Numerical simulation of strong coupling between silver nanorod and dielectric layer detected by electron energy loss spectrum

Zhao Shi-Hang; Zhang Yuan; Lü Si-Yuan; Cheng Shao-Bo; Zheng Chang-Lin; Wang Lu-Xia

doi:10.7498/aps.71.20220194

Abstract

The strong coupling phenomenon between surface plasmons and quantum emitters has received extensive attention in recent years. It is usually studied by the far-field spectral detection method such as scattering, absorption, and fluorescence. In the electron energy loss spectroscopy (EELS), highly focused electron beams are used for implementing the local detection on a sub-nanometer scale, which can be more effective to study strong coupling. In this work, the electron energy loss spectrum of silver nanorods, dielectric materials and their composite core-shell nanostructures are theoretically simulated respectively, and the energy and mode characteristics of surface plasmons on the silver nanorods and the excitation characteristics of dielectric materials are obtained. The electron energy loss spectrum of surface plasmon is basically consistent with the related experimental result. Rabi splitting of spectral peaks is observed in the electron energy loss spectra of the above composite structures, and the effect of Ag nanorod size on Rabi splitting is explored. The strong coupling between the radiative dipolar and non-radiative higher-order plasmon with the excitation of the dielectric materials in the infrared and visible band is discussed, and the corresponding dispersion relation is analyzed with the coupled oscillator mode. Furthermore, the plexciton caused by strong coupling are discussed from the perspective of spatial distribution of loss spectrum imaging. Our study builds the basis for further theoretical study, and can guide the further experimental research.

Keywords:

Authors and contacts

1.
Institute of Theoretical Physics, Department of Physics, School of Mathematics and Physics, University of Science and Technology Beijing, Beijing 100083, China
2.
Key Laboratory of Material Physics Ministry of Education, School of Physics, Zhengzhou University, Zhengzhou 450052, China
3.
State Key Laboratory of Surface Physics, Department of Physics, Fudan University, Shanghai 200438, China

Corresponding author: Zhang Yuan, yzhuaudipc@zzu.edu.cn ; Wang Lu-Xia, luxiawang@sas.ustb.edu.cn

Funds: Project supported by the National Natural Science Foundation of China (Grant Nos. 21961132023, 12004344, 11774026, 61871134).

