电磁场调制下的应变黑磷烯带间光电导

柏文庆; 杨江涛; 杨翠红; 陈云云

doi:10.7498/aps.73.20240445

摘要

黑磷烯具有各向异性且独特的光电性能被广泛研究. 应变、电压等常用来调制能带结构, 进而调制其光电特性. 本文采用紧束缚近似哈密顿量, 考虑施加垂直磁场、电场、面内面外应变条件下的黑磷烯能带结构, 进一步利用Kubo公式研究了黑磷烯光电导率在多个调制因子下的特征, 并从能带结构进行了机理分析. 垂直磁场使能带劈裂, 产生多通道带间跃迁, 光电导率表现出多个峰. 随着面内拉伸应变增加能隙增加, 光电导峰位依赖于能隙. 而面外拉伸应变对能隙的调制区别于面内应变, 能隙表现出非单调变化. 电场通过带隙的变化, 调制光电导率峰值位置. 综合不同的调制因子, 能带和光电导表现出丰富的调制效果, 为研究基于黑磷烯光电器件的应用提供理论支持.

关键词:

Abstract

Black phosphorene (BP) has been widely investigated for its anisotropic and unique photoelectric properties. Strain, voltage and so on are commonly used to modulate the energy band structure and accordingly its photoelectric characteristics. In this study, we consider the energy band structure of BP in the vertical magnetic field, electric field, and in-plane/out-of-plane strains by using the tight-binding approximate Hamiltonian. The anisotropic frequency-dependent interband optical conductivity (IOC) of BP is investigated by using the Kubo formula in these modulation factors. Inherent asymmetry in band dispersion along the armchair (AC) direction and the zigzag (ZZ) direction leads to anisotropic IOC. The introduction of a vertical magnetic field induces band splitting, thereby generating multiple interband transition channels. In this case, the IOC along both the AC direction and the ZZ direction exhibits three peaks around the original peak position, and the magnitudes of the peaks are also modulated. With the increase of in-plane strain (from –20% to 20%), the band gap increases monotonically, and both the position and magnitude of the peaks vary with band gap changing. However, the band gap of BP undergoes a non-monotonic change under out-of-plane strain (from –20% to 20%), which is different from the change under in-plane strain. The band gap reaches a minimum value when a tensile strain of 12% is applied. Along the AC direction, the modulation of the IOC by in-plane strain is opposite to the modulation of out-of-plane strain (ε_z < 12%), indicating a competitive effect when triaxial strains are applied. Along the ZZ direction, in-plane strain primarily modulates the peak magnitude, while out-of-plane strain effectively modulates not only the peak position but also the peak magnitude obviously. The modulation of the IOC by forward and reverse electric fields are symmetrical. The coefficient for the peak position shift due to the vertical electric field is 1/2 in the AC direction and 1/10 in the ZZ direction. By integrating various modulation factors, we achieve versatile control over the energy band and IOC of BP, providing theoretical support for the application of BP in optoelectronic devices.

Keywords:

作者及机构信息

1.
南京信息工程大学物理与光电工程学院, 南京　210044

2.
南京信息工程大学, 江苏省大气海洋光电探测重点实验室, 南京　210044

3.
南京信息工程大学, 江苏省气象光子学与光电探测国际合作联合实验室, 南京　210044

通信作者: 杨翠红, chyang@nuist.edu.cn

基金项目: 国家自然科学基金(批准号: 11547030)资助的课题.

Authors and contacts

1.
School of Physics and Optoelectronic Engineering, Nanjing University of Information Science & Technology, Nanjing 210044, China

2.
Jiangsu Key Laboratory for Optoelectronic Detection of Atmosphere and Ocean, Nanjing University of Information Science & Technology, Nanjing 210044, China

3.
Jiangsu International Joint Laboratory on Meteorological Photonics and Optoelectronic Detection, Nanjing University of Information Science & Technology, Nanjing 210044, China

Corresponding author: Yang Cui-Hong, chyang@nuist.edu.cn

Funds: Project supported by the National Natural Science Foundation of China (Grant No. 11547030).

