n-i-p结构钙钛矿太阳能电池界面钝化的研究进展

李晓果; 张欣; 施则骄; 张海娟; 朱成军; 詹义强

doi:10.7498/aps.68.20190468

摘要

近年来有机-无机杂化钙钛矿材料因其吸收系数高、成本低廉、制备工艺简单等优点吸引了大批科研人员进行研究, 目前在实验室制备的电池能量转换效率已经超过23%. 钙钛矿太阳能电池一般采用溶液法逐层制备, 在此过程中由于退火温度、结晶速率等因素的影响, 钙钛矿内部以及界面会产生大量的缺陷, 这些缺陷会增加载流子复合概率, 降低载流子寿命, 严重影响钙钛矿太阳能电池的性能. 因此研究和理解钙钛矿的缺陷对制备高效钙钛矿太阳能电池至关重要. 本文讨论了在正式结构中, 钙钛矿太阳能电池缺陷的产生以及缺陷对钙钛矿太阳能电池的影响, 分析了不同材料钝化电子传输层/钙钛矿层界面以及钙钛矿层/空穴传输层界面缺陷的机理, 对比了不同钝化材料对钙钛矿太阳能电池光伏性能的影响, 总结了界面钝化材料在钙钛矿太阳能电池中的作用. 最后指出了钙钛矿太阳能电池钝化缺陷的研究趋势和发展方向.

关键词:

Abstract

In recent years, organic-inorganic hybrid perovskite solar cells have aroused the interest of a large number of researchers due to the advantages of large optical absorption coefficient, tunable bandgap and easy fabrication. Recently, the power conversion efficiency of organic-inorganic hybrid perovskite solar cells has been enhanced to more than 23% in laboratory. In solution processed perovskite solar cells, perovskite and charge transport layer are stacked together, due to the different crystallization rates leading to lattice mismatch near the surface region of perovskite film, resulting in a lot of interface defects, especially at the interface between perovskite and charge transport layer. What is more, the photo-induced free carriers must transfer across the interfaces to be collected. But the defects near the interface can trap photogeneration electrons, thus reducing the carrier lifetime and causing the charges to be recombined, which greatly influence the performance and stability of perovskite solar cells. Therefore, reducing and passivating these defects is critical for obtaining the high performance perovskite solar cells. Now, there have been made tremendous efforts devoting to advancing passivation techniques, such as doping and surface modification, for high efficiency perovskite solar cell with improved stability and reduced hysteresis. These approaches also contribute to improving the energy band alignment between carrier transport layers and perovskite absorber improving device performance, or resistance moisture to enhance device stability. In this review we mainly introduce the formation and the effect of defects on perovskite solar cells, analyze the mechanism for passivating the interfacial defects between charge transport layer and perovskite photo absorption layer for different materials, compare the effects of different passivation materials on the photovoltaic performance of perovskite solar cells, and summarize the role of these materials in passivating the defects. Finally we discuss the research trend and development direction of passivation defects in perovskite solar cells.

Keywords:

作者及机构信息

1.
内蒙古大学物理科学与技术学院, 内蒙古自治区半导体光伏技术重点实验室, 呼和浩特　010021

2.
复旦大学工程与应用技术研究院, 上海　200433

3.
复旦大学信息科学与工程学院, 上海　200433

通信作者: 朱成军, cjzhu@imu.edu.cn ; 詹义强, yqzhan@fudan.edu.cn

基金项目: 国家自然科学基金(批准号: 11564027)资助的课题.

Authors and contacts

1.
Key Laboratory of Semiconductor Photovoltaic Technology of Inner Mongolia Autonomous Region, School of Physical Science and Technology, Inner Mongolia University, Hohhot 010021, China

2.
Academy for Engineering and Technology, Fudan University, Shanghai 200433, China

3.
School of Information Science and Technology, Fudan University, Shanghai 200433, China

Corresponding author: Zhu Cheng-Jun, cjzhu@imu.edu.cn ; Zhan Yi-Qiang, yqzhan@fudan.edu.cn

Funds: Project supported by the National Natural Science Foundation of China (Grant No. 11564027).

