Recent advances in synthesis and memory computing of large-area <i>α</i>-MoO<sub>3</sub>

Shan Xin; Wang Fang; Hu Kai; Wei Jun-Qing; Lin Xin; Zhao Xuan-Yu; Zhou Bao-Zeng; Zhang Kai-Liang

doi:10.7498/aps.70.20201813

Abstract

In recent years, α-MoO₃ has received extensive attention in the research of memristor devices. The variation of valence of molybdenum will lead the resistivity to change, and the unique layer structure is beneficial to the implantation of donor ion into free space to adjust the conductance, so that it has a great influence on the study of synaptic transistors. This paper mainly summarize the properties of α-MoO₃, the method and characteristics of large-scale two-dimensional α-MoO₃ and analyze the recent progress of in-memory computing based on α-MoO₃. Primarily, this paper introduces crystal structures, band structure and defect state of α-MoO₃. The synthesis methods of large-area α-MoO₃ are compared with each other, including the one-step method to directly obtain α-MoO₃ nanosheets, and the combined post-annealing process of magnetron sputtering or atomic layer deposition to prepare the thin α-MoO₃ films. In the one-step synthesis method we conclude that the chamber pressure influences the ratio of MoO₃ to MoO_3–x, and the growth temperature affects the ratio of α-MoO₃ to β-MoO₃. That is to say, the phase composition of molybdenum trioxide, the concentration of precursors has an important influence on the film size. The advantages of α-MoO₃ synthesis by different methods in memory computing applications are discussed in detail. And then, this paper summarizes the device performance of α-MoO₃ in memristor and the application progress of α-MoO₃-based neuromorphic devices, and analyzes the performance of α-MoO₃-based resistive random access memory such as switching ratio, endurance, and stability in detail. The synaptic functions of different structural device units are extensively studied, and various typical synapse functions are realized such as short-term plasticity, long-term plasticity, paired pulse facilitation, etc. It shows the excellent characteristics of low energy consumption in the simulation of synaptic plasticity. The use of short-term memory and long-term memory modes of the device can realize the functions of image memory and preprocessing. Through the memristor array combined with the back-propagation network, the high-precision handwriting recognition can be realized. Finally, combining the recent research progress of α-MoO₃, its opportunities and challenges in the field of memory computing are prospected.

Keywords:

Authors and contacts

1.
School of Materials Science and Engineering, Tianjin University of Technology, Tianjin 300384, China
2.
Tianjin Key Laboratory of Film Electronic & Communication Devices, School of Electrical and Electronic Engineering, Tianjin University of Technology, Tianjin 300384, China
3.
School of Microelectronics and Tianjin Key Laboratory of Imaging and Sensing Microelectronic Technology, Tianjin University, Tianjin 300072, China

Corresponding author: Wang Fang, fwang75@163.com ; Zhang Kai-Liang, kailiang_zhang@163.com

Funds: Project supported by the Natural Science Foundation of Tianjin, China (Grant Nos. 18JCZDJC30500, 17JCYBJC16100, 17JCZDJC31700), the National Natural Science Foundation of China (Grant Nos. 61404091, 61274113, 61505144, 51502203, 51502204), the Science and Technology Planning Project of Tianjin, China (Grant No. 20ZYQCGX00070), the Open Project of State Key Laboratory of Functional Materials for Information, China (Grant No. SKL202007), and the National Key Research and Development Program of China (Grant No. 2017YFB0405600)