文章全文 : translate this paragraph

参考文献

[1]	Novoselov K S, Geim A K, Morozov S V, et al. 2004 Science 306 666 Google Scholar
[2]	Manzeli S, Ovchinnikov D, Pasquier D, Yazyev O V, Kis A 2017 Nat. Rev. Mater. 2 17033 Google Scholar
[3]	Li L K, Yu Y J, Ye G J, Ge Q Q, Ou X D, Wu H, Feng D L, Chen X H, Zhang Y B 2014 Nat. Nanotechnol. 9 372 Google Scholar
[4]	Liu H, Neal A T, Zhu Z, Luo Z, Xu X F, Tománek D, Ye P D 2014 ACS Nano 8 4033 Google Scholar
[5]	Xia F N, Wang H, Jia Y C 2014 Nat. Commun. 5 4458 Google Scholar
[6]	Jain A, McGaughey A J H 2015 Sci. Rep. 5 8501 Google Scholar
[7]	Qiao J S, Kong X H, Hu Z X, Yang F, Ji W 2014 Nat. Commun. 5 4475 Google Scholar
[8]	Ezawa M 2014 New J. Phys. 16 115004 Google Scholar
[9]	Tran V, Soklaski R, Liang Y F, Yang L 2014 Phys. Rev. B 89 235319 Google Scholar
[10]	Li L K, Kim J, Jin C H, et al. 2017 Nat. Nanotechnol. 12 21 Google Scholar
[11]	Kim J, Baik S S, Ryu S H, Sohn Y, Park S, Park B G, Denlinger J, Yi Y, Choi H J, Kim K S 2015 Science 349 723 Google Scholar
[12]	Peng X H, Wei Q, Copple A 2014 Phys. Rev. B 90 085402 Google Scholar
[13]	Rodin A S, Carvalho A, Castro Neto A H 2014 Phys. Rev. Lett. 112 176801 Google Scholar
[14]	Fei R, Yang L 2014 Nano Lett. 14 2884 Google Scholar
[15]	Dai J, Zeng X C 2014 J. Phys. Chem. Lett. 5 1289 Google Scholar
[16]	Chen X L, Lu X B, Deng B C, et al. 2017 Nat. Commun. 8 1672 Google Scholar
[17]	Li L K, Yang F Y, Ye G J, et al. 2016 Nat. Nanotechnol. 11 593 Google Scholar
[18]	Pereira Jr J M, Katsnelson M I 2015 Phys. Rev. B 92 075437 Google Scholar
[19]	Zhou X Y, Lou W K, Zhai F, Chang K 2015 Phys. Rev. B 92 165405 Google Scholar
[20]	Phuong L T T, Phong T C, Yarmohammadi M 2020 Sci. Rep. 10 9201 Google Scholar
[21]	Keshtan M A M, Esmaeilzadeh M 2015 J. Phys. D: Appl. Phys. 48 485301 Google Scholar
[22]	Wang Y, Guo Y L, Wang Z K, et al. 2021 ACS Nano 15 12069 Google Scholar
[23]	Wang Y, Xu W, Fu L, et al. 2023 ACS Appl. Mater. Interfaces 15 54797 Google Scholar
[24]	Wang Y, Xu W, Yang D Y, et al. 2023 ACS Nano 17 24320 Google Scholar
[25]	Li P K, Appelbaum I 2014 Phys. Rev. B 90 115439 Google Scholar
[26]	Le P T T, Yarmohammadi M 2019 J. Magn. Magn. Mater. 491 165629 Google Scholar
[27]	Rudenko A N, Katsnelson M I 2014 Phys. Rev. B 89 201408 Google Scholar
[28]	Yang C H, Zhang J Y, Wang G X, Zhang C 2018 Phys. Rev. B 97 245408 Google Scholar
[29]	Jiang J W, Park H S 2015 Phys. Rev. B 91 235118 Google Scholar
[30]	Khang P D, Davoudiniya M, Phuong L T T, Phong T C, Yarmohammadi M 2019 Phys. Chem. Chem. Phys. 21 15133 Google Scholar
[31]	Yang C H, Zhang J Y, Wieser R, Xu W 2022 J. Phys. D: Appl. Phys. 55 085103 Google Scholar
[32]	Le P T T, Mirabbaszadeh K, Yarmohammadi M 2019 J. Appl. Phys. 125 193101 Google Scholar

