Gallium oxide (Ga2O3) single crystal nanoribbons have the potential applications in electronic devices due to their unique properties. However, the current small surface area makes the fabrication of device based on this nano-material very complex and challenging, and the introduction of catalyst also makes the growth process of Ga2O3 nanomaterial complicated and hard to control. Therefore, it is very important to study the growth method and physical mechanism of Ga2O3 nanoribbon with the larger surface area without catalyst. In this paper, the carbothermal reduction method is used to grow the Ga2O3 nanomaterial. In this paper, the gallium oxide powder mixes with the carbon nanotubes at a mass ratio of 1:1.5 without the catalyst, and then they are put into a high temperature diffusion furnace for the growth of Ga2O3 nanomaterials with different structures on silicon-based substrates by controlling the reaction temperature. In this paper, it is found that the reaction temperature directly affects the diameter and ratio of gallium oxide nanostructures. The reason is that the bonding energy of gallium oxide crystal is different in different crystal directions which leads to the different growth speed. The interface energy along the growth direction is the smallest and the growth speed is the fastest, while the growth speed along the vertical direction is slow. Finally, the crystal gradually grows into nanoriband, nanometer sheet and other structures. In addition, the ultra-wide β-Ga2O3 single crystal nanobelt up to the millimeter level was prepared in this paper. This nanobelt’s lateral dimension is observed to reach 44.3 μm under the scanning electron microscope (SEM), and the transmission electron microscope (TEM) is used to confirm that the nanoribbons have a single crystal structure. Further, Raman spectroscopy (Raman) shows that the β-Ga2O3 nanoribbons grown by this method have the smaller strain and the lower defect density. Additionally, the room temperature photoluminescence spectrum (PL) test shows that the gallium oxide nanoribbon emits a stable and high-brightness blue light at 425 nm at the excitation wavelength of 295 nm. This growth method can provide a useful way for the preparation of device-level gallium oxide nanoribbons in the future. -
Keywords:
- β-Ga2O3 /
- carbothermal reduction /
- crystal nanoribbons /
- defect density
[1] 冯秋菊, 李芳, 李彤彤, 李昀铮, 石博, 李梦轲, 梁红伟 2018 物理学报 67 218101
Google Scholar
Feng Q J, Li F, Li T T, Li X Z, Shi B, Li M K, Liang H W 2018 Acta Phys. Sin. 67 218101
Google Scholar
[2] Guo D, Guo Q, Chen Z, Wu Z, Li P, Tang W 2019 Mater. Today Phys. 11 100157
Google Scholar
[3] Wang H, Wang Y, Gong S Y, Zhou X Y, Yang Z X, Yang J, Han N, Chen Y F 2019 Cryst. 9 155
Google Scholar
[4] Ma J W, Fan H Q, Zheng X K, Wang H, Zhao N, Zhang M C, Yadav A K, Wang W J, Dong W Q, Wang S R 2020 J. Hazard. Mater. 387 122017
Google Scholar
[5] 郑树文, 范广涵, 何苗, 赵灵智 2014 物理学报 63 057102
Google Scholar
Zheng S W, Fan G H, He M, Zhao L Z 2014 Acta Phys. Sin. 63 057102
Google Scholar
[6] He T, Zhang X D, Ding X Y, Sun C, Zhao Y K, Yu Q, Ning J, Wang R X, Yu G H, Lu S L, Zhang K, Zhang X P, Zhang B S 2019 Adv. Opt. Mater. 7 1801563
Google Scholar
[7] Wu Z Y, Jiang Z X, Song P Y, Tian P F, Hu L G, Liu R, Fang Z L, Kang J Y, Zhang T Y 2019 Small 15 1900580