FullText HTML : translate this paragraph

References

[1]	Yang J J, Strukov D B, Stewart D R 2013 Nat. Nanotechnol. 8 13 Google Scholar
[2]	Chua L O 1971 IEEE Trans. Circuit Theory 18 507 Google Scholar
[3]	Ielmini D, Wong H S P 2018 Nat. Electron. 1 333 Google Scholar
[4]	Liu Y, Huang Y, Duan X 2019 Nature 567 323 Google Scholar
[5]	张宝军, 王芳, 沈稼强, 单欣, 邸希超, 胡凯, 张楷亮 2020 物理学报 69 048101 Google Scholar Zhang B J, Wang F, Shen J Q, Shan X, Di X C, Hu K, Zhang K L 2020 Acta Phys. Sin. 69 048101 Google Scholar
[6]	Hanson E D, Lajaunie L, Hao S, Myers B D, Shi F, Murthy A A, Wolverton C, Arenal R, Dravid V P 2017 Adv. Funct. Mater. 27 1605380 Google Scholar
[7]	Carcia P F, Mccarron E M 1987 Thin Solid Films 155 53 Google Scholar
[8]	De Castro I A, Datta R S, Ou J Z, Castellanos-Gomez A, Sriram S, Daeneke T, Kalantar-zadeh K 2017 Adv. Mater. 29 1701619 Google Scholar
[9]	Yao D D, Ou J Z, Latham K, Zhuiykov S, O’Mullane A P, Kalantar-zadeh K 2012 Cryst. Growth Des. 12 1865 Google Scholar
[10]	Pan W, Tian R, Jin H, Guo Y, Zhang L, Wu X, Zhang L, Han Z, Liu G, Li J, Rao G, Wang H, Chu W 2010 Chem. Mater. 22 6202 Google Scholar
[11]	Lei Y H, Chen Z X 2016 Appl. Surf. Sci. 361 107 Google Scholar
[12]	Inzani K, Grande T, Vullum-Bruer F, Selbach S M 2016 J. Phys. Chem. C 120 8959 Google Scholar
[13]	Wang Y, Du X, Wang J, Su M, Wan X, Meng H, Xie W, Xu J, Liu P 2017 ACS Appl. Mater. Interfaces 9 5543 Google Scholar
[14]	Crowley K, Ye G, He R, Abbasi K, Gao X P A 2018 ACS Appl. Nano Mater. 1 6407 Google Scholar
[15]	Zhang C, Pudasaini P R, Oyedele A D, Ievlev A V, Xu L, Haglund A V, Noh J H, Wong A T, Xiao K, Ward T Z, Mandrus D G, Xu H, Ovchinnikova O S, Rack P D 2018 ACS Appl. Mater. Interfaces 10 22623 Google Scholar
[16]	Zheng B, Wang Z, Chen Y, Zhang W, Li X 2018 2D Mater. 5 045011 Google Scholar
[17]	Sun H, Zhang H, Jing X, Hu J, Shen K, Liang Z, Hu J, Tian Q, Luo M, Zhu Z, Jiang Z, Huang H, Song F 2019 Appl. Surf. Sci. 476 789 Google Scholar
[18]	Arash A, Ahmed T, Rajan A G, Walia S, Rahman F, Mazumder A, Ramanathan R, Sriram S, Bhaskaran M, Mayes E 2019 2D Mater. 6 035031 Google Scholar
[19]	Kim H U, Son J, Kulkarni A, Ahn C, Kim K S, Shin D, Yeom G Y, Kim T 2017 Nanotechnology 28 175601 Google Scholar
[20]	Molina-Mendoza A J, Lado J L, Island J O, Niño M A, Aballe L, Foerster M, Bruno F Y, López-Moreno A, Vaquero-Garzon L, van der Zant H S J, Rubio-Bollinger G, Agraït N, Pérez E M, Fernández-Rossier J, Castellanos-Gomez A 2016 Chem. Mater. 28 4042 Google Scholar
[21]	Wang D, Li J N, Zhou Y, Xu D H, Xiong X, Peng R W, Wang M 2016 Appl. Phys. Lett. 108 053107 Google Scholar
[22]	Diaz-Droguett D E, Fuenzalida V M 2010 J. Nanosci. Nanotechnol. 10 6694 Google Scholar
[23]	Cauduro A L F, dos Reis R, Chen G, Schmid A K, Méthivier C, Rubahn H G, Bossard-Giannesini L, Cruguel H, Witkowski N, Madsen M 2017 ACS Appl. Mater. Interfaces 9 7717 Google Scholar
[24]	Arita M, Kaji H, Fujii T, Takahashi Y 2012 Thin Solid Films 520 4762 Google Scholar
[25]	George S M 2010 Chem. Rev. 110 111 Google Scholar
[26]	Leskelä M , Ritala M 2002 Thin Solid Films 1 138 Google Scholar
[27]	Shi M L, Chen L, Zhang T B, Xu J, Zhu H, Sun Q Q, Zhang D W 2017 Small 13 1603157 Google Scholar
[28]	Diskus M, Nilsen O, Fjellvåg H 2011 J. Mater. Chem. 21 705 Google Scholar
[29]	Diskus M, Nilsen O, Fjellvåg H, et al. 2012 J. Vac. Sci. Technol. 30 01A107 Google Scholar
[30]	Zhou G, Ren Z, Wang L, Sun B, Duan S, Song Q 2019 Mater. Horiz. 6 1877 Google Scholar
