Recent advances in photo-stability of lead halide perovskites

Lou Hao-Ran Ye Zhi-Zhen He Hai-Ping

Citation:

Recent advances in photo-stability of lead halide perovskites

Lou Hao-Ran, Ye Zhi-Zhen, He Hai-Ping
PDF
HTML
Get Citation
  • Lead halide perovskites, which can be grown by solution process, are very suitable for various optoelectronic applications, such as in solar cells, light-emitting diodes, lasers and photo-detectors, due to their outstanding electrical and optical properties. However, lead halide perovskites are unstable under continuous light illumination, which severely degrades the performance and lifetime of optoelectronic devices based on them. Therefore, the photo-stability of perovskites and the mechanisms have received more and more attention. In this article we review the main phenomena in perovskites, induced by continuous light illumination, namely photo curing, photo dissociation, photo-induced phase separation, and photo-induced phase transition. The proposed mechanisms for the instability from the perspectives of defect states, ion migration, thermodynamics and chemical bonds, respectively, are also introduced. Finally, the complexity presented in the studying of photo-stability, and the issues should be addressed in the future are also briefly discussed.
      Corresponding author: He Hai-Ping, hphe@zju.edu.cn
    • Funds: Project supported by the National Natural Science Foundation of China (Grant No. 51772271).
    [1]

    Sutherland B R, Sargent E H 2016 Nat. Photon. 10 295Google Scholar

    [2]

    Heo J H, Im S H, Noh J H, Mandal T N, Lim C S, Chang J A, Lee Y H, Kim H J, Sarkar A, Nazeeruddin M K, Grätzel M, Seok S I 2013 Nat. Photon. 7 486Google Scholar

    [3]

    Giorgi G, Fujisawa J I, Segawa H, Yamashita K 2013 J. Phys. Chem. Lett. 4 4213Google Scholar

    [4]

    Bisquert J 2013 J. Phys. Chem. Lett. 4 1051Google Scholar

    [5]

    Etgar L, Gao P, Xue Z, Peng Q, Chandiran A K, Liu B, Nazeeruddin M K, Grätzel M 2012 J. Am. Chem. Soc. 134 17396Google Scholar

    [6]

    Abu Laban W, Etgar L 2013 Energy Environ. Sci. 6 3249Google Scholar

    [7]

    Xing G, Mathews N, Sun S, Lim S S, Lam Y M, Grätzel M, Mhaisalkar S, Sum T C 2013 Science 342 344Google Scholar

    [8]

    Stranks S D, Eperon G E, Grancini G, Menelaou C, Alcocer M J P, Leijtens T, Herz L M, Petrozza A, Snaith H J 2013 Science 342 341Google Scholar

    [9]

    Yamada Y, Nakamura T, Endo M, Wakamiya A, Kanemitsu Y 2014 J. Am. Chem. Soc. 136 11610Google Scholar

    [10]

    Stranks S D, Burlakov V M, Leijtens T, Ball J M, Goriely A, Snaith H J 2014 Phys. Rev. Appl. 2 034007Google Scholar

    [11]

    Stoumpos C C, Malliakas C D, Kanatzidis M G 2013 Inorg. Chem. 52 9019Google Scholar

    [12]

    Yantara N, Bhaumik S, Yan F, Sabba D, Dewi H A, Mathews N, Boix P P, Demir H V, Mhaisalkar S 2015 J. Phys. Chem. Lett. 6 4360Google Scholar

    [13]

    Adachi M M, Fan F, Sellan D P, Hoogland S, Voznyy O, Houtepen A J, Parrish K D, Kanjanaboos P, Malen J A, Sargent E H 2015 Nat. Commun. 6 8694Google Scholar

    [14]

    Kojima A, Teshima K, Shirai Y, Miyasaka T 2009 J. Am. Chem. Soc. 131 6050Google Scholar

    [15]

    Kim H S, Lee C R, Im J H, Lee K B, Moehl T, Marchioro A, Moon S J, Humphry-Baker R, Yum J H, Moser J E, Grätzel M, Park N G 2012 Sci. Rep. 2 591Google Scholar

    [16]

    Yang W S, Park B W, Jung E H, Jeon N J, Kim Y C, Lee D U, Shin S S, Seo J, Kim E K, Noh J H, Seok S I 2017 Science 356 1376Google Scholar

    [17]

    Yao K, Li F, He Q Q, Wang X F, Jiang Y H, Huang H T, Jen A K Y 2017 Nano Energy 40 155Google Scholar

    [18]

    Chen R, Hou D, Lu C, Zhang J, Liu P, Tian H, Zeng Z, Xiong Q, Hu Z, Zhu Y, Han L 2018 Sustain. Energ. Fuels 2 1093Google Scholar

    [19]

    Jaramillo-Quintero O A, Sanchez R S, Rincon M, Mora-Sero I 2015 J. Phys. Chem. Lett. 6 1883Google Scholar

    [20]

    Kim Y H, Cho H, Heo J H, Kim T S, Myoung N, Lee C L, Im S H, Lee T W 2015 Adv. Mater. 27 1248Google Scholar

    [21]

    Li J Q, Bade S G R, Shan X, Yu Z B 2015 Adv. Mater. 27 5196Google Scholar

    [22]

    Tang B, Dong H, Sun L, Zheng W, Wang Q, Sun F, Jiang X, Pan A, Zhang L 2017 ACS Nano 11 10681Google Scholar

    [23]

    Yakunin S, Protesescu L, Krieg F, Bodnarchuk M I, Nedelcu G, Humer M, de Luca G, Fiebig M, Heiss W, Kovalenko M V 2015 Nat. Commun. 6 8056Google Scholar

    [24]

    Sutherland B R, Hoogland S, Adachi M M, Wong C T O, Sargent E H 2014 ACS Nano 8 10947Google Scholar

    [25]

    Fu Y, Zhu H, Stoumpos C C, Ding Q, Wang J, Kanatzidis M G, Zhu X, Jin S 2016 ACS Nano 10 7963Google Scholar

    [26]

    Domanski K, Tress W, Moehl T, Saliba M, Nazeeruddin M K, Gratzel M 2015 Adv. Funct. Mater. 25 6936Google Scholar

    [27]

    Sutherland B R, Johnston A K, Ip A H, Xu J, Adinolfi V, Kanjanaboos P, Sargent E H 2015 ACS Photon. 2 1117Google Scholar

    [28]

    Lian Z, Yan Q, Lv Q, Wang Y, Liu L, Zhang L, Pan S, Li Q, Wang L, Sun J L 2015 Sci. Rep. 5 16563Google Scholar

    [29]

    Adinolfi V, Ouellette O, Saidaminov M I, Walters G, Abdelhady A L, Bakr O M, Sargent E H 2016 Adv. Mater. 28 7264Google Scholar

    [30]

    Zhao D, Wang C, Song Z, Yu Y, Chen C, Zhao X, Zhu K, Yan Y 2018 ACS Energy Lett. 3 305Google Scholar

    [31]

    Lin K, Xing J, Quan L N, de Arquer F P G, Gong X, Lu J, Xie L, Zhao W, Zhang D, Yan C, Li W, Liu X, Lu Y, Kirman J, Sargent E H, Xiong Q, Wei Z 2018 Nature 562 245Google Scholar

    [32]

    Chiba T, Hayashi Y, Ebe H, Hoshi K, Sato J, Sato S, Pu Y J, Ohisa S, Kido J 2018 Nat. Photon. 12 681Google Scholar

