Research on near infrared photoelectric response and surface-enhanced Raman scatteringof urchin-like Au-Ag-Pt-Pd nanoalloy

Ma Hui; Tian Yue; Jiao An-Xin; Zhang Meng-Ya; Wang Chang; Chen Ming

doi:10.7498/aps.71.20212094

Abstract

Compared with the single metal, multi-metallic nanoparticle has excellent localized surface plasmon resonance with a wide spectral range response, which is beneficial to improving both the photoinduced electron transfer efficiency and the effective electron-hole separation. In this work, the urchin-like Au-Ag-Pt-Pd nanoalloy (Au-Ag-Pt-Pd NU) with multiple tentacles is successfully synthesized by the seed growth method and chemical reduction method. And we explore the optical properties of Au-Ag-Pt-Pd NU at different annealing temperatures. The results show that the transient photocurrent intensity of Au-Ag-Pt-Pd NU annealed at 200 ℃ is 1.6 times that of the primitive Au-Ag-Pt-Pd NUs at 808 nm excitation. In addition, the SERS signal intensity of crystal violet (CV) adsorbed on the Au-Ag-Pt-Pd NUs annealed at 200 ℃ is 1.8 times that of the primitive Au-Ag-Pt-Pd NUs at 785 nm excitation. For the Au-Ag-Pt-Pd NUs in this work, the concentration of CV can be detected to be as low as 10^–12 M. Furthermore, the interesting NIR-SERS sensor enables the detection limit of H₂O₂ at low concentration to reach 0.09–1.02 μmol/L. The results show that the obtained nanoalloy has excellent photoelectric response characteristics and high SERS sensitivity due to the synergistic effect of multi-metal. Thus, it possesses great potential for biological NIR detection in the future.

Keywords:

Authors and contacts

School of Physics, Shandong University, Jinan 250100, China

Corresponding author: Chen Ming, chenming@sdu.edu.cn

Funds: Project supported by National Natural Science Foundation of China (Grant Nos. 11905115, 11575102), and the Fundamental Research Funds of Shandong University, China (Grant No. 2018JC022)