Google Scholar
[8] Afzal A 2019 J. Materiomics 5 542
Google Scholar
[9] Gundiah G, Govindaraj A, Rao C 2002 Chem. Phys. Lett. 351 189
Google Scholar
[10] Cha S Y, Ahn B G, Ka ng, H C, Lee S Y, Noh D Y 2018 Ceram. Int. 44 16470
Google Scholar
[11] Tang C C, Fan S S, Chapelle M L, Li P 2001 Chem. Phys. Lett. 333 12
Google Scholar
[12] Feng Q Y, Liu J Y, Yang Y Q, Pan D Z, Xing Y, Shi X C, Xia X C and Liang H 2016 J. Alloys Compd. 687 964
Google Scholar
[13] Alhalaili B, Bunk R, Vidu R, Islam M S 2019 Nanomaterials 9 1272
Google Scholar
[14] Fang J W, Fan H Q, Tian H L, Dong G Z 2015 Mater. Charact. 108 51
Google Scholar
[15] Kumar M, Kumar V, Singh R 2017 Scr. Mater. 138 75
Google Scholar
[16] Calestani D, Alabib A B, Coppede N, Villani M, Lazzarini L, Fabbri F, Salviati G, Zappettinia A 2017 J. Cryst. Growth 457 255
Google Scholar
[17] Feng Q J, Lia T T, Lia F, Lia Y Z, Shi B, Gao C, Wang D Y, Liang H W 2019 J. Cryst. Growth 509 91
Google Scholar
[18] Korbutowicz R, Stafiniak A, Serafinczuk J 2017 Mater. Sci-Poland 35 412
Google Scholar
[19] Wang S, Li Y W, Xiu X Q, Zhang L Y, Hua X M, Xie Z L, Tao T, Liu B, Chen P, Zhang R, Zheng Y D 2019 Chin. Phys. B 28 028104
Google Scholar
[20] Kumar M, Kumar V, Singh R 2017 Nano Res. Lett. 12 184
Google Scholar
[21] Li J, Fan H Q, Chen X P, Cao Z Y 2009 Colloid. Surf., A 349 202
Google Scholar
[22] Wang S L, Sun H L, Wang Z, Zeng X H, Ungar G, Guo D Y, Shen J Y, Li P G, Liu A P, Li C R, Tang W H 2019 J. Alloys Compd. 787 133
Google Scholar
[23] Gonzalo A, Nogales E, Lorenz K, Víllora E G, Shimamura K, Piqueras J, Méndez B 2017 J. Lumin. 191 56
Google Scholar
[24] Hu D Q, Zhuang S W, Dong X, Du G T, Zhang B L, Zhang Y T, Yin J Z 2018 Mater. Sci. Semicond. Process. 75 31
Google Scholar
[25] Dohy D, Lucazeau G 1982 J. Mol. Struct. 79 419
Google Scholar
[26] Alonso-Orts M, Sanchez A M, Lopez I, Nogales E, Piquerasa J, Mendeza B 2017 Cryst. Eng. Commun. 19 6217
Google Scholar
[27] Cheng J P, Zhang X B, Kong F Z, Ye Y, Tao X Y 2006 Rare Met. Mater. Eng. 35 1629
Google Scholar
[28] Binet L, Gourier D 1998 J. Phys. Chem. Solids 59 1241
Google Scholar
[29] Harwig T, Kellendonk F 1978 J. Solid State Chem. 24 255
Google Scholar
[30] Harwig T, Kellendonk F, Slappendel S 1978 J. Phys. Chem. Solids 39 675
Google Scholar
[31] Li J, Fan H Q, Jia X H, Chen J, Cao Z Y, Chen X P 2009 J. Alloys Compd. 481 735
Google Scholar
-
图 1 样品A—D在不同生长温度下的SEM图像 (a) 样品A (800 ℃); (b) 样品B (850 ℃); (c) 样品C (900 ℃); (d) 样品D (950 ℃)
Figure 1. SEM images of samples a-d at different growth temperatures: (a) Sample A (800 ℃); (b) sample B (850 ℃); (c) sample C (900 ℃); (d) sample D (950 ℃).
图 2 (a) 低倍镜下样品C超长的氧化镓纳米带; (b) 样品C高倍率下单个氧化镓纳米带; (c)互相缠绕弯曲的纳米带; (d) 高倍镜下样品D纳米带表面结块恶化
Figure 2. (a) The ultra-long gallium oxide nanoribbons of sample C under low magnification; (b) single gallium oxide nanoribbon at high magnification of sample C; (c) intertwined curved nanoribbons; (d) under high power, the agglomeration of the surface of the sample D nanoribbons deteriorates.
图 3 (a)样品C的X射线衍射图; (b)样品C的拉曼光谱
Figure 3. (a) X-ray diffraction pattern of the sample C; (b) raman of the sample C.
图 4 (a) 样品C的TEM图像, 插图显示了SAED模式; (b) 样品C的HR-TEM图像
Figure 4. (a) TEM image of the sample C. Inset shows the SAED pattern; (b) HR-TEM image of the sample C.
