Recent progress of 2-dimensional layered thermoelectric materials

Yu Ze-Hao; Zhang Li-Fa; Wu Jing; Zhao Yun-Shan

doi:10.7498/aps.72.20222095

Abstract

Nowadays, there are enormous amounts of energy wasted in the world, most of which is in the form of wasted heat. Thermoelectric effect, by converting heat energy into electricity without releasing dangerous substances, has aroused more and more interest from researchers. Since the discovery of graphene, more and more two-dimensional layered materials have been reported, which typically own superior electrical, optical and other physical properties over the bulk materials, and the development of the new theory and experimental technologies stimulates further research for them as well. In this work, first we introduce the measurement methods and techniques that are suitable for characterizing the thermoelectric properties of two-dimensional materials, and then discuss the relevant current challenging issues. Subsequently, graphene, transition metal disulfides, black phosphorus and other 2-dimensional materials in thermoelectric applications are introduced. Finally, we discuss the various strategies to improve the thermoelectric performance and the problems that need solving urgently.

Keywords:

Authors and contacts

1.
Phonon Engineering Research Center of Jiangsu Province, Center for Quantum Transport and Thermal Energy Science, Institute of Physics Frontiers and Interdisciplinary Sciences, School of Physics and Technology, Nanjing Normal University, Nanjing 210023, China
2.
Institute of Materials Research and Engineering, Agency for Science, Technology and Research, Singapore 138634, Singapore

Corresponding author: Zhang Li-Fa, phyzlf@njnu.edu.cn ; Wu Jing, wujing@imre.a-star.edu.sg ; Zhao Yun-Shan, phyzys@njnu.edu.cn

Funds: Project supported by the National Natural Science Foundation of China (Grant No. 12204244), the Natural Science Foundation of Jiangsu Province, China (Grant No. BK20210556), and the Jiangsu Specially-Appointed Professor Program, China.