FullText HTML : translate this paragraph

References

[1]	Liang C, Lu Z, Wu J, Chen M, Zhang Y, Zhang B, Gao G, Li S, Xu P 2020 ACS Appl. Mater. Interfaces 12 54266 Google Scholar
[2]	Zhang Z, Zhang C, Zheng H, Xu H 2019 Acc. Chem. Res. 52 2506 Google Scholar
[3]	Zheng B Y, Zhao H, Manjavacas A, McClain M, Nordlander P, Halas N J 2015 Nat. Commun. 6 7797 Google Scholar
[4]	Zhang Y, He S, Guo W, Hu Y, Huang J, Mulcahy J R, Wei W D 2018 Chem. Rev. 118 2927 Google Scholar
[5]	Kang Y, Xue Q, Peng R, Jin P, Zeng J, Jiang J, Chen Y 2017 NPG Asia Mater. 9 e407 Google Scholar
[6]	Willets K A, Van Duyne R P 2007 Annu. Rev. Phys. Chem. 58 267 Google Scholar
[7]	Duchene J S, Niu W, Abendroth J M, Sun Q, Zhao W, Huo F, Wei W D 2013 Chem. Mater. 25 1392 Google Scholar
[8]	Duchene J S, Almeida R P, Wei W D 2012 Dalton Trans. 41 7879 Google Scholar
[9]	Wang J, Ma L, Xu J, Xu Y, Sun K, Peng Z 2021 SusMat 1 345 Google Scholar
[10]	Yaseen T, Pu H, Sun D 2019 Food Anal. Methods 12 2094 Google Scholar
[11]	Camacho S A, Sobral-Filho R G, Aoki P H B, Constantino C J L, Brolo A G 2018 ACS Sens. 3 587 Google Scholar
[12]	Qiao X, Su B, Liu C, Song Q, Luo D, Mo G, Wang T 2018 Adv. Mater. 30 1702275 Google Scholar
[13]	Romero-Natale A, Palchetti I, Avelar M, González-Vergara E, Garate-Morales J, Torres E 2019 Water 11 719 Google Scholar
[14]	刘小红, 姜珊, 常林, 张炜 2020 物理学报 69 190701 Google Scholar Liu X H, Jiang S, Chang L, Zhang W 2020 Acta Phys. Sin. 69 190701 Google Scholar
[15]	Ma Y, Li W, Cho E C, Li Z, Yu T, Zeng J, Xie Z, Xia Y 2010 ACS Nano 4 6725 Google Scholar
[16]	Bu L, Ding J, Guo S, Zhang X, Su D, Zhu X, Yao J, Guo J, Lu G, Huang X 2015 Adv. Mater. 27 7204 Google Scholar
[17]	Genç A, Patarroyo J, Sancho-Parramon J, Arenal R, Duchamp M, Gonzalez E E, Henrard L, Bastús N G, Dunin-Borkowski R E, Puntes V F, Arbiol J 2016 ACS Photonics 3 770 Google Scholar
[18]	Wang X, Ma G, Li A, Yu J, Yang Z, Lin J, Li A, Han X, Guo L 2018 Chem. Sci. 9 4009 Google Scholar
[19]	Li J, Liu J, Yang Y, Qin D 2015 J. Am. Chem. Soc. 137 7039 Google Scholar
[20]	He Y, Lu H, Sai L, Su Y, Hu M, Fan C, Huang W, Wang L 2008 Adv. Mater. 20 3416 Google Scholar
[21]	Malankowska A, Mikolajczyk A, Mędrzycka J O, Wysocka I, Nowaczyk G, Jarek M, Puzyn T, Mulkiewicz E 2020 Environ. Sci. -Nano 7 3557 Google Scholar
[22]	Bai X, Wang L, Wang Y, Yao W, Zhu Y 2014 Appl. Catal., B 152-153 262 Google Scholar
[23]	Wang C, Nie X G, Shi Y, Zhou Y, Xu J J, Xia X H, Chen H Y 2017 ACS Nano 11 5897 Google Scholar
[24]	Zhang C, Zhao H, Zhou L, Schlather A E, Dong L, McClain M J, Swearer D F, Nordlander P, Halas N J 2016 Nano Lett. 16 6677 Google Scholar
[25]	Swearer D F, Zhao H, Zhou L, Zhang C, Robatjazi H, Martirez J M P, Krauter C M, Yazdi S, McClain M J, Ringe E, Carter E A, Nordlander P, Halas N J 2016 Proc. Natl. Acad. Sci. U. S. A. 113 8916 Google Scholar
[26]	Zhang X, Ke X, Yao J 2018 J. Mater. Chem. A 6 1941 Google Scholar
[27]	Kumar V, O'Donnell S C, Sang D L, Maggard P A, Wang G 2019 Front. Chem. 7 299 Google Scholar
[28]	Jiang L, Hassan M M, Ali S, Li H, Sheng R, Chen Q 2021 Trends Food Sci. Technol. 112 225 Google Scholar
[29]	Tian Y, Zhang H, Xu L, Chen M, Chen F 2018 Opt. Lett. 43 635 Google Scholar
[30]	Ting A S Y, Lee M V J, Chow Y Y, Cheong S L 2016 Water Air Soil Pollut. 227 109 Google Scholar
[31]	Meng M, Fang Z, Zhang C, Su H, He R, Zhang R, Li H, Li Z, Wu X, Ma C, Zeng J 2016 Nano Lett. 16 3036 Google Scholar
[32]	Huang C, Valinton J A A, Hung Y, Chen C 2018 Sens. Actuators, B 266 463 Google Scholar
[33]	Aparicio-Martínez E, Ibarra A, Estrada-Moreno I A, Osuna V, Dominguez R B 2019 Sens. Actuators, B 301 127101 Google Scholar
[34]	Asadian E, Ghalkhani M, Shahrokhian S 2019 Sens. Actuators, B 293 183 Google Scholar
[35]	Zhang R, Chen W 2017 Biosens. Bioelectron. 89 249 Google Scholar
[36]	Yao D, Li C, Liang A, Jiang Z 2019 Spectrochim. Acta, Part A 216 146 Google Scholar
[37]	Ma J, Feng G, Ying Y, Shao Y, She Y, Zheng L, Abd Ei-Aty A M, Wang J 2021 Analyst 146 956 Google Scholar

Cited By

图 1 (a) 在初始状态下, Au-Ag-Pt-Pd NUs的SEM图像(插图: Au, Ag, Pt和Pd元素分布饼状图, 其中, Au, Ag, Pt和Pd元素比例分别是80.2%, 10.0%, 7.0%和2.8%); (b) 退火200 ℃, Au-Ag-Pt-Pd NUs的高倍SEM图像; 在退火200 ℃情况下, (c)和(d)分别Au-Ag-Pt-Pd NUs的TEM和HRTEM图像; (e)在退火200 ℃情况下, Au-Ag-Pt-Pd NUs的元素映射图像

