In the present work, the nanocrystalline CeB6 and SmB6 powder are successfully prepared by evaporative condensation method. The phase composition, grain morphology, microstructure and optical absorption properties for each of the prepared powders are studied systematically. The results show that the main phase of nanocrystalline CeB6 powder and SmB6 powder are both composed of CaB6-type cubic structure with space group of Pm-3m. The scanning electron microscope results show that the synthesized CeB6 and SmB6 nanoparticles display an spherical morphology with an average grain size of 50 nm. The high resolution transmission electron microscopy observation results show that there exist many intrinsic crystal defects in nanocrystalline SmB6, such as lattice distortions or edge dislocations, due to the high volatility characteristic of Sm atom in the condensation (crystallization) process. The optical absorption results show that the absorption valley of nanocrystalline CeB6 and SmB6 are respectively located at 599 nm and 632 nm, indicating the high transparency characteristic of visible light. To further qualitatively explain the difference in optical absorption mechanism between CeB6 and SmB6, the first principle calculations are employed to calculate their band structures, densities of states, optical absorption energy, and plasma resonance frequency energy. The calculation results show that there is an electron band crossing the Fermi energy for both CeB6 and SmB6, indicating their typical conductor behaviors. The upmost valence band of CeB6 and SmB6 are composed of B-2p and B-2s states, and their bottommost conduction bands are mainly composed of Ce-4f, Ce-5d, Sm-4f, Sm-5d, B-2p and B-2s states. In addition, the volume plasma of carrier electrons can be described in the electron energy-loss function. The peak position in the low energy region of the loss function corresponds to the relevant plasma frequency. As a result, the calculated low energy loss function of CeB6 and SmB6 are 1.96 eV and 1.5 eV, respectively. Moreover, the calculated absorption valley of CeB6 and SmB6 respectively appear at 639 nm and 800 nm, which are in good accordance with the experimental results. Therefore, as an efficient optical absorption materials, the nanocrystalline CeB6 and SmB6 should open the way to extending the optical applications of rare-earth hexaborides.
-
Keywords:
- evaporative condensation method /
- rare earth hexaboride /
- nanocrystalline material /
- optical absorption
[1] Bao L H, Chao L M, Wei W, Tegus O 2014 Mater. Lett. 139 187
[2] 包黎红, 那仁格日乐, 特古斯, 张忻, 张久兴 2013 物理学报 62 196105
Google Scholar
Bao L H, Narengerile, Tegus O, Zhang X, Zhang J X 2013 Acta Phys. Sin. 62 196105
Google Scholar
[3] 刘洪亮, 张忻, 王杨, 肖怡新, 张久兴 2018 物理学报 67 048101
Google Scholar
Liu H L, Zhang X, Wang Y, Xiao Y X, Zhang J X 2018 Acta Phys. Sin. 67 048101
Google Scholar
[4] 王杨, 张忻, 张久兴, 刘洪亮, 江浩, 李录录 2016 无机化学学报 31 797
Wang Y, Zhang X, Zhang J X, Liu H L, Jiang H, Li L L 2016 J. Inorg. Mater. 31 797
[5] 包黎红, 张久兴, 周身林, 张宁 2011 物理学报 60 106501
Google Scholar
Bao L H, Zhang J X, Zhou S L, Zhang N 2011 Acta Phys. Sin. 60 106501
