熔融盐法合成锂离子电池正极材料纳米LiNiO2

白莹; 王蓓; 张伟风

doi:10.7498/aps.60.068202

摘要

采用熔融盐法,在较低的温度和较短的时间制备了符合理论化学计量比的纳米LiNiO2.研究表明,经过空气中的低温预烧,可以使制备的纯相纳米LiNiO2具有更加优良的结晶性能和更佳的电化学特性.添加预烧步骤前后所得最终产物的初始容量分别为151和148 mAh ·g-1,经过100周的循环,容量衰减到55和118 mAh ·g-1,容量保持率分别为36.4%和79.7%.原因在于预烧后再进行煅烧降低了阳离子无序度,减少了混杂

关键词:

Abstract

Molten salt method is applied to synthesis stoichiometric nano-LiNiO2 in rather low temperature and short time. Our results indicate that in the process of preheating the better-crystallized LiNiO2 powder with better electrochemical performances can be produced. The final samples before and after preheating exhibit the initial discharge capacities of 151 and 148 mAh ·g-1 respectively. After 100 cycles, they decay to only 55 and 118 mAh ·g-1, with capacity retentions being 36.4% and 79.7% respectively. The lowered cation disordering is thought to be favorable for the diffusion of lithium ions, by which the enhanced electrochemial properties can be explained.

Keywords:

作者及机构信息

1.
河南省光伏材料重点实验室,河南大学物理与电子学院,开封 475004

基金项目: 国家自然科学基金(批准号:50902044,60976016)、河南省教育厅自然科学基金(批准号:2010B480004)和河南大学自然科学基金(批准号:2008YBZR018)资助的课题.

Authors and contacts

1.
Key Laboratory of Photovoltaic Materials of Henan Province and School of Physics & Electronics, Henan University, Kaifeng 475004, China

参考文献

[1]	Kang K, Meng Y S, Breger J, Grey C P, Ceder G 2006 Science 311 977
[2]	Paek S M, Yoo E J, Honma I 2009 Nano Lett. 9 72
[3]	Li J, Yang C Z, Zhang X G, Zhang J, Xia B J 2009 Acta Phys. Sin. 58 6573 (in Chinese) [李佳、杨传铮、张熙贵、张建、夏保佳 2009 物理学报 58 6573]
[4]	Hou X H, Yu H W, Hu S J 2010 Acta Phys. Sin. 59 8226 (in Chinese) [侯贤华、余洪文、胡社军 2009 物理学报 59 8226]
[5]	Hou X H, Du S J, Li W S, Zhao L Z, Yu H W, Tan C L 2008 Acta Phys. Sin. 57 2374 (in Chinese) [侯贤华、杜社军、李伟善、赵灵智、余洪文、谭春林 2008 物理学报 57 2374]
[6]	Hou Z F, Liu H Y, Zhu Z Z, Huang M C, Yang Y 2003 Acta Phys. Sin. 52 952 (in Chinese) [候柱锋、刘慧英、朱梓忠、黄美纯、杨勇 2003 物理学报 52 952]
[7]	Hu G J, Ouyang C Y 2010 Acta Phys. Sin. 59 5863 (in Chinese) [胡国进、欧阳楚英 2010 物理学报 59 5863]
[8]	Nishida Y, Nakane K, Stoh T 1997 J. Power Sour. 68 561
[9]	Han C H, Kim J H, Paeng S H, Kwak D J, Sung Y M 2009 Thin Solid Films 517 4215
[10]	Kim C J, Ahn I S, Cho K K, Lee S G, Chung J K 2008 J. Alloys Compd. 449 335
[11]	Mehrdad B, Sirous A 2010 J. Nanomater. 2010 695083
[12]	Wang J M, Hu J P, Ouyang C Y, Shi S Q, Lei M S 2011 Solid State Commun.151 234
[13]	Park H R 2010 J. Ind. Eng. Chem. 16 698
[14]	Song M Y, Kwon I H, Shim S, Song J H 2010 Ceram. Int. 36 1225
[15]	Lee K K, Yoon W S, Kim K Bum, Lee K Y, Hong S T 2001 J. Electrochem. Soc. 148 A716
[16]	Kalyani P, Kalaiselvi N 2005 Sci. Technol. Adv. Mater. 6 689
[17]	Han C H, Hong Y S, Kim K 2003 Solid State Ionics 159 241
[18]	Kim J H, Myung S T, Sun Y K 2004 Electrochim. Acta 49 219
[19]	Ni J F, Zhou H H, Chen J T, Zhang X X 2007 Mater. Lett. 61 1260
[20]	Han C H, Hong Y S, Park C M, Kim K 2001 J. Power Sour. 92 95
[21]	Liang H Y, Qiu X P, Zhang S C, He Z Q, Zhu W T, Chen L Q 2004 Electrochem. Commun. 6 505
[22]	Liang H Y, Qiu X P, Chen H L, He Z Q, Zhu W T, Chen L Q 2004 Electrochem. Commun. 6 789
[23]	Chang Z R, Qi X, Wu F, Tang H W, Xu Q H 2006 Funct. Mater. 37 896 (in Chinese) [常照荣、齐霞、吴锋、汤宏伟、徐秋红 2006 功能材料 37 896]
[24]	Wang J P, Bai Y, Wu M Y, Zhang W F 2009 J. Power Sourc. 191 614
[25]	Zhao S, Bai Y, Zhang W F 2010 Electrochim. Acta 55 3891
[26]	Song M, Kwon I, Kim H 2005 J. Appl. Electrochem. 35 1073
[27]	Ohzuku T, Ueda A, Nagayama M 1993 J. Electrochem. Soc. 140 1862