[1]	Hamann H F, Kuno M, Gallagher A, Nesbitt D J 2001 J. Chem. Phys. 114 8596 Google Scholar
[2]	Hartschuh A, Sanchez E J, Xie X S, Novotny L 2003 Phys. Rev. Lett. 90 095503 Google Scholar
[3]	Fleischmann M, Hendra P J, McQuillan A J 1974 Chem. Phys. Lett. 26 163 Google Scholar
[4]	Nie S, Emory S R 1997 Science 275 1102 Google Scholar
[5]	Osawa M, Ikeda 1991 J. Phys. Chem. 95 9914 Google Scholar
[6]	Hirsch L, Stafford R J, Bankson J A, Sershen 2003 Proc. Natl. Acad. Sci. 100 13549 Google Scholar
[7]	Cao Y C, Jin R, Mirkin C A 2002 Science 297 1536 Google Scholar
[8]	Rossouw D, Couillard M, Vickery J, Kumacheva E, Botton G A 2011 Nano Lett. 11 1499 Google Scholar
[9]	Aizpurua J, Hanarp P, Sutherland D S, Käll M, Bryant G W, García de Abajo F J 2003 Phys. Rev. Lett. 90 057401 Google Scholar
[10]	Yankovich A B, Munkhbat B, Baranov D G, Cuadra J, Olsén E, Lourenço-Martins H, Tizei L H G, Kociak M, Eva Olsson, Shegai T 2019 Nano Lett. 19 8171 Google Scholar
[11]	Zanfrognini M, Rotunno E, Frabboni S, Sit A, Karimi E, Hohenester U, Grillo V 2019 ACS Photon. 6 620 Google Scholar
[12]	Benz F, Schmidt M K, Dreismann A, Chikkaraddy R, Zhang Y, Demetriadou A, Carnegie C, Ohadi H, De Nijs B, Esteban R, Aizpurua J, Baumberg J J 2016 Science 354 726 Google Scholar
[13]	Lee J, Tallarida N, Chen X, Liu P, Jensen L, Apkarian V A 2017 ACS Nano 11 11466 Google Scholar
[14]	Carnegie C, Griffiths J, de Nijs B, Readman C, Chikkaraddy R, Deacon W M, Zhang Y, Szabó I, Rosta E, Aizpurua J, Baumberg J J 2018 J. Phys. Chem. Lett. 9 7146 Google Scholar
[15]	Urbieta M, Barbry M, Zhang Y, Koval P, Sánchez-Portal D, Zabala N, Aizpurua J 2018 ACS Nano 12 585 Google Scholar
[16]	Doppagne B, Neuman T, Soria-Martinez R, López L E P, Bulou H, Romeo M, Berciaud S, Scheurer F, Aizpurua J, Schull G 2020 Nature Nanotechnol. 15 207 Google Scholar
[17]	Nan F, Zhang Y F, Li X G, Zhang X T, Hang Li H, Zhang X H, Jiang R B, Wang J F, Zhang W, Li Zhou, Wang J H, Wang Q Q, Zhang Z Y 2015 Nano Lett. 15 2705 Google Scholar
[18]	Guo Y Z, Zhu G D, Fanga Y 2021 J. Appl. Phys. 129 043104 Google Scholar
[19]	Qin J, Chen Y H, Zhang Z P, Zhang Y F, Blaikie R J, Ding B Y, Qiu M 2020 Phys. Rev. Lett. 124 063902 Google Scholar
[20]	Li P N, Yang X S, Maß T W W, Hanss J, Lewin M, Ann-Katrin U Michel, Wuttig M, Taubner T 2016 Nature Mater. 15 870 Google Scholar
[21]	Hutchison J A, Schwartz T, Genet C, Devaux E, Ebbesen T W 2012 Angew. Chem. 51 1592 Google Scholar
[22]	Törmä P, Barnes W L 2015 Rep. Prog. Phys. 78 013901 Google Scholar
[23]	Konečná A, Neuman T, Aizpurua J, Hillenbrand R 2018 ACS Nano 12 4775 Google Scholar
[24]	Zhang Y, Meng Q S, Zhang L, Luo Y, Yu Y J, Yang B, Zhang Y, Esteban R, Aizpurua J, Luo Y, Yang J L, Dong Z C, Hou J G 2017 Nat. Commun. 8 15225 Google Scholar
[25]	Tizei L H G, Mkhitaryan V, Lourenço-Martins H, et al. 2020 Nano Lett. 20 2973 Google Scholar
[26]	Liu H H, Gage T E, Singh P, Jaiswal A, Schaller R D, Tang J, Park S T, Gray S K, Arslan I 2021 Nano Lett. 21 5842 Google Scholar
[27]	Wei J K, Jiang N, Xu J, Bai X D, Liu J Y 2015 Nano Lett. 15 5926 Google Scholar
[28]	Lagos M J, Batson P E, Lyu Z, Hohenester U 2021 ACS Photon. 8 1293 Google Scholar
[29]	Zouros G P, Kolezas G D, N Asger Mortensen, Christos Tserkezis 2020 Phys. Rev. B 101 085416 Google Scholar
[30]	Goodman J J, Draine B T, Flatau P J 1991 Opt. Lett. 16 1198 Google Scholar
[31]	Yee K S 1966 IEEE T. Antenn. Propag. 14 302 Google Scholar
[32]	de Abajo F J G, Howie A 2002 Phys. Rev. B 65 115418 Google Scholar
[33]	Hohenester U 2014 Computer Phys. Commun. 185 1177 Google Scholar
[34]	Hohenester U, Trügler A 2012 Computer Phys. Commun. 183 370 Google Scholar
[35]	Johnson P, Christy R 1972 Phys. Rev. B 6 4370 Google Scholar
[36]	Maomao Zhang, Xueyi Shi, Xinyu Mu, Luxia Wang, Kun Gao 2021 Appl. Phys. Lett. 118 133301 Google Scholar
[37]	Hachtel J A, Huang J S, Popovs I, Jansone-Popova S, Keum J K, Jakowski J, Lovejoy T C, Dellby N, Krivanek O L, Idrobo J C 2019 Science 363 525 Google Scholar
[38]	Rudin S, Reinecke T L 1999 Phys. Rev. B 59 10227
[39]	Manjavacas A, de Abajo F J G, Nordlander P 2011 Nano Lett. 11 2318 Google Scholar
[40]	Autore M, Li P, Dolado I, et al. 2018 Light:Science & Applications 7 17172
[41]	Santhosh K, Bitton O, Chuntonov L, Haran G 2016 Nat. Commun. 10 1038 Google Scholar
[42]	Chikkaraddy R, de Nijs B, Benz F, Barrow S J, Scherman O A, Rosta E, Demetriadou A, Fox P, Hess O, Baumberg J J 2016 Nature 535 127 Google Scholar