图 5 β-Ga2O3纳米带的室温PL光谱
Figure 5. Room temperature PL spectra of β-Ga2O3 nanowires.
表 1 样品A—D在不同温度下的生长参数
Table 1. The growth parameters of samples A–D at different temperature.
Samples Ga2O3/g CNTs/g Growth temperature/℃ Times/min N2 carrier gas /sccm A 1 1.5 800 90 2 B 1 1.5 850 90 2 C 1 1.5 900 90 2 D 1 1.5 950 90 2 
DownLoad: CSV
-
[1] 冯秋菊, 李芳, 李彤彤, 李昀铮, 石博, 李梦轲, 梁红伟 2018 物理学报 67 218101
Google Scholar
Feng Q J, Li F, Li T T, Li X Z, Shi B, Li M K, Liang H W 2018 Acta Phys. Sin. 67 218101
Google Scholar
[2] Guo D, Guo Q, Chen Z, Wu Z, Li P, Tang W 2019 Mater. Today Phys. 11 100157
Google Scholar
[3] Wang H, Wang Y, Gong S Y, Zhou X Y, Yang Z X, Yang J, Han N, Chen Y F 2019 Cryst. 9 155
Google Scholar
[4] Ma J W, Fan H Q, Zheng X K, Wang H, Zhao N, Zhang M C, Yadav A K, Wang W J, Dong W Q, Wang S R 2020 J. Hazard. Mater. 387 122017
Google Scholar
[5] 郑树文, 范广涵, 何苗, 赵灵智 2014 物理学报 63 057102
Google Scholar
Zheng S W, Fan G H, He M, Zhao L Z 2014 Acta Phys. Sin. 63 057102
Google Scholar
[6] He T, Zhang X D, Ding X Y, Sun C, Zhao Y K, Yu Q, Ning J, Wang R X, Yu G H, Lu S L, Zhang K, Zhang X P, Zhang B S 2019 Adv. Opt. Mater. 7 1801563
Google Scholar
[7] Wu Z Y, Jiang Z X, Song P Y, Tian P F, Hu L G, Liu R, Fang Z L, Kang J Y, Zhang T Y 2019 Small 15 1900580
Google Scholar
[8] Afzal A 2019 J. Materiomics 5 542
Google Scholar
[9] Gundiah G, Govindaraj A, Rao C 2002 Chem. Phys. Lett. 351 189
Google Scholar
[10] Cha S Y, Ahn B G, Ka ng, H C, Lee S Y, Noh D Y 2018 Ceram. Int. 44 16470
Google Scholar
[11] Tang C C, Fan S S, Chapelle M L, Li P 2001 Chem. Phys. Lett. 333 12
Google Scholar
[12] Feng Q Y, Liu J Y, Yang Y Q, Pan D Z, Xing Y, Shi X C, Xia X C and Liang H 2016 J. Alloys Compd. 687 964
Google Scholar
[13] Alhalaili B, Bunk R, Vidu R, Islam M S 2019 Nanomaterials 9 1272
Google Scholar
[14] Fang J W, Fan H Q, Tian H L, Dong G Z 2015 Mater. Charact. 108 51
Google Scholar
[15] Kumar M, Kumar V, Singh R 2017 Scr. Mater. 138 75
Google Scholar
[16] Calestani D, Alabib A B, Coppede N, Villani M, Lazzarini L, Fabbri F, Salviati G, Zappettinia A 2017 J. Cryst. Growth 457 255
Google Scholar
[17] Feng Q J, Lia T T, Lia F, Lia Y Z, Shi B, Gao C, Wang D Y, Liang H W 2019 J. Cryst. Growth 509 91
Google Scholar
[18] Korbutowicz R, Stafiniak A, Serafinczuk J 2017 Mater. Sci-Poland 35 412
Google Scholar
[19] Wang S, Li Y W, Xiu X Q, Zhang L Y, Hua X M, Xie Z L, Tao T, Liu B, Chen P, Zhang R, Zheng Y D 2019 Chin. Phys. B 28 028104
Google Scholar
[20] Kumar M, Kumar V, Singh R 2017 Nano Res. Lett. 12 184
Google Scholar
[21] Li J, Fan H Q, Chen X P, Cao Z Y 2009 Colloid. Surf., A 349 202
Google Scholar
[22] Wang S L, Sun H L, Wang Z, Zeng X H, Ungar G, Guo D Y, Shen J Y, Li P G, Liu A P, Li C R, Tang W H 2019 J. Alloys Compd. 787 133
Google Scholar
[23] Gonzalo A, Nogales E, Lorenz K, Víllora E G, Shimamura K, Piqueras J, Méndez B 2017 J. Lumin. 191 56
Google Scholar
