Barium titanate dielectric regulation improved output performance of paper-based triboelectric nanogenerator

Liang Shuai-Bo; Yuan Tao; Qiu Yang; Zhang Zhen; Miao Ya-Ning; Han Jing-Feng; Liu Xiu-Tong; Yao Chun-Li

doi:10.7498/aps.71.20212022

Abstract

As a new energy conversion device that can convert mechanical energy into electrical energy, triboelectric nanogenerator has attracted extensive attention since its invention. However, its environmental performance is limited because the raw materials are mostly synthetic polymer materials. Using green and environmentally friendly cellulose materials to prepare triboelectric nanogenerators is one of the important ways to solve the above problems. In this study, cellulose/barium titanate composite paper is prepared by using bamboo cellulose and barium carbonate (BaTiO₃) as raw materials and combining wet papermaking and doping modification. The paper based triboelectric nanogenerator (C/BT-TENG) is constructed by using the cellulose/barium titanate composite paper as a positive friction layer. The results show that the addition of BaTiO₃ significantly improves the relative dielectric constant of the composite paper, and the output performance of C/BT-TENG increases with the augment of BaTiO₃ doping amount. When the doping amount is 4%, the open-circuit voltage and short-circuit current of C/BT-TENG reach the maximum values of 118.5 V and 13.51 µA, respectively, which are 51.3% and 41.2% higher than when pure cellulose paper is used as the positive friction layer. The mechanism of dielectric regulation to improve the C/BT-TENG output performance is analyzed by the modeling method. In addition, the C/BT-TENG has a good output performance and operation stability. When the load resistance is 5 MΩ, the maximum output power density of C/BT-TENG reaches 0.36 W/m², simplying a good application prospect.

Keywords:

Authors and contacts

College of Materials Science and Technology, Beijing Forestry University, Beijing 100083, China

Corresponding author: Yao Chun-Li, chunliyao2006@163.com

Funds: Project supported by the National Key R&D Program of China (Grant No. 2017YFD0600804), the National Natural Science Foundation of China (Grant No. 31470605) and the Project 948 of State Forestry Administration, China (Grant No. 20140436).