施引文献

图 1 黑磷烯晶格结构示意图　(a) 三维; (b) 二维

Fig. 1. Schematic diagram of lattice structure of BP: (a) Three-dimensional; (b) two-dimensional.

下载: 全尺寸图片幻灯片

图 2 黑磷烯能带示意图　(a) 磁场下; (b) 电场下; (c) x轴应变下

Fig. 2. Energy band structure of BP in the presence: (a) Magnetic field; (b) electric field; (c) x-axis strain.

下载: 全尺寸图片幻灯片

图 3 同时施加磁场和应变下的黑磷烯带隙(虚线1.52对应的是本征带隙的位置)　(a) 施加x轴应变 ; (b) 施加y轴应变; (c) 施加z轴应变

Fig. 3. Bandgap of BP in the presence of the magnetic field and strain applied along (Dashed line corresponds to the position of the intrinsic band gap): (a) x-axis; (b) y-axis; (c) z-axis.

下载: 全尺寸图片幻灯片

图 4 同时施加电场和应变下的黑磷烯带隙(虚线1.52对应的是本征带隙的位置)　(a) 施加x轴应变; (b) 施加y轴应变; (c) 施加z轴应变

Fig. 4. Bandgap of BP in the presence of the electric field and strain applied along (Dashed line corresponds to the position of the intrinsic band gap): (a) x-axis; (b) y-axis; (c) z-axis.

下载: 全尺寸图片幻灯片

图 5 AC方向的带间光电导率在不同x轴应变条件下随入射光能量的变化　(a), (c) 不同磁场下的光电导实部; (b), (d) 不同磁场下的光电导虚部. 黑色、红色和蓝色曲线分别表示无应变、压缩应变和拉伸应变下的结果

Fig. 5. Interband optical conductivity along the AC direction as a function of the incident photon energy at different x-axial strain: (a), (c) Real part under different magnetic fields; (b), (d) the imaginary part under different magnetic fields. Black, red, and blue curves represent the results with no strain, compressive strain, and tensile strain, respectively.

下载: 全尺寸图片幻灯片

图 8 带间光电导率实部在不同z轴应变条件下随入射光能量的变化　(a), (c)不同磁场下AC方向的结果; (b), (d)不同磁场下ZZ方向的结果

Fig. 8. Real part of the interband optical conductivity as a function of the incident photon energy at different z-axial strain: (a), (c) Results along the AC direction under different magnetic fields; (b), (d) results along the ZZ direction under different magnetic fields.

下载: 全尺寸图片幻灯片

图 7 带间光电导率实部在不同y轴应变条件下随入射光能量的变化　(a), (c) 不同磁场下AC方向的结果; (b), (d)不同磁场下ZZ方向的结果

Fig. 7. Real part of the interband optical conductivity as a function of the incident photon energy at different y-axial strain: (a), (c) Results along the AC direction under different magnetic fields; (b), (d) the results along the ZZ direction under different magnetic fields.

下载: 全尺寸图片幻灯片

图 6 ZZ方向的带间光电导率在不同x轴应变条件下随入射光能量的变化　(a), (c) 不同磁场下的光电导实部; (b), (d) 不同磁场下的光电导虚部

Fig. 6. Interband optical conductivity along the ZZ direction as a function of the incident photon energy at different x-axial strain: (a), (c) Real part under different magnetic fields; (b), (d) the imaginary part under different magnetic fields.