    [33]

    Cao Y, Wang N, Tian H, Guo J, Wei Y, Chen H, Miao Y, Zou W, Pan K, He Y, Cao H, Ke Y, Xu M, Wang Y, Yang M, Du K, Fu Z, Kong D, Dai D, Jin Y, Li G, Li H, Peng Q, Wang J, Huang W 2018 Nature 562 249Google Scholar

    [34]

    Berhe T A, Su W N, Chen C H, Pan C J, Cheng J H, Chen H M, Tsai M C, Chen L Y, Dubale A A, Hwang B J 2016 Energy Environ. Sci. 9 323Google Scholar

    [35]

    Abdi-Jalebi M, Andaji-Garmaroudi Z, Cacovich S, Stavrakas C, Philippe B, Richter J M, Alsari M, Booker E P, Hutter E M, Pearson A J, Lilliu S, Savenije T J, Rensmo H, Divitini G, Ducati C, Friend R H, Stranks S D 2018 Nature 555 497Google Scholar

    [36]

    Frost J M, Butler K T, Brivio F, Hendon C H, van Schilfgaarde M, Walsh A 2014 Nano Lett. 14 2584Google Scholar

    [37]

    Yang J, Siempelkamp B D, Liu D, Kelly T L 2015 ACS Nano 9 1955Google Scholar

    [38]

    Christians J A, Miranda Herrera P A, Kamat P V 2015 J. Am. Chem. Soc. 137 1530Google Scholar

    [39]

    Li Y, Xu X, Wang C, Wang C, Xie F, Yang J, Gao Y 2015 J. Phys. Chem. C 119 23996Google Scholar

    [40]

    Song Z N, Abate A, Watthage S C, Liyanage G K, Phillips A B, Steiner U, Graetzel M, Heben M J 2016 Adv. Energy Mater. 6 1600846Google Scholar

    [41]

    Aristidou N, Sanchez-Molina I, Chotchuangchutchaval T, Brown M, Martinez L, Rath T, Haque S A 2015 Angew. Chem. Int. Ed. 54 8208Google Scholar

    [42]

    Bryant D, Aristidou N, Pont S, Sanchez-Molina I, Chotchunangatchaval T, Wheeler S, Durrant J R, Haque S A 2016 Energy Environ. Sci. 9 1655Google Scholar

    [43]

    Alberti A, Deretzis I, Pellegrino G, Bongiorno C, Smecca E, Mannino G, Giannazzo F, Condorelli G G, Sakai N, Miyasaka T, Spinella C, La Magna A 2015 Chem. Phys. Chem. 16 3064Google Scholar

    [44]

    Merdasa A, Bag M, Tian Y, Källman E, Dobrovolsky A, Scheblykin I G 2016 J. Phys. Chem. C 120 10711Google Scholar

    [45]

    Slotcavage D J, Karunadasa H I, McGehee M D 2016 ACS Energy Lett. 1 1199Google Scholar

    [46]

    Yang X, Yan X L, Wang W, Zhu X X, Li H, Ma W L, Sheng C X 2016 Org. Electron. 34 79Google Scholar

    [47]

    Hoke E T, Slotcavage D J, Dohner E R, Bowring A R, Karunadasa H I, McGehee M D 2015 Chem. Sci. 6 613Google Scholar

    [48]

    Yoon S J, Kuno M, Kamat P V 2017 ACS Energy Lett. 2 1507Google Scholar

    [49]

    Chen S, Wen X M, Huang S J, Huang F Z, Cheng Y B, Green M, Ho-Baillie A 2017 Solar RRL 1 Unsp 1600001Google Scholar

    [50]

    Mosconi E, Meggiolaro D, Snaith H J, Stranks S D, de Angelis F 2016 Energy Environ. Sci. 9 3180Google Scholar

    [51]

    Divitini G, Cacovich S, Matteocci F, Cinà L, Di Carlo A, Ducati C 2016 Nature Energy 1 15012Google Scholar

    [52]

    Kim N K, Min Y H, Noh S, Cho E, Jeong G, Joo M, Ahn S W, Lee J S, Kim S, Ihm K, Ahn H, Kang Y, Lee H S, Kim D 2017 Sci. Rep. 7 4645Google Scholar

    [53]

    Conings B, Drijkoningen J, Gauquelin N, Babayigit A, D'Haen J, D'Olieslaeger L, Ethirajan A, Verbeeck J, Manca J, Mosconi E, de Angelis F, Boyen H G 2015 Adv. Energy Mater. 5 1500477Google Scholar

    [54]

    Chen W, Wu Y, Yue Y, Liu J, Zhang W, Yang X, Chen H, Bi E, Ashraful I, Grätzel M, Han L 2015 Science 350 944Google Scholar

    [55]

    Kaltenbrunner M, Adam G, Głowacki E D, Drack M, Schwödiauer R, Leonat L, Apaydin D H, Groiss H, Scharber M C, White M S, Sariciftci N S, Bauer S 2015 Nat. Mater. 14 1032Google Scholar

    [56]

    You J, Meng L, Song T B, Guo T F, Yang Y, Chang W H, Hong Z, Chen H, Zhou H, Chen Q, Liu Y, De Marco N, Yang Y 2016 Nat. Nanotechnol. 11 75

    [57]

    deQuilettes D W, Zhang W, Burlakov V M, Graham D J, Leijtens T, Osherov A, Bulović V, Snaith H J, Ginger D S, Stranks S D 2016 Nat. Commun. 7 11683Google Scholar

    [58]

    Gottesman R, Gouda L, Kalanoor B S, Haltzi E, Tirosh S, Rosh-Hodesh E, Tischler Y, Zaban A, Quarti C, Mosconi E, de Angelis F 2015 J. Phys. Chem. Lett. 6 2332Google Scholar

    [59]

    Domanski K, Roose B, Matsui T, Saliba M, Turren-Cruz S H, Correa-Baena J P, Roldan-Carmona C, Richardson G, Foster J M, de Angelis F, Ball J M, Petrozza A, Mine N, Nazeeruddin M K, Tress W, Gratzel M, Steiner U, Hagfeldt A, Abate A 2017 Energy Environ. Sci. 10 604Google Scholar

    [60]

    Zhou Y, You L, Wang S, Ku Z, Fan H, Schmidt D, Rusydi A, Chang L, Wang L, Ren P, Chen L, Yuan G, Chen L, Wang J 2016 Nat. Commun. 7 11193Google Scholar

    [61]

    Brivio F, Caetano C, Walsh A 2016 J. Phys. Chem. Lett. 7 1083Google Scholar

    [62]

    Zhao C, Chen B B, Qiao X F, Luan L, Lu K, Hu B 2015 Adv. Energy Mater. 5 1500279Google Scholar

    [63]

    Huang F, Jiang L, Pascoe A R, Yan Y, Bach U, Spiccia L, Cheng Y B 2016 Nano Energy 27 509Google Scholar

    [64]

    Deschler F, Price M, Pathak S, Klintberg L E, Jarausch D D, Higler R, Hüttner S, Leijtens T, Stranks S D, Snaith H J, Atatüre M, Phillips R T, Friend R H 2014 J. Phys. Chem. Lett. 5 1421Google Scholar

    [65]