FullText HTML : translate this paragraph

References

[1]	Meyar-Naimi H, Vaez-Zadeh S 2012 Energ. Policy 43 351 Google Scholar
[2]	Goldemberg J 2006 Energ. Policy 34 2185 Google Scholar
[3]	Bai Y X, Shen B Y, Zhang S L, Zhu Z X, Sun S L, Gao J, Li B H, Wang Y, Zhang R F, Wei F 2019 Adv. Mater. 31 1800680 Google Scholar
[4]	Jie Y, Jia X T, Zou J D, Chen Y D, Wang N, Wang Z L, Cao X 2018 Adv. Energy Mater. 8 1703133
[5]	Zi Y L, Wang J, Wang S H, Li S M, Wen Z, Guo H Y, Wang Z L 2016 Nat. Commun. 7 1 Google Scholar
[6]	Wang Z L 2020 Adv. Energy Mater. 10 2000137 Google Scholar
[7]	Shang W Y, Gu G Q, Zhang W H, Luo H C, Wang T Y, Zhang B, Guo J M, Cui P, Yang F, Cheng G, Du Z L 2021 Nano Energy 82 105725 Google Scholar
[8]	Qin H F, Gu G Q, Shang W Y, Luo H C, Zhang W H, Cui P, Zhang B, Guo J M, Cheng G, Du Z L 2020 Nano Energy 68 104372 Google Scholar
[9]	Qin H F, Cheng G, Zi Y L, Gu G Q, Zhang B, Shang W Y, Yang F, Yang J J, Du Z L, Wang Z L 2018 Adv. Funct. Mater. 28 1805216 Google Scholar
[10]	Zhang H, Quan L W, Chen J K, Xu C K, Zhang C H, Dong S R, Lu C F, Luo J K 2019 Nano Energy 56 700 Google Scholar
[11]	Singh M, Sheetal A, Singh H, Sawhney R S, Kaur J 2020 J. Electron. Mater. 49 3409 Google Scholar
[12]	Kwak S S, Kim S M, Ryu H, Kim J, Khan U, Yoon H J, Jeong Y H, Kim S W 2019 Energy Environ. Sci. 12 3156 Google Scholar
[13]	Xu G P, Zheng Y B, Feng Y G, Ma S C, Luo N, Feng M, Chen S G, Wang D 2021 Sci. China Technol. Sc. 64 2003 Google Scholar
[14]	Landauer J, Aigner F, Kuhn M, Foerst P 2019 Adv. Powder Technol. 30 1099 Google Scholar
[15]	Kang H, Kim H T, Woo H J, Kim H, Kim D H, Lee S, Kim S, Song Y J, Kim S W, Cho J H 2019 Nano Energy 58 227 Google Scholar
[16]	Chao S, Ouyang H, Jiang D, Fan Y, Li Z 2021 Eco. Mat. 3 e12072 Google Scholar
[17]	Pang B, Jiang G Y, Zhou J H, Zhu Y, Cheng W K, Zhao D W, Wang K J, Xu G W, Yu H P 2021 Adv. Electron. Mater. 7 2000944 Google Scholar
[18]	Kim I, Jeon H, Kim D, You J, Kim D 2018 Nano Energy 53 975 Google Scholar
[19]	Kafy A, Sadasivuni K K, Akther A, Min S K, Kim J 2015 Mater. Lett. 159 20 Google Scholar
[20]	Darabi S, Hummel M, Rantasalo S, Rissanen M, Mansson I O, Hilke H, Hwang B, Skrifvars M, Hamedi M M, Sixta H, Lund A, Muller C 2020 Acs Appl. Mater. Inter. 12 56403 Google Scholar
[21]	Yao C H, Hernandez A, Yu Y H, Cai Z Y, Wang X D 2016 Nano Energy 30 103 Google Scholar
[22]	Diaz A F, Felix-Navarro R M 2004 J. Electrostat. 62 277 Google Scholar
[23]	Yu A F, Zhu Y X, Wang W, Zhai J Y 2019 Adv. Funct. Mater. 29 1900098 Google Scholar
[24]	Shao J J, Jiang T, Wang Z L 2020 Sci. China Technol. Sc. 63 1087 Google Scholar
[25]	Min G, Manjakkal L, Mulvihill D M, Dahiya R S 2020 IEEE Sens. J. 20 6856 Google Scholar
[26]	Wu C, Kim T W, Choi H Y 2017 Nano Energy 32 542 Google Scholar
[27]	Wang X Z, Yang B, Liu J Q, Zhu Y B, Yang C S, He Q 2016 Sci. Rep. 6 1 Google Scholar
[28]	Ba Y Y, Bao J F, Deng H T, Wang Z Y, Li X W, Gong T X, Huang W, Zhang X S 2020 Acs Appl. Mater. Inter. 12 42859 Google Scholar
[29]	Jia C, Shao Z Q, Fan H Y, Feng R, Wang F J, Wang W J, Wang J Q, Zhang D L, Lü Y Y 2016 Compos. Part A-Appl. S 86 1 Google Scholar
[30]	Ma M Y, Kang Z, Liao Q L, Zhang Q, Gao F F, Zhao X, Zhang Z, Zhang Y 2018 Nano Res. 11 2951 Google Scholar
[31]	Li W B, Zhou D, Pang L X, Xu R, Guo H H 2017 J. Mater. Chem. A 5 19607 Google Scholar
[32]	Zhang X, Lü S S, Lu X C, Yu H, Huang T, Zhang Q H, Zhu M F 2020 Nano Energy 75 104894 Google Scholar
[33]	Sriphan S, Nawanil C, Vittayakorn N 2018 Ceram. Int. 44 S38 Google Scholar
[34]	Dudem B, Kim D H, Bharat L K, Yu J S 2018 Appl. Energ. 230 865 Google Scholar
[35]	Chen J, Guo H Y, He X M, Liu G L, Xi Y, Shi H F, Hu C G 2016 Acs Appl. Mater. Inter. 8 736 Google Scholar
[36]	Zhang W H, Gu G Q, Qin H F, Li S M, Shang W Y, Wang T Y, Zhang B, Cui P, Guo J M, Yang F, Cheng G, Du Z L 2020 Nano Energy 77 105108 Google Scholar
[37]	Zhang W H, Gu G Q, Shang W Y, Luo H C, Wang T Y, Zhang B, Cui P, Guo J M, Yang F, Cheng G, Du Z L 2021 Nano Energy 86 106056 Google Scholar
[38]	Song H M, Yu H W, Zhu L J, Xue L X, Wu D C, Chen H 2017 React. Funct. Polym. 114 110 Google Scholar
[39]	Xiao S H, Jiang W F 2012 Int. J. Min. Met. Mater. 19 762 Google Scholar
[40]	Chen H M, Xu Y, Zhang J S, Wu W T, Song G F 2018 Nanoscale Res. Lett. 13 1 Google Scholar
[41]	Wang Z L 2017 Mater. Today 20 74 Google Scholar
[42]	Wang Z L, Chen J, Lin L 2015 Energy Environ. Sci. 8 2250 Google Scholar
[43]	Shi Y X, Wang F, Tian J W, Li S Y, Fu E G, Nie J H, Lei R, Ding Y F, Chen X Y, Wang Z L 2021 Sci. Adv. 7 eabe2943 Google Scholar
[44]	Nie J H, Ren Z W, Xu L, Lin S Q, Zhan F, Chen X Y, Wang Z L 2020 Adv. Mater. 32 1905696 Google Scholar
[45]	Li S Y, Fan Y, Chen H Q, Nie J H, Liang Y X, Tao X L, Zhang J, Chen X Y, Fu E G, Wang Z L 2020 Energy Environ. Sci. 13 896 Google Scholar