FullText HTML : translate this paragraph

References

[1]	Dresselhaus M S, Chen G, Tang M Y, Yang R, Lee H, Wang D, Ren Z, Fleurial J P, Gogna P 2007 Adv. Mater. 19 1043 Google Scholar
[2]	Kim R, Datta S, Lundstrom M S 2009 J. Appl. Phys. 105 034506 Google Scholar
[3]	Maassen J, Lundstrom M 2013 Appl. Phys. Lett. 102 093103 Google Scholar
[4]	Pichanusakorn P, Bandaru P 2010 Mater. Sci. Eng. , R 67 19 Google Scholar
[5]	Hicks L D, Dresselhaus M S 1993 Phys. Rev. B 47 16631 Google Scholar
[6]	Hicks L D, Dresselhaus M S 1993 Phys. Rev. B 47 12727 Google Scholar
[7]	Song H, Liu J, Liu B, Wu J, Cheng H M, Kang F 2018 Joule 2 442 Google Scholar
[8]	Ioffe A F, Stil'Bans L, Iordanishvili E, Stavitskaya T, Gelbtuch A, Vineyard G 1959 Phys. Today 12 42
[9]	Wood C 1988 Rep. Prog. Phys. 51 459 Google Scholar
[10]	Wu J, Chen Y, Wu J, Hippalgaonkar K 2018 Adv. Electron. Mater. 4 1800248 Google Scholar
[11]	Graf M J, Yip S K, Sauls J A, Rainer D 1996 Phys. Rev. B 53 15147 Google Scholar
[12]	Jonson M, Mahan G D 1980 Phys. Rev. B 21 4223 Google Scholar
[13]	Mao J, Liu Z, Ren Z 2016 NPJ Quantum Mater. 1 16028 Google Scholar
[14]	Cutler M, Mott N F 1969 Phys. Rev. 181 1336 Google Scholar
[15]	Zuev Y M, Chang W, Kim P 2009 Phys. Rev. Lett. 102 096807 Google Scholar
[16]	Sun P, Wei B, Zhang J, Tomczak J M, Strydom A, Søndergaard M, Iversen B B, Steglich F 2015 Nat. Commun. 6 7475 Google Scholar
[17]	Mahan G, Sofo J 1996 PNAS 93 7436 Google Scholar
[18]	Sootsman J R, Chung D Y, Kanatzidis M G 2009 Angew. Chem. Int. Ed. 48 8616 Google Scholar
[19]	Ishida A, Cao D, Morioka S, Veis M, Inoue Y, Kita T 2008 Appl. Phys. Lett. 92 182105 Google Scholar
[20]	Heremans J P, Jovovic V, Toberer E S, Saramat A, Kurosaki K, Charoenphakdee A, Yamanaka S, Snyder G J 2008 Science 321 554 Google Scholar
[21]	Lee G H, Cooper R C, An S J, Lee S, Van Der Zande A, Petrone N, Hammerberg A G, Lee C, Crawford B, Oliver W 2013 Science 340 1073 Google Scholar
[22]	吴祥冰, 汤雯婷, 徐象繁 2020 物理学报 69 196602 Google Scholar Wu X, Tang W, Xu X 2020 Acta Phys. Sin. 69 196602 Google Scholar
[23]	Choi S J, Kim B K, Lee T H, Kim Y H, Li Z, Pop E, Kim J J, Song J H, Bae M H 2016 Nano Lett. 16 3969 Google Scholar
[24]	Yang F, Wu J, Suwardi A, Zhao Y, Liang B, Jiang J, Xu J, Chi D, Hippalgaonkar K, Lu J 2021 Adv. Mater. 33 2004786 Google Scholar
[25]	Saito Y, Iizuka T, Koretsune T, Arita R, Shimizu S, Iwasa Y 2016 Nano Lett. 16 4819 Google Scholar
[26]	Aiyiti A, Bai X, Wu J, Xu X, Li B 2018 Sci. Bull. 63 452 Google Scholar
[27]	Wang H, Zheng D, Zhang X, Takamatsu H, Hu W 2017 RSC Adv. 7 25298 Google Scholar
[28]	Kayyalha M, Maassen J, Lundstrom M, Shi L, Chen Y P 2016 J. Appl. Phys. 120 134305 Google Scholar
[29]	Klarskov M B, Dam H F, Petersen D H, Hansen T M, Löwenborg A, Booth T, Schmidt M S, Lin R, Nielsen P, Bøggild P 2011 Nanotechnology 22 445702 Google Scholar
[30]	Yoshimoto S, Murata Y, Kubo K, Tomita K, Motoyoshi K, Kimura T, Okino H, Hobara R, Matsuda I, Honda S, Katayama M, Hasegawa S 2007 Nano Lett. 7 956 Google Scholar
[31]	Liu K K, Zhang W, Lee Y H, Lin Y C, Chang M T, Su C Y, Chang C S, Li H, Shi Y, Zhang H 2012 Nano Lett. 12 1538 Google Scholar
[32]	Lee Y H, Zhang X Q, Zhang W, Chang M T, Lin C T, Chang K D, Yu Y C, Wang J T W, Chang C S, Li L J 2012 Adv. Mater. 24 2320 Google Scholar
[33]	Wang H, Yu L, Lee Y H, Fang W, Hsu A, Herring P, Chin M, Dubey M, Li L J, Kong J, Palacios T 2012 International Electron Devices Meeting (IEDM) San Francisco, CA, December 10-13, 2012, pp4.6.1–4.6. 4
[34]	Podzorov V, Gershenson M, Kloc C, Zeis R, Bucher E 2004 Appl. Phys. Lett. 84 3301 Google Scholar
[35]	Hippalgaonkar K, Wang Y, Ye Y, Qiu D Y, Zhu H, Wang Y, Moore J, Louie S G, Zhang X 2017 Phys. Rev. B 95 115407 Google Scholar
[36]	Song H F, Kang F Y 2022 Acta Phys. Chim. Sin 38 2101013
[37]	Zhao Y, Cai Y, Zhang L, Li B, Zhang G, Thong J T 2020 Adv. Funct. Mater. 30 1903929 Google Scholar
[38]	Gu X, Wei Y, Yin X, Li B, Yang R 2018 Rev. Mod. Phys. 90 041002 Google Scholar
[39]	Shi L, Li D, Yu C, Jang W, Kim D, Yao Z, Kim P, Majumdar A 2003 J. Heat Transfer 125 881 Google Scholar
[40]	Kim S, Shin S, Kim T, Du H, Song M, Lee C, Kim K, Cho S, Seo D H, Seo S 2016 Carbon 98 352 Google Scholar
[41]	Pettes M T, Jo I, Yao Z, Shi L 2011 Nano Lett. 11 1195 Google Scholar
[42]	Pizzocchero F, Gammelgaard L, Jessen B S, Caridad J M, Wang L, Hone J, Bøggild P, Booth T J 2016 Nat. Commun. 7 11894 Google Scholar
[43]	Zhao S, Wang H 2020 ES Energy Environ. 9 59
[44]	Wang H, Kurata K, Fukunaga T, Ago H, Takamatsu H, Zhang X, Ikuta T, Takahashi K, Nishiyama T, Takata Y 2016 Sens. Actuators, A 247 24 Google Scholar
[45]	Suh J, Yu K M, Fu D, Liu X, Yang F, Fan J, Smith D J, Zhang Y H, Furdyna J K, Dames C 2015 Adv. Mater. 27 3681 Google Scholar
[46]	Goldsmid H, Sharp J 1999 J. Electron. Mater. 28 869 Google Scholar
[47]	Kim H S, Gibbs Z M, Tang Y, Wang H, Snyder G J 2015 APL Mater. 3 041506 Google Scholar
[48]	Lee C, Wei X, Kysar J W, Hone J 2008 Science 321 385 Google Scholar
[49]	Grigorenko A N, Polini M, Novoselov K 2012 Nat. Photonics 6 749 Google Scholar
[50]	Novoselov K S, Geim A K, Morozov S V, Jiang D, Katsnelson M I, Grigorieva I, Dubonos S, Firsov a 2005 Nature 438 197 Google Scholar
[51]	Novoselov K S, Geim A K, Morozov S V, Jiang D, Zhang Y, Dubonos S V, Grigorieva I V, Firsov A A 2004 Science 306 666 Google Scholar
[52]	Zhang Y, Tan Y W, Stormer H L, Kim P 2005 Nature 438 201 Google Scholar
[53]	Neto A C, Guinea F, Peres N M, Novoselov K S, Geim A K 2009 Rev. Mod. Phys. 81 109 Google Scholar
[54]	Cai W, Moore A L, Zhu Y, Li X, Chen S, Shi L, Ruoff R S 2010 Nano Lett. 10 1645 Google Scholar
[55]	Novoselov K S, Jiang D, Schedin F, Booth T, Khotkevich V, Morozov S, Geim A K 2005 PNAS 102 10451 Google Scholar
[56]	Balandin A A, Ghosh S, Bao W, Calizo I, Teweldebrhan D, Miao F, Lau C N 2008 Nano Lett. 8 902 Google Scholar
[57]	Ghosh D, Calizo I, Teweldebrhan D, Pokatilov E P, Nika D L, Balandin A A, Bao W, Miao F, Lau C N 2008 Appl. Phys. Lett. 92 151911 Google Scholar
[58]	Xu X, Pereira L F, Wang Y, Wu J, Zhang K, Zhao X, Bae S, Tinh Bui C, Xie R, Thong J T 2014 Nat. Commun. 5 3689 Google Scholar
[59]	Lindsay L, Broido D, Mingo N 2011 Phys. Rev. B 83 235428 Google Scholar
[60]	Wei P, Bao W, Pu Y, Lau C N, Shi J 2009 Phys. Rev. Lett. 102 166808 Google Scholar
[61]	Checkelsky J G, Ong N 2009 Phys. Rev. B 80 081413 Google Scholar
[62]	Hwang E, Rossi E, Sarma S D 2009 Phys. Rev. B 80 235415 Google Scholar
[63]	Wang C R, Lu W S, Hao L, Lee W L, Lee T K, Lin F, Cheng I C, Chen J Z 2011 Phys. Rev. Lett. 107 186602 Google Scholar
[64]	Nam S G, Ki D K, Lee H J 2010 Phys. Rev. B 82 245416 Google Scholar
[65]	Wang D, Shi J 2011 Phys. Rev. B 83 113403 Google Scholar
[66]	Seol J H, Moore A L, Shi L, Jo I, Yao Z 2011 J. Heat Transfer 133 022403 Google Scholar
[67]	Jang W, Chen Z, Bao W, Lau C N, Dames C 2010 Nano Lett. 10 3909 Google Scholar
[68]	Yang J, Ziade E, Maragliano C, Crowder R, Wang X, Stefancich M, Chiesa M, Swan A K, Schmidt A J 2014 J. Appl. Phys. 116 023515 Google Scholar
[69]	Ghosh S, Bao W, Nika D L, Subrina S, Pokatilov E P, Lau C N, Balandin A A 2010 Nat. Mater. 9 555 Google Scholar
[70]	Wang J, Zhu L, Chen J, Li B, Thong J T 2013 Adv. Mater. 25 6884 Google Scholar
[71]	Dean C R, Young A F, Meric I, Lee C, Wang L, Sorgenfrei S, Watanabe K, Taniguchi T, Kim P, Shepard K L 2010 Nat. Nanotechnol. 5 722 Google Scholar
[72]	Nomura K, MacDonald A H 2007 Phys. Rev. Lett. 98 076602 Google Scholar
[73]	Chen J H, Jang C, Xiao S, Ishigami M, Fuhrer M S 2008 Nat. Nanotechnol. 3 206 Google Scholar
[74]	Hwang E, Adam S, Sarma S D 2007 Phys. Rev. Lett. 98 186806 Google Scholar
[75]	Ando T 2006 J. Phys. Soc. Jpn. 75 074716 Google Scholar
[76]	Morozov S, Novoselov K, Katsnelson M, Schedin F, Elias D C, Jaszczak J A, Geim A 2008 Phys. Rev. Lett. 100 016602 Google Scholar
[77]	Katsnelson M, Geim A 2008 Philos. Trans. R. Soc. London, Ser. A 366 195
[78]	Ishigami M, Chen J, Cullen W, Fuhrer M, Williams E 2007 Nano Lett. 7 1643 Google Scholar
[79]	Fratini S, Guinea F 2008 Phys. Rev. B 77 195415 Google Scholar
[80]	Duan J, Wang X, Lai X, Li G, Watanabe K, Taniguchi T, Zebarjadi M, Andrei E Y 2016 PNAS 113 14272 Google Scholar
[81]	Zebarjadi M 2015 Appl. Phys. Lett. 106 203506 Google Scholar
[82]	Seol J H, Jo I, Moore A L, Lindsay L, Aitken Z H, Pettes M T, Li X, Yao Z, Huang R, Broido D 2010 Science 328 213 Google Scholar
[83]	Mak K F, Lee C, Hone J, Shan J, Heinz T F 2010 Phys. Rev. Lett. 105 136805 Google Scholar
[84]	Liu X, Zhang G, Pei Q X, Zhang Y W 2013 Appl. Phys. Lett. 103 133113 Google Scholar
[85]	Bertolazzi S, Brivio J, Kis A 2011 ACS Nano 5 9703 Google Scholar
[86]	Wilson J A, Yoffe A 1969 Adv. Phys. 18 193 Google Scholar
[87]	Seh Z W, Yu J H, Li W, Hsu P-C, Wang H, Sun Y, Yao H, Zhang Q, Cui Y 2014 Nat. Commun. 5 5017 Google Scholar
[88]	Yin Z, Li H, Li H, Jiang L, Shi Y, Sun Y, Lu G, Zhang Q, Chen X, Zhang H 2012 ACS Nano 6 74 Google Scholar
[89]	Wang X, Wang P, Wang J, Hu W, Zhou X, Guo N, Huang H, Sun S, Shen H, Lin T 2015 Adv. Mater. 27 6575 Google Scholar
[90]	Zhu H, Wang Y, Xiao J, Liu M, Xiong S, Wong Z J, Ye Z, Ye Y, Yin X, Zhang X 2015 Nat. Nanotechnol. 10 151 Google Scholar
[91]	Wu W, Wang L, Li Y, Zhang F, Lin L, Niu S, Chenet D, Zhang X, Hao Y, Heinz T F 2014 Nature 514 470 Google Scholar
[92]	Cao T, Wang G, Han W, Ye H, Zhu C, Shi J, Niu Q, Tan P, Wang E, Liu B 2012 Nat. Commun. 3 887 Google Scholar
[93]	Yu H, Yao W 2017 Nat. Mater. 16 876 Google Scholar
[94]	Wei X, Wang Y, Shen Y, Xie G, Xiao H, Zhong J, Zhang G 2014 Appl. Phys. Lett. 105 103902 Google Scholar
[95]	Ding Z, Jiang J W, Pei Q X, Zhang Y W 2015 Nanotechnology 26 065703 Google Scholar
[96]	Zhao Y, Zheng M, Wu J, Huang B, Thong J T 2020 Nanotechnology 31 225702 Google Scholar
[97]	Peng B, Ning Z, Zhang H, Shao H, Xu Y, Ni G, Zhu H 2016 J. Phys. Chem. C 120 29324 Google Scholar
[98]	Ding Z, Pei Q X, Jiang J W, Zhang Y W 2015 J. Phys. Chem. C 119 16358 Google Scholar
[99]	Gu X, Li B, Yang R 2016 J. Appl. Phys. 119 085106 Google Scholar
[100]	Xu K, Gabourie A J, Hashemi A, Fan Z, Wei N, Farimani A B, Komsa H-P, Krasheninnikov A V, Pop E, Ala-Nissila T 2019 Phys. Rev. B 99 054303 Google Scholar
[101]	Zhou W, Gong H M, Jin X H, Chen Y, Li H M, Liu S 2022 Front. Phys. 10 842789 Google Scholar
[102]	Yoon Y, Ganapathi K, Salahuddin S 2011 Nano Lett. 11 3768 Google Scholar