[31]	Zhou G, Wu J, Wang L, et al. 2019 Nanoscale 11 17222 Google Scholar
[32]	Sun L, Zhang Y, Han G, Hwang G, Jiang J, Joo B, Watanabe K, Taniguchi T, Kim Y M, Yu W J, Kong B S, Zhao R, Yang H 2019 Nat. Commun. 10 3161 Google Scholar
[33]	张志超, 王芳, 吴仕剑, 李毅, 弥伟, 赵金石, 张楷亮 2018 物理学报 67 057301 Google Scholar Zhang Z C, Wang F, Wu S J, Li Y, Mi W, Zhao J S, Zhang K L 2018 Acta Phys. Sin. 67 057301 Google Scholar
[34]	Du H, Chen J, Tu M, Luo S, Li S, Yuan S, Gong T, Huang W, Jie W, Hao J 2019 J. Mater. Chem. C 7 12160 Google Scholar
[35]	Zhou F, Zhou Z, Chen J, Choy T H, Wang J, Zhang N, Lin Z, Yu S, Kang J, Wong H S P, Chai Y 2019 Nat. Nanotechnol. 14 776 Google Scholar
[36]	Tan Z H, Yin X B, Guo X 2015 Appl. Phys. Lett. 106 023503 Google Scholar
[37]	Wang J, Wang F, Yin L, Sendeku M G, Zhang Y, Cheng R, Wang Z, Li N, Huang W, He J 2019 Nanoscale 11 20497 Google Scholar
[38]	Rahman F, Ahmed T, Walia S, Mayes E, Sriram S, Bhaskaran M, Balendhran S 2018 Nanoscale 10 19711 Google Scholar
[39]	Yang C S, Shang D S, Chai Y S, Yan L Q, Shen B G, Sun Y 2016 Phys. Chem. Chem. Phys. 18 12466 Google Scholar
[40]	Hasegawa J, Nagase T, Kobayashi T, Naito H 2016 Jpn. J. Appl. Phys. 55 03DC05 Google Scholar
[41]	Abhijith T, Kumar T V, Reddy V S 2017 Nanotechnology 28 095203 Google Scholar
[42]	Hsu C C, Wang S Y, Lin Y S, Chen Y T 2019 J. Alloys Compd. 779 609 Google Scholar
[43]	Fang S L, Liu W H, Li X, Wang X L, Geng L, Wu M S, Huang X D, Han C Y 2019 Appl. Phys. Lett. 115 244102 Google Scholar
[44]	Dai T, Qian L, Ren Y, Liu X 2017 International Conference on Electron Devices and Solid-State Circuits (EDSSC) Hsinchu, Taiwan China, October 18–20, 2017 p1
[45]	Xue Q, Wang Y C, Wei X H 2019 Appl. Surf. Sci. 479 469 Google Scholar
[46]	Kim G H, Lee, J H, Ahn Y, Jeon W, Song S J, Seok J Y, Yoon J H, Yoon K J, Park T J, Hwang C S 2013 Adv. Funct. Mater. 23 1440 Google Scholar
[47]	Rehman M M, Rehman H M M U, Gul J Z, Kim W Y, Karimov K S, Ahmed N 2020 Sci. Technol. Adv. Mater. 21 147 Google Scholar
[48]	Wang X, Xie W, Xu J B 2014 Adv. Mater. 26 5496 Google Scholar
[49]	Yang C S, Shang D S, Chai Y S, Yan L Q, Shen B G, Sun Y 2017 Phys. Chem. Chem. Phys. 19 4190 Google Scholar
[50]	Wang Z, Yang R, Huang H M, He H K, Shaibo J, Guo X 2020 Adv. Electron. Mater. 6 1901290 Google Scholar
[51]	Danesh C D, Shaffer C M, Nathan D, Shenoy R, Tudor A, Tadayon M, Lin Y, Chen Y 2019 Adv. Mater. 31 e1808032 Google Scholar
[52]	Lenz J, Del Giudice F, Geisenhof F R, Winterer F, Weitz R T 2019 Nat. Nanotechnol. 14 579 Google Scholar
[53]	Nie S, He Y, Liu R, Shi Y, Wan Q 2019 IEEE Electron Device Lett. 40 459 Google Scholar
[54]	Chernova N A, Roppolo M, Dillon A C, Whittingham M S 2009 J. Mater. Chem. 19 2526 Google Scholar
[55]	李琦, 章勇 2018 物理学报 67 067201 Google Scholar Li Q, Zhang Y 2018 Acta Phys. Sin. 67 067201 Google Scholar
[56]	Yang C S, Shang D S, Liu N, Shi G, Shen X, Yu R C, Li Y Q, Sun Y 2017 Adv. Mater. 29 1700906 Google Scholar
[57]	Yang C S, Shang D S, Liu N, et al. 2018 Adv. Funct. Mater. 28 1804170 Google Scholar
[58]	He Y, Nie S, Liu R, Jiang S, Shi Y, Wan Q 2019 Adv. Mater. 31 e1900903 Google Scholar
[59]	Guo L, Wen J, Ding J, Wan C, Cheng G 2016 Sci. Rep. 6 38578 Google Scholar
[60]	Hu W, Jiang J, Xie D, Liu B, Yang J, He J 2019 J. Mater. Chem. C 7 682 Google Scholar
[61]	Shao L, Wang H, Yang Y, et al. 2019 ACS Appl. Mater. Interfaces 11 12161 Google Scholar
[62]	Wang K, Dai S, Zhao Y, Wang Y, Liu C, Huang J 2019 Small 15 e1900010 Google Scholar

