P, Ilnicka A M, Radecka M 2018 J. Mol. Struct. 1157 327 Google Scholar
[14]	Al-Tayeb M A-A, Khan M Y, Drmosh Q A, Hossain M K, Asim M, Dafalla H, Khan A 2023 Inorg. Chim. Acta 556 121611 Google Scholar
[15]	Ma Q, Qiu T, Liu S J, Weng L Q, Dong W Y 2010 Appl. Phys. A 104 365 Google Scholar
[16]	Liu Y, Peng Q, Zhou Z P, Yang G 2018 Chin. Phys. Lett. 35 048101 Google Scholar
[17]	Resende P D, Maria R, Silva J D, Azevedo I, Santos L A, Tadeu V 2020 J. Mater. Res. Technol. 9 10121 Google Scholar
[18]	Chen C C, Hu S H, Fu Y P 2015 J. Alloys Compd. 632 326 Google Scholar
[19]	Ahadi S, Moalej N S, Sheibani S 2019 Solid State Sci. 96 105975 Google Scholar
[20]	Yoon Y H, Lee S Y, Gwon J, Cho H J, Wu Q, Kim Y H, Lee W H 2018 Ceram. Int. 44 16647 Google Scholar
[21]	Qu X, Lin J B, Wei Q, Chen C T, Sun D P 2022 Chemosphere 308 136239 Google Scholar
[22]	Jaimy K B, Safeena V P, Ghosh S, Hebalkar N, Warrier K 2012 Dalton Trans. 41 4824 Google Scholar
[23]	Chen K T, Hsu C H, Jiang S C, Liang L S, Gao P, Qiu Y, Wu W Y, Zhang S, Zhu W Z, Lien S Y 2022 IEEE Trans. Electron Devices 69 1149 Google Scholar
[24]	Nair P K, Mizukami F, Nair J, Salou M, Oosawa Y, Izutsu H, Maeda K, Okubo T 1998 Mater. Res. Bull. 33 1495 Google Scholar
[25]	Chen P C, Chen C C, Chen S H 2017 Curr. Nanosci. 13 373 Google Scholar
[26]	Ren T Z, Yuan Z Y, Su B L 2004 Colloids Surf., A 241 67 Google Scholar
[27]	Lang J, Takahashi K, Kubo M, Shimada M 2022 Catalysts 12 365 Google Scholar
[28]	Mercado C C, Seeley Z M, Bandyopadhyay A, Bose S, McHale J L 2011 ACS Appl. Mater. Interfaces 3 2281 Google Scholar
[29]	Henderson M 2002 Surf. Sci. Rep. 46 1 Google Scholar
[30]	Dikici T, Yılmaz O, Akalin A S, Demirci S, Gültekin S, Yıldırım S, Yurddaşkal M 2022 J. Aust. Ceram. Soc. 58 1415 Google Scholar
[31]	Xu W, Li X J, Zhang S J, Wang J G, Xu Z K 2005 Trans. Nonferrous Met. Soc. China 15 119 Google Scholar
[32]	Wang C T, Lin H S, Wang W P 2019 Mater. Sci. Semicond. Process. 99 85 Google Scholar
[33]	Liao C Z, Li Y C, Tjong S C 2020 Nanomaterials 10 124 Google Scholar
[34]	Ismael M 2020 Sol. Energy 211 522 Google Scholar
[35]	Matsumoto Y, Katayama M, Abe T, Ohsawa T, Ohkubo I, Kumigashira H, Oshima M, Koinuma H 2010 J. Ceram. Soc. Jpn. 118 993 Google Scholar
[36]	Ribao P, Rivero M J, Ortiz I 2017 Environ. Sci. Pollut. Res. 24 12628 Google Scholar
[37]	Tang T, Wang T, Gao Y, Xiao H, Xu J H 2019 J. Mater. Sci. -Mater. Electron. 30 8471 Google Scholar
[38]	Xavier A M, Jacob I D, Surender S, Saravana kumaar M S S, Elangovan P 2022 Inorg. Chem. Commun. 146 110168 Google Scholar
[39]	Pecherskaya M D, Butanov K T, Ruzimuradov O N, Mamatkulov S I, Parpiev O 2022 Glass Phys. Chem. 48 327 Google Scholar
[40]	Heiba Z K, Mohamed M B, Badawi A, Abdellatief M 2022 J. Mater. Sci. -Mater. Electron. 33 10399 Google Scholar
[41]	Castellón E, Zayat M, Lévy D 2017 Adv. Funct. Mater. 28 04717 Google Scholar
[42]	Chu J Y, Sun Y C, Han X J, Zhang B, Du Y C, Song B, Xu P 2019 ACS Appl. Mater. Interfaces 11 18475 Google Scholar
[43]	Maleki K, Abdizadeh H, Golobostanfard M R, Adelfar R 2017 Appl. Surf. Sci. 394 37 Google Scholar