Cited By

图 1 (a)竹材多级结构示意图; (b) C/BT复合纸制备流程示意图; (c) C/BT-TENG结构示意图

Figure 1. (a) Diagram of hierarchical structure of bamboo; (b) schematic illustration of the preparation of C/BT composite paper; (c) structure diagram of C/BT-TENG.

DownLoad: Full-Size Img PowerPoint

图 2 (a) C/BT-4复合纸表面SEM图; (b) BaTiO₃与纤维之间的氢键示意图; C/BT-4复合纸表面(c) Ti元素和(d) Ba元素的EDS能谱图

Figure 2. (a) The surface SEM image of C/BT-4 composite paper; (b) diagram of hydrogen bond between BaTiO₃ and fiber; EDS spectrum of (c) Ti and (d) Ba on C/BT-4 composite paper surface.

DownLoad: Full-Size Img PowerPoint

图 3 (a) PTFE表面SEM图(右上角插图为其光学照片); (b) PTFE的红外光谱图; (c) BaTiO₃颗粒的SEM图(右上角插图为其光学照片); (d) BaTiO₃的X射线衍射图

Figure 3. (a) The surface SEM image of PTFE (The illustration in the upper right corner is its optical photo); (b) the infrared spectrogram of PTFE; (c) the SEM image of BaTiO₃ particles (The illustration in the upper right corner is its optical photo); (d) X-ray diffraction pattern of BaTiO₃.

DownLoad: Full-Size Img PowerPoint

图 4 不同BaTiO₃含量C/BT复合纸的应力-应变曲线

Figure 4. Tensile stress-strain curves of C/BT composite paper with different BaTiO₃ content.

DownLoad: Full-Size Img PowerPoint

图 5 不同BaTiO₃含量C/BT复合纸作为正极摩擦层的C/BT-TENG的(a)开路电压和(b)短路电流; 不同BaTiO₃含量C/BT复合纸的(c)相对介电常数和(d)介电损耗角正切随频率的变化情况

Figure 5. (a) Open circuit voltage and (b) short circuit current of C/BT-TENG with C/BT composite paper with different BaTiO₃ content as the positive friction layer; frequency dependence of (c) dielectric constant and (d) dielectric loss tangent of C/BT composite paper with different BaTiO₃ content.