Cited By

图 1 (a) α-MoO₃晶体结构; (b) β-MoO₃晶体结构; (c) h-MoO₃晶体结构

Figure 1. (a) Crystal structure of α-MoO₃; (b) crystal structure of β-MoO₃; (c) crystal structure of h-MoO₃.

DownLoad: Full-Size Img PowerPoint

图 2 (a) 块体电子结构^[6]; (b) 单层电子结构^[6]

Figure 2. (a) Bulk electronic structure^[6]; (b) monolayer electronic structure^[6].

DownLoad: Full-Size Img PowerPoint

图 3 (a) 在化学计量比情况下MoO₃能带结构^[12]; (b) 在O1空位情况下MoO₃能带结构^[12]; (c) 在O2 空位情况下MoO₃能带结构^[12]; (d) 在O3空位情况下MoO₃能带结构^[12]

Figure 3. (a) Band structures of MoO₃ in the stoichiometric case^[12]; (b) band structures of MoO₃ in the vacancy on O1 case^[12]; (c) band structures of MoO₃ in the vacancy on O2 case^[12]; (d) band structures of MoO₃ in the vacancy on O3 case^[12].

DownLoad: Full-Size Img PowerPoint

图 4 (a) 在两温区的物理气相沉积系统中合成α-MoO₃原理图^[13]; (b) 在SiO₂/Si衬底上生长的α-MoO₃单晶的照片^[16]; (c) α-MoO₃的HRTEM图像, 内嵌图为相应的透射电子显微镜图像和傅里叶变换图像^[16]; (d) 生长α-MoO₃的O 1s和Mo 3d的高分辨XPS能谱^[16]

Figure 4. (a) Schematic illustration of synthesis of α-MoO₃ in a two-temperature-zone PVD system^[13]; (b) photograph of as-grown α-MoO₃ single crystals on SiO₂/Si substrate^[16]; (c) HRTEM image of the α-MoO₃ sheet. Insets: corresponding TEM and FFT images^[16]; (d) high-resolution XPS spectra of O 1s and Mo 3d of as-grown α-MoO₃^[16].