Cited By

图 1 不同Zn²⁺成分占比的薄膜的 XRD 图样

Figure 1. XRD patterns of thin films with different Zn²⁺ compositions.

DownLoad: Full-Size Img PowerPoint

图 2 不同Zn²⁺成分占比的薄膜的SEM图样

Figure 2. SEM patterns of thin films with different Zn²⁺ compositions.

DownLoad: Full-Size Img PowerPoint

图 3 (a)纯TiO₂以及(b)—(d) 3%, 15%和40% Zn²⁺成分占比的薄膜的二维和三维AFM图像

Figure 3. 2D and 3D AFM images of thin films with (a) pure TiO₂ and (b)–(d) 3%, 15% and 40% Zn²⁺ composition.

DownLoad: Full-Size Img PowerPoint

图 4 纯TiO₂以及3%, 15% 和 40%Zn²⁺成分占比的薄膜的XPS光谱

Figure 4. XPS spectra of pure TiO₂ and thin films with 3%, 15% and 40% Zn²⁺ compositions.

DownLoad: Full-Size Img PowerPoint

图 5 不同Zn²⁺成分占比的薄膜的(a)吸收光谱和(b) 光带隙能

Figure 5. (a) Absorption spectra and (b) optical band gap energy of films with different Zn²⁺ composition.

DownLoad: Full-Size Img PowerPoint

图 6 (a) 不同Zn²⁺成分占比的薄膜的吸收阈值波长和光带隙能; (b) 纯TiO₂和Zn²⁺成分占比为3%, 15% 和 40%的薄膜的价带

Figure 6. (a) Absorption threshold wavelengths and optical band gap energies of films with different Zn²⁺ compositions; (b) valence bands of pure TiO₂ and films with 3%, 15% and 40% Zn²⁺ compositions.

DownLoad: Full-Size Img PowerPoint

图 7 不同Zn²⁺成分占比的薄膜的能带位置示意图

Figure 7. Schematic representation of the energy band positions of films with different Zn²⁺ compositions.

DownLoad: Full-Size Img PowerPoint

图 8 降解亚甲基蓝的光催化活性　(a) 随时间变化的降解量; (b) 相应的降解反应速率常数图

Figure 8. Photocatalytic activity for degradation of methylene blue: (a) Degradation amount with time; (b) corresponding degradation rate constant plots.

DownLoad: Full-Size Img PowerPoint

图 9 光催化反应速率(η)与光催化反应常数(K_app)的关系图

Figure 9. Plot of photocatalytic reaction rate (η) versus photocatalytic reaction constant (K_app).

DownLoad: Full-Size Img PowerPoint

表 1 从 XRD 图谱获得的结构参数

Table 1. Structural parameters obtained from XRD spectra.