DownLoad: Full-Size Img PowerPoint

图 6 (a) 400倍和(b) 4000倍下C/BT-5复合纸表面SEM图; C/BT-5复合纸表面(c) Ti元素和(d) Ba元素的EDS能谱图

Figure 6. The surface SEM image of (a) low and (b) high magnification showing the C/BT-5 composite paper surface; EDS spectrum of (c) Ti and (d) Ba on C/BT-5 composite paper surface.

DownLoad: Full-Size Img PowerPoint

图 7 C/BT-TENG的等效电路模型

Figure 7. Schematic diagram and an equivalent circuit model of the C/BT-TENG.

DownLoad: Full-Size Img PowerPoint

图 8 C/BT-TENG在不同大小外力下的(a)开路电压和(b)短路电流; (c) C/BT-TENG的开路电压与外力大小的线性拟合; (d) C/BT-TENG在5000次连续循环工作过程中的输出电压

Figure 8. (a) Open circuit voltage and (b) short circuit current of C/BT-TENG under different external forces; (c) linear fit between open circuit voltage of C/BT-TENG and external force; (d) the output voltage of C/BT-TENG during 5000 continuous cycles.

DownLoad: Full-Size Img PowerPoint

图 9 C/BT-TENG在不同外接负载电阻下的(a)输出电压-电流和(b)输出功率

Figure 9. (a) Output voltage-current and (b) output power of C/BT-TENG with external resistances.

DownLoad: Full-Size Img PowerPoint

图 10 C/BT-TENG的工作机理示意图

Figure 10. The schematic illustration showing the working mechanism of the C/BT-TENG.