文章全文 : translate this paragraph

参考文献

[1]	Kojima A, Teshima K, Shirai Y, Miyasaka T 2009 J. Am. Chem. Soc. 131 6050 Google Scholar
[2]	NREL https://www.nrel.gov/pv/assets/pdfs/best-reserch-cell-efficiencies.pdf [2019-03-31]
[3]	Christians J A, Schulz P, Tinkham J S, Schloemer T H, Harvey S P, Tremolet de Villers B J, Sellinger A, Berry J J, Luther J M 2018 Nat. Energy 3 68 Google Scholar
[4]	Wu Y, Xie F, Chen H, Yang X, Su H, Cai M, Zhou Z, Noda T, Han L 2017 Adv. Mater. 29 1701073 Google Scholar
[5]	Lin Y, Bai Y, Fang Y, Chen Z, Yang S, Zheng X, Tang S, Liu Y, Zhao J, Huang J 2018 J. Phys. Chem. Lett. 9 654 Google Scholar
[6]	Ball J M, Petrozza A 2016 Nat. Energy 1 16149 Google Scholar
[7]	Meggiolaro D, Mosconi E, De Angelis F 2017 ACS Energy Lett. 2 2794 Google Scholar
[8]	Kieslich G, Sun S, Cheetham A K 2014 Chem. Sci. 5 4712 Google Scholar
[9]	Travis W, Glover E N K, Bronstein H, Scanlon D O, Palgrave R G 2016 Chem. Sci. 7 4548 Google Scholar
[10]	Cai B, Xing Y, Yang Z, Zhang W H, Qiu J 2013 Energy Environ. Sci. 6 1480 Google Scholar
[11]	Xing G, Mathews N, Lim S S, Yantara N, Liu X, Sabba D, Grätzel M, Mhaisalkar S, Sum T C 2014 Nat. Mater. 13 476 Google Scholar
[12]	Stranks S D, Eperon G E, Grancini G, Menelaou C, Alcocer M J P, Leijtens T, Herz L M, Petrozza A, Snaith H J 2013 Science 342 341 Google Scholar
[13]	Chen B, Bai Y, Yu Z, Li T, Zheng X, Dong Q, Shen L, Boccard M, Gruverman A, Holman Z, Huang J 2016 Adv. Energy Mater. 6 1601128 Google Scholar
[14]	Sahli F, Werner J, Kamino B A, et al. 2018 Nat. Mater. 17 820 Google Scholar
[15]	Bush K A, Palmstrom A F, Yu Z J, et al. 2017 Nat. Energy 2 17009 Google Scholar
[16]	Li B, Ferguson V, Silva S R P, Zhang W 2018 Adv. Mater. Interfaces 5 1800326 Google Scholar
[17]	Liu N, Yam C 2018 Phys. Chem. Chem. Phys. 20 6800 Google Scholar
[18]	Yin W J, Shi T, Yan Y 2014 Appl. Phys. Lett. 104 063903 Google Scholar
[19]	Li W, Liu J, Bai F Q, Zhang H X, Prezhdo O V 2017 ACS Energy Lett. 2 1270 Google Scholar
[20]	Xiao Z, Yuan Y, Wang Q, Shao Y, Bai Y, Deng Y, Dong Q, Hu M, Bi C, Huang J 2016 Materials Science and Engineering R 101 1 Google Scholar
[21]	Sherkar T S, Momblona C, Gil-Escrig L, Ávila J, Sessolo M, Bolink H J, Koster L J A 2017 ACS Energy Lett. 2 1214 Google Scholar
[22]	Queisser H J, Haller E E 1998 Science 281 945 Google Scholar
[23]	Shao Y, Xiao Z, Bi C, Yuan Y, Huang J 2014 Nat. Commun. 5 5784 Google Scholar
[24]	Collins J 2015 ECS J. Solid State Sci. Technol. 5 R3170
[25]	Ran C, Xu J, Gao W, Huang C, Dou S 2018 Chem. Soc. Rev. 47 4581 Google Scholar
[26]	Conwell E, Weisskopf V F 1950 Phys. Rev. 77 388 Google Scholar
[27]	Yuan S, Wang J, Yang K, Wang P, Zhang X, Zhan Y, Zheng L 2018 Nanoscale 10 18909 Google Scholar
[28]	Hou Y, Chen W, Baran D, Stubhan T, Luechinger N A, Hartmeier B, Richter M, Min J, Chen S, Quiroz C O, Li N, Zhang H, Heumueller T, Matt G J, Osvet A, Forberich K, Zhang Z G, Li Y, Winter B, Schweizer P, Spiecker E, Brabec C J 2016 Adv. Mater. 28 5112 Google Scholar
[29]	Tress W, Marinova N, Inganäs O, Nazeeruddin M K, Zakeeruddin S M, Graetzel M 2015 Adv. Energy Mater. 5 1400812 Google Scholar
[30]	Kim H S, Mora-Sero I, Gonzalez-Pedro V, Fabregat-Santiago F, Juarez-Perez E J, Park N G, Bisquert J 2013 Nat. Commun. 4 2242 Google Scholar
[31]	Snaith H J, Abate A, Ball J M, Eperon G E, Leijtens T, Noel N K, Stranks S D, Wang J T, Wojciechowski K, Zhang W 2014 J. Phys. Chem. Lett. 5 1511 Google Scholar
[32]	Yoon H, Kang S M, Lee J K, Choi M 2016 Energy Environ. Sci. 9 2262 Google Scholar
[33]	Unger E L, Hoke E T, Bailie C D, Nguyen W H, Bowring A R, Heumüller T, Christoforo M G, McGehee M D 2014 Energy Environ. Sci. 7 3690 Google Scholar