Samples	(h k l )	FWHM β/(°)	D/nm
TiO₂	(1 0 1)	0.177	8.384
3% Zn-TiO₂	(1 0 1)	0.161	9.217
5% Zn-TiO₂	(1 0 1)	0.197	7.533
10% Zn-TiO₂	(1 0 1)	0.180	8.244
15% Zn-TiO₂	(1 0 1)	0.259	5.730
20% Zn-TiO₂	(1 0 1)	0.152	9.762
40% Zn-TiO₂	(1 0 1)	0.227	6.537

DownLoad: CSV

表 2 从AFM获得的粗糙度参数(R_a为算数平均粗糙度, R_MS为均方根粗糙度, R_Sk为粗糙度斜率, R_Ku为粗糙度峰度)

Table 2. Roughness parameters obtained from AFM (R_a, R_MS, R_Sk, R_Ku are the average, root- mean-square, Skewness, and Kurtosis values of surface roughness, respectively).

Samples	Roughness R_a/nm	Roughness R_MS/nm	Skewness R_Sk	Kurtosis R_Ku
TiO₂	3.515	4.359	–0.492	0.276
3%Zn-TiO₂	2.230	2.851	–0.077	0.089
15%Zn-TiO₂	5.590	6.990	–0.313	0.819
40%Zn-TiO₂	6.115	8.703	–1.079	3.318

