本文基于注氢纯铁和铁基二元合金(Fe-3%Cr、Fe-1.4%Ni和Fe-1.4%Mn, 质量分数)开展常规透射电镜(200 kV)的原位表征观察, 揭示了材料中辐照位错环的形态、尺寸演化行为及退火温度影响, 并依据辐照损伤演化理论、退火过程中位错环平均尺寸变化推断得到空位型位错环形成温度的范围. 注氢纯铁中空位型位错环的形成温度(Tc)约为500 ℃; 添加Ni可使Tc降低至 ~450 ℃, 添加Cr可使Tc升高至600 ℃以上, 而Mn的作用与Cr相似, 亦可使Tc升高. 注氘实验和热脱附谱分析进一步表明, 纯铁和铁基二元合金中空位型位错环的形成温度受氢同位素与空位结合、释放过程影响. 合金元素Ni对氢同位素与空位的结合、释放有促进作用, 故导致Tc降低; 而Cr和Mn均对氢同位素与空位的结合、释放产生抑制作用, 故导致Tc升高. 本文展示的有关合金元素对空位型位错环形成温度影响的研究将有助于更深刻理解铁基合金体系中损伤结构演化和辐照肿胀产生机理.Reduced activation ferritic/martensitic (RAFM) steels have been considered as a family of prime candidate structural materials for fusion reactors due to low radioactivity and good resistance to irradiation swelling. Various types of defects such as dislocation loops can form in these materials during irradiation. Effects of alloying elements in iron on the formation and migration of dislocation loops have been widely investigated. However, most studies dealt with interstitial-type dislocation loops in iron alloys, while very few focused on vacancy-type dislocation loops. Previous high voltage electron microscope (HVEM) studies from the authors' group have shown that interstitial loops are fully eliminated in hydrogen-ion-implanted α-Fe at 500 ℃, only vacancy loops remain and can achieve up to 100 nm in size. The addition of Ni in α-Fe can reduce the formation temperature of vacancy-type dislocation loops (Tc) to ~450 ℃, while the addition of Cr can increase the temperature to above 600 ℃. However, these experiments are usually difficult to perform due to the scarce resource of HVEM facilities. In this work, in-situ observations by conventional transmission electron microscope (CTEM, 200 kV) are systematically carried out on the hydrogen-ion-implanted α-Fe and Fe-based binary alloys (Fe-3wt.%Cr, Fe-1.4wt.%Ni and Fe-1.4wt.%Mn). The evolutions of morphology and average size of dislocation loops under different annealing temperatures are investigated. The formation temperatures of vacancy-type dislocation loops are determined from the change of average loop size with annealing temperature. The results are consistent with previous studies by HVEM. The effect of Mn atoms in α-Fe is similar to that of Cr atoms, which leads to Tc increase, and the addition of Ni in α-Fe can reduce Tc. Furthermore, the results of D thermal desorption spectrum analysis show that Tc is affected by the binding and release process of hydrogen isotopes to vacancies in α-Fe. Alloying element Ni promotes the binding and release of hydrogen isotopes to vacancies, which leads to Tc decrease. Cr and Mn inhibit the binding and release of hydrogen isotopes to vacancies, causing Tc to increase.