施引文献

[1]	Kang K, Meng Y S, Breger J, Grey C P, Ceder G 2006 Science 311 977
[2]	Paek S M, Yoo E J, Honma I 2009 Nano Lett. 9 72
[3]	Li J, Yang C Z, Zhang X G, Zhang J, Xia B J 2009 Acta Phys. Sin. 58 6573 (in Chinese) [李佳、杨传铮、张熙贵、张建、夏保佳 2009 物理学报 58 6573]
[4]	Hou X H, Yu H W, Hu S J 2010 Acta Phys. Sin. 59 8226 (in Chinese) [侯贤华、余洪文、胡社军 2009 物理学报 59 8226]
[5]	Hou X H, Du S J, Li W S, Zhao L Z, Yu H W, Tan C L 2008 Acta Phys. Sin. 57 2374 (in Chinese) [侯贤华、杜社军、李伟善、赵灵智、余洪文、谭春林 2008 物理学报 57 2374]
[6]	Hou Z F, Liu H Y, Zhu Z Z, Huang M C, Yang Y 2003 Acta Phys. Sin. 52 952 (in Chinese) [候柱锋、刘慧英、朱梓忠、黄美纯、杨勇 2003 物理学报 52 952]
[7]	Hu G J, Ouyang C Y 2010 Acta Phys. Sin. 59 5863 (in Chinese) [胡国进、欧阳楚英 2010 物理学报 59 5863]
[8]	Nishida Y, Nakane K, Stoh T 1997 J. Power Sour. 68 561
[9]	Han C H, Kim J H, Paeng S H, Kwak D J, Sung Y M 2009 Thin Solid Films 517 4215
[10]	Kim C J, Ahn I S, Cho K K, Lee S G, Chung J K 2008 J. Alloys Compd. 449 335
[11]	Mehrdad B, Sirous A 2010 J. Nanomater. 2010 695083
[12]	Wang J M, Hu J P, Ouyang C Y, Shi S Q, Lei M S 2011 Solid State Commun.151 234
[13]	Park H R 2010 J. Ind. Eng. Chem. 16 698
[14]	Song M Y, Kwon I H, Shim S, Song J H 2010 Ceram. Int. 36 1225
[15]	Lee K K, Yoon W S, Kim K Bum, Lee K Y, Hong S T 2001 J. Electrochem. Soc. 148 A716
[16]	Kalyani P, Kalaiselvi N 2005 Sci. Technol. Adv. Mater. 6 689
[17]	Han C H, Hong Y S, Kim K 2003 Solid State Ionics 159 241
[18]	Kim J H, Myung S T, Sun Y K 2004 Electrochim. Acta 49 219
[19]	Ni J F, Zhou H H, Chen J T, Zhang X X 2007 Mater. Lett. 61 1260
[20]	Han C H, Hong Y S, Park C M, Kim K 2001 J. Power Sour. 92 95
[21]	Liang H Y, Qiu X P, Zhang S C, He Z Q, Zhu W T, Chen L Q 2004 Electrochem. Commun. 6 505
[22]	Liang H Y, Qiu X P, Chen H L, He Z Q, Zhu W T, Chen L Q 2004 Electrochem. Commun. 6 789
[23]	Chang Z R, Qi X, Wu F, Tang H W, Xu Q H 2006 Funct. Mater. 37 896 (in Chinese) [常照荣、齐霞、吴锋、汤宏伟、徐秋红 2006 功能材料 37 896]
[24]	Wang J P, Bai Y, Wu M Y, Zhang W F 2009 J. Power Sourc. 191 614
[25]	Zhao S, Bai Y, Zhang W F 2010 Electrochim. Acta 55 3891
[26]	Song M, Kwon I, Kim H 2005 J. Appl. Electrochem. 35 1073
[27]	Ohzuku T, Ueda A, Nagayama M 1993 J. Electrochem. Soc. 140 1862