Figure 1. (a) The SEM image of Au-Ag-Pt-Pd NUs unannealed (inset: the proportions of Au, Ag, Pt and Pd are 80.2%, 10.0%, 7.0% and 2.8%, respectively); (b) the SEM image of Au-Ag-Pt-Pd NUs annealed 200 ℃; (c), (d) the TEM and HRTEM of Au-Ag-Pt-Pd NUs annealed 200 ℃; (e) the element mapping images of Au-Ag-Pt-Pd NUs annealed 200 ℃.

DownLoad: Full-Size Img PowerPoint

图 2 (a) Au-Ag-Pt-Pd NUs在不同退火温度下的XRD; (b) Au-Ag-Pt-Pd NUs在不同退火温度下的吸收谱

Figure 2. (a) and (b) are XRD and absorption of Au-Ag-Pt-Pd NUs at different annealing temperatures, respectively.

DownLoad: Full-Size Img PowerPoint

图 3 Au, Ag, Pt 和Pd在不同退火温度下的XPS谱图　(a) Au; (b) Ag; (c) Pt; (d) Pd

Figure 3. XPS spectra of (a) Au, (b) Ag, (c) Pt and (d) Pd at different annealing temperatures.

DownLoad: Full-Size Img PowerPoint

图 4 (a), (b) 在808 nm激发下, Au-Ag-Pt-Pd NUs不同退火温度的瞬态光电流响应和峰值的柱状图; (c), (d) Au-Ag-Pt-Pd NUs在不同波长激光激发下瞬态光电流响应和峰值的柱状图

Figure 4. (a), (b) The transient photocurrent responses and peak histogram of Au-Ag-Pt-Pd NUs at different annealing temperatures under excitation at 808 nm. (c), (d) the transient photocurrent responses and peak histogram of Au-Ag-Pt-Pd NUs at different wavelengths of laser.

DownLoad: Full-Size Img PowerPoint

图 5 (a), (b) 退火200 ℃的Au-Ag-Pt-Pd NUs在808 nm不同激光强度下瞬态光电流响应和强度线性关系图

Figure 5. (a) The transient photocurrent responses of Au-Ag-Pt-Pd NUs annealed 200 ℃ at the different output power of 808 nm laser; (b) the relationship between the output power of 808 nm and current intensity.

DownLoad: Full-Size Img PowerPoint

图 6 (a) SERS信号采集示意图. 不同退火温度下, Au-Ag-Pt-Pd NUs的CV(10^–7 M)拉曼信号谱图(b)和峰值的柱状图(c). (d) 在退火200 ℃ Au-Ag-Pt-Pd NUs的SERS基底下, 不同浓度CV分子的SERS谱图. (e) 探针分子CV位于1177, 1367, 1587和1615 cm^–1特征峰的SERS信号强度与CV分子浓度的线性关系

Figure 6. (a) The SERS system with Au-Ag-Pt-Pd NUs as substrate and 785 nm NIR laser source. (b) SERS signal and (c) peak histogram of CV absorbed on Au-Ag-Pt-Pd NUs at different annealed temperatures. (d) based on the obtained Au-Ag-Pt-Pd NUs annealed 200 ℃, SERS spectra of CV at different concentrations. (e) the relationships between SERS peak intensities at 1177, 1376, 1587 and 1615 cm^–1, and the concentration of CV molecules.

DownLoad: Full-Size Img PowerPoint

图 7 (a)在不同H₂O₂浓度下, 探针分子TMB在Au-Ag-Pt-Pd NUs的SERS信号; (b)在1605 cm^–1拉曼峰处, H₂O₂浓度和拉曼信号强度的线性关系

Figure 7. (a) SERS signal of TMB on Au-Ag-Pt-Pd NUs substrate under different concentrations of H₂O_2; (b) the relationship between SERS signal intensity and the concentration of H₂O₂ at peak of 1605 cm^–1.