[103]	Baugher B W, Churchill H O, Yang Y, Jarillo-Herrero P 2013 Nano Lett. 13 4212 Google Scholar
[104]	Cai X, Wu Z, Han X, Chen Y, Xu S, Lin J, Han T, He P, Feng X, An L 2022 Nat. Commun. 13 1777 Google Scholar
[105]	Ng H, Chi D, Hippalgaonkar K 2017 J. Appl. Phys. 121 204303 Google Scholar
[106]	Yoshida M, Iizuka T, Saito Y, Onga M, Suzuki R, Zhang Y, Iwasa Y, Shimizu S 2016 Nano Lett. 16 2061 Google Scholar
[107]	Zhao Y, Yu P, Zhang G, Sun M, Chi D, Hippalgaonkar K, Thong J T, Wu J 2020 Adv. Funct. Mater. 30 2004896 Google Scholar
[108]	Zeng J, He X, Liang S J, Liu E, Sun Y, Pan C, Wang Y, Cao T, Liu X, Wang C 2018 Nano Lett. 18 7538 Google Scholar
[109]	Lindroth D O, Erhart P 2016 Phys. Rev. B 94 115205 Google Scholar
[110]	Jiang P, Qian X, Gu X, Yang R 2017 Adv. Mater. 29 1701068 Google Scholar
[111]	Wickramaratne D, Zahid F, Lake R K 2014 J. Phys. Chem. 140 124710 Google Scholar
[112]	Imai H, Shimakawa Y, Kubo Y 2001 Phys. Rev. B 64 241104 Google Scholar
[113]	Qin D, Yan P, Ding G, Ge X, Song H, Gao G 2018 Sci. Rep. 8 2764 Google Scholar
[114]	Oyedele A D, Yang S, Liang L, Puretzky A A, Wang K, Zhang J, Yu P, Pudasaini P R, Ghosh A W, Liu Z 2017 J. Am. Chem. Soc. 139 14090 Google Scholar
[115]	Li J, Zhang X, Chen Z, Lin S, Li W, Shen J, Witting I T, Faghaninia A, Chen Y, Jain A 2018 Joule 2 976 Google Scholar
[116]	Tangpakonsab P, Moontragoon P, Hussain T, Kaewmaraya T 2022 ACS Appl. Energy Mater. 5 13081 Google Scholar
[117]	Hung N T, Nugraha A R T, Saito R 2017 Appl. Phys. Lett. 111 092107 Google Scholar
[118]	Hung N T, Nugraha A R T, Yang T, Zhang Z D, Saito R 2019 J. Appl. Phys. 125 082502 Google Scholar
[119]	Wang Q, Han L, Wu L, Zhang T, Li S, Lu P 2019 Nanoscale Res. Lett. 14 287 Google Scholar
[120]	Li L, Yu Y, Ye G J, Ge Q, Ou X, Wu H, Feng D, Chen X H, Zhang Y 2014 Nat. Nanotechnol. 9 372 Google Scholar
[121]	St Laurent B, Dey D, Yu L, Hollen S 2021 ACS Appl. Electron. Mater. 3 4066 Google Scholar
[122]	Hu Z, Li Q, Lei B, Zhou Q, Xiang D, Lyu Z, Hu F, Wang J, Ren Y, Guo R 2017 Angew. Chem. Int. Ed. 56 9131 Google Scholar
[123]	Abate Y, Akinwande D, Gamage S, Wang H, Snure M, Poudel N, Cronin S B 2018 Adv. Mater. 30 1704749 Google Scholar
[124]	Zhang J L, Han C, Hu Z, Wang L, Liu L, Wee A T, Chen W 2018 Adv. Mater. 30 1802207 Google Scholar
[125]	Lee S, Yang F, Suh J, Yang S, Lee Y, Li G, Choe H S, Suslu A, Chen Y, Ko C 2015 Nat. Commun. 6 8573 Google Scholar
[126]	Zhao Y, Zhang G, Nai M H, Ding G, Li D, Liu Y, Hippalgaonkar K, Lim C T, Chi D, Li B 2018 Adv. Mater. 30 1804928 Google Scholar
[127]	Liu H, Choe H S, Chen Y, Suh J, Ko C, Tongay S, Wu J 2017 Appl. Phys. Lett. 111 102101 Google Scholar
[128]	Luo Z, Maassen J, Deng Y, Du Y, Garrelts R P, Lundstrom M S, Ye P D, Xu X 2015 Nat. Commun. 6 8572 Google Scholar
[129]	Qin G, Yan Q B, Qin Z, Yue S Y, Hu M, Su G 2015 Phys. Chem. Chem. Phys. 17 4854 Google Scholar
[130]	Zhao Y, Yang L, Kong L, Nai M H, Liu D, Wu J, Liu Y, Chiam S Y, Chim W K, Lim C T 2017 Adv. Funct. Mater. 27 1702824 Google Scholar
[131]	Flores E, Ares J R, Castellanos-Gomez A, Barawi M, Ferrer I J, Sánchez C 2015 Appl. Phys. Lett. 106 022102 Google Scholar
[132]	Zhang J, Liu H, Cheng L, Wei J, Liang J, Fan D, Jiang P, Sun L, Shi J 2016 J. Mater. Chem. C 4 991 Google Scholar
[133]	Lü H, Lu W, Shao D, Lu H, Sun Y 2016 J. Mater. Chem. C 4 4538 Google Scholar
[134]	Carrete J, Mingo N, Curtarolo S 2014 Appl. Phys. Lett. 105 101907 Google Scholar
[135]	Zhang L C, Qin G, Fang W Z, Cui H J, Zheng Q R, Yan Q B, Su G 2016 Sci. Rep. 6 35705 Google Scholar
[136]	Ding G, Hu Y, Li D, Wang X 2019 Results Phys. 15 102631 Google Scholar
[137]	Guo R, Wang X, Kuang Y, Huang B 2015 Phys. Rev. B 92 115202 Google Scholar
[138]	Zhao L D, Lo S H, Zhang Y, Sun H, Tan G, Uher C, Wolverton C, Dravid V P, Kanatzidis M G 2014 Nature 508 373 Google Scholar
[139]	Zhou C, Lee Y K, Yu Y, Byun S, Luo Z Z, Lee H, Ge B, Lee Y L, Chen X, Lee J Y 2021 Nat. Mater. 20 1378 Google Scholar
[140]	Sun Y, Shuai Z, Wang D 2019 J. Phys. Chem. C 123 12001 Google Scholar
[141]	Zhao T, Sun Y, Shuai Z, Wang D 2017 Chem. Mater. 29 6261 Google Scholar
[142]	Wu M, Zeng X C 2017 Nano Lett. 17 6309 Google Scholar
[143]	Wu J, Liu Y, Tan Z, Tan C, Yin J, Li T, Tu T, Peng H 2017 Adv. Mater. 29 1704060 Google Scholar
[144]	Fu Q, Zhu C, Zhao X, Wang X, Chaturvedi A, Zhu C, Wang X, Zeng Q, Zhou J, Liu F 2019 Adv. Mater. 31 1804945 Google Scholar
[145]	Wu J, Yuan H, Meng M, Chen C, Sun Y, Chen Z, Dang W, Tan C, Liu Y, Yin J 2017 Nat. Nanotechnol. 12 530 Google Scholar
[146]	Yang F, Wang R, Zhao W, Jiang J, Wei X, Zheng T, Yang Y, Wang X, Lu J, Ni Z 2019 Appl. Phys. Lett. 115 193103 Google Scholar
[147]	Leburton J P 1984 J. Appl. Phys. 56 2850 Google Scholar
[148]	Gelmont B, Shur M, Stroscio M 1995 J. Appl. Phys. 77 657 Google Scholar
[149]	Paul S, Bhattacharya D 1989 Phys. Rev. B 39 13521 Google Scholar
[150]	Alkan B, Unal B, Ozdemir A 1995 Semicond. Sci. Technol. 10 1458 Google Scholar
[151]	Zook J D 1964 Phys. Rev. 136 A869 Google Scholar
[152]	Wang F Q, Guo Y, Wang Q, Kawazoe Y, Jena P 2017 Chem. Mater. 29 9300 Google Scholar
[153]	Rau J W, Kannewurf C 1971 Phys. Rev. B 3 2581 Google Scholar
[154]	Li L, Gong P, Sheng D, Wang S, Wang W, Zhu X, Shi X, Wang F, Han W, Yang S 2018 Adv. Mater. 30 1804541 Google Scholar
[155]	Panasci S, Schilirò E, Migliore F, Cannas M, Gelardi F, Roccaforte F, Giannazzo F, Agnello S 2021 Appl. Phys. Lett. 119 093103 Google Scholar
[156]	Velicky M, Donnelly G E, Hendren W R, McFarland S, Scullion D, DeBenedetti W J, Correa G C, Han Y, Wain A J, Hines M A 2018 ACS Nano 12 10463 Google Scholar
[157]	Liu F 2021 Prog. Surf. Sci. 96 100626 Google Scholar
[158]	Zou B, Zhou Y, Zhou Y, Wu Y, He Y, Wang X, Yang J, Zhang L, Chen Y, Zhou S, Guo H, Sun H 2022 Nano Res. 15 8470 Google Scholar
[159]	Wu J, Liu Y, Liu Y, Cai Y, Zhao Y, Ng H K, Watanabe K, Taniguchi T, Zhang G, Qiu C W 2020 PNAS 117 13929 Google Scholar
[160]	Sharma M, Kumar A, Ahluwalia P 2019 Physica E 107 117 Google Scholar
[161]	Zheng Y, Slade T J, Hu L, Tan X Y, Luo Y, Luo Z Z, Xu J, Yan Q, Kanatzidis M G 2021 Chem. Soc. Rev. 50 9022 Google Scholar
[162]	Yan Z, Yoon M, Kumar S 2018 2 D Mater. 5 031008
[163]	Zhao Y, Zheng M, Wu J, Guan X, Suwardi A, Li Y, Lal M, Xie G, Zhang G, Zhang L 2021 Nanoscale 13 11561 Google Scholar
[164]	Aiyiti A, Hu S, Wang C, Xi Q, Cheng Z, Xia M, Ma Y, Wu J, Guo J, Wang Q 2018 Nanoscale 10 2727 Google Scholar
[165]	Chen J H, Li L, Cullen W G, Williams E D, Fuhrer M S 2011 Nat. Phys. 7 535 Google Scholar
[166]	Takahashi H, Okazaki R, Ishiwata S, Taniguchi H, Okutani A, Hagiwara M, Terasaki I 2016 Nat. Commun. 7 12732 Google Scholar
[167]	Zhou J, Liao B, Qiu B, Huberman S, Esfarjani K, Dresselhaus M S, Chen G 2015 PNAS 112 14777 Google Scholar
[168]	Pan Y, Chen S, Wang P, Li Y, Zheng Q 2019 Ceram. Int. 45 19534 Google Scholar
[169]	Lee W, Lim G, Ko S H 2021 Nano Energy 87 106188 Google Scholar
[170]	Wu X, Yang N, Luo T 2015 Appl. Phys. Lett. 107 191907 Google Scholar
[171]	Rosi F 1968 Solid-State Electron. 11 833 Google Scholar
[172]	Guo Y, Dun C, Xu J, Li P, Huang W, Mu J, Hou C, Hewitt C A, Zhang Q, Li Y 2018 ACS Appl. Mater. Interfaces 10 33316 Google Scholar
[173]	Ng H K, Abutaha A, Voiry D, Verzhbitskiy I, Cai Y, Zhang G, Liu Y, Wu J, Chhowalla M, Eda G 2019 ACS Appl. Mater. Interfaces 11 12184 Google Scholar
[174]	An C J, Kang Y H, Lee C, Cho S Y 2018 Adv. Funct. Mater. 28 1800532 Google Scholar
[175]	Xiang D, Han C, Wu J, Zhong S, Liu Y, Lin J, Zhang X A, Ping Hu W, Özyilmaz B, Neto A 2015 Nat. Commun. 6 8949 Google Scholar
[176]	Kong S, Wu T, Yuan M, Huang Z, Meng Q L, Jiang Q, Zhuang W, Jiang P, Bao X 2017 J. Mater. Chem. A 5 2004 Google Scholar
[177]	Perera M M, Lin M W, Chuang H J, Chamlagain B P, Wang C T, Tan X B, Cheng M M C, Tománek D, Zhou Z X 2013 ACS Nano 7 4449 Google Scholar
[178]	Böttner H, Chen G, Venkatasubramanian R 2006 MRS Bull. 31 211 Google Scholar
[179]	Venkatasubramanian R, Siivola E, Colpitts T, O'quinn B 2001 Nature 413 597 Google Scholar
[180]	Harman T, Taylor P, Walsh M, LaForge B 2002 Science 297 2229 Google Scholar
[181]	Harman T, Taylor P, Spears D, Walsh M 2000 J. Electron. Mater. 29 L1 Google Scholar
[182]	Hicks L, Harman T, Sun X, Dresselhaus M 1996 Phys. Rev. B 53 R10493 Google Scholar
[183]	Ding G, He J, Gao G, Yao K 2018 J. Appl. Phys. 124 165101 Google Scholar
[184]	Wan C, Gu X, Dang F, Itoh T, Wang Y, Sasaki H, Kondo M, Koga K, Yabuki K, Snyder G J 2015 Nat. Mater. 14 622 Google Scholar
[185]	Wang S, Yang X, Hou L, Cui X, Zheng X, Zheng J 2022 Nat. Commun. 13 4401 Google Scholar
[186]	Luckyanova M N, Garg J, Esfarjani K, Jandl A, Bulsara M T, Schmidt A J, Minnich A J, Chen S, Dresselhaus M S, Ren Z 2012 Science 338 936 Google Scholar
[187]	Zhang G, Zhang Y W 2015 Mech. Mater. 91 382 Google Scholar
[188]	Peng Z, Chen X, Fan Y, Srolovitz D J, Lei D 2020 Light Sci. Appl. 9 190 Google Scholar
[189]	Yang S, Chen Y, Jiang C 2021 InfoMat 3 397 Google Scholar
[190]	Yan Y, Ding S, Wu X, Zhu J, Feng D, Yang X, Li F 2020 RSC Adv. 10 39455 Google Scholar
[191]	Manzeli S, Allain A, Ghadimi A, Kis A 2015 Nano Lett. 15 5330 Google Scholar
[192]	Meng L, Zhang Y, Hu S, Wang X, Liu C, Guo Y, Wang X, Yan X 2016 Appl. Phys. Lett. 108 263104 Google Scholar
[193]	Castellanos-Gomez A, Roldán R, Cappelluti E, Buscema M, Guinea F, van der Zant H S, Steele G A 2013 Nano Lett. 13 5361 Google Scholar
[194]	Zhu C, Wang G, Liu B, Marie X, Qiao X, Zhang X, Wu X, Fan H, Tan P, Amand T 2013 Phys. Rev. B 88 121301 Google Scholar
[195]	Ng H K, Xiang D, Suwardi A, Hu G, Yang K, Zhao Y, Liu T, Cao Z, Liu H, Li S 2022 Nat. Electron. 5 489 Google Scholar
[196]	Jiang J W, Park H S, Rabczuk T 2013 J. Appl. Phys. 114 064307 Google Scholar
[197]	Conley H J, Wang B, Ziegler J I, Haglund Jr R F, Pantelides S T, Bolotin K I 2013 Nano Lett. 13 3626 Google Scholar
[198]	Desai S B, Seol G, Kang J S, Fang H, Battaglia C, Kapadia R, Ager J W, Guo J, Javey A 2014 Nano Lett. 14 4592 Google Scholar
[199]	Hoat D, Naseri M, Binh N T, Vu T V, Rivas-Silva J, Obeid M M, Cocoletzi G H 2021 Phys. B:Condens. Matter 603 412757 Google Scholar
[200]	Qin G, Yan Q B, Qin Z, Yue S Y, Cui H J, Zheng Q R, Su G 2014 Sci. Rep. 4 6946 Google Scholar
[201]	Bera J, Sahu S 2019 RSC Adv. 9 25216 Google Scholar
[202]	Qin D, Ge X J, Ding G Q, Gao G Y, Lü J T 2017 RSC Adv. 7 47243 Google Scholar