    Tian Y, Merdasa A, Unger E, Abdellah M, Zheng K, McKibbin S, Mikkelsen A, Pullerits T, Yartsev A, Sundström V, Scheblykin I G 2015 J. Phys. Chem. Lett. 6 4171Google Scholar

    [66]

    Tian Y X, Peter M, Unger E, Abdellah M, Zheng K, Pullerits T, Yartsev A, Sundstrom V, Scheblykin I G 2015 Phys. Chem. Chem. Phys. 17 24978Google Scholar

    [67]

    Brenes R, Guo D, Osherov A, Noel N K, Eames C, Hutter E M, Pathak S K, Niroui F, Friend R H, Islam M S, Snaith H J, Bulović V, Savenije T J, Stranks S D 2017 Joule 1 155Google Scholar

    [68]

    Buin A, Pietsch P, Xu J, Voznyy O, Ip A H, Comin R, Sargent E H 2014 Nano Lett. 14 6281Google Scholar

    [69]

    Yin W J, Shi T, Yan Y 2014 Appl. Phys. Lett. 104 063903Google Scholar

    [70]

    Buin A, Comin R, Xu J, Ip A H, Sargent E H 2015 Chem. Mater. 27 4405Google Scholar

    [71]

    Mosconi E, de Angelis F 2016 ACS Energy Lett. 1 182Google Scholar

    [72]

    Meloni S, Moehl T, Tress W, Franckevičius M, Saliba M, Lee Y H, Gao P, Nazeeruddin M K, Zakeeruddin S M, Rothlisberger U, Graetzel M 2016 Nat. Commun. 7 10334Google Scholar

    [73]

    Haruyama J, Sodeyama K, Han L, Tateyama Y 2015 J. Am. Chem. Soc. 137 10048Google Scholar

    [74]

    Huang F, Dkhissi Y, Huang W, Xiao M, Benesperi I, Rubanov S, Zhu Y, Lin X, Jiang L, Zhou Y, Gray-Weale A, Etheridge J, McNeill C R, Caruso R A, Bach U, Spiccia L, Cheng Y B 2014 Nano Energy 10 10Google Scholar

    [75]

    Wen X M, Feng Y, Huang S J, Huang F Z, Cheng Y B, Green M, Ho-Baillie A 2016 J. Mater. Chem. C 4 793Google Scholar

    [76]

    Nie W, Blancon J C, Neukirch A J, Appavoo K, Tsai H, Chhowalla M, Alam M A, Sfeir M Y, Katan C, Even J, Tretiak S, Crochet J J, Gupta G, Mohite A D 2016 Nat. Commun. 7 11574Google Scholar

    [77]

    Gottesman R, Haltzi E, Gouda L, Tirosh S, Bouhadana Y, Zaban A, Mosconi E, de Angelis F 2014 J. Phys. Chem. Lett. 5 2662Google Scholar

    [78]

    Azpiroz J M, Mosconi E, Bisquert J, de Angelis F 2015 Energy Environ. Sci. 8 2118Google Scholar

    [79]

    Eames C, Frost J M, Barnes P R F, O’Regan B C, Walsh A, Islam M S 2015 Nat. Commun. 6 7497Google Scholar

    [80]

    Walsh A, Scanlon D O, Chen S Y, Gong X G, Wei S H 2015 Angew. Chem. Int. Ed. 54 1791Google Scholar

    [81]

    Zhang H M, Liang C J, Zhao Y, Sun M J, Liu H, Liang J J, Li D, Zhang F J, He Z Q 2015 Phys. Chem. Chem. Phys. 17 9613Google Scholar

    [82]

    Zu F S, Amsalem P, Salzmann I, Wang R B, Ralaiarisoa M, Kowarik S, Duhm S, Koch N 2017 Adv. Opt. Mater. 5 Unsp 1700139Google Scholar

    [83]

    Noh J H, Im S H, Heo J H, Mandal T N, Seok S I 2013 Nano Lett. 13 1764Google Scholar

    [84]

    Aharon S, Cohen B E, Etgar L 2014 J. Phys. Chem. C 118 17160Google Scholar

    [85]

    Gil-Escrig L, Miquel-Sempere A, Sessolo M, Bolink H J 2015 J. Phys. Chem. Lett. 6 3743Google Scholar

    [86]

    Bischak C G, Hetherington C L, Wu H, Aloni S, Ogletree D F, Limmer D T, Ginsberg N S 2017 Nano Lett. 17 1028Google Scholar

    [87]

    Barker A J, Sadhanala A, deschler F, Gandini M, Senanayak S P, Pearce P M, Mosconi E, Pearson A J, Wu Y, Srimath Kandada A R, Leijtens T, De Angelis F, Dutton S E, Petrozza A, Friend R H 2017 ACS Energy Lett. 2 1416Google Scholar

    [88]

    Draguta S, Sharia O, Yoon S J, Brennan M C, Morozov Y V, Manser J S, Kamat P V, Schneider W F, Kuno M 2017 Nat. Commun. 8 200Google Scholar

    [89]

    Beal R E, Slotcavage D J, Leijtens T, Bowring A R, Belisle R A, Nguyen W H, Burkhard G F, Hoke E T, McGehee M D 2016 J. Phys. Chem. Lett. 7 746Google Scholar

    [90]

    McMeekin D P, Sadoughi G, Rehman W, Eperon G E, Saliba M, Hörantner M T, Haghighirad A, Sakai N, Korte L, Rech B, Johnston M B, Herz L M, Snaith H J 2016 Science 351 151Google Scholar

    [91]

    Jaffe A, Lin Y, Beavers C M, Voss J, Mao W L, Karunadasa H I 2016 ACS Cent. Sci. 2 201Google Scholar

    [92]

    Hu M, Bi C, Yuan Y B, Bai Y, Huang J S 2016 Adv. Sci. 3 1500301Google Scholar

    [93]

    Wei T C, Wang H P, Li T Y, Lin C H, Hsieh Y H, Chu Y H, He J H 2017 Adv. Mater. 29 Unsp 1701789Google Scholar

    [94]

    Kirschner M S, Diroll B T, Guo P, Harvey S M, Helweh W, Flanders N C, Brumberg A, Watkins N E, Leonard A A, Evans A M, Wasielewski M R, Dichtel W R, Zhang X, Chen L X, Schaller R D 2019 Nat. Commun. 10 504Google Scholar

    [95]

    Cottingham P, Brutchey R L 2018 Chem. Mater. 30 6711Google Scholar

    [96]

    Xue J, Yang D, Cai B, Xu X, Wang J, Ma H, Yu X, Yuan G, Zou Y, Song J, Zeng H 2019 Adv. Funct. Mater. 29 1807922

    [97]

    Yettapu G R, Talukdar D, Sarkar S, Swarnkar A, Nag A, Ghosh P, Mandal P 2016 Nano Lett. 16 4838Google Scholar

    [98]

    He Y, Matei L, Jung H J, McCall K M, Chen M, Stoumpos C C, Liu Z, Peters J A, Chung D Y, Wessels B W, Wasielewski M R, Dravid V P, Burger A, Kanatzidis M G 2018 Nat. Commun. 9 1609Google Scholar

    [99]

    Meng Y, Ahmadi M, Wu X, Xu T, Xu L, Xiong Z, Chen P 2019 Org. Electron. 64 47Google Scholar

    [100]

    Zhang Y, Sun H, Zhang S, Li S, Wang X, Zhang X, Liu T, Guo Z 2019 Opt. Mater. 89 563Google Scholar

    [101]

    Huang M Y, Veeramuthu L, Kuo C C, Liao Y C, Jiang D H, Liang F C, Yan Z L, Borsali R, Chueh C C 2019 Org. Electron. 67 294Google Scholar

    [102]

    Tan Z, Wu Y, Hong H, Yin J, Zhang J, Lin L, Wang M, Sun X, Sun L, Huang Y, Liu K, Liu Z, Peng H 2016 J. Am. Chem. Soc. 138 16612Google Scholar

    [103]

    Chen S, Shi G 2017 Adv. Mater. 29 1605448Google Scholar

  • 图 1  铅卤钙钛矿ABX3的结构示意图[1]

    Figure 1.  Structure of lead halide perovskites[1].