DownLoad: Full-Size Img PowerPoint

[1]	Meyar-Naimi H, Vaez-Zadeh S 2012 Energ. Policy 43 351 Google Scholar
[2]	Goldemberg J 2006 Energ. Policy 34 2185 Google Scholar
[3]	Bai Y X, Shen B Y, Zhang S L, Zhu Z X, Sun S L, Gao J, Li B H, Wang Y, Zhang R F, Wei F 2019 Adv. Mater. 31 1800680 Google Scholar
[4]	Jie Y, Jia X T, Zou J D, Chen Y D, Wang N, Wang Z L, Cao X 2018 Adv. Energy Mater. 8 1703133
[5]	Zi Y L, Wang J, Wang S H, Li S M, Wen Z, Guo H Y, Wang Z L 2016 Nat. Commun. 7 1 Google Scholar
[6]	Wang Z L 2020 Adv. Energy Mater. 10 2000137 Google Scholar
[7]	Shang W Y, Gu G Q, Zhang W H, Luo H C, Wang T Y, Zhang B, Guo J M, Cui P, Yang F, Cheng G, Du Z L 2021 Nano Energy 82 105725 Google Scholar
[8]	Qin H F, Gu G Q, Shang W Y, Luo H C, Zhang W H, Cui P, Zhang B, Guo J M, Cheng G, Du Z L 2020 Nano Energy 68 104372 Google Scholar
[9]	Qin H F, Cheng G, Zi Y L, Gu G Q, Zhang B, Shang W Y, Yang F, Yang J J, Du Z L, Wang Z L 2018 Adv. Funct. Mater. 28 1805216 Google Scholar
[10]	Zhang H, Quan L W, Chen J K, Xu C K, Zhang C H, Dong S R, Lu C F, Luo J K 2019 Nano Energy 56 700 Google Scholar
[11]	Singh M, Sheetal A, Singh H, Sawhney R S, Kaur J 2020 J. Electron. Mater. 49 3409 Google Scholar
[12]	Kwak S S, Kim S M, Ryu H, Kim J, Khan U, Yoon H J, Jeong Y H, Kim S W 2019 Energy Environ. Sci. 12 3156 Google Scholar
[13]	Xu G P, Zheng Y B, Feng Y G, Ma S C, Luo N, Feng M, Chen S G, Wang D 2021 Sci. China Technol. Sc. 64 2003 Google Scholar
[14]	Landauer J, Aigner F, Kuhn M, Foerst P 2019 Adv. Powder Technol. 30 1099 Google Scholar
[15]	Kang H, Kim H T, Woo H J, Kim H, Kim D H, Lee S, Kim S, Song Y J, Kim S W, Cho J H 2019 Nano Energy 58 227 Google Scholar
[16]	Chao S, Ouyang H, Jiang D, Fan Y, Li Z 2021 Eco. Mat. 3 e12072 Google Scholar
[17]	Pang B, Jiang G Y, Zhou J H, Zhu Y, Cheng W K, Zhao D W, Wang K J, Xu G W, Yu H P 2021 Adv. Electron. Mater. 7 2000944 Google Scholar
[18]	Kim I, Jeon H, Kim D, You J, Kim D 2018 Nano Energy 53 975 Google Scholar
[19]	Kafy A, Sadasivuni K K, Akther A, Min S K, Kim J 2015 Mater. Lett. 159 20 Google Scholar
[20]	Darabi S, Hummel M, Rantasalo S, Rissanen M, Mansson I O, Hilke H, Hwang B, Skrifvars M, Hamedi M M, Sixta H, Lund A, Muller C 2020 Acs Appl. Mater. Inter. 12 56403 Google Scholar
[21]	Yao C H, Hernandez A, Yu Y H, Cai Z Y, Wang X D 2016 Nano Energy 30 103 Google Scholar
[22]	Diaz A F, Felix-Navarro R M 2004 J. Electrostat. 62 277 Google Scholar