Cited By

图 1 (a) 塞贝克系数、电导率、功率因数随载流子浓度的相互依赖关系和电子热导率与晶格热导率随载流子浓度的依赖关系^[10]; (b) 不同维度材料的电子态密度随能量的变化关系^[13]

Figure 1. (a) The interdependence of Seebeck coefficient, conductivity, power factor for different carrier concentration and electron thermal conductivity and lattice thermal conductivity as a function of carrier concentration^[10]; (b) electronic DOS of different dimensional materials as a function of energy^[13].

DownLoad: Full-Size Img PowerPoint

图 2 (a) 基于场效应晶体管对二维半导体热电性质测量器件示意图^[24]; (b) 利用电子双层结构离子液体晶体管对二维材料的热电性质测量器件示意图^[25]; (c) 悬空热桥法器件示意图^[26]; (d) 利用H型方法测量样品的塞贝克系数示意图^[27]

Figure 2. (a) Schematic image of device for measuring thermoelectric property based on field effect transistor (FET)^[24]; (b) schematic image of device for thermoelectric property measurement based on electronic double-layer structure ionic liquid transistor^[25]; (c) schematic image of suspended thermal bridge device^[26]; (d) schematic image of H-type method device^[27].

DownLoad: Full-Size Img PowerPoint

图 3 (a) 石墨烯中不同声子模式对热导率的贡献^[59]; (b) 石墨烯热导率与样品长度关系的不同结果汇总^[38]; (c) 石墨烯的电导率和塞贝克系数随栅极电压的变化关系(上方插图为石墨烯器件的扫描电子显微镜图像, 下方插图为${V_{\rm{g}}}$ = –5, –30 V时塞贝克系数随温度的变化)^[15]; (d) 在290 K下, G/hBN和G/SiO₂的PFT随栅极电压的变化关系^[10]

Figure 3. (a) Contribution of different phonon modes to thermal conductivity in graphene^[59]; (b) summary of thermal conductivity of graphene as a function of sample length^[38]; (c) conductivity and Seebeck coefficient of graphene as a function of gate voltage (Upper inset: SEM image of a graphene device, the scale bar is 2 μm. Lower inset: Seebeck coefficient of graphene as a function of temperature at ${V_{\rm{g}}}$ = –5, –30 V) ^[15]; (d) PFT as a function of gate voltage in both devices at 290 K^[10].

DownLoad: Full-Size Img PowerPoint

图 4 (a) 单层二硫化钼的示意图(其中紫色为Mo原子、黄色为S原子)^[84]; (b) 室温下关于MoS₂的热导率研究结果的汇总^[38]; (c) 不同${V_{\rm{g}}} - {V_{\rm th}}$下, 四端法测得的MoS₂的电导率和塞贝克系数随样品厚度(层数)的变化关系^[28]; (d) 不同${V_{\rm{g}}} - {V_{\rm th}}$下, MoS₂的功率因数随样品厚度(层数)的变化关系^[28]; (e) 不同厚度(1—3层)的MoS₂的功率因数随${V_g}$的变化关系^[35]

Figure 4. (a) Schematic image of monolayer MoS₂ (Where purple is Mo atom and yellow is S atom) ^[84]; (b) summary of thermal conductivity of MoS₂ at room temperature^[38]; (c) four-probe conductivity and Seebeck coefficient of MoS₂ as a function of the thickness (number of layers) measured at different ${V_{\rm{g}}} - {V_{\rm th}}$ values; (d) PF of MoS₂ as a function of the thickness (number of layers) measured at different ${V_{\rm{g}}} - {V_{\rm th}}$ values^[28]; (e) PF of MoS₂ with different thick (monolayer-three layers) as a function of the ${V_{\rm{g}}}$^[35].

DownLoad: Full-Size Img PowerPoint

图 5 (a) 300 K下, 极薄单晶WSe₂的电导率(两端法)、塞贝克系数和功率因数随${V_{\rm{g}}}$的变化关系^[106]; (b) 厚度为5和9 nm的PdSe₂薄片的功率因数^[107]; (c) 室温下不同厚度的InSe薄膜的功率因数随载流子浓度的变化关系^[108]

Figure 5. (a) ${\sigma _{{\text{2D}}}}$, $S$ and ${S^2}\sigma $ of ultrathin WSe₂ single crystals as a function of the ${V_{\text{g}}}$ at T = 300 K^[106]; (b) power factor of PdSe₂ flakes with thickness of 5 and 9 nm^[107]; (c) power factor of InSe film with different thickness as a function of carrier concentration at room temperature^[108].

DownLoad: Full-Size Img PowerPoint

图 6 (a) 黑磷晶体结构的示意图^[125]; (b) 黑磷纳米带在AC和ZZ方向的热导率和杨氏模量测量值, 其中热导率和杨氏模量有着相似的各向异性比值(分别为2.24和2.05)^[126]; (c) AC方向和ZZ方向的黑磷纳米带电导率(c)和塞贝克系数(d)随温度的变化关系^[127]; (e) 黑磷塞贝克系数的少层实验数据和体块理论计算数值(实线为${S_x}$, 虚线为${S_y}$)的比较^[25]; (f) 210 K下, 少层黑磷的功率因数随栅极电压的变化关系^[25]

Figure 6. (a) Schematic image of BP reproduced with permission^[125]; (b) thermal conductivity and Young’s modulus values of the BP nanoribbons. The thermal conductivity anisotropy ratio (≈2.24) between ZZ and AC is similar to that of Young’s modulus (≈2.05)^[126]; temperature dependence of electrical conductivity (c) and Seebeck coefficient (d) of BP nanoribbons along the AC and ZZ directions^[127]; (e) comparison between experimental data and bulk values of theoretical calculation (${S_x}$, solid line; ${S_y}$ dashed line) of Seebeck coefficient of BP^[25]; (f) power factor of few layer BP as a function of gate voltage at 210 K^[25].

DownLoad: Full-Size Img PowerPoint

图 7 (a) 少层Bi₂O₂Se晶体的功率因数随着栅极电压和温度的变化关系^[24]; (b) 单层GeAs₂(n型或p型)在不同温度下的热电优值的最大值^[141]

Figure 7. (a) PF of few-layer Bi₂O₂Se as a function of gate voltage and temperature^[24]; (b) maximum ZT of monolayer GeAs₂ at different temperature (including n type and p type)^[141].

DownLoad: Full-Size Img PowerPoint

图 8 (a) MoS₂/hBN器件的四端法电导率随温度和栅极电压的变化关系(低温下电导率出现异常的峰值用红色虚线标出)^[159]; (b) MoS₂/SiO₂和MoS₂/hBN器件的塞贝克系数与温度的变化关系(其中MoS₂/hBN器件${V_{\rm{g}}}$ = 70 V以圆形表示, ${V_g}$ = 50 V以方形表示, ${V_{\rm{g}}}$= 30 V以钻石形状表示)^[159]; (c) 氦离子辐射同时增加Bi₂Te₃塞贝克系数和载流子浓度(虚线为不同散射弛豫时间指数下塞贝克系数的计算结果)^[45]; (d) 不同厚度的Bi₂Te₃的功率因数随辐射剂量的变化关系^[45]

Figure 8. (a) Four-probe electrical conductivity of MoS₂/hBN devices as a function of Temperature and back gate voltage^[159]; (b) temperature dependent Seebeck coefficient of MoS₂/SiO₂ and MoS₂/hBN device at ${V_{\rm{g}}}$ = 70 V (circle), 50 V (square), and 30 V (diamond) ^[159]; (c) the simultaneous increase of Seebeck coefficient and carrier concentration of helium ion irradiated Bi₂Te₃^[45]; (d) irradiation dose dependent power factor of Bi₂Te₃ with different thicknesses^[45].

DownLoad: Full-Size Img PowerPoint

图 9 (a) 在SiO₂/Si基底上, 真空退火3次Li_xMoS₂的拉曼光谱图^[173]; (b) 经过每次退火后的Li_xMoS₂的塞贝克系数、电导率和功率因数^[173]; (c) 沿各个方向的本征MoS₂和氧原子掺杂MoS₂的PF随温度的变化^[176]; (d) 沿各个方向的本征MoS₂和氧原子掺杂MoS₂的热导率随温度的变化^[176]

Figure 9. (a) Raman spectra of a Li_xMoS₂ flake on SiO₂/Si substrate across three separate annealing cycles performed in vacuum^[173]; (b) Seebeck coefficient, electrical conductivity, and power factor of Li_xMoS₂ device across all annealing cycles^[173]; (c) power factor of the pristine MoS₂ and oxygen-doped MoS₂ along both directions^[176]; (d) thermal conductivity of the pristine MoS₂ and oxygen-doped MoS₂ along both directions^[176].