    图 2  铅卤钙钛矿及其太阳能电池在持续光照下发生光修复现象时的性能变化 (a) CH3NH3PbI3薄膜在持续光照下的时间分辨PL衰减随光照时间的变化[57]; (b) CH3NH3PbI3薄膜在持续光照下以及不同温度下的PL强度随光照时间的变化[57]; (c) 铅卤钙钛矿太阳能电池ITO/PEDOT:PSS/CH3NH3PbI3–xClx/PCBM/Al在持续光照下的J-V曲线变化[62]; (d) 铅卤钙钛矿太阳能电池ITO/PEDOT:PSS/CH3NH3PbI3–xClx/PCBM/Al在持续光照下的光电转化效率的变化曲线[62]

    Figure 2.  Performance changes of lead halide perovskite and its solar cells under continuous illunination: (a) A series of time-resolved PL decays from CH3NH3PbI3 films measured over time under continuous illumination[57]; (b) the normalized PL intensity of CH3NH3PbI3 films measured over time under continuous illumination at different temperatures[57]; (c) the J-V characteristics of lead halide perovskite solar cell with the architecture of ITO/PEDOT:PSS/CH3NH3PbI3–xClx/PCBM/Al under continuous illumination[62]; (d) the reversibility of power conversion efficiency of lead halide perovskite solar cell with the architecture of ITO/PEDOT:PSS/CH3NH3PbI3–xClx/PCBM/Al under continuous illumination[62].

    图 3  CH3NH3PbI3薄膜发生光修复现象的机理[57] (a) 在发光较弱的晶粒中分布有高浓度的缺陷态以及过量的碘离子; (b) CH3NH3PbI3薄膜经过光照后, 电子迅速填充缺陷, 产生电场, 造成碘离子从照射区域开始迁移, 填充空位; (c)照射区域中的缺陷态密度和碘离子浓度降低, 薄膜最终达到稳定的状态; (d) 当移除光照后, 碘离子存在浓度梯度, 驱使其扩散回弱发光区域, 直至达到新的碘离子浓度平衡

    Figure 3.  Mechanism of photo curing in CH3NH3PbI3 film[57]: (a) Iodide in a "dark spot" is initially high with a corresponding excess of trap density; (b) electrons quickly fill traps under illumination, inducing an electric field that results in iodide to migrate away from the illuminated region and fill vacancies; (c) the fill will reaches a stabilized state, with the reduction of the density of the traps and the concentration of the iodide in illuminated region; (d) when the illumination is removed, there may be a concentration gradients driving some iodides in to the dark spot and the film will reaches a new equilibrium with a net redistributed iodide profile.

    图 4  (a) 传统旋涂法制备的CH3NH3PbI3薄膜在激发密度0.2和0.65 W/cm2下的光致发光强度随时间的变化; (b) 气体辅助溶液工程技术制备的CH3NH3PbI3薄膜在激发密度0.90, 1.55和2.00 W/cm2下的光致发光强度随时间的变化; (c) 传统旋涂法以及气体辅助溶液工程技术制备的CH3NH3PbI3薄膜的光致发光谱和吸收光谱[49]

    Figure 4.  (a) PL intensities over time of CH3NH3PbI3 film fabricated by conventional spin coating under laser excitations at 0.2 and 0.65 W/cm2; (b) PL intensities over time of CH3NH3PbI3 film fabricated by gas-assisted solution process technique under laser excitations at 0.9, 1.55 and 2.00 W/cm2; (c) absorption and PL spectra of samples fabricated conventional spin coating and gas-assisted solution process technique[49].

    图 5  (a) CH3NH3PbI3薄膜在黑暗-光照-黑暗循环中的光致发光强度随时间的变化; (b) CH3NH3PbI3薄膜的光致发光谱随黑暗或光照下放置时间的变化; (c) CH3NH3PbI3薄膜的实验中和理论上的拉曼光谱以及CH3NH3PbI3薄膜在黑暗环境和光照20, 40和60 min后的拉曼光谱[58]

    Figure 5.  (a) PL measurements performed throughout a dark-light-dark cycle, showing the effect of white-light illumination on the PL intensity of the CH3NH3PbI3 film; (b) a graph showing six PL measurements points from the dark-light-dark cycles at different times; (c) a graph showing Experimental (taken in the dark) and theoretical Raman spectra of a CH3NH3PbI3 film as well as the Raman spectra of the same film taken in the dark and following illumination for 20, 40 and 60 min[58]

    图 6  (a) 铅卤钙钛矿太阳能电池ITO/PEDOT:PSS/MAPbI3/PCBM/Al在持续光照下的光电转化效率的变化趋势, 其中工作条件A对应于J = 0, V = Voc; 工作条件B对应于J = Jsc, V = 0; (b) 铅卤钙钛矿材料发生可逆光解现象的机理[76]

    Figure 6.  (a) Time evolution of power conversion efficiency of lead halide perovskite solar cell with the architecture of ITO/PEDOT:PSS/MAPbI3/PCBM/Al under constant 1-Sun illumination. The device is stressed at point A (red circles, J = 0, V = Voc) or point B (blue squares, J = Jsc, V = 0); (b) schematics of the photocurrent degradation and self-healing mechanism[76].

    图 7  (a) 铅卤钙钛矿太阳能电池FTO/TiO2/mp-TiO2/(FAPbI3)x(MAPbBr3)y/spiro-OMeTAD/Au在滤过紫外光后的LED灯光持续照射下的最大功率输出的变化趋势; (b) 钙钛矿层中的离子分布的变化趋势[59]

    Figure 7.  (a) Maximum power output tracking for 3 identically prepared perovskite solar cells (device A, B and C), with the architecture of FTO/TiO2/mp-TiO2/(FAPbI3)x(MAPbBr3)y/spiro-OMeTAD/Au, measured under UV-filtered 1-Sun LED illumination. Experimental data were fitted to an exponential decay (single or double). (b) Schematics of the evolution of ion distribution within the perovskite layer[59].

