退火对非故意掺杂4H-SiC外延材料386 nm和388 nm发射峰的影响

程萍 张玉明 张义门

引用本文:
Citation:

退火对非故意掺杂4H-SiC外延材料386 nm和388 nm发射峰的影响

程萍, 张玉明, 张义门

Effect of annealing treatment on the 386 nm and 388 nm emission peaks in unintentionally doped 4H-SiC epilayer

Cheng Ping, Zhang Yu-Ming, Zhang Yi-Men
PDF
导出引用
  • 10 K条件下,采用光致发光(PL)技术研究了不同退火处理后非故意掺杂4H-SiC外延材料的低温PL特性.结果发现,在370—400 nm范围内出现了三个发射峰,能量较高的峰约为3.26 eV,与4H-SiC材料的室温禁带宽度相当.波长约为386 nm和388 nm的两个发射峰分别位于~3.21 eV和~3.19 eV,与材料中的N杂质有关.当退火时间为30 min时,随退火温度的升高,386 nm和388 nm两个发射峰的PL强度先增加后减小,且退火温度为1573 K时,两个发射峰的PL强度均达到最大.
    Under different annealing treatment conditions, the low temperature PL properties of unintentionally doped 4H-SiC epilayer have been studied by photoluminescence (PL) technique at 10 K. The results show that there are three emission peaks in the range from 370 nm to 400 nm and the maximum energy is about 3.26 eV, which is in accordance with the energy gaps (Eg) of 4H-SiC at room temperature. The 386 nm and 388 nm peaks (corresponding to ~3.21 eV and ~3.19 eV, respectively) are related with N impurity. When keeping annealing time at 30 min, the PL intensity of 386 nm and 388 nm peaks increases and then decreases with the annealing temperature increasing and reaches a maximum at 1573 K. The PL at 386 nm and 388nm change in quite the same manner with annealing time during isothermal annealing at temperature of 1573 K, whereas the difference is small. With the same annealing treatment, the low temperature PL results of 386 nm and 388 nm coincide with that of intrinsic defects in unintentionally doped 4H-SiC, which results from the interaction of infinitesimal disturbance potential energy between N impurity and native defects.
    • 基金项目: 国家自然科学基金(批准号: 60876061),预研基金(批准号: 9140A08050508)和陕西省13115创新工程(批准号: 2008ZDKG-30)资助的课题.
    [1]

    Sriram S, Ward A, Henning J, Allen S T 2005 MRS Bull. 30 308

    [2]

    Son N T, Carlsson P, Gllstrm A, Magnusson B, Janzén E 2007 Phys. B 401 67

    [3]

    Janzén E, Son N T, Magnusson B, Ellison A 2006 Microelectron. Eng. 83 130

    [4]

    Carlos W E, Garces N Y, Glaser E R 2006 Phys. Rev. B 74 235201

    [5]

    Alfieri G, Kimoto T 2007 J. Phys. Condens. Matter 19 306204

    [6]

    Son N T, Chen W M, Lindstrm J L, Monemar B, Janzén E 1999 Phys. Scr. T79 162 46

    [7]

    Srman E, Son N T, Chen W M, Kordina O, Hallin C, Janzén E 2000 Phys. Rev. B 61 2613

    [8]

    Zvanut M E, Tol J van 2007 Phys. B 401-402 73

    [9]

    Young C F, Xie K, Poindexter E H, Gerardi G J, Keeble D J 1997 Appl. phys. Lett. 70 1858

    [10]

    Gerstmann U, Rauls E, Greulich-Weber S, Kalabukhova E N, Savchenko D V, Poppl A, Mauri F 2007 Mater. Sci. Forum 556 391

    [11]

    Goldberg Y, Levinshtein M E, Rumyantsev S L 2001 Eds. Levinshtein M E, Rumyantsev S L, Shur M S, John Wiley & Sons, Inc., New York 93

    [12]

    Yang Y T, Han R, Wang P 2008 Chin. Phys. B 17 3459

    [13]

    Gao X, Sun G S, Li J M, Zhao W S, Wang L, Zhang Y X, Zeng Y P 2005 Chin. J. Semicond. 26 936 (in Chinese) [高 欣、 孙国胜、 李晋闽、 赵万顺、 王 雷、 张永兴、 曾一平 2005 半导体学报 26 936]

    [14]