-
Keywords:
- Fe-based binary alloy /
- H+/D+ ion implantation /
- vacancy-type dislocation loop /
- TEM
[1] Kano S, Yang H L, Suzue R, Matsukawa Y, Satoh Y, Sakasegawa H, Tanigawa H, Abe H 2016 Nucl. Mater. Energy 9 331
Google Scholar
[2] Hishinuma A, Kohyama A, Klueh R, Gelles D, Dietz W, Ehrlich K 1998 J. Nucl. Mater. 258–263 193
[3] Sojak S, Slugeň V, Petriska M, Veterníková JŠ, Stacho M, Sabelová V 2013 22nd International Conference Nuclear Energy for New Europe Bled, Slovenia September 8–13, 2013 p314
[4] 杜玉峰 2019 博士学位论文 (北京: 北京科技大学)
Du Y F 2019 Ph. D. Dissertation (Beijing: University of Science and Technology Beijing) (in Chinese)
[5] Kohno Y, Kohyama A, Hirose T, Hamilton M, Narui M 1999 J. Nucl. Mater. 272 145
[6] Klueh R, Alexander D, Rieth M 1999 J. Nucl. Mater. 273 146
Google Scholar
[7] Sacksteder I, Schneider H C, Materna-Morris E 2011 J. Nucl. Mater. 417 127
Google Scholar
[8] Schäublin R, Henry J, Dai Y 2008 Cr. Phys. 9 389
Google Scholar
[9] Dubinko V I, Kotrechko S A, Klepikov V F 2009 Radiat. Eff. Defect. S. 164 647
Google Scholar
[10] 姜少宁, 万发荣, 龙毅 刘传歆, 詹倩, 大貫惣明 2013 物理学报 62 166801
Google Scholar
Jiang S N, Wan F R, Long Y, Liu C X, Zhan Q, Ohnuki S. 2013 Acta Phys. Sin. 62 166801
Google Scholar
[11] Osetsky Y N, Serra A, Singh B N, Golubov S I 2000 Philos. Mag. A 80 2131
Google Scholar
[12] Kim S M, Buyers W 1978 J. Phys. F:Metal Physics 8 L103
Google Scholar
[13] Willaime F, Fu C C, Marinica M C, Dalla Torre J 2005 Nucl. Instrum. Meth. B 228 92
Google Scholar
[14] Hashimoto N, Sakuraya S, Tanimoto J, Ohnuki S 2014 J. Nucl. Mater. 445 224
Google Scholar
[15] 万发荣 2020 工程科学学报 42 1535
Wan F R 2020 Chinese J. Eng. 42 1535
[16] Hoelzer D T, Ebrahimi F 1994 MRS Online Proceedings Library 373 57
Google Scholar
[17] Ward A, Fisher S B 1989 J. Nucl. Mater. 166(3) 227
[18] Chen L, Murakami K, Chen D, Abe H, Li Z, Sekimura N 2020 Scripta Mater. 187 453
Google Scholar
[19] Mizandrontsev D B, Vasiliev A A 2000 Proceedings of SPIE-The International Society for Optical Engineering 4064 220
[20] Eyre B L, Bartlett A F 1965 Philos. Mag. 12 261
Google Scholar
[21] Masters B C 1965 Philos. Mag. 11 881
Google Scholar
[22] Yabuuchi K, Saito M, Kasada R, Kimura A 2011 J. Nucl. Mater. 414 498
Google Scholar
[23] Yabuuchi K, Kasada R, Kimura A 2013 Acta Mater. 61 6517
Google Scholar
[24] Watanabe H, Masaki S, Masubuchi S, Yoshida N, Dohi K 2013 J. Nucl. Mater. 439 268
Google Scholar
[25] Horton L L, Bentley J, Farrell K 1982 J. Nucl. Mater. 108 222
[26] Wirth B D, Odette G R, Maroudas D, Lucas G E 2000 J. Nucl. Mater. 276 33
Google Scholar
[27] Terentyev D, Grammatikopoulos P, Bacon D J, Osetsky Y N 2008 Acta Mater. 56 5034