[1]	周斌, 肖事成, 王一楠, 张晓毓, 钟雪, 马丹, 戴赢, 范志强, 唐贵平. VS₂作为锂离子电池负极材料的第一性原理研究. 物理学报, 2024, 73(11): 113101. doi: 10.7498/aps.73.20231681
[2]	李晓杰, 喻云泰, 张志文, 董小瑞. 基于电化学老化衰退模型的锂离子动力电池外特性. 物理学报, 2022, 71(3): 038803. doi: 10.7498/aps.71.20211401
[3]	柳小伟, 宋辉, 郭美卿, 王根伟, 迟青卓. 基于电化学-应力耦合模型的锂离子电池硅/碳核壳结构的模拟与优化. 物理学报, 2021, 70(17): 178201. doi: 10.7498/aps.70.20210455
[4]	李涛, 程夕明, 胡晨华. 锂离子电池电化学降阶模型性能对比. 物理学报, 2021, 70(13): 138801. doi: 10.7498/aps.70.20201894
[5]	张永泉, 姚安权, 杨柳, 朱凯, 曹殿学. 水系镁离子电池正极材料钠锰氧化物的制备及电化学性能. 物理学报, 2021, 70(16): 168201. doi: 10.7498/aps.70.20202130
[6]	郑路敏, 钟淑英, 徐波, 欧阳楚英. 锂离子电池正极材料Li₂MnO₃稀土掺杂的第一性原理研究. 物理学报, 2019, 68(13): 138201. doi: 10.7498/aps.68.20190509
[7]	曾建邦, 郭雪莹, 刘立超, 沈祖英, 单丰武, 罗玉峰. 基于电化学-热耦合模型研究隔膜孔隙结构对锂离子电池性能的影响机制. 物理学报, 2019, 68(1): 018201. doi: 10.7498/aps.68.20181726
[8]	蒋梅燕, 朱政杰, 陈成克, 李晓, 胡晓君. 硫离子注入纳米金刚石薄膜的微结构和电化学性能. 物理学报, 2019, 68(14): 148101. doi: 10.7498/aps.68.20190394
[9]	庞辉. 基于电化学模型的锂离子电池多尺度建模及其简化方法. 物理学报, 2017, 66(23): 238801. doi: 10.7498/aps.66.238801
[10]	马昊, 刘磊, 路雪森, 刘素平, 师建英. 锂离子电池正极材料Li2FeSiO4的电子结构与输运特性. 物理学报, 2015, 64(24): 248201. doi: 10.7498/aps.64.248201
[11]	李娟, 汝强, 胡社军, 郭凌云. 锂离子电池SnSb/C复合负极材料的热碳还原法制备及电化学性能研究. 物理学报, 2014, 63(16): 168201. doi: 10.7498/aps.63.168201
[12]	王锐, 胡晓君. 氧离子注入纳米金刚石薄膜的微结构和电化学性能研究. 物理学报, 2014, 63(14): 148102. doi: 10.7498/aps.63.148102
[13]	陈畅, 汝强, 胡社军, 安柏楠, 宋雄. Co2SnO4/Graphene复合材料的制备与电化学性能研究. 物理学报, 2014, 63(19): 198201. doi: 10.7498/aps.63.198201
[14]	李娟, 汝强, 孙大伟, 张贝贝, 胡社军, 侯贤华. 锂离子电池SnSb/MCMB核壳结构负极材料嵌锂性能研究. 物理学报, 2013, 62(9): 098201. doi: 10.7498/aps.62.098201
[15]	黄乐旭, 陈远富, 李萍剑, 黄然, 贺加瑞, 王泽高, 郝昕, 刘竞博, 张万里, 李言荣. 氧化石墨制备温度对石墨烯结构及其锂离子电池性能的影响. 物理学报, 2012, 61(15): 156103. doi: 10.7498/aps.61.156103
[16]	刘相, 谢凯, 郑春满, 王军. 不同气氛下裂解含苯环聚硅氧烷制备锂离子电池Si-O-C复合负极材料的电池性能研究. 物理学报, 2011, 60(11): 118202. doi: 10.7498/aps.60.118202
[17]	彭薇, 岳敏, 梁奇, 胡社军, 侯贤华. 锂离子电池LiMn1-xFexPO4(0x<1)正极材料的制备及性能研究. 物理学报, 2011, 60(3): 038202. doi: 10.7498/aps.60.038202
[18]	白莹, 丁玲红, 张伟风. ZnFe2O4的固相法和水热法制备及其电化学性能研究. 物理学报, 2011, 60(5): 058201. doi: 10.7498/aps.60.058201
[19]	侯贤华, 胡社军, 石璐. 锂离子电池Sn-Ti合金负极材料的制备及性能研究. 物理学报, 2010, 59(3): 2109-2113. doi: 10.7498/aps.59.2109
[20]	侯贤华, 余洪文, 胡社军. 锂离子电池Sn-Al薄膜电极的制备及电化学性能研究. 物理学报, 2010, 59(11): 8226-8230. doi: 10.7498/aps.59.8226

计量

文章访问数: 10312
PDF下载量: 822
被引次数: 0

姓名
邮箱
手机号码
标题
留言内容
验证码

搜索

留言板