[23]	Yu A F, Zhu Y X, Wang W, Zhai J Y 2019 Adv. Funct. Mater. 29 1900098 Google Scholar
[24]	Shao J J, Jiang T, Wang Z L 2020 Sci. China Technol. Sc. 63 1087 Google Scholar
[25]	Min G, Manjakkal L, Mulvihill D M, Dahiya R S 2020 IEEE Sens. J. 20 6856 Google Scholar
[26]	Wu C, Kim T W, Choi H Y 2017 Nano Energy 32 542 Google Scholar
[27]	Wang X Z, Yang B, Liu J Q, Zhu Y B, Yang C S, He Q 2016 Sci. Rep. 6 1 Google Scholar
[28]	Ba Y Y, Bao J F, Deng H T, Wang Z Y, Li X W, Gong T X, Huang W, Zhang X S 2020 Acs Appl. Mater. Inter. 12 42859 Google Scholar
[29]	Jia C, Shao Z Q, Fan H Y, Feng R, Wang F J, Wang W J, Wang J Q, Zhang D L, Lü Y Y 2016 Compos. Part A-Appl. S 86 1 Google Scholar
[30]	Ma M Y, Kang Z, Liao Q L, Zhang Q, Gao F F, Zhao X, Zhang Z, Zhang Y 2018 Nano Res. 11 2951 Google Scholar
[31]	Li W B, Zhou D, Pang L X, Xu R, Guo H H 2017 J. Mater. Chem. A 5 19607 Google Scholar
[32]	Zhang X, Lü S S, Lu X C, Yu H, Huang T, Zhang Q H, Zhu M F 2020 Nano Energy 75 104894 Google Scholar
[33]	Sriphan S, Nawanil C, Vittayakorn N 2018 Ceram. Int. 44 S38 Google Scholar
[34]	Dudem B, Kim D H, Bharat L K, Yu J S 2018 Appl. Energ. 230 865 Google Scholar
[35]	Chen J, Guo H Y, He X M, Liu G L, Xi Y, Shi H F, Hu C G 2016 Acs Appl. Mater. Inter. 8 736 Google Scholar
[36]	Zhang W H, Gu G Q, Qin H F, Li S M, Shang W Y, Wang T Y, Zhang B, Cui P, Guo J M, Yang F, Cheng G, Du Z L 2020 Nano Energy 77 105108 Google Scholar
[37]	Zhang W H, Gu G Q, Shang W Y, Luo H C, Wang T Y, Zhang B, Cui P, Guo J M, Yang F, Cheng G, Du Z L 2021 Nano Energy 86 106056 Google Scholar
[38]	Song H M, Yu H W, Zhu L J, Xue L X, Wu D C, Chen H 2017 React. Funct. Polym. 114 110 Google Scholar
[39]	Xiao S H, Jiang W F 2012 Int. J. Min. Met. Mater. 19 762 Google Scholar
[40]	Chen H M, Xu Y, Zhang J S, Wu W T, Song G F 2018 Nanoscale Res. Lett. 13 1 Google Scholar
[41]	Wang Z L 2017 Mater. Today 20 74 Google Scholar
[42]	Wang Z L, Chen J, Lin L 2015 Energy Environ. Sci. 8 2250 Google Scholar
[43]	Shi Y X, Wang F, Tian J W, Li S Y, Fu E G, Nie J H, Lei R, Ding Y F, Chen X Y, Wang Z L 2021 Sci. Adv. 7 eabe2943 Google Scholar
[44]	Nie J H, Ren Z W, Xu L, Lin S Q, Zhan F, Chen X Y, Wang Z L 2020 Adv. Mater. 32 1905696 Google Scholar
[45]	Li S Y, Fan Y, Chen H Q, Nie J H, Liang Y X, Tao X L, Zhang J, Chen X Y, Fu E G, Wang Z L 2020 Energy Environ. Sci. 13 896 Google Scholar