[34]	Ahn N, Kwak K, Jang M S, Yoon H, Lee B Y, Lee J K, Pikhitsa P V, Byun J, Choi M 2016 Nat. Commun. 7 13422 Google Scholar
[35]	Leijtens T, Eperon G E, Noel N K, Habisreutinger S N, Petrozza A, Snaith H J 2015 Adv. Energy Mater. 5 1500963 Google Scholar
[36]	Aristidou N, Eames C, Sanchez-Molina I, Bu X, Kosco J, Islam M S, Haque S A 2017 Nat. Commun. 8 15218 Google Scholar
[37]	Aristidou N, Sanchez-Molina I, Chotchuangchutchaval T, Brown M, Martinez L, Rath T, Haque S A 2015 Angew. Chem. Int. Edit. 54 8208 Google Scholar
[38]	Leijtens T, Eperon G E, Pathak S, Abate A, Lee M M, Snaith H J 2013 Nat. Commun. 4 2885 Google Scholar
[39]	Du M H 2015 J. Phys. Chem. Lett. 6 1461 Google Scholar
[40]	Jiang H, Jiang G, Xing W, Xiong W, Zhang X, Wang B, Zhang H, Zheng Y 2018 ACS Appl. Mater. Interfaces 10 29954 Google Scholar
[41]	Sidhik S, Panikar S S, Pérez C R, Luke T L, Carriles R, Carrera S C, de la Rosa E 2018 ACS Sustainable Chem. Eng. 6 15391 Google Scholar
[42]	Wang P, Wang J, Zhang X, Wang H, Cui X, Yuan S, Lu H, Tu L, Zhan Y, Zheng L 2018 J. Mater. Chem. A 6 15853 Google Scholar
[43]	Son D Y, Kim S G, Seo J Y, Lee S H, Shin H, Lee D, Park N G 2018 J. Am. Chem. Soc. 140 1358 Google Scholar
[44]	Li W, Zhang W, Van Reenen S, Sutton R J, Fan J, Haghighirad A A, Johnston M B, Wang L, Snaith H J 2016 Energy Environ. Sci. 9 490 Google Scholar
[45]	Wang Z, Kamarudin M A, Huey N C, Yang F, Pandey M, Kapil G, Ma T, Hayase S 2018 ChemSusChem 11 3941 Google Scholar
[46]	Yang G, Wang C, Lei H, Zheng X, Qin P, Xiong L, Zhao X, Yan Y, Fang G 2017 J. Mater. Chem. A 5 1658 Google Scholar
[47]	Abate A, Saliba M, Hollman D J, Stranks S D, Wojciechowski K, Avolio R, Grancini G, Petrozza A, Snaith H J 2014 Nano Lett. 14 3247 Google Scholar
[48]	Hou M, Zhang H, Wang Z, Xia Y, Chen Y, Huang W 2018 ACS Appl. Mater. Interfaces 10 30607 Google Scholar
[49]	You S, Wang H, Bi S, Zhou J, Qin L, Qiu X, Zhao Z, Xu Y, Zhang Y, Shi X, Zhou H, Tang Z 2018 Adv. Mater. 30 1706924 Google Scholar
[50]	Ogomi Y, Morita A, Tsukamoto S, Saitho T, Shen Q, Toyoda T, Yoshino K, Pandey S S, Ma T, Hayase S 2014 J. Phys. Chem. C 118 16651 Google Scholar
[51]	Shih Y C, Lan Y B, Li C S, Hsieh H C, Wang L, Wu C I, Lin K F 2017 Small 13 1604305
[52]	Hou X, Zhou J, Huang S, Ou-Yang W, Pan L, Chen X 2017 Chem. Eng. J 330 947 Google Scholar
[53]	Hou X, Pan L, Huang S, Wei O Y, Chen X 2017 Electrochimica Acta 236 351 Google Scholar
[54]	Noel N K, Abate A, Stranks S D, Parrott E S, Burlakov V M, Goriely A, Snaith H J 2014 ACS Nano 8 9815 Google Scholar
[55]	Jain S M, Qiu Z, Häggman L, Mirmohades M, Johansson M B, Edvinsson T, Boschloo G 2016 Energy Environ. Sci. 9 3770 Google Scholar
[56]	Song D, Wei D, Cui P, Li M, Duan Z, Wang T, Ji J, Li Y, Mbengue J M, Li Y, He Y, Trevor M, Park N-G 2016 J. Mater. Chem. A 4 6091 Google Scholar
[57]	Hayashi H, Lightcap I V, Tsujimoto M, Takano M, Umeyama T, Kamat P V, Imahori H 2011 J. Am. Chem. Soc. 133 7684 Google Scholar
[58]	Gomez De Arco L, Zhang Y, Schlenker C W, Ryu K, Thompson M E, Zhou C 2010 ACS Nano 4 2865 Google Scholar
[59]	Li W, Dong H, Guo X, Li N, Li J, Niu G, Wang L 2014 J. Mater. Chem. A 2 20105 Google Scholar
[60]	Luo H, Lin X, Hou X, Pan L, Huang S, Chen X 2017 Nanomicro Lett. 9 39
[61]	Yang Z, Dou J, Wang M 2018 Solar RRL 2 1800177 Google Scholar
[62]	Tsai H, Nie W, Blancon J C, et al. 2016 Nature 536 312 Google Scholar
[63]	Yao K, Wang X, Xu Y X, Li F 2015 Nano Energy 18 165 Google Scholar
[64]	Lin Y, Bai Y, Fang Y, Wang Q, Deng Y, Huang J 2017 ACS Energy Lett. 2 1571 Google Scholar
[65]	Li C, Lv X, Cao J, Tang Y 2019 Chin. J. Chem. 37 30
[66]	Hou X, Huang S, Ou-Yang W, Pan L, Sun Z, Chen X 2017 ACS Appl. Mater. Interfaces 9 35200 Google Scholar