DownLoad: Full-Size Img PowerPoint

[1]	Liang C, Lu Z, Wu J, Chen M, Zhang Y, Zhang B, Gao G, Li S, Xu P 2020 ACS Appl. Mater. Interfaces 12 54266 Google Scholar
[2]	Zhang Z, Zhang C, Zheng H, Xu H 2019 Acc. Chem. Res. 52 2506 Google Scholar
[3]	Zheng B Y, Zhao H, Manjavacas A, McClain M, Nordlander P, Halas N J 2015 Nat. Commun. 6 7797 Google Scholar
[4]	Zhang Y, He S, Guo W, Hu Y, Huang J, Mulcahy J R, Wei W D 2018 Chem. Rev. 118 2927 Google Scholar
[5]	Kang Y, Xue Q, Peng R, Jin P, Zeng J, Jiang J, Chen Y 2017 NPG Asia Mater. 9 e407 Google Scholar
[6]	Willets K A, Van Duyne R P 2007 Annu. Rev. Phys. Chem. 58 267 Google Scholar
[7]	Duchene J S, Niu W, Abendroth J M, Sun Q, Zhao W, Huo F, Wei W D 2013 Chem. Mater. 25 1392 Google Scholar
[8]	Duchene J S, Almeida R P, Wei W D 2012 Dalton Trans. 41 7879 Google Scholar
[9]	Wang J, Ma L, Xu J, Xu Y, Sun K, Peng Z 2021 SusMat 1 345 Google Scholar
[10]	Yaseen T, Pu H, Sun D 2019 Food Anal. Methods 12 2094 Google Scholar
[11]	Camacho S A, Sobral-Filho R G, Aoki P H B, Constantino C J L, Brolo A G 2018 ACS Sens. 3 587 Google Scholar
[12]	Qiao X, Su B, Liu C, Song Q, Luo D, Mo G, Wang T 2018 Adv. Mater. 30 1702275 Google Scholar
[13]	Romero-Natale A, Palchetti I, Avelar M, González-Vergara E, Garate-Morales J, Torres E 2019 Water 11 719 Google Scholar
[14]	刘小红, 姜珊, 常林, 张炜 2020 物理学报 69 190701 Google Scholar Liu X H, Jiang S, Chang L, Zhang W 2020 Acta Phys. Sin. 69 190701 Google Scholar
[15]	Ma Y, Li W, Cho E C, Li Z, Yu T, Zeng J, Xie Z, Xia Y 2010 ACS Nano 4 6725 Google Scholar
[16]	Bu L, Ding J, Guo S, Zhang X, Su D, Zhu X, Yao J, Guo J, Lu G, Huang X 2015 Adv. Mater. 27 7204 Google Scholar
[17]	Genç A, Patarroyo J, Sancho-Parramon J, Arenal R, Duchamp M, Gonzalez E E, Henrard L, Bastús N G, Dunin-Borkowski R E, Puntes V F, Arbiol J 2016 ACS Photonics 3 770 Google Scholar
[18]	Wang X, Ma G, Li A, Yu J, Yang Z, Lin J, Li A, Han X, Guo L 2018 Chem. Sci. 9 4009 Google Scholar
[19]	Li J, Liu J, Yang Y, Qin D 2015 J. Am. Chem. Soc. 137 7039 Google Scholar
[20]	He Y, Lu H, Sai L, Su Y, Hu M, Fan C, Huang W, Wang L 2008 Adv. Mater. 20 3416 Google Scholar
[21]	Malankowska A, Mikolajczyk A, Mędrzycka J O, Wysocka I, Nowaczyk G, Jarek M, Puzyn T, Mulkiewicz E 2020 Environ. Sci. -Nano 7 3557 Google Scholar
[22]	Bai X, Wang L, Wang Y, Yao W, Zhu Y 2014 Appl. Catal., B 152-153 262 Google Scholar
[23]	Wang C, Nie X G, Shi Y, Zhou Y, Xu J J, Xia X H, Chen H Y 2017 ACS Nano 11 5897 Google Scholar
[24]	Zhang C, Zhao H, Zhou L, Schlather A E, Dong L, McClain M J, Swearer D F, Nordlander P, Halas N J 2016 Nano Lett. 16 6677 Google Scholar
[25]	Swearer D F, Zhao H, Zhou L, Zhang C, Robatjazi H, Martirez J M P, Krauter C M, Yazdi S, McClain M J, Ringe E, Carter E A, Nordlander P, Halas N J 2016 Proc. Natl. Acad. Sci. U. S. A. 113 8916 Google Scholar
[26]	Zhang X, Ke X, Yao J 2018 J. Mater. Chem. A 6 1941 Google Scholar
[27]	Kumar V, O'Donnell S C, Sang D L, Maggard P A, Wang G 2019 Front. Chem. 7 299 Google Scholar
[28]	Jiang L, Hassan M M, Ali S, Li H, Sheng R, Chen Q 2021 Trends Food Sci. Technol. 112 225 Google Scholar
[29]	Tian Y, Zhang H, Xu L, Chen M, Chen F 2018 Opt. Lett. 43 635 Google Scholar
[30]	Ting A S Y, Lee M V J, Chow Y Y, Cheong S L 2016 Water Air Soil Pollut. 227 109 Google Scholar
[31]	Meng M, Fang Z, Zhang C, Su H, He R, Zhang R, Li H, Li Z, Wu X, Ma C, Zeng J 2016 Nano Lett. 16 3036 Google Scholar
[32]	Huang C, Valinton J A A, Hung Y, Chen C 2018 Sens. Actuators, B 266 463 Google Scholar
[33]	Aparicio-Martínez E, Ibarra A, Estrada-Moreno I A, Osuna V, Dominguez R B 2019 Sens. Actuators, B 301 127101 Google Scholar
[34]	Asadian E, Ghalkhani M, Shahrokhian S 2019 Sens. Actuators, B 293 183 Google Scholar
[35]	Zhang R, Chen W 2017 Biosens. Bioelectron. 89 249 Google Scholar
[36]	Yao D, Li C, Liang A, Jiang Z 2019 Spectrochim. Acta, Part A 216 146 Google Scholar
[37]	Ma J, Feng G, Ying Y, Shao Y, She Y, Zheng L, Abd Ei-Aty A M, Wang J 2021 Analyst 146 956 Google Scholar