DownLoad: Full-Size Img PowerPoint

图 5 在不同温度下氧化的Mo薄膜的XRD图谱^[24]

Figure 5. XRD patterns of Mo films oxidized at various temperatures^[24].

DownLoad: Full-Size Img PowerPoint

图 6 (a) 采用ALD合成MoO₃薄膜的一个循环的工艺原理图^[27]; (b) 采用ALD在Al₂O₃上沉积得到的40 nm MoO₃薄膜的拉曼光谱: a)沉积和空气中退火, b) 400 ℃退火8 min, c) 600 ℃退火4 min, d) 600 ℃退火7.5 min^[29]

Figure 6. (a) Schematic of one cycle ALD process for MoO₃ film^[27]; (b) Raman spectra of 40 nm thin films of MoO₃ deposited on Al₂O₃ by ALD: a) as deposited, and annealed in air; b) 8 min at 400 ℃; c) 4 min at 600 ℃; d) 7.5 min at 600 ℃^[29].

DownLoad: Full-Size Img PowerPoint

图 7 (a) 单极电阻开关的代表性行为, 横向面积为2 μm × 2 μm的α-MoO₃横杆三明治器件中的I-V曲线, 内嵌图显示了Au/Cr/α-MoO₃/Au横杆夹层结构的相应光学图像, 刻度线代表5 μm^[37]; (b) α-MoO₃横杆器件开关在室温下具有稳定的保持性; 在0.01 V的小偏置下, 通过测量电流来确定HRS和LRS^[37]; (c) 存储器单元在重复开关周期下的特性电流-电压曲线^[38]; (d) 开关周期的耐久性(读取电压为500 mV时获得的电阻值), 内嵌图为耐久性测量过程中的电压脉冲序列, 每个脉冲的持续时间为2 ms^[38]

Figure 7. (a) Representative I-V curves of unipolar resistive switching behavior in the α-MoO₃ crossbar sandwich device with a lateral area of 2 μm × 2 μm. The inset shows the corresponding optical image of Au/Cr/α-MoO₃/Au crossbar sandwich structures and the scale bar represents 5 μm^[37]. (b) Time-dependent measurements of α-MoO₃ crossbar device switch featuring stable retention at room temperature. The resistance of the HRS and LRS is determined by measuring the current at a small bias of 0.01 V^[37]. (c) Characteristic current-voltage curves of a memory cell subjected to repetitive switching cycles^[38]. (d) Performance endurance with respect to number of switching cycles (Resistance values obtained at a read voltage of 500 mV). The inset shows the voltage pulse train during endurance measurement with duration of 2 ms of each pulse^[38].

DownLoad: Full-Size Img PowerPoint

图 8 (a) MoO_x RRAMs的电流-电压特性^[42]; (b) MoO_x RRAMs的耐久性^[42]

Figure 8. (a) Current-voltage characteristics of the MoO_x RRAMs^[42]; (b) endurance characteristics of the MoO_x RRAMs^[42].

DownLoad: Full-Size Img PowerPoint

图 9 (a) 垂直器件结构示意图及测试说明^[45]; (b) 负电压I-V曲线^[45]; (c) 正电压I-V曲线; 内嵌图为 ± 0.25 V读电压下随周期的增加, 电流的变化^[45]; (d) 由施加的10个不同电压和宽度的脉冲所表示的STM和LTM^[50]; (e) 电导在第一个像素内的变化, 蓝色虚线表示对于一个给定字母, 输入最后一个脉冲后的读出时间^[50]; (f), (g), (h)在STM模式下(e)图中蓝线标记的时刻所记忆的字母“x”和“z”, 而字母“y”是在LTM模式下被记忆^[50]

Figure 9. (a) Schematic illustration of vertical device structure and measurement; (b) I-V curves of negative voltage^[45]; (c) I-V curves of positive voltage, the insets show the variation of the current read at ±0.25 V with increasing cycle^[45]; (d) STM and LTM demonstrated by applying 10 pulses with different amplitudes and widths^[50]; (e) conductance change at the first pixel; the blue dashed lines indicate the read-out moment after inputting the last pulse for a given letter^[50]; (f), (g), (h) images memorized at the moments marked by blue lines in (e) letters “x” and “z” are memorized in the STM mode, while the letter “y” is memorized in the LTM mode^[50].

DownLoad: Full-Size Img PowerPoint

图 10 (a) 生物突触示意图^[56]; (b) 三端突触晶体管结构原理图^[56]; (c) 由电压编程锂离子突触晶体管crossbar阵列和接入器件组成的突触权重层示意图^[57]; (d) 对于8 × 8像素手写数字图像, 其识别精度随训练epochs的变化^[57]

Figure 10. (a) Schematic illustration of a biological synapse^[56]; (b) schematic diagram of the three-terminal synaptic transistor^[56]; (c) schematics of a synaptic weight layer composed of voltage programmed Li-ion synaptic transistor crossbar array and access devices^[57]; (d) the recognition accuracy evolution with training epochs for 8 × 8 pixel handwritten digit image^[57].

DownLoad: Full-Size Img PowerPoint

图 11 (a) 8 × 8 ORRAM阵列原理图^[35]; (b) 带有ORRAM阵列的三层人工神经网络连接结构^[35]; (c) 经ORRAM阵列预处理前(左列)和后(右列)的图像示例^[35]; (d) 有无ORRAM阵列图像预处理情况下图像识别率的对比^[35]

Figure 11. (a) Schematic structure of an 8 × 8 ORRAM array^[35]; (b) structure of the three-layered artificial neural network with ORRAM^[35]; (c) examples of images before (left columns) and after (right columns) ORRAM-based pre-processing^[35]; (d) comparisons of the image recognition rate with and without ORRAM-based image preprocessing^[35].