DownLoad: Full-Size Img PowerPoint

图 10 (a) Bi₂Te₃/Sb₂Te₃超晶格、PbSnSeTe/PbTe量子点超晶格、PbTe_0.02Se_0.98/PbTe量子点超晶格的热电优值^[178]; (b) 计算获得的不同周期厚度的横向超晶格晶格热导率随温度的关系^[183]; (c) TiS₂[(HA)_x(H₂O)_y(DMSO)_z]超晶格材料的HAADF-STEM 图像(展示了褶皱的晶格结构)^[10]; (d) 放大的TiS₂[(HA)_x(H₂O)_y(DMSO)_z]超晶格材料的HAADF-STEM 图像^[10]; (e) 本征TaS₂和SCCM-TaS₂的电导率^[185]; (f) 本征TaS₂和SCCM-TaS₂的塞贝克系数^[185]

Figure 10. (a) Thermoelectric figure of merit for Bi₂Te₃/Sb₂Te₃ superlattices, PbSnSeTe/PbTe quantum dot superlattices, and PbTe_0.02Se_0.98/PbTe quantum dot superlattices^[178]; (b) temperature dependence of calculated lattice thermal conductivity of lateral superlattices with different periodic thicknesses^[183]; (c) HAADF-STEM (high-angle annular dark field scanning transmission electron microscope) image of the TiS₂[(HA)_x(H₂O)_y(DMSO)_z] hybrid superlattice showing a wavy structure^[10]. (d) magnified HAADF-STEM image of TiS₂[(HA)_x(H₂O)_y(DMSO)_z]^[10]; (e) electrical conductivity of the pristine TaS₂ crystals and SCCM-TaS₂ hybrid structure^[185]; (f) seebeck coefficient of the pristine TaS₂ crystals and SCCM-TaS₂ hybrid structure^[185].

DownLoad: Full-Size Img PowerPoint

图 11 (a) 利用AFM对悬空单层MoS₂施加应力的示意图^[85]; (b) 褶皱的单层MoS₂的构造过程示意图^[193]; (c) 利用三点弯曲法对MoS₂进行延伸示意图^[194]; (d) 黑磷的热电优值随温度和应变的变化关系^[199]; (e) 在300, 600和900 K下施加双向压缩和拉伸应变的n型或p型WS₂的${{{S^2}\sigma } \mathord{\left/ {\vphantom {{{S^2}\sigma } \tau }} \right. } \tau }$值^[201]; (f) 不同厚度(层数)的平坦和褶皱的MoS₂的功率因数随载流子浓度的变化关系^[195]

Figure 11. (a) Schematic image of inducing strain to the suspended monolayer MoS₂ by AFM^[85]; (b) schematic image of the fabrication process of wrinkled MoS₂ nanolayers^[193]; (c) schematic image of the extension of MoS₂ by the three-point bending apparatus^[194]; (d) ZT of BP as a function of temperature and strain^[199]; (e)${{{S^2}\sigma } \mathord{\left/ {\vphantom {{{S^2}\sigma } \tau }} \right. } \tau }$ of WS₂ with applied both biaxial compressive and tensile strain for n-type and p-type doping at 300, 600 and 900 K^[201]; (f) PF of flat and ripped MoS₂ as a function of carrier concentration with different thickness^[195].