Google Scholar
[28] Zhang W P, Song L G, Zhu T, Xiong Y, Ma H L, Yan Q Z, Cao X Z, Wang B Y, Jin S X 2021 J. Nucl. Mater. 548 152862
Google Scholar
[29] Gao N, Perez D, Lu G H, Wang Z G 2018 J. Nucl. Mater. 498 378
Google Scholar
[30] Kiritani M, Yoshiie T, Iseki M, Kojima S, Hamada K, Horiki M, Kizuka Y, Inoue H, Tada T, Ogasawara Y 1994 J. Nucl. Mater. 212 241
[31] Wei Y X, Gao N, Shen Z Y, Chen C, Xie Z Y, Guo L P 2020 Comp. Mater. Sci. 180 109724
Google Scholar
[32] Pan X D, Lu T, Lyu Y M, Xu Y P, Zhou H S, Yang Z S, Niu G J, Li X C, Gao F, Luo G N 2020 J. Nucl. Mater. 542 152500
Google Scholar
[33] Wei Y X, Gao N, Wang D, Chen C, Guo L P 2019 Nucl. Instrum. Meth. B 461 83
Google Scholar
[34] Huang Y N, Wan F R, Xiao X, Shi S, Long Y, Ohnuki S, Hashimoto N 2010 Fusion Eng. Des. 85 2203
Google Scholar
[35] Wan F R, Ohnuki S, Takahashi H, Takeyama T, Nagasaki R 1986 Philos. Mag. A 53 L21
Google Scholar
[36] Gao J, Du Y, Ohnuki S, Wan F 2016 J. Nucl. Mater. 481 81
Google Scholar
[37] Wan F R, Zhan Q, Long Y, Yang S W, Zhang G W, Du Y F, Jiao Z J, Ohnuki S 2014 J. Nucl. Mater. 455 253
Google Scholar
[38] Du Y F, Cui L J, Han W T, Wan F R 2019 Acta Metall. Sin-Engl. 32 566
Google Scholar
[39] Foll H, Wilkens M 1975 Phys. Status Solidi A 31 519
Google Scholar
[40] 黄依娜, 万发荣, 焦治杰 2011 物理学报 60 509
Google Scholar
Huang Y N, Wan F R, Jiao Z J 2011 Acta Phys. Sin. 60 509
Google Scholar
[41] Stoller R E, Toloczko M B, Was G S, Certain A G, Dwaraknath S, Garner F A 2013 Nucl. Instrum. Meth. B 310 75
Google Scholar
[42] ASTM-Committee 2003 Standard Practice for Neutron Radiation Damage Simulation by Charged-particle Irradiation (West Conshohocken: Copyright © ASTM International) p8
[43] 颜强 2017 博士学位论文 (哈尔滨: 哈尔滨工程大学)
Yan Q 2017 Ph. D. Dissertation (Harbin: Harbin Engineering University) (in Chinese)
[44] 万发荣 1993 金属材料的辐照损伤 (北京: 科学出版社) 第85页
Wan F R 1993 Irradiation Damage of Metal Materials (Beijing: Science Press) p85 (in Chinese)
[45] Morishita K, Sugano R, Wirth B D, de La Rubia T D 2003 Nucl. Instrum. Meth. B 202 76
Google Scholar
[46] 徐玉平 2017 博士学位论文 (合肥: 中国科学技术大学)
Xu Y P 2017 Ph. D. Dissertation (Hefei: University of Science and Technology of China) (in Chinese)
[47] Sugano R, Morishita K, Iwakiri H, Yoshida N 2002 J. Nucl. Mater. 307 941
[48] Sugano R, Morishita K, Kimura A, Iwakiri H, Yoshida N 2004 J. Nucl. Mater. 329 942
-
图 1 实验过程示意图 (a)不同退火温度下位错环的TEM原位观察; (b) TDS实验. 铁基合金指Fe-3Cr, Fe-1.4Ni和Fe-1.4Mn
Fig. 1. A schematic illustration of experiment procedures: (a) In-situ TEM observation of dislocation loops at different annealing temperatures; (b) TDS experiment. Fe-based binary alloys refer to Fe-3Cr, Fe-1.4Ni and Fe-1.4Mn.