[24] Hu D Q, Zhuang S W, Dong X, Du G T, Zhang B L, Zhang Y T, Yin J Z 2018 Mater. Sci. Semicond. Process. 75 31
Google Scholar
[25] Dohy D, Lucazeau G 1982 J. Mol. Struct. 79 419
Google Scholar
[26] Alonso-Orts M, Sanchez A M, Lopez I, Nogales E, Piquerasa J, Mendeza B 2017 Cryst. Eng. Commun. 19 6217
Google Scholar
[27] Cheng J P, Zhang X B, Kong F Z, Ye Y, Tao X Y 2006 Rare Met. Mater. Eng. 35 1629
Google Scholar
[28] Binet L, Gourier D 1998 J. Phys. Chem. Solids 59 1241
Google Scholar
[29] Harwig T, Kellendonk F 1978 J. Solid State Chem. 24 255
Google Scholar
[30] Harwig T, Kellendonk F, Slappendel S 1978 J. Phys. Chem. Solids 39 675
Google Scholar
[31] Li J, Fan H Q, Jia X H, Chen J, Cao Z Y, Chen X P 2009 J. Alloys Compd. 481 735
Google Scholar
-
[1] Su Ran, Xi Zhao-Ying, Li Shan, Zhang Jia-Han, Jiang Ming-Ming, Liu Zeng, Tang Wei-Hua. GaSe/β-Ga2O3 heterojunction based self-powered solar-blind ultraviolet photoelectric detector. Acta Physica Sinica, 2024, 73(11): 118502. doi: 10.7498/aps.73.20240267 [2] Yi Zi-Qi, Wang Yan-Ming, Wang Shuo, Sui Xue, Shi Jia-Hui, Yang Yi-Han, Wang De-Yu, Feng Qiu-Ju, Sun Jing-Chang, Liang Hong-Wei. Performance of UV photodetector of mechanical exfoliation prepared PEDOT:PSS/β-Ga2O3 microsheet heterojunction. Acta Physica Sinica, 2024, 73(15): 157102. doi: 10.7498/aps.73.20240630 [3] Liu Wei, Feng Qiu-Ju, Yi Zi-Qi, Yu Chen, Wang Shuo, Wang Yan-Ming, Sui Xue, Liang Hong-Wei. Preparation and ultraviolet detection performance of Cu doped β-Ga2O3 thin films. Acta Physica Sinica, 2023, 72(19): 198503. doi: 10.7498/aps.72.20230971 [4] Zhou Zhan-Hui, Li Qun, He Xiao-Min. Electron transport mechanism in AlN/β-Ga2O3 heterostructures. Acta Physica Sinica, 2023, 72(2): 028501. doi: 10.7498/aps.72.20221545 [5] Zhang Mao-Lin, Ma Wan-Yu, Wang Lei, Liu Zeng, Yang Li-Li, Li Shan, Tang Wei-Hua, Guo Yu-Feng. Investigation of high-temperature performance of WO3/β-Ga2O3 heterojunction deep-ultraviolet photodetectors. Acta Physica Sinica, 2023, 72(16): 160201. doi: 10.7498/aps.72.20230638 [6] Wang Lu-Xuan, Liu Yi-Tong, Shi Fang-Yuan, Qi Xian-Wen, Shen Han, Song Ying-Lin, Fang Yu. Broadband ultrafast photogenerated carrier dynamics induced by intrinsic defects in $\boldsymbol\beta$ -Ga2O3. Acta Physica Sinica, 2023, 72(21): 214202. doi: 10.7498/aps.72.20231173[7] Zhu Yong-Qi, Liu Yu-Xue, Shi Yang, Wu Cong-Cong. High performance perovskite solar cells synthesized by dissolving FAPbI3 single crystal. Acta Physica Sinica, 2023, 72(1): 018801. doi: 10.7498/aps.72.20221461 [8] . Effect of film thickness on photoelectric properties of β-Ga2O3 films by radio frequency magnetron sputtering*. Acta Physica Sinica, 2021, (): . doi: 10.7498/aps.70.20211744 [9] Long Ze, Xia Xiao-Chuan, Shi Jian-Jun, Liu Jun, Geng Xin-Lei, Zhang He-Zhi, Liang Hong-Wei. Temperature dependent characteristics of Ni/Au vertical Schottky diode based on mechanically exfoliated beta-Ga2O3 single