施引文献

图 1 钙钛矿晶体结构示意图

Fig. 1. Structure diagram of perovskite crystal.

下载: 全尺寸图片幻灯片

图 2 晶体缺陷类型^[16]　(a)完美晶体结构; (b)空位缺陷; (c)间隙缺陷; (d)反位替代缺陷; (e)替位杂质缺陷; (f)间隙杂质缺陷

Fig. 2. Types of crystal defects^[16]: (a) perfect lattice; (b) vacancy defects; (c) interstitial defects; (d) antisite substitution defects; (e) substitutional impurity; (f) interstitial impurity.

下载: 全尺寸图片幻灯片

图 3 (a) KCl钝化缺陷原理图^[42]; (b)磺酸钾钝化缺陷示意图^[45]; (c) APTES钝化缺陷原理图^[46]; (d) DA钝化缺陷原理图^[48]; (e) HS的结构式^[49]; (f) HOCO-R-NH₃⁺在界面处的结构^[50]

Fig. 3. (a) Schematic diagram of KCl passivation defects^[42]; (b) schematic diagram of potassium xanthate passivation defects^[45]; (c) schematic diagram of APTES passivation PSCs interface defects^[46]; (d) schematic diagram of DA passivation PSCs interface defects^[48]; (e) diagram structure of HS^[49]; (f) structure of HOCO-R-NH₃⁺ at interface^[50].

下载: 全尺寸图片幻灯片

图 4 (a)钙钛矿表面电子陷阱的产生^[54]; (b)吡啶缺陷钝化原理图^[54]; (c)碘五氟苯与卤素阴离子之间卤素键作用的示意图^[47]; (d) TPA掺杂钙钛矿器件的I-V曲线, 插图为TPA钝化原理图以及钙钛矿薄膜的SEM图^[66]

Fig. 4. (a) Formation of perovskite surface traps^[54]; (b) schematic diagram of pyridine passivation defects^[54]; (c) schematic of the halogen bond interaction between the IPFB and halogen anion^[47]; (d) I-V curves of TAP-doped perovskite devices, illustrated diagrams is TAP passivation schematic and SEM of perovskite films^[66].

下载: 全尺寸图片幻灯片

图 5 所有钝化方法以及钝化的机理的总结

Fig. 5. Summary of all passivation methods and passivation mechanism.

下载: 全尺寸图片幻灯片

表 1 钝化和不钝化ETL/Perovskite界面钙钛矿太阳能电池的性能

Table 1. Performance of perovskite solar cells with and without passivation on ETL/Perovskite interface.

Interface to be modified	Modifier		V_oc/V	J_sc/mA·cm^–2	FF	PCE/%	文献
SnO₂/MAPbI_xCl_3–x	LiF	W	1.15	21.62	0.73	18.33	[27]
SnO₂/MAPbI_xCl_3–x	LiF	W/O	1.08	20.40	0.71	15.60	[27]
SnO₂/MAPbI_xCl_3–x	KCl	W	1.12	21.82	0.79	19.44	[42]
SnO₂/MAPbI_xCl_3–x	KCl	W/O	1.08	21.59	0.76	18.12	[42]
TiO₂/MAPbI_xCl_3–x	CsBr	W	1.06	20.70	0.75	16.30	[44]
TiO₂/MAPbI_xCl_3–x	CsBr	W/O	0.99	18.70	0.69	13.10	[44]
SnO₂/MAPbI₃	Xanthate	W	1.06	22.61	0.70	18.41	[45]
SnO₂/MAPbI₃	Xanthate	W/O	1.03	21.74	0.73	16.56	[45]
SnO₂/MAPbI₃	APTES SAM	W	1.06	20.84	0.66	14.69	[46]
SnO₂/MAPbI₃	APTES SAM	W/O	1.16	21.23	0.69	17.03	[46]
SnO₂/MAPbI₃	DA SAM	W	1.05	21.80	0.73	16.87	[48]
SnO₂/MAPbI₃	DA SAM	W/O	1.04	19.96	0.67	14.05	[48]
TiO₂/MAPbI₃	Li-TiO₂	W	1.03	23.91	0.74	18.25	[52]
TiO₂/MAPbI₃	Li-TiO₂	W/O	1.01	22.46	0.69	15.64	[52]
TiO₂/MAPbI₃	HS	W	1.11	23.34	0.77	20.10	[49]
TiO₂/MAPbI₃	HS	W/O	1.09	21.29	0.74	17.20	[49]
TiO2/MAPbI₃	GABAH⁺I^–	W	1.00	19.20	0.62	12.00	[50]
TiO2/MAPbI₃	GABAH⁺I^–	W/O	—	—	—	8.00	[50]
TiO2/MAPbI₃	LA	W	0.99	22.40	0.64	14.22	[51]
TiO2/MAPbI₃	LA	W/O	0.95	17.08	0.66	10.76	[51]
TiO2/MAPbI₃	GnPs	W	1.00	23.67	0.69	15.14	[41]
TiO2/MAPbI₃	GnPs	W/O	0.97	22.33	0.80	19.23	[41]