[1]	Du Li-Jie, Chen Jing-Wen, Wang Rong-Ming. Self-driven near infrared photoelectric detector based on C₁₄H₃₁O₃P-Ti₃C₂/Au Schottky junction. Acta Physica Sinica, 2023, 72(13): 138502. doi: 10.7498/aps.72.20230480
[2]	Zheng Lin-Qi, Shi Shu-Hua, Li Jin-Ze, Wang Zi-Yu, Li Shuang. Optimization of h-BN/Ag/Ag₂O heterostructure by high temperature annealing and its surface-enhanced Raman scattering performance. Acta Physica Sinica, 2023, 72(22): 227401. doi: 10.7498/aps.72.20231105
[3]	Zhao Yu-Chen, Zheng Jia-Huan, Wang Yong, Xi Xiao-Li, Song Hai-Zhi. Infrared broadband photoresponse characteristics of nanoporous NbN film. Acta Physica Sinica, 2022, 71(5): 058501. doi: 10.7498/aps.71.20211694
[4]	. Infrared Broadband Photoresponse Characteristics of Nanoporous NbN Film. Acta Physica Sinica, 2021, (): . doi: 10.7498/aps.70.20211694
[5]	Wang Xiang-Xian, Bai Xue-Lin, Pang Zhi-Yuan, Yang Hua, Qi Yun-Ping, Wen Xiao-Lei. Surface-enhanced Raman scattering effect of composite structure with gold nano-cubes and gold film separated by polymethylmethacrylate film. Acta Physica Sinica, 2019, 68(3): 037301. doi: 10.7498/aps.68.20190054
[6]	Li Jin-Hua, Zhang Si-Nan, Zhai Ying-Jiao, Ma Jian-Gang, Fang Wen-Hui, Zhang Yu. Development and application of MoS₂ and its metal composite surface enhanced Raman scattering substrates. Acta Physica Sinica, 2019, 68(13): 134203. doi: 10.7498/aps.68.20182113
[7]	Cheng Zi-Qiang, Shi Hai-Quan, Yu Ping, Liu Zhi-Min. Surface-enhanced Raman scattering effect of silver nanoparticles array. Acta Physica Sinica, 2018, 67(19): 197302. doi: 10.7498/aps.67.20180650
[8]	Tang Jian, Liu Ai-Ping, Li Pei-Gang, Shen Jing-Qin, Tang Wei-Hua. Surface-enhanced Raman scattering of gold/graphene oxide composite materials fabricated by interface self-assembling. Acta Physica Sinica, 2014, 63(10): 107801. doi: 10.7498/aps.63.107801
[9]	Zhang Zhe, Liu Qian, Qi Zhi-Mei. Study of Au-Ag alloy film based infrared surface plasmon resonance sensors. Acta Physica Sinica, 2013, 62(6): 060703. doi: 10.7498/aps.62.060703
[10]	Zhang Xin, Zhang Xiao-Zhong, Tan Xin-Yu, Yu Yi, Wan Cai-Hua. Enhancing photovoltaic effect of Co2-C98/Al2O3/Si heterostructures by Al2O3. Acta Physica Sinica, 2012, 61(14): 147303. doi: 10.7498/aps.61.147303