DownLoad: Full-Size Img PowerPoint

表 1 一步法制备α-MoO₃的生长条件(1 Torr = 1.33322 × 10² Pa)

Table 1. Growth conditions of α-MoO₃ prepared by one-step method.

Ref.	Carrier flow	Pressure	Substrate temperature/℃	Growth time/min	Lateral size	Thickness/nm
[13]	—	Atmospheric	580	120	69.6 μm	5.3—89.8
[16]	—	Atmospheric	850—1050	30	0.72 cm	—
[17]	Ar	Atmospheric	750	20	Centimeters scale	4.3—550
[18]	Ar	310 mTorr	530	45	500 µm × 500 µm	8 ± 0.75
[19]	Ar & O₂	100 mTorr	150	90	Wafer-scale	30
[20]	—	Atmospheric	540	20	Centimeters scale	≥ 1.4
[21]	N₂	Atmospheric	350—480	20	Several tens micron	2.8—14

DownLoad: CSV

表 2 三氧化钼基忆阻器件性能对比

Table 2. Comparison of performance of molybdenum trioxide memristors.

Ref.	R_on/R_off	Endurence	V_forming/V	V_set/V	V_reset/V	Retention/s	Compliance/mA
[24]	10—10²	60	1.8—3	1—2	0.5—1	—	2—5
[36]	10³	—	–2.2	1.7	3.3	10³	10^-3
[37]	> 10⁵	50	3.2—4.1	3—3.9	4.45—5.9	10⁴	50
[38]	10³	> 6000	–2.7	–2	2.5	> 10⁴	0.8
[39]	18	—	24.5	1.8	–1.1	3.6 × 10³	1
[40]	～350	—	—	1—3	—	2.6 × 10⁶	—
[41]	1.15 × 10³	7	—	4	8	4.5 × 10³	—
[42]	1.6 × 10²	500	—	–3	3	—	—
[43]	10⁶	> 100	—	0.8	–0.2—1.6	2 × 10⁴	10²
[44]	20	—	—	2.2	–1.1	1.4 × 10³	0.1
[45]	—	—	Free	0.4	–1	—	0.1

DownLoad: CSV

表 3 突触晶体管性能对比

Table 3. Performance comparison of synaptic transistors.

Ref.	Channel material	Electrolyte	Operation votage/V	Pulse width/ ms	Energy consumption
[56]	α-MoO₃	EMIM(CF₃SO₂)₂N	2.5	1	9.6 pJ
[57]	α-MoO₃	LiClO₄/PEO	2.5	1	≈0.16 pJ
[58]	IGZO	Chitosan	2	25	1.0 nJ
[59]	IZO	Methyl cellulose	0.2—1	15—60	16 nJ
[60]	MoS₂	chitosan	1.5	10	5 pJ