[1]	Zhang Yu-Ye, Zhang Yi-Yi, Wei Wen-Chang, Su Zhi-Cheng, Lan Dan-Quan, Luo Shi-Hao. Molecular dynamics simulation of mechanical and thermal properties of nano-zinc oxide modified cellulose insulating paper. Acta Physica Sinica, 2024, 73(12): 127701. doi: 10.7498/aps.73.20240208
[2]	Deng Hao-Cheng, Li Yi, Tian Shuang-Shuang, Zhang Xiao-Xing, Xiao Song. Dielectric materials for high-performance triboelectric nanogenerators. Acta Physica Sinica, 2024, 73(7): 070702. doi: 10.7498/aps.73.20240150
[3]	Zhang Jia-Wei, Yao Hong-Bo, Zhang Yuan-Zheng, Jiang Wei-Bo, Wu Yong-Hui, Zhang Ya-Ju, Ao Tian-Yong, Zheng Hai-Wu. Self-powered sensing based on triboelectric nanogenerator through machine learning and its application. Acta Physica Sinica, 2022, 71(7): 078702. doi: 10.7498/aps.71.20211632
[4]	Wang Chuang, Bao Rong-Rong, Pan Cao-Feng. Research and application of flexible wearable electronics based on nanogenerator in touch sensor. Acta Physica Sinica, 2021, 70(10): 100705. doi: 10.7498/aps.70.20202157
[5]	Shen Mao-Liang, Zhang Yan. Flexible sensor and energy storage device based on piezoelectric nanogenerator. Acta Physica Sinica, 2020, 69(17): 170701. doi: 10.7498/aps.69.20200784
[6]	Wang Jiao, Liu Shao-Hui, Chen Chang-Qing, Hao Hao-Shan, Zhai Ji-Wei. Interface modification and energy storage properties of barium titanate-based/ polyvinylidene fluoride composite. Acta Physica Sinica, 2020, 69(21): 217702. doi: 10.7498/aps.69.20201031
[7]	Cao Jie, Gu Wei-Guang, Qu Zhao-Qi, Zhong Yan, Cheng Guang-Gui, Zhang Zhong-Qiang. Design and research of non-contact triboelectric nanogenerator based on changing electrostatic field. Acta Physica Sinica, 2020, 69(23): 230201. doi: 10.7498/aps.69.20201052
[8]	Ding Ya-Fei, Chen Xiang-Yu. Triboelectric nanogenerator based wearable energy harvesting devices. Acta Physica Sinica, 2020, 69(17): 170202. doi: 10.7498/aps.69.20200867
[9]	Jing Qi, Li Xiao-Juan. Preparation of porous barium titanate ceramics and enhancement of piezoelectric sensitivity. Acta Physica Sinica, 2019, 68(5): 057701. doi: 10.7498/aps.68.20181790
[10]	Sun Zhi-Zheng, Xun Wei, Zhang Jia-Yong, Liu Chuan-Yang, Zhong Jia-Lin, Wu Yin-Zhong. Optical properties of BaTiO₃ and its volume effects. Acta Physica Sinica, 2019, 68(8): 087801. doi: 10.7498/aps.68.20182087
[11]	Wu Ye-Sheng, Liu Qi, Cao Jie, Li Kai, Cheng Guang-Gui, Zhang Zhong-Qiang, Ding Jian-Ning, Jiang Shi-Yu. Design and output performance of vibration energy harvesting triboelectric nanogenerator. Acta Physica Sinica, 2019, 68(19): 190201. doi: 10.7498/aps.68.20190806
[12]	Cheng Guang-Gui, Zhang Wei, Fang Jun, Jiang Shi-Yu, Ding Jian-Ning, Noshir S. Pesika, Zhang Zhong-Qiang, Guo Li-Qiang, Wang Ying. Fabrication of triboelectric nanogenerator with textured surface and its electric output performance. Acta Physica Sinica, 2016, 65(6): 060201. doi: 10.7498/aps.65.060201
[13]	Liu Yong-Guang, Kang Ai-Guo, Zhang Shao-Fei, Hou Zhi-Wen, Liu Wen-Bin. Theoretical analysis on ferroelectricity critical dimension of BaTiO3 nanoparticles. Acta Physica Sinica, 2015, 64(17): 177702. doi: 10.7498/aps.64.177702
[14]	Ni Jian-Gang, Liu Nuo, Yang Guo-Lai, Zhang Xi. First-principle study on electronic structure of BaTiO3 (001) surfaces. Acta Physica Sinica, 2008, 57(7): 4434-4440. doi: 10.7498/aps.57.4434
[15]	Wang Pei-Ji, Zhou Zhong-Xiang, Su Yan, Rong Zhen-Yu, Zhao Peng, Zhang Feng-Jun. Influence of tantalum doping on the thermal conduction of BaTiO3 materials. Acta Physica Sinica, 2006, 55(4): 1959-1964. doi: 10.7498/aps.55.1959
[16]	Xu Cun-Ying, Zhang Peng-Xiang, Yan Lei. Blue shift of Raman peaks of coated BaTiO3 nanoparticles. Acta Physica Sinica, 2005, 54(11): 5089-5092. doi: 10.7498/aps.54.5089
[17]	Li Zhi-Qiang, Lu Xia-Lian, Chen Min, He Shan, Li Jing-De. . Acta Physica Sinica, 2002, 51(7): 1581-1585. doi: 10.7498/aps.51.1581
[18]	LIU LI-WEI, WANG ZUO-WEI, ZHOU LU-WEI, WANG ZHI-JIN, GAO GUANG-JUN, LIU XIAO-JUN. SQUEEZE FLOW VISCOELASTICITY OF ELECTRORHEOLOGICAL FLUIDS BASED ON MICROCRYSTAL LINE CELLULOSE. Acta Physica Sinica, 2000, 49(9): 1886-1891. doi: 10.7498/aps.49.1886
[19]	WANG GUO-PING, GUO LU-RONG, CHEN QI-RUI, DAI CHAO-MING, HE LONG-QING. RED SENSITIVITY OF DICHROMATED CELLULOSE TRIACETATE HOLOGRAPHIC MATERIAL. Acta Physica Sinica, 1994, 43(10): 1593-1597. doi: 10.7498/aps.43.1593
[20]	. . Acta Physica Sinica, 1933, 1(1): 87-90. doi: 10.7498/aps.1.87

Catalog

Vol. 71, Issue 7 - 2022-04-05

Metrics

Abstract views: 6839
PDF Downloads: 148
Cited By: 0

姓名
邮箱
手机号码
标题
留言内容
验证码

Search

Article

留言板