下载: 导出CSV

表 2 钝化和不钝化Perovskite/HTL钙钛矿太阳能电池的性能

Table 2. Performance of perovskite solar cells with and without passivation on Perovskite/HTL interface.

Interface to be modified	Modifier		V_oc/V	J_sc/mA·cm^–2	FF	PCE/%	文献
MAPbI_xCl_3–x/Spiro-OMeTAD	IPFB	W	1.06	23.38	0.67	15.70	[47]
MAPbI_xCl_3–x/Spiro-OMeTAD	IPFB	W/O	1.02	23.80	0.57	13.00	[47]
MAPbI₃/Spiro-OMeTAD	GO	W	1.03	20.00	0.72	14.50	[59]
MAPbI₃/Spiro-OMeTAD	GO	W/O	0.93	18.50	0.64	10.00	[59]
MAPbI_xCl_3–x/Spiro-OMeTAD	Thiophene	W	0.95	20.70	0.68	13.10	[54]
MAPbI_xCl_3–x/Spiro-OMeTAD	Thiophene	W/O	1.02	21.30	0.68	15.30	[54]
MAPbI_xCl_3–x/Spiro-OMeTAD	Pyridine	W	0.95	20.70	0.68	13.10	[54]
MAPbI_xCl_3–x/Spiro-OMeTAD	Pyridine	W/O	1.05	24.10	0.72	16.50	[54]
MAPbI₃/Spiro-OMeTAD	V-pyridine	W	1.15	22.00	0.73	9.50	[55]
MAPbI₃/Spiro-OMeTAD	V-pyridine	W/O	0.80	19.20	0.63	18.50	[55]
MAPbI₃/Spiro-OMeTAD	F4TCNQ	W	1.04	19.40	0.70	15.30	[56]
MAPbI₃/Spiro-OMeTAD	F4TCNQ	W/O	1.06	20.30	0.75	18.10	[56]
MAPbI₃/Spiro-OMeTAD	ZnPc	W	1.09	23.23	0.77	19.56	[65]
MAPbI₃/Spiro-OMeTAD	ZnPc	W/O	1.08	22.93	0.76	18.83	[65]
MAPbI₃/Spiro-OMeTAD	TAP	W	1.05	23.49	0.75	18.51	[66]
MAPbI₃/Spiro-OMeTAD	TAP	W/O	0.99	22.09	0.71	15.53	[66]