Cited By

图 1 银纳米棒-介质层系统的电子损失探测示意图. 电子束沿z轴负方向入射, 作用于纳米核壳结构上, 出射电子能量损失谱表征体系支持的激发. 核壳结构的长度为$ l = 481{\text{ nm}} $, 核心部分为直径$ {\text{2}}r{\text{ = 20 nm}} $的银纳米棒, 介质层厚度$ h{\text{ = 20 nm}} $; 右图为强耦合导致电子能量损失谱中峰的拉比劈裂, 以及劈裂峰对应的能量损失空间分布图

Figure 1. Schematic diagram of electron loss detection of silver nanorod-dielectric layer system. The incident electron beam is along the negative direction of z axis and acts on the core-shell nano-structure with length l = 481 nm, and the electron energy loss spectrum characterizes the excitation supported by the system. The nanostructure is made of a silver nanorod core with a diameter $ {\text{2}}r{\text{ = 20 nm}} $ and a dielectric layer with a thickness of $ h{\text{ = 20 nm}} $. The figure on the right side shows the Rabi splitting of the peak in the electron energy loss spectrum caused by strong coupling, and the spatial map of the energy loss corresponding to the splitting peaks.

DownLoad: Full-Size Img PowerPoint

图 2 实验测量和理论模拟的银纳米棒 (a), (b) 电子能量损失谱及(c), (d)不同损失能量下的空间成像的对比　(a), (c) 实验测量结果^[8]; (b), (d) 理论模拟结果

Figure 2. Comparison of experimental measurements and theoretical simulations of electron energy loss spectrum (a), (b) and electron energy loss spatial distribution map under different loss energies (c), (d) of silver nanorods: (a), (c) Experimental measurements^[8]; (b), (d) theoretical simulations.

DownLoad: Full-Size Img PowerPoint

图 3 电子束作用于银纳米棒的(a)尖端, (b)中部和(c) 1/3长度处的电子能量损失谱; 电子束作用于银纳米棒不同位置不同激发能量的归一化电场分布　(d)尖端, 0.65 eV; (e)中间, 1.08 eV; (f) 1/3处, 1.46 eV

Figure 3. Electron energy loss spectrum for an electron beam at the (a) tip, (b) middle and (c) 1/3 length of a silver nanorod; the normalized electric field distribution with different excited energy by the electron beam acting on the different positions of the silver nanorod: (d) Tip, 0.65 eV; (e) middle, 1.08 eV; (f) 1/3 of the length, 1.46 eV.