[11]	Huang Qian, Wang Jing, Cao Li-Ran, Sun Jian, Zhang Xiao-Dan, Geng Wei-Dong, Xiong Shao-Zhen, Zhao Ying. Research of surface enhanced Raman scattering caused by surface plasmon of Ag nano-structures. Acta Physica Sinica, 2009, 58(3): 1980-1986. doi: 10.7498/aps.58.1980
[12]	Huang Jin-Hua, Zhang Kun, Pan Nan, Gao Zhi-Wei, Wang Xiao-Ping. Enhancing ultraviolet photoresponse of ZnO nanowire device by surface functionalization. Acta Physica Sinica, 2008, 57(12): 7855-7859. doi: 10.7498/aps.57.7855
[13]	Liu Lin, Ye Yu-Tang, Wu Yun-Feng, Fang Liang, Lu Jia-Jia. Infrared characteristics of acidic droplet in different movement states on the surface of GaAs. Acta Physica Sinica, 2007, 56(6): 3172-3177. doi: 10.7498/aps.56.3172
[14]	Li Fa-Shen, Wang Tao, Wang Ying. Method for fabricating Fe3O4 nanoparticles using H2O2 and its comparison with coprecipitation method. Acta Physica Sinica, 2005, 54(7): 3100-3105. doi: 10.7498/aps.54.3100
[15]	XU KE-XI, ZHOU SHI-PING, BAO JIA-SHAN. NONLINEAR OPTICAL RESPONSE OF EPITAXIAL YBa2Cu3O7-δ FILMS. Acta Physica Sinica, 1998, 47(2): 307-315. doi: 10.7498/aps.47.307
[16]	YE XIAO-LAN, DENG WEN-JIE, LIANG ER-JUN. NEAR INFRARED SURFACE ENHANCED RAMAN-SCATTERING OF HALATE IONS. Acta Physica Sinica, 1997, 46(11): 2130-2137. doi: 10.7498/aps.46.2130
[17]	LIN JUN, ZHANG LI-ZHU, ZHANG BO-RUI, ZONG BO-QING, QIN GUO-GANG, XU ZHEN-HUA. PHOTOLUMINESCENCE OF POROUS SILICON PROCESSED IN H2O2 UNDER ILLUMINATION. Acta Physica Sinica, 1994, 43(4): 646-650. doi: 10.7498/aps.43.646
[18]	Chen Qun-qi; Lin Zhang-da; Ji Shang-xue;Xie Kan; Chang Ying-zhuan;Hou De-sen;Wang Tai-hong. STUDIES ON UPS AND XPS OF 0_2_ AND H_2_0 ABSORPTION ON SURFACES OF SrTi0_3_. Acta Physica Sinica, 1987, 36(8): 1075-1080. doi: 10.7498/aps.36.1075
[19]	HU YONG-JUN, LIN ZHANG-DA, WANG CHANG-HENG, XIE KAN. THE INFLUENCE OF O2 ON THE ELECTRONIC STRUCTURE OF CLEAN AND ION SPUTTERED SURFACES OF 2H-MoS2(0001). Acta Physica Sinica, 1986, 35(1): 50-57. doi: 10.7498/aps.35.50
[20]	YU XIN-NAN, ZHANG QING-ZHE, XIE KAN, QI SHANG-XUE, KANG JIN, LIN ZHANG-DA. THE SURFACE FEATURES OF THE POISONING OF LATHANIUM RICH MIXED RARE EARTH-NICKEL HYDROGEN STORAGE MATERIAL BY CO,O2 AND H2O. Acta Physica Sinica, 1983, 32(10): 1333-1338. doi: 10.7498/aps.32.1333

Catalog

Vol. 71, Issue 10 - 2022-05-20

Metrics

Abstract views: 5227
PDF Downloads: 92
Cited By: 0

姓名
邮箱
手机号码
标题
留言内容
验证码

Search

Article

留言板