图 2 SRIM 2013模拟注氢纯铁的辐照损伤量(dpa)和氢离子浓度(H, at.%)随注入深度的分布情况. 纯铁离位阈能为40 eV[43]. 辐照条件: 30 keV H+, 1.0 × 1021 ions /m2
Fig. 2. SRIM 3013 calculated depth profiles of displacement damage (dpa) and hydrogen concentration (H, at.%) in H+ ion implanted pure Fe. Displacement threshold energy of pure Fe: 40 eV[43]. Irradiation condition: 30 keV H+, 1.0 × 1021 ions /m2.
图 3 辐照位错环在恒定时间内(本文指20 min)、不同退火温度下的形态和尺寸演化示意图. 尺寸表示位错环的平均尺寸, 阶段II-IV指辐照缺陷的第II至IV热回复阶段[44]
Fig. 3. A schematic diagram illustrating the morphology/size evolution of irradiation-induced dislocation loops during post-irradiation isochronal annealing for 20 min. ‘Loop size’ refers to the average size of dislocation loops. Stages ‘II-IV’ refer to the thermal recovery stages of radiation defects [44].
图 4 注氢纯铁/铁基二元合金中位错环在辐照后退火过程中的演化. 辐照条件: 30 keV H+, 1.0 × 1021 ions/m2, 25 ℃; 辐照后退火条件: 400—600 ℃, 20 min; 成像条件: 双束运动学明场像, g = 200
Fig. 4. Loop evolution in H+ ion implanted Fe/Fe-based binary alloys during post-irradiation annealing (PIA) treatment. Irradiation condition: 30 keV H+, 1.0 × 1021 ions/m2, 25 ℃. PIA condition: 400–600 ℃, 20 min. Imaging condition: two-beam kinematical bright-field, g = 200.
图 5 注氢纯铁/铁基二元合金中位错环在辐照后退火过程中的平均尺寸变化. 辐照条件: 30 keV H+, 1.0 × 1021 ions/m2, 25 ℃. 辐照后退火条件: 400—600 ℃, 20 min.
Fig. 5. Average loop size changes in H+ ion implanted Fe/Fe-based binary alloys during post-irradiation annealing (PIA) treatment. Irradiation condition: 30 keV H+, 1.0 × 1021 ions/m2, 25 ℃. PIA condition: 400–600 ℃, 20 min.
图 6 注氘纯铁/铁基二元合金的热脱附谱图. 辐照条件: 30 keV D+, 1.0 × 1021 ions /m2, 25 ℃.
Fig. 6. Thermal desorption spectra of deuterium in D+ ion implanted Fe/Fe-based binary alloys. Irradiation condition: 30 keV D+, 1.0 × 1021 ions /m2, 25 ℃.
表 1 纯铁/铁基二元合金离子辐照条件
Table 1. Ion irradiation conditions of Fe/Fe-based binary alloys.
材料 用途 温度/℃ 注入离子 注入能量/keV 注入剂量/(ions·m–2) 纯铁/铁基二元合金* TEM 25 H+ 30 1×1021 TDS 25 D+ 30 1×1021 注: *铁基二元合金指Fe-3Cr, Fe-1.4Ni和Fe-1.4Mn合金. 