下载: 导出CSV

[1]	Kojima A, Teshima K, Shirai Y, Miyasaka T 2009 J. Am. Chem. Soc. 131 6050 Google Scholar
[2]	NREL https://www.nrel.gov/pv/assets/pdfs/best-reserch-cell-efficiencies.pdf [2019-03-31]
[3]	Christians J A, Schulz P, Tinkham J S, Schloemer T H, Harvey S P, Tremolet de Villers B J, Sellinger A, Berry J J, Luther J M 2018 Nat. Energy 3 68 Google Scholar
[4]	Wu Y, Xie F, Chen H, Yang X, Su H, Cai M, Zhou Z, Noda T, Han L 2017 Adv. Mater. 29 1701073 Google Scholar
[5]	Lin Y, Bai Y, Fang Y, Chen Z, Yang S, Zheng X, Tang S, Liu Y, Zhao J, Huang J 2018 J. Phys. Chem. Lett. 9 654 Google Scholar
[6]	Ball J M, Petrozza A 2016 Nat. Energy 1 16149 Google Scholar
[7]	Meggiolaro D, Mosconi E, De Angelis F 2017 ACS Energy Lett. 2 2794 Google Scholar
[8]	Kieslich G, Sun S, Cheetham A K 2014 Chem. Sci. 5 4712 Google Scholar
[9]	Travis W, Glover E N K, Bronstein H, Scanlon D O, Palgrave R G 2016 Chem. Sci. 7 4548 Google Scholar
[10]	Cai B, Xing Y, Yang Z, Zhang W H, Qiu J 2013 Energy Environ. Sci. 6 1480 Google Scholar
[11]	Xing G, Mathews N, Lim S S, Yantara N, Liu X, Sabba D, Grätzel M, Mhaisalkar S, Sum T C 2014 Nat. Mater. 13 476 Google Scholar
[12]	Stranks S D, Eperon G E, Grancini G, Menelaou C, Alcocer M J P, Leijtens T, Herz L M, Petrozza A, Snaith H J 2013 Science 342 341 Google Scholar
[13]	Chen B, Bai Y, Yu Z, Li T, Zheng X, Dong Q, Shen L, Boccard M, Gruverman A, Holman Z, Huang J 2016 Adv. Energy Mater. 6 1601128 Google Scholar
[14]	Sahli F, Werner J, Kamino B A, et al. 2018 Nat. Mater. 17 820 Google Scholar
[15]	Bush K A, Palmstrom A F, Yu Z J, et al. 2017 Nat. Energy 2 17009 Google Scholar
[16]	Li B, Ferguson V, Silva S R P, Zhang W 2018 Adv. Mater. Interfaces 5 1800326 Google Scholar
[17]	Liu N, Yam C 2018 Phys. Chem. Chem. Phys. 20 6800 Google Scholar
[18]	Yin W J, Shi T, Yan Y 2014 Appl. Phys. Lett. 104 063903 Google Scholar
[19]	Li W, Liu J, Bai F Q, Zhang H X, Prezhdo O V 2017 ACS Energy Lett. 2 1270 Google Scholar
[20]	Xiao Z, Yuan Y, Wang Q, Shao Y, Bai Y, Deng Y, Dong Q, Hu M, Bi C, Huang J 2016 Materials Science and Engineering R 101 1 Google Scholar
[21]	Sherkar T S, Momblona C, Gil-Escrig L, Ávila J, Sessolo M, Bolink H J, Koster L J A 2017 ACS Energy Lett. 2 1214 Google Scholar
[22]	Queisser H J, Haller E E 1998 Science 281 945 Google Scholar
[23]	Shao Y, Xiao Z, Bi C, Yuan Y, Huang J 2014 Nat. Commun. 5 5784 Google Scholar
[24]	Collins J 2015 ECS J. Solid State Sci. Technol. 5 R3170
[25]	Ran C, Xu J, Gao W, Huang C, Dou S 2018 Chem. Soc. Rev. 47 4581 Google Scholar
[26]	Conwell E, Weisskopf V F 1950 Phys. Rev. 77 388 Google Scholar
[27]	Yuan S, Wang J, Yang K, Wang P, Zhang X, Zhan Y, Zheng L 2018 Nanoscale 10 18909 Google Scholar
[28]	Hou Y, Chen W, Baran D, Stubhan T, Luechinger N A, Hartmeier B, Richter M, Min J, Chen S, Quiroz C O, Li N, Zhang H, Heumueller T, Matt G J, Osvet A, Forberich K, Zhang Z G, Li Y, Winter B, Schweizer P, Spiecker E, Brabec C J 2016 Adv. Mater. 28 5112 Google Scholar
[29]	Tress W, Marinova N, Inganäs O, Nazeeruddin M K, Zakeeruddin S M, Graetzel M 2015 Adv. Energy Mater. 5 1400812 Google Scholar
[30]	Kim H S, Mora-Sero I, Gonzalez-Pedro V, Fabregat-Santiago F, Juarez-Perez E J, Park N G, Bisquert J 2013 Nat. Commun. 4 2242 Google Scholar
[31]	Snaith H J, Abate A, Ball J M, Eperon G E, Leijtens T, Noel N K, Stranks S D, Wang J T, Wojciechowski K, Zhang W 2014 J. Phys. Chem. Lett. 5 1511 Google Scholar
[32]	Yoon H, Kang S M, Lee J K, Choi M 2016 Energy Environ. Sci. 9 2262 Google Scholar
[33]	Unger E L, Hoke E T, Bailie C D, Nguyen W H, Bowring A R, Heumüller T, Christoforo M G, McGehee M D 2014 Energy Environ. Sci. 7 3690 Google Scholar