    图 8  (a) CH3NH3Pb(Br0.6I0.4)3在激发密度50 mW/cm2下光照5 min前(黑线)和后(红线)的XRD图像, 其中虚线分别为CH3NH3Pb(Br0.2I0.8)3和CH3NH3Pb(Br0.7I0.3)3的XRD图像[47]; (b) CH3NH3Pb(Br0.4I0.6)3在激发密度为15 mW/cm2的457 nm激光持续照射下的光致发光谱的变化趋势[47]; (c) CH3NH3Pb(Br0.9I0.1)3在激发密度为50 mW/cm2的405 nm激光持续照射下的阴极发光图像随时间的变化[86]; (d) CH3NH3Pb(Br1–xIx)3在光照下发生光致相分解现象的机理[46]

    Figure 8.  (a) The XRD peak of CH3NH3Pb(Br0.6I0.4)3 film before (black) and after (red) white-light soaking for 5 minutes 50 mW/cm2. XRD patterns of CH3NH3Pb(Br0.2I0.8)3 and CH3NH3Pb(Br0.7I0.3)3 films (dashed brown) are included for comparison[47]; (b) photoluminescence spectra of CH3NH3Pb(Br0.4I0.6)3 film over 45 s in 5 s increments under 457 nm, 15 mW/cm2 at 300 K[47]; (c) a series of cathodo luminescence image after light soaking under a 405 nm LED at 50 mW/cm2[86]; (d) the schematic of two-step mechanism for light-induced phase separation[46].

    图 9  铅卤钙钛矿在持续光照下发生的主要四种不稳定现象 (a) 碘间隙离子/碘空位缺陷对的消除引起光修复现象; (b) 碘空位与阳离子空位的迁移引起光解现象; (c) 亥姆霍兹自由能最小化促使铅卤钙钛矿内部的卤素离子从无序排列向有序排列, 引起光致相分离现象; (d) 光生载流子迁移率差异产生电位差, 造成PBI64–六面体扭力方向的改变, 引起光致相变现象

    Figure 9.  Main four kinds of instability of lead halide perovskites under continuous illumination: (a) Photo-curing induced by the elimination of iodine interstitial ions/iodine vacancies; (b) photo dissociation induced by the migration of iodine vacancies and cation vacancies; (c) phase separation induced by the minimization of Helmholtz free energy; (d) phase transition induced by the difference in the mobility of electrons and holes.

  • [1]

    Sutherland B R, Sargent E H 2016 Nat. Photon. 10 295Google Scholar

    [2]

    Heo J H, Im S H, Noh J H, Mandal T N, Lim C S, Chang J A, Lee Y H, Kim H J, Sarkar A, Nazeeruddin M K, Grätzel M, Seok S I 2013 Nat. Photon. 7 486Google Scholar

    [3]

    Giorgi G, Fujisawa J I, Segawa H, Yamashita K 2013 J. Phys. Chem. Lett. 4 4213Google Scholar

    [4]

    Bisquert J 2013 J. Phys. Chem. Lett. 4 1051Google Scholar

    [5]

    Etgar L, Gao P, Xue Z, Peng Q, Chandiran A K, Liu B, Nazeeruddin M K, Grätzel M 2012 J. Am. Chem. Soc. 134 17396Google Scholar

    [6]

    Abu Laban W, Etgar L 2013 Energy Environ. Sci. 6 3249Google Scholar

    [7]

    Xing G, Mathews N, Sun S, Lim S S, Lam Y M, Grätzel M, Mhaisalkar S, Sum T C 2013 Science 342 344Google Scholar

    [8]

    Stranks S D, Eperon G E, Grancini G, Menelaou C, Alcocer M J P, Leijtens T, Herz L M, Petrozza A, Snaith H J 2013 Science 342 341Google Scholar

    [9]

    Yamada Y, Nakamura T, Endo M, Wakamiya A, Kanemitsu Y 2014 J. Am. Chem. Soc. 136 11610Google Scholar

    [10]

    Stranks S D, Burlakov V M, Leijtens T, Ball J M, Goriely A, Snaith H J 2014 Phys. Rev. Appl. 2 034007Google Scholar

    [11]

    Stoumpos C C, Malliakas C D, Kanatzidis M G 2013 Inorg. Chem. 52 9019Google Scholar

    [12]

    Yantara N, Bhaumik S, Yan F, Sabba D, Dewi H A, Mathews N, Boix P P, Demir H V, Mhaisalkar S 2015 J. Phys. Chem. Lett. 6 4360Google Scholar

    [13]

    Adachi M M, Fan F, Sellan D P, Hoogland S, Voznyy O, Houtepen A J, Parrish K D, Kanjanaboos P, Malen J A, Sargent E H 2015 Nat. Commun. 6 8694Google Scholar

    [14]

    Kojima A, Teshima K, Shirai Y, Miyasaka T 2009 J. Am. Chem. Soc. 131 6050Google Scholar

    [15]

    Kim H S, Lee C R, Im J H, Lee K B, Moehl T, Marchioro A, Moon S J, Humphry-Baker R, Yum J H, Moser J E, Grätzel M, Park N G 2012 Sci. Rep. 2 591Google Scholar

    [16]

    Yang W S, Park B W, Jung E H, Jeon N J, Kim Y C, Lee D U, Shin S S, Seo J, Kim E K, Noh J H, Seok S I 2017 Science 356 1376Google Scholar

    [17]

    Yao K, Li F, He Q Q, Wang X F, Jiang Y H, Huang H T, Jen A K Y 2017 Nano Energy 40 155Google Scholar

    [18]

    Chen R, Hou D, Lu C, Zhang J, Liu P, Tian H, Zeng Z, Xiong Q, Hu Z, Zhu Y, Han L 2018 Sustain. Energ. Fuels 2 1093Google Scholar

    [19]

    Jaramillo-Quintero O A, Sanchez R S, Rincon M, Mora-Sero I 2015 J. Phys. Chem. Lett. 6 1883Google Scholar

    [20]

    Kim Y H, Cho H, Heo J H, Kim T S, Myoung N, Lee C L, Im S H, Lee T W 2015 Adv. Mater. 27 1248Google Scholar

    [21]

    Li J Q, Bade S G R, Shan X, Yu Z B 2015 Adv. Mater. 27 5196Google Scholar

    [22]

    Tang B, Dong H, Sun L, Zheng W, Wang Q, Sun F, Jiang X, Pan A, Zhang L 2017 ACS Nano 11 10681Google Scholar

    [23]

    Yakunin S, Protesescu L, Krieg F, Bodnarchuk M I, Nedelcu G, Humer M, de Luca G, Fiebig M, Heiss W, Kovalenko M V 2015 Nat. Commun. 6 8056Google Scholar

    [24]

    Sutherland B R, Hoogland S, Adachi M M, Wong C T O, Sargent E H 2014 ACS Nano 8 10947Google Scholar

    [25]

    Fu Y, Zhu H, Stoumpos C C, Ding Q, Wang J, Kanatzidis M G, Zhu X, Jin S 2016 ACS Nano 10 7963Google Scholar

    [26]

    Domanski K, Tress W, Moehl T, Saliba M, Nazeeruddin M K, Gratzel M 2015 Adv. Funct. Mater. 25 6936Google Scholar

    [27]

    Sutherland B R, Johnston A K, Ip A H, Xu J, Adinolfi V, Kanjanaboos P, Sargent E H 2015 ACS Photon. 2 1117Google Scholar

    [28]

    Lian Z, Yan Q, Lv Q, Wang Y, Liu L, Zhang L, Pan S, Li Q, Wang L, Sun J L 2015 Sci. Rep. 5 16563Google Scholar

    [29]

    Adinolfi V, Ouellette O, Saidaminov M I, Walters G, Abdelhady A L, Bakr O M, Sargent E H 2016 Adv. Mater. 28 7264Google Scholar

    [30]

    Zhao D, Wang C, Song Z, Yu Y, Chen C, Zhao X, Zhu K, Yan Y 2018 ACS Energy Lett. 3 305Google Scholar