DownLoad: Full-Size Img PowerPoint

[1]	Dresselhaus M S, Chen G, Tang M Y, Yang R, Lee H, Wang D, Ren Z, Fleurial J P, Gogna P 2007 Adv. Mater. 19 1043 Google Scholar
[2]	Kim R, Datta S, Lundstrom M S 2009 J. Appl. Phys. 105 034506 Google Scholar
[3]	Maassen J, Lundstrom M 2013 Appl. Phys. Lett. 102 093103 Google Scholar
[4]	Pichanusakorn P, Bandaru P 2010 Mater. Sci. Eng. , R 67 19 Google Scholar
[5]	Hicks L D, Dresselhaus M S 1993 Phys. Rev. B 47 16631 Google Scholar
[6]	Hicks L D, Dresselhaus M S 1993 Phys. Rev. B 47 12727 Google Scholar
[7]	Song H, Liu J, Liu B, Wu J, Cheng H M, Kang F 2018 Joule 2 442 Google Scholar
[8]	Ioffe A F, Stil'Bans L, Iordanishvili E, Stavitskaya T, Gelbtuch A, Vineyard G 1959 Phys. Today 12 42
[9]	Wood C 1988 Rep. Prog. Phys. 51 459 Google Scholar
[10]	Wu J, Chen Y, Wu J, Hippalgaonkar K 2018 Adv. Electron. Mater. 4 1800248 Google Scholar
[11]	Graf M J, Yip S K, Sauls J A, Rainer D 1996 Phys. Rev. B 53 15147 Google Scholar
[12]	Jonson M, Mahan G D 1980 Phys. Rev. B 21 4223 Google Scholar
[13]	Mao J, Liu Z, Ren Z 2016 NPJ Quantum Mater. 1 16028 Google Scholar
[14]	Cutler M, Mott N F 1969 Phys. Rev. 181 1336 Google Scholar
[15]	Zuev Y M, Chang W, Kim P 2009 Phys. Rev. Lett. 102 096807 Google Scholar
[16]	Sun P, Wei B, Zhang J, Tomczak J M, Strydom A, Søndergaard M, Iversen B B, Steglich F 2015 Nat. Commun. 6 7475 Google Scholar
[17]	Mahan G, Sofo J 1996 PNAS 93 7436 Google Scholar
[18]	Sootsman J R, Chung D Y, Kanatzidis M G 2009 Angew. Chem. Int. Ed. 48 8616 Google Scholar
[19]	Ishida A, Cao D, Morioka S, Veis M, Inoue Y, Kita T 2008 Appl. Phys. Lett. 92 182105 Google Scholar
[20]	Heremans J P, Jovovic V, Toberer E S, Saramat A, Kurosaki K, Charoenphakdee A, Yamanaka S, Snyder G J 2008 Science 321 554 Google Scholar
[21]	Lee G H, Cooper R C, An S J, Lee S, Van Der Zande A, Petrone N, Hammerberg A G, Lee C, Crawford B, Oliver W 2013 Science 340 1073 Google Scholar
[22]	吴祥冰, 汤雯婷, 徐象繁 2020 物理学报 69 196602 Google Scholar Wu X, Tang W, Xu X 2020 Acta Phys. Sin. 69 196602 Google Scholar
[23]	Choi S J, Kim B K, Lee T H, Kim Y H, Li Z, Pop E, Kim J J, Song J H, Bae M H 2016 Nano Lett. 16 3969 Google Scholar
[24]	Yang F, Wu J, Suwardi A, Zhao Y, Liang B, Jiang J, Xu J, Chi D, Hippalgaonkar K, Lu J 2021 Adv. Mater. 33 2004786 Google Scholar
[25]	Saito Y, Iizuka T, Koretsune T, Arita R, Shimizu S, Iwasa Y 2016 Nano Lett. 16 4819 Google Scholar
[26]	Aiyiti A, Bai X, Wu J, Xu X, Li B 2018 Sci. Bull. 63 452 Google Scholar
[27]	Wang H, Zheng D, Zhang X, Takamatsu H, Hu W 2017 RSC Adv. 7 25298 Google Scholar
[28]	Kayyalha M, Maassen J, Lundstrom M, Shi L, Chen Y P 2016 J. Appl. Phys. 120 134305 Google Scholar
[29]	Klarskov M B, Dam H F, Petersen D H, Hansen T M, Löwenborg A, Booth T, Schmidt M S, Lin R, Nielsen P, Bøggild P 2011 Nanotechnology 22 445702 Google Scholar
[30]	Yoshimoto S, Murata Y, Kubo K, Tomita K, Motoyoshi K, Kimura T, Okino H, Hobara R, Matsuda I, Honda S, Katayama M, Hasegawa S 2007 Nano Lett. 7 956 Google Scholar
[31]	Liu K K, Zhang W, Lee Y H, Lin Y C, Chang M T, Su C Y, Chang C S, Li H, Shi Y, Zhang H 2012 Nano Lett. 12 1538 Google Scholar
[32]	Lee Y H, Zhang X Q, Zhang W, Chang M T, Lin C T, Chang K D, Yu Y C, Wang J T W, Chang C S, Li L J 2012 Adv. Mater. 24 2320 Google Scholar
[33]	Wang H, Yu L, Lee Y H, Fang W, Hsu A, Herring P, Chin M, Dubey M, Li L J, Kong J, Palacios T 2012 International Electron Devices Meeting (IEDM) San Francisco, CA, December 10-13, 2012, pp4.6.1–4.6. 4
[34]	Podzorov V, Gershenson M, Kloc C, Zeis R, Bucher E 2004 Appl. Phys. Lett. 84 3301 Google Scholar
[35]	Hippalgaonkar K, Wang Y, Ye Y, Qiu D Y, Zhu H, Wang Y, Moore J, Louie S G, Zhang X 2017 Phys. Rev. B 95 115407 Google Scholar
[36]	Song H F, Kang F Y 2022 Acta Phys. Chim. Sin 38 2101013
[37]	Zhao Y, Cai Y, Zhang L, Li B, Zhang G, Thong J T 2020 Adv. Funct. Mater. 30 1903929 Google Scholar
[38]	Gu X, Wei Y, Yin X, Li B, Yang R 2018 Rev. Mod. Phys. 90 041002 Google Scholar
[39]	Shi L, Li D, Yu C, Jang W, Kim D, Yao Z, Kim P, Majumdar A 2003 J. Heat Transfer 125 881 Google Scholar
[40]	Kim S, Shin S, Kim T, Du H, Song M, Lee C, Kim K, Cho S, Seo D H, Seo S 2016 Carbon 98 352 Google Scholar
[41]	Pettes M T, Jo I, Yao Z, Shi L 2011 Nano Lett. 11 1195 Google Scholar
[42]	Pizzocchero F, Gammelgaard L, Jessen B S, Caridad J M, Wang L, Hone J, Bøggild P, Booth T J 2016 Nat. Commun. 7 11894 Google Scholar
[43]	Zhao S, Wang H 2020 ES Energy Environ. 9 59
[44]	Wang H, Kurata K, Fukunaga T, Ago H, Takamatsu H, Zhang X, Ikuta T, Takahashi K, Nishiyama T, Takata Y 2016 Sens. Actuators, A 247 24 Google Scholar
[45]	Suh J, Yu K M, Fu D, Liu X, Yang F, Fan J, Smith D J, Zhang Y H, Furdyna J K, Dames C 2015 Adv. Mater. 27 3681 Google Scholar
[46]	Goldsmid H, Sharp J 1999 J. Electron. Mater. 28 869 Google Scholar
[47]	Kim H S, Gibbs Z M, Tang Y, Wang H, Snyder G J 2015 APL Mater. 3 041506 Google Scholar
[48]	Lee C, Wei X, Kysar J W, Hone J 2008 Science 321 385 Google Scholar
[49]	Grigorenko A N, Polini M, Novoselov K 2012 Nat. Photonics 6 749 Google Scholar
[50]	Novoselov K S, Geim A K, Morozov S V, Jiang D, Katsnelson M I, Grigorieva I, Dubonos S, Firsov a 2005 Nature 438 197 Google Scholar
[51]	Novoselov K S, Geim A K, Morozov S V, Jiang D, Zhang Y, Dubonos S V, Grigorieva I V, Firsov A A 2004 Science 306 666 Google Scholar
[52]	Zhang Y, Tan Y W, Stormer H L, Kim P 2005 Nature 438 201 Google Scholar
[53]	Neto A C, Guinea F, Peres N M, Novoselov K S, Geim A K 2009 Rev. Mod. Phys. 81 109 Google Scholar
[54]	Cai W, Moore A L, Zhu Y, Li X, Chen S, Shi L, Ruoff R S 2010 Nano Lett. 10 1645 Google Scholar
[55]	Novoselov K S, Jiang D, Schedin F, Booth T, Khotkevich V, Morozov S, Geim A K 2005 PNAS 102 10451 Google Scholar
[56]	Balandin A A, Ghosh S, Bao W, Calizo I, Teweldebrhan D, Miao F, Lau C N 2008 Nano Lett. 8 902 Google Scholar
[57]	Ghosh D, Calizo I, Teweldebrhan D, Pokatilov E P, Nika D L, Balandin A A, Bao W, Miao F, Lau C N 2008 Appl. Phys. Lett. 92 151911 Google Scholar
[58]	Xu X, Pereira L F, Wang Y, Wu J, Zhang K, Zhao X, Bae S, Tinh Bui C, Xie R, Thong J T 2014 Nat. Commun. 5 3689 Google Scholar
[59]	Lindsay L, Broido D, Mingo N 2011 Phys. Rev. B 83 235428 Google Scholar
[60]	Wei P, Bao W, Pu Y, Lau C N, Shi J 2009 Phys. Rev. Lett. 102 166808 Google Scholar
[61]	Checkelsky J G, Ong N 2009 Phys. Rev. B 80 081413 Google Scholar
[62]	Hwang E, Rossi E, Sarma S D 2009 Phys. Rev. B 80 235415 Google Scholar
[63]	Wang C R, Lu W S, Hao L, Lee W L, Lee T K, Lin F, Cheng I C, Chen J Z 2011 Phys. Rev. Lett. 107 186602 Google Scholar
[64]	Nam S G, Ki D K, Lee H J 2010 Phys. Rev. B 82 245416 Google Scholar
[65]	Wang D, Shi J 2011 Phys. Rev. B 83 113403 Google Scholar
[66]	Seol J H, Moore A L, Shi L, Jo I, Yao Z 2011 J. Heat Transfer 133 022403 Google Scholar
[67]	Jang W, Chen Z, Bao W, Lau C N, Dames C 2010 Nano Lett. 10 3909 Google Scholar
[68]	Yang J, Ziade E, Maragliano C, Crowder R, Wang X, Stefancich M, Chiesa M, Swan A K, Schmidt A J 2014 J. Appl. Phys. 116 023515 Google Scholar
[69]	Ghosh S, Bao W, Nika D L, Subrina S, Pokatilov E P, Lau C N, Balandin A A 2010 Nat. Mater. 9 555 Google Scholar
[70]	Wang J, Zhu L, Chen J, Li B, Thong J T 2013 Adv. Mater. 25 6884 Google Scholar
[71]	Dean C R, Young A F, Meric I, Lee C, Wang L, Sorgenfrei S, Watanabe K, Taniguchi T, Kim P, Shepard K L 2010 Nat. Nanotechnol. 5 722 Google Scholar
[72]	Nomura K, MacDonald A H 2007 Phys. Rev. Lett. 98 076602 Google Scholar
[73]	Chen J H, Jang C, Xiao S, Ishigami M, Fuhrer M S 2008 Nat. Nanotechnol. 3 206 Google Scholar
[74]	Hwang E, Adam S, Sarma S D 2007 Phys. Rev. Lett. 98 186806 Google Scholar
[75]	Ando T 2006 J. Phys. Soc. Jpn. 75 074716 Google Scholar
[76]	Morozov S, Novoselov K, Katsnelson M, Schedin F, Elias D C, Jaszczak J A, Geim A 2008 Phys. Rev. Lett. 100 016602 Google Scholar
[77]	Katsnelson M, Geim A 2008 Philos. Trans. R. Soc. London, Ser. A 366 195
[78]	Ishigami M, Chen J, Cullen W, Fuhrer M, Williams E 2007 Nano Lett. 7 1643 Google Scholar
[79]	Fratini S, Guinea F 2008 Phys. Rev. B 77 195415 Google Scholar
[80]	Duan J, Wang X, Lai X, Li G, Watanabe K, Taniguchi T, Zebarjadi M, Andrei E Y 2016 PNAS 113 14272 Google Scholar
[81]	Zebarjadi M 2015 Appl. Phys. Lett. 106 203506 Google Scholar
[82]	Seol J H, Jo I, Moore A L, Lindsay L, Aitken Z H, Pettes M T, Li X, Yao Z, Huang R, Broido D 2010 Science 328 213 Google Scholar
[83]	Mak K F, Lee C, Hone J, Shan J, Heinz T F 2010 Phys. Rev. Lett. 105 136805 Google Scholar
[84]	Liu X, Zhang G, Pei Q X, Zhang Y W 2013 Appl. Phys. Lett. 103 133113 Google Scholar
[85]	Bertolazzi S, Brivio J, Kis A 2011 ACS Nano 5 9703 Google Scholar
[86]	Wilson J A, Yoffe A 1969 Adv. Phys. 18 193 Google Scholar
[87]	Seh Z W, Yu J H, Li W, Hsu P-C, Wang H, Sun Y, Yao H, Zhang Q, Cui Y 2014 Nat. Commun. 5 5017 Google Scholar
[88]	Yin Z, Li H, Li H, Jiang L, Shi Y, Sun Y, Lu G, Zhang Q, Chen X, Zhang H 2012 ACS Nano 6 74 Google Scholar
[89]	Wang X, Wang P, Wang J, Hu W, Zhou X, Guo N, Huang H, Sun S, Shen H, Lin T 2015 Adv. Mater. 27 6575 Google Scholar
[90]	Zhu H, Wang Y, Xiao J, Liu M, Xiong S, Wong Z J, Ye Z, Ye Y, Yin X, Zhang X 2015 Nat. Nanotechnol. 10 151 Google Scholar
[91]	Wu W, Wang L, Li Y, Zhang F, Lin L, Niu S, Chenet D, Zhang X, Hao Y, Heinz T F 2014 Nature 514 470 Google Scholar
[92]	Cao T, Wang G, Han W, Ye H, Zhu C, Shi J, Niu Q, Tan P, Wang E, Liu B 2012 Nat. Commun. 3 887 Google Scholar
[93]	Yu H, Yao W 2017 Nat. Mater. 16 876 Google Scholar
[94]	Wei X, Wang Y, Shen Y, Xie G, Xiao H, Zhong J, Zhang G 2014 Appl. Phys. Lett. 105 103902 Google Scholar
[95]	Ding Z, Jiang J W, Pei Q X, Zhang Y W 2015 Nanotechnology 26 065703 Google Scholar
[96]	Zhao Y, Zheng M, Wu J, Huang B, Thong J T 2020 Nanotechnology 31 225702 Google Scholar
[97]	Peng B, Ning Z, Zhang H, Shao H, Xu Y, Ni G, Zhu H 2016 J. Phys. Chem. C 120 29324 Google Scholar
[98]	Ding Z, Pei Q X, Jiang J W, Zhang Y W 2015 J. Phys. Chem. C 119 16358 Google Scholar
[99]	Gu X, Li B, Yang R 2016 J. Appl. Phys. 119 085106 Google Scholar
[100]	Xu K, Gabourie A J, Hashemi A, Fan Z, Wei N, Farimani A B, Komsa H-P, Krasheninnikov A V, Pop E, Ala-Nissila T 2019 Phys. Rev. B 99 054303 Google Scholar
[101]	Zhou W, Gong H M, Jin X H, Chen Y, Li H M, Liu S 2022 Front. Phys. 10 842789 Google Scholar
[102]	Yoon Y, Ganapathi K, Salahuddin S 2011 Nano Lett. 11 3768 Google Scholar