    Ivanov V Y, Godlewski M, Kalabukhova E N, Dimitriadis C A, Zekentes K 2008 Opt. Mater. 30 746

    [15]

    Cheng P, Zhang Y M, Zhang Y M, Wang Y H, Guo H 2010 Acta Phys . Sin. 59 3542 (in Chinese) [程 萍、 张玉明、 张义门、 王悦湖、 郭 辉 2010 物理学报 59 3542]

    [16]

    Cheng P, Zhang Y M, Zhang Y M, Guo H 2010 Chin. Phys. B 19 097802

  • [1]

    Sriram S, Ward A, Henning J, Allen S T 2005 MRS Bull. 30 308

    [2]

    Son N T, Carlsson P, Gllstrm A, Magnusson B, Janzén E 2007 Phys. B 401 67

    [3]

    Janzén E, Son N T, Magnusson B, Ellison A 2006 Microelectron. Eng. 83 130

    [4]

    Carlos W E, Garces N Y, Glaser E R 2006 Phys. Rev. B 74 235201

    [5]

    Alfieri G, Kimoto T 2007 J. Phys. Condens. Matter 19 306204

    [6]

    Son N T, Chen W M, Lindstrm J L, Monemar B, Janzén E 1999 Phys. Scr. T79 162 46

    [7]

    Srman E, Son N T, Chen W M, Kordina O, Hallin C, Janzén E 2000 Phys. Rev. B 61 2613

    [8]

    Zvanut M E, Tol J van 2007 Phys. B 401-402 73

    [9]

    Young C F, Xie K, Poindexter E H, Gerardi G J, Keeble D J 1997 Appl. phys. Lett. 70 1858

    [10]

    Gerstmann U, Rauls E, Greulich-Weber S, Kalabukhova E N, Savchenko D V, Poppl A, Mauri F 2007 Mater. Sci. Forum 556 391

    [11]

    Goldberg Y, Levinshtein M E, Rumyantsev S L 2001 Eds. Levinshtein M E, Rumyantsev S L, Shur M S, John Wiley & Sons, Inc., New York 93

    [12]

    Yang Y T, Han R, Wang P 2008 Chin. Phys. B 17 3459

    [13]

    Gao X, Sun G S, Li J M, Zhao W S, Wang L, Zhang Y X, Zeng Y P 2005 Chin. J. Semicond. 26 936 (in Chinese) [高 欣、 孙国胜、 李晋闽、 赵万顺、 王 雷、 张永兴、 曾一平 2005 半导体学报 26 936]

    [14]

    Ivanov V Y, Godlewski M, Kalabukhova E N, Dimitriadis C A, Zekentes K 2008 Opt. Mater. 30 746

    [15]

    Cheng P, Zhang Y M, Zhang Y M, Wang Y H, Guo H 2010 Acta Phys . Sin. 59 3542 (in Chinese) [程 萍、 张玉明、 张义门、 王悦湖、 郭 辉 2010 物理学报 59 3542]

    [16]