DownLoad: Full-Size Img PowerPoint

图 4 通过改变银纳米棒尺寸来主动调控表面等离激元激发　(a) 直径20 nm不变, 改变银纳米棒的长度, 在棒的尖端激发得到的一系列电子能量损失谱; (b)长度481 nm不变, 改变纳米棒的直径, 在尖端激发得到的一系列电子能量损失谱; (c)偶极表面等离激元激发能量随银纳米棒长度的倒数(π/L)的比例关系

Figure 4. Actively regulate surface plasmon excitation by changing the size of silver nanorods: (a) Electron energy loss spectrum obtained from an electron beam acting on a silver nanorod with the fixed diameter 20 nm and increasing length; (b) the electron energy loss spectrum obtained from an electron beam acting on a silver nanorod with fixed length 481 nm and increasing diameter; (c) dipole plasmon excitation energy as a function of the inverse of the silver nanorod length (π/L).

DownLoad: Full-Size Img PowerPoint

图 5 介质层介电函数的(a)实部和(b)虚部随能量的变化(R.P.指相对介电常数); 0.58 eV处介质层的(c)电子能量损失谱和(d)电子能量损失空间分布图

Figure 5. Real (a) and imaginary (b) parts of the dielectric layer dielectric function as a function of energy (R. P. refers to relative permittivity); (c) the electron energy loss spectrum and (d) the electron energy loss spatial distribution map of the dielectric layer at 0.58 eV energy.

DownLoad: Full-Size Img PowerPoint

图 6 利用EELS探测红外波段偶极辐射表面等离激元模式和介质层的强耦合　(a)电子束作用于介质层尖端(黑实线), 银纳米棒尖端(红虚线)及银纳米棒-介质层核壳结构尖端(蓝色点线)的电子能量损失谱; 红移后偶极表面等离激元与介质层的元激发能量(b)零失谐与(c)失谐时, 在不同能量处劈裂峰对应的电子能量损失概率空间成像

Figure 6. Strong coupling between the infrared radiation dipole surface plasmon mode and the dielectric layer detected by EELS: (a) Electron energy loss spectrum of an electron beam acting on the tip of the dielectric layer (black solid line), the tip of silver nanorods (red dotted line) and the tip of the silver nanorod-dielectric layer core-shell structure (blue dotted line); spatial distribution of electron energy loss probability for two splitting peaks with different energies when the surface plasmon energy is (b) zero detuned and (c) detuned from the meta excitation energy of the dielectric layer.

DownLoad: Full-Size Img PowerPoint

图 7 不同波段辐射偶极和非辐射高级表面等离激元与介质层元激发间强耦合导致的反交叉色散关系　(a), (b) 直径为20 nm、不同长度的银纳米棒-介质层核壳结构的电子能量损失谱 (虚线标注了上、下杂化等离激子的能量) (a) 红外波段; (b) 可见波段; (c), (d) 对应的杂化等离激子能量的色散关系 (横虚线为介质层激发能量, 斜虚线为银纳米棒的偶极(m = 1, 4)表面等离激元能量)

Figure 7. Anti-crossing dispersion relationship caused by the strong coupling between the radiative dipolar and non-radiative higher-order plasmon in different range and the excitation of dielectric layer. (a), (b) Electron energy loss spectrum of silver nanorod-dielectric layer core-shell structures with a diameter of 20 nm and different lengths (The dotted lines mark the energies of the upper and lower plexciton): (a) Infrared range; (b) visible range; (c), (d) corresponding dispersion relationship of the plexciton energy (The horizontal dotted line is the excitation energy of the dielectric layer, and the oblique line is the energy of dipole (m = 1, 4) radiative plasmon of the silver nanorod).