    [31]

    Lin K, Xing J, Quan L N, de Arquer F P G, Gong X, Lu J, Xie L, Zhao W, Zhang D, Yan C, Li W, Liu X, Lu Y, Kirman J, Sargent E H, Xiong Q, Wei Z 2018 Nature 562 245Google Scholar

    [32]

    Chiba T, Hayashi Y, Ebe H, Hoshi K, Sato J, Sato S, Pu Y J, Ohisa S, Kido J 2018 Nat. Photon. 12 681Google Scholar

    [33]

    Cao Y, Wang N, Tian H, Guo J, Wei Y, Chen H, Miao Y, Zou W, Pan K, He Y, Cao H, Ke Y, Xu M, Wang Y, Yang M, Du K, Fu Z, Kong D, Dai D, Jin Y, Li G, Li H, Peng Q, Wang J, Huang W 2018 Nature 562 249Google Scholar

    [34]

    Berhe T A, Su W N, Chen C H, Pan C J, Cheng J H, Chen H M, Tsai M C, Chen L Y, Dubale A A, Hwang B J 2016 Energy Environ. Sci. 9 323Google Scholar

    [35]

    Abdi-Jalebi M, Andaji-Garmaroudi Z, Cacovich S, Stavrakas C, Philippe B, Richter J M, Alsari M, Booker E P, Hutter E M, Pearson A J, Lilliu S, Savenije T J, Rensmo H, Divitini G, Ducati C, Friend R H, Stranks S D 2018 Nature 555 497Google Scholar

    [36]

    Frost J M, Butler K T, Brivio F, Hendon C H, van Schilfgaarde M, Walsh A 2014 Nano Lett. 14 2584Google Scholar

    [37]

    Yang J, Siempelkamp B D, Liu D, Kelly T L 2015 ACS Nano 9 1955Google Scholar

    [38]

    Christians J A, Miranda Herrera P A, Kamat P V 2015 J. Am. Chem. Soc. 137 1530Google Scholar

    [39]

    Li Y, Xu X, Wang C, Wang C, Xie F, Yang J, Gao Y 2015 J. Phys. Chem. C 119 23996Google Scholar

    [40]

    Song Z N, Abate A, Watthage S C, Liyanage G K, Phillips A B, Steiner U, Graetzel M, Heben M J 2016 Adv. Energy Mater. 6 1600846Google Scholar

    [41]

    Aristidou N, Sanchez-Molina I, Chotchuangchutchaval T, Brown M, Martinez L, Rath T, Haque S A 2015 Angew. Chem. Int. Ed. 54 8208Google Scholar

    [42]

    Bryant D, Aristidou N, Pont S, Sanchez-Molina I, Chotchunangatchaval T, Wheeler S, Durrant J R, Haque S A 2016 Energy Environ. Sci. 9 1655Google Scholar

    [43]

    Alberti A, Deretzis I, Pellegrino G, Bongiorno C, Smecca E, Mannino G, Giannazzo F, Condorelli G G, Sakai N, Miyasaka T, Spinella C, La Magna A 2015 Chem. Phys. Chem. 16 3064Google Scholar

    [44]

    Merdasa A, Bag M, Tian Y, Källman E, Dobrovolsky A, Scheblykin I G 2016 J. Phys. Chem. C 120 10711Google Scholar

    [45]

    Slotcavage D J, Karunadasa H I, McGehee M D 2016 ACS Energy Lett. 1 1199Google Scholar

    [46]

    Yang X, Yan X L, Wang W, Zhu X X, Li H, Ma W L, Sheng C X 2016 Org. Electron. 34 79Google Scholar

    [47]

    Hoke E T, Slotcavage D J, Dohner E R, Bowring A R, Karunadasa H I, McGehee M D 2015 Chem. Sci. 6 613Google Scholar

    [48]

    Yoon S J, Kuno M, Kamat P V 2017 ACS Energy Lett. 2 1507Google Scholar

    [49]

    Chen S, Wen X M, Huang S J, Huang F Z, Cheng Y B, Green M, Ho-Baillie A 2017 Solar RRL 1 Unsp 1600001Google Scholar

    [50]

    Mosconi E, Meggiolaro D, Snaith H J, Stranks S D, de Angelis F 2016 Energy Environ. Sci. 9 3180Google Scholar

    [51]

    Divitini G, Cacovich S, Matteocci F, Cinà L, Di Carlo A, Ducati C 2016 Nature Energy 1 15012Google Scholar

    [52]

    Kim N K, Min Y H, Noh S, Cho E, Jeong G, Joo M, Ahn S W, Lee J S, Kim S, Ihm K, Ahn H, Kang Y, Lee H S, Kim D 2017 Sci. Rep. 7 4645Google Scholar

    [53]

    Conings B, Drijkoningen J, Gauquelin N, Babayigit A, D'Haen J, D'Olieslaeger L, Ethirajan A, Verbeeck J, Manca J, Mosconi E, de Angelis F, Boyen H G 2015 Adv. Energy Mater. 5 1500477Google Scholar

    [54]

    Chen W, Wu Y, Yue Y, Liu J, Zhang W, Yang X, Chen H, Bi E, Ashraful I, Grätzel M, Han L 2015 Science 350 944Google Scholar

    [55]

    Kaltenbrunner M, Adam G, Głowacki E D, Drack M, Schwödiauer R, Leonat L, Apaydin D H, Groiss H, Scharber M C, White M S, Sariciftci N S, Bauer S 2015 Nat. Mater. 14 1032Google Scholar

    [56]

    You J, Meng L, Song T B, Guo T F, Yang Y, Chang W H, Hong Z, Chen H, Zhou H, Chen Q, Liu Y, De Marco N, Yang Y 2016 Nat. Nanotechnol. 11 75

    [57]

    deQuilettes D W, Zhang W, Burlakov V M, Graham D J, Leijtens T, Osherov A, Bulović V, Snaith H J, Ginger D S, Stranks S D 2016 Nat. Commun. 7 11683Google Scholar

    [58]

    Gottesman R, Gouda L, Kalanoor B S, Haltzi E, Tirosh S, Rosh-Hodesh E, Tischler Y, Zaban A, Quarti C, Mosconi E, de Angelis F 2015 J. Phys. Chem. Lett. 6 2332Google Scholar

    [59]

    Domanski K, Roose B, Matsui T, Saliba M, Turren-Cruz S H, Correa-Baena J P, Roldan-Carmona C, Richardson G, Foster J M, de Angelis F, Ball J M, Petrozza A, Mine N, Nazeeruddin M K, Tress W, Gratzel M, Steiner U, Hagfeldt A, Abate A 2017 Energy Environ. Sci. 10 604Google Scholar

    [60]

    Zhou Y, You L, Wang S, Ku Z, Fan H, Schmidt D, Rusydi A, Chang L, Wang L, Ren P, Chen L, Yuan G, Chen L, Wang J 2016 Nat. Commun. 7 11193Google Scholar

    [61]

    Brivio F, Caetano C, Walsh A 2016 J. Phys. Chem. Lett. 7 1083Google Scholar

    [62]

    Zhao C, Chen B B, Qiao X F, Luan L, Lu K, Hu B 2015 Adv. Energy Mater. 5 1500279Google Scholar

    [63]

    Huang F, Jiang L, Pascoe A R, Yan Y, Bach U, Spiccia L, Cheng Y B 2016 Nano Energy 27 509Google Scholar