DownLoad: CSV

[1]	Yang J J, Strukov D B, Stewart D R 2013 Nat. Nanotechnol. 8 13 Google Scholar
[2]	Chua L O 1971 IEEE Trans. Circuit Theory 18 507 Google Scholar
[3]	Ielmini D, Wong H S P 2018 Nat. Electron. 1 333 Google Scholar
[4]	Liu Y, Huang Y, Duan X 2019 Nature 567 323 Google Scholar
[5]	张宝军, 王芳, 沈稼强, 单欣, 邸希超, 胡凯, 张楷亮 2020 物理学报 69 048101 Google Scholar Zhang B J, Wang F, Shen J Q, Shan X, Di X C, Hu K, Zhang K L 2020 Acta Phys. Sin. 69 048101 Google Scholar
[6]	Hanson E D, Lajaunie L, Hao S, Myers B D, Shi F, Murthy A A, Wolverton C, Arenal R, Dravid V P 2017 Adv. Funct. Mater. 27 1605380 Google Scholar
[7]	Carcia P F, Mccarron E M 1987 Thin Solid Films 155 53 Google Scholar
[8]	De Castro I A, Datta R S, Ou J Z, Castellanos-Gomez A, Sriram S, Daeneke T, Kalantar-zadeh K 2017 Adv. Mater. 29 1701619 Google Scholar
[9]	Yao D D, Ou J Z, Latham K, Zhuiykov S, O’Mullane A P, Kalantar-zadeh K 2012 Cryst. Growth Des. 12 1865 Google Scholar
[10]	Pan W, Tian R, Jin H, Guo Y, Zhang L, Wu X, Zhang L, Han Z, Liu G, Li J, Rao G, Wang H, Chu W 2010 Chem. Mater. 22 6202 Google Scholar
[11]	Lei Y H, Chen Z X 2016 Appl. Surf. Sci. 361 107 Google Scholar
[12]	Inzani K, Grande T, Vullum-Bruer F, Selbach S M 2016 J. Phys. Chem. C 120 8959 Google Scholar
[13]	Wang Y, Du X, Wang J, Su M, Wan X, Meng H, Xie W, Xu J, Liu P 2017 ACS Appl. Mater. Interfaces 9 5543 Google Scholar
[14]	Crowley K, Ye G, He R, Abbasi K, Gao X P A 2018 ACS Appl. Nano Mater. 1 6407 Google Scholar
[15]	Zhang C, Pudasaini P R, Oyedele A D, Ievlev A V, Xu L, Haglund A V, Noh J H, Wong A T, Xiao K, Ward T Z, Mandrus D G, Xu H, Ovchinnikova O S, Rack P D 2018 ACS Appl. Mater. Interfaces 10 22623 Google Scholar
[16]	Zheng B, Wang Z, Chen Y, Zhang W, Li X 2018 2D Mater. 5 045011 Google Scholar
[17]	Sun H, Zhang H, Jing X, Hu J, Shen K, Liang Z, Hu J, Tian Q, Luo M, Zhu Z, Jiang Z, Huang H, Song F 2019 Appl. Surf. Sci. 476 789 Google Scholar
[18]	Arash A, Ahmed T, Rajan A G, Walia S, Rahman F, Mazumder A, Ramanathan R, Sriram S, Bhaskaran M, Mayes E 2019 2D Mater. 6 035031 Google Scholar
[19]	Kim H U, Son J, Kulkarni A, Ahn C, Kim K S, Shin D, Yeom G Y, Kim T 2017 Nanotechnology 28 175601 Google Scholar
[20]	Molina-Mendoza A J, Lado J L, Island J O, Niño M A, Aballe L, Foerster M, Bruno F Y, López-Moreno A, Vaquero-Garzon L, van der Zant H S J, Rubio-Bollinger G, Agraït N, Pérez E M, Fernández-Rossier J, Castellanos-Gomez A 2016 Chem. Mater. 28 4042 Google Scholar
[21]	Wang D, Li J N, Zhou Y, Xu D H, Xiong X, Peng R W, Wang M 2016 Appl. Phys. Lett. 108 053107 Google Scholar
[22]	Diaz-Droguett D E, Fuenzalida V M 2010 J. Nanosci. Nanotechnol. 10 6694 Google Scholar
[23]	Cauduro A L F, dos Reis R, Chen G, Schmid A K, Méthivier C, Rubahn H G, Bossard-Giannesini L, Cruguel H, Witkowski N, Madsen M 2017 ACS Appl. Mater. Interfaces 9 7717 Google Scholar
[24]	Arita M, Kaji H, Fujii T, Takahashi Y 2012 Thin Solid Films 520 4762 Google Scholar
[25]	George S M 2010 Chem. Rev. 110 111 Google Scholar
[26]	Leskelä M , Ritala M 2002 Thin Solid Films 1 138 Google Scholar
[27]	Shi M L, Chen L, Zhang T B, Xu J, Zhu H, Sun Q Q, Zhang D W 2017 Small 13 1603157 Google Scholar
[28]	Diskus M, Nilsen O, Fjellvåg H 2011 J. Mater. Chem. 21 705 Google Scholar
[29]	Diskus M, Nilsen O, Fjellvåg H, et al. 2012 J. Vac. Sci. Technol. 30 01A107 Google Scholar
[30]	Zhou G, Ren Z, Wang L, Sun B, Duan S, Song Q 2019 Mater. Horiz. 6 1877 Google Scholar
[31]	Zhou G, Wu J, Wang L, et al. 2019 Nanoscale 11 17222 Google Scholar
[32]	Sun L, Zhang Y, Han G, Hwang G, Jiang J, Joo B, Watanabe K, Taniguchi T, Kim Y M, Yu W J, Kong B S, Zhao R, Yang H 2019 Nat. Commun. 10 3161 Google Scholar
[33]	张志超, 王芳, 吴仕剑, 李毅, 弥伟, 赵金石, 张楷亮 2018 物理学报 67 057301 Google Scholar Zhang Z C, Wang F, Wu S J, Li Y, Mi W, Zhao J S, Zhang K L 2018 Acta Phys. Sin. 67 057301 Google Scholar
[34]	Du H, Chen J, Tu M, Luo S, Li S, Yuan S, Gong T, Huang W, Jie W, Hao J 2019 J. Mater. Chem. C 7 12160 Google Scholar
[35]	Zhou F, Zhou Z, Chen J, Choy T H, Wang J, Zhang N, Lin Z, Yu S, Kang J, Wong H S P, Chai Y 2019 Nat. Nanotechnol. 14 776 Google Scholar
[36]	Tan Z H, Yin X B, Guo X 2015 Appl. Phys. Lett. 106 023503 Google Scholar
[37]	Wang J, Wang F, Yin L, Sendeku M G, Zhang Y, Cheng R, Wang Z, Li N, Huang W, He J 2019 Nanoscale 11 20497 Google Scholar
[38]	Rahman F, Ahmed T, Walia S, Mayes E, Sriram S, Bhaskaran M, Balendhran S 2018 Nanoscale 10 19711 Google Scholar
[39]	Yang C S, Shang D S, Chai Y S, Yan L Q, Shen B G, Sun Y 2016 Phys. Chem. Chem. Phys. 18 12466 Google Scholar
[40]	Hasegawa J, Nagase T, Kobayashi T, Naito H 2016 Jpn. J. Appl. Phys. 55 03DC05 Google Scholar
[41]	Abhijith T, Kumar T V, Reddy V S 2017 Nanotechnology 28 095203 Google Scholar
[42]	Hsu C C, Wang S Y, Lin Y S, Chen Y T 2019 J. Alloys Compd. 779 609 Google Scholar
[43]	Fang S L, Liu W H, Li X, Wang X L, Geng L, Wu M S, Huang X D, Han C Y 2019 Appl. Phys. Lett. 115 244102 Google Scholar
[44]	Dai T, Qian L, Ren Y, Liu X 2017 International Conference on Electron Devices and Solid-State Circuits (EDSSC) Hsinchu, Taiwan China, October 18–20, 2017 p1
[45]	Xue Q, Wang Y C, Wei X H 2019 Appl. Surf. Sci. 479 469 Google Scholar
[46]	Kim G H, Lee, J H, Ahn Y, Jeon W, Song S J, Seok J Y, Yoon J H, Yoon K J, Park T J, Hwang C S 2013 Adv. Funct. Mater. 23 1440 Google Scholar
[47]	Rehman M M, Rehman H M M U, Gul J Z, Kim W Y, Karimov K S, Ahmed N 2020 Sci. Technol. Adv. Mater. 21 147 Google Scholar
[48]	Wang X, Xie W, Xu J B 2014 Adv. Mater. 26 5496 Google Scholar
[49]	Yang C S, Shang D S, Chai Y S, Yan L Q, Shen B G, Sun Y 2017 Phys. Chem. Chem. Phys. 19 4190 Google Scholar
[50]	Wang Z, Yang R, Huang H M, He H K, Shaibo J, Guo X 2020 Adv. Electron. Mater. 6 1901290 Google Scholar
[51]	Danesh C D, Shaffer C M, Nathan D, Shenoy R, Tudor A, Tadayon M, Lin Y, Chen Y 2019 Adv. Mater. 31 e1808032 Google Scholar
[52]	Lenz J, Del Giudice F, Geisenhof F R, Winterer F, Weitz R T 2019 Nat. Nanotechnol. 14 579 Google Scholar
[53]	Nie S, He Y, Liu R, Shi Y, Wan Q 2019 IEEE Electron Device Lett. 40 459 Google Scholar
[54]	Chernova N A, Roppolo M, Dillon A C, Whittingham M S 2009 J. Mater. Chem. 19 2526 Google Scholar
[55]	李琦, 章勇 2018 物理学报 67 067201 Google Scholar Li Q, Zhang Y 2018 Acta Phys. Sin. 67 067201 Google Scholar
[56]	Yang C S, Shang D S, Liu N, Shi G, Shen X, Yu R C, Li Y Q, Sun Y 2017 Adv. Mater. 29 1700906 Google Scholar
[57]	Yang C S, Shang D S, Liu N, et al. 2018 Adv. Funct. Mater. 28 1804170 Google Scholar
[58]	He Y, Nie S, Liu R, Jiang S, Shi Y, Wan Q 2019 Adv. Mater. 31 e1900903 Google Scholar
[59]	Guo L, Wen J, Ding J, Wan C, Cheng G 2016 Sci. Rep. 6 38578 Google Scholar
[60]	Hu W, Jiang J, Xie D, Liu B, Yang J, He J 2019 J. Mater. Chem. C 7 682 Google Scholar
[61]	Shao L, Wang H, Yang Y, et al. 2019 ACS Appl. Mater. Interfaces 11 12161 Google Scholar
[62]	Wang K, Dai S, Zhao Y, Wang Y, Liu C, Huang J 2019 Small 15 e1900010 Google Scholar