DownLoad: Full-Size Img PowerPoint

[1]	Hamann H F, Kuno M, Gallagher A, Nesbitt D J 2001 J. Chem. Phys. 114 8596 Google Scholar
[2]	Hartschuh A, Sanchez E J, Xie X S, Novotny L 2003 Phys. Rev. Lett. 90 095503 Google Scholar
[3]	Fleischmann M, Hendra P J, McQuillan A J 1974 Chem. Phys. Lett. 26 163 Google Scholar
[4]	Nie S, Emory S R 1997 Science 275 1102 Google Scholar
[5]	Osawa M, Ikeda 1991 J. Phys. Chem. 95 9914 Google Scholar
[6]	Hirsch L, Stafford R J, Bankson J A, Sershen 2003 Proc. Natl. Acad. Sci. 100 13549 Google Scholar
[7]	Cao Y C, Jin R, Mirkin C A 2002 Science 297 1536 Google Scholar
[8]	Rossouw D, Couillard M, Vickery J, Kumacheva E, Botton G A 2011 Nano Lett. 11 1499 Google Scholar
[9]	Aizpurua J, Hanarp P, Sutherland D S, Käll M, Bryant G W, García de Abajo F J 2003 Phys. Rev. Lett. 90 057401 Google Scholar
[10]	Yankovich A B, Munkhbat B, Baranov D G, Cuadra J, Olsén E, Lourenço-Martins H, Tizei L H G, Kociak M, Eva Olsson, Shegai T 2019 Nano Lett. 19 8171 Google Scholar
[11]	Zanfrognini M, Rotunno E, Frabboni S, Sit A, Karimi E, Hohenester U, Grillo V 2019 ACS Photon. 6 620 Google Scholar
[12]	Benz F, Schmidt M K, Dreismann A, Chikkaraddy R, Zhang Y, Demetriadou A, Carnegie C, Ohadi H, De Nijs B, Esteban R, Aizpurua J, Baumberg J J 2016 Science 354 726 Google Scholar
[13]	Lee J, Tallarida N, Chen X, Liu P, Jensen L, Apkarian V A 2017 ACS Nano 11 11466 Google Scholar
[14]	Carnegie C, Griffiths J, de Nijs B, Readman C, Chikkaraddy R, Deacon W M, Zhang Y, Szabó I, Rosta E, Aizpurua J, Baumberg J J 2018 J. Phys. Chem. Lett. 9 7146 Google Scholar
[15]	Urbieta M, Barbry M, Zhang Y, Koval P, Sánchez-Portal D, Zabala N, Aizpurua J 2018 ACS Nano 12 585 Google Scholar
[16]	Doppagne B, Neuman T, Soria-Martinez R, López L E P, Bulou H, Romeo M, Berciaud S, Scheurer F, Aizpurua J, Schull G 2020 Nature Nanotechnol. 15 207 Google Scholar
[17]	Nan F, Zhang Y F, Li X G, Zhang X T, Hang Li H, Zhang X H, Jiang R B, Wang J F, Zhang W, Li Zhou, Wang J H, Wang Q Q, Zhang Z Y 2015 Nano Lett. 15 2705 Google Scholar
[18]	Guo Y Z, Zhu G D, Fanga Y 2021 J. Appl. Phys. 129 043104 Google Scholar
[19]	Qin J, Chen Y H, Zhang Z P, Zhang Y F, Blaikie R J, Ding B Y, Qiu M 2020 Phys. Rev. Lett. 124 063902 Google Scholar