下载: 全尺寸图片幻灯片

图 9 带间光电导率实部在三轴应变条件下随入射光能量的变化　(a), (c)不同磁场下AC方向的结果; (b), (d)不同磁场下ZZ方向的结果

Fig. 9. Real part of the interband optical conductivity as a function of the incident photon energy at different triaxial strains: (a), (c) Results along the AC direction under different magnetic fields; (b), (d) the results along the ZZ direction under different magnetic fields.

下载: 全尺寸图片幻灯片

图 10 带间光电导率实部在三轴应变条件下随入射光能量的变化　(a), (c) 不同电场下AC方向的结果; (b), (d) 不同电场下ZZ方向的结果

Fig. 10. Real part of the interband optical conductivity as a function of the incident photon energy at different triaxial strains: (a), (c) Results along the AC direction under different electric fields; (b), (d) the results along the ZZ direction under different electric fields.

下载: 全尺寸图片幻灯片

下载: 全尺寸图片幻灯片

表 1 黑磷烯的跳变参数与晶格常数^[27,28]

Table 1. Hopping energy and lattice parameter of BP^[27,28].

t_i 具体数值/eV a_i 具体数值/Å

t₁ –1.22 a₁ 1.41763

t₂ 3.665 a₂ 0.79732

t₃ –0.205 a₃ 3.01227

t₄ –0.105 a₄ 2.21468

t₅ –0.055 a₅ 3.63258

下载: 导出CSV

表 2 黑磷烯的应变系数^[29,30]

Table 2. Strain coefficient of BP^[29,30].

γ $ \alpha _{1}^\gamma $ $ \alpha _{2}^\gamma $ $ \alpha _{3}^\gamma $ $ \alpha _{4}^\gamma $ $ \alpha _{5}^\gamma $

x 0.4460 0.0992 0.7505 0.3976 0.7530
y 0.5571 0 0.2461 0.2280 0
z 0 0.9052 0 0.3722 0.2538