    [64]

    Deschler F, Price M, Pathak S, Klintberg L E, Jarausch D D, Higler R, Hüttner S, Leijtens T, Stranks S D, Snaith H J, Atatüre M, Phillips R T, Friend R H 2014 J. Phys. Chem. Lett. 5 1421Google Scholar

    [65]

    Tian Y, Merdasa A, Unger E, Abdellah M, Zheng K, McKibbin S, Mikkelsen A, Pullerits T, Yartsev A, Sundström V, Scheblykin I G 2015 J. Phys. Chem. Lett. 6 4171Google Scholar

    [66]

    Tian Y X, Peter M, Unger E, Abdellah M, Zheng K, Pullerits T, Yartsev A, Sundstrom V, Scheblykin I G 2015 Phys. Chem. Chem. Phys. 17 24978Google Scholar

    [67]

    Brenes R, Guo D, Osherov A, Noel N K, Eames C, Hutter E M, Pathak S K, Niroui F, Friend R H, Islam M S, Snaith H J, Bulović V, Savenije T J, Stranks S D 2017 Joule 1 155Google Scholar

    [68]

    Buin A, Pietsch P, Xu J, Voznyy O, Ip A H, Comin R, Sargent E H 2014 Nano Lett. 14 6281Google Scholar

    [69]

    Yin W J, Shi T, Yan Y 2014 Appl. Phys. Lett. 104 063903Google Scholar

    [70]

    Buin A, Comin R, Xu J, Ip A H, Sargent E H 2015 Chem. Mater. 27 4405Google Scholar

    [71]

    Mosconi E, de Angelis F 2016 ACS Energy Lett. 1 182Google Scholar

    [72]

    Meloni S, Moehl T, Tress W, Franckevičius M, Saliba M, Lee Y H, Gao P, Nazeeruddin M K, Zakeeruddin S M, Rothlisberger U, Graetzel M 2016 Nat. Commun. 7 10334Google Scholar

    [73]

    Haruyama J, Sodeyama K, Han L, Tateyama Y 2015 J. Am. Chem. Soc. 137 10048Google Scholar

    [74]

    Huang F, Dkhissi Y, Huang W, Xiao M, Benesperi I, Rubanov S, Zhu Y, Lin X, Jiang L, Zhou Y, Gray-Weale A, Etheridge J, McNeill C R, Caruso R A, Bach U, Spiccia L, Cheng Y B 2014 Nano Energy 10 10Google Scholar

    [75]

    Wen X M, Feng Y, Huang S J, Huang F Z, Cheng Y B, Green M, Ho-Baillie A 2016 J. Mater. Chem. C 4 793Google Scholar

    [76]

    Nie W, Blancon J C, Neukirch A J, Appavoo K, Tsai H, Chhowalla M, Alam M A, Sfeir M Y, Katan C, Even J, Tretiak S, Crochet J J, Gupta G, Mohite A D 2016 Nat. Commun. 7 11574Google Scholar

    [77]

    Gottesman R, Haltzi E, Gouda L, Tirosh S, Bouhadana Y, Zaban A, Mosconi E, de Angelis F 2014 J. Phys. Chem. Lett. 5 2662Google Scholar

    [78]

    Azpiroz J M, Mosconi E, Bisquert J, de Angelis F 2015 Energy Environ. Sci. 8 2118Google Scholar

    [79]

    Eames C, Frost J M, Barnes P R F, O’Regan B C, Walsh A, Islam M S 2015 Nat. Commun. 6 7497Google Scholar

    [80]

    Walsh A, Scanlon D O, Chen S Y, Gong X G, Wei S H 2015 Angew. Chem. Int. Ed. 54 1791Google Scholar

    [81]

    Zhang H M, Liang C J, Zhao Y, Sun M J, Liu H, Liang J J, Li D, Zhang F J, He Z Q 2015 Phys. Chem. Chem. Phys. 17 9613Google Scholar

    [82]

    Zu F S, Amsalem P, Salzmann I, Wang R B, Ralaiarisoa M, Kowarik S, Duhm S, Koch N 2017 Adv. Opt. Mater. 5 Unsp 1700139Google Scholar

    [83]

    Noh J H, Im S H, Heo J H, Mandal T N, Seok S I 2013 Nano Lett. 13 1764Google Scholar

    [84]

    Aharon S, Cohen B E, Etgar L 2014 J. Phys. Chem. C 118 17160Google Scholar

    [85]

    Gil-Escrig L, Miquel-Sempere A, Sessolo M, Bolink H J 2015 J. Phys. Chem. Lett. 6 3743Google Scholar

    [86]

    Bischak C G, Hetherington C L, Wu H, Aloni S, Ogletree D F, Limmer D T, Ginsberg N S 2017 Nano Lett. 17 1028Google Scholar

    [87]

    Barker A J, Sadhanala A, deschler F, Gandini M, Senanayak S P, Pearce P M, Mosconi E, Pearson A J, Wu Y, Srimath Kandada A R, Leijtens T, De Angelis F, Dutton S E, Petrozza A, Friend R H 2017 ACS Energy Lett. 2 1416Google Scholar

    [88]

    Draguta S, Sharia O, Yoon S J, Brennan M C, Morozov Y V, Manser J S, Kamat P V, Schneider W F, Kuno M 2017 Nat. Commun. 8 200Google Scholar

    [89]

    Beal R E, Slotcavage D J, Leijtens T, Bowring A R, Belisle R A, Nguyen W H, Burkhard G F, Hoke E T, McGehee M D 2016 J. Phys. Chem. Lett. 7 746Google Scholar

    [90]

    McMeekin D P, Sadoughi G, Rehman W, Eperon G E, Saliba M, Hörantner M T, Haghighirad A, Sakai N, Korte L, Rech B, Johnston M B, Herz L M, Snaith H J 2016 Science 351 151Google Scholar

    [91]

    Jaffe A, Lin Y, Beavers C M, Voss J, Mao W L, Karunadasa H I 2016 ACS Cent. Sci. 2 201Google Scholar

    [92]

    Hu M, Bi C, Yuan Y B, Bai Y, Huang J S 2016 Adv. Sci. 3 1500301Google Scholar

    [93]

    Wei T C, Wang H P, Li T Y, Lin C H, Hsieh Y H, Chu Y H, He J H 2017 Adv. Mater. 29 Unsp 1701789Google Scholar

    [94]

    Kirschner M S, Diroll B T, Guo P, Harvey S M, Helweh W, Flanders N C, Brumberg A, Watkins N E, Leonard A A, Evans A M, Wasielewski M R, Dichtel W R, Zhang X, Chen L X, Schaller R D 2019 Nat. Commun. 10 504Google Scholar

    [95]

    Cottingham P, Brutchey R L 2018 Chem. Mater. 30 6711Google Scholar

    [96]

    Xue J, Yang D, Cai B, Xu X, Wang J, Ma H, Yu X, Yuan G, Zou Y, Song J, Zeng H 2019 Adv. Funct. Mater. 29 1807922

    [97]

    Yettapu G R, Talukdar D, Sarkar S, Swarnkar A, Nag A, Ghosh P, Mandal P 2016 Nano Lett. 16 4838Google Scholar

    [98]