    Cheng P, Zhang Y M, Zhang Y M, Guo H 2010 Chin. Phys. B 19 097802

  • [1] 常帅军, 马海伦, 李浩, 欧树基, 郭建飞, 钟鸣浩, 刘莉. 一种能够改善鲁棒性的新型4H-SiC ESD防护器件. 物理学报, 2022, 71(19): 198501. doi: 10.7498/aps.71.20220879
    [2] 李传纲, 鞠涛, 张立国, 李杨, 张璇, 秦娟, 张宝顺, 张泽洪. Ti, N共掺杂4H-SiC复合增强缓冲层生长及其对PiN二极管正向性能稳定性的改善. 物理学报, 2021, 70(3): 037102. doi: 10.7498/aps.70.20200921
    [3] 牟致栋. Rh XIII—Cd XVI离子4s24p3—4s4p4能级与跃迁的理论计算. 物理学报, 2019, 68(6): 063101. doi: 10.7498/aps.68.20181976
    [4] 杜园园, 张春雷, 曹学蕾. 基于4H-SiC肖特基势垒二极管的射线探测器. 物理学报, 2016, 65(20): 207301. doi: 10.7498/aps.65.207301
    [5] 姜大朋, 苏良碧, 徐军, 唐慧丽, 吴锋, 郑丽和, 王庆国, 郭鑫, 邹宇琦. Cr,Mg:GSGG 晶体生长、光谱性能及Cr4+形成机理的研究. 物理学报, 2012, 61(3): 038102. doi: 10.7498/aps.61.038102
    [6] 晁月盛, 郭红, 高翔宇, 罗丽平, 朱涵娴. 退火处理Fe43Co43Hf7B6Cu1非晶合金的正电子湮没研究. 物理学报, 2011, 60(1): 017504. doi: 10.7498/aps.60.017504
    [7] 苗瑞霞, 张玉明, 汤晓燕, 张义门. 4H-SiC中基面位错发光特性研究. 物理学报, 2011, 60(3): 037808. doi: 10.7498/aps.60.037808
    [8] 喻军, 周朋, 赵衡煜, 吴锋, 夏海平, 苏良碧, 徐军. γ射线辐照诱导Bi:α-BaB2O4单晶近红外宽带发光的研究. 物理学报, 2010, 59(5): 3538-3541. doi: 10.7498/aps.59.3538
    [9] 黎兵, 刘才, 冯良桓, 张静全, 郑家贵, 蔡亚平, 蔡伟, 武莉莉, 李卫, 雷智, 曾广根, 夏庚培. CdS/CdTe薄膜太阳电池的深能级瞬态谱和光致发光研究. 物理学报, 2009, 58(3): 1987-1991. doi: 10.7498/aps.58.1987
    [10] 魏玮, 刘明, 曲盛薇, 张庆瑜. Ti缓冲层及退火处理对Si(111)基片上生长的ZnO薄膜结构和发光特性的影响. 物理学报, 2009, 58(8): 5736-5743. doi: 10.7498/aps.58.5736
    [11] 贾仁需, 张义门, 张玉明, 王悦湖. N型4H-SiC同质外延生长. 物理学报, 2008, 57(10): 6649-6653. doi: 10.7498/aps.57.6649
    [12] 袁艳红, 侯 洵, 高 恒. 超声处理对ZnO薄膜光致发光特性的影响. 物理学报, 2006, 55(1): 446-449. doi: 10.7498/aps.55.446
    [13] 徐静平, 李春霞, 吴海平. 4H-SiC n-MOSFET的高温特性分析. 物理学报, 2005, 54(6): 2918-2923. doi: 10.7498/aps.54.2918
    [14] 马忠元, 黄信凡, 朱 达, 李 伟, 陈坤基, 冯 端. 原位等离子体逐层氧化a-Si:H/SiO2多层膜的光致发光研究. 物理学报, 2004, 53(8): 2746-2750. doi: 10.7498/aps.53.2746
    [15] 徐大印, 刘彦平, 何志巍, 方泽波, 刘雪芹, 王印月. 多孔硅衬底上溅射沉积SiC:Tb薄膜的光致发光行为. 物理学报, 2004, 53(8): 2694-2698. doi: 10.7498/aps.53.2694
    [16] 吕红亮, 张义门, 张玉明. 4H-SiC pn结型二极管击穿特性中隧穿效应影响的模拟研究. 物理学报, 2003, 52(10): 2541-2546. doi: 10.7498/aps.52.2541
    [17] 杨林安, 张义门, 龚仁喜, 张玉明. 4H-SiC射频功率MESFET的自热效应分析. 物理学报, 2002, 51(1): 148-152. doi: 10.7498/aps.51.148
    [18] 张洪涛, 徐重阳, 邹雪城, 王长安, 赵伯芳, 周雪梅, 曾祥斌. 4H-SiC纳米薄膜的微结构及其光电性质研究. 物理学报, 2002, 51(2): 304-309. doi: 10.7498/aps.51.304
    [19] 徐昌发, 杨银堂, 刘莉. 4H-SiC MOSFET的温度特性研究. 物理学报, 2002, 51(5): 1113-1117. doi: 10.7498/aps.51.1113
    [20] 尹 民, J.C. KRUPA. 光谱探针法确定Eu3+:ThO2的格位对称性及选择激发下样品的光致发光研究. 物理学报, 2000, 49(9): 1859-1866. doi: 10.7498/aps.49.1859
计量
  • 文章访问数:  7422
  • PDF下载量:  652
  • 被引次数: 0
出版历程
  • 收稿日期:  2010-01-27
  • 修回日期:  2010-04-28
  • 刊出日期:  2011-01-15

/

返回文章
返回