[20]	Li P N, Yang X S, Maß T W W, Hanss J, Lewin M, Ann-Katrin U Michel, Wuttig M, Taubner T 2016 Nature Mater. 15 870 Google Scholar
[21]	Hutchison J A, Schwartz T, Genet C, Devaux E, Ebbesen T W 2012 Angew. Chem. 51 1592 Google Scholar
[22]	Törmä P, Barnes W L 2015 Rep. Prog. Phys. 78 013901 Google Scholar
[23]	Konečná A, Neuman T, Aizpurua J, Hillenbrand R 2018 ACS Nano 12 4775 Google Scholar
[24]	Zhang Y, Meng Q S, Zhang L, Luo Y, Yu Y J, Yang B, Zhang Y, Esteban R, Aizpurua J, Luo Y, Yang J L, Dong Z C, Hou J G 2017 Nat. Commun. 8 15225 Google Scholar
[25]	Tizei L H G, Mkhitaryan V, Lourenço-Martins H, et al. 2020 Nano Lett. 20 2973 Google Scholar
[26]	Liu H H, Gage T E, Singh P, Jaiswal A, Schaller R D, Tang J, Park S T, Gray S K, Arslan I 2021 Nano Lett. 21 5842 Google Scholar
[27]	Wei J K, Jiang N, Xu J, Bai X D, Liu J Y 2015 Nano Lett. 15 5926 Google Scholar
[28]	Lagos M J, Batson P E, Lyu Z, Hohenester U 2021 ACS Photon. 8 1293 Google Scholar
[29]	Zouros G P, Kolezas G D, N Asger Mortensen, Christos Tserkezis 2020 Phys. Rev. B 101 085416 Google Scholar
[30]	Goodman J J, Draine B T, Flatau P J 1991 Opt. Lett. 16 1198 Google Scholar
[31]	Yee K S 1966 IEEE T. Antenn. Propag. 14 302 Google Scholar
[32]	de Abajo F J G, Howie A 2002 Phys. Rev. B 65 115418 Google Scholar
[33]	Hohenester U 2014 Computer Phys. Commun. 185 1177 Google Scholar
[34]	Hohenester U, Trügler A 2012 Computer Phys. Commun. 183 370 Google Scholar
[35]	Johnson P, Christy R 1972 Phys. Rev. B 6 4370 Google Scholar
[36]	Maomao Zhang, Xueyi Shi, Xinyu Mu, Luxia Wang, Kun Gao 2021 Appl. Phys. Lett. 118 133301 Google Scholar
[37]	Hachtel J A, Huang J S, Popovs I, Jansone-Popova S, Keum J K, Jakowski J, Lovejoy T C, Dellby N, Krivanek O L, Idrobo J C 2019 Science 363 525 Google Scholar
[38]	Rudin S, Reinecke T L 1999 Phys. Rev. B 59 10227
[39]	Manjavacas A, de Abajo F J G, Nordlander P 2011 Nano Lett. 11 2318 Google Scholar
[40]	Autore M, Li P, Dolado I, et al. 2018 Light:Science & Applications 7 17172
[41]	Santhosh K, Bitton O, Chuntonov L, Haran G 2016 Nat. Commun. 10 1038 Google Scholar
[42]	Chikkaraddy R, de Nijs B, Benz F, Barrow S J, Scherman O A, Rosta E, Demetriadou A, Fox P, Hess O, Baumberg J J 2016 Nature 535 127 Google Scholar