[34]	Ahn N, Kwak K, Jang M S, Yoon H, Lee B Y, Lee J K, Pikhitsa P V, Byun J, Choi M 2016 Nat. Commun. 7 13422 Google Scholar
[35]	Leijtens T, Eperon G E, Noel N K, Habisreutinger S N, Petrozza A, Snaith H J 2015 Adv. Energy Mater. 5 1500963 Google Scholar
[36]	Aristidou N, Eames C, Sanchez-Molina I, Bu X, Kosco J, Islam M S, Haque S A 2017 Nat. Commun. 8 15218 Google Scholar
[37]	Aristidou N, Sanchez-Molina I, Chotchuangchutchaval T, Brown M, Martinez L, Rath T, Haque S A 2015 Angew. Chem. Int. Edit. 54 8208 Google Scholar
[38]	Leijtens T, Eperon G E, Pathak S, Abate A, Lee M M, Snaith H J 2013 Nat. Commun. 4 2885 Google Scholar
[39]	Du M H 2015 J. Phys. Chem. Lett. 6 1461 Google Scholar
[40]	Jiang H, Jiang G, Xing W, Xiong W, Zhang X, Wang B, Zhang H, Zheng Y 2018 ACS Appl. Mater. Interfaces 10 29954 Google Scholar
[41]	Sidhik S, Panikar S S, Pérez C R, Luke T L, Carriles R, Carrera S C, de la Rosa E 2018 ACS Sustainable Chem. Eng. 6 15391 Google Scholar
[42]	Wang P, Wang J, Zhang X, Wang H, Cui X, Yuan S, Lu H, Tu L, Zhan Y, Zheng L 2018 J. Mater. Chem. A 6 15853 Google Scholar
[43]	Son D Y, Kim S G, Seo J Y, Lee S H, Shin H, Lee D, Park N G 2018 J. Am. Chem. Soc. 140 1358 Google Scholar
[44]	Li W, Zhang W, Van Reenen S, Sutton R J, Fan J, Haghighirad A A, Johnston M B, Wang L, Snaith H J 2016 Energy Environ. Sci. 9 490 Google Scholar
[45]	Wang Z, Kamarudin M A, Huey N C, Yang F, Pandey M, Kapil G, Ma T, Hayase S 2018 ChemSusChem 11 3941 Google Scholar
[46]	Yang G, Wang C, Lei H, Zheng X, Qin P, Xiong L, Zhao X, Yan Y, Fang G 2017 J. Mater. Chem. A 5 1658 Google Scholar
[47]	Abate A, Saliba M, Hollman D J, Stranks S D, Wojciechowski K, Avolio R, Grancini G, Petrozza A, Snaith H J 2014 Nano Lett. 14 3247 Google Scholar
[48]	Hou M, Zhang H, Wang Z, Xia Y, Chen Y, Huang W 2018 ACS Appl. Mater. Interfaces 10 30607 Google Scholar
[49]	You S, Wang H, Bi S, Zhou J, Qin L, Qiu X, Zhao Z, Xu Y, Zhang Y, Shi X, Zhou H, Tang Z 2018 Adv. Mater. 30 1706924 Google Scholar
[50]	Ogomi Y, Morita A, Tsukamoto S, Saitho T, Shen Q, Toyoda T, Yoshino K, Pandey S S, Ma T, Hayase S 2014 J. Phys. Chem. C 118 16651 Google Scholar
[51]	Shih Y C, Lan Y B, Li C S, Hsieh H C, Wang L, Wu C I, Lin K F 2017 Small 13 1604305
[52]	Hou X, Zhou J, Huang S, Ou-Yang W, Pan L, Chen X 2017 Chem. Eng. J 330 947 Google Scholar
[53]	Hou X, Pan L, Huang S, Wei O Y, Chen X 2017 Electrochimica Acta 236 351 Google Scholar
[54]	Noel N K, Abate A, Stranks S D, Parrott E S, Burlakov V M, Goriely A, Snaith H J 2014 ACS Nano 8 9815 Google Scholar
[55]	Jain S M, Qiu Z, Häggman L, Mirmohades M, Johansson M B, Edvinsson T, Boschloo G 2016 Energy Environ. Sci. 9 3770 Google Scholar
[56]	Song D, Wei D, Cui P, Li M, Duan Z, Wang T, Ji J, Li Y, Mbengue J M, Li Y, He Y, Trevor M, Park N-G 2016 J. Mater. Chem. A 4 6091 Google Scholar
[57]	Hayashi H, Lightcap I V, Tsujimoto M, Takano M, Umeyama T, Kamat P V, Imahori H 2011 J. Am. Chem. Soc. 133 7684 Google Scholar
[58]	Gomez De Arco L, Zhang Y, Schlenker C W, Ryu K, Thompson M E, Zhou C 2010 ACS Nano 4 2865 Google Scholar
[59]	Li W, Dong H, Guo X, Li N, Li J, Niu G, Wang L 2014 J. Mater. Chem. A 2 20105 Google Scholar
[60]	Luo H, Lin X, Hou X, Pan L, Huang S, Chen X 2017 Nanomicro Lett. 9 39
[61]	Yang Z, Dou J, Wang M 2018 Solar RRL 2 1800177 Google Scholar
[62]	Tsai H, Nie W, Blancon J C, et al. 2016 Nature 536 312 Google Scholar
[63]	Yao K, Wang X, Xu Y X, Li F 2015 Nano Energy 18 165 Google Scholar
[64]	Lin Y, Bai Y, Fang Y, Wang Q, Deng Y, Huang J 2017 ACS Energy Lett. 2 1571 Google Scholar
[65]	Li C, Lv X, Cao J, Tang Y 2019 Chin. J. Chem. 37 30
[66]	Hou X, Huang S, Ou-Yang W, Pan L, Sun Z, Chen X 2017 ACS Appl. Mater. Interfaces 9 35200 Google Scholar