Google Scholar
[6] 包黎红, 朝洛蒙, 伟伟, 特古斯 2015 物理学报 64 096104
Google Scholar
Bao L H, Chao L M, Wei W, Tegus O 2015 Acta Phys. Sin. 64 096104
Google Scholar
[7] 韩伟 2017 博士学位论文 (广州: 华南理工大学)
Han W 2017 Ph. D. Dissertation (Guangzhou: South China University of Technology) (in Chinese)
[8] 吴锦雷, 刘盛 2003 贵金属 24 1
Google Scholar
Wu J L, Liu S 2003 Precious Metals 24 1
Google Scholar
[9] 周爱秋, 许效红, 姚伟峰, 曾凡亮, 宋邦强 2004 化学物理学报 3 305
Google Scholar
Zhou A Q, Xu X H, Yao W F, Zeng F L, Song B Q 2004 Chin. J. Chem. Phys. 3 305
Google Scholar
[10] Chao L M, Bao L H, Shi J J, Wei W, Tegus O, Zhang Z D 2015 J. Alloys Compd. 622 618
Google Scholar
[11] Chen M C, Lin Z W, Ling M H 2016 ACS Nano 10 93
Google Scholar
[12] Bai L, Ma N, Liu F L 2009 Physica B 404 4086
Google Scholar
[13] Kim S S, Na S I, Jo J, Kim D Y, Nah Y C 2008 Appl. Phys. Lett. 93 073307
Google Scholar
[14] Nedyalkov N N, Nakajima Y, Takami A, Koleva M, Karashanova D, Terakawa M 2016 Opt. Laser Technol. 79 179
Google Scholar
[15] Takeda H, Kuno H, Adachi K 2008 J. Am. Ceram. Soc. 91 2897
Google Scholar
[16] Sato Y, Terauchi M, Mukai M, Kaneyama T, Adachi K 2011 Ultramicroscopy 111 1381
Google Scholar
[17] 肖立华, 苏玉长, 刘仪柯, 冉景榆, 杨涛, 彭平 2017 功能材料信息 3 19
Xiao L H, Su Y C, Liu Y K, Ran J Y, Yang T, Peng P 2017 Func. Mate. Info. 3 19
[18] Zeng X S, Ye Y X, Zou S L, Gou Q D, Wen Y F, Ou P 2017 Crystals 7 320
Google Scholar
[19] Kimura S, Nanba T, Kunii S, Suzuki T, Kasuya T 1990 Solid State Commun. 75 717
Google Scholar
[20] 包黎红, 陶如玉, 特古斯, 黄颖楷, 冷华倩, Anne de Visser 2017 物理学报 66 186102
Google Scholar
Bao L H, Tao R Y, Tegus O, Huang Y K, Leng H Q, Anne de Visser 2017 Acta Phys. Sin. 66 186102
Google Scholar
-
图 1 (a) 蒸发冷凝实验示意图; (b)形成稳定熔区照片
Figure 1. (a) Sketch of evaporation-condensation method; (b) photo of stable molten zone.
图 2 (a)和(b)原料CeB6和SmB6粗粉的FESEM照片; (c)和(d)蒸发冷凝法制备的纳米CeB6和SmB6的FESEM照片; (e)和(f)为纳米CeB6和SmB6的XRD图谱
Figure 2. (a), (b) FESEM image of precursor powder CeB6 and SmB6; (c), (d) FESEM image of CeB6 and SmB6 nanocrystals prepared by evaporation condensation; (e), (f) XRD spectra of CeB6 and SmB6 nanocrystals prepared by evaporation condensation.
图 3 (a) 纳米CeB6的TEM照片; 单颗粒纳米CeB6的(b) HRTEM照片、(c) 快速傅里叶变换照片、(d) HAADF-STEM分析, 以及相应(e), (f) Ce和B的元素分布照片
Figure 3. (a) TEM image of nanocrystalline CeB6; (b) HRTEM image, (c) fast Fourier transform pattern, (d) HAADF-STEM, and (e), (f) elemental distribution of Ce and B for single particle of nanocrystalline CeB6.
图 4 (a), (c) 纳米CeB6和SmB6的HRTEM照片; (b), (d) 反快速傅里叶照片
Figure 4. (a), (c) HRTEM images of nanocrystalline CeB6 and SmB6; (b), (d) inverse fast Fourier transform image of nanocrystalline CeB6 and SmB6.
图 5 纳米CeB6和SmB6光吸收图谱
Figure 5. Optical absorption spectra of nanocrystalline CeB6 and SmB6.
图 6 第一性原理计算能带结构图 (a) CeB6; (b) SmB6
Figure 6. First-principle calculation results of band structure: (a) CeB6; (b) SmB6.
图 7 第一性原理计算态密度曲线 (a) CeB6; (b) SmB6
Figure 7. First-principle calculation results of total density of states (TDOS) and partial density of states (PDOS) curves: (a) CeB6; (b) SmB6.
图 8 (a) CeB6和(b) SmB6的能量损失函数曲线
Figure 8. Energy loss function curves of (a) CeB6 and (b) SmB6.