[1]	Li Yuan-Fang, Jiang Yuan, Zhao Lei. Weak pulse signal detection method based on improved strongly coupled oscillators. Acta Physica Sinica, 2024, 73(4): 040503. doi: 10.7498/aps.73.20231343
[2]	Yan Xiao-Hong, Niu Yi-Jie, Xu Hong-Xing, Wei Hong. Strong coupling of single plasmonic nanoparticles and nanogaps with quantum emitters. Acta Physica Sinica, 2022, 71(6): 067301. doi: 10.7498/aps.71.20211900
[3]	Zhang Meng-Lai, Qin Zhao-Fu, Chen Zhuo. Conditions for surface lattice resonances and enhancement of second harmonic generation based on split-ring resonators. Acta Physica Sinica, 2021, 70(5): 054206. doi: 10.7498/aps.70.20201424
[4]	Guo Qi-Qi, Chen Yi-Hang. Enhanced nonlinear optical effects based on strong coupling between epsilon-near-zero mode and gap surface plasmons. Acta Physica Sinica, 2021, 70(18): 187303. doi: 10.7498/aps.70.20210290
[5]	Chu Pei-Xin, Zhang Yu-Bin, Chen Jun-Xue. Surface plasmon induced transparency in coupled microcavities assisted by slits. Acta Physica Sinica, 2020, 69(13): 134205. doi: 10.7498/aps.69.20200369
[6]	Wu Han, Wu Jing-Yu, Chen Zhuo. Strong coupling between metasurface based Tamm plasmon microcavity and exciton. Acta Physica Sinica, 2020, 69(1): 010201. doi: 10.7498/aps.69.20191225
[7]	Wu Li-Xiang, Li Xin, Yang Yuan-Jie. Generation of surface plasmon vortices based on double-layer Archimedes spirals. Acta Physica Sinica, 2019, 68(23): 234201. doi: 10.7498/aps.68.20190747
[8]	Yu Hua-Kang, Liu Bo-Dong, Wu Wan-Ling, Li Zhi-Yuan. Surface plasmaons enhanced light-matter interactions. Acta Physica Sinica, 2019, 68(14): 149101. doi: 10.7498/aps.68.20190337
[9]	Zhang Bao-Bao, Zhang Cheng-Yun, Zhang Zheng-Long, Zheng Hai-Rong. Surface plasmon mediated chemical reaction. Acta Physica Sinica, 2019, 68(14): 147102. doi: 10.7498/aps.68.20190345
[10]	Li Pan. Research progress of plasmonic nanofocusing. Acta Physica Sinica, 2019, 68(14): 146201. doi: 10.7498/aps.68.20190564
[11]	Zhang Wen-Jun, Gao Long, Wei Hong, Xu Hong-Xing. Modulation of propagating surface plasmons. Acta Physica Sinica, 2019, 68(14): 147302. doi: 10.7498/aps.68.20190802
[12]	Zhou Li, Wang Qu-Quan. Plasmon resonance energy transfer and research progress in plasmon-enhanced photocatalysis. Acta Physica Sinica, 2019, 68(14): 147301. doi: 10.7498/aps.68.20190276
[13]	Duan Xue-Ke, Ren Juan-Juan, Hao He, Zhang Qi, Gong Qi-Huang, Gu Ying. Interactions between photons and excitons in micro-nano photonic structures. Acta Physica Sinica, 2019, 68(14): 144201. doi: 10.7498/aps.68.20190269
[14]	Zhu Xue-Tao, Guo Jian-Dong. Development of novel high-resolution electron energy loss spectroscopy and related studies on surface excitations. Acta Physica Sinica, 2018, 67(12): 127901. doi: 10.7498/aps.67.20180689
[15]	Wang Dong, Xu Jun, Chen Yi-Hang. Broadband absorption caused by coupling of epsilon-near-zero mode with plasmon mode. Acta Physica Sinica, 2018, 67(20): 207301. doi: 10.7498/aps.67.20181106
[16]	Wang Wen-Hui, Zhang Nao. Energy loss of surface plasmon polaritons on Ag nanowire waveguide. Acta Physica Sinica, 2018, 67(24): 247302. doi: 10.7498/aps.67.20182085
[17]	Deng Hong-Mei, Huang Lei, Li Jing, Lu Ye, Li Chuan-Qi. Tunable unidirectional surface plasmon polariton coupler utilizing graphene-based asymmetric nanoantenna pairs. Acta Physica Sinica, 2017, 66(14): 145201. doi: 10.7498/aps.66.145201
[18]	Zhao Ze-Yu, Liu Jin-Qiao, Li Ai-Wu, Xu Ying. Strong coupling between J-aggregates and surface plasmon polaritons in gold nanodisks arrays. Acta Physica Sinica, 2016, 65(23): 231101. doi: 10.7498/aps.65.231101
[19]	Wang Lei, Cai Wei, Tan Xin-Hui, Xiang Yin-Xiao, Zhang Xin-Zheng, Xu Jing-Jun. Effects of cross-section shape on fast electron beams excited plasmons in the surface of nanowire pairs. Acta Physica Sinica, 2011, 60(6): 067305. doi: 10.7498/aps.60.067305
[20]	Yang Wei-Guo, Zhang Xiao-Zhong, Yuan Jun. Optimization of the method to measure d electron occupancy in transition elements from electron energy loss spectrum. Acta Physica Sinica, 2006, 55(7): 3413-3419. doi: 10.7498/aps.55.3413

147302-20220194补充材料.pdf

Catalog

Vol. 71, Issue 14 - 2022-07-20

Metrics

Abstract views: 5386
PDF Downloads: 101
Cited By: 0

姓名
邮箱
手机号码
标题
留言内容
验证码

Search

Article

留言板