[1]	罗攀, 李响, 孙学银, 谭骁洪, 罗俊, 甄良. 新型空间太阳能电池用的钙钛矿薄膜与器件的电子辐照效应. 物理学报, 2024, 73(3): 036102. doi: 10.7498/aps.73.20231568
[2]	隽珽, 邢家赫, 曾凡聪, 郑鑫, 徐琳. 基于SnO₂:DPEPO混合电子传输层的钙钛矿太阳能电池性能研究. 物理学报, 2024, 73(19): 198401. doi: 10.7498/aps.73.20240827
[3]	王静, 高姗, 段香梅, 尹万健. 钙钛矿太阳能电池材料缺陷对器件性能与稳定性的影响. 物理学报, 2024, 73(6): 063101. doi: 10.7498/aps.73.20231631
[4]	王辉, 郑德旭, 姜箫, 曹越先, 杜敏永, 王开, 刘生忠, 张春福. 基于协同钝化策略制备高性能柔性钙钛矿太阳能电池. 物理学报, 2024, 73(7): 078401. doi: 10.7498/aps.73.20231846
[5]	张晓春, 王立坤, 商文丽, 万政慧, 岳鑫, 杨华翼, 李婷, 王辉. 基于双修饰策略制备高性能反式钙钛矿太阳能电池. 物理学报, 2024, 73(24): 1-11. doi: 10.7498/aps.73.20241238
[6]	羊美丽, 邹丽, 程佳杰, 王佳明, 江钰帆, 郝会颖, 邢杰, 刘昊, 樊振军, 董敬敬. 聚偏氟乙烯添加剂提高CsPbBr₃钙钛矿太阳能电池性能. 物理学报, 2023, 72(16): 168101. doi: 10.7498/aps.72.20230636
[7]	李培, 徐洁, 贺朝会, 刘佳欣. 钙钛矿太阳能电池辐照实验研究. 物理学报, 2023, 72(12): 126101. doi: 10.7498/aps.72.20230230
[8]	朱咏琪, 刘钰雪, 石洋, 吴聪聪. 甲脒碘化铅单晶基钙钛矿太阳能电池的研究. 物理学报, 2023, 72(1): 018801. doi: 10.7498/aps.72.20221461
[9]	周玚, 任信钢, 闫业强, 任昊, 杜红梅, 蔡雪原, 黄志祥. 基于双层电子传输层钙钛矿太阳能电池的物理机制. 物理学报, 2022, 71(20): 208802. doi: 10.7498/aps.71.20220725
[10]	刘钰雪, 明逸东, 吴聪聪. 氯掺杂甲胺基钙钛矿电池的性能及其改进. 物理学报, 2022, 71(20): 207303. doi: 10.7498/aps.71.20220966
[11]	孙盟杰, 何志群, 郑毅帆, 邵宇川. EDTA/SnO₂双层复合电子传输层在钙钛矿电池中的应用. 物理学报, 2022, 71(13): 137201. doi: 10.7498/aps.71.20220074
[12]	王成麟, 张左林, 朱云飞, 赵雪帆, 宋宏伟, 陈聪. 钙钛矿太阳能电池中缺陷及其钝化策略研究进展. 物理学报, 2022, 71(16): 166801. doi: 10.7498/aps.71.20220359
[13]	高九林, 连亚军, 杨晔, 李国庆, 杨晓晖. 采用硫氰酸铵添加剂的高效天蓝色钙钛矿发光二极管. 物理学报, 2021, 70(19): 198502. doi: 10.7498/aps.70.20211046
[14]	王佩佩, 张晨曦, 胡李纳, 李仕奇, 任炜桦, 郝玉英. 氧化镍在倒置平面钙钛矿太阳能电池中的应用进展. 物理学报, 2021, 70(11): 118801. doi: 10.7498/aps.70.20201896
[15]	姬超, 梁春军, 由芳田, 何志群. 界面修饰对有机-无机杂化钙钛矿太阳能电池性能的影响. 物理学报, 2021, 70(2): 028402. doi: 10.7498/aps.70.20201222
[16]	王言博, 崔丹钰, 张才益, 韩礼元, 杨旭东. 钙钛矿太阳能电池研究进展: 空间电势与光电转换机制. 物理学报, 2019, 68(15): 158401. doi: 10.7498/aps.68.20190569
[17]	柴磊, 钟敏. 钙钛矿太阳能电池近期进展. 物理学报, 2016, 65(23): 237902. doi: 10.7498/aps.65.237902
[18]	石将建, 卫会云, 朱立峰, 许信, 徐余颛, 吕松涛, 吴会觉, 罗艳红, 李冬梅, 孟庆波. 钙钛矿太阳能电池中S形伏安特性研究. 物理学报, 2015, 64(3): 038402. doi: 10.7498/aps.64.038402
[19]	丁雄傑, 倪露, 马圣博, 马英壮, 肖立新, 陈志坚. 钙钛矿太阳能电池中电子传输材料的研究进展. 物理学报, 2015, 64(3): 038802. doi: 10.7498/aps.64.038802
[20]	黄林泉, 周玲玉, 于为, 杨栋, 张坚, 李灿. 石墨烯衍生物作为有机太阳能电池界面材料的研究进展. 物理学报, 2015, 64(3): 038103. doi: 10.7498/aps.64.038103

计量

文章访问数: 23236
PDF下载量: 687
被引次数: 0

姓名
邮箱
手机号码
标题
留言内容
验证码

搜索

留言板