crystal. Acta Physica Sinica, 2020, 69(13): 138501. doi: 10.7498/aps.69.20200424 [10] Hong Zi-Fan, Chen Hai-Feng, Jia Yi-Fan, Qi Qi, Liu Ying-Ying, Guo Li-Xin, Liu Xiang-Tai, Lu Qin, Li Li-Jun, Wang Shao-Qing, Guan Yun-He, Hu Qi-Ren. Characteristics of Ga2O3 epitaxial films on seed layer grown by magnetron sputtering. Acta Physica Sinica, 2020, 69(22): 228103. doi: 10.7498/aps.69.20200810 [11] Ma Teng-Yu, Li Wan-Jun, He Xian-Wang, Hu Hui, Huang Li-Juan, Zhang Hong, Xiong Yuan-Qiang, Li Hong-Lin, Ye Li-Juan, Kong Chun-Yang. Size Regulation and Photoluminescence Properties of β-Ga2O3 Nanomaterials. Acta Physica Sinica, 2020, 69(10): 108102. doi: 10.7498/aps.69.20200158 [12] Guo Dao-You, Li Pei-Gang, Chen Zheng-Wei, Wu Zhen-Ping, Tang Wei-Hua. Ultra-wide bandgap semiconductor of β-Ga2O3 and its research progress of deep ultraviolet transparent electrode and solar-blind photodetector. Acta Physica Sinica, 2019, 68(7): 078501. doi: 10.7498/aps.68.20181845 [13] Feng Qiu-Ju, Li Fang, Li Tong-Tong, Li Yun-Zheng, Shi Bo, Li Meng-Ke, Liang Hong-Wei. Growth and characterization of grid-like β-Ga2O3 nanowires by electric field assisted chemical vapor deposition method. Acta Physica Sinica, 2018, 67(21): 218101. doi: 10.7498/aps.67.20180805 [14] Li Juan, Ru Qiang, Hu She-Jun, Guo Ling-Yun. Lithium intercalation properties of SnSb/C composite in carbonthermal reduction as the anode material for lithium ion battery. Acta Physica Sinica, 2014, 63(16): 168201. doi: 10.7498/aps.63.168201 [15] Zheng Shu-Wen, Fan Guang-Han, He Miao, Zhao Ling-Zhi. Theoretical study of the effect of W-doping on the conductivity of β-Ga2O3. Acta Physica Sinica, 2014, 63(5): 057102. doi: 10.7498/aps.63.057102 [16] Yao Hai-Feng, Xie Yue-E, Ouyang Tao, Chen Yuan-Ping. Thermal transport of graphene nanoribbons embedding linear defects. Acta Physica Sinica, 2013, 62(6): 068102. doi: 10.7498/aps.62.068102 [17] Zhang Yi-Jun, Yan Jin-Liang, Zhao Gang, Xie Wan-Feng. First-principles calculation and experimental study of Si-doped β-Ga2O3. Acta Physica Sinica, 2011, 60(3): 037103. doi: 10.7498/aps.60.037103 [18] Lin Qiong-Fei, Xia Hai-Ping, Wang Jin-Hao, Zhang Yue-Pin, Zhang Qin-Yuan. Effect of Ga2O3 on the spectroscopic properties of Tm3+-doped GeO2-Ga2O3-Li2O-BaO-La2O3 glasses. Acta Physica Sinica, 2008, 57(4): 2554-2561. doi: 10.7498/aps.57.2554 [19] Ma Hai-Lin, Su Qing, Lan Wei, Liu Xue-Qin. Influence of oxygen pressure on the structure and photoluminescence of β-Ga2O3 nano-material prepared by thermal evaporation. Acta Physica Sinica, 2008, 57(11): 7322-7326. doi: 10.7498/aps.57.7322 [20] Zhang Chun-Xiang, Lin Li-Bin, P. L. Leung, Tang Qiang, Mike Li, Luo Da-Ling. Thermoluminescence and optical stimulated luminescence of undoped α-Al2O3 single crystal. Acta Physica Sinica, 2004, 53(1): 291-295. doi: 10.7498/aps.53.291
DownLoad:
Catalog
Metrics
- Abstract views: 8730
- PDF Downloads: 222
- Cited By: 0