下载: 导出CSV
-
[1] Kano S, Yang H L, Suzue R, Matsukawa Y, Satoh Y, Sakasegawa H, Tanigawa H, Abe H 2016 Nucl. Mater. Energy 9 331
Google Scholar
[2] Hishinuma A, Kohyama A, Klueh R, Gelles D, Dietz W, Ehrlich K 1998 J. Nucl. Mater. 258–263 193
[3] Sojak S, Slugeň V, Petriska M, Veterníková JŠ, Stacho M, Sabelová V 2013 22nd International Conference Nuclear Energy for New Europe Bled, Slovenia September 8–13, 2013 p314
[4] 杜玉峰 2019 博士学位论文 (北京: 北京科技大学)
Du Y F 2019 Ph. D. Dissertation (Beijing: University of Science and Technology Beijing) (in Chinese)
[5] Kohno Y, Kohyama A, Hirose T, Hamilton M, Narui M 1999 J. Nucl. Mater. 272 145
[6] Klueh R, Alexander D, Rieth M 1999 J. Nucl. Mater. 273 146
Google Scholar
[7] Sacksteder I, Schneider H C, Materna-Morris E 2011 J. Nucl. Mater. 417 127
Google Scholar
[8] Schäublin R, Henry J, Dai Y 2008 Cr. Phys. 9 389
Google Scholar
[9] Dubinko V I, Kotrechko S A, Klepikov V F 2009 Radiat. Eff. Defect. S. 164 647
Google Scholar
[10] 姜少宁, 万发荣, 龙毅 刘传歆, 詹倩, 大貫惣明 2013 物理学报 62 166801
Google Scholar
Jiang S N, Wan F R, Long Y, Liu C X, Zhan Q, Ohnuki S. 2013 Acta Phys. Sin. 62 166801
Google Scholar
[11] Osetsky Y N, Serra A, Singh B N, Golubov S I 2000 Philos. Mag. A 80 2131
Google Scholar
[12] Kim S M, Buyers W 1978 J. Phys. F:Metal Physics 8 L103
Google Scholar
[13] Willaime F, Fu C C, Marinica M C, Dalla Torre J 2005 Nucl. Instrum. Meth. B 228 92
Google Scholar
[14] Hashimoto N, Sakuraya S, Tanimoto J, Ohnuki S 2014 J. Nucl. Mater. 445 224
Google Scholar
[15] 万发荣 2020 工程科学学报 42 1535
Wan F R 2020 Chinese J. Eng. 42 1535
[16] Hoelzer D T, Ebrahimi F 1994 MRS Online Proceedings Library 373 57
Google Scholar
[17] Ward A, Fisher S B 1989 J. Nucl. Mater. 166(3) 227
[18] Chen L, Murakami K, Chen D, Abe H, Li Z, Sekimura N 2020 Scripta Mater. 187 453
Google Scholar
[19] Mizandrontsev D B, Vasiliev A A 2000 Proceedings of SPIE-The International Society for Optical Engineering 4064 220
[20] Eyre B L, Bartlett A F 1965 Philos. Mag. 12 261
Google Scholar
[21] Masters B C 1965 Philos. Mag. 11 881
Google Scholar
[22] Yabuuchi K, Saito M, Kasada R, Kimura A 2011 J. Nucl. Mater. 414 498
Google Scholar
[23] Yabuuchi K, Kasada R, Kimura A 2013 Acta Mater. 61 6517
Google Scholar
[24] Watanabe H, Masaki S, Masubuchi S, Yoshida N, Dohi K 2013 J. Nucl. Mater. 439 268
Google Scholar