[1]	Wu Peng, Tan Lun, Li Wei, Cao Li-Wei, Zhao Jun-Bo, Qu Yao, Li Ang. Preparation and photoelectric property of large scale monolayer MoS₂. Acta Physica Sinica, 2023, 72(11): 118101. doi: 10.7498/aps.72.20230273
[2]	Bi Wen-Jie, Yang Shuang, Zhou Jing, Jin Wei, Chen Wen. Research on synthesis of Cu₃Mo₂O₉/MoO₃ nanocomposite and trimethylamine gas sensing properties. Acta Physica Sinica, 2023, 72(16): 168103. doi: 10.7498/aps.72.20230720
[3]	Zhu Jia-Xue, Zhang Xu-Meng, Wang Rui, Liu Qi. Flexible memristive spiking neuron for neuromorphic sensing and computing. Acta Physica Sinica, 2022, 71(14): 148503. doi: 10.7498/aps.71.20212323
[4]	Zhang Xiao, Lü Jia-Yu, Guan Yan-Qiu, Li Hui, Wang Xi-Ming, Zhang La-Bao, Wang Hao, Tu Xue-Cou, Kang Lin, Jia Xiao-Qing, Zhao Qing-Yuan, Chen Jian, Wu Pei-Heng. Design and fabrication of single photon detector with ultra-large area superconducting nanowire array. Acta Physica Sinica, 2022, 71(24): 248501. doi: 10.7498/aps.71.20221569
[5]	Shen Liu-Feng, Hu Ling-Xiang, Kang Feng-Wen, Ye Yu-Min, Zhuge Fei. Optoelectronic neuromorphic devices and their applications. Acta Physica Sinica, 2022, 71(14): 148505. doi: 10.7498/aps.71.20220111
[6]	Chen Yang-Yang, He Yu-Hui, Miao Xiang-Shui, Yang Dao-Hong. 3D-NAND flash memory based neuromorphic computing. Acta Physica Sinica, 2022, 71(21): 210702. doi: 10.7498/aps.71.20220974
[7]	Li Ce, Yang Dong-Liang, Sun Lin-Feng. Research progress of neuromorphic devices based on two-dimensional layered materials. Acta Physica Sinica, 2022, 71(21): 218504. doi: 10.7498/aps.71.20221424
[8]	Wang Shuo, Wang Wen-Hui, Lü Jun-Peng, Ni Zhen-Hua. Chemical vapor deposition growth of large-areas two dimensional materials: Approaches and mechanisms. Acta Physica Sinica, 2021, 70(2): 026802. doi: 10.7498/aps.70.20201398
[9]	Wang Hai-Yu, Liu Ying-Jie, Xun Lu-Lu, Li Jing, Yang Qing, Tian Qi-Yun, Nie Tian-Xiao, Zhao Wei-Sheng. Research progress of preparation of large-scale two-dimensional magnetic materials and manipulation of Curie temperature. Acta Physica Sinica, 2021, 70(12): 127301. doi: 10.7498/aps.70.20210223
[10]	Ren Kuan, Zhang Ke-Jia, Qin Xi-Zi, Ren Huan-Xin, Zhu Shou-Hui, Yang Feng, Sun Bai, Zhao Yong, Zhang Yong. Research progress of neuromorphic computation based on memcapacitors. Acta Physica Sinica, 2021, 70(7): 078701. doi: 10.7498/aps.70.20201632
[11]	Wei Chen-Wei, Cao Tun. α-MoO₃ based tunable Fabry-Pérot cavity colorimetric biosensor. Acta Physica Sinica, 2021, 70(4): 048701. doi: 10.7498/aps.70.20201548
[12]	Gao Bo-Wen, Meng Jing. Large area and flexible CH₃NH₃PbI₃ perovskite solar cell fabricated by all ink jet printing. Acta Physica Sinica, 2021, 70(20): 208801. doi: 10.7498/aps.70.20210788
[13]	Li Rui-Dong, Deng Jin-Xiang, Zhang Hao, Xu Zhi-Yang, Pan Zhi-Wei, Sun Jun-Jie, Wang Gui-Sheng. Preparation, optical, and electrical properties of rubrene∶MoO₃ films. Acta Physica Sinica, 2019, 68(17): 178101. doi: 10.7498/aps.68.20190035
[14]	Wang Wen-Rong, Zhou Yu-Xiu, Li Tie, Wang Yue-Lin, Xie Xiao-Ming. Research on synthesis of high-quality and large-scale graphene films by chemical vapor deposition. Acta Physica Sinica, 2012, 61(3): 038702. doi: 10.7498/aps.61.038702
[15]	You Feng, Ji Lu, Xie Qing-Lian, Wang Zheng, Yue Hong-Wei, Zhao Xin-Jie, Fang Lan, Yan Shao-Lin. Fabrication and properties of large area Tl2Ba2CaCu2O8 superconducting thin film on sapphire substrate. Acta Physica Sinica, 2010, 59(7): 5035-5043. doi: 10.7498/aps.59.5035
[16]	Cai Ya-Ping, Li Wei, Feng Liang-Huan, Li Bing, Cai Wei, Lei Zhi, Zhang Jing-Quan, Wu Li-Li, Zheng Jia-Gui. Preparation of large area CdS thin film and its application in photovoltaic cells. Acta Physica Sinica, 2009, 58(1): 438-443. doi: 10.7498/aps.58.438
[17]	Hai Kuo, Tang Dong-Sheng, Yuan Hua-Jun, Peng Yue-Hua, Luo Zhi-Hua, Liu Hong-Xia, Chen Ya-Qi, Yu Fang, Yang Yi. Synthesis of large-area, vertically aligned α-Fe2O3 nanowire and nanobelt arrays. Acta Physica Sinica, 2009, 58(2): 1120-1125. doi: 10.7498/aps.58.1120
[18]	Zhang Hong-Jun, Wang Dong, Chen Zhi-Quan, Wang Shao-Jie, Xu You-Ming, Luo Xi-Hui. Positron annihilation study of Mo dispersion in MoO3/Al2O3 catalysts. Acta Physica Sinica, 2008, 57(11): 7333-7337. doi: 10.7498/aps.57.7333
[19]	San Hai-Sheng, Chen Chong, He Yu-Yang, Wang Jun, Feng Bo-Xue. Study on electrical properties of n-type transparent and conductiveCdIn22O44 thin film and the optimum preparation parameters for large- area film. Acta Physica Sinica, 2005, 54(4): 1736-1741. doi: 10.7498/aps.54.1736
[20]	Oyangxiaoping, Li Zhen-Fu, Zhang Guo-Guang, Huo Yu-Kun, Zhang Qian-Mei, Zhang Xian-Peng, Song Xian-Cai, Jia Huan-Yi, Lei Jian-Hua, Sun Yuan-Cheng. . Acta Physica Sinica, 2002, 51(7): 1502-1505. doi: 10.7498/aps.51.1502

Catalog

Vol. 70, Issue 9 - 2021-05-05

Metrics

Abstract views: 11150
PDF Downloads: 245
Cited By: 0

姓名
邮箱
手机号码
标题
留言内容
验证码

Search

Article

留言板

Recent advances in synthesis and memory computing of large-area α-MoO₃

Abstract

Authors and contacts

Corresponding author: Wang Fang, fwang75@163.com ; Zhang Kai-Liang, kailiang_zhang@163.com

FullText HTML : translate this paragraph

References

Cited By

Catalog

Metrics

Authors

Referees

About Journal

About

Search

Article

留言板

Recent advances in synthesis and memory computing of large-area α-MoO3

Abstract

Authors and contacts

Corresponding author: Wang Fang, fwang75@163.com ; Zhang Kai-Liang, kailiang_zhang@163.com

FullText HTML : translate this paragraph

References

Cited By

Catalog

Metrics

Publishing process

Authors

Referees

About Journal

About

Recent advances in synthesis and memory computing of large-area α-MoO₃