    He Y, Matei L, Jung H J, McCall K M, Chen M, Stoumpos C C, Liu Z, Peters J A, Chung D Y, Wessels B W, Wasielewski M R, Dravid V P, Burger A, Kanatzidis M G 2018 Nat. Commun. 9 1609Google Scholar

    [99]

    Meng Y, Ahmadi M, Wu X, Xu T, Xu L, Xiong Z, Chen P 2019 Org. Electron. 64 47Google Scholar

    [100]

    Zhang Y, Sun H, Zhang S, Li S, Wang X, Zhang X, Liu T, Guo Z 2019 Opt. Mater. 89 563Google Scholar

    [101]

    Huang M Y, Veeramuthu L, Kuo C C, Liao Y C, Jiang D H, Liang F C, Yan Z L, Borsali R, Chueh C C 2019 Org. Electron. 67 294Google Scholar

    [102]

    Tan Z, Wu Y, Hong H, Yin J, Zhang J, Lin L, Wang M, Sun X, Sun L, Huang Y, Liu K, Liu Z, Peng H 2016 J. Am. Chem. Soc. 138 16612Google Scholar

    [103]

    Chen S, Shi G 2017 Adv. Mater. 29 1605448Google Scholar

  • [1] Meiling Yao, Jixing Liao, Haofeng Lu, Qiang Huang, Yanfeng Cui, Xiang Li, Xueying Yang, Yang Bai. Key issues and solutions affecting the efficiency and stability of perovskite/heterojunction tandem solar cells. Acta Physica Sinica, 2024, 0(0): . doi: 10.7498/aps.73.20231977
    [2] Liu Si-Wen, Ren Li-Zhi, Jin Bo-Wen, Song Xin, Wu Cong-Cong. Preparation of two-dimensional perovskite layer by solution method for improving stability of FAPbI3 perovskite solar cells. Acta Physica Sinica, 2024, 73(6): 068801. doi: 10.7498/aps.73.20231678
    [3] Wang Jing, Gao Shan, Duan Xiang-Mei, Yin Wan-Jian. Influence of defect in perovskite solar cell materials on device performance and stability. Acta Physica Sinica, 2024, 73(6): 063101. doi: 10.7498/aps.73.20231631
    [4] Meng Jing, Gao Bo-Wen. Photovoltaic performance of novel Perovskite/organic integrated solar cells with high efficiency and high stability. Acta Physica Sinica, 2023, 72(1): 018802. doi: 10.7498/aps.72.20221120
    [5] Ma Shu-Peng, Lin Fei-Yu, Luo Yuan, Zhu Liu, Guo Xue-Yi, Yang Ying. Formation mechanism of CsPbBr3 in multi-step spin-coating process. Acta Physica Sinica, 2022, 71(15): 158101. doi: 10.7498/aps.71.20220171
    [6] Xu Ting, Wang Zi-Shuai, Li Xuan-Hua, Sha Wei E. I.. Loss mechanism analyses of perovskite solar cells with equivalent circuit model. Acta Physica Sinica, 2021, 70(9): 098801. doi: 10.7498/aps.70.20201975
    [7] Zhao Xin-Wei, Lü Jun-Peng, Ni Zhen-Hua. Lead halide perovskites Fabry-Pérot resonant cavity laser. Acta Physica Sinica, 2021, 70(5): 054205. doi: 10.7498/aps.70.20201302
    [8] Li Yan, He Hong, Dang Wei-Wu, Chen Xue-Lian, Sun Can, Zheng Jia-Lu. Research progress of light irradiation stability of functional layers in perovskite solar cells. Acta Physica Sinica, 2021, 70(9): 098402. doi: 10.7498/aps.70.20201762
    [9] Fan Qin-Hua, Zu Yan-Qing, Li Lu, Dai Jin-Fei, Wu Zhao-Xin. Research progress of stability of luminous lead halide perovskite nanocrystals. Acta Physica Sinica, 2020, 69(11): 118501. doi: 10.7498/aps.69.20191767
    [10] Bai Qing-Shun, Dou Yu-Hao, He Xin, Zhang Ai-Min, Guo Yong-Bo. Deposition and growth mechanism of graphene on copper crystal surface based on molecular dynamics simulation. Acta Physica Sinica, 2020, 69(22): 226102. doi: 10.7498/aps.69.20200781
    [11] Zhang Yu, Zhou Huan-Ping. Intrinsic stability of organic-inorganic hybrid perovskite. Acta Physica Sinica, 2019, 68(15): 158804. doi: 10.7498/aps.68.20190343
    [12] Zhu Zhen-Ye. Piezoelectric effect mechanism in lead-free tetragonal perovskite short-period superlattices. Acta Physica Sinica, 2018, 67(7): 077701. doi: 10.7498/aps.67.20172710
    [13] Liu Na, Wei Yang, Ma Xin-Guo, Zhu Lin, Xu Guo-Wang, Chu Liang, Huang Chu-Yun. Theoretical study on the stability and photoelectric properties of APbI3 perovskite. Acta Physica Sinica, 2017, 66(5): 057103. doi: 10.7498/aps.66.057103
    [14] Zheng Jian, Zhang Duo, Jiang Bang-Hai, Lu Fang-Yun. Formation mechanism of water jets induced by the interaction between bubble and free surface. Acta Physica Sinica, 2017, 66(4): 044702. doi: 10.7498/aps.66.044702
    [15] Zhang Dan-Fei, Zheng Ling-Ling, Ma Ying-Zhuang, Wang Shu-Feng, Bian Zu-Qiang, Huang Chun-Hui, Gong Qi-Huang, Xiao Li-Xin. Factors influencing the stability of perovskite solar cells. Acta Physica Sinica, 2015, 64(3): 038803. doi: 10.7498/aps.64.038803
    [16] Wang Gong-Tang, Liu Xiu-Xi. Studies on the mechanisms of enhancing the performances of thyristors by Ga-Al doping. Acta Physica Sinica, 2010, 59(3): 1964-1969. doi: 10.7498/aps.59.1964
    [17] Liu Jian-Ye, Guo Wen-Jun, Zuo Wei, Li Xi-Guo. The equation of state of the isospin asymmetrical nuclear matter. Acta Physica Sinica, 2009, 58(3): 1517-1525. doi: 10.7498/aps.58.1517
    [18] Liu Jian-Ye, Guo Wen-Jun, Zuo Wei, Lee Xi-Guo. Isospin effect of nucleon-nucleon cross section on the isoscaling parameter α. Acta Physica Sinica, 2008, 57(9): 5458-5463. doi: 10.7498/aps.57.5458
    [19] Liu Xiu-Xi, Wang Gong-Tang. Fabrication of high voltage thyristor based on silicon organic compounds and metal oxides type isolation protective material. Acta Physica Sinica, 2008, 57(1): 576-580. doi: 10.7498/aps.57.576
    [20] FU RONG-TANG, SUN XIN. PEIERLS MECHANISM OF HYDROGEN CHAIN (Ⅱ)——THE DEPENDENCE OF THE PEIERLS INSTABILITY ON THE ELECTRON CORRELATION. Acta Physica Sinica, 1992, 41(2): 221-227. doi: 10.7498/aps.41.221
Metrics
  • Abstract views:  14682
  • PDF Downloads:  543
  • Cited By: 0
Publishing process
  • Received Date:  07 March 2019
  • Accepted Date:  12 April 2019
  • Available Online:  01 August 2019
  • Published Online:  05 August 2019

/

返回文章
返回