DownLoad: CSV

[1]	Lukong V T, Ukoba K, Jen T C 2022 Int. J. Adv. Manuf. Technol. 122 3525 Google Scholar
[2]	李冬冬, 王丽莉 2012 物理学报 61 034212 Google Scholar Li D D, Wang L L 2012 Acta Phys. Sin. 61 034212 Google Scholar
[3]	Chinnarani M, Suresh S, Prabu K M, Kandasamy M, Pugazhenthiran N 2024 Inorg. Chim. Acta 560 121842 Google Scholar
[4]	Sanattalab E, Gürdağ G, Sığırcı B D 2023 Biomater. Adv. 148 213365 Google Scholar
[5]	Ziental D, Goslinska B C, Mlynarczyk D T, Sobotta A G, Stanisz B, Goslinski T L 2020 Nanomaterials 10 387 Google Scholar
[6]	Zhu Z W, Chen S F, Zhang Y, Wang W 2022 Prog. Org. Coat. 173 107226 Google Scholar
[7]	Alrowaili Z A, Alsohaimi I H, Betiha M A, Essawy A A, Mousa A A, Alruwaili S F, Hassan H M A 2020 Mater. Chem. Phys. 241 122403 Google Scholar
[8]	Ike P O, Ezugwu S, Chikwenze R, Nwanya A C, Ezugwu A E, Madiba I G, Ezekoye B A, Ahmed M S, Maaza M, Ezema F I 2019 Optik 191 1 Google Scholar
[9]	Aruna S T, Vismaya A, Balaji N 2021 Mater. Manuf. Processes 36 868 Google Scholar
[10]	Mittireddi R T, Makani N H, Prajapati D, Raj A, Banerjee R, Panda E 2023 Mater. Charact. 199 112818 Google Scholar
[11]	Sun N R, Wang J W, Yao J Z, Chen H M, Deng C H 2019 Microchim. Acta 186 159 Google Scholar
[12]	Zhang Q, Li C Y 2020 Nanomaterials 10 911 Google Scholar
[13]	Kusior A, Banas J, Zajac A T, Zubrzycka P, Ilnicka A M, Radecka M 2018 J. Mol. Struct. 1157 327 Google Scholar
[14]	Al-Tayeb M A-A, Khan M Y, Drmosh Q A, Hossain M K, Asim M, Dafalla H, Khan A 2023 Inorg. Chim. Acta 556 121611 Google Scholar
[15]	Ma Q, Qiu T, Liu S J, Weng L Q, Dong W Y 2010 Appl. Phys. A 104 365 Google Scholar
[16]	Liu Y, Peng Q, Zhou Z P, Yang G 2018 Chin. Phys. Lett. 35 048101 Google Scholar
[17]	Resende P D, Maria R, Silva J D, Azevedo I, Santos L A, Tadeu V 2020 J. Mater. Res. Technol. 9 10121 Google Scholar
[18]	Chen C C, Hu S H, Fu Y P 2015 J. Alloys Compd. 632 326 Google Scholar
[19]	Ahadi S, Moalej N S, Sheibani S 2019 Solid State Sci. 96 105975 Google Scholar
[20]	Yoon Y H, Lee S Y, Gwon J, Cho H J, Wu Q, Kim Y H, Lee W H 2018 Ceram. Int. 44 16647 Google Scholar
[21]	Qu X, Lin J B, Wei Q, Chen C T, Sun D P 2022 Chemosphere 308 136239 Google Scholar
[22]	Jaimy K B, Safeena V P, Ghosh S, Hebalkar N, Warrier K 2012 Dalton Trans. 41 4824 Google Scholar
[23]	Chen K T, Hsu C H, Jiang S C, Liang L S, Gao P, Qiu Y, Wu W Y, Zhang S, Zhu W Z, Lien S Y 2022 IEEE Trans. Electron Devices 69 1149 Google Scholar
[24]	Nair P K, Mizukami F, Nair J, Salou M, Oosawa Y, Izutsu H, Maeda K, Okubo T 1998 Mater. Res. Bull. 33 1495 Google Scholar
[25]	Chen P C, Chen C C, Chen S H 2017 Curr. Nanosci. 13 373 Google Scholar
[26]	Ren T Z, Yuan Z Y, Su B L 2004 Colloids Surf., A 241 67 Google Scholar
[27]	Lang J, Takahashi K, Kubo M, Shimada M 2022 Catalysts 12 365 Google Scholar
[28]	Mercado C C, Seeley Z M, Bandyopadhyay A, Bose S, McHale J L 2011 ACS Appl. Mater. Interfaces 3 2281 Google Scholar
[29]	Henderson M 2002 Surf. Sci. Rep. 46 1 Google Scholar
[30]	Dikici T, Yılmaz O, Akalin A S, Demirci S, Gültekin S, Yıldırım S, Yurddaşkal M 2022 J. Aust. Ceram. Soc. 58 1415 Google Scholar
[31]	Xu W, Li X J, Zhang S J, Wang J G, Xu Z K 2005 Trans. Nonferrous Met. Soc. China 15 119 Google Scholar
[32]	Wang C T, Lin H S, Wang W P 2019 Mater. Sci. Semicond. Process. 99 85 Google Scholar
[33]	Liao C Z, Li Y C, Tjong S C 2020 Nanomaterials 10 124 Google Scholar
[34]	Ismael M 2020 Sol. Energy 211 522 Google Scholar
[35]	Matsumoto Y, Katayama M, Abe T, Ohsawa T, Ohkubo I, Kumigashira H, Oshima M, Koinuma H 2010 J. Ceram. Soc. Jpn. 118 993 Google Scholar
[36]	Ribao P, Rivero M J, Ortiz I 2017 Environ. Sci. Pollut. Res. 24 12628 Google Scholar
[37]	Tang T, Wang T, Gao Y, Xiao H, Xu J H 2019 J. Mater. Sci. -Mater. Electron. 30 8471 Google Scholar
[38]	Xavier A M, Jacob I D, Surender S, Saravana kumaar M S S, Elangovan P 2022 Inorg. Chem. Commun. 146 110168 Google Scholar
[39]	Pecherskaya M D, Butanov K T, Ruzimuradov O N, Mamatkulov S I, Parpiev O 2022 Glass Phys. Chem. 48 327 Google Scholar
[40]	Heiba Z K, Mohamed M B, Badawi A, Abdellatief M 2022 J. Mater. Sci. -Mater. Electron. 33 10399 Google Scholar
[41]	Castellón E, Zayat M, Lévy D 2017 Adv. Funct. Mater. 28 04717 Google Scholar
[42]	Chu J Y, Sun Y C, Han X J, Zhang B, Du Y C, Song B, Xu P 2019 ACS Appl. Mater. Interfaces 11 18475 Google Scholar
[43]	Maleki K, Abdizadeh H, Golobostanfard M R, Adelfar R 2017 Appl. Surf. Sci. 394 37 Google Scholar