[25] Horton L L, Bentley J, Farrell K 1982 J. Nucl. Mater. 108 222
[26] Wirth B D, Odette G R, Maroudas D, Lucas G E 2000 J. Nucl. Mater. 276 33
Google Scholar
[27] Terentyev D, Grammatikopoulos P, Bacon D J, Osetsky Y N 2008 Acta Mater. 56 5034
Google Scholar
[28] Zhang W P, Song L G, Zhu T, Xiong Y, Ma H L, Yan Q Z, Cao X Z, Wang B Y, Jin S X 2021 J. Nucl. Mater. 548 152862
Google Scholar
[29] Gao N, Perez D, Lu G H, Wang Z G 2018 J. Nucl. Mater. 498 378
Google Scholar
[30] Kiritani M, Yoshiie T, Iseki M, Kojima S, Hamada K, Horiki M, Kizuka Y, Inoue H, Tada T, Ogasawara Y 1994 J. Nucl. Mater. 212 241
[31] Wei Y X, Gao N, Shen Z Y, Chen C, Xie Z Y, Guo L P 2020 Comp. Mater. Sci. 180 109724
Google Scholar
[32] Pan X D, Lu T, Lyu Y M, Xu Y P, Zhou H S, Yang Z S, Niu G J, Li X C, Gao F, Luo G N 2020 J. Nucl. Mater. 542 152500
Google Scholar
[33] Wei Y X, Gao N, Wang D, Chen C, Guo L P 2019 Nucl. Instrum. Meth. B 461 83
Google Scholar
[34] Huang Y N, Wan F R, Xiao X, Shi S, Long Y, Ohnuki S, Hashimoto N 2010 Fusion Eng. Des. 85 2203
Google Scholar
[35] Wan F R, Ohnuki S, Takahashi H, Takeyama T, Nagasaki R 1986 Philos. Mag. A 53 L21
Google Scholar
[36] Gao J, Du Y, Ohnuki S, Wan F 2016 J. Nucl. Mater. 481 81
Google Scholar
[37] Wan F R, Zhan Q, Long Y, Yang S W, Zhang G W, Du Y F, Jiao Z J, Ohnuki S 2014 J. Nucl. Mater. 455 253
Google Scholar
[38] Du Y F, Cui L J, Han W T, Wan F R 2019 Acta Metall. Sin-Engl. 32 566
Google Scholar
[39] Foll H, Wilkens M 1975 Phys. Status Solidi A 31 519
Google Scholar
[40] 黄依娜, 万发荣, 焦治杰 2011 物理学报 60 509
Google Scholar
Huang Y N, Wan F R, Jiao Z J 2011 Acta Phys. Sin. 60 509
Google Scholar
[41] Stoller R E, Toloczko M B, Was G S, Certain A G, Dwaraknath S, Garner F A 2013 Nucl. Instrum. Meth. B 310 75
Google Scholar
[42] ASTM-Committee 2003 Standard Practice for Neutron Radiation Damage Simulation by Charged-particle Irradiation (West Conshohocken: Copyright © ASTM International) p8
[43] 颜强 2017 博士学位论文 (哈尔滨: 哈尔滨工程大学)
Yan Q 2017 Ph. D. Dissertation (Harbin: Harbin Engineering University) (in Chinese)
[44] 万发荣 1993 金属材料的辐照损伤 (北京: 科学出版社) 第85页
Wan F R 1993 Irradiation Damage of Metal Materials (Beijing: Science Press) p85 (in Chinese)
[45] Morishita K, Sugano R, Wirth B D, de La Rubia T D 2003 Nucl. Instrum. Meth. B 202 76
Google Scholar
[46] 徐玉平 2017 博士学位论文 (合肥: 中国科学技术大学)