图 9 第一性原理计算光吸收曲线 (a) CeB6; (b) SmB6
Figure 9. First principle calculation results of optical absorption curves: (a) CeB6; (b) SmB6.
-
[1] Bao L H, Chao L M, Wei W, Tegus O 2014 Mater. Lett. 139 187
[2] 包黎红, 那仁格日乐, 特古斯, 张忻, 张久兴 2013 物理学报 62 196105
Google Scholar
Bao L H, Narengerile, Tegus O, Zhang X, Zhang J X 2013 Acta Phys. Sin. 62 196105
Google Scholar
[3] 刘洪亮, 张忻, 王杨, 肖怡新, 张久兴 2018 物理学报 67 048101
Google Scholar
Liu H L, Zhang X, Wang Y, Xiao Y X, Zhang J X 2018 Acta Phys. Sin. 67 048101
Google Scholar
[4] 王杨, 张忻, 张久兴, 刘洪亮, 江浩, 李录录 2016 无机化学学报 31 797
Wang Y, Zhang X, Zhang J X, Liu H L, Jiang H, Li L L 2016 J. Inorg. Mater. 31 797
[5] 包黎红, 张久兴, 周身林, 张宁 2011 物理学报 60 106501
Google Scholar
Bao L H, Zhang J X, Zhou S L, Zhang N 2011 Acta Phys. Sin. 60 106501
Google Scholar
[6] 包黎红, 朝洛蒙, 伟伟, 特古斯 2015 物理学报 64 096104
Google Scholar
Bao L H, Chao L M, Wei W, Tegus O 2015 Acta Phys. Sin. 64 096104
Google Scholar
[7] 韩伟 2017 博士学位论文 (广州: 华南理工大学)
Han W 2017 Ph. D. Dissertation (Guangzhou: South China University of Technology) (in Chinese)
[8] 吴锦雷, 刘盛 2003 贵金属 24 1
Google Scholar
Wu J L, Liu S 2003 Precious Metals 24 1
Google Scholar
[9] 周爱秋, 许效红, 姚伟峰, 曾凡亮, 宋邦强 2004 化学物理学报 3 305
Google Scholar
Zhou A Q, Xu X H, Yao W F, Zeng F L, Song B Q 2004 Chin. J. Chem. Phys. 3 305
Google Scholar
[10] Chao L M, Bao L H, Shi J J, Wei W, Tegus O, Zhang Z D 2015 J. Alloys Compd. 622 618
Google Scholar
[11] Chen M C, Lin Z W, Ling M H 2016 ACS Nano 10 93
Google Scholar
[12] Bai L, Ma N, Liu F L 2009 Physica B 404 4086
Google Scholar
[13] Kim S S, Na S I, Jo J, Kim D Y, Nah Y C 2008 Appl. Phys. Lett. 93 073307
Google Scholar
[14] Nedyalkov N N, Nakajima Y, Takami A, Koleva M, Karashanova D, Terakawa M 2016 Opt. Laser Technol. 79 179
Google Scholar
[15] Takeda H, Kuno H, Adachi K 2008 J. Am. Ceram. Soc. 91 2897
Google Scholar
[16] Sato Y, Terauchi M, Mukai M, Kaneyama T, Adachi K 2011 Ultramicroscopy 111 1381
Google Scholar
[17] 肖立华, 苏玉长, 刘仪柯, 冉景榆, 杨涛, 彭平 2017 功能材料信息 3 19
Xiao L H, Su Y C, Liu Y K, Ran J Y, Yang T, Peng P 2017 Func. Mate. Info. 3 19
[18] Zeng X S, Ye Y X, Zou S L, Gou Q D, Wen Y F, Ou P 2017 Crystals 7 320
Google Scholar
[19] Kimura S, Nanba T, Kunii S, Suzuki T, Kasuya T 1990 Solid State Commun. 75 717
Google Scholar
[20] 包黎红, 陶如玉, 特古斯, 黄颖楷, 冷华倩, Anne de Visser 2017 物理学报 66 186102
Google Scholar
Bao L H, Tao R Y, Tegus O, Huang Y K, Leng H Q, Anne de Visser 2017 Acta Phys. Sin. 66 186102
Google Scholar
DownLoad:
Catalog
Metrics
- Abstract views: 8192
- PDF Downloads: 73
- Cited By: 0