[103]	Baugher B W, Churchill H O, Yang Y, Jarillo-Herrero P 2013 Nano Lett. 13 4212 Google Scholar
[104]	Cai X, Wu Z, Han X, Chen Y, Xu S, Lin J, Han T, He P, Feng X, An L 2022 Nat. Commun. 13 1777 Google Scholar
[105]	Ng H, Chi D, Hippalgaonkar K 2017 J. Appl. Phys. 121 204303 Google Scholar
[106]	Yoshida M, Iizuka T, Saito Y, Onga M, Suzuki R, Zhang Y, Iwasa Y, Shimizu S 2016 Nano Lett. 16 2061 Google Scholar
[107]	Zhao Y, Yu P, Zhang G, Sun M, Chi D, Hippalgaonkar K, Thong J T, Wu J 2020 Adv. Funct. Mater. 30 2004896 Google Scholar
[108]	Zeng J, He X, Liang S J, Liu E, Sun Y, Pan C, Wang Y, Cao T, Liu X, Wang C 2018 Nano Lett. 18 7538 Google Scholar
[109]	Lindroth D O, Erhart P 2016 Phys. Rev. B 94 115205 Google Scholar
[110]	Jiang P, Qian X, Gu X, Yang R 2017 Adv. Mater. 29 1701068 Google Scholar
[111]	Wickramaratne D, Zahid F, Lake R K 2014 J. Phys. Chem. 140 124710 Google Scholar
[112]	Imai H, Shimakawa Y, Kubo Y 2001 Phys. Rev. B 64 241104 Google Scholar
[113]	Qin D, Yan P, Ding G, Ge X, Song H, Gao G 2018 Sci. Rep. 8 2764 Google Scholar
[114]	Oyedele A D, Yang S, Liang L, Puretzky A A, Wang K, Zhang J, Yu P, Pudasaini P R, Ghosh A W, Liu Z 2017 J. Am. Chem. Soc. 139 14090 Google Scholar
[115]	Li J, Zhang X, Chen Z, Lin S, Li W, Shen J, Witting I T, Faghaninia A, Chen Y, Jain A 2018 Joule 2 976 Google Scholar
[116]	Tangpakonsab P, Moontragoon P, Hussain T, Kaewmaraya T 2022 ACS Appl. Energy Mater. 5 13081 Google Scholar
[117]	Hung N T, Nugraha A R T, Saito R 2017 Appl. Phys. Lett. 111 092107 Google Scholar
[118]	Hung N T, Nugraha A R T, Yang T, Zhang Z D, Saito R 2019 J. Appl. Phys. 125 082502 Google Scholar
[119]	Wang Q, Han L, Wu L, Zhang T, Li S, Lu P 2019 Nanoscale Res. Lett. 14 287 Google Scholar
[120]	Li L, Yu Y, Ye G J, Ge Q, Ou X, Wu H, Feng D, Chen X H, Zhang Y 2014 Nat. Nanotechnol. 9 372 Google Scholar
[121]	St Laurent B, Dey D, Yu L, Hollen S 2021 ACS Appl. Electron. Mater. 3 4066 Google Scholar
[122]	Hu Z, Li Q, Lei B, Zhou Q, Xiang D, Lyu Z, Hu F, Wang J, Ren Y, Guo R 2017 Angew. Chem. Int. Ed. 56 9131 Google Scholar
[123]	Abate Y, Akinwande D, Gamage S, Wang H, Snure M, Poudel N, Cronin S B 2018 Adv. Mater. 30 1704749 Google Scholar
[124]	Zhang J L, Han C, Hu Z, Wang L, Liu L, Wee A T, Chen W 2018 Adv. Mater. 30 1802207 Google Scholar
[125]	Lee S, Yang F, Suh J, Yang S, Lee Y, Li G, Choe H S, Suslu A, Chen Y, Ko C 2015 Nat. Commun. 6 8573 Google Scholar
[126]	Zhao Y, Zhang G, Nai M H, Ding G, Li D, Liu Y, Hippalgaonkar K, Lim C T, Chi D, Li B 2018 Adv. Mater. 30 1804928 Google Scholar
[127]	Liu H, Choe H S, Chen Y, Suh J, Ko C, Tongay S, Wu J 2017 Appl. Phys. Lett. 111 102101 Google Scholar
[128]	Luo Z, Maassen J, Deng Y, Du Y, Garrelts R P, Lundstrom M S, Ye P D, Xu X 2015 Nat. Commun. 6 8572 Google Scholar
[129]	Qin G, Yan Q B, Qin Z, Yue S Y, Hu M, Su G 2015 Phys. Chem. Chem. Phys. 17 4854 Google Scholar
[130]	Zhao Y, Yang L, Kong L, Nai M H, Liu D, Wu J, Liu Y, Chiam S Y, Chim W K, Lim C T 2017 Adv. Funct. Mater. 27 1702824 Google Scholar
[131]	Flores E, Ares J R, Castellanos-Gomez A, Barawi M, Ferrer I J, Sánchez C 2015 Appl. Phys. Lett. 106 022102 Google Scholar
[132]	Zhang J, Liu H, Cheng L, Wei J, Liang J, Fan D, Jiang P, Sun L, Shi J 2016 J. Mater. Chem. C 4 991 Google Scholar
[133]	Lü H, Lu W, Shao D, Lu H, Sun Y 2016 J. Mater. Chem. C 4 4538 Google Scholar
[134]	Carrete J, Mingo N, Curtarolo S 2014 Appl. Phys. Lett. 105 101907 Google Scholar
[135]	Zhang L C, Qin G, Fang W Z, Cui H J, Zheng Q R, Yan Q B, Su G 2016 Sci. Rep. 6 35705 Google Scholar
[136]	Ding G, Hu Y, Li D, Wang X 2019 Results Phys. 15 102631 Google Scholar
[137]	Guo R, Wang X, Kuang Y, Huang B 2015 Phys. Rev. B 92 115202 Google Scholar
[138]	Zhao L D, Lo S H, Zhang Y, Sun H, Tan G, Uher C, Wolverton C, Dravid V P, Kanatzidis M G 2014 Nature 508 373 Google Scholar
[139]	Zhou C, Lee Y K, Yu Y, Byun S, Luo Z Z, Lee H, Ge B, Lee Y L, Chen X, Lee J Y 2021 Nat. Mater. 20 1378 Google Scholar
[140]	Sun Y, Shuai Z, Wang D 2019 J. Phys. Chem. C 123 12001 Google Scholar
[141]	Zhao T, Sun Y, Shuai Z, Wang D 2017 Chem. Mater. 29 6261 Google Scholar
[142]	Wu M, Zeng X C 2017 Nano Lett. 17 6309 Google Scholar
[143]	Wu J, Liu Y, Tan Z, Tan C, Yin J, Li T, Tu T, Peng H 2017 Adv. Mater. 29 1704060 Google Scholar
[144]	Fu Q, Zhu C, Zhao X, Wang X, Chaturvedi A, Zhu C, Wang X, Zeng Q, Zhou J, Liu F 2019 Adv. Mater. 31 1804945 Google Scholar
[145]	Wu J, Yuan H, Meng M, Chen C, Sun Y, Chen Z, Dang W, Tan C, Liu Y, Yin J 2017 Nat. Nanotechnol. 12 530 Google Scholar
[146]	Yang F, Wang R, Zhao W, Jiang J, Wei X, Zheng T, Yang Y, Wang X, Lu J, Ni Z 2019 Appl. Phys. Lett. 115 193103 Google Scholar
[147]	Leburton J P 1984 J. Appl. Phys. 56 2850 Google Scholar
[148]	Gelmont B, Shur M, Stroscio M 1995 J. Appl. Phys. 77 657 Google Scholar
[149]	Paul S, Bhattacharya D 1989 Phys. Rev. B 39 13521 Google Scholar
[150]	Alkan B, Unal B, Ozdemir A 1995 Semicond. Sci. Technol. 10 1458 Google Scholar
[151]	Zook J D 1964 Phys. Rev. 136 A869 Google Scholar
[152]	Wang F Q, Guo Y, Wang Q, Kawazoe Y, Jena P 2017 Chem. Mater. 29 9300 Google Scholar
[153]	Rau J W, Kannewurf C 1971 Phys. Rev. B 3 2581 Google Scholar
[154]	Li L, Gong P, Sheng D, Wang S, Wang W, Zhu X, Shi X, Wang F, Han W, Yang S 2018 Adv. Mater. 30 1804541 Google Scholar
[155]	Panasci S, Schilirò E, Migliore F, Cannas M, Gelardi F, Roccaforte F, Giannazzo F, Agnello S 2021 Appl. Phys. Lett. 119 093103 Google Scholar
[156]	Velicky M, Donnelly G E, Hendren W R, McFarland S, Scullion D, DeBenedetti W J, Correa G C, Han Y, Wain A J, Hines M A 2018 ACS Nano 12 10463 Google Scholar
[157]	Liu F 2021 Prog. Surf. Sci. 96 100626 Google Scholar
[158]	Zou B, Zhou Y, Zhou Y, Wu Y, He Y, Wang X, Yang J, Zhang L, Chen Y, Zhou S, Guo H, Sun H 2022 Nano Res. 15 8470 Google Scholar
[159]	Wu J, Liu Y, Liu Y, Cai Y, Zhao Y, Ng H K, Watanabe K, Taniguchi T, Zhang G, Qiu C W 2020 PNAS 117 13929 Google Scholar
[160]	Sharma M, Kumar A, Ahluwalia P 2019 Physica E 107 117 Google Scholar
[161]	Zheng Y, Slade T J, Hu L, Tan X Y, Luo Y, Luo Z Z, Xu J, Yan Q, Kanatzidis M G 2021 Chem. Soc. Rev. 50 9022 Google Scholar
[162]	Yan Z, Yoon M, Kumar S 2018 2 D Mater. 5 031008
[163]	Zhao Y, Zheng M, Wu J, Guan X, Suwardi A, Li Y, Lal M, Xie G, Zhang G, Zhang L 2021 Nanoscale 13 11561 Google Scholar
[164]	Aiyiti A, Hu S, Wang C, Xi Q, Cheng Z, Xia M, Ma Y, Wu J, Guo J, Wang Q 2018 Nanoscale 10 2727 Google Scholar
[165]	Chen J H, Li L, Cullen W G, Williams E D, Fuhrer M S 2011 Nat. Phys. 7 535 Google Scholar
[166]	Takahashi H, Okazaki R, Ishiwata S, Taniguchi H, Okutani A, Hagiwara M, Terasaki I 2016 Nat. Commun. 7 12732 Google Scholar
[167]	Zhou J, Liao B, Qiu B, Huberman S, Esfarjani K, Dresselhaus M S, Chen G 2015 PNAS 112 14777 Google Scholar
[168]	Pan Y, Chen S, Wang P, Li Y, Zheng Q 2019 Ceram. Int. 45 19534 Google Scholar
[169]	Lee W, Lim G, Ko S H 2021 Nano Energy 87 106188 Google Scholar
[170]	Wu X, Yang N, Luo T 2015 Appl. Phys. Lett. 107 191907 Google Scholar
[171]	Rosi F 1968 Solid-State Electron. 11 833 Google Scholar
[172]	Guo Y, Dun C, Xu J, Li P, Huang W, Mu J, Hou C, Hewitt C A, Zhang Q, Li Y 2018 ACS Appl. Mater. Interfaces 10 33316 Google Scholar
[173]	Ng H K, Abutaha A, Voiry D, Verzhbitskiy I, Cai Y, Zhang G, Liu Y, Wu J, Chhowalla M, Eda G 2019 ACS Appl. Mater. Interfaces 11 12184 Google Scholar
[174]	An C J, Kang Y H, Lee C, Cho S Y 2018 Adv. Funct. Mater. 28 1800532 Google Scholar
[175]	Xiang D, Han C, Wu J, Zhong S, Liu Y, Lin J, Zhang X A, Ping Hu W, Özyilmaz B, Neto A 2015 Nat. Commun. 6 8949 Google Scholar
[176]	Kong S, Wu T, Yuan M, Huang Z, Meng Q L, Jiang Q, Zhuang W, Jiang P, Bao X 2017 J. Mater. Chem. A 5 2004 Google Scholar
[177]	Perera M M, Lin M W, Chuang H J, Chamlagain B P, Wang C T, Tan X B, Cheng M M C, Tománek D, Zhou Z X 2013 ACS Nano 7 4449 Google Scholar
[178]	Böttner H, Chen G, Venkatasubramanian R 2006 MRS Bull. 31 211 Google Scholar
[179]	Venkatasubramanian R, Siivola E, Colpitts T, O'quinn B 2001 Nature 413 597 Google Scholar
[180]	Harman T, Taylor P, Walsh M, LaForge B 2002 Science 297 2229 Google Scholar
[181]	Harman T, Taylor P, Spears D, Walsh M 2000 J. Electron. Mater. 29 L1 Google Scholar
[182]	Hicks L, Harman T, Sun X, Dresselhaus M 1996 Phys. Rev. B 53 R10493 Google Scholar
[183]	Ding G, He J, Gao G, Yao K 2018 J. Appl. Phys. 124 165101 Google Scholar
[184]	Wan C, Gu X, Dang F, Itoh T, Wang Y, Sasaki H, Kondo M, Koga K, Yabuki K, Snyder G J 2015 Nat. Mater. 14 622 Google Scholar
[185]	Wang S, Yang X, Hou L, Cui X, Zheng X, Zheng J 2022 Nat. Commun. 13 4401 Google Scholar
[186]	Luckyanova M N, Garg J, Esfarjani K, Jandl A, Bulsara M T, Schmidt A J, Minnich A J, Chen S, Dresselhaus M S, Ren Z 2012 Science 338 936 Google Scholar
[187]	Zhang G, Zhang Y W 2015 Mech. Mater. 91 382 Google Scholar
[188]	Peng Z, Chen X, Fan Y, Srolovitz D J, Lei D 2020 Light Sci. Appl. 9 190 Google Scholar
[189]	Yang S, Chen Y, Jiang C 2021 InfoMat 3 397 Google Scholar
[190]	Yan Y, Ding S, Wu X, Zhu J, Feng D, Yang X, Li F 2020 RSC Adv. 10 39455 Google Scholar
[191]	Manzeli S, Allain A, Ghadimi A, Kis A 2015 Nano Lett. 15 5330 Google Scholar
[192]	Meng L, Zhang Y, Hu S, Wang X, Liu C, Guo Y, Wang X, Yan X 2016 Appl. Phys. Lett. 108 263104 Google Scholar
[193]	Castellanos-Gomez A, Roldán R, Cappelluti E, Buscema M, Guinea F, van der Zant H S, Steele G A 2013 Nano Lett. 13 5361 Google Scholar
[194]	Zhu C, Wang G, Liu B, Marie X, Qiao X, Zhang X, Wu X, Fan H, Tan P, Amand T 2013 Phys. Rev. B 88 121301 Google Scholar
[195]	Ng H K, Xiang D, Suwardi A, Hu G, Yang K, Zhao Y, Liu T, Cao Z, Liu H, Li S 2022 Nat. Electron. 5 489 Google Scholar
[196]	Jiang J W, Park H S, Rabczuk T 2013 J. Appl. Phys. 114 064307 Google Scholar
[197]	Conley H J, Wang B, Ziegler J I, Haglund Jr R F, Pantelides S T, Bolotin K I 2013 Nano Lett. 13 3626 Google Scholar
[198]	Desai S B, Seol G, Kang J S, Fang H, Battaglia C, Kapadia R, Ager J W, Guo J, Javey A 2014 Nano Lett. 14 4592 Google Scholar
[199]	Hoat D, Naseri M, Binh N T, Vu T V, Rivas-Silva J, Obeid M M, Cocoletzi G H 2021 Phys. B:Condens. Matter 603 412757 Google Scholar
[200]	Qin G, Yan Q B, Qin Z, Yue S Y, Cui H J, Zheng Q R, Su G 2014 Sci. Rep. 4 6946 Google Scholar
[201]	Bera J, Sahu S 2019 RSC Adv. 9 25216 Google Scholar
[202]	Qin D, Ge X J, Ding G Q, Gao G Y, Lü J T 2017 RSC Adv. 7 47243 Google Scholar