Xu Y P 2017 Ph. D. Dissertation (Hefei: University of Science and Technology of China) (in Chinese)
[47] Sugano R, Morishita K, Iwakiri H, Yoshida N 2002 J. Nucl. Mater. 307 941
[48] Sugano R, Morishita K, Kimura A, Iwakiri H, Yoshida N 2004 J. Nucl. Mater. 329 942
-
[1] 李然然, 张一帆, 殷玉鹏, 渡边英雄, 韩文妥, 易晓鸥, 刘平平, 张高伟, 詹倩, 万发荣. 注氢纯铝中间隙型位错环一维迁移现象的原位观察. 物理学报, 2022, 71(1): 016102. doi: 10.7498/aps.71.20211229 [2] 李然然, 张一帆, 殷玉鹏, 渡边英雄, 韩文妥, 易晓鸥, 刘平平, 张高伟, 詹倩, 万发荣. 注氢纯铝中间隙型位错环一维迁移现象的原位观察. 物理学报, 2021, (): . doi: 10.7498/aps.70.20211229 [3] 梁晋洁, 高宁, 李玉红. 表面效应对铁 ${\left\langle 100 \right\rangle} $ 间隙型位错环的影响. 物理学报, 2020, 69(3): 036101. doi: 10.7498/aps.69.20191379[4] 熊雨薇, 尹奎波, 文一峰, 辛磊, 姚利兵, 朱重阳, 孙立涛. 纳米氧化锡负极材料锂化反应机理的原位透射电镜研究. 物理学报, 2019, 68(15): 158201. doi: 10.7498/aps.68.20190431 [5] 黎栋栋, 周武. 二维原子晶体的低电压扫描透射电子显微学研究. 物理学报, 2017, 66(21): 217303. doi: 10.7498/aps.66.217303 [6] 崔丽娟, 高进, 杜玉峰, 张高伟, 张磊, 龙毅, 杨善武, 詹倩, 万发荣. 氢离子辐照纯钒中形成的位错环. 物理学报, 2016, 65(6): 066102. doi: 10.7498/aps.65.066102 [7] 林志宇, 张进成, 许晟瑞, 吕玲, 刘子扬, 马俊彩, 薛晓咏, 薛军帅, 郝跃. 斜切蓝宝石衬底MOCVD生长GaN薄膜的透射电镜研究. 物理学报, 2012, 61(18): 186103. doi: 10.7498/aps.61.186103 [8] 黄依娜, 万发荣, 焦治杰. 利用透射电镜衬度像变化判定位错环类型及注氢纯铁中形成的位错环分析. 物理学报, 2011, 60(3): 036802. doi: 10.7498/aps.60.036802 [9] 徐 进, 李福龙, 杨德仁. 直拉硅单晶中原生氧沉淀的透射电镜研究. 物理学报, 2007, 56(7): 4113-4116. doi: 10.7498/aps.56.4113 [10] 刘向绯, 蒋昌忠, 任 峰, 付 强. Ag离子注入非晶SiO2的光学吸收、拉曼谱和透射电镜研究. 物理学报, 2005, 54(10): 4633-4637. doi: 10.7498/aps.54.4633 [11] 徐 进, 杨德仁, 储 佳, 马向阳, 阙端麟. 微氮直拉硅单晶中氧化诱生层错透射电镜研究. 物理学报, 2004, 53(2): 550-554. doi: 10.7498/aps.53.550 [12] 万发荣, 褚武扬, 肖纪美, 高桥平七郎. 注氢Fe-1wt%Ni合金中的辐照诱导偏析. 物理学报, 1999, 48(8): 1491-1495. doi: 10.7498/aps.48.1491 [13] 赵庆兰, 关铁堂. 邻苯二甲酸氢铊单晶位错的Borrmann象衬度. 物理学报, 1993, 42(4): 626-630. doi: 10.7498/aps.42.626 [14] 杨顺华, 李国旺, 黄军平. 二相介质中的运动位错. 物理学报, 1991, 40(5): 771-780. doi: 10.7498/aps.40.771 [15] 郭可信, 林保军. 镍铬合金中不全位错的透射电子显微镜观察. 物理学报, 1980, 29(4): 494-499. doi: 10.7498/aps.29.494 [16] 郭可信, 林保军. 镍铬合金中的位错运动与位错反应. 物理学报, 1978, 27(6): 729-745. doi: 10.7498/aps.27.729 [17] 孔庆平, 龙起易. 用电子显微镜透射方法研究一种镍基合金高温蠕变过程的位错结构. 物理学报, 1975, 24(2): 83-86. doi: 10.7498/aps.24.83 [18] 邢修三. 空位位错环的形成. 物理学报, 1966, 22(5): 541-546. doi: 10.7498/aps.22.541 [19] 张修睦, 林保军, 郭可信. 铝镁合金中位错网络与位错子反应的电显微镜透射观察. 物理学报, 1965, 21(2): 476-480. doi: 10.7498/aps.21.476 [20] 杨顺华. 位错环与点阵空位间的弹性相互作用. 物理学报, 1964, 20(8): 720-727. doi: 10.7498/aps.20.720
下载:
计量
- 文章访问数: 4444
- PDF下载量: 63
- 被引次数: 0