[1]	Wang Yue, Shao Bo-Huai, Chen Shuang-Long, Wang Chun-Jie, Gao Chun-Xiao. Effects of defects on electrical transport properties of anatase TiO₂ polycrystalline under high pressure: AC impedance measurement. Acta Physica Sinica, 2023, 72(12): 126401. doi: 10.7498/aps.72.20230020
[2]	Zhang Li-Sheng. Photocatalytic properties of gold nanoarrays driven by surface plasmon. Acta Physica Sinica, 2021, 70(23): 235202. doi: 10.7498/aps.70.20210424
[3]	Gao Xu-Dong, Yang De-Cao, Wei Wen-Jing, Li Gong-Ping. Simulation study of electron beam irradiation damage to ZnO and TiO₂. Acta Physica Sinica, 2021, 70(23): 234101. doi: 10.7498/aps.70.20211223
[4]	Li Peng-Cheng, Tang Chong-Yang, Cheng Liang, Hu Yong-Ming, Xiao Xiang-Heng, Chen Wan-Ping. Reduction of CO₂ by TiO₂ nanoparticles through friction in water. Acta Physica Sinica, 2021, 70(21): 214601. doi: 10.7498/aps.70.20210210
[5]	Cui Zong-Yang, Xie Zhong-Shuai, Wang Yao-Jin, Yuan Guo-Liang, Liu Jun-Ming. Research progress and prospects of photocatalytic devices with perovskite ferroelectric semiconductors. Acta Physica Sinica, 2020, 69(12): 127706. doi: 10.7498/aps.69.20200287
[6]	Yao Pan-Pan, Wang Ling-Rui, Wang Jia-Xiang, Guo Hai-Zhong. Evolutions of structural and optical properties of lead-free double perovskite Cs₂TeCl₆ under high pressure. Acta Physica Sinica, 2020, 69(21): 218801. doi: 10.7498/aps.69.20200988
[7]	Wang Shao-Xia, Zhao Xu-Cai, Pan Duo-Qiao, Pang Guo-Wang, Liu Chen-Xi, Shi Lei-Qian, Liu Gui-An, Lei Bo-Cheng, Huang Yi-Neng, Zhang Li-Li. First principle study of influence of transition metal (Cr, Mn, Fe, Co) doping on magnetism of TiO₂. Acta Physica Sinica, 2020, 69(19): 197101. doi: 10.7498/aps.69.20200644
[8]	Zhou Li, Wang Qu-Quan. Plasmon resonance energy transfer and research progress in plasmon-enhanced photocatalysis. Acta Physica Sinica, 2019, 68(14): 147301. doi: 10.7498/aps.68.20190276
[9]	Wang Chun-Jie, Wang Yue, Gao Chun-Xiao. Grain boundary electrical characteristics for rutile TiO₂ under pressure. Acta Physica Sinica, 2019, 68(20): 206401. doi: 10.7498/aps.68.20190630
[10]	Wu Hua-Ping, Ling Huan, Zhang Zheng, Li Yan-Biao, Liang Li-Hua, Chai Guo-Zhong. Research progress on photocatalytic activity of ferroelectric materials. Acta Physica Sinica, 2017, 66(16): 167702. doi: 10.7498/aps.66.167702
[11]	Cheng Cheng, Wang Guo-Dong, Cheng Xiao-Yu. Effects of surface polarization on the bandgap and the absorption-peak wavelength of quantum dot at room temperature. Acta Physica Sinica, 2017, 66(13): 137802. doi: 10.7498/aps.66.137802
[12]	Guo Zhao-Long, Zhao Hai-Xin, Zhao Wei. Preparation and characterization of self-cleaning and anti-reflection ZnO-SiO2 nanometric films. Acta Physica Sinica, 2016, 65(6): 064206. doi: 10.7498/aps.65.064206