下载: 导出CSV

[1]	Novoselov K S, Geim A K, Morozov S V, et al. 2004 Science 306 666 Google Scholar
[2]	Manzeli S, Ovchinnikov D, Pasquier D, Yazyev O V, Kis A 2017 Nat. Rev. Mater. 2 17033 Google Scholar
[3]	Li L K, Yu Y J, Ye G J, Ge Q Q, Ou X D, Wu H, Feng D L, Chen X H, Zhang Y B 2014 Nat. Nanotechnol. 9 372 Google Scholar
[4]	Liu H, Neal A T, Zhu Z, Luo Z, Xu X F, Tománek D, Ye P D 2014 ACS Nano 8 4033 Google Scholar
[5]	Xia F N, Wang H, Jia Y C 2014 Nat. Commun. 5 4458 Google Scholar
[6]	Jain A, McGaughey A J H 2015 Sci. Rep. 5 8501 Google Scholar
[7]	Qiao J S, Kong X H, Hu Z X, Yang F, Ji W 2014 Nat. Commun. 5 4475 Google Scholar
[8]	Ezawa M 2014 New J. Phys. 16 115004 Google Scholar
[9]	Tran V, Soklaski R, Liang Y F, Yang L 2014 Phys. Rev. B 89 235319 Google Scholar
[10]	Li L K, Kim J, Jin C H, et al. 2017 Nat. Nanotechnol. 12 21 Google Scholar
[11]	Kim J, Baik S S, Ryu S H, Sohn Y, Park S, Park B G, Denlinger J, Yi Y, Choi H J, Kim K S 2015 Science 349 723 Google Scholar
[12]	Peng X H, Wei Q, Copple A 2014 Phys. Rev. B 90 085402 Google Scholar
[13]	Rodin A S, Carvalho A, Castro Neto A H 2014 Phys. Rev. Lett. 112 176801 Google Scholar
[14]	Fei R, Yang L 2014 Nano Lett. 14 2884 Google Scholar
[15]	Dai J, Zeng X C 2014 J. Phys. Chem. Lett. 5 1289 Google Scholar
[16]	Chen X L, Lu X B, Deng B C, et al. 2017 Nat. Commun. 8 1672 Google Scholar
[17]	Li L K, Yang F Y, Ye G J, et al. 2016 Nat. Nanotechnol. 11 593 Google Scholar
[18]	Pereira Jr J M, Katsnelson M I 2015 Phys. Rev. B 92 075437 Google Scholar
[19]	Zhou X Y, Lou W K, Zhai F, Chang K 2015 Phys. Rev. B 92 165405 Google Scholar
[20]	Phuong L T T, Phong T C, Yarmohammadi M 2020 Sci. Rep. 10 9201 Google Scholar
[21]	Keshtan M A M, Esmaeilzadeh M 2015 J. Phys. D: Appl. Phys. 48 485301 Google Scholar
[22]	Wang Y, Guo Y L, Wang Z K, et al. 2021 ACS Nano 15 12069 Google Scholar
[23]	Wang Y, Xu W, Fu L, et al. 2023 ACS Appl. Mater. Interfaces 15 54797 Google Scholar
[24]	Wang Y, Xu W, Yang D Y, et al. 2023 ACS Nano 17 24320 Google Scholar
[25]	Li P K, Appelbaum I 2014 Phys. Rev. B 90 115439 Google Scholar
[26]	Le P T T, Yarmohammadi M 2019 J. Magn. Magn. Mater. 491 165629 Google Scholar
[27]	Rudenko A N, Katsnelson M I 2014 Phys. Rev. B 89 201408 Google Scholar
[28]	Yang C H, Zhang J Y, Wang G X, Zhang C 2018 Phys. Rev. B 97 245408 Google Scholar
[29]	Jiang J W, Park H S 2015 Phys. Rev. B 91 235118 Google Scholar
[30]	Khang P D, Davoudiniya M, Phuong L T T, Phong T C, Yarmohammadi M 2019 Phys. Chem. Chem. Phys. 21 15133 Google Scholar
[31]	Yang C H, Zhang J Y, Wieser R, Xu W 2022 J. Phys. D: Appl. Phys. 55 085103 Google Scholar
[32]	Le P T T, Mirabbaszadeh K, Yarmohammadi M 2019 J. Appl. Phys. 125 193101 Google Scholar