[1]	Zhao Shi-Jie, Ma Hao-Nan, Liu Xia. Research progress in the regulation of physical properties of two-dimensional materials based on thermal scanning probe lithography. Acta Physica Sinica, 2025, 74(3): . doi: 10.7498/aps.74.20241590
[2]	Zhao Jun, Yao Can, Zeng Hui. Theoretical study of adsorption properties and electrical transport performance of toxic gas molecules on novel orthorhombic BN monolayer semiconductor. Acta Physica Sinica, 2024, 73(12): 126802. doi: 10.7498/aps.73.20231621
[3]	Luo Tian-Lin, Ding Ya-Fei, Wei Bao-Jie, Du Jian-Ying, Shen Xiang-Ying, Zhu Gui-Mei, Li Bao-Wen. Phononic thermal conduction and thermal regulation in low-dimensional micro-nano scale systems: Nonequilibrium statistical physics problems from chip heat dissipation. Acta Physica Sinica, 2023, 72(23): 234401. doi: 10.7498/aps.72.20231546
[4]	Duan Xiu-Ming, Yi Zhi-Jun. Theoretical study on regulatory mechanism of dielectric environmental screening effects on binding energy of two-dimensional InX (X = Se, Te) exciton. Acta Physica Sinica, 2023, 72(14): 147102. doi: 10.7498/aps.72.20230528
[5]	Xie Zhong-Xiang, Yu Xia, Jia Pin-Zhen, Chen Xue-Kun, Deng Yuan-Xiang, Zhang Yong, Zhou Wu-Xing. Thermoelectric properties of acene molecular junctions. Acta Physica Sinica, 2023, 72(12): 124401. doi: 10.7498/aps.72.20230354
[6]	Wu Cheng-Wei, Xie Guo-Feng, Zhou Wu-Xing. Frontiers of investigation on thermal transport in all-solid-state lithium-ion battery. Acta Physica Sinica, 2022, 71(2): 026501. doi: 10.7498/aps.71.20211887
[7]	Li Miao-Cong, Tao Qian, Xu Zhu-An. The transport properties of iron-based superconductors. Acta Physica Sinica, 2021, 70(1): 017404. doi: 10.7498/aps.70.20201836
[8]	Wei Jiang-Tao, Yang Liang-Liang, Qin Yuan-Hao, Song Pei-Shuai, Zhang Ming-Liang, Yang Fu-Hua, Wang Xiao-Dong. Methodology of teasting thermoelectric properties of low-dimensional nanomaterials. Acta Physica Sinica, 2021, 70(4): 047301. doi: 10.7498/aps.70.20201175
[9]	Wang Yan, Chen Nan-Di, Yang Chen, Zeng Zhao-Yi, Hu Cui-E, Chen Xiang-Rong. Thermoelectric transport properties of two-dimensional materials XTe₂ (X = Pd, Pt) via first-principles calculations. Acta Physica Sinica, 2021, 70(11): 116301. doi: 10.7498/aps.70.20201939
[10]	Wang Hui, Xu Meng, Zheng Ren-Kui. Research progress and device applications of multifunctional materials based on two-dimensional film/ferroelectrics heterostructures. Acta Physica Sinica, 2020, 69(1): 017301. doi: 10.7498/aps.69.20191486
[11]	Chen Ya-Qi, Xu Hua-Kai, Tang Dong-Sheng, Yu Fang, Lei Le, Ouyang Gang. Electrical transport properties and related mechanism of single SnO₂ nanowire device. Acta Physica Sinica, 2018, 67(24): 246801. doi: 10.7498/aps.67.20181402
[12]	Qi Wei-Hua, Ma Li, Li Zhuang-Zhi, Tang Gui-De, Wu Guang-Heng. Dependences of valence electronic structure on magnetic moment and electrical resistivity of metals. Acta Physica Sinica, 2017, 66(2): 027101. doi: 10.7498/aps.66.027101
[13]	Bai Ji-Yuan, He Ze-Long, Li Li, Han Gui-Hua, Zhang Bin-Lin, Jiang Ping-Hui, Fan Yu-Huan. Electron transport through a two-terminal Aharonov-Bohm interferometer coupled with linear di-quantum dot molecules. Acta Physica Sinica, 2015, 64(20): 207304. doi: 10.7498/aps.64.207304
[14]	Zhang Fei-Peng, Zhang Xin, Lu Qing-Mei, Liu Yan-Qin, Zhang Jiu-Xing. Preparation and electrical transport properties of Fe doped Ca1-xFexMnO3(x=00.12) oxide. Acta Physica Sinica, 2011, 60(8): 087205. doi: 10.7498/aps.60.087205
[15]	Ding Lei, Wang Cong, Chu Li-Hua, Na Yuan-Yuan, Yan Jun. Comprehensive Survey for the Frontier Disciplines Progress in lattice, magnetic and electronic transport properties of antiperovskite Mn3AX. Acta Physica Sinica, 2011, 60(9): 097507. doi: 10.7498/aps.60.097507
[16]	Bao Zhi-Gang, Chen Yuan-Ping, Ouyang Tao, Yang Kai-Ke, Zhong Jian-Xin. Thermal transport in L-shaped graphene nano-junctions. Acta Physica Sinica, 2011, 60(2): 028103. doi: 10.7498/aps.60.028103
[17]	Zhang Fei-Peng, Zhang Xin, Lu Qing-Mei, Zhang Jiu-Xing. Electrical transport properties of Ca3－xAgxCo4O9(x=0—0.05) oxide. Acta Physica Sinica, 2010, 59(6): 4211-4215. doi: 10.7498/aps.59.4211
[18]	Song Chao, Chen Gu-Ran, Xu Jun, Wang Tao, Sun Hong-Cheng, Liu Yu, Li Wei, Chen Kun-Ji. Properties of electric transport in crystallized silicon films under different annealing temperatures. Acta Physica Sinica, 2009, 58(11): 7878-7883. doi: 10.7498/aps.58.7878
[19]	Xiong Chang-Min, Sun Ji-Rong, Wang Deng-Jing, Shen Bao-Gen. Thickness and strain effects on electronic transport and Curie temperature in La_0.67Ca0.33MnO_3 films. Acta Physica Sinica, 2004, 53(11): 3909-3915. doi: 10.7498/aps.53.3909
[20]	XU GANG-YI, WANG TIAN-MIN, HE YU-LIANG, MA ZHI-XUN, ZHENG GUO-ZHEN. THE TRANSPORT MECHANISM IN NANOCRYSTALLINE SILICON FILMS AT LOW TEMPERATURE. Acta Physica Sinica, 2000, 49(9): 1798-1803. doi: 10.7498/aps.49.1798

Catalog

Vol. 72, Issue 5 - 2023-03-05

Metrics

Abstract views: 9934
PDF Downloads: 450
Cited By: 0

姓名
邮箱
手机号码
标题
留言内容
验证码

Search

Article

留言板