[13]	Jiang En-Hai, Zhu Xing-Feng, Chen Ling-Fu. First-principles study of the electronic structure, magnetism, and spin-polarization in Heusler alloy Co2MnAl(100) surface. Acta Physica Sinica, 2015, 64(14): 147301. doi: 10.7498/aps.64.147301
[14]	Li Pei-Xin, Feng Ming-Yang, Wu Cai-Ping, Li Shao-Bo, Hou Lei-Tian, Ma Jia-Sai, Yin Chun-Hao. Study on the photocatalytic mechanism of tio2 sensitized by zinc porphyrin. Acta Physica Sinica, 2015, 64(13): 137601. doi: 10.7498/aps.64.137601
[15]	Wang Tao, Chen Jian-Feng, Le Yuan. First-principles investigation of iodine doped rutile TiO2(110) surface. Acta Physica Sinica, 2014, 63(20): 207302. doi: 10.7498/aps.63.207302
[16]	Liu Fang, Jiang Zhen-Yi. First-principles study on the electronic and optical properties of the (Eu,N)-codoped anatase TiO2 photocatalyst. Acta Physica Sinica, 2013, 62(19): 193103. doi: 10.7498/aps.62.193103
[17]	Liang Pei, Wang Le, Xiong Si-Yu, Dong Qian-Min, Li Xiao-Yan. Research on the photocatalysis synergistic effect of Mo-X(B, C, N, O, F) codoped TiO2. Acta Physica Sinica, 2012, 61(5): 053101. doi: 10.7498/aps.61.053101
[18]	Ma Hai-Min, Hong Liang, Yin Yi, Xu Jian, Ye Hui. Preparation and property of super-hydrophilic SiO2-TiO2 nano-particle layer. Acta Physica Sinica, 2011, 60(9): 098105. doi: 10.7498/aps.60.098105
[19]	Lu Shuo, Zhang Yue, Shang Jia-Xiang. First principles study on structure and property of Si2 CN4(010) surface. Acta Physica Sinica, 2011, 60(2): 027302. doi: 10.7498/aps.60.027302
[20]	Meng Qing-Yu, Chen Bao-Jiu, Zhao Xiao-Xia, Yan Bin, Wang Xiao-Jun, Xu Wu. Luminescence intensity of Ag+ doped Y2O3:Eu nanocrystals. Acta Physica Sinica, 2006, 55(5): 2623-2627. doi: 10.7498/aps.55.2623

Catalog

Vol. 73, Issue 18 - 2024-09-20

Metrics

Abstract views: 321
PDF Downloads: 13
Cited By: 0

姓名
邮箱
手机号码
标题
留言内容
验证码

Search

Article

留言板

Effects of different compositional ratios on physical structure and optical properties of thin films during alloying of Zn²⁺ and TiO₂

Abstract

Authors and contacts

Corresponding author: Mamatrishat Mamat, rxtmmt@xju.edu.cn

FullText HTML : translate this paragraph

References

Cited By

Catalog

Metrics

Authors

Referees

About Journal

About

Search

Article

留言板

Effects of different compositional ratios on physical structure and optical properties of thin films during alloying of Zn2+ and TiO2

Abstract

Authors and contacts

Corresponding author: Mamatrishat Mamat, rxtmmt@xju.edu.cn

FullText HTML : translate this paragraph

References

Cited By

Catalog

Metrics

Publishing process

Authors

Referees

About Journal

About

Effects of different compositional ratios on physical structure and optical properties of thin films during alloying of Zn²⁺ and TiO₂