[1]	李永宁, 谢逸群, 王音. 二维铁电In₂Se₃/InSe垂直异质结能带的应力调控. 物理学报, 2021, 70(22): 227701. doi: 10.7498/aps.70.20211158
[2]	卫琳, 刘贵立, 王家鑫, 穆光耀, 张国英. 拉伸形变及电场作用对黑磷烯吸附Si原子电学特性影响的密度泛函理论研究. 物理学报, 2021, 70(21): 216301. doi: 10.7498/aps.70.20210812
[3]	丁燕, 钟粤华, 郭俊青, 卢毅, 罗昊宇, 沈云, 邓晓华. 黑磷各向异性拉曼光谱表征及电学特性. 物理学报, 2021, 70(3): 037801. doi: 10.7498/aps.70.20201271
[4]	张国英, 焦兴强, 刘业舒, 张安国, 孟春雪. 缺陷与掺杂共存的黑磷烯甲醛传感行为的电子理论. 物理学报, 2020, 69(23): 237101. doi: 10.7498/aps.69.20200990
[5]	蔡成欣, 陈韶赓, 王学梅, 梁俊燕, 王兆宏. 各向异性三维非对称双锥五模超材料的能带结构及品质因数. 物理学报, 2020, 69(13): 134302. doi: 10.7498/aps.69.20200364
[6]	马浩浩, 张显斌, 魏旭艳, 曹佳萌. 非金属元素掺杂二硒化钨/石墨烯异质结对其肖特基调控的理论研究. 物理学报, 2020, 69(11): 117101. doi: 10.7498/aps.69.20200080
[7]	张忠强, 刘汉伦, 范晋伟, 丁建宁, 程广贵. 黑磷纳米通道内压力驱动流体流动特性. 物理学报, 2019, 68(17): 170202. doi: 10.7498/aps.68.20190531
[8]	魏相飞, 何锐, 张刚, 刘向远. InAs/GaSb量子阱中太赫兹光电导特性. 物理学报, 2018, 67(18): 187301. doi: 10.7498/aps.67.20180769
[9]	卢敏, 黄惠莲, 余冬海, 刘维清, 魏望和. 不同晶面银纳米晶高温熔化的各向异性. 物理学报, 2015, 64(10): 106101. doi: 10.7498/aps.64.106101
[10]	陈小兰, 张耘, 冉启义. 掺铁铌酸锂晶体的光电导衰减特性研究. 物理学报, 2013, 62(3): 037201. doi: 10.7498/aps.62.037201
[11]	董占民, 孙红三, 许佳, 李一, 孙家林. 宏观长Ag2S纳米线簇的制备及其温度电导特性和光电导特性. 物理学报, 2011, 60(7): 077304. doi: 10.7498/aps.60.077304
[12]	孟繁义, 吴群, 傅佳辉, 顾学迈, 李乐伟. 三维各向异性超常媒质交错结构的亚波长谐振特性研究. 物理学报, 2008, 57(10): 6213-6220. doi: 10.7498/aps.57.6213
[13]	王志军, 王锦程, 杨根仓. 各向异性作用下合金定向凝固界面稳定性的渐近分析. 物理学报, 2008, 57(2): 1246-1253. doi: 10.7498/aps.57.1246
[14]	周建华, 刘虹遥, 罗海陆, 文双春. 各向异性超常材料中倒退波的传播研究. 物理学报, 2008, 57(12): 7729-7736. doi: 10.7498/aps.57.7729
[15]	杨宏伟, 袁洪, 陈如山, 杨阳. 各向异性磁化等离子体的SO-FDTD算法. 物理学报, 2007, 56(3): 1443-1446. doi: 10.7498/aps.56.1443
[16]	翁紫梅, 陈浩. 单离子各向异性影响下的一维铁磁链中的孤子. 物理学报, 2007, 56(4): 1911-1918. doi: 10.7498/aps.56.1911
[17]	穆全全, 刘永军, 胡立发, 李大禹, 曹召良, 宣丽. 光谱型椭偏仪对各向异性液晶层的测量. 物理学报, 2006, 55(3): 1055-1060. doi: 10.7498/aps.55.1055
[18]	张世斌, 孔光临, 徐艳月, 王永谦, 刁宏伟, 廖显伯. 微量硼掺杂非晶硅的瞬态光电导衰退及其光致变化. 物理学报, 2002, 51(1): 111-114. doi: 10.7498/aps.51.111
[19]	张德恒, 刘云燕, 张德骏. 用MOCVD方法制备的n型GaN薄膜紫外光电导. 物理学报, 2001, 50(9): 1800-1804. doi: 10.7498/aps.50.1800
[20]	袁先漳, 裴慧元, 陆卫, 李宁, 史国良, 方家熊, 沈学础. Zn0.04Cd0.96Te中深能级的红外光电导谱研究. 物理学报, 2001, 50(4): 775-778. doi: 10.7498/aps.50.775

计量

文章访问数: 1152
PDF下载量: 37
被引次数: 0

姓名
邮箱
手机号码
标题
留言内容
验证码

搜索

留言板

电磁场调制下